(19)
(11)EP 1 731 446 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
27.05.2009 Bulletin 2009/22

(21)Application number: 06252931.8

(22)Date of filing:  06.06.2006
(51)International Patent Classification (IPC): 
B65D 81/26(2006.01)
A23L 3/3436(2006.01)

(54)

A method of oxygen scavenging by triggering a film containing an oxygen scavenger

Verfahren zum Sauerstofffangen durch Auslösen eines sauerstofffänger haltigen Films

Procédé d'élimination d'oxygène par l'activation d'un film contenant un absorbeur d'oxygène


(84)Designated Contracting States:
AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LI LT LU LV MC NL PL PT RO SE SI SK TR

(30)Priority: 07.06.2005 US 146848

(43)Date of publication of application:
13.12.2006 Bulletin 2006/50

(73)Proprietor: Cryovac, Inc.
Duncan, South Carolina 29334 (US)

(72)Inventors:
  • Speer, Drew V.
    Simpsonville, SC 29681 (US)
  • Edwards, Frank B.
    Simpsonville, SC 29681 (US)
  • Beckwith, Scott W.
    Greer, SC 29651 (US)
  • Rivett, Janet
    Simpsonville, SC 29680 (US)
  • Kennedy, Thomas D.
    Simpsonville, SC 29681 (US)

(74)Representative: Duckworth, Timothy John 
J.A. Kemp & Co., 14 South Square, Gray's Inn
London WC1R 5JJ
London WC1R 5JJ (GB)


(56)References cited: : 
US-A- 5 346 644
US-A1- 2004 081 584
US-A1- 2002 081 358
US-A1- 2005 092 963
  
      
    Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


    Description

    Field of the Invention



    [0001] The invention relates to a method of scavenging oxygen from a package containing a product that comprises a peroxide.

    Background of the Invention



    [0002] Peroxides such as hydrogen peroxide and carbamide peroxide are used in many products. US Patent Application Publication No. US 20020086039 (Lee et al.) describes the use of peroxide in such products as cosmetic, personal care, cleaning agent, biocidal agent, functional food, and nutritional supplement compositions, antibacterial, antiseptic, antibiotic and first aid products, depilatory, epilatory and hair bleaching products, toothpaste products, mouthwash and mouth rinse products, contact lens treatment products, laundry detergent, stain remover, and fabric softening products. It is well known that the decomposition of peroxides produces a significant volume increase. It is well understood that the liquid form of hydrogen peroxide decomposes to produced a volume increase of 11.2 times the volume of gaseous oxygen, on a molar basis. It is also well known that the breakdown of peroxides is accelerated by various factors including heat, light (particularly UV light) and the presence of transition metals. Thus, as described in US Patent No. 5,814,304 (Wong et al.), these peroxy compounds can have the undesirable effect of gas evolution that can cause the swelling and sometimes bursting of tubes containing a product having a hydrogen peroxide.

    [0003] Oxygen scavengers are well known in packaging materials for use in packaging many oxygen sensitive products, including food products. Exemplary is US Patent No. 5,350,622 (Speer et al.)

    [0004] US 6,818,150 (Galland et al.) (see also US-A-2005/092963) discloses a packaging article, such as a rigid container or flexible bag, having an oxygen scavenging polymer, and wetting the interior surface of the article with a solution containing a peroxide. The '150 patent requires that the wetted surface be exposed to an initiating factor in the form of ultraviolet light, heat at a certain minimum level of hydrogen peroxide, visible light at certain wavelengths, or electron beam radiation, to initiate the oxygen scavenging reaction.

    Summary Of The Invention



    [0005] The inventors have now found that an oxygen scavenger can be triggered by exposure to a peroxide, such as hydrogen peroxide present in a packaged product, and exposure to the associated enriched (hyperbaric) oxygen atmosphere in the package, without the need for, and in the absence of, activation with actinic radiation such as ultraviolet light, visible light, and electron beam radiation, or heat, to trigger the oxygen scavenging reaction. The presence and activation of the oxygen scavenger is useful in the packaging of compositions that contain a peroxide and as a result generate oxygen over time. The likelihood of explosion or expansion of the package is reduced, as the oxygen scavenger scavenges oxygen being given off by the natural degradation of the peroxide. Since peroxide decomposition can be accelerated by light, in one embodiment the package can be opaque to UV and/or visible light.

    [0006] In a first aspect of the present invention, a method is provided of scavenging oxygen from a package containing a product that comprises peroxide comprising packaging the product in a film comprising an oxygen scavenger; wherein the peroxide or an associated enriched oxygen environment triggers the scavenging in the absence of ultraviolet light, heat, visible light, and electron beam radiation.

    [0007] The method of the present invention may be used in a package which comprises an oxygen scavenger film comprising a first layer comprising a material selected from the group consisting of metallized or pigmented polyester, polypropylene, polyamide, high density polyethylene, ethylene/vinyl alcohol copolymer, polytetrafluoroethylene, poly(vinyl chloride), cycloolefin copolymer, oriented poly(styrene), and ethylene/propylene copolymer; a second layer comprising ink, pigment or a metallized polymeric substrate, a third layer comprising an oxygen scavenger, and a fourth layer comprising an ethylene homopolymer or copolymer; and a product, contained in the package, comprising a peroxide.

    [0008] The method of the present invention may also be used in a package which comprises an oxygen scavenger film comprising a first layer comprising a material selected from the group consisting of metallized or pigmented polyester, polypropylene, polyamide, high density polyethylene, ethylene/vinyl alcohol copolymer, polytetrafluoroethylene, poly(vinyl chloride), cycloolefin copolymer, oriented poly(styrene), and ethylene/propylene copolymer; a second layer comprising an oxygen scavenger, and a third layer comprising an ethylene homopolymer or copolymer; and a product, contained in the package, comprising a peroxide.

    Definitions



    [0009] An "associated enriched oxygen environment" herein means any atmosphere, inside a package, containing greater than 21% oxygen by volume, the atmosphere generated by the presence of a composition, in the package, comprising a peroxide.

    [0010] A "composition comprising a peroxide" herein refers to any composition that comprises hydrogen peroxide or any organic or inorganic peroxide or hydroperoxide, or a percarbonate or perborate that liberates oxygen when wet.

    [0011] "Oxygen scavenger", "oxygen scavenging", and the like herein means or refers to a composition, compound, film, film layer, coating, plastisol, gasket, or the like which can consume, deplete or react with oxygen from a given environment.

    [0012] "Film" herein means a film, laminate, sheet, web, coating, or the like. The film can be used as a component in a rigid, semi-rigid, or flexible product, and can be adhered to a non-polymeric or non-thermoplastic substrate such as paper or metal.

    [0013] "Polymer" and the like herein means a homopolymer, but also copolymers thereof, including bispolymers, terpolymers, etc.

    [0014] "Polyester" herein includes copolyesters.

    [0015] "Polyamide" herein includes copolyamides.

    [0016] "Polypropylene" herein includes propylene copolymers such as propylene/ethylene copolymer.

    [0017] High oxygen barrier films can be made from materials having an oxygen permeability, of the barrier material, less than 500 cm3 O2 / m2• day • atmosphere (tested at 1 mil thick and at 25 °C according to ASTM D3985), such as less than 100, less than 50 and less than 25 cm3 O2 / m2 • day • atmosphere such as less than 10, less than 5, and less than 1 cm3 O2 / m2 • day • atmosphere. Examples of polymeric materials with low oxygen transmission rates are ethylene/vinyl alcohol copolymer (EVOH), polyvinylidene dichloride (PVDC), vinylidene chloride/ methyl acrylate copolymer, polyamide, amorphous polyamide and polyester.

    [0018] Alternatively, metal foil or SiOx compounds can be used to provide low oxygen transmission and low moisture transmission rate properties to the container. Metallized foils can include a sputter coating or other application of a metal layer to a polymeric substrate such as high density polyethylene (HDPE), ethylene/vinyl alcohol copolymer (EVOH), polypropylene (PP), cavitated polypropylene, polyethylene terephthalate (PET), polyethylene naphthalate (PEN), and polyamide (PA).

    [0019] Additionally, barrier properties of polymeric packaging materials can be enhanced by applying a non-polymeric, non-oxide, non-metallic barrier coating. One such technology uses a carbon deposition.

    [0020] Alternatively, oxide coated webs (e.g. aluminum oxide or silicon oxide) can be used to provide low oxygen and low moisture transmission rate properties to the container. Oxide coated webs can include a coating or other application of the oxide, such as alumina or silica, to a polymeric substrate such as high density polyethylene (HDPE), ethylene/vinyl alcohol copolymer (EVOH), polypropylene (PP), polyethylene terephthalate (PET), polyethylene naphthalate (PEN), and polyamide (PA).

    [0021] Also useful in the present invention are high aspect ratio particles that are dispersed in the polymer used to produce the wall of the container, or coatings containing high aspect ratio particles that are applied to the surface of a film. These coatings may be used on one of the exterior surfaces of the package, or they may be buried in the composition through processes such as lamination or subsequent coating processes. High aspect-ratio particles include, but are not limited to, nano-clays, silicas, mica, talc, and vermiculite.

    [0022] High moisture barrier films can be made from materials having a moisture vapor transmission rate (MVTR) of less than 1.0 g·mm/m2·day at 25 °C, preferably less than 0.5 g·mm/m2·day and more preferably less than 0.2 g·mm/m2·day at 25 °C. Materials such as high density polyethylene, cyclic olefin copolymers, polypropylene, PVDC, metal, metallized and metal oxide coated webs can thusly provide excellent moisture barrier properties.

    [0023] "Ethylene/alpha-olefin copolymer" (EAO) herein refers to copolymers of ethylene with one or more comonomers selected from C3 to C10 alpha-olefins such as propene, butene-1,hexene-1, octene-1, etc. in which the molecules of the copolymers comprise long polymer chains with relatively few side chain branches arising from the alpha-olefin which was reacted with ethylene. This molecular structure is to be contrasted with conventional high pressure low or medium density polyethylenes which are highly branched with respect to EAOs and which high pressure polyethylenes contain both long chain and short chain branches. EAO includes such heterogeneous materials as linear medium density polyethylene (LMDPE), linear low density polyethylene (LLDPE), and very low and ultra low density polyethylene (VLDPE and ULDPE), such as DOWLEX™ or ATTANE™ resins supplied by Dow, ESCORENE™ or EXCEED™ resins supplied by Exxon; as well as linear homogeneous ethylene/alpha olefin copolymers (HEAO) such as TAFMER™ resins supplied by Mitsui Petrochemical Corporation, EXACT™ resins supplied by Exxon, or long chain branched (HEAO) AFFINITY™ resins supplied by the Dow Chemical Company, or ENGAGE™ resins supplied by DuPont Dow Elastomers.

    [0024] "Trigger" and the like herein means that process whereby oxygen scavenging is initiated (i.e. activated), wherein after initiation the oxygen scavenging rate of the article is at least about 0.05 cc oxygen per day per gram of oxidizable organic compound for at least two days after oxygen scavenging is initiated.

    [0025] All compositional percentages used herein are presented on a "by weight" basis, unless designated otherwise.

    Detailed Description of the Invention



    [0026] An oxygen scavenger film for use in the invention can include multiple layers, dependent upon the properties required of the film.

    [0027] Polymeric adhesives can be used in some embodiments of the present invention to adhere adjacent layers together, and can include e.g. ethylene/vinyl acetate copolymer; anhydride grafted ethylene/vinyl acetate copolymer; anhydride grafted ethylene/alpha olefin copolymer; anhydride grafted polypropylene; anhydride grafted low density polyethylene; ethylene/ methyl acrylate copolymer; and anhydride grafted ethylene/ methyl acrylate copolymer.

    The peroxide



    [0028] The peroxide composition of the method and package of the invention can have from 0.5% to 25%, such as from 1% to 20%, 3% to 18%, 4% to 16%, and 5% to 10% by weight of the composition, of a peroxide. The peroxide can be any suitable peroxide, such as hydrogen peroxide, carbamide peroxide, sodium peroxide carbonate, or any organic or inorganic peroxide or hydroperoxide as well as percarbonates and perborates that liberate oxygen when wet.

    The oxygen scavenger



    [0029] Oxygen scavengers suitable for commercial use in articles of the present invention, such as films, are disclosed in U.S. Patent No. 5,350,622. According to U.S. Patent No. 5,350,622, oxygen scavengers are made of an ethylenically unsaturated hydrocarbon and transition metal catalyst. The ethylenically unsaturated hydrocarbon may be either substituted or unsubstituted. As defined herein, an unsubstituted ethylenically unsaturated hydrocarbon is any compound that possesses at least one aliphatic carbon-carbon double bond and comprises 100% by weight carbon and hydrogen. A substituted ethylenically unsaturated hydrocarbon is defined herein as an ethylenically unsaturated hydrocarbon which possesses at least one aliphatic carbon-carbon double bond and comprises about 50% - 99% by weight carbon and hydrogen. Suitable substituted or unsubstituted ethylenically unsaturated hydrocarbons are those having two or more ethylenically unsaturated groups per molecule, e.g. a polymeric compound having three or more ethylenically unsaturated groups and a molecular weight equal to or greater than 1,000 weight average molecular weight.

    [0030] Examples of unsubstituted ethylenically unsaturated hydrocarbons include, but are not limited to, diene polymers such as polyisoprene, (e.g., trans-polyisoprene) and copolymers thereof, cis and trans 1,4-polybutadiene, 1,2-polybutadienes, (which are defined as those polybutadienes possessing greater than or equal to 50% 1,2 microstructure), and copolymers thereof, such as styrene/butadiene copolymer and styrene/isoprene copolymer. Such hydrocarbons also include polymeric compounds such as polypentenamer, polyoctenamer, and other polymers prepared by cyclic olefin metathesis; diene oligomers such as squalene; and polymers or copolymers with unsaturation derived from dicyclopentadiene, norbornadiene, 5-ethylidene-2-norbornene, 5-vinyl-2-norbornene, 4-vinylcyclohexene, 1,7-octadiene, or other monomers containing more than one carbon-carbon double bond (conjugated or non-conjugated).

    [0031] Examples of substituted ethylenically unsaturated hydrocarbons include, but are not limited to, those with oxygen-containing moieties, such as esters, carboxylic acids, aldehydes, ethers, ketones, alcohols, peroxides, and/or hydroperoxides. Specific examples of such hydrocarbons include, but are not limited to, condensation polymers such as polyesters derived from monomers containing carbon-carbon double bonds, and unsaturated fatty acids such as oleic, ricinoleic, dehydrated ricinoleic, and linoleic acids and derivatives thereof, e.g. esters. Specific examples also include esters or polyesters of functionalized unsaturated hydrocarbons such as hydroxy terminated polybutadiene. Such hydrocarbons also include polymers or copolymers derived from (meth)allyl (meth)acrylates. Suitable oxygen scavenging polymers can be made by trans-esterification. Such polymers are disclosed in US Patent No. 5,859,145 (Ching et al.) (Chevron Research and Technology Company). The composition used may also comprise a mixture of two or more of the substituted or unsubstituted ethylenically unsaturated hydrocarbons described above. While a weight average molecular weight of 1,000 or more is beneficial, an ethylenically unsaturated hydrocarbon having a lower molecular weight is also usable, especially if it is blended with a film-forming polymer or blend of polymers.

    [0032] An additional example of oxygen scavengers which can be used in connection with this invention are disclosed in PCT patent publication WO 99/48963 (Chevron Chemical et al.). These oxygen scavengers include a polymer or oligomer having at least one cyclohexene group or functionality. These oxygen scavengers include a polymer having a polymeric backbone, cyclic olefinic pendent group, and linking group linking the olefinic pendent group to the polymeric backbone. An oxygen scavenger that has proven useful commercially is poly(ethylene/methyl acrylate/ cyclohexene methyl acrylate) (abbreviated as EMCM).

    [0033] An oxygen scavenging composition suitable for use with the invention comprises:
    1. (a) a polymer or lower molecular weight material containing substituted cyclohexene functionality according to the following diagram:

      where A may be hydrogen or methyl and either one or two of the B groups is a heteroatom-containing linkage which attaches the cyclohexene ring to the said material, and wherein the remaining B groups are hydrogen or methyl; and
    2. (b) a transition metal catalyst.


    [0034] The compositions may be polymeric in nature or they may be lower molecular weight materials. In either case, they may be blended with further polymers or other additives. In the case of low molecular weight materials, they will most likely be compounded with a carrier resin before use.

    [0035] Also suitable for use in the present invention is the oxygen scavenger of US Patent No. 6,255,248 (Bansleben et al.) which discloses a copolymer of ethylene and a strained, cyclic alkylene, preferably cyclopentene; and a transition metal catalyst.

    [0036] Another oxygen scavenger which can be used in connection with this invention is the oxygen scavenger of US Patent No. 6,214,254 (Gauthier et al.) which discloses ethylene/vinyl aralkyl copolymer and a transition metal catalyst.

    [0037] Alternative oxygen scavengers that can beneficially be used in connection with the second and third aspects of the invention include ascorbate; isoascorbate; sulfite; sulfite exchanged hydrotalcite; ascorbate and a transition metal catalyst, the catalyst comprising a simple metal or salt, or a compound, complex or chelate of the transition metal; a transition metal complex or chelate of a polycarboxylic acid, salicylic acid, or polyamine; a tannin; or a reduced metal such as iron. Suitable oxygen scavenging hydrotalcite compositions are disclosed in US 5,941,037. Suitable reduced metal compositions are disclosed in US 5,798,055. Suitable ascorbate based oxygen scavenging compositions are disclosed in US 5,977,212. These inorganic oxygen scavengers can be advantageous in providing both oxygen scavenging capability and opacity.

    [0038] An optimal package structure may contain more than one type of oxygen scavenger and/or more than one layer comprising an oxygen scavenger.

    Transition Metal Catalysts



    [0039] As indicated above, the ethylenically unsaturated hydrocarbon is combined with a transition metal catalyst. Suitable metal catalysts are those that can readily interconvert between at least two oxidation states.

    [0040] The catalyst can be in the form of a transition metal salt, with the metal selected from the first, second or third transition series of the Periodic Table. Suitable metals include, but are not limited to, manganese II or III, iron II or III, cobalt II or III, nickel II or III, copper I or II, rhodium II, III or IV, and ruthenium II or III. The oxidation state of the metal when introduced is not necessarily that of the active form. Suitable counterions for the metal include, but are not limited to, chloride, acetate, stearate, palmitate, caprylate, linoleate, tallate, 2-ethylhexanoate, neodecanoate, oleate or naphthenate. Useful salts include cobalt (II) 2-ethylhexanoate, cobalt stearate, and cobalt (II) neodecanoate. The metal salt may also be an ionomer, in which case a polymeric counterion is employed. Such ionomers are well known in the art.

    [0041] Any of the above-mentioned oxygen scavengers and transition metal catalyst can be further combined with one or more polymeric diluents, such as thermoplastic polymers, which are typically used to form film layers in plastic packaging articles. In the manufacture of certain packaging articles well known thermosets can also be used as the polymeric diluent.

    [0042] Further additives can also be included in the composition to impart properties desired for the particular article being manufactured. Such additives include, but are not necessarily limited to, fillers, pigments, dyestuffs, antioxidants, stabilizers, processing aids, plasticizers, fire retardants,etc.

    [0043] The mixing of the components listed above can be accomplished by melt blending at a temperature in the range of 50°C to 300°C. However, alternatives such as the use of a solvent followed by evaporation may also be employed.

    Photoinitiators



    [0044] Some of the materials useful in connection with the invention include:

    1,3,5-tris(4-benzoylphenyl)benzene (BBP3)

    isopropylthioxanthone (ITX)

    bis(2,4,6-trimethylbenzoyl)phenylphosphineoxide (IRGACURE® 819)

    2,4,6-trimethylbenzoyldiphenylphosphine oxide

    ethyl-2,4,6-trimethylbenzoylphenyl phosphinate

    bis(2,6-dimethoxybenzoyl)-2,4,4-trimethylpentyl phosphine oxide

    4,4'-benzoylmethyl diphenyl sulfide (BMS)



    [0045] The amount of photoinitiator can depend on the amount and type of unsaturation present in the polymer, the wavelength and intensity of radiation used; the nature and amount of antioxidants used; and the type of photoinitiator used.

    Examples


    Example 1



    [0046] A representative film structure in accordance with the invention is identified below.
    PETPrint layermetallized polymeric substrateOSLPE
    0.48 mils   0.50 mils 0.75 mils 0.25 mils


    [0047] The total gauge of the film is 1.98 mils, with the thickness of each layer, in mils, as indicated above. The print layer is an optional layer, and in one embodiment is reverse printed onto the PET layer.

    [0048] "PET" herein is poly(ethylene terephthalate), although another suitable polyester or copolyester can be used.

    [0049] The polymer for the metallized layer can be e.g. polypropylene or polyamide, including biaxially oriented polypropylene (BOPP) and polyamide (BON).

    [0050] The OSL is the oxygen scavenging layer, and includes one or more of the oxygen scavengers disclosed herein.

    [0051] "PE" is an ethylene homopolymer, such as low density polyethylene, or an ethylene copolymer such as an ethylene/alpha olefin copolymer.

    [0052] "PS" is polystyrene or styrenic copolymer.

    [0053] The various layers can be adhered together by lamination, such as adhesive lamination, or any other suitable means.

    [0054] The PE layer can comprise, instead of EAO, a propylene polymer or copolymer, such as ethylene/propylene copolymer, or an ethylene copolymer such as ethylene/vinyl acetate copolymer, or ethylene/acrylic or methacrylic acid copolymer, or ionomer resin.

    [0055] Additional materials, including polymeric materials or other organic or inorganic additives, can be added to any or all of the layers of the above structures as needed, and additional film layers can be included either within the film structure, or adhered to an outer layer thereof.

    [0056] Film as described herein can be produced by any suitable method.

    [0057] The PE layer can act as a sealant that will adhere to itself upon the application of heat sealing or alternative sealing techniques, to form a package containing the composition, or can alternatively be adhered by adhesive or other suitable means to another polymer, to paperboard, or to foil such as metal foil.

    [0058] Films useful in connection with the invention can have any suitable number of layers, such as a total of from 2 to 20 layers.

    [0059] In general, the film can have any total thickness desired, and each layer can have any thickness desired, so long as the film provides the desired properties for the particular packaging operation in which the film is used. Typical total thicknesses are from 0.5 mils to 15 mils, such as 1 mil to 12 mils, such as 2 mils to 10 mils, 3 mils to 8 mils, and 4 mils to 6 mils.

    Package Formats



    [0060] A package of the invention can take the form of a pouch or container in which the film structure of the invention surrounds and packages a peroxide composition as described herein. The PE layer can function as a sealant layer, and can be sealed to itself as shown in the "X" regions of the package schematically shown here. The composition can be supported on a suitable substrate or support.

    Example 2



    [0061] 
    PET
    PRINT
    METALLIZED POLYMER
    OSL
    PE
    XXXXXXX PEROXIDE COMPOSITION XXXXXXX
    PE
    OSL
    METALLIZED POLYMER
    PRINT
    PET

    Example 3



    [0062] Alternatively, the peroxide composition can be disposed on a suitable substrate, made from metal, polymer, metallized foil, or any suitable material or combination of materials. The peroxide composition can be covered with a film of the invention, as shown in the following:
    PET
    PRINT
    METALLIZED POLYMER
    OSL
    PE
    PEROXIDE COMPOSITION
    SUBSTRATE


    [0063] Alternatively, the structures of examples 2 and 3 may be surface printed and may further comprise an overprint varnish.

    Example 4



    [0064] In another alternative, the peroxide composition can be disposed inside a tube. The film of the invention can form the tube, or an interior part of the tube, such that
    1. 1. the oxygen scavenger in the film is triggered by the peroxide in the composition; and
    2. 2. oxygen that evolves from the breakdown of the peroxide in the composition can be scavenged by the now triggered oxygen scavenger of the film.

    Further Examples



    [0065] Some types of oxygen scavengers will discolor when incorporated in a film and triggered by hydrogen peroxide. This color change is beneficially masked to avoid producing an aesthetically unattractive package. The additional examples below include a colored layer for this purpose. The color can be provided by any well known coloring agents, which can be premixed into a polymer host that is then extruded as a layer. In Example 7, the coloring agent is included in one or more of the polymers making up the oxygen scavenger layer. In Example 8, the coloring agent is included in the polymer, or one or more of the polymers, making up the PE layer.

    [0066] In some of the examples, a bulk layer is present. This layer can comprise any suitable polymer, or blend thereof, and serves to contribute to the abuse resistance, rigidity, or other physical properties of the film.

    [0067] The narrow double vertical lines in these Examples indicates that the PET is laminated by adhesives or otherwise to a multilayer polymeric film as described. The multilayer film can be produced by e.g. coextrusion, extrusion coating, extrusion lamination, or lamination techniques, or any other suitable technique well known in the art.

    [0068] Any of the example structures below could be printed on the PET surface and may further comprise an overprint varnish.

    Example 5



    [0069] 
    PET Bulk Layer OSL Colored Layer PE

    Example 6



    [0070] 
    PET Colored Layer OSL PE

    Example 7



    [0071] 
    PET Bulk Layer Colored OSL PE

    Example 8



    [0072] 
    PET Bulk Layer OSL Colored PE


    [0073] The PET in these structures may be metallized or PVDC coated to provide barrier to light, oxygen and moisture. If transparent barrier PET is used the one or more of the other layers of the structure can provide the desired opacity to UV and/or visible light.

    Example 9



    [0074] 
    Substrate O2 Barrier Bulk Layer OSL PE


    [0075] The substrate comprises oriented or unoriented PA, PP, PET, or PS.

    [0076] O2 barriers can comprise PVDC, aluminum (or other metals), oxides, nanoclay coatings, EVOH, acrylonitrile containing polymers with these materials being coatings applied to the substrate via melt coating or deposition processes, or as layers applied via coextrusion.

    Example 10



    [0077] 
    BOPP Bulk Layer OSL PE


    [0078] The BOPP layer may be metallized, or PVDC coated to provide barrier to light oxygen and moisture. If transparent barrier BOPP is used the one or more of the other layers of the structure will provide the desired opacity to UV and/or visible light. The structure can be printed on the BOPP surface and may further comprise an overprint varnish.

    Example 11



    [0079] 
    BON Bulk Layer OSL PE


    [0080] The biaxially oriented nylon (BON) layer may be metallized, or PVDC coated to provide barrier to light oxygen and moisture. If transparent barrier BON is used the one or more of the other layers of the structure will provide the desired opacity to UV and/or visible light. The structure can be printed on the BON surface and may further comprise an overprint varnish.

    [0081] The invention is not limited to the illustrations described herein, which are deemed to be merely illustrative, and susceptible of modification of form, size, arrangement of parts and details of operation. For example, an alternative method for providing an opaque layer, i.e. a layer opaque to UV and/or visible light, is to provide a layer comprising an incompatible blend, that is, a blend of resins that results in relatively high haze values; or to provide a polymeric layer that is cavitated; or to provide a foamed polymeric layer.


    Claims

    1. A method of scavenging oxygen from a package containing a product that comprises a peroxide comprising:

    a) packaging the product in a film comprising an oxygen scavenger; wherein the peroxide or an associated enriched oxygen environment triggers the scavenging in the absence of ultraviolet light, heat, visible light, and electron beam radiation.


     
    2. A method according to claim 1 wherein the oxygen scavenger comprises:

    a) an organic oxygen scavenger, and

    b) a transition metal catalyst.


     
    3. A method according to claim 2 wherein the organic oxygen scavenger comprises one or more of the following materials:

    i) ethylenically unsaturated hydrocarbon,

    ii) a polymer having a polymeric backbone, cyclic olefinic pendent group, and linking group linking the olefinic pendent group to the polymeric backbone,

    iii) a copolymer of ethylene and a strained, cyclic alkylene, and

    iv) ethylene/vinyl aralkyl copolymer.


     
    4. A method according to any one of the preceding claims, wherein the product comprises peroxide in an amount from 0.5% to 25% by weight of the product.
     
    5. A method according to any one of the preceding claims, wherein the average oxygen scavenging rate of the film is at least 25 cc/m2/day for at least two days after the oxygen scavenging property of the film is triggered
     
    6. A method according to any one of the preceding claims, wherein the film comprises multiple layers.
     
    7. A method according to any one of the preceding claims wherein at least one layer of the film is cross-linked.
     
    8. A method according to any one of the preceding claims wherein the film is solid state oriented.
     
    9. A method according to any one of the preceding claims wherein the film is heat shrinkable.
     
    10. A method according to any one of the preceding claims wherein the peroxide comprises hydrogen peroxide.
     


    Ansprüche

    1. Verfahren zum Abfangen von Sauerstoff aus einer Packung, die ein ein Peroxyd umfassendes Produkt enthält, bei dem

    a) das Produkt in einer ein Sauerstoffabfangmittel umfassenden Folie verpackt wird, wobei das Peroxyd oder eine assoziierte Sauerstoff angereicherte Umgebung das Abfangen in Abwesenheit von ultraviolettem Licht, Wärme, sichtbarem Licht und Elektronenstrahlbestrahlung auslöst.


     
    2. Verfahren nach Anspruch 1, bei dem das Sauerstoffabfangmittel

    a) ein organisches Sauerstoffabfangmittel und

    b) einen Übergangsmetallkatalysator umfasst.


     
    3. Verfahren nach Anspruch 2, bei dem das organische Sauerstoffabfangmittel ein oder mehrere der folgenden Materialien umfasst:

    i) ethylenisch ungesättigten Kohlenwasserstoff,

    ii) ein Polymer mit einem polymeren Gerüst, cyclischer olefinischer Seitengruppe und einer Verbindungsgruppe, die die olefinische Seitengruppe mit dem polymeren Gerüst verbindet,

    iii) ein Copolymer aus Ethylen und einem gespannten cyclischen Alkylen und

    iv) Ethylen/Vinylaralkyl-Copolymer.


     
    4. Verfahren nach einem der vorangehenden Ansprüche, bei dem das Produkt ein Peroxyd in einer Menge von 0,5 bis 25 Gew.% des Produkts umfasst.
     
    5. Verfahren nach einem der vorangehenden Ansprüche, bei dem die Sauerstoffabfangrate der Folie mindestens 25 cm3/m2/Tag für mindestens zwei Tage beträgt, nachdem die Sauerstoffabfangeigenschaft der Folie ausgelöst worden ist.
     
    6. Verfahren nach einem der vorangehenden Ansprüche, bei dem die Folie mehrere Schichten umfasst.
     
    7. Verfahren nach einem der vorangehenden Ansprüche, bei dem mindestens eine Schicht der Folie vernetzt ist.
     
    8. Verfahren nach einem der vorangehenden Ansprüche, bei dem die Folie im festen Zustand orientiert worden ist.
     
    9. Verfahren nach einem der vorangehenden Ansprüche, bei dem die Folie wärmeschrumpfbar ist.
     
    10. Verfahren nach einem der vorangehenden Ansprüche, bei dem das Peroxyd Wasserstoffperoxyd umfasst.
     


    Revendications

    1. Procédé de piégeage d'oxygène dans un emballage contenant un produit qui comprend un peroxyde, lequel procédé comporte :

    a) le fait d'emballer le produit dans un film comprenant un agent de piégeage d'oxygène ;

    et dans lequel procédé le peroxyde ou un milieu associé enrichi en oxygène amorce le piégeage en l'absence de rayonnement ultraviolet, de chaleur, de lumière visible et de rayonnement électronique.
     
    2. Procédé conforme à la revendication 1, dans lequel l'agent de piégeage d'oxygène comprend :

    a) un agent organique absorbeur d'oxygène,

    b) et un catalyseur à base de métal de transition.


     
    3. Procédé conforme à la revendication 2, dans lequel l'agent organique absorbeur d'oxygène comprend une ou plusieurs des substances suivantes :

    i) un hydrocarbure à insaturation éthylénique,

    ii) un polymère comportant un squelette polymère, des groupes latéraux dérivés de cyclooléfine, et des groupes de raccord qui relient ces groupes latéraux dérivés d'oléfine au squelette polymère ;

    iii) un copolymère d'éthylène et d'un alcène cyclique à contrainte ;

    iv) un copolymère d'éthylène et de vinyl-aryl-alcane.


     
    4. Procédé conforme à l'une des revendications précédentes, dans lequel le produit comprend un peroxyde en une quantité représentant de 0,5 à 25 % de son poids.
     
    5. Procédé conforme à l'une des revendications précédentes, dans lequel la vitesse moyenne à laquelle le film piège l'oxygène vaut au moins 25 cm3/m2.j pendant au moins deux jours après l'amorçage du piégeage d'oxygène par le film.
     
    6. Procédé conforme à l'une des revendications précédentes, dans lequel le film comporte plusieurs couches.
     
    7. Procédé conforme à l'une des revendications précédentes, dans lequel au moins une couche du film est réticulée.
     
    8. Procédé conforme à l'une des revendications précédentes, dans lequel le film a été orienté à l'état solide.
     
    9. Procédé conforme à l'une des revendications précédentes, dans lequel le film est thermo-rétractable.
     
    10. Procédé conforme à l'une des revendications précédentes, dans lequel le peroxyde comprend du peroxyde d'hydrogène.
     






    Cited references

    REFERENCES CITED IN THE DESCRIPTION



    This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

    Patent documents cited in the description