(11)EP 0 422 900 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
16.03.1994 Bulletin 1994/11

(21)Application number: 90311058.3

(22)Date of filing:  09.10.1990
(51)International Patent Classification (IPC)5G02F 1/35, C07D 263/36, C07D 277/34, C07D 233/32, C07D 307/58

(54)

Organic nonlinear optical material and nonlinear optical element

Organisches Material für die nichtlineare Optik und nichtlineare optische Vorrichtung

Matériau organique pour l'optique non-linéaire et élément d'optique non-linéaire


(84)Designated Contracting States:
DE FR GB

(30)Priority: 09.10.1989 JP 262052/89
27.03.1990 JP 75412/90

(43)Date of publication of application:
17.04.1991 Bulletin 1991/16

(73)Proprietor: KABUSHIKI KAISHA TOSHIBA
Kawasaki-shi, Kanagawa-ken 210 (JP)

(72)Inventors:
  • Kawamonzen, Yoshiaki, c/o Intellect. Property Div.
    Minato-ku, Tokyo 105 (JP)
  • Mori, Yasushi, c/o Intellectual Property Div.
    Minato-ku, Tokyo 105 (JP)

(74)Representative: Sturt, Clifford Mark et al
MARKS & CLERK 57-60 Lincoln's Inn Fields
London WC2A 3LS
London WC2A 3LS (GB)


(56)References cited: : 
EP-A- 0 335 641
GB-A- 2 083 239
DE-A- 3 707 835
US-A- 4 727 155
  
      
    Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


    Description


    [0001] The present invention relates to a novel organic nonlinear optical material and a nonlinear optical element having this organic nonlinear optical material and available for generating short wavelength light by conversion of laser beam into second harmonic wave.

    [0002] Light communication and light information processing are expected as basic technologies for development of information society in future. It is essential for these technologies to establish means for properly controlling wavelength, amplitude, and phase of laser beam, in other words harmonic generation, light switching, and light mixing, for example. Utilization of nonlinear optical effect is quite advantageous in controlling properties of light at fast speed.

    [0003] Conventionally, inorganic ferroelectric crystals, for example bulk crystals made of LiNbO₃ or KTP, are used to the conversion of wave length for either a YAG laser or a dye laser. However, these inorganic materials cannot sufficiently yield the desired non-linear optical effect. Because of this reason, they are merely used for high-output lasers, but they are not applied to low-output semiconductor lasers which are developed in recent years.

    [0004] On the other hand, recently, a variety of organic compounds have been found, which have far greater nonlinear optical constant than that of inorganic crystals and excellent durability against optical damage. It is expected that utilization of these organic nonlinear optical materials will lead to elements capable of generating a sufficient second harmonic wave for low-output semiconductor lasers.

    [0005] There are a number of technical papers on the organic nonlinear optical material including the following: "Nonlinear Optical Properties of Organic and Polymeric Materials", by D.J. Williams et al., published by American Chemical Society, in 1983, and "Nonlinear Optical properties of Organic Molecules and Crystals", by D.S. Chelma and J. Zyss, published by Academic Press, in 1987, for example.

    [0006] The feature in molecular structure of such organic nonlinear optical materials is that an electron-releasing group and an electron-withdrawing group are attached to π-electron system like benzene ring at opposite positions for each other.

    [0007] However, dipole moment in the ground state inevitably increases as to these organic nonlinear optical materials having the above-mentioned molecular structure. In a solid made of molecules having large dipole moment, energetical stability is obtained when the molecules are aligned with directing their dipole moments in opposite directions for each other, and thus the molecules are likely to be crystallized in the form of centrosymmetry. With regard to the centrosymmetrical crystals, second harmonic generation is inhibited in principle. Nonlinear characteristic is promoted in such molecules having widely spread π-electron system. On the other hand, absorption band of the molecules superposes the wavelength of the fundamental wave or the second harmonic wave to retard effective second harmonic generation.

    [0008] Furthermore, like the case of using inorganic compound, if a nonlinear optical element is manufactured by using a bulk crystal made of organic nonlinear optical material, there are some problems as described below. First, in order to produce bulk crystal made of organic nonlinear optical material, those processes rarely applicable to organic materials must be executed, which include growth, cutting, and polishing of single-crystals. Crystals of organic compound are in general molecular crystals containing weakly bonded molecules, in other words, have weaker mechanical strength than that of inorganic crystals, and thus much difficulty is involved in the execution of the above-mentioned processes.

    [0009] Furthermore, when operating the wavelength converting element composed of bulk crystals, it is essential to attain phase matching by compensating for the difference of phase velocity between the fundamental wave and the harmonic wave by means of double refraction of crystals. However, even when using such crystals capable of most efficiently utilizing β₃₃₃ component which is presumably the largest nonlinear polarizability tensor component in terms of molecular level of organic compound, since the directions of the electric field vectors of the fundamental wave and second-harmonic wave are identical to each other, phase matching can hardly be attained.

    [0010] The object of the invention is to provide organic nonlinear optical material which shows distinctive nonlinear optical characteristic and efficiently generates second harmonic, and also provide a nonlinear optical element capable of efficiently generating second harmonic by applying the above organic nonlinear optical material.

    [0011] The organic nonlinear optical material according to the invention consists of a compound according to Formula (I) shown below:


    where Z₁ is O, S, Se, Te, SO₂ group or NR₁ group;
       Z₂ is N or CR₂ group;
       Y is O, S or NR₃ group;
       X is CR₄R₅ group, NR₆ group, O or S; and
       R, R₁, R₂, R₃, R₄, R₅, R₆ may be identical to or different from each other, and each of them is heterocyclic group, aromatic hydrocarbon group, or aliphatic hydrocarbon group, which may be unsubstituted or substituted, or characteristic group or H, where R₄ and R₅ may jointly form a carbocyclic or a heterocyclic ring.

    [0012] The nonlinear optical element of the invention is provided with a hollow optical fiber and a single-crystal of the above-mentioned organic nonlinear optical material filled in the hollow space of the optical fiber.

    [0013] The organic nonlinear optical material of the invention can easily be synthesized, absorbs light having relatively short wavelength, shows distinctive nonlinear optical characteristic, and efficiently generates second harmonic. Accordingly, the organic nonlinear optical material of the invention is applicable to not only second harmonic generation but to the optoelectronics utilizing nonlinear phenomena like high-speed light shutters or modulator and optical bistable devices and so on.

    [0014] The nonlinear optical element according to the invention can easily be manufactured, and generates second harmonic with high efficiency.

    [0015] This invention can be more fully understood from the following detailed description when taken in conjunction with the accompanying drawings, in which:

    Fig. 1 is the sectional view of the nonlinear optical element according to an example of the invention; and

    Fig. 2 is a simplified diagram of an apparatus for measuring the efficiency of second harmonic generation by the nonlinear optical element according to an example of the invention.



    [0016] Referring to the foregoing general formula (I), there are a variety of heterocyclic compounds for making up basic structure determinable by combination of Z₁, Z₂, and Y, including the following:

    (1) Those heterocyclic ketone compounds shown in A to H in Table 1 including 5-oxazolone, 5-thiazolone, 5-imidazolone, 5-thiazolone-1,1-dioxide, 3H-fran-2-one, 3H-thiophen-2-one, 3H-pyrrol-2-one, and 3H-thiphen-2-one-1, 1-dioxide.

    (2) Those heterocyclic thioketone compound in which O of carbonyl group of those compounds shown in the above category (1) is substituted with S.

    (3) Those heterocyclic Schiff compounds in which O of carbonyl group of those compounds shown in the above category (1) is substituted with NR₃ group.



    [0017] Referring to the foregoing general formula (I), examples of unsubstituted heterocyclic group, aromatic hydrocarbon group, aliphatic hydrocarbon group, and alicyclic group, which are introduced as R, and R₁ to R₆ are cited below.

    [0018] Examples of the heterocyclic group are as follows; pyrrole ring, pyrroline ring, pyrrolidine ring, indole ring, isoindole ring, indoline ring, isoindoline ring, indolizine ring, carbazole ring, carboline ring, furan ring, oxolane ring, coumarone ring, coumaran ring, isobenzofuran ring, phthalan ring, dibenzofuran ring, thiophene ring, thiolane ring, benzothiophene ring, dibenzothiophene ring, pyrazole ring, pyrazoline ring, indazole ring, imidazole ring, imidazoline ring, imidazolidine ring, benzimidazole ring, benzimidazoline ring, naphthimidazole ring, oxazole ring, oxazoline ring, oxazolidine ring, benzoxazole ring, benzoxazoline ring, naphthoxazole ring, isoxazole ring, benzisoxazole ring, thiazole ring, thiazoline ring, thiazolidine ring, benzothiazole ring, benzothiazoline ring, naphthothiazole ring, isothiazole ring, benzisothiazole ring, triazole ring, benzotriazole ring, oxadiazole ring, thiadiazole ring, benzoxadiazole ring, benzothiadiazole ring, tetrazole ring, purine ring, pyridine ring, piperidine ring, quinoline ring, isoquinoline ring, acridine ring, phenanthridine ring, benzoquinoline ring, naphthoquinoline ring, naphthyridine ring, phenanthroline ring, pyridazine ring, pyrimidine ring, pyrazine ring, piperazine ring, phthalazine ring, quinoxaline ring, quinazoline ring, cinnoline ring, phenazine ring, perimidine ring, triazine ring, tetrazine ring, pteridine ring, oxazine ring, benzoxazine ring, phenoxazine ring, thiazine ring, benzothiazine ring, phenothiazine ring, oxadiazine ring, thiadiazine ring, dioxolane ring, benzodioxole ring, dioxane ring, benzodioxane ring, dithiolane ring, benzodithiole ring, dithiane ring, benzodithiane ring, pyran ring, chromene ring, xanthene ring, oxane ring, chroman ring, isochroman ring, trioxane ring, thian ring, trithian ring, morpholine ring, quinuclidine ring, selenazole ring, benzoselenazole ring, naphthoselenazole ring, tellurazole ring, benzotellurazole ring, and so on.

    [0019] Examples of aromatic hydrocarbon group are as follows: phenyl, naphthyl, anthryl, phenanthryl, tetralinyl, azulenyl, biphenylenyl, acenaphthylenyl, acenaphthenyl, fluorenyl, triphenylenyl, pyrenyl, chrysenyl, picenyl, perylenyl, benzopyrenyl, rubicenyl, coronenyl, ovalenyl, indenyl, pentalenyl, heptalenyl, indacenyl, phenalenyl, fluoranthenyl, acephenanthrylenyl, aceanthrenyl, naphthacenyl, pleiadenyl, pentaphenyl, pentacenyl, tetraphenylenyl, hexaphenyl, hexacenyl, trinaphthylenyl, heptaphenyl, heptacenyl, pyranthrenyl, and so on.

    [0020] Examples of aliphatic hydrocarbon group are as follows: methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, tert-butyl, pentyl, tert-pentyl, isopentyl, neopentyl, hexyl, isohexyl, heptyl, octyl, nonyl, decyl, vinyl, allyl, isopropenyl, propenyl, methallyl, crotyl, ethynyl, propynyl, butenyl, butynyl, pentenyl, pentynyl, butadienyl, and so on.

    [0021] Examples of alicyclic hydrocarbon group, are as follows: cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclopentenyl, cyclohexenyl, cycloheptenyl, cyclooctenyl, cyclopentadienyl, cyclohexadienyl, and so on.

    [0022] Referring to the foregoing general formula (I), examples of characteristic group introduced as R, and R₁ to R₆ are as follows: disubstituted amino group, for example, dimethylamino, diethylamino, dibutylamino, ethylmethylamino, butylmethylamino, diamylamino, dibenzylamino, diphenethylamino, diphenylamino, ditolylamino, dixylylamino, methylphenylamino, and benzylmethylamino; monosubstituted amino group, for example, methylamino, ethylamino, propylamino, isopropylamino, tert-butylamino, anilino, anisidino, phenetidino, toluidino, xylidino, pyridylamino, thiazolylamino, benzylamino, and benzylideneamino; cyclic amino group, for example, pyrrolidino, piperidino, morpholino, 1-pyrrolyl, 1-pyrazolyl, 1-imidazolyl, and 1-triazolyl; acylamino group, for example, formylamino, acetylamino, benzoylamino, cinnamoylamino, pyridinecarbonylamino, and trifluoroacetylamino; amino group; hydroxyamino group; ureido group; semicarbazido group; carbazido group; disubstituted hydrazino group, for example, dimethylhydrazino, diphenylhydrazino, and methylphenylhydrazino; monosubstituted hydrazino group, for example, methylhydrazino, phenylhydrazino, pyridylhydrazino, and benzylidenehydrazino; hydrazino group; azo group, for example, phenylazo, pyridylazo, and thiazolylazo; azoxy group; amidino group; aminocarbonyl group, for example, carbamoyl, methylcarbamoyl, phenylcarbamoyl, pyridylcarbamoyl, carbazoyl, allophanoyl, oxamoyl, and succinamoyl; cyano group; cyanato group; thiocyanato group; nitro group; nitroso group; oxy group, for example, methoxy, ethoxy, propoxy, butoxy, hydroxyethoxy, phenoxy, naphthoxy, pyridyloxy, thiazolyloxy, and acetoxy; hydroxy group; thio group, for example, methylthio, ethylthio, phenylthio, pyridylthio, and thiazolylthio; mercapto group; halogen group, for example fluoro, chloro, bromo, and iodo; carboxyl group and its salt; oxycarbonyl group, for example, methoxycarbonyl, ethoxycarbonyl, phenoxycarbonyl, and pyridyloxycarbonyl; thiocarboxyl group and its salt; dithiocarboxyl group and its salt; thiocarbonyl group, for example, methoxythiocarbonyl, methylthiocarbonyl, and methylthiothiocarbonyl; acyl group, for example, formyl, acetyl, propionyl, acryloyl, benzoyl, cinnamoyl, pyridinecarbonyl, thiazolecarbonyl, and trifluoroacetyl; thioacyl group, for example, thioformyl, thioacetyl, thiobenzoyl, and pyridinethiocarbonyl; sulfinic acid group and its salt; sulfonic acid and its salt; sulfinyl group, for example, methylsulfinyl, ethylsulfinyl, and phenylsulfinyl; sulfonyl group, for example, methylsulfonyl, ethylsulfonyl, phenylsulfonyl, pyridylsufonyl, tosyl, tauryl, trifluoromethylsulfonyl, sulfamoyl, methylsulfamoyl, sulfanilyl, and acetylsulfanilyl; organosilicic group, for example silyl, disilanyl, trimethylsilyl, and triphenylsilyl; sulfonylamino group, for example, mesylamino, ethylsulfonylamino, phenylsulfonylamino, pyridylsulfonylamino, tosylamino, taurylamino, trifluoromethylsulfonylamino, sulfamoylamino, methylsulfamoylamino, sulfanilylamino, and acetylsulfanilylamino; oxysulfonyl group, for example, methoxysulfonyl, ethoxysulfonyl, phenoxysulfonyl, acetaminophenoxysulfonyl, and pyridyloxysulfonyl; thiosulfonyl group, for example, methylthiosulfonyl, ethylthiosulfonyl, phenylthiosulfonyl, acetaminophenylthiosulfonyl, and pyridylthiosulfonyl; aminosulfonyl group, for example, methylsulfamoyl, dimethylsulfamoyl, ethylsulfamoyl, diethylsulfamoyl, phenylsulfamoyl, acetaminophenylsulfamoyl, and pyridylsulfamoyl; halogenated alkyl group, for example, chloromethyl, bromomethyl, fluoromethyl, dichloromethyl, dibromomethyl, difluoromethyl, trifluoromethyl, pentafluoroethyl, and heptafluoropropyl; and so on.

    [0023] Referring to the foregoing general formula (I), examples of a carbocyclic and a heterocyclic ring can be jointly formed by R₄ and R₅ are as follows: cyclopropane ring, cyclobutane ring, cyclopentane ring, cyclohexane ring, cycloheptane ring, cyclooctane ring, cyclopentene ring, cyclohexene ring, cycloheptene ring, cyclooctene ring, cyclopentadiene ring, cyclohexadiene ring, indan ring, indene ring, tetralin ring, fluorene ring, anthrone ring, oxane ring, thiane ring, piperidine ring, piperazine ring, morpholine ring, oxazoline ring, thiazoline ring, imidazoline ring, isoxazoline ring, isothiazoline ring, pyrazoline ring, benzoxazoline ring, benzothiazoline ring, benzimidazoline ring, benzisoxazoline ring, benzisothiazoline ring, benzothiazoline ring, dihydropyridine ring, dihydroquinoline ring, and so on.

    [0024] Referring again to the foregoing general formula (I), the above-mentioned heterocyclic, aromatic hydrocarbon, aliphatic hydrocarbon, and alicyclic hydrocarbon, which are as cited unsubstituted one may be substituted with characteristic group, hydrocarbon group (for example, alkyl, aryl, alkenyl, and alkynyl), and heterocyclic cited above.

    [0025] Table 2 R1 through R80 respectively designate examples of the substituent R introduced to the above general formula (I).

    [0026] Table 3 X1 through X160 respectively designate examples of the substituent X introduced to the above general formula (I).









































    [0027] Those compounds represented by the foregoing general formula (I) respectively contain heterocyclic π electrons in the central portion, whereas an electron-withdrawing group and an electron-releasing group are disposed on two sides. As a whole, each of these compound has such a structure characteristically being curved in bow shape. Such a compound has substantial nonlinear polarization. However, since the distance between the electron-withdrawing group and the electron-releasing group is short in correspondence with the length of the bow-string, dipole moment in the ground state is small. In consequence, any of these compounds cannot easily enter into centrosymmetrical structure in a solid state. This in turn does not inhibit second harmonic generation.

    [0028] In accordance with the molecular structure of the compound, a variety of characteristics can be generated from the compounds embodied by the invention. For example, a consideration is hereby given to such a compound wherein Z₁ is O, S or NR₁ group; Z₂ is N; Y is O; X is CR₄R₅ group, where either R₄ or R₅ is an electron-releasing group; and R is a substantially neutral substituent related to withdrawing and releasing of electrons (neither electron-withdrawing nor electron-releasing). In this case, if aryl group is selected for R, intensity of the second harmonic wave is substantially promoted, whereas absorption of the molecule shifts to the longer-wavelength side. On the other hand, if alkyl group is selected for R, intensity of the second harmonic wave is not noticeably promoted, whereas the absorption of the molecule shifts to the shorter-wavelength side.

    [0029] In the same way, a consideration is also given to another compound wherein; Z₁ is O, S, or NR₁ group; Z₂ is N; Y is O; X is CR₄R₅ group, where R₄ and R₅ are both substantially neutral substituent related to the withdrawing and releasing of electrons; and R is electron-withdrawing group. In this case, if aryl group is selected for R₄ or R₅, intensity of the second harmonic is substantially promoted, whereas absorption of molecules shifts to the longer-wavelength side. On the other hand, if alkyl group is selected for R₄ or R₅, intensity of the second harmonic wave is not noticeably promoted, whereas the absorption of molecules shifts to the shorter-wavelength side.

    [0030] Accordingly, it is desired that molecular structure of compound can be modified in accordance with the needed characteristic when applying the above compounds to a nonlinear optical element.

    [0031] Generally, the compound expressed by the foregoing general formula (I) can be synthesized by dehydrating and condensing keton, thioketone, or keton-imide, which have active methylene group, with carbonyl compound or isonitroso compound. More particularly, in accordance with the basic structure of the objective compound, a variety of synthesis methods can be available, for example, including the following:

    [0032] As described by J.S. Buck et al., in Org. Synth., 13, 8 (1933), 5-oxazolone derivative can be synthesized by dehydrating and condensing N-acylglycine and carbonyl compound.

    [0033] As described by J.B. Jepson et al., in J. Chem. Soc., 1955, 1791 (1955), 5-thiazolone derivative can be synthesized by dehydrating and condensing N-thioacylglycine and carbonyl compound.

    [0034] As described by H. Lehr et al., in J. Am. Chem. Soc., 75, 3640 (1953), 5-imidazolone derivative can be synthesized by dehydrating and condensing 4,4-dihydro-5-imidazolone compound and carbonyl compound. Likewise, as described by C. Granacher et al., in Helv. Chem. Acta., 10, 819 (1927), 5-imidazolone derivative can also be synthesized by reacting 4-arylidene-5-oxazolone with amino compound.

    [0035] Also, as described by L. S. E1-Assal et al., in J. Chem. Soc., 1961, 1658 (1961), 3H-furan-2-one derivative can be synthesized by dehydrating and condensing β-acylpropionic acid and carbonyl compound.

    [0036] The nonlinear optical element of the invention can be manufactured by executing those sequential processes described below. First, one end of a hollow optical fiber is immersed in melted organic nonlinear optical material, thereby filling up hollow space of the fiber with the melt availing of capillarity, and then the melt-filled fiber is cooled to solidify the melt. Next, the fiber is heated and gradually cooled to crystallize the organic nonlinear optical material.

    [0037] The nonlinear optical element of the invention is substantially made of optical fiber incorporating the organic nonlinear optical material as a core. When operating the nonlinear optical element of the invention, since the Cerenkov phase matching can be attained between the guiding mode of the incident fundamental wave in the core and the radiation mode of the second harmonic from the core to the clad, the nonlinear optical element of the invention can securely generate second-harmonic wave with extremely high efficiency.

    [0038] Now, based on examples, detail of the invention is described below.

    [0039] First, examples of synthesis of typical heterocyclic compounds available for the organic nonlinear optical material of the invention are shown below.

    [0040] Tables 4 to 7 respectively designate the synthesized compounds by combining the following; basic structure which is designated by respective notations (like A, ..., E), R which is designated by abbreviation of substituent and the symbol in Table 2, and X which is designated by a combination of R₄ (H-) and abbreviation or name of substituent R₅, and the symbol in Table 3.

    Synthesis of 5-oxazolone derivative



    [0041] 10 mℓ (106 mmol) of acetic anhydride was added to 33 mmol of N-acylglycine, 30 mmol of aldehyde, and 2.5 g (30 mmol) of sodium acetate anhydride or sodium hydrogencarbonate anhydride. The mixture was stirred and heated at 100°C for an hour, and was further stirred at room temperature for 4 to 5 hours. After cooling, the reaction solution was poured into water to precipitate crystals. The precipitated crystals were filtrated and washed with water. The coarse crystals were recrystallized twice from acetic acid, acetone or ethanol, thus the objective compound was obtained. Melting points of respective compounds are shown in Table 4.

    Synthesis of 5-thiazolone derivative



    [0042] 10 mℓ (106 mmol) of acetic anhydride was added to 33 mmol of N-thioacylglycine, 30 mmol of aldehyde, and 2.5 g (30 mmol) of sodium acetate anhydride or sodium hydrogencarbonate anhydride. The mixture was stirred and heated at 100°C for an hour, and was further stirred at room temperature for 4 to 5 hours. After cooling, the reaction solution was poured into water to precipitate crystals. The precipitated crystals were filtrated and washed with water. The coarse crystals were recrystallized twice from acetic acid, acetone or ethanol, thus the objective compound was obtained. Melting points of respective compounds are shown in Table 5.

    Synthesis of 5-imidazolone derivative



    [0043] 

    (A)
    33 mmol of 4,4-dihydro-5-imidazolone compound, 30 mmol of aldehyde, and 1.0 mℓ (10 mmol) of piperidine were dissolved in 20 mℓ of toluene or ethanol, and then the mixture was stirred and heated at 70°C for 5 hours. After cooling, the reaction solution was concentrated under reduced pressure, and then the residue was recrystallized twice from acetic acid, acetone or ethanol, thus the objective compound was obtained.

    (B)
    20 mmol of 4-arylidene-5-oxazolone derivative was dissolved in 50 mℓ of ethanol, and then 100 mmol of amino compound was added to the mixture. The mixture was refluxed for an hour. The reaction solution was cooled to precipitate crystals. The precipitated coarse crystals were filtrated and washed with water. The coarse crystals were recrystallized from ethanol, thus β-aryl-α-(N-acylamino) acrylamide derivative was obtained. The derivative was heated at 170°C to 180°C under reduced pressure, and cooled to precipitate crystals. The coarse crystals were recrystallized twice from acetic acid, acetone or ethanol, thus the objective compound was obtained.



    [0044] Melting points of respective compounds are shown in Table 6.

    Synthesis of 3H-furan-2-one derivative



    [0045] 10 mℓ (106 mmol) of acetic anhydride was added to 33 mmol of β-acylpropionic acid, 30 mmol of aldehyde, and 2.5 g (30 mmol) of sodium acetate anhydride or sodium hydrogencarbonate anhydride. The mixture was stirred and heated at 100°C for an hour, and was further stirred at room temperature for 4 to 5 hours. After cooling, the reaction solution was poured into water to precipitate crystals. The precipitated crystals were filtrated and washed with water. The coarse crystals were recrystallized twice from acetic acid, acetone or ethanol, thus the objective compound was obtained. Melting points of respective compounds are shown in Table 7.

    Examples 1 to 20



    [0046] With respect to the obtained 5-oxazolone derivatives, 5-thiazolone derivatives, 5-imidazolone derivatives, and 3H-furan-2-one derivatives, the second-order nonlinear optical characteristic was evaluated by powder method, as follows. Crystal powder of respective compounds was ground with an agate mortar. Each powder was sieved to adjust particle size to a range from 100 to 150 microns. Each powder was sandwitched between a couple of glass slides, thus samples for measurement were prepared. Then, the fundamental wave (having 1.064 µm of wave length) of an Nd-YAG laser was irradiated against each sample, and the intensity of second harmonic (SH) light in reflective light was measured. High-purity urea powder was used as the reference sample. SH intensity of respective samples was normalized with SH intensity of urea powder. Results of the measurement are shown in Table 8. Table 8 also designates the maximum absorption wavelength in visible-ultraviolet spectrum.










    Examples 21 to 25



    [0047] An example of the optical-fiber type nonlinear optical element of the present invention is described below. Fig. 1 is the sectional view of the nonlinear optical element. The nonlinear optical element 1 comprises clad 2 composed of a quartz-made hollow fiber having 100 µm of external diameter, 2 µm of internal diameter, and 100 mm of length, and core 3 made of singlecrystal of the compound represented by the foregoing general formula (I). A reflection preventive film 4 against incident fundamental wave is formed on the surface of one end of the nonlinear optical element 1, whereas a reflection preventive film 5 against the generated second-harmonic wave is formed on the surface of the other end.

    [0048] The nonlinear optical element having the above-mentioned structure was manufactured in accordance with sequential processes described below. Those compounds (shown in Table 9 by numbers in Tables 4 to 7) represented by the foregoing general formula (I) were melted, and held at such temperature 10°C higher than the melting points of respective compounds. One end of the quartz-made hollow fiber was immersed in each melt, thereby filling up the hollow space with the melt availing of capillarity. The melt-filled fiber was removed from the melt, and then quickly cooled to solidify the melt filled in the hollow space. At this point, the compounds were in a state of fine crystals. In order to prevent these compounds from being oxidized, these processes were executed in a nitrogen glove box.

    [0049] Each fiber filled with fine crystals in its hollow space was conveyed in a furnace held at temperature 10°C higher than the melting point of each compound, and then gradually extracted from the furnace. The compound was crystallized at the extracted portion, and as a result, singlecrystal of each compound grew up in the hollow space of the fiber. Optimal rate of extracting the fiber from the furnace is variable corresponding to the kind of the compounds. Therefore, the optimal extracting rate was preliminarily determined, by observing quality of crystals formed under various extracting rate with a polarized microscope. In order to prevent the compounds from being oxidized, the process for growing the crystals was also carried out in a nitrogen glove box.

    [0050] The end portions of the produced elements were cut off and then polished. The reflection preventive film 4 against the incident fundamental wave on the surface of one end, and the reflection preventive film 5 against the generated second-harmonic wave on the surface of the other end were formed by sputtering MgF₂ for each element.

    [0051] In order to evaluate performance of the produced optical fiber-type nonlinear optical elements, SHG efficiency was measured using the fundamental wave (having 1.064 µm of wavelength) from an Nd-YAG laser, as shown in Fig. 2.

    [0052] Laser beam from the Nd-YAG laser 6 was irradiated through a lens 7, of which numerical aperture (NA) is 0.5, onto the core 3 at one end of the element. The intensity of the incident basic wave was 10 nJ/pulse, the pulse width was 10 ns, and the pulse repetition frequency was 10 Hz, respectively. The generated second-harmonic wave was allowed to pass through a lens 8 and an interference filter 9 set to 532 nm corresponding to the wavelength of the second harmonic wave, thereby being converged to a photoelectron multiplier 10, and the intensity of SH light was measured by operating a digital oscilloscope 11. Since the second-harmonic wave from the fiber formed ring-shaped pattern, it was confirmed that the Cerenkov radiation type phase matching was attained.

    [0053] Table 9 shows the SHG efficiency of each element. As is clear from Table 9, each element yielded 40 to 50% of the conversion efficiency against 10 nJ of input pulse. It is estimated from these results that substantial amount of the second-harmonic wave enough for practical use can be generated even when semiconductor lasers, having about 100 mW of output, are used.




    Claims

    1. Organic nonlinear optical material consisting of a compound according to formula (I) shown below;

    wherein Z₁ is O, S, Se, Te, SO₂ group or NR₁ group;
       Z₂ is N or CR₂ group;
       Y is O, S or NR₃ group;
       X is CR₄R₅ group, NR₆ group, O or S; and
       R, R₁, R₂, R₃, R₄, R₅, and R₆ may be identical to or different from each other, and each of them is heterocyclic group, aromatic hydrocarbon group, aliphatic hydrocarbon group or alicyclic hydrocarbon group, which may be unsubstituted or substituted, characteristic group or H, where R₄ and R₅ may jointly form a carbocyclic or a heterocyclic ring.
     
    2. The organic nonlinear optical material according to claim 1, characterized in that Z₁ is O, S, or NR₁ group; Z₂ is N; Y is O, X is CR₄R₅ group; either R₄ or R₅ is an electron-releasing group; and R is substantially a neutral group related to withdrawing and releasing of electrons.
     
    3. The organic nonlinear optical material according to claim 2, characterized in that R is aryl group.
     
    4. The organic nonlinear optical material according to claim 2, characterized in that R is alkyl group.
     
    5. The organic nonlinear optical material according to claim 1, characterized in that Z₁ is O, S, or NR₁ group; Z₂ is N; Y is O; X is CR₄R₅ group; both R₄ and R₅ are substantially a neutral group related to withdrawing and releasing of electrons; and R is an electron-withdrawing group.
     
    6. The organic nonlinear optical material according to claim 5, characterized in that R₄ and R₅ are aryl group and H.
     
    7. The organic nonlinear optical material according to claim 5, characterized in that R₄ and R₅ are alkyl group and H.
     
    8. A nonlinear optical element comprising:
       a hollow optical fiber; and
       a singlecrystal of organic nonlinear optical material according to claim 1 filled in hollow space of said optical fiber.
     
    9. The nonlinear optical element according to claim 8, characterized in that films for preventing reflection of incident fundamental wave and generated second-harmonic wave are provided on each surface of both ends of said optical fiber.
     


    Ansprüche

    1. Organisches nicht-lineares optisches Material, bestehend aus einer Verbindung der folgenden Formel (I)

    worin bedeuten:

    Z₁   O, S, Se, Te, eine SO₂-Gruppe oder eine NR₁-Gruppe;

    Z₂   N oder eine CR₂-Gruppe;

    Y   O, S oder eine NR₃-Gruppe;

    X   eine CR₄R₅-Gruppe, eine NR₆-Gruppe, O oder S und

    R, R₁, R₂, R₃, R₄, R₅ und R₆,   die gleich oder voneinander verschieden sein können, jeweils eine gegebenenfalls substituierte heterocyclische Gruppe, aromatische Kohlenwasserstoffgruppe, aliphatische Kohlenwasserstoffgruppe oder alicyclische Kohlenwasserstoffgruppe, eine charakteristische Gruppe oder H, wobei R₄ und R₅ zusammen einen carbocyclischen oder einen heterocyclischen Ring bilden können.


     
    2. Organisches nicht-lineares optisches Material nach Anspruch 1, dadurch gekennzeichnet, daß Z₁ für O, S oder eine NR₁-Gruppe steht, Z₂ N darstellt, Y O bedeutet, X einer CR₄R₅-Gruppe entspricht, wobei einer der Reste R₄ oder R₅ für eine elektronenfreigebende Gruppe steht, und R eine in bezug auf das Abziehen und die Freigabe von Elektronen praktisch neutrale Gruppe darstellt.
     
    3. Organisches nicht-lineares optisches Material nach Anspruch 2, dadurch gekennzeichnet, daß R für eine Arylgruppe steht.
     
    4. Organisches nicht-lineares optisches Material nach Anspruch 2, dadurch gekennzeichnet, daß R für eine Alkylgruppe steht.
     
    5. Organisches nicht-lineares optisches Material nach Anspruch 1, dadurch gekennzeichnet, daß Z₁ für O, S oder eine NR₁-Gruppe steht, Z₂ N darstellt, Y O bedeutet, X einer CR₄R₅-Gruppe entspricht, wobei beide Reste R₄ und R₅ für eine in bezug auf das Abziehen und die Freigabe von Elektronen praktisch neutrale Gruppe stehen und R eine elektronenabziehende Gruppe darstellt.
     
    6. Organisches nicht-lineares optisches Material nach Anspruch 5, dadurch gekennzeichnet, daß R₄ und R₅ für eine Arylgruppe und H stehen.
     
    7. Organisches nicht-lineares optisches Material nach Anspruch 5, dadurch gekennzeichnet, daß R₄ und R₅ für eine Alkylgruppe und H stehen.
     
    8. Nicht-lineares optisches Element, umfassend eine hohle optische Faser und einen Einkristall aus einem organischen nicht-linearen optischen Material nach Anspruch 1 im Hohlraum der optischen Faser.
     
    9. Nicht-lineares optisches Element nach Anspruch 8, dadurch gekennzeichnet, daß auf jeder Oberfläche beider Enden der optischen Faser Filme zur Verhinderung einer Reflexion einer einfallenden Grundwelle und einer entstandenen zweiten Harmonischen vorgesehen sind.
     


    Revendications

    1. Matériau organique pour l'optique non-linéaire constitué d'un composé suivant la formule (I) indiquée ci-dessous:

    dans laquelle:
       Z₁ est O, S, Se, Te, un groupement SO₂ ou un groupement NR₁;
       Z₂ est N ou un groupement CR₂;
       Y est O, S ou un groupement NR₃;
       X est un groupement CR₄R₅, un groupement NR₆, O ou S et
       R, R₁, R₂, R₃, R₄, R₅ et R₆ peuvent être identiques ou différents l'un de l'autre et chacun d'eux est un groupement hétérocyclique, un groupement d'hydrocarbure aromatique, un groupement d'hydrocarbure aliphatique ou un groupement d'hydrocarbure alicyclique qui peut être non substitué ou substitué, un groupement caractéristique ou H, où R₄ et R₅ peuvent former ensemble un noyau carbocyclique ou hétérocyclique.
     
    2. Matériau organique pour l'optique non-linéaire selon la revendication 1, caractérisé en ce que Z₁ est O, S ou un groupement NR₁; Z₂ est N; Y est O, X est un groupement CR₄R₅; l'un ou l'autre des R₄ et R₅ est un groupement donneur d'électrons et R est substantiellement un groupement neutre en rapport avec l'enlèvement et la libération d'électrons.
     
    3. Matériau organique pour l'optique non-linéaire selon la revendication 2, caractérisé en ce que R est un groupement aryle.
     
    4. Matériau organique pour l'optique non-linéaire selon la revendication 2, caractérisé en ce que R est un groupement alkyle.
     
    5. Matériau organique pour l'optique non-linéaire selon la revendication 1, caractérisé en ce que Z₁ est O, S ou un groupement NR₁; Z₂ est N; Y est O; X est un groupement CR₄R₅; R₄ et R₅ sont substantiellement tous les deux un groupement neutre en rapport avec l'enlèvement et la libération d'électrons et R est un groupement enlevant des électrons.
     
    6. Matériau organique pour l'optique non-linéaire selon la revendication 5, caractérisé en ce que R₄ et R₅ sont un groupement aryle et H.
     
    7. Matériau organique pour l'optique non-linéaire selon la revendication 5, caractérisé en ce que R₄ et R₅ sont un groupement alkyle et H.
     
    8. Matériau organique pour l'optique non-linéaire comprenant:

    - une fibre optique creuse et

    - un cristal unique d'un matériau organique pour l'optique non-linéaire selon la revendication 1 introduit dans l'espace creux de ladite fibre optique.


     
    9. Matériau organique pour l'optique non-linéaire selon la revendication 8, caractérisé en ce que des films évitant la réflexion d'onde fondamentale incidente et d'onde de seconde harmonique générée sont disposés sur la surface de chacune des deux extrémités de ladite fibre optique.
     




    Drawing