(19)
(11)EP 0 589 237 A2

(12)EUROPEAN PATENT APPLICATION

(43)Date of publication:
30.03.1994 Bulletin 1994/13

(21)Application number: 93113770.7

(22)Date of filing:  27.08.1993
(51)International Patent Classification (IPC)5C23C 14/02, B24C 1/00, H01J 37/16
(84)Designated Contracting States:
BE DE ES FR GB IT NL

(30)Priority: 27.08.1992 US 936433

(71)Applicant: APPLIED MATERIALS, INC.
Santa Clara California 95054-3299 (US)

(72)Inventors:
  • Banholzer, Thomas
    San Jose, CA 95119 (US)
  • Marohl, Dan
    San Jose, CA 95134 (US)
  • Tepman, Avi
    Cupertino, CA 95014 (US)
  • Mintz, Donald M.
    Sunnyvale, CA 94087 (US)

(74)Representative: Diehl, Hermann, Dr. Dipl.-Phys. et al
DIEHL, GLÄSER, HILTL & PARTNER Patentanwälte Flüggenstrasse 13
80639 München
80639 München (DE)


(56)References cited: : 
  
      


    (54)Vacuum etch chamber and method for treating parts thereof


    (57) Replaceable parts for a vacuum chamber including a lid (12), a door (16) and a shield (18), are treated to clean and roughen their surfaces to increase adhesion of materials deposited thereon during substrate processing in said chamber, thereby reducing downtime of the equipment. The parts (12,16,18) can be chemically cleaned, rinsed to remove the chemicals and dried in a first step. Then the parts are subjected to bead blasting to roughen the surface of the part and improve adhesion thereon of deposited material. In a succeeding step the parts are cleaned ultrasonically to remove all loose particles. And in an optional last step the parts are rinsed and dried to remove moisture. The parts can then be packaged or used. Furthermore, disclosed is a single-piece machined aluminum lid (12) which has an extension wall (14) from a first surface that fits into the door (16) of the chamber, and an overlying portion (13) of said first surface that optionally sealingly engages the door (16) when the lid (12) is closed.




    Description


    [0001] This invention relates to a vacuum chamber and a method for treating parts thereof.

    [0002] Vacuum chambers are well known and are employed in the semiconductor industry to etch and deposit thin films and form contacts in semiconductor substrates during manufacture of, inter alia, integrated circuits. State-of-the art processing chambers form a part of a system able to condition and preclean substrates for vacuum processing and process them without leaving a vacuum environment.

    [0003] However, a substrate preclean step, while it is effective in removing material adhered to the surface of the substrate, distributes this material on other surfaces within the vacuum chamber, e.g., on the walls or shields, lid and door of the chamber. In time there is a build up of this material that causes flakes to form on these surfaces that can deposit onto the substrate surface: At that point the chamber must be disassembled for cleaning.

    [0004] The present lid for a vacuum etch chamber comprises a two-piece aluminum lid separated by an RF gasket, which is a low resistance contact for the 60 MHz RF power supply for the vacuum chamber. Two aluminum plates are screwed together by a plurality of screws that fasten the two plates together so they make good contact to the RF gasket therebetween. As material builds up on the lid however, as described hereinabove, it must be periodically cleaned to remove the built up material. This is generally done by a wet chemical cleaning process which requires that the lid be disassembled, the screws removed, the lid cleaned and then the lid be reassembled. However, the act of assembly, e.g., inserting and fastening the screws, itself creates particles, so that the chamber is not clean, i.e., free of particles, even after the cleaning step. Other parts of the vacuum chamber, such as the door for the lid and a shield around the substrate support that prevents material from depositing on the walls of the chamber, must also be periodically cleaned; this adds to the downtime of the equipment and consequently increases costs of manufacture.

    [0005] Thus it would be desirable to have a vacuum chamber lid that does not have to be disassembled and assembled again for cleaning.

    [0006] It is therefore the object of the present invention to provide a vacuum chamber which avoids the above mentioned drawbacks. It is furthermore the object of the present invention to provide a method for manufacturing improved parts of a vacuum chamber.

    [0007] These objects are solved by the method according to independent claim 1 and the vacuum chamber according to independent claim 9. Further advantageous features, aspects and details of the invention are evident from independent claim 12, the dependent claims, the description and the drawings. The claims are to be understood as a first non-limiting approach to define the invention in general terms.

    [0008] This invention relates to improved replaceable parts for a vacuum chamber. More particularly, this invention relates to replaceable parts for a vacuum etch chamber that are pre-treated to extend the time for replacement. The pre-treatment of the parts of the vacuum chamber affects that particles generated in the vacuum chamber that adhere to the lid, door and shield surfaces have improved adherence to these surfaces with the result that the time between cleaning cycles can be extended, thereby reducing downtime of the equipment. The door and shield prevent particles, which are generated within the chamber, to reach the walls of the chamber and/or a further door within said chamber walls.

    [0009] The present invention furthermore provides a novel lid and door for a vacuum chamber comprising a single, machined aluminum plate that optionally sealingly engages a quartz ring or door, and, when the lid and door to the vacuum chamber are closed, in turn fits into a shield surrounding the substrate support. The novel, single-piece lid requires no screws, thereby preventing the generation of detrimental particles in the chamber, when assembling or disassembling the lid.

    [0010] The lid, shield and door replaceable parts are pre-treated so that particles generated within the chamber during precleaning of the substrate and processing thereof will better adhere to these surfaces, allowing more substrates to be processed before the vacuum chamber needs to be taken apart and cleaned or parts replaced. This pre-treatment comprises a bead blasting step that creates an irregular surface in the aluminum and quartz materials of the replaceable parts, e.g., lid, door and shield respectively, to which materials or particles generated in the chamber adhere better than on a smooth surface, followed by removal of all particles remaining on the surface after the bead blasting step by an ultrasonic cleaning step of the replaceable parts. This pre-treatment produces aluminum and quartz door/lid/shield combinations that have a long lifetime in a vacuum processing chamber.

    [0011] Figure 1a is a cross sectional view showing parts of a vacuum processing chamber according to one embodiment of the invention.

    [0012] Figure 1b is a cross sectional view showing parts of another embodiment of a vacuum processing chamber according to the invention.

    [0013] Figure 2 is flow chart for the process of the invention.

    [0014] Figure 1a illustrates one embodiment of the invention showing a one piece aluminum lid of the invention, a quartz door therefor and a quartz substrate support shield for a vacuum processing chamber. The lid is opposed to the cathode within the chamber on which the substrate to be treated is placed during processing. The lid, the door and the shield of this embodiment have been pre-treated in accordance with the process of the invention.

    [0015] An extension wall 14 of a lid 12 fits inside a quartz door 16. When the lid 12 is in place and the door 16 is closed, the door 16 fits atop a quartz shield 18 which is shaped to surround a cathode 17 onto which the substrate to be processed is located during processing. The door 16 is raised and lowered with lid 12 stationary by an externally driven actuator. At the same time the door 16 is raised and lowered, ceramic fingers (not shown), which pass through slots in the quartz shield 18, raise and lower the substrate onto the cathode 17. This occurs during the transfer of substrates into and out of the chamber. The fixed quartz shield 18 serves to prevent material etched from the substrate from adhering to the walls of the vacuum chamber (not shown). The lid 12 also has an overlying portion 13 of said first surface that contacts and seals the door during processing. A suitable O-ring seal (not shown) conventionally is used to seal the chamber when a vacuum is drawn.

    [0016] Figure 1b illustrates a further embodiment of the invention where a one piece aluminum lid, a quartz door therefor and a quartz substrate support shield for a vacuum processing chamber are shown. The lid is opposed to the cathode within the chamber on which the substrate to be treated is placed during processing. The lid, the door and the shield have been pre-treated in accordance with the process of the invention.

    [0017] The extension wall 14 and the quartz shield 18 fit inside a quartz door 16. The quartz shield 18 is shaped to surround the cathode 17 onto which the substrate to be processed is located during processing. The door 16 is raised and lowered with lid 12 stationary by an externally driven actuator. At the same time the door 16 is raised and lowered, ceramic fingers (not shown), which pass through slots in the quartz shield 18, raise and lower the substrate onto the cathode 17. This occurs during the transfer of substrates into and out of the chamber. The fixed quartz shield 18, the extension wall 14 and the quartz door 16 serve to prevent material etched from the substrate from adhering to the walls of the vacuum chamber (not shown). The lid 12 also has an overlying portion 13 of said first surface. The lid 12 need not sealingly engage with the door during processing.

    [0018] The aluminum lid 12, the quartz door 16 and shield 18 are pre-treated in accordance with the cleaning process of the invention, described in greater detail hereinbelow.

    [0019] The novel lid of the invention requires no screws, thereby generating fewer particles in a vacuum preclean or processing chamber; has a pre-treated surface to which particles generated during processing better adhere; does not require an RF gasket, resulting in better grounding of the lid; and no assembly or disassembly of the lid is required for cleaning or replacement. A simple replacement of the lid and the door can be effected when required, reducing the downtime of the equipment. The lid, door and shield also can be readily re-cleaned and retreated for reuse in any suitable vacuum chamber. Aluminum parts and quartz parts are recycle-cleaned by a combination of bead blasting and chemical cleaning steps. The last step in both cases is a bead blasting step followed by ultrasonic processing in deionized water, rinsing and drying as explained further hereinbelow.

    [0020] The pretreatment process of the invention comprises a bead blasting step followed by an ultrasonic cleaning step.

    [0021] The bead blasting step treatment of the aluminum lid and the quartz door is suitably effected by bombarding the lid, the door and the shield using about 552kPa (about 80 psi) of pressure and aluminum oxide powder having a rather coarse grit, suitably about 590-177µm (about 36-80 grit) in size. Bead blasting can be carried out in commercially available bead blasting equipment. The bead blasting powder particles must be large enough to make the aluminum surface of the lid and the quartz door and shield surfaces slightly irregular or roughened. The machined one-piece aluminum lid can withstand bead blasting with coarser grit size material because it is thicker than the prior art two-plate aluminum sheet metal lid, and thus it is more durable. The irregular surfaces, on a microscopic scale, will enhance interface crack propagation of material that may be deposited during substrate processing. The surface irregularities will result in the breaking up of the deposited films into sections that are small with respect to flake sizes, which significantly hinders flaking. In addition, the irregular or roughened surfaces have an increased surface area to which material can deposit, increasing the amount of deposited material that can be accommodated.

    [0022] The bead blasting step is followed by an ultrasonic cleaning step that removes all loose particles on the surfaces of the lid, door and shield, whether they are due to particles remaining from the head blasting, or minute particles of aluminum, quartz, dust particles and the like. The lid, door and shield are first rinsed with deionized water and immersed in an ultrasonic cleaner filled with deionized water. Suitable ultrasonic cleaners are commercially available and are generally set to run at power densities of from about 9 - 19 Watt/l (about 35-70 Watts/gallon) using a chamber containing about 38 l (about 10 gallons) of deionized water for several minutes. As soon as the ultrasonic generator is turned on, a cloud of formerly embedded solid residue is seen to form over the bead blasted surfaces from which it originated. This cloud quickly dissipates and the solid material removed either remains in aqueous suspension or settles out. Thus, most of the activity of ultrasonic processing occurs during the initial few seconds of treatment. Treatment is usually continued for about 5 minutes however, in order to assure thorough removal of all loose solid material. The parts are then thoroughly rinsed with hot deionized water to ensure that no particles remain on the surfaces of the treated aluminum and quartz parts.

    [0023] Lastly, the aluminum lid and quartz door and shield parts may be dried to remove all moisture from their surfaces. Suitably the parts can be blown dry with filtered air or nitrogen and then lightly baked, e.g., at about 60°C for one-half hour in filtered air atmosphere to remove all moisture from the parts. The cleaned parts can then be packed for shipment.

    [0024] In a preferred cleaning process, prior to the bead blasting step the parts are chemically cleaned to remove surface contamination, such as oxides from the aluminum and organics from the quartz surfaces. A suitable chemical cleaning solution for ceramics for example can be 1/3 nitric acid, 1/3 hydrofluoric acid and 1/3 water. Dipping the part in the chemical cleaning solution for about 15 seconds is generally sufficient. The part is then rinsed with deionized water to remove the chemicals and blown dry using clean, filtered air or nitrogen.

    [0025] Figure 2 is a flow chart of a preferred embodiment of the process of the invention, showing the chemical clean first step, followed by a bead blasting step, an ultrasonic cleaning step, and lastly the part finished by rinsing and drying and packaging the part.

    [0026] Treating the lid and quartz parts of the vacuum chamber in accordance with the process of the invention, and utilizing the simplified, sturdier lid of the present invention, results in a cleaner vacuum chamber, one that can process more substrates than prior art chamber, reducing downtime of the equipment, and also provides a fast and low cost method of cleaning the chambers, and replacing the above-described parts.

    [0027] Although the above invention has been described in terms of certain presently preferred embodiments, one skilled in the art will know of alternative embodiments of processing and equipment which are meant to be included herein. For example, although semiconductor substrates are generally silicon wafers which are circular in cross section, resulting in shields and cathode supports that are also circular in cross section, other substrates such as rectangular glass plates can also be employed. Other materials can be substituted for aluminum, such as stainless steel; and other cleaning and rinsing steps inserted into the process for particular results. The invention is only meant to be limited by the appended claims.


    Claims

    1. A process for treating replaceable parts in a vacuum etch chamber comprising the following steps:

    a). bead blasting the surface of the part to roughen the surface; and

    b) ultrasonically cleaning the part to remove surface particles.


     
    2. The process according to claim 1, further comprising the step of rinsing and drying the part.
     
    3. The process according to claim 1 or 2, wherein the parts are first cleaned with a chemical cleaning solution.
     
    4. The process according to one of the preceding claims, wherein one of the parts is an aluminum single-piece lid for the vacuum chamber.
     
    5. The process according to one of claims 1 to 3, wherein one or more parts are made of quartz.
     
    6. The process of one of the preceding claims wherein the bead blasting step is carried out using a pressure of about 552kPa (about 80 psi).
     
    7. The process of one of the preceding claims, wherein the blasting step is carried out with aluminum oxide powder.
     
    8. The process according to claim 7, wherein the aluminum has a size of about 590 to 177 µm (about 36 to 80 grit).
     
    9. A vacuum chamber having an opening therein which can be closed, a cathode support (17) for a substrate to be processed within said chamber and replaceable parts including a shield (18) surrounding said cathode support, a door (16), which can fit into said shield (18), and a single-piece lid (12) for said shield (18), said replaceable parts being obtainable by treating same according to one of the processes of claims 1 to 7.
     
    10. The vacuum chamber according to claim 9, wherein said shield (18) is a quartz shield, said door (16) is a quartz door and said single-piece lid (12) is an aluminum lid.
     
    11. The vacuum chamber according to one of claims 9 or 10, wherein said single-piece lid (12) has an overlying portion (13) that, optionally sealingly, engages said door (16).
     
    12. A single-piece machined lid (12) for a vacuum etch chamber having an extension wall (14) from and an overlying portion (13) of a first surface that optionally sealingly engages a door (16) of said chamber when the lid (12) is closed.
     
    13. The single-piece machined lid (12) according to claim 12, wherein the lid is made from aluminum.
     
    14. The single-piece machined lid according to one of claims 12 or 13, being obtainable by treating same in accordance with the methods of one of claims 1 to 8.
     




    Drawing