(54)

Vacuum drying method

Trocknungsverfahren unter Vakuum

Méthode de séchage sous vide


(84)Designated Contracting States:
DE FR GB NL

(30)Priority: 20.01.1989 JP 11618/89

(43)Date of publication of application:
01.08.1990 Bulletin 1990/31

(73)Proprietor: FUJI PHOTO FILM CO., LTD.
Kanagawa (JP)

(72)Inventor:
  • Naitoh, Kenji, c/o Fuji Photo Film Co., Ltd.
    Minami Ashigara-shi, Kanagawa (JP)

(74)Representative: Hansen, Bernd, Dr. Dipl.-Chem. et al
Hoffmann Eitle, Patent- und Rechtsanwälte, Postfach 81 04 20
81904 München
81904 München (DE)


(56)References cited: : 
DE-A- 3 536 608
JP-A-62 192 471
JP-A- 6 064 108
JP-B- 6 114 777
  
      
    Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


    Description


    [0001] This invention relates to a method of obtaining a powdery dry polymerizate from a solution of polymerizate to be dried.

    [0002] Various methods have been proposed in the past to obtain a powdery polymerizate from a solution of polymerizate to be dried. In one method, for example, using a centrifugal thin film evaporator, a polymerizate is extracted in the molten state and then cooled and solidified; while in another method, the solution is coated in the form of a sheet on a belt in a band drier, and a dry powder is obtained. The former method, however, has the disadvantages that the viscosity rises sharply so that the material cannot be drawn off, and as operations are carried out at high temperature, deteriorations occur which are undesirable from the viewpoint of quality. The latter method, on the other hand, suffers from the disadvantage that due to a sharp rise in viscosity, the volatile constituents cannot be completely evaporated.

    [0003] In addition, in another conventional method known as reprecipitation, a solution of the polymerizate is dripped into a solvent which is a poor solvent for the polymerizate but a good solvent for the solvent in which the polymerizate is dissolved. This precipitates the polymerizate, which is then filtered and dried. As this method requires a very large amount of solvent, however, it requires a large tank and productivity therefore declines. Further, the mother liquors from filtration must also be treated, and the method is thus not economical.

    [0004] Another method uses a heated long tube as described in, for example, JP-A-58-79501 and JP-A-60-90001 . In this method, the solution containing volatile component and component which is difficult to volatize is evaporated in a heated evaporator, and supplied continuously to a cooling crusher. In the crusher, the component which is difficult to volatize is cooled, solidified and crushed while volatile components remaining in said non-volatile components are further evaporated.

    [0005] There are however various problems in attempting to dry a polymerizate solution by means of a heated long tube. When polymerizate solution supplied at a constant flow rate is blown from said tube into a reduced pressure vessel, the product obtained is often a sticky solution containing 10 - 20 wt % of residual volatile components, or a massive material which contains sticky solution and is not yet dry. Even if the operating conditions and equipment conditions are varied, it only produces a slight change in the volatile components, and a dry material that can be handled as a powder is not easily obtained. Furthermore, if the product of blowing is a sticky solution and a massive material containing a sticky solution, it is extremely difficult to remove it from the reduced pressure vessel to a condition under atmospheric pressure.

    [0006] To blow a polymerizate as powdery state from a heated long tube is thus an important issue.

    [0007] Further, the cooling crusher has a complex structure and is costly, and if it is attempted to produce many different types of powders with one apparatus, its complex structure makes cleaning difficult when changing over from one product to the other product. In particular, it was found that this problem constitutes a considerable obstacle industrially when the non-volatile component is the objective product.

    [0008] According to past experience, when the long tube was heated, hot water is used as heating medium if a temperature of 100°C or below was desired, or steam is used if the temperature was 100°C or above. An example of the former process is disclosed in JP-B-61-14777, and an example of the latter in JP-A-58-79501 and JP-A-6090001. If said methods are applied to a polymerizate of low softening point, however, the heat capacity of hot water is insufficient, and then only a thick sticky liquid can be obtained. If on the other hand, steam at 100°C or over is used as in the latter method, a powdery polymerizate is blown out. As this has a low softening point, however, it is soft, and the powder sticks together to form lumps or adhere to the wall of the reduced pressure vessel, and cannot be drawn off.

    [0009] This invention was conceived to overcome the above problems. One object of the invention is to provide a drying method wherein an organic compound for photograph, and in particular a polymerizate with photoraphically useful groups, can be separated from solution, wherein different compounds can be easily produced with one apparatus, and wherein cost of the equipment is low.

    [0010] The objects of this invention are achieved by a method of vacuum drying a solution of a polymerizate having a glass transition temperature of 30°C to 100°C, wherein the method contains the steps that the solution is diluted with a solvent, so that its viscosity is adjusted to 1 to 20 centipoise, that the diluted solution is supplied to a steam-heated long tube, wherein the steam is at a temperature of 50 to 100°C, that the solid-vapor mixture of powdery dry polymerizate and vapor produced in said tube is blown out under reduced pressure, and that the powdery dry polymerizate and vapor are separated, so as to obtain the powdery dry polymerizate.

    [0011] It is preferred to adjust the viscosity of the solution to 2 to 10 centipoise.

    [0012] The method of the present invention is in particular useful if a solution of a polymerizate having photographically useful groups is used to be dried.

    [0013] This invention can be more fully understood from the following detailed description when taken in conjunction with the accompanying drawings, in which:

    [0014] Fig. 1 is a schematic drawing of the equipment which can be used in the vacuum drying method of this invention.

    [0015] We shall now describe this invention in more detail.

    [0016] The action of the vacuum drying method using a heating tube is generally explained by the successive formation of 4 regions as follows:

    (1) a laminar preheating region where the temperature of the solution is increased by sensible heat up to its boiling point,

    (2) a bubbling region where volatile components are partially evaporated by latent heat of vaporization so as to form minute bubbles,

    (3) a thin film evaporating region where evaporation proceeds further, vapor passes the center of the tube, and the solution becomes more concentrated on the tube walls,

    (4) a crystallizing region where substantially all of the volatile components in the solution are vaporized, and the great expansion of the volume has the powerful effect which scraps the concentrated material off the tube wall thereby forming a solid-gas (vapor) two phase flow.



    [0017] The inventor of the present invention, as a result of intensive research, found that by diluting the solution of a polymerizate having a glass transition temperature of 30°C to 100°C with a solvent has a boiling point of preferably 40 - 160°C under normal pressure such that its viscosity is adjusted to 1 - 20 cps, and supplying of the diluted solution to a steam-heated long tube at a constant flow rate, a powdery dry polymerizate which contained no sticky material whatever can be blown out of the heating tube. This is due to the successful formation of the above mentioned thin film evaporation region and crystallization region inside the heating tube, and it can be explained as follows. When the viscosity of the solution supplied is high, the solution in the thin film evaporating region in the neighborhood of the tube wall becomes more concentrated, and heat transfer from the wall falls sharply. It is thought that as a result, evaporation cannot proceed properly toward the center of the tube, the material blown out of the tube is a sticky solution, or massive material containing sticky material.

    [0018] On the other hand, it is conjectured, when the viscosity of the solution supplied is low, evaporation of solvent is greater, and due to the scraping effect mentioned above, heat transfer in the thin film evaporating region is adequate.

    [0019] Dilution with solvent is not desirable from an energy or a productivity viewpoint. However, from the overall viewpoint that this method makes it possible to convert a solution of a polymerizate to powdery state in one step, it does offer a considerable economic advantage.

    [0020] The inventor of the present invention found that by supplying a polymerizate solution of 1 - 20 cps to a steam-heated long tube whose temperature is maintained with water vapor the temperature of which is controlled to be 50 - 100°C (referred to hereafter as low-pressure steam), it can be prevented that the powdery polymerizate blown out of the end of the tune sticks together. The low-pressure steam mentioned here is water vapor at 100°C or less, and preferably at 50 - 100°C, produced by for example the method disclosed in JP-A-60-64108. It is however also possible to produce low-pressure steam by analog instruments, and the method of producing low-pressure steam is not limited to that given here.

    [0021] In this way, by adjusting the solution of the polymerizate to be dried to 1 - 20 cps, more preferably 2 - 10 cps, supplying it, preferably at a constant flow rate, to a steam-heated long tube, blowing out the solid/gas mixture of the powdery polymerizate to be dried and vapor, produced in the tube, to a reduced pressure atmosphere (referred to hereafter also as "to a reduced pressure vessel"), and separating the powdery polymerizate to be dried and gas, a powdery polymerizate can be obtained, and in particular, in the case of a polymerizate solution of 1 - 20 cps, by passing low-pressure steam at 50 - 100°C through the heating tube, adhesion of the blown-out powder in the reduced pressure vessel can be prevented, and powdery dry polymerizate can be obtained either continuously or intermittently without damage to the equipment. Further, if polymerizates, preferably, polymers (to be defined later) are used as the material to be dried, this method gives remarkable results.

    [0022] This invention may be implemented by suitably choosing equipment conditions and choosing operating conditions, such as the internal diameter and length of the steam-heated long tube, supply rate and degree of reduced pressure of the vacuum vessel, within the limits known to those skilled in the art.

    [0023] The steam-heated long tube used in this invention may be a double-pipe tube of the prior art, for example the tube disclosed in Japanese Utility Model No. 1222088 (Orient Kagaku Kogyo K.K., JP-B-52-28862).

    [0024] The length of the inner tube through which the solution of the material to be dried passes should preferably be 100 to 10,000, more preferably 500 - 2,000 times its internal diameter. The internal diameter of the inner tube of the steam-heated long tube should be 3 - 50 mm, more preferably 10 - 25 mm.

    [0025] Any outer tube which surrounds this inner tube may be used provided it is of such a form that heating steam can be passed through it, and it may typically be cylindrical.

    [0026] The material of the inner tube should preferably be a stainless steel such as SUS-304 or 316 from the viewpoint of anti-corrosion properties, and for the outer tube, gas piping such as SGP may be used.

    [0027] One end of the inner tube of the steam-heated long tube is connected to the upper part of a vessel under reduced pressure (referred to hereafter also as a reduced pressure vessel). The vessel is a cylinder with a conical base. The conical shape is chosen for the base to facilitate removal of the dried powder.

    [0028] The capacity of the vessel may be chosen freely depending on the hourly quantity processed. This capacity also varies depending on the bulk density of the material to be dried and the quantity that is to be temporarily stored, but it may typically be 100 - 10,000 litter, and more preferably, 500 - 2,000 litter.

    [0029] To maintain the whole vessel at a different temperature to that of the environment, any suitable means, preferably the means which can automatically control temperature, may be provided.

    [0030] As the polymerizate to be dried, polymerizates with a glass transition temperature of 30 - 100°C and preferably 35 - 80°C can be used.

    [0031] If such substances with a low glass transition temperature are used as polymerizates to be dried, the use of low-pressure steam is preferable.

    [0032] In this invention, the word "polymerizate" has a wide range of meaning, including both addition polymerizates and polycondensation polymerizates, and including polymerizates with a number-averaged molecular weight from 1,000 - 1,000,000. Further, in this invention, the term "polymer" refers to addition polymerizates and particularly vinyl polymers with a molecular weight of 10,000 or more, the same definition being applied to the term polymer in the expression "polymer coupler". Further, in this invention, the term "telomer" refers to addition polymerizates and particularly vinyl polymers with a number-averaged molecular weight of 1,000 - 10,000, the same definition being applied to the term telomer in the expression "telomer coupler".

    [0033] The glass transition temperature may be easily determined by, for example, differential thermal analysis.

    [0034] Polymerizates with a low glass transition temperature include polycondensation polymerizates and addition polymerizates, typical examples being the chain polymers obtained by the polymerization of so-called vinyl monomers, and typical weight-averaged molecular weights being 1,000 - 500,000.

    [0035] In this invention, the polymerizate to be dried is supplied as a solution which has been adjusted to 1 - 20 centipoise (cps), and preferably at a constant flow rate, to a steam-heated long tube. Viscosities specified in this invention are absolute viscosities at 25°C.

    [0036] The solvent used to dissolve the polymerizate may be any solvent provided it has a boiling point in the range 40 - 160°C at normal pressure, and preferably one which is a good solvent for the polymerizate. It is still more preferable that the solvent has a boiling point in the range 40 - 120°C at normal pressure. If the boiling point of the solvent is above 160°C at normal pressure, a heating medium at 180°C or more is required for the long tube, with the result that the powdery polymerizate is not obtained and the product is partially molten. Even if the powdery polymerizate is obtained, it sticks together in the vacuum vessel or to the walls of the vessel, and the process does not go smoothly. If on the other hand the the boiling point of the solvent is at 40°C or below, an extremely large condensation vessel is required when recovering evaporated solvent, and the process loses its industrial value.

    [0037] We shall describe the method of adjusting the polymerizate solution to 1 - 20 cps. If the polymerization reaction solution is within the above limits there is no need to perform any adjustment, however if the viscosity is above 20 cps, it must be diluted with a suitable solvent to give a homogeneous solution. It is preferable that 80 volume % or more of the solvent comprises a good solvent for the polymerizate. The actual degree of dilution to be made is intricately linked to, for example, the molecular weight of the polymerizate, its concentration and its softening point, but in general the final concentration will be 0.1 - 40 wt %.

    [0038] Constant flow rate supplying may be performed by any suitable device, and it may be performed with or without pulsation. The preferred quantity of solution to be supplied depends on the heat transfer area defined by the internal diameter and length of the heated part of the duplex tube. If the quantity supplied is too great, the polymerizate becomes sticky, and if the quantity is too small, blockages occur in the tube. The optimum quantity may be determined by preliminary tests.

    [0039] By suitably choosing the quantity of solution supplied, a solid/gas mixture consisting of powdery dry polymerizate and vapor is produced in the heating tube, and by blowing this mixture into a vessel under reduced pressure, the powdery dry polymerizate and solvent vapor are separated. In this case, a suitable reduced pressure is 3 - 500 Torr, more preferably 30 - 200 Torr.

    [0040] Examples of polymerizates which can be applied to this invention are polymerizates with photographically useful groups.

    [0041] Examples of such polymerizates are typical oil soluble polymer couplers. The monomer couplers and polymer initiators of polymer coupler, used to synthesize these polymerizates, are disclosed in JP-A-59-42543 (Patent Application No. 57-153452) by Yagihara et al. Monomer couplers which are used preferably are disclosed in the reference, page (3), upper right column, line 5 to page (13), upper right column, and methods of manufacturing them are disclosed as (1) - (25), on page (18), lower left column.

    [0042] These are obtained by copolymerization of couplers with vinyl groups (monomer couplers) and vinyl monomers without photographically useful groups. Examples of photographically useful groups of polymerizates which can be used in this invention include groups known to those skilled in the art such as ultra-violet absorbent (for example as disclosed in JP-B-63-53541 and JP-A-58-178351), dyes, redox (reduction-oxidation) groups, and cationic residue groups useful as mordants.

    [0043] Specific examples of oil soluble polymer couplers are disclosed in the following references.

    [0044] Pyrazolone magenta polymer couplers are disclosed, for example, in US-A-3,767,412, US-A-3,623,871, US-A-4,207,109, US-A-3,424,583, US-A-3,370,952, JP-A-57-94742, JP-A-58-28745, JP-A-58-120252, and JP-A-57-94752.

    [0045] Pyrazoloazole magenta polymer couplers are disclosed, for example, in JP-A-59-228252, JP-A-59-171956, JP-A-60-220346, and Research Disclosure 25724.

    [0046] Other useful oil soluble polymer couplers are disclosed, for example, in US-A-3,451,820, JP-A-60-46555, JP-A-58-145944 and JP-A-60-158365, and polymer couplers which is a relatively low molecular weight the average molecular weight being in the range 1000 - 10,000, (these polymers are also known as telomer couplers), are disclosed in JP-A-62-276548 and JP-A-62-278547, and may be dried according to the method of this invention.

    [0047] Specific examples of lipophilic polymer couplers to which this invention can be applied are given in Table 1, and specific examples of telomer couplers are given in Table 2.

    [0048] Further, specific examples of monomers that can be used in the manufacture of polymerizates to which this invention can be applied are given later in Table 3.

    [0049] The compound numbers in the coupler monomer columns of Table 1 and Table 2 correspond to the compound numbers shown in Table 3.









    [0050] According to the vacuum drying method of this invention, low-molecular-weight oil-soluble couplers, for color developing or telomers or polymers containing e.g. coupler residue groups, redox residue groups or ultra-violet absorbent residue groups, may be easily obtained from its solution in the form of a dry powder with very little residual solvent. In particular, a dry powdery material can still be obtained if the method is applied to oil soluble polymers with a glass transition temperature of 30 - 100°C. Further, this method gives a polymer coupler which, when used as a color photo-sensitive material, gives little background fog and has excellent coloring properties in comparison to the product dried by the known method of reprecipitation.

    EXAMPLES


    Example 1



    [0051] A solution of a material to be dried was dried using vacuum drying equipment having the construction shown in Fig. 1. A glass window was installed in the upper wall of first reduced pressure vessel 4 so as to be able to observe the state of the powdery material blown, and the interior of the vessel.

    [0052] The sample to be dried was a oil soluble polymer magenta coupler having weight-average molecular weight of 30 × 10⁴ (determined by GPC based on monodispersed polystyrene) and a glass transition temperature Tg of 70°C (determined by DSC). Its repeating unit and copolymerization ratio expressed as wt % is as follows:



    [0053] 250 kg of a homogeneous solution containing 30 wt % of a sample to be dried in toluene/n-BuOH (9:1 W/W), was diluted with ethyl acetate to give a homogenous solution containing 10 wt % of the sample to be dried. The viscosity of this solution was 3 cps (measured at 25°C by a B type viscosimeter). This solution was delivered by constant rate pump 2 at a constant flow rate of 50 litter/hr from dilute solution tank 1 to one end of steam-heated long tube 3 in which pressurized steam at 121°C was passed, and the product was blown from the other end of the tube into first reduced pressure vessel 4. First reduced pressure vessel 4 had been previously evacuated to a vacuum of 20 - 40 Torr by vacuum generator 9, and hot water at 40°C had been circulated in jacket 16 such that solvent vapor did not condense.

    [0054] It was confirmed that said solution supplied at a constant rate was blown out continuously from the other end of said heating tube as a powder/gas mixture. On the otherhand, solvent vapor was passed through 1st bag filter 6, condensed by condenser 7 and collected in solvent tank 8.

    [0055] When there was no more solution in diluted solution tank 1, 100 litter of ethyl acetate was added to the tank, and the solution in the steam-heated long tube swept out with ethyl acetate vapor by operating the system under the same conditions.

    [0056] The powder in 1st reduced pressure vessel 4 occupied about 70% of its volume. First valve 11 was then opened and, while operating stirrer 5 which so far had been at rest, the powder was transferred to 2nd reduced pressure vessel 12 which had been previously evacuated via 2nd bag filter 14 to 20 - 40 Torr by 2nd vacuum generator 15. When the transfer of powder to the 2nd vacuum vessel was complete, the 1st valve was shut and the stirrer 5 was stopped.

    [0057] Next, the 2nd reduced pressure vessel 12 was put under atmospheric pressure, 2nd valve 13 was opened, and the powdery material was withdrawn outside the system.

    [0058] It was found that in moving the powder from the 1st reduced pressure vessel to the 2nd reduced pressure vessel, the opening and closing operation of the 1st valve and the rotation operation of the stirrer went smoothly, and all the powder was transferred to the 2nd reduced pressure vessel. Further, when the 1st reduced pressure vessel was observed through the window, it was found that there was no adhesion of powder at all to the walls of the vessel or to the stirrer. Further, the powder removed from the system was in the state of dry powder and contained 2.0 wt % of volatile constituents.

    Comparative Example (Comparison with Example 1)



    [0059] The operations were carried out in the same way as Example 1 except that the homogeneous solution containing 30 wt % of a sample to be dried in toluene/n-BuOH (9:1 W/W) was not diluted. The absolute viscosity of this solution was 70 cps.

    [0060] The material blown out from the end of the steam-heated long tube was a sticky material.

    Example 2



    [0061] A polymerization was carried out to prepare a sample to be dried as in Example 1, the copolymer ratio of monomer containing 5-pyrazolone and butyl acrylate being changed to 45/55 (by weight), and a oil soluble polymer coupler being weight-averaged molecular weight Mw of 7 × 10⁴ and glass transition temperature Tg of 35°C was obtained. 250 kg of a homogeneous solution containing 30 wt % of this polymer coupler in ethyl acetate/IPA (70:30 W/W), was diluted with ethyl acetate to give a homogenous solution containing 12 wt % of the sample. The viscosity of this solution was 2 cps (centipoise) (measured at 25°C by a B type viscosimeter).

    [0062] The diluted solution was delivered at a constant flow rate of 80 litter/hr from to the steam-heated long tube in which low-pressure steam at 95°C, supplied by low-pressure steam generator 17, was passed. Well water at 18°C was circulated through jacket 16 of the 1st reduced pressure vessel. The other operations were same as those of Example 1.

    [0063] As in Example 1, it was found that the powdery material could be transferred smoothly from the 1st reduced pressure vessel to the 2nd reduced pressure vessel. It was also found that there was no adhesion of the powder at all to the interior of the 1st reduced pressure vessel. Further, the powdery material removed from the system contained 2.5 wt % of volatile constituents and was in the state of dry powder.

    Comparative Example



    [0064] The same operations as in Example 2 were carried out, excepting that pressurized steam at 121°C was passed in heat the tube instead of low-pressure steam.

    [0065] The material blown out from the tube was in a state of satisfactory powder, however when transferring this powder from 1st reduced pressure vessel to 2nd reduced pressure vessel, it stuck together, or adhered to the walls of the 1st reduced pressure vessel, the stirrer and 1st valve. The 1st valve could no longer be open and shut, and as a result, the powder in 1st reduced pressure vessel could not be removed from the system.

    Example 3



    [0066] 250 kg of a solution containing 30 wt % of the oil soluble coupler (B) (mp = 166°C), in acetone was dried by carrying out the same operations as in Example 1. The viscosity of this solution was 2 cps.

    [0067] As in Example 1, it was found that the powder could be transferred smoothly from the 1st reduced pressure vessel to the 2nd reduced pressure vessel. It was also found that there was no adhesion of the powder at all to the interior of the 1st reduced pressure vessel. Further, the powdery material removed from the system was in a state of dry powder containing 2.0 wt % of volatile constituents.


    5-[2-2(2,4-di-tert-amylphenoxy)hexanamido]-2-[3-(4-cyanophenyl)ureido]phenol

    Example 4



    [0068] The oil soluble polymer couplers (1) - (3) were vacuum dried by the method based on the method of Example 1. These couplers and the solutions had the following characteristics:
    Coupler (1):
       Weight-averaged molecular weight = 250,000
       Tg = 65°C
       Viscosity of solution = 3 cps
    Coupler (2):
       Weight-averaged molecular weight = 30,000
       Tg = 75°C
       Viscosity of solution = 12 cps
    Coupler (3):
       Weight-averaged molecular weight = 40,000
       Tg = 55°C
       Viscosity of solution = 18 cps

    [0069] All the couplers were obtained in a state of dry powder containing no more than 2.0% wt % of volatile constituents.






































































































































































    Claims

    1. A method of vacuum drying a solution of a polymerizate having a glass transition temperature of 30°C to 100°C, wherein the method contains the steps that the solution is diluted with a solvent, so that its viscosity is adjusted to 1 to 20 centipoise, that the diluted solution is supplied to a steam-heated long tube, wherein the steam is at a temperature of 50 to 100°C, that the solid-vapor mixture of powdery dry polymerizate and vapor produced in said tube is blown out under reduced pressure, and that the powdery dry polymerizate and vapor are separated, so as to obtain the powdery dry polymerizate.
     
    2. The vacuum drying method as in claim 1, characterized in that the solution has been adjusted to 2 to 10 centipoise.
     
    3. The vacuum drying method as in claim 1 or 2, characterized in that a solution of a polymerizate having photographically useful groups is used to be dried.
     
    4. The vacuum drying method as claimed in any of the claims 1 to 3, characterized in that a solution of a polymerizate having a glass transition temperature of 35°C to 80°C is used to be dried.
     
    5. The vacuum drying method as claimed in anyone of the claims 1 to 4, wherein the solution is adjusted with a solvent having a boiling point of 40 to 160°C under normal pressure.
     
    6. The vacuum drying method as claimed in anyone of the claims 1 to 5, wherein the adjusted solution is supplied to the tube at a constant flow rate.
     
    7. The vacuum drying method as claimed in anyone of the claims 1 to 6, wherein the length of the tube is 100 to 10,000 times its internal diameter.
     
    8. The vacuum drying method as claimed in anyone of the claims 1 to 7, wherein the internal diameter of an inner tube of the steam-heated long tube is 3 to 50 mm.
     
    9. The vacuum drying method as claimed in anyone of the claims 1 to 8, wherein the steam is low pressure steam.
     


    Ansprüche

    1. Verfahren zum Vakuumtrocknen einer Lösung eines Polymerisates mit einer Glasübergangstemperatur von 30 bis 100°C, wobei das Verfahren die Schritte umfaßt, daß die Lösung mit einem Lösungsmittel verdünnt wird, so daß deren Viskosität auf 1 bis 20 Centipoise eingestellt wird, daß die verdünnte Lösung einer dampferhitzten langen Röhre zugeführt wird, wobei der Dampf bei einer Temperatur von 50 bis 100°C vorliegt, daß die Feststoff-Dampf-Mischung des pulverförmigen trockenen Polymerisates und des Dampfes, die in der Röhre erzeugt ist, unter vermindertem Druck herausgeblasen wird, und daß das pulverförmige trockene Polymerisat und der Dampf getrennt werden, um so das pulerförmige trockene Polymerisat zu erhalten.
     
    2. Vakuumtrocknungsverfahren nach Anspruch 1, dadurch gekennzeichnet, daß die Lösung auf 2 bis 10 Centipoise eingestellt worden ist.
     
    3. Vakuumtrocknungsverfahren nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß eine Lösung eines Polymerisates mit photographisch nützlichen Gruppen verwendet wird, das getrocknet werden soll.
     
    4. Vakuumtrocknungsverfahren nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß eine Lösung aus einem Polymerisat mit einer Glasübergangstemperatur von 35 bis 80°C zum Trocknen verwendet wird.
     
    5. Vakuumtrocknungsverfahren nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß die Lösung mit einem Lösungsmittel mit einem Siedepunkt von 40 bis 160°C unter normalem Druck eingestellt wird.
     
    6. Vakuumtrocknungsverfahren nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß die eingestellte Lösung zu der Röhre mit einer konstanten Flußrate zugeführt wird.
     
    7. Vakuumtrocknungsverfahren nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß die Länge der Röhre 100 bis 10000mal dem inneren Durchmesser ist.
     
    8. Vakuumtrocknungsverfahren nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, daß der innere Durchmesser einer inneren Röhre der dampferhitzten langen Röhre 3 bis 50 mm ist.
     
    9. Vakuumtrocknungsverfahren nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, daß der Dampf-Niederdruck Dampf ist.
     


    Revendications

    1. Procédé de séchage sous vide d'une solution d'un polymérisat ayant une température de transition vitreuse de 30°C à 100°C, où le procédé comprend les stades consistant en ce que la solution est diluée avec un solvant, de façon que sa viscosité soit réglée de 1 à 20 centipoises, en ce que la solution diluée est fournie à un long tube chauffé à la vapeur, où la vapeur est à une température de 50 à 100°C, en ce que le mélange solide-vapeur du polymérisat pulvérulent sec et de la vapeur produit dans ledit tube est expulsé sous pression réduite, et en ce que le polymérisat pulvérulent sec et la vapeur sont séparés, de manière à obtenir le polymérisat pulvérulent sec.
     
    2. Procédé de séchage sous vide selon la revendication 1, caractérisé en ce que la solution a été ajustée à 2-10 centipoises.
     
    3. Procédé de séchage sous vide selon la revendication 1 ou 2, caractérisé en ce qu'on utilise pour être séchée une solution d'un polymérisat ayant des groupes utiles sur le plan photographique.
     
    4. Procédé de séchage sous vide selon l'une quelconque des revendications 1 à 3, caractérisé en ce qu'on utilise pour être séchée une solution d'un polymérisat ayant une température de transition vitreuse comprise entre 35°C et 80°C.
     
    5. Procédé de séchage sous vide selon l'une quelconque des revendications 1 à 4, dans lequel la solution est ajustée avec un solvant ayant un point d'ébullition compris entre 40 et 160°C sous pression normale.
     
    6. Procédé de séchage sous vide selon l'une quelconque des revendications 1 à 5, dans lequel la solution ajustée est fournie au tube à un débit constant.
     
    7. Procédé de séchage sous vide selon l'une quelconque des revendications 1 à 6, dans lequel la longueur du tube est égale à 100-10'000 fois son diamètre interne.
     
    8. Procédé de séchage sous vide selon l'une quelconque des revendications 1 à 7, dans lequel le diamètre interne d'un tube intérieur du long tube chauffé à la vapeur est de 3 à 50 mm.
     
    9. Procédé de séchage sous vide selon l'une quelconque des revendications 1 à 8, dans lequel la vapeur est une vapeur à basse pression.
     