(19)
(11)EP 1 910 239 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
11.09.2019 Bulletin 2019/37

(21)Application number: 06788485.8

(22)Date of filing:  25.07.2006
(51)International Patent Classification (IPC): 
C03C 3/087(2006.01)
C03C 4/08(2006.01)
C03C 4/02(2006.01)
(86)International application number:
PCT/US2006/028916
(87)International publication number:
WO 2007/016126 (08.02.2007 Gazette  2007/06)

(54)

GREEN GLASS COMPOSITION

GRÜNGLASZUSAMMENSETZUNG

COMPOSITION DE VERRE VERT


(84)Designated Contracting States:
BE DE ES FR GB IT

(30)Priority: 29.07.2005 US 192497

(43)Date of publication of application:
16.04.2008 Bulletin 2008/16

(73)Proprietor: Vitro, S.A.B. de C.V.
Nuevo León, México 66265 (MX)

(72)Inventor:
  • SHELESTAK, Larry J.
    Bairdford, Pennsylvania 15006 (US)

(74)Representative: f & e patent 
Fleischer, Engels & Partner mbB, Patentanwälte Braunsberger Feld 29
51429 Bergisch Gladbach
51429 Bergisch Gladbach (DE)


(56)References cited: : 
EP-A- 1 681 277
EP-A1- 0 639 537
WO-A-00/29344
JP-A- 9 208 254
EP-A1- 0 297 404
EP-A1- 0 979 804
GB-A- 2 393 717
US-A- 5 830 812
  
      
    Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


    Description

    FIELD OF THE INVENTION



    [0001] The present invention relates to glass compositions, particularly, green glass compositions having improved ultraviolet ("UV") performance.

    BACKGROUND OF THE INVENTION



    [0002] Glass substrates are used in a variety of applications such as automotive applications, architectural applications, aerospace applications, etc. Depending on the end use of the glass substrate, it will be desirable for the glass substrate to exhibit certain (a) aesthetic properties, such as, but not limited to, color and (b) solar control properties, such as, but not limited to, total solar energy transmittance ("TSET"), infrared transmittance and ultraviolet transmittance.

    [0003] For example, in automotive applications, glass substrates are used as automotive vision panels (i.e., front windows, sidelights, etc.). Automotive vision panels need to exhibit a desirable color. At the present time, desirable colors for automotive vision panels include blue, green and gray. Further, if the automotive vision panel is used as a front windshield, it will have to exhibit a visible light transmittance ("Lta") of equal to or greater than 70% in the United States. The Lta requirement for front windshields in countries other than the United States may be different.

    [0004] The aesthetic properties and solar control properties of a glass substrate can be modified in several of different ways. The first way involves depositing a coating on the surface of a glass substrate. The second way involves changing the chemical composition (i.e., the type of materials that make up the glass composition and/or the weight percentages of the various materials in the glass composition) that make up the glass substrate. Oftentimes, colorants and/or other materials capable of modifying the solar properties of the glass composition are added to a well known base glass composition, such as a soda-lime-silica base glass composition, to provide a glass substrate capable of exhibiting unique performance properties. Although the effect of one colorant or one material capable of modifying the solar properties of the glass composition may be known (for example, it is known that adding FeO to a base glass composition increases the infrared (IR) absorption of the glass composition), it is the essence of invention to use various colorants and/or materials capable of modifying the solar properties of the glass composition, each colorant or material capable of producing a unique effect individually, to achieve a combination of properties collectively.

    [0005] According to the present invention, specific materials capable of modifying the solar properties of a glass composition are added in specific amounts to a soda-lime-silica base glass composition to provide glass substrates capable of exhibiting the desired aesthetic and solar control properties. The combination of aesthetic and solar control properties provided by glass substrates formed from the glass composition of the present invention are as follows at a reference thickness of 0.189 inches (4.8 mm):

    a green color characterized by a dominant wavelength ranging from 495 to 535 nanometers and an excitation purity of greater than 1 percent;

    an Lta equal to or greater than 60 percent;

    a total solar energy transmittance (TSET) of less than or equal to 48 percent; and

    a total solar ultraviolet transmittance (SAE UV) of less than or equal to 55 percent.



    [0006] WO 00/29344 discloses a green glass composition that contains at least 14.5 wt.-% Na2O, at least 10.5 wt.-% CaO, and at least 0.5 wt.-% total iron, wherein the ferrous value is at least 30%. The glass composition is substantially magnesium-free and does not contain molybdenum oxide.

    [0007] US patent No. 5,830,812 relates to another green colored glass which contains in addition to a soda-lime-silica glass base composition iron, cerium, chromium and optionally titanium as infrared and ultraviolet radiation absorbing materials and colorants. Also, these glass compositions do not contain molybdenum oxide.

    [0008] EP 0 639 537 A1 relates to the use of at least 0.010 wt.-% of a material selected from the group consisting essentially of molybdenum, arsenic, antimony, bismuth, copper, silver, potassium dichromate and iron chromite to a soda-lime-silica float glass for reducing the occurrence of nickel sulfide stone defects.

    SUMMARY OF THE INVENTION



    [0009] The present invention relates to a glass composition comprising a base glass composition comprising: SiO2 from 65 to 75 weight percent, Na2O from 10 to 20 weight percent, CaO from 5 to 15 weight percent, MgO from 0 to 5 weight percent, Al2O3 from 0 to 5 weight percent, K2O from 0 to 5 weight percent, and BaO from 0 to 1 weight percent, and a colorant and property modifying portion comprising total iron ranging from 0.50 to 0.58 weight percent; MoO3 from 10 to 100 ppm and TiO2 ranging from 0.2 to 0.5 weight percent, wherein the redox ratio ranges from 0.33 to 0.45 and the weight percents are based on the total weight of the composition.

    [0010] The present invention also relates to a glass sheet made from such glass composition according to the present invention. The glass sheet may exhibit one or more of the following performance properties at a thickness of 0.189 inches (4.8 mm): an Lta of at least 70%,; a TSET of up to 48%; a SAE UV of up to 42%; a DW ranging from 495 to 500 nm; and a Pe of at least 1 percent.

    [0011] The present invention is also drawn to a laminated glass article comprising such a glass sheet made from a glass composition of the present invention, wherein the glass sheet exhibits one or more of the following performance properties at a thickness of 0.189 inches (4.8 mm): an Lta of at least 60 percent; a TSET of up to 47 percent; an SAE UV transmittance of up to 55 percent; a DW ranging from 495 to 535 nm; and a Pe of at least 1 percent.

    DESCRIPTION OF THE INVENTION



    [0012] At the very least, and not as an attempt to limit the application of the doctrine of equivalents to the scope of the claims, each numerical value should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques.

    [0013] The glass composition of the present invention comprises a base glass portion and colorants and materials capable of modifying the solar control properties of the glass. Both colorants and materials capable of modifying the solar control properties of the glass are referred to herein as "colorants and property modifying materials". According to the present invention, the base glass portion includes the components in the amounts shown in Table 1 below.
    Table 1. Base Glass Portion
    ComponentConcentration in the Glass Composition [Weight Percent based on the Total Weight of the Glass Composition]
    SiO2 65-75%
    Na2O 10-20%
    CaO 5-15%
    MgO 0-5%
    Al2O3 0-5%
    K2O 0-5%
    BaO 0-1%


    [0014] The described base glass portion is referred in the art as a "soda-lime-silica" glass composition.

    [0015] According to the present invention, various colorants and materials capable of modifying the solar performance properties of the glass are added to the base glass composition. The colorants and property modifying materials included in the glass composition of the invention include: iron oxide (Fe2O3 and FeO) and titanium oxide ("TiO2").

    [0016] According to the present invention, iron can be present in the glass composition as both ferric oxide (Fe2O3) and ferrous oxide (FeO). As is well known in the art, Fe2O3 is a strong absorber of ultraviolet radiation and is a yellow colorant. As is well known in the art, FeO is a strong absorber of infrared radiation and is a blue colorant.

    [0017] The "total iron" present in the glass composition of the invention is expressed in terms of the weight percentage of "Fe2O3" present in the glass composition as is standard practice in the industry. This does not imply that all of the iron present in the glass composition is in the form of Fe2O3. According to the present invention, the total iron in the glass composition of the present invention ranges from 0.50 to 0.58 weight percent based on the total weight of the glass composition.

    [0018] The amount of iron present in the ferrous state in the glass composition of the present invention is expressed in terms of the weight percentage of "FeO" present in the glass composition as is standard practice in the industry. Although the amount of iron in the ferrous state is expressed as FeO, the entire amount in the ferrous state may not actually be present in the glass as FeO.

    [0019] The glass composition of the present invention has a certain "redox ratio". As used herein, the "redox ratio" is the amount of iron in the ferrous state (expressed as "FeO") divided by the amount of total iron (expressed as "Fe2O3"). Glass compositions according to the present invention have a redox ratio ranging from 0.33 to 0.45, for example, from 0.36 to 0.42, or from 0.37 to 0.40.

    [0020] The glass composition of the present invention contains TiO2 in an amount ranging from 0.2 weight percent to 0.5 weight percent, where the weight percent is based on the total weight of the glass composition. TiO2 is known in the art as an absorber of ultraviolet radiation.

    [0021] The glass composition of the invention contains molybdenum oxide (MoO3) to inhibit the formation of nickel-sulfide stones which can be present in glass and degrade the quality of the glass. MoO3 is added to the composition of the invention in an amount ranging from 10 to 100 PPM.

    [0022] The glass composition of the present invention can be produced by conventional glass making processes. For example, the glass composition can be formed from batch materials via crucible melts, a sheet drawing process, a float glass process, etc. Typically, well known batch materials are mixed with other components to form the starting materials which are processed into the glass compositions of the present invention. In a non-limiting embodiment, the glass composition of the present invention is formed via a float glass process as is well known in the art.

    [0023] As a result of the raw materials and/or equipment used to produce the glass composition of the present invention, certain impurities, for example, SrO and ZrO2, can be present in the final glass composition. Such materials are present in the glass composition in minor amounts and are referred to herein as "tramp materials". Tramp materials do not contribute to the performance properties of the glass.

    [0024] In a non-limiting embodiment of the invention, the described glass composition is formed into a glass substrate and/or laminated glass article as is well known in the art. Glass substrates having various thicknesses can be formed. For example, glass substrates having a thickness of up to 24 mm can be formed.

    [0025] In a non-limiting embodiment, the present invention is a laminated article made up of at least one glass substrate according to the present invention wherein such glass substrate exhibits one or more of the following performance properties at a thickness of 0.189 inches (4.8 mm):

    a green color characterized by a dominant wavelength ranging from 495 to 535 nanometers, for example, from 500 to 530 nanometers, or from 505 to 525 nanometers and an excitation purity of greater than or equal to 1 percent, for example, greater than or equal to 2 percent, or greater than or equal to 3 percent;

    an Lta of equal to or greater than 60 percent, for example, equal to or greater than 65 percent, or equal to or greater than 70 percent;

    a TSET less than or equal to 45 percent, or equal to or less than 43 percent; and

    a total solar ultraviolet transmittance (expressed in terms of "SAE UV ") of less than or equal to 55 percent, for example, equal to or less than 52 percent, or equal to or less than 50 percent.



    [0026] According to the present invention, the abovementioned performance properties are measured as described below:
    The visible light transmittance (Lta) represents a computed value based on measured data using C.I.E. 1931 standard illuminant "A" over the wavelength range of 380 to 770 nanometers at 10 nanometer intervals.

    [0027] The total solar ultraviolet transmittance (SAE UV) represents a computed value based on measured data over the wavelength range of 300 to 400 nanometers at 5 nanometer intervals using the SAE 1796 standard.

    [0028] The total solar energy transmittance (TSET) represents a computed value based on measured transmittances from 300 to 2500 nanometers at 50 nanometer intervals.

    [0029] Color is described in terms of dominant wavelength (DW) and the excitation purity (Pe) represent computed values based on measured data using a C.I.E. 1931 standard illuminant "C" with a 2° observer.

    [0030] All solar transmittance data is calculated using air mass solar data according to the ASTM am1 .5g (E892T. 1). All of the transmittance values are integrated over the wavelength range using the Trapezoidal Rule, as is well known in the art.

    [0031] In a non-limiting embodiment of the invention, the glass substrate is used as a glass vision panel. In a further non-limiting embodiment, the glass vision panel is an automotive front windshield that exhibits an Lta equal to or greater than 70%.

    EXAMPLES



    [0032] Disclosed herein are the following non-limiting examples. The Examples were made in the following manner.

    [0033] For Examples 1-2, the batch materials were weighed out, mixed and added into a crucible. The batch materials are shown in Table 2 below. All material weights are in grams. The batch materials were melted in a 20.3 cm (8 inch) platinum crucible in an electric resistance furnace set to a temperature of 1 ,343°C (2,450°F) in an air atmosphere for 30 minutes. The furnace temperature was raised to 1,371 °C (2,500°F), and the batch materials were heated for 30 minutes. The furnace temperature was raised to 1,399°C (2,550°F), and the batch materials were heated for 30 minutes. The furnace temperature was raised to 1,454°C (2,650°F), and the batch materials were heated for 30 minutes. The glass melt was then poured into water at room temperature (referred to as "glass fritting" in the art) to produce a glass frit. The glass frit was dried in an annealing oven set to a temperature of 593°C (1,100°F) for 20 minutes. The glass frit was placed back into a crucible, and the crucible was placed in an oven set to a temperature of 1,454°C (2,650°F). The glass frit was then heated in the oven for one hour.

    [0034] The contents of the crucible were fritted again as described above. The glass frit was then placed in a crucible, and the crucible was placed in an oven set to a temperature of 1,454°C (2,650°F). The glass frit was then heated in the oven for two hours. The glass melt was then cast on a metal table. The resulting glass sheet was placed into an annealing lehr set to a temperature of 593°C (1,100°F) for one hour. The power to the lehr was shut off, and the glass sheet was allowed to stay in the lehr for sixteen hours as it cooled down. Examples made from the glass melts were next ground and polished.

    [0035] For Examples 3-10, the batch materials were weighed out, mixed and added into a crucible. Half of the batch materials were melted in a 20.3 cm (4 inch) platinum crucible in an electric resistance furnace set to a temperature of 1,343°C (2,450°F) in an air atmosphere for 30 minutes. Then, the other half of the batch materials was added to the crucible. The furnace temperature was raised to 1,371°C (2,500°F), and the batch materials were heated for 30 minutes. The furnace temperature was raised to 1,399°C (2,550°F), and the batch materials were heated for 30 minutes. The furnace temperature was raised to 1,454°C (2,650°F), and the batch materials were heated for 30 minutes. The glass melt was fritted to produce a glass frit in a manner as discussed earlier. The glass frit was dried in an annealing oven set to a temperature of 593°C (1,100°F) for 20 minutes. The glass frit was placed back into a crucible, and the crucible was placed in an oven set to a temperature of 1,454°C (2,650°F). The glass frit was then heated the oven for one hour. The contents of the crucible were fritted again as described above. The glass frit was placed in a crucible, and the crucible was placed in an oven set to a temperature of 1,454°C (2,650°F). The glass frit was then heated in the oven for two hours. The glass melt was cast on a metal table. The resulting glass sheet was placed into an annealing lehr set to a temperature of 593°C (1,100°F) for one hour. The power to the lehr was shut off, and the glass sheet was allowed to stay in the lehr for sixteen hours as it cooled down. Examples made from the glass melts were ground and polished.
    Table 2. Glass Batch Materials
     Ex. 1Ex. 2Ex. 3Ex. 4Ex. 5Ex. 6Ex. 7Ex. 8Ex. 9Ex. 10
    Sand [g] 1000 1000 500 500 500 500 500 500 500 500
    Soda Ash [g] 326 326 163 163 163 163 163 163 163 163
    Limestone [g] 128 128 64 64 64 64 64 64 64 64
    Dolomite [g] 204 204 102 102 102 102 102 102 102 102
    Salt cake [g] 10 10 5 5 5 3.5 2.5 2.5 2.5 2.5
    Rouge [g] 7.5 7.5 3.75 3.75 3.75 3.75 4.05 4.05 4.15 4.15
    TiO2 [g] 7.0 7.0 3.5 3.5 3.5 3.5 4.0 4.0 4.0 4.0
    Coal [g] 1.0 1.1 0.85 0.6375 0.6375 - 0.45 0.50 0.50 0.55
    Si [g] - - - 0.2338 0.2975 1.30 - - - -


    [0036] Compositional information for the exemplary glass compositions made according to Examples 1 to 10 is shown below in Table 3. The exemplary compositions did contain the following tramp materials which are not included in the table: SO3, SrO, ZrO2, Cl and BaO.
    Table 3. Glass Compositions of Examples 1 to 10
    ComponentEx. 1Ex. 2Ex. 3Ex. 4Ex. 5Ex. 6Ex. 7Ex. 8Ex. 9*Ex.10*
    SiO2 71.73 71.64 73.31 73.31 73.19 73.27 73.45 73.16 73.38 73.05
    Na2O 13.75 13.79 13.08 13.12 13.18 13.09 12.91 13.04 12.92 13.13
    K2O 0.039 0.028 0.028 0.028 0.027 0.027 0.035 0.036 0.038 0.039
    CaO 9.83 9.89 9.25 9.23 9.28 9.26 9.17 9.29 9.23 9.31
    MgO 3.34 3.38 3.14 3.11 3.14 3.13 3.13 3.14 3.12 3.13
    Al2O3 0.09 0.09 0.11 0.10 0.10 0.10 0.13 0.13 0.13 0.13
    Fe2O3 0.538 0.534 0.520 0.521 0.526 0.526 0.560 0.573 0.589 0.594
    TiO2 0.444 0.439 0.430 0.432 0.438 0.436 0.490 0.499 0.494 0.500
    Redox Ratio 0.372 0.388 0.398 0.358 0.390 0.343 0.386 0.375 0.406 0.402
    *: Comparative Example


    [0037] Table 4 shows various performance properties of glass substrates having a thickness of 4.8 mm (0.189 inches) formed from glass compositions of Examples 1 to 10. The spectral properties of the Examples were measured using a Perkin Elmer Lambda 9 spectrophotometer.
    Table 4. Performance Properties of Substrates made from Glass Compositions of Examples 1 to 10
    Performance PropertyEx. 1Ex. 2Ex. 3Ex. 4Ex. 5Ex. 6Ex. 7Ex. 8Ex. 9*Ex. 10*
    Lta [%] 72.63 72.23 72.78 73.96 72.10 73.81 71.41 71.52 69.68 69.52
    TSET [%] 44.72 44.04 44.19 46.34 44.01 46.75 42.59 42.72 40.22 40.13
    SAE UV [%] 38.01 38.26 40.82 40.61 40.28 39.77 36.54 36.45 35.54 35.21
    DW [nm] 498.29 497.35 496.61 497.89 496.87 498.90 499.51 499.87 499.06 499.29
    Pe [%] 4.02 4.36 4.49 3.86 4.40 3.55 4.08 3.97 4.52 4.47
    *: Comparative Example


    [0038] Table 5 shows various performance properties of laminated glass articles formed from the glass compositions according to Examples 1 to 10. A computer model was used to calculate the spectral properties and color for laminated glass articles based on the measured data for a single substrate. The modeled laminated article contained two pieces of glass, each having the same composition and thickness as specified in Table 5, and a 0.76 mm (0.030 inches) thick, ultraviolet radiation absorbing, vinyl interlayer commercially available from E. I. du Pont de Nemours and Company (Wilmington, DEL.) as BE1700.
    Table 5. Performance Properties of Laminated Articles including a Substrate made up from a Glass Composition according to Examples 1 to 10
    Performance PropertyEx. 1Ex. 2Ex. 3Ex. 4Ex. 5Ex. 6Ex. 7Ex. 8Ex. 9*Ex. 10*
    Thickness of each glass substrate [mm] 2.29 2.24 2.24 2.24 2.24 2.51 2.11 2.11 1.93 1.93
    Laminate Thickness [mm] 5.33 5.23 5.23 5.64 5.23 5.79 4.98 4.98 4.62 4.62
    Lta [%] 72.49 72.47 72.99 72.78 72.35 72.14 72.63 72.74 72.51 72.38
    TSET [%] 41.99 41.84 41.88 41.97 41.74 41.70 41.87 42.01 41.62 41.57
    SAE UV [%] 2.70 2.72 2.79 2.74 2.76 2.69 2.05 2.05 2.06 2.06
    DW [nm] 501.90 500.60 499.67 501.38 500.03 502.76 503.53 504.10 502.93 503.23
    Pe [%] 3.38 3.59 3.69 3.45 3.61 3.26 3.17 3.07 3.22 3.19
    *: Comparative Example

    CONCLUSIONS



    [0039] Based on Table 4, non-limiting examples of the glass composition of the present invention can be used to form glass substrates having a thickness of 4.8 mm (0.189 inches) that exhibit one or more of the following performance properties: an Lta of greater than 70%, for example, from 72 to 75%; a TSET of less than 48%, for example, from 44 to 47%; a SAE UV of less than 42%, for example, from 37 to 41%; a DW ranging from 495 to 500 nm; and a Pe of greater than 3%, for example, from 3.3 to 4.5%.

    [0040] Based on Table 5, non-limiting examples of the glass composition of the present invention can be used to form laminated glass articles that exhibit one or more of the following performance properties: an Lta of greater than 70%, for example, from 72 to 75%; a TSET of less than 44%, for example, from 40 to 43%; a SAE UV of less than 5%, for example, from 2 to 3% (a significant amount of the exhibited UV absorption in the laminate examples is attributable to the interlayer); a DW ranging from 497 to 505 nm; and a Pe of greater than 1%, for example, from 3 to 5%.


    Claims

    1. A glass composition comprising:

    SiO2 65 to 75 weight percent,

    Na2O 10 to 20 weight percent,

    CaO 5 to 15 weight percent,

    MgO 0 to 5 weight percent,

    Al2O3 0 to 5 weight percent,

    K2O 0 to 5 weight percent, and

    BaO 0 to 1 weight percent,

    and a colorant and property modifying portion comprising total iron ranging from 0.50 to 0.58 weight percent;

    MoO3 ranging from 10 to 100 ppm; and

    TiO2 ranging from 0.2 to 0.5 weight percent,

    wherein the redox ratio ranges from 0.33 to 0.45 and the weight percent are based on the total weight of the composition.


     
    2. A glass sheet made from the composition according to claim 1.
     
    3. The glass sheet according to claim 2 that exhibits one or more of the following performance properties at a thickness of 0.189 inches (4.8 mm): an Lta of at least 60%, preferably at least 70%; a TSET of up to 48%, preferably up to 45%; a SAE UV of up to 55%, preferably up to 52%; a DW ranging from 495 to 535 nm, preferably from 500 to 530 nm; and a Pe of at least 1%, preferably at least 2%.
     
    4. A laminated article made from at least one glass sheet according to claim 2.
     
    5. The glass sheet according to claim 3, wherein the glass sheet exhibits one or more of the following performance properties at a thickness of 0.189 inches (4.8 mm): an Lta of at least 70%; a TSET of up to 48%; a SAE UV of up to 42%; a DW ranging from 495 to 500 nm; and a Pe of at least 1 percent.
     
    6. A laminated glass article comprising a glass sheet according to claim 2, wherein the glass sheet exhibits one or more of the following performance properties at a thickness of 0.189 inches (4.8mm): an Lta of at least 60 percent; a TSET of up to 47 percent; an SAE UV transmittance of up to 55 percent; a dominant wavelength ranging from 495 to 535 nm; and a Pe of at least 1 percent.
     


    Ansprüche

    1. Eine Glaszusammensetzung umfassend:

    SiO2 65 bis 75 Gew.-%,

    Na2O 10 bis 20 Gew.-%,

    CaO 5 bis 15 Gew.-%,

    MgO 0 bis 5 Gew.-%,

    Al2O3 0 bis 5 Gew.-%,

    K2O 0 bis 5 Gew.-%, und

    BaO 0 bis 1 Gew.-%,

    und einen farbgebenden und eigenschaftsmodifizierenden Teil umfassend: Gesamteisen im Bereich von 0,50 bis 0,58 Gew.-%,

    MoO3 im Bereich von 10 bis 100 ppm; und

    TiO2 im Bereich von 0,2 bis 0,5 Gew.-%,

    wobei das Redox-Verhältnis im Bereich von 0,33 bis 0,45 liegt und die Gewichtsprozente sich auf das Gesamtgewicht der Zusammensetzung beziehen.


     
    2. Eine Glasscheibe, hergestellt aus der Zusammensetzung gemäß Anspruch 1.
     
    3. Die Glasscheibe gemäß Anspruch 2, welche eine oder mehrere der folgenden Eigenschaften bei einer Dicke von 0,189 Zoll (4,8 mm) aufweist: eine Lta von wenigstens 60%, vorzugsweise wenigstens 70%, eine TSET von bis zu 48%, vorzugsweise bis zu 45%; eine SAE UV von bis zu 55%, vorzugsweise bis zu 52%; eine DW im Bereich von 495 bis 535 nm, vorzugsweise von 500 bis 530 nm; und eine Pe von wenigstens 1%, vorzugsweise wenigstens 2%.
     
    4. Ein laminierter Gegenstand, hergestellt aus wenigstens einer Glasscheibe gemäß Anspruch 2.
     
    5. Die Glasscheibe gemäß Anspruch 3, wobei die Glasscheibe eine oder mehrere der folgenden Eigenschaften bei einer Dicke von 0,189 Zoll (4,8 mm) aufweist: eine Lta von wenigstens 70%; eine TSET von bis zu 48%; eine SAE UV von bis zu 42%; eine DW im Bereich von 495 bis 500 nm und eine Pe von wenigstens 1%.
     
    6. Ein laminierter Glasgegenstand umfassend eine Glasscheibe gemäß Anspruch 2, wobei die Glasscheibe eine oder mehrere der folgenden Eigenschaften bei einer Dicke von 0,189 Zoll (4,8 mm) aufweist: eine Lta von wenigstens 60%; eine TSET von bis zu 47%; einen SAE UV Transmissionsgrad von bis zu 55%; eine dominante Wellenlänge im Bereich von 495 bis 535 nm und eine Pe von wenigstens 1%.
     


    Revendications

    1. Composition de verre comprenant :

    SiO2 65 à 75 pour cent en poids,

    Na2O 10 à 20 pour cent en poids,

    CaO 5 à 15 pour cent en poids,

    MgO 0 à 5 pour cent en poids,

    Al2O3 0 à 5 pour cent en poids,

    K2O 0 à 5 pour cent en poids, et

    BaO 0 à 1 pour cent en poids,

    et un colorant et une partie modificatrice de propriété comprenant du fer total se situant dans la plage de 0,50 à 0,58 pour cent en poids ;

    du MoO3 se situant dans la plage de 10 à 100 ppm ; et

    du TiO2 se situant dans la plage de 0,2 à 0,5 pour cent en poids,

    dans laquelle le rapport redox se situe dans la plage de 0,33 à 0,45 et les pourcentages en poids sont basés sur le poids total de la composition.


     
    2. Feuille de verre produite à partir de la composition selon la revendication 1.
     
    3. Feuille de verre selon la revendication 2, qui présente une ou plusieurs des caractéristiques suivantes en une épaisseur de 0,189 pouce (4,8 mm): une transmittance Lta d'au moins 60%, de préférence d'au moins 70% ; une transmittance TSET de jusqu'à 48%, de préférence de jusqu'à 45%; une transmittance SAE UV de jusqu'à 55%, de préférence de jusqu'à 52%; une longueur d'onde dominante DW se situant dans la plage de 495 à 535 nm, de préférence de 500 à 530 nm; et une pureté d'excitation d'au moins 1%, de préférence d'au moins 2%.
     
    4. Article feuilleté produit à partir d'au moins une feuille de verre selon la revendication 2.
     
    5. Feuille de verre selon la revendication 3, où la feuille de verre présente une ou plusieurs des caractéristiques suivantes en une épaisseur de 0,189 pouce (4,8 mm) : une transmittance Lta d'au moins 70%; une transmittance TSET de jusqu'à 48%; une transmittance SAE UV de jusqu'à 42%; une longueur d'onde dominante DW se situant dans la plage de 495 à 500 nm ; et une pureté d'excitation Pe d'au moins 1 pour cent.
     
    6. Article en verre feuilleté comprenant une feuille de verre selon la revendication 2, dans lequel la feuille de verre présente une ou plusieurs des caractéristiques suivantes en une épaisseur de 0,189 pouce (4,8 mm): une transmittance Lta d'au moins 60 pour cent; une transmittance TSET de jusqu'à 47 pour cent ; une transmittance SAE UV de jusqu'à 55% ; une longueur d'onde dominante se situant dans la plage de 495 à 535 nm ; et une pureté d'excitation Pe d'au moins 1 pour cent.
     






    Cited references

    REFERENCES CITED IN THE DESCRIPTION



    This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

    Patent documents cited in the description