(54)

POROUS RESIN BEAD AND METHOD FOR PRODUCING NUCLEIC ACID USING THE SAME

PORÖSE HARZKÜGELCHEN UND VERFAHREN ZUR HERSTELLUNG VON NUKLEINSÄURE DAMIT

BILLES RÉSINE POREUSES ET PROCÉDÉ DE PRODUCTION D'ACIDE NUCLÉIQUE L'UTILISANT


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO SE SI SK SM TR

(30)Priority: 17.09.2009 JP 2009216214

(43)Date of publication of application:
23.03.2011 Bulletin 2011/12

(73)Proprietor: Nitto Denko Corporation
Ibaraki-shi, Osaka (JP)

(72)Inventors:
  • Mori, Kenjiro
    Ibaraki-shi Osaka (JP)
  • Konishi, Tatsuya
    Ibaraki-shi Osaka (JP)
  • Maeta, Eri
    Ibaraki-shi Osaka (JP)

(74)Representative: Grünecker Patent- und Rechtsanwälte PartG mbB 
Leopoldstraße 4
80802 München
80802 München (DE)


(56)References cited: : 
JP-A- 2006 342 245
US-A1- 2008 039 604
JP-A- 2008 074 979
  
      
    Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


    Description


    [0001] This invention relates to a porous resin bead and a method for producing a nucleaic acid. More illustratively, it relates to a porous resin bead which contains a first aromatic monovinyl compound-divinyl compound-(meth)acrylonitrile-second aromatic monovinyl compound copolymer. This porous resin bead is particularly useful in synthesizing nucleic acid.

    BACKGROUND OF THE INVENTION



    [0002] A solid-phase synthesis method which uses the phosphoramidite method is broadly used in the chemical synthesis of nucleic acids such as a DNA oligonucleotide and RNA. In this method, for example, a nucleoside which becomes the 3'-terminal of the nucleic acid to be synthesized is firstly supported in advance on a solid-phase synthesis support via a cleavable linker such as succinyl group, and this support is put into a reaction column and set on an automatic nucleic acid synthesizer. Thereafter, synthesizing reagents are fed into the reaction column, for example, in the following manner in accordance with the synthesizing program of the automatic nucleic acid synthesizer. (1) Deprotection of nucleoside 5'-OH group by a trichloroacetic acid/dichloromethane solution, dichloroacetic acid/toluene solution or the like, (2) coupling reaction of amidite with the 5'-OH group by a nucleoside phosphoramidite (nucleic acid monomer)/acetonitrile solution and an activator (tetrazole or the like)/acetonitrile solution, (3) capping of the unreacted 5'-OH group by acetic anhydride/pyridine/methyl imidazole/THF or the like, and (4) oxidation of phosphite by iodine/water/pyridine or the like.
    By repeating this synthesis cycle, a nucleic acid having the intended sequence is synthesized. The finally synthesized nucleic acid cut out from the solid-phase synthesis support by hydrolyzing the cleavable linker with ammonia, methylamine or the like (cf. Non-patent Reference 1).

    [0003] As the solid-phase synthesis support to be used in the synthesis of nucleic acid, CPG (Controlled Pore Glass), silica gel and the like inorganic particles have so far been used, but in recent years, resin beads which can increase quantity of nucleic acid synthesized per weight of solid-phase synthesis support have been started to be used in order to synthesize at a moderate price and in a large quantity. As such resin beads, a highly-crosslinked and non-swelling porous polystyrene bead (cf. Patent Reference 1), a low-crosslinked and swelling porous polystyrene bead (cf. Patent Reference 2) and the like can for example be mentioned.

    [0004] However, when supporting amount of the nucleoside linker as the starting point of synthesis is increased to too high level in order to further increase the quantity of nucleic acid synthesized per weight of solid-phase synthesis support, it poses a problem in that the coupling efficiency of amidite becomes poor and purity of the nucleic acid obtained is considerably lowered. For example, upper limit of the nucleoside linker supporting amount of a commercially available solid-phase synthesis support, which can synthesize a DNA oligonucleotide of 20 bases in high purity, is so far about 200 µmol/g at the most.

    [0005]  An attempt has been made to improve nucleic acid synthesizing ability by, using acrylonitrile, suppressing a fluctuation of swelling ratio of a porous resin bead in various organic solvents (cf. Patent Reference 3). However, although the porous resin bead used in this reference is small in the fluctuation of swelling ratio of the porous resin bead in various organic solvents, further improvement is in demand regarding the nucleic acid synthesizing ability.

    [0006] Patent Reference 4 discloses a support for solid-phase synthesis, which comprises a porous copolymer particle, said copolymer particle comprising 25 to 60% by weight of an aromatic-vinyl structural unit, 20 to 55% by weight of a vinyl cyamide structural unit, 5 to 18% by weight of an ethylenically-unsaturated-carboxylic-acid structural unit, and 2 to 15% by weight of an aromatic-divinyl structural unit.

    [0007] Patent Reference 5 relates to a porous resin bead made of a styrene-hydroxystyrene-divinylbenzene copolymer.

    [0008] 

    ∘ Patent Reference 1: JP-A-3-68593

    ∘ Patent Reference 2: JP-A-2005-325272

    ∘ Patent Reference 3: JP-A-2008-74979

    ∘ Patent Reference 4: US 2008/039604 A1

    ∘ Patent Reference 5: JP-A-2006-342245



    [0009] Non-patent Reference 1: Current Protocols in Nucleic Acid Chemistry (2000), UNIT 3.6 Synthesis of Unmodified Oligonucleotides

    SUMMARY OF THE INVENTION



    [0010] The invention aims at providing a porous resin bead for synthesizing nucleic acid in high synthesizing quantity and with high purity.

    [0011] The present inventors have found for the first time to our surprise that when, among the porous resin beads containing a first aromatic monovinyl compound-divinyl compound-(meth)acrylonitrile-second aromatic monovinyl compound copolymer, a porous resin bead where
    1. (1) the second aromatic monovinyl compound contains a group capable of binding with carboxyl group by dehydration condensation reaction, and
    2. (2) dry volume is from 2 to 3 ml/g,
      is used in the nucleic acid synthesis as a solid-phase synthesis support, synthesized quantity of the nucleic acid obtained is increased and its purity is improved.
      The inventors have further carried out intensive studies based on these findings and accomplished the invention as a result.


    [0012] Thus, the present invention provides a porous resin bead comprising a first aromatic monovinyl compound-divinyl compound-(meth)acrylonitrile-second aromatic monovinyl compound copolymer, in which the second aromatic monovinyl compound contains a group capable of binding with a carboxyl group by dehydration condensation reaction, wherein the amount of a structural unit derived from said (meth)acrylonitrile is from 1.8 to 3 mmol/g, and wherein the porous resin bead has a dry volume of from 2 to 3 ml/g.
    The present invention also provides a method for producing a nucleic acid, comprising sequentially binding a nucleoside or nucleotide to the afore-mentioned porous resin bead via a cleavable linker, thereby obtaining an oligonucleotide.

    [0013] The porous resin bead of the invention has a high nucleic acid synthesizing quantity and nucleic acid synthesizing purity. Therefore, when the porous bead of the invention is used, it becomes possible to carry out a nucleic acid synthesis efficiently in comparison with cases where the conventional porous resin beads are used.

    DETAILED DESCRIPTION OF THE INVENTION



    [0014] The porous resin bead of the invention contains a first aromatic monovinyl compound-divinyl compound-(meth)acrylonitrile-second aromatic monovinyl compound copolymer. Herein, the term "first aromatic monovinyl compound-divinyl compound-(meth)acrylonitrile-second aromatic monovinyl compound copolymer" refers to a copolymer containing structural units each derived from a first aromatic monovinyl compound, divinyl compound, (meth)acrylonitrile, and second aromatic monovinyl compound, respectively. In other words, the term "first aromatic monovinyl compound-divinyl compound-(meth)acrylonitrile-second aromatic monovinyl compound copolymer" means a copolymer obtained by copolymerizing as monomers a first aromatic monovinyl compound, divinyl compound, (meth)acrylonitrile, and second aromatic monovinyl compound.

    [0015] The "first aromatic monovinyl compound", which provides one of the structural units of the porous resin bead of the invention (namely, structural units of the first aromatic monovinyl compound-divinyl compound-(meth)acrylonitrile-second aromatic monovinyl compound copolymer), means styrene or a substitution product thereof. As the substitution product of styrene, for example, there may be mentioned those compounds in which one or more hydrogen atoms of styrene are substituted with an alkyl group having from 1 to 5 carbon atoms (e.g., methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, isobutyl group, sec-butyl group, tert-butyl group, n-amyl group, isoamyl group, sec-amyl group or tert-amyl group), a halogen atom, carboxyl group , sulfonate group , cyano group , an alkoxy group having from 1 to 5 carbon atoms (e.g., methoxy group, ethoxy group, propoxy group, butoxy group or pentyloxy group), nitro group , an acyl group (e.g., acetoxy group or benzoxy group) and the like.

    [0016] As such a first aromatic monovinyl compound, for example, illustratively, there may be mentioned: styrene; a "nucleus alkyl-substituted styrene" which is a styrene of which benzene ring moiety is substituted, such as o-methylstyrene, m-methylstyrene, p-methylstyrene, 2,4-dimethylstyrene, ethylstyrene, trimethylstyrene, and p-t-butylstyrene; an "α-alkyl-substituted styrene", such as α-methylstyrene, and α-methyl-p-methylstyrene; a "nucleus halogenated styrene" which is a styrene of which benzene ring moiety is halogenated, such as chlorostyrene, dichlorostyrene, fluorostyrene, pentafluorostyrene, bromostyrene; a "halogenated alkyl styrene", such as chloromethylstyrene, and fluoromethylstyrene; an "acyloxystyrene", such as hydroxystyrene, hydroxymethylstyrene, vinyl benzoate, sodium styrenesulfonate, cyanostyrene, methoxystyrene, ethoxystyrene, butoxystyrene, nitrostyrene, acetoxystyrene, and benzoyloxystyrene; and the like, although not limited thereto. Preferred as the first aromatic monovinyl compound is styrene.

    [0017] The "divinyl compound" which provides one of the structural units of the porous resin bead of the invention means an aromatic divinyl compound, a di(meth)acrylic acid ester or a substitution product thereof. As a substitution product of an aromatic divinyl compound or a substitution product of a di(meth)acrylic acid ester, there may be mentioned, for example, a compound in which one or more hydrogen atoms of the aromatic divinyl compound or di(meth)acrylic acid ester are substituted with: an alkyl group having from 1 to 5 carbon atoms; a halogen atom; carboxyl group; sulfonate group; cyano group; an alkoxy group having from 1 to 5 carbon atoms; and nitro group.

    [0018] As such a divinyl compound, illustratively, for example, there may be mentioned: an aromatic divinyl compound such as divinylbenzene, methyldivinylbenzene, divinyltoluene, and divinylnaphthalene; di(meth)acrylate compounds such as ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, further polyhydric ethylene glycol di(meth)acrylates, propylene glycol di(meth)acrylate, dipropylene ethylene glycol di(meth)acrylate, further polyhydric propylene glycol di(meth)acrylates, 1,2-butanediol di(meth)acrylate, 1,3-butanediol di(meth)acrylate, 1,4-butanediol di(meth)acrylate, 1,5-pentanediol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, 1,9-nonanediol di(meth)acrylate, 1,10-decanediol di(meth)acrylate, 2-methyl-1,8-octanediol di(meth)acrylate, and 1,4-cyclohexanediol di(meth)acrylate; and the like. Preferred as the divinyl compound of the invention is divinylbenzene. Regarding the divinylbenzene, o-, m- or p-divinylbenzene or a mixture thereof is preferably used as the compound providing the structural unit. Particularly preferred among them is m- or p-divinylbenzene. The divinyl compound functions as a crosslinking agent in the porous resin bead of the invention. Since there is a tendency that a porous resin bead is apt to swell when amount of a crosslinking agent is small, amount of the divinyl compound may contribute to the increase of swelling ratio.

    [0019] The "(meth)acrylonitrile" which provides one of the structural units of the porous resin bead of the invention means "acrylonitrile" or "methacrylonitrile", or "both of acrylonitrile and methacrylonitrile". That is, regarding the structural unit derived from the (meth)acrylonitrile to be contained in the porous resin bead of the invention, the structural unit derived from acrylonitrile or structural unit derived from methacrylonitrile may be contained each independently or both of these units may be contained.

    [0020] The "second aromatic monovinyl compound" which provides one of the structural units of the porous resin bead of the invention means styrene or a substitution product thereof, contains "a functional group capable of binding with carboxyl group by dehydration condensation reaction". Accordingly, in the case of synthesizing an objective nucleic acid, a nucleoside is connected to the porous resin bead, and when carboxyl group is present in a linker in that case, the carboxyl group of the linker can be easily connected with the porous resin bead, so that it is advantageous from the viewpoint that the nucleic acid synthesis can be carried out efficiently. As such a "functional group capable of binding with carboxyl group by dehydration condensation reaction", there can be mentioned, amino group, aminoalkyl group, hydroxyl group, hydroxyalkyl group and the like. More preferably, there can be mentioned, primary amino group, aminomethyl group, hydroxyl group, hydroxymethyl group and the like. It is preferable that the "functional group capable of binding with carboxyl group by dehydration condensation reaction" is arranged at para-position to vinyl group, but it may also be ortho- or meta-position.

    [0021] As such a second aromatic monovinyl compound, for example, illustratively, there may be mentioned: aminostyrene monomer or a substitution product thereof such as aminostyrene; aminoalkylstyrene monomer or a substitution product thereof such as aminomethylstyrene; hydroxystyrene monomer or a substitution product thereof such as hydroxystyrene; hydroxyalkyl styrene monomer or a substitution product thereof such as hydroxymethylstyrene; and the like, among which p-aminostyrene, p-aminomethylstyrene, p-hydroxystyrene and p-hydroxymethylstyrene are preferred.
    As the "substitution product" of hydroxystyrene monomer or aminostyrene monomer, there may be mentioned those compounds in which one or more hydrogen atom other then the "functional group capable of binding with carboxyl group by dehydration condensation reaction" are substituted with: an alkyl group having from 1 to 5 carbon atom; a halogen atom; carboxyl group; sulfonate group; cyano group; methoxy group; nitro group; and the like.

    [0022] The porous resin bead of the invention may be produced by directly using a second aromatic monovinyl compound which contains the "functional group capable of binding with carboxyl group by dehydration condensation reaction" (the production method is described later) in early stage of the production, but it may also be produced by once synthesizing a porous resin bead by suspension copolymerization or the like and then introducing the "functional group capable of binding with carboxyl group by dehydration condensation reaction". Particularly, when a second aromatic monovinyl compound having hydroxy group as the "functional group capable of binding with carboxyl group by dehydration condensation reaction" is introduced as a monomer providing a structural unit of the porous resin bead of the invention (i.e., introducing hydroxystyrene as a monomer providing a structural unit of the porous resin bead of the invention), it is preferable to produce the bead by the latter production method because the hydroxystyrene itself is a very unstable monomer due to its aptness to cause polymerization and its handling and preservation therefore are not easy.

    [0023] According to such a production process, as the aromatic monovinyl compound which becomes the base of the "second aromatic monovinyl compound" of the invention, there may be mentioned, for example: acylaminostyrene such as acetaminostyrene; acyloxystyrene such as acetoxystyrene, ethanoyloxystyrene, and benzoyloxystyrene; haloalkylstyrene such as chloromethylstyrene; and the like.

    [0024] Structural units derived from the acyloxystyrene or acylaminostyrene in the porous resin bead synthesized by suspension copolymerization or the like can be converted into the "structural unit derived from the second aromatic monovinyl compound" as a structural unit of the porous resin bead of the invention, illustratively, structural units derived from hydroxystyrene, aminostyrene and the like, by hydrolysis with an alkali or acid. Also, the structural unit derived from haloalkylstyrene can be converted into the "structural unit derived from the second aromatic monovinyl compound" as a structural unit of the porous resin bead of the invention, illustratively, structural units derived from aminoalkylstyrene, hydroxyalkylstyrene and the like, by the reaction with phthalimide and hydrazine, ammonia, sodium hydroxide or the like. Namely, the structural unit derived from haloalkylstyrene can be converted into the structural unit derived from aminoalkylstyrene by the reaction with phthalimide and hydrazine, ammonia or the like, and the structural unit derived from haloalkylstyrene can be converted into the structural unit derived from hydroxyalkylstyrene by the reaction with sodium hydroxide or the like. It is preferable that the acyloxy group, acylamino group, haloalkyl group or the like which is converted to become the "functional group capable of binding with carboxyl group by dehydration condensation reaction" is arranged at para-position to vinyl group, but it may also be ortho- or meta-position.

    [0025] Alternatively, a porous resin bead comprising a first aromatic monovinyl compound-divinyl compound-(meth)acrylonitrile compound copolymer synthesized by suspension copolymerization or the like may be subjected to post-treatment to introduce a haloalkyl group into the aromatic ring of the structural unit derived from the first aromatic monovinyl compound, subsequently converting this into the structural unit derived from an aminoalkylstyrene or hydroxyalkylstyrene. For example, chloromethyl group is introduced by adding chloromethyl ether and zinc chloride to a dispersion of the porous resin bead comprising a first aromatic monovinyl compound-divinyl compound-(meth)acrylonitrile compound copolymer and allowing them to undergo the reaction. Next, the "structural unit derived from the second aromatic monovinyl compound" is introduced through the introduction of aminomethyl group by allowing the copolymer to react with ammonia. The porous resin bead of the invention can also be obtained even via such a production process. It is preferable that the haloalkyl group is arranged at para-position to vinyl group, but it may also be at ortho-or meta-position.

    [0026]  Although the amount of the structural unit derived from the first monovinyl compound (may be also referred to as "first monovinyl compound structural unit") based on the total amount of structural units of the porous resin bead of the invention is not particularly limited, its occupying amount per weight of the porous resin bead is preferably from 3.0 to 8.3 mmol/g, more preferably from 4.5 to 8.0 mmol/g. further preferably from 5.0 to 7.5 mmol/g.
    When amount of the structural unit derived from the first monovinyl compound is smaller than the above-mentioned range, solvent resistance, heat stability and porosity of the porous resin bead may not be sufficient so that desired effects can hardly be expected when used in the solid-phase synthesis of a nucleic acid. Also, when its amount is larger than the above-mentioned range, degree of swelling in the organic solvent is lowered so that when used in the solid-phase synthesis of a nucleic acid, synthesized quantity of the nucleic acid becomes small, and further, purity of the nucleic acid is also reduced.

    [0027] Although the amount of the structural unit derived from the divinyl compound (may be also referred to as "divinyl compound structural unit") based on the total amount of structural units of the porous resin bead of the invention is not particularly limited, its occupying amount per weight of the porous resin bead is preferably from 0.2 to 1.0 mmol/g, more preferably from 0.25 to 0.8 mmol/g, further preferably from 0.3 to 0.7 mmol/g.
    When amount of the structural unit derived from the divinyl compound is smaller than the above-mentioned range, solvent resistance, heat stability and porosity of the porous resin bead may not be sufficient so that desired effects can hardly be expected when used in the solid-phase synthesis of a nucleic acid. Also, when its amount is larger than the above-mentioned range, degree of swelling in the organic solvent is lowered so that when used in the solid-phase synthesis of a nucleic acid, synthesized quantity of the nucleic acid may become small, and further, purity of the nucleic acid may be also reduced.

    [0028] The porous resin bead of the invention markedly swells in acetonitrile but its dry volume is from 2 to 3 ml/g. This dry volume is small in comparison with the general porous resin beads. However, since the porous resin bead of the invention shows a large swelling ratio in acetonitrile, reaction field of the nucleic acid synthesis employing acetonitrile can be widened, whereby, reactivity of the nucleic acid synthesis can be improved. Thus, according to the invention, there can be obtained a porous resin bead for use in the solid-phase synthesis support, which renders it possible to synthesize a nucleic acid having both of the high synthesizing quantity and synthesizing purity in comparison with the conventional porous resin beads for use in nucleic acid synthesis.

    [0029] Thus, in order to adjust dry volume of the porous resin bead of the invention from 2 to 3 ml/g, it is necessary to consider amount of the structural unit derived from (meth)acrylonitrile (may be also referred to as "(meth)acrylonitrile structural unit") based on the total amount of structural units of the porous resin bead.
    Amount of the structural unit derived from (meth)acrylonitrile based on the total amount of structural units of the porous resin bead of the invention is from 1.8 to 3.0 mmol/g.
    When amount of the structural unit derived from (meth)acrylonitrile is smaller than the above-mentioned range, a porous resin bead of the desired dry weight can hardly be obtained and the desired effect can hardly be expected when used in the solid-phase synthesis of a nucleic acid. Also, the porous resin bead itself can hardly be formed when the amount is larger than the above-mentioned range. Amount of the structural unit derived from (meth)acrylonitrile in the porous resin bead of the invention is measured by a total nitrogen analysis. Illustratively, this is calculated from the molecular weight of the structural unit derived from (meth)acrylonitrile, by putting a sample in a platinum pan, weighing it on a micro balance and then measuring the amount of nitrogen by a micro total nitrogen analyzer TN-110 (mfd. by Mitsubishi Chemical Corporation).

    [0030] Although not particularly limited, amount of the structural unit derived from the second aromatic monovinyl compound (may be also referred to as "second aromatic monovinyl compound structural unit") based on the total weight of structural units of the porous resin bead of the invention is preferably from 0.05 to 1.5 mmol/g, more preferably from 0.1 to 1.0 mmol/g, further preferably from 0.2 to 0.8 mmol/g.
    This is because its effect can hardly be obtained when amount of the structural unit derived from the second aromatic monovinyl compound is smaller than the above-mentioned range, while the porous resin bead itself can hardly be formed when the amount is larger than the above-mentioned range.

    [0031] Regarding the amount of the "functional group capable of binding with carboxyl group by dehydration condensation reaction" possessed by the structural unit derived from the second aromatic monovinyl compound, in the porous resin bead of the invention, for example in the case of amino group, aminoalkyl group, hydroxyl group or hydroxyalkyl group, its occupying amount per weight of the porous resin bead is preferably from 0.05 to 1.5 mmol/g, more preferably from 0.1 to 1.0 mmol/g, further preferably from 0.2 to 0.8 mmol/g.
    When amount of the "functional group capable of binding with carboxyl group by dehydration condensation reaction" is smaller than the above-mentioned range, there is a tendency that synthesized quantity of a nucleic acid becomes small when used as a support for solid-phase synthesis of nucleic acid. Also, when the amount is larger than the above-mentioned range, there is a tendency that purity of a nucleic acid is lowered when used as a support for solid-phase synthesis of nucleic acid.

    [0032] Regarding the amount of the "functional group capable of binding with carboxyl group by dehydration condensation reaction" possessed by the structural unit derived from the second aromatic monovinyl compound, in the porous resin bead of the invention, for example in the case of amino group, aminoalkyl group, hydroxyl group or hydroxyalkyl group, it is measured by titration based on JIS K 0070. Illustratively, amount of the functional group can be calculated by acetylating the hydroxyl group of the objective solid-phase synthesis support with known amount of an acetylating reagent (acetic anhydride/pyridine) and then measuring the amount of acetic anhydride which was not consumed by the acetylation, by titration of potassium hydroxide.

    [0033] The method for producing the porous resin bead of the invention is not particularly limited, and there may be mentioned, for example:
    1. (1) a method for producing a porous resin bead, including allowing a first aromatic monovinyl compound, a divinyl compound, (meth)acrylonitrile and a second aromatic monovinyl compound which contains a functional group capable of binding with carboxyl group by dehydration condensation reaction to undergo suspension copolymerization using an organic solvent and water;
    2. (2) a method for producing a porous resin bead, including synthesizing a porous resin bead through suspension copolymerization or the like and then introducing a functional group capable of binding with carboxyl group by dehydration condensation reaction into the structural unit derived from the second aromatic monovinyl compound; and the like.


    [0034] In carrying out the suspension copolymerization, amount (feedstock amount) of the first aromatic monovinyl compound based on the total amount of the first aromatic monovinyl compound, divinyl compound, (meth)acrylonitrile and second aromatic monovinyl compound is preferably from 31 to 85% by mol, more preferably from 45 to 82% by mol, further preferably from 53 to 76% by mol.

    [0035] In carrying out the suspension copolymerization, amount (feedstock amount) of the divinyl compound based on the total amount of the first aromatic monovinyl compound, divinyl compound, (meth)acrylonitrile and second aromatic monovinyl compound is preferably from 2 to 10% by mol, more preferably from 2.5 to 8% by mol, further preferably from 3 to 7% by mol.

    [0036] In carrying out the suspension copolymerization, amount (feedstock amount) of the (meth)acrylonitrile based on the total amount of the first aromatic monovinyl compound, divinyl compound, (meth)acrylonitrile and second aromatic monovinyl compound is preferably from 10 to 40% by mol, more preferably from 13 to 35% by mol, further preferably from 18 to 30% by mol.

    [0037] In carrying out the suspension copolymerization, amount (feedstock amount) of the second aromatic monovinyl compound based on the total amount of the first aromatic monovinyl compound, divinyl compound, (meth)acrylonitrile and second aromatic monovinyl compound is preferably from 0.5 to 15% by mol, more preferably from 1 to 10% by mol, further preferably from 2 to 8% by mol. This amount is the same for the aromatic monovinyl compound which becomes the base of the second aromatic monovinyl compound in the case of a production method including once synthesizing a porous resin bead through suspension copolymerization or the like and then introducing a "functional group capable of binding with carboxyl group by dehydration condensation reaction".

    [0038] The suspension copolymerization is carried out by agitating and emulsifying a mixture of the above-mentioned respective compounds (each of the composing components of the porous resin bead of the invention to be subjected to suspension copolymerization (i.e., first aromatic monovinyl compound, divinyl compound, (meth)acrylonitrile and second aromatic monovinyl compound) is referred sometimes to as "monomer" hereinafter) and an organic solvent in water.

    [0039] In the present invention, the organic solvent means a solvent other than water in suspension copolymerization system, and a hydrocarbon and an alcohol are suitably used. Illustratively as the hydrocarbon, an aliphatic saturated or unsaturated hydrocarbon or an aromatic hydrocarbon can be used, of which an aliphatic hydrocarbon having from 5 to 12 carbon atoms is preferable, and more preferably, there may be mentioned n-hexane, n-heptane, n-octane, isooctane, undecane, dodecane and the like. In addition, it is preferable to allow an alcohol to coexist in order to increase porosity of the beads obtained at this juncture (the alcohol to be used with the aim of increasing porosity is referred to as "porogen" hereinafter). As the alcohol according to the invention, an aliphatic alcohol can for example be mentioned, and the number of carbon atoms thereof is preferably from 5 to 9. As such an alcohol, illustratively, there can be mentioned 2-ethylhexanol, amyl alcohol (e.g., t-amyl alcohol), nonyl alcohol, 2-octanol, cyclohexanol and the like.

    [0040] Weight ratio of the hydrocarbon and alcohol to be used in the suspension copolymerization can be optionally changed depending on the illustrative combination of the hydrocarbon and alcohol, and specific surface area of the solid-phase synthesis support can be increased thereby. Preferable blending ratio of the hydrocarbon and alcohol is from 1:9 to 6:4 by weight ratio.

    [0041] Weight of the organic solvent at the time of suspension copolymerization is preferably from 0.5 to 2.5 times, more preferably from 0.8 to 2.2 times, further preferably from 1.0 to 2.0 times, based on the total weight of the above-mentioned respective monomers. When this value is larger or smaller than that, specific surface area of the obtained porous resin bead becomes small and quantity of the synthesis reaction product by chemical reaction using the beads becomes small.

    [0042] According to the invention, the method itself for carrying out the suspension copolymerization may be carried out by applying a conventionally known method.

    [0043] The dispersion stabilizer to be used in the suspension copolymerization is not particularly limited, and there can be used a conventionally known polyvinyl alcohol, polyacrylic acid, gelatin, starch, carboxymethylcellulose and the like hydrophilic protective colloid agents, and calcium carbonate, magnesium carbonate, calcium phosphate, valium sulfate, calcium sulfate, bentonite and the like slightly soluble powders, and the like. Although amount of the dispersion stabilizer is not particularly limited, it is preferably from 0.01 to 10% by weight based on the weight of water in the suspension copolymerization system. When this value is smaller, dispersion stability of suspension copolymerization may be spoiled and a large quantity of aggregates may be formed. When this value is larger, a large number of minute beads may be formed.

    [0044] A polymerization initiator to be used in carrying out the suspension copolymerization is not particularly limited, and there can be used conventionally known dibenzoyl peroxide, dilauroyl peroxide, distearoyl peroxide, 1,1-di(t-butylperoxy)-2-methylcyclohexane, 1,1-di(t-hexylperoxy)-3,3,5-trimethylcyclohexane, 1,1-di(t-hexylperoxy)cyclohexane, 1,1-di(t-butylperoxy)-cyclohexane, di-t-hexyl peroxide, t-butylcumyl peroxide, di-t-butyl peroxide, 1,1,3,3-tetramethylbutylperoxy-2-ethyl hexanoate, t-hexylperoxy-2-ethyl hexanoate, t-butylperoxy-2-ethyl hexanoate, t-butylperoxy-isopropyl monocarbonate and the like peroxides, and 2,2'-azobisisobutyronitrile, 2,2'-azobis-2-methylbutyronitrile, 2,2'-azobis-2,4-dimethylvaleronitrile and the like azo compounds. Adding amount of the polymerization initiator is not particularly limited, and it is possible to select an appropriate amount by those skilled in the art.

    [0045] The reaction condition in carrying out suspension copolymerization can be optionally set, and for example, agitation of from 30 minutes to 48 hours at from 60 to 90°C may be mentioned. The agitation rate is for example from 100 rpm to 1,000 rpm, preferably from 200 rpm to 500 rpm. By the suspension copolymerization, the first aromatic monovinyl compound-divinyl compound-(meth)acrylonitrile-second aromatic monovinyl compound copolymer can be obtained.

    [0046] The thus obtained copolymer may be optionally subjected to washing, drying, classification and the like treatments. In addition, after synthesis of a porous resin bead by suspension copolymerization or the like, a functional group capable of binding with carboxyl group by dehydration condensation reaction may be introduced into the structural unit derived from the second aromatic monovinyl compound. The introducing method is as described in the foregoing.

    [0047] The porous resin bead of the invention can be obtained via the above treatments. This porous resin bead can be used as a solid-phase synthesis support.

    [0048] The "porous resin bead" of the invention is not always necessary to show strict spherical shape, and it may be at least in a granular shape. However, the porous resin bead of the invention (support for solid-phase synthesis) is preferably in a spherical shape from the viewpoint that its efficiency for filling in a solid-phase synthesis reaction column can be increased and it can hardly be broken.

    [0049]  The median particle diameter of the porous resin bead of the invention measured by a laser diffraction scattering method is not particularly limited, but is preferably from 1 to 1,000 µm, more preferably from 10 to 500 µm, further preferably from 20 to 300 µm. The median particle diameter of the porous resin bead of the invention is measured by a laser diffraction scattering method. Illustratively, average particle diameter is calculated by measuring it by a laser diffraction scattering type particle size distribution analyzer LA-950 (mfd. by Horiba, Ltd.) using 50% v/v ethanol aqueous solution as the dispersion medium.

    [0050] The median particle diameter depends on the stirring condition before the commencement of polymerization in case of suspension polymerization, kind and amount of the porogen, and concentration of the dispersion stabilizer in carrying out the suspension polymerization. Accordingly, by adjusting these conditions, it is possible to adjust the median particle diameter within a desired range. As the porogen, the aforementioned alcohol can be mentioned. In addition, enlargement of the median particle diameter under swelling condition contributes to the increase of swelling ratio of the porous resin bead.

    [0051] The median pore diameter of the porous resin bead of the invention measured by a method of mercury penetration is not particularly limited, but is preferably from 1 to 1,000 nm, more preferably from 5 to 500 nm, further preferably from 10 to 300 nm.
    The median pore diameter of the porous resin bead of the invention is measured by a mercury penetration method. Illustratively, 0.2 g of the porous resin bead is put into a mercury porosimeter PoreMaster 60-GT (mfd. by Quantachrome Instruments) and measured by the mercury penetration method under conditions of 140° in mercury contact angle and 480 dyn/cm in mercury surface tension.

    [0052] Dry volume of the porous resin bead of the invention is preferably from 2 to 3 ml/g, more preferably from 2.2 to 3 ml/g, further preferably from 2.2 to 2.8 ml/g. The porous resin bead of the invention has a dry volume of within the above-mentioned range and thus enables a nucleic acid synthesis where both of the synthesized quantity and synthesis purity are high in comparison with the porous resin beads for nucleic acid synthesis so far developed.
    When the dry volume is smaller than the above-mentioned lower limit of dry volume, synthesized quantity and synthesis purity of nucleic acid are lowered. On the other hand, when the dry volume is larger than the above-mentioned upper limit of dry volume, the number of starting points of the nucleic acid synthesis becomes small due to less resin content, and synthesized quantity of nucleic acid per reaction container is lowered as a result. When dry volume is small, it is considered in general that the field of nucleic acid synthesis becomes small which is disadvantageous for nucleic acid synthesis. However, in spite of the smaller volume in comparison with the general solid-phase synthesis resin beads, the porous resin bead of the invention unexpectedly can increase synthesized quantity and synthesis purity of nucleic acid in comparison with the general solid-phase synthesis resin beads.

    [0053] Dry volume of the porous resin bead of the invention is measured by a measuring cylinder. Illustratively, 1.00 g of a porous resin bead is put into a 10 ml capacity measuring cylinder, the porous resin bead is thoroughly filled in the measuring cylinder by lightly adding vibration, and then its apparent volume is measured.

    [0054] The dry volume depends on the amount of (meth)acrylonitrile monomer at the time of suspension copolymerization. There is a tendency that when blending amount of (meth)acrylonitrile is from 10 to 40% by mol, dry volume of the obtained porous resin bead becomes small in comparison with a case of blending no (meth)acrylonitrile.

    [0055] In addition, the dry volume is influenced by the amount and kind of organic solvent to be mixed with the monomers in carrying out suspension copolymerization. There is a tendency that the dry volume becomes small as the amount of organic solvent becomes less. However, when the amount of organic solvent is too little, the pore diameter becomes too small and the nucleic acid synthesizing ability therefore is lowered, so that the amount of organic solvent is preferably from 0.5 to 2.5 times based on the total weight of monomers.

    [0056] The porous resin bead of the invention can be used as a support for various chemical synthesis reactions, and can be used particularly effectively in the nucleic acid synthesis.

    [0057] Regarding the nucleic acid synthesis using the porous resin bead of the invention, conventionally known methods may be applied. For example, the following nucleoside succinyl linker:

    (in which DMT is a 5'-protection group, and B1 is a base.)
    is bonded to a functional group on the porous resin bead of the invention which is capable of binding with carboxyl group by dehydration condensation reaction. Next, nucleoside phosphoramidite is bonded step by step from 5' end of this nucleoside in such a manner that it becomes a predetermined nucleotide sequence. This synthesis reaction can be carried out using an automatic synthesizer. For example, the reaction is repeated by successively feeding a 5'-OH deprotection agent, a nucleoside phosphoramidite solution, an amidite activator solution, an oxidizing agent solution, a capping agent solution, acetonitrile as a washing solution, and the like into the device's reaction column packed with the nucleoside succinyl linker-bonded porous resin bead. Finally, the desired nucleic acid can be obtained by cutting the succinyl linker moiety for example through its hydrolysis with an alkali solution. A conventionally known linker can be used, for example, a porous resin bead bonded to a nucleoside linker and having the following structure, and the like can be cited.

    (in which the member represented by a large circle is a support for solid-phase synthesis, DMT is a 5'-protection group, and B1 is a base.)

    EXAMPLES



    [0058] The following describes the invention further illustratively with reference to examples.

    Inventive Example 1



    [0059] A 500 ml capacity separable flask equipped with a condenser, an agitator and a nitrogen introducing tube was arranged on a constant temperature water bath, and 2.5 g of polyvinyl alcohol (mfd. by KURARAY) and 250 g of distilled water were charged therein and stirred at 300 rpm to dissolve the polyvinyl alcohol. There was added a solution prepared by mixing and dissolving 35 g of styrene (mfd. by Wako Pure Chemical Industries), 4.5 g (4.8% by mol) of p-acetoxystyrene (mfd. by Sigma-Aldrich), 5.5 g (4.0% by mol) of divinylbenzene (55% content, mfd. by Wako Pure Chemical Industries), 11.5 g (29.7% by mol) of methacrylonitrile (mfd. by Wako Pure Chemical Industries), 60 g of 2-ethylhexanol (mfd. by Wako Pure Chemical Industries), 30 g of isooctane (mfd. by Wako Pure Chemical Industries), and 1 g of benzoyl peroxide (25% moisture, mfd. by NOF CORPORATION) to the resulting solution, and stirred (300 rpm) at room temperature under a stream of nitrogen, and then suspension copolymerization was carried out for 24 hours by rising the temperature to 80°C.

    [0060]  The polymerization product was washed by filtration using distilled water and acetone (mfd. by Wako Pure Chemical Industries) and dispersed in acetone to a total volume of about 1 L. This was allowed to stand for such a period of time that the precipitate did not become loose even when the container was slanted, and then the supernatant acetone was discarded. Classification of this precipitate was carried out by again adding acetone to a total volume of about 1 L and repeating the standing and acetone discharge operations. By filtering this dispersion and drying it under a reduced pressure, a porous resin bead containing a styrenedivinylbenzene-methacrylonitrile- p-acetoxystyrene copolymer was obtained.

    [0061] Next, 20 g of a powder of the porous resin bead containing the above-mentioned copolymer, 80 g of ethanol, 50 g of distilled water, and 2 g of sodium hydroxide were charged into a 500 ml capacity flask equipped with a condenser, an agitator and a nitrogen introducing tube, and allowed to undergo the reaction at 75°C for 18 hours while stirring. By filtering this dispersion and drying it under a reduced pressure, a porous resin bead containing a styrenedivinylbenzene-methacrylonitrile-4-hydroxystyrene copolymer was obtained.

    Inventive Example 2



    [0062] A porous resin bead containing a styrene-divinylbenzene-acrylonitrile-4-hydroxystyrene copolymer was obtained in the same manner as in Inventive Example 1, except that in Inventive Example 1, as the monomers, there was used 34 g of styrene, 6 g (5.7% by mol) of p-acetoxystyrene (mfd. by Sigma-Aldrich), 8.5 g (5.5% by mol) divinylbenzene (55% content, mfd. by Wako Pure Chemical Industries), and 12 g (34.6% by mol) of acrylonitrile.

    Inventive Example 3



    [0063] A porous resin bead containing a styrene-divinylbenzene-methacrylonitrile-4-hydroxystyrene copolymer was obtained in the same manner as in Inventive Example 1, except that in Inventive Example 1, there was charged 2.6 g of polyvinyl alcohol, 260 g of distilled water, 29 g of styrene, 5 g (5.9% by mol) of p-acetoxystyrene, 7.5 g (6.1 % by mol) of divinylbenzene, 10.5 g (29.9% by mol) of methacrylonitrile, 58 g of 2-ethylhexanol, and 25 g of isooctane, and the agitation rate was set to 350 rpm.

    Comparative Example 1



    [0064] A porous resin bead containing a styrene-divinylbenzene-4-hydroxystyrene copolymer was obtained in the same manner as in Inventive Example 1, except that in Inventive Example 1, 49 g of styrene, 4 g (4.5 % by mol) of p-acetoxystyrene, 7 g (5.4% by mol) of divinylbenzene (and 0 g of methacrylonitrile) were used as the monomers and 2-ethylhexanol was changed to 52 g, and isooctane to 23g.

    Comparative Example 2



    [0065] A porous resin bead containing a styrene-divinylbenzene-methacrylonitrile-4-hydroxystyrene copolymer was obtained in the same manner as in Inventive Example 1, except that in Inventive Example 1, there was charged 2.6 g of polyvinyl alcohol, 260 g of distilled water, 33 g of styrene, 4 g (5.3 % by mol) of p-acetoxystyrene and 7 g (6.3% by mol) of divinylbenzene, 5 g (15.9% by mol) of methacrylonitrile, 61 g of 2-ethylhexanol, and 26 g of isooctane, and the agitation rate was set to 400 rpm.

    Comparative Example 3



    [0066] A porous resin bead containing a styrene-divinylbenzene-methacrylonitrile-4-hydroxystyrene copolymer was obtained in the same manner as in Inventive Example 1, except that in Inventive Example 1, there was charged 2.6 g of polyvinyl alcohol, 260 g of distilled water, 42 g of styrene, 7 g (6.3% by mol) of p-acetoxystyrene, 5.5 g (3.4% by mol) of divinylbenzene, 13.5 g (29.2% by mol) of methacrylonitrile, 20 g of isooctane, and 1.5 g of benzoyl peroxide, 48 g of 1-decanol was used instead of 60 g of 2-ethylhexanol, and the agitation rate was set to 450 rpm.

    Test Example 1: Measurement of physical properties of porous resin beads



    [0067] The following measurement of physical properties was carried out on the porous resin beads obtained in Inventive Examples 1 to 3 and Comparative Examples 1 to 3.

    (Median particle diameter)



    [0068] Each sample to be measured was subjected to ultrasonic dispersion in a 50% v/v ethanol liquid. For this dispersion, Median particle diameter was measured by a laser diffraction/scattering type particle size distribution analyzer LA-920 (mfd. by Horiba, Ltd.) using the 50% v/v ethanol liquid as dispersion medium.

    (Median pore diameter)



    [0069] A 0.2 g portion of each sample to be measured was put into a mercury porosimeter PoreMaster 60-GT (mfd. by Quantachrome Instruments) and Median pore diameter was measured by the method of mercury penetration under conditions of 140° in mercury contact angle and 480 dyn/cm in mercury surface tension.

    (Functional group quantity)



    [0070] From 0.5 to 2 g of each sample to be measured was weighed and put into a flask, and 0.5 ml of an acetylation reagent (prepared by adding pyridine into 25 g of acetic anhydride adjusting the total volume to 100 ml) and 4.5 ml of pyridine were accurately added thereto. After a lapse of 2 hours by adjusting the mixture in the flask to 95 to 100°C, this was spontaneously cooled to room temperature and 1 ml of distilled water was added thereto. By heating the mixture for 10 minutes, the acetic anhydride which was not consumed by the acetylation was degraded. The whole contents in the flask were transferred into a beaker, diluted to a total volume of 150 ml with distilled water and then titrated with 0.5 N of potassium hydroxide aqueous solution. Separately from this, a blank assay was carried out by the same operation of the above without adding the sample to be measured. The functional group quantity (hydroxyl group quantity) of the sample to be measured was calculated by the following formula (1). Herein, A (mmol/g) means amount of hydroxyl group in the sample to be measured, B (ml) is titrated volume of the potassium hydroxide aqueous solution in the blank assay, C (ml) is titrated volume of the potassium hydroxide aqueous solution in the measurement of sample to be measured, f is a factor of the potassium hydroxide aqueous solution and M (g) is weight of the weighed sample to be measured.


    (Content of structural unit derived from (meth)acrylonitrile)



    [0071] A 2 to 3 mg portion of each sample to be measured was put into a platinum pan and weighed using a micro balance and then subjected to measured by a total nitrogen analyzer TN-110 (mfd. by Mitsubishi Chemical Corporation). The content of the structural unit D derived from (meth)acrylonitrile was calculated from the thus obtained N concentration (% by weight) by the following formula (2).


    (Dry volume)



    [0072] A 1.00 g portion of each sample to be measured was put into a 10 ml capacity measuring cylinder, the sample was thoroughly filled therein by applying vibration and then its apparent volume was measured.

    [0073] These results are shown in Table 1.
    [Table 1]
     UnitInv. Ex. 1Inv. Ex. 2Inv. Ex. 3Comp. Ex. 1Comp. Ex. 2Comp. Ex. 3
    Median particle diameter µm 80 83 83 90 80 72
    Median pore diameter nm 45 30 - 53 - -
    Functional group quantity mmol/g 0.57 0.70 0.70 0.42 0.57 0.84
    (Meth)acrylonitrile content mmol/g 2.8 2.8 2.7 0.0 1.3 2.7
    Dry volume ml/g 2.7 2.2 2.3 3.2 4.3 1.8

    Test Example 2: Synthesis of DNA oligonucleotide and evaluation thereof



    [0074] Using the porous resin beads obtained in Inventive Examples 1 and 2 and Comparative Examples 1 and 2, a DNA oligonucleotide having a length of 20 bases was synthesized in the following manner and evaluation thereof was carried out.

    [0075] In the case of the porous resin beads obtained in Inventive Example 1 and Comparative Example 2, 5 g of porous resin bead, 1.95 g of DMT-dT-3'-succinate (mfd. by Beijing OM Chemicals), 1.00 g of HBTU (mfd. by Novabiochem), 0.90 ml of N,N-diisopropyl ethylamine (mfd. by Sigma-Aldrich) and 50 ml of acetonitrile (mfd. by Wako Pure Chemical Industries) were mixed, allowed to undergo the reaction at room temperature for 12 hours while stirring, washed through filtration using acetonitrile and then dried.

    [0076] In the case of the porous resin bead obtained in Inventive Example 2, 5 g of the porous resin bead, 1.35 g of DMT-dT-3'-succinate, 0.70 g of HBTU, 0.65 ml of N,N-diisopropyl ethylamine and 50 ml of acetonitrile were mixed, allowed to undergo the reaction at room temperature for 12 hours while stirring, washed through filtration using acetonitrile and then dried.

    [0077] In the case of the porous resin bead obtained in Comparative Example 1, 5 g of the porous resin bead, 1.95 g of DMT-dT-3'-succinate, 1.00 g of HBTU, 0.94 ml of N,N-diisopropyl ethylamine and 50 ml of acetonitrile were mixed, allowed to undergo the reaction at room temperature for 12 hours while stirring, washed through filtration using acetonitrile and then dried.

    [0078] Each of these porous resin beads was mixed with 10 ml of CapA (20% acetic anhydride/80% acetonitrile), 10 ml of CapB (20% N-methylimidazole/30% pyridine/50% acetonitrile), 0.1 g of 4-dimethylaminopyridine (mfd. by Sigma-Aldrich) and 25 ml of acetonitrile were mixed, allowed to undergo the reaction at room temperature for 12 hours while stirring, washed through filtration using acetonitrile and then dried under a reduced pressure to obtain a solid-phase synthesis support to which DMT-dT-3'-succinate was bonded. Bonded amount of DMT-dT-3'-succinate was calculated from absorbance measurement (412 nm) of DMT group which had been generated by deprotection using p-toluenesulfonic acid/acetonitrile solution.

    [0079] A 0.8 to 1.1 g portion of the DMT-dT-3'-succinate-bonded porous resin bead obtained in the above was filled in a synthesis column (6.3 ml capacity) and set on AKTA oligopilot plus 100 (mfd. by GE Healthcare), and a DNA oligonucleotide of 20 mer mixed sequence was synthesized under conditions of 2 eq/synthesis scale in nucleoside phosphoramidite concentration and DMT-on. After the synthesis, the porous resin bead was dried, soaked in 25 ml of 28% aqueous ammonia and then allowed to undergo the reaction at 55°C for 18 hours to carry out the cutting out of the DNA oligonucleotide and deprotection of the base amino group. The porous resin bead was separated by filter filtration and the OD yield of nucleic acid (equivalent to nucleic acid synthesis quantity) was calculated from the UV absorbance measurement (260 nm) of the filtrate. In addition, Full-length % (ratio of DNA oligonucleotide having the desired sequence length) was calculated from the HPLC (mfd. by Waters Corporation) measurement of the filtrate. The results are show in Table 2.
    [Table 2]
     UnitInv. Ex. 1Inv. Ex. 2Comp. Ex. 1Comp. Ex.2
    Bonded amount of DMT-dT-3'-succinate µmol/g-resin bead 400 310 303 389
    OD yield OD/µmol 115 117 93 75
    OD yield OD/g-resin bead 46,000 36,270 28,179 29,175
    Full-Length % 76 74 61 49


    [0080] Using the porous resin beads obtained in Inventive Example 3 and Comparative Example 3, a DNA oligonucleotide having a length of 20 bases was synthesized in the following manner and evaluation thereof was carried out.

    [0081] In the case of the porous resin beads obtained in Inventive Example 3, 5 g of porous resin bead, 1.95 g of DMT-dT-3'-succinate (mfd. by Beijing OM Chemicals), 1.00 g of HBTU (mfd. by Novabiochem), 0.90 ml of N,N-diisopropyl ethylamine (mfd. by Sigma-Aldrich) and 50 ml of acetonitrile (mfd. by Wako Pure Chemical Industries) were mixed, allowed to undergo the reaction at room temperature for 12 hours while stirring, washed through filtration using acetonitrile and then dried.

    [0082]  In the case of the porous resin bead obtained in Comparative Example 3, 5 g of the porous resin bead, 1.46 g of DMT-dT-3'-succinate, 0.75 g of HBTU, 0.68 ml of N,N-diisopropyl ethylamine and 50 ml of acetonitrile were mixed, allowed to undergo the reaction at room temperature for 12 hours while stirring, washed through filtration using acetonitrile and then dried.

    [0083] Each of these porous resin beads was mixed with 10 ml of CapA (20% acetic anhydride/80% acetonitrile), 10 ml of CapB (20% N-methylimidazole/30% pyridine/50% acetonitrile), 0.1 g of 4-dimethylaminopyridine (mfd. by Sigma-Aldrich) and 25 ml of acetonitrile were mixed, allowed to undergo the reaction at room temperature for 12 hours while stirring, washed through filtration using acetonitrile and then dried under a reduced pressure to obtain a solid-phase synthesis support to which DMT-dT-3'-succinate was bonded. Bonded amount of DMT-dT-3'-succinate was calculated from absorbance measurement (412 nm) of DMT group which had been generated by deprotection using p-toluenesulfonic acid/acetonitrile solution.

    [0084] A 3.3 mg portion of the DMT-dT-3'-succinate-bonded porous resin bead obtained in the above was filled in a synthesis column and set on Applied Biosystems 3400 DNA Synthesizer (mfd. by Applied Biosystems), and a DNA oligonucleotide of 20 mer mixed sequence was synthesized under a condition of DMT-on. After the synthesis, the porous resin bead was dried, transferred into a glass bottle, mixed with 1 ml of 28% aqueous ammonia and then allowed to undergo the reaction at 55°C for 15 hours to carry out the cutting out of the DNA oligonucleotide and deprotection of the base amino group. The porous resin bead was separated by filter filtration and the OD yield of nucleic acid (equivalent to nucleic acid synthesis quantity) was calculated from the UV absorbance measurement (260 nm) of the filtrate. In addition, Full-length % (ratio of DNA oligonucleotide having the desired sequence length) was calculated from the HPLC (mfd. by Waters Corporation) measurement of the filtrate. The results are show in Table 3.
    [Table 3]
     UnitInv. Ex. 3Comp. Ex. 3
    Bonded amount of DMT-dT-3'-succinate µmol/g-resin bead 305 308
    OD yield OD/µmol 137 53
    OD yield OD/g-resin bead 41,785 16,324
    Full-Length % 72 25


    [0085] As is evident from Tables 2 and 3, it was found that the synthesized quantity of DNA oligonucleotide per resin bead (OD yield) becomes high and the synthesis purity (Full-Length %) also becomes high when the porous resin bead of the invention were used, in comparison with the comparative examples.

    [0086] The invention provides a porous resin bead which is useful as a solid-phase synthesis support for nucleic acid synthesis. Since the porous resin bead of the invention achieves high nucleic acid synthesis quantity and synthesis purity, it becomes possible, owing to using this porous resin bead, to carry out nucleic acid synthesis more efficiently than the case of the use of conventional porous resin beads.


    Claims

    1. A porous resin bead comprising a first aromatic monovinyl compound-divinyl compound-(meth)acrylonitrile-second aromatic monovinyl compound copolymer, wherein the second aromatic monovinyl compound contains a group capable of binding with a carboxyl group by dehydration condensation reaction, wherein the amount of a structural unit derived from said (meth)acrylonitrile is from 1.8 to 3.0 mmol/g, and wherein the porous resin bead has a dry volume of from 2 to 3 ml/g, determined in accordance with indications provided in the description.
     
    2. The porous resin bead described in claim 1, wherein the group capable of binding with a carboxyl group by dehydration condensation reaction is a group selected from the group consisting of an amino group, an aminoalkyl group, a hydroxyl group and a hydroxyalkyl group.
     
    3. The porous resin bead described in claim 1 or 2, wherein an amount of the divinyl compound based on the total amount of monomers is from 2 to 10% by mol.
     
    4. The porous resin bead described in any one of claims 1 to 3, wherein the divinyl compound is divinylbenzene.
     
    5. A method for producing a nucleic acid, comprising sequentially binding a nucleoside or nucleotide to the porous resin bead described in any one of claims 1 to 4 via cleavable linker, thereby obtaining an oligonucleotide.
     


    Ansprüche

    1. Poröses Harzkügelchen, umfassend ein Copolymer aus erster monovinylaromatischer Verbindung-Divinylverbindung-(Meth)acrylnitril-zweiter monovinylaromatischer Verbindung, wobei die zweite monovinylaromatische Verbindung eine Gruppe enthält, die zum Binden an eine Carboxylgruppe durch eine Dehydrierungs-Kondensationsreaktion fähig ist, wobei die Menge einer von dem (Meth)acrylnitril abgeleiteten Struktureinheit 1,8 bis 3 mmol/g beträgt und wobei das poröse Harzkügelchen ein Trockenvolumen von 2 bis 3 ml/g aufweist, bestimmt in Übereinstimmung mit in der Beschreibung bereitgestellten Angaben.
     
    2. In Anspruch 1 beschriebenes poröses Harzkügelchen, wobei es sich bei der Gruppe, die zum Binden an eine Carboxylgruppe durch eine Dehydrierungs-Kondensationsreaktion fähig ist, um eine Gruppe handelt, ausgewählt aus der Gruppe, bestehend aus einer Aminogruppe, einer Aminoalkylgruppe, einer Hydroxylgruppe und einer Hydroxyalkylgruppe.
     
    3. In Anspruch 1 oder 2 beschriebenes poröses Harzkügelchen, wobei eine Menge der Divinylverbindung basierend auf der Gesamtmenge der Monomere 2 bis 10 Mol-% beträgt.
     
    4. In einem der Ansprüche 1 bis 3 beschriebenes poröses Harzkügelchen, wobei es sich bei der Divinylverbindung um Divinylbenzol handelt.
     
    5. Verfahren zum Herstellen einer Nucleinsäure, umfassend das sequenzielle Binden eines Nucleosids oder Nucleotids an das in einem der Ansprüche 1 bis 4 beschriebene poröse Harzkügelchen mittels spaltbarem Linker, wodurch ein Oligonucleotid erhalten wird.
     


    Revendications

    1. Perle de résine poreuse comprenant un copolymère de premier composé monovinylique aromatique-composé divinylique-(méth)acrylonitrile-deuxième composé monovinylique aromatique, dans laquelle le deuxième composé monovinylique aromatique contient un groupe capable de se lier à un groupe carboxyle par une réaction de condensation avec déshydratation, dans laquelle la quantité d'un motif structural dérivé dudit (méth) acrylonitrile est de 1,8 à 3,0 mmol/g, et dans laquelle la perle de résine poreuse a un volume sec de 2 à 3 ml/g, déterminé conformément aux indications données dans la description.
     
    2. Perle de résine poreuse décrite dans la revendication 1, dans laquelle le groupe capable de se lier à un groupe carboxyle par une réaction de condensation avec déshydratation est un groupe choisi dans le groupe constitué par un groupe amino, un groupe aminoalkyle, un groupe hydroxyle et un groupe hydroxyalkyle.
     
    3. Perle de résine poreuse décrite dans la revendication 1 ou 2, dans laquelle la quantité du composé divinylique par rapport à la quantité totale des monomères est de 2 à 10 % en moles.
     
    4. Perle de résine poreuse décrite dans l'une quelconque des revendications 1 à 3, dans laquelle le composé divinylique est le divinylbenzène.
     
    5. Procédé pour préparer un acide nucléique, comprenant la liaison en séquence d'un nucléoside ou nucléotide à la perle de résine poreuse décrite dans l'une quelconque des revendications 1 à 4 par l'intermédiaire d'un groupe de liaison clivable, moyennant quoi on obtient ainsi un oligonucléotide.
     






    Cited references

    REFERENCES CITED IN THE DESCRIPTION



    This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

    Patent documents cited in the description




    Non-patent literature cited in the description