(19)
(11)EP 0 933 803 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
29.01.2003 Bulletin 2003/05

(21)Application number: 97912458.3

(22)Date of filing:  14.11.1997
(51)International Patent Classification (IPC)7H01L 21/31, H01L 21/205, C23C 16/50, C23C 16/52, H01L 21/3065, H01J 37/32
(86)International application number:
PCT/JP9704/151
(87)International publication number:
WO 9802/1746 (22.05.1998 Gazette  1998/20)

(54)

METHOD OF PLASMA TREATMENT

PLASMABEHANDLUNGSMETHODE

PROCEDE DE TRAITEMENT AU PLASMA


(84)Designated Contracting States:
DE FR GB IT NL

(30)Priority: 14.11.1996 JP 32091596

(43)Date of publication of application:
04.08.1999 Bulletin 1999/31

(73)Proprietor: TOKYO ELECTRON LIMITED
Minato-ku, Tokyo 107-8481 (JP)

(72)Inventors:
  • AKAHORI, Takashi
    Hachioji-shi, Tokyo 192-03 (JP)
  • NAKASE, Risa
    Sagamihara-shi, Kanagawa 229 (JP)
  • OKA, Shinsuke
    Sagamihara-shi, Kanagawa 229 (JP)

(74)Representative: HOFFMANN - EITLE 
Patent- und Rechtsanwälte Arabellastrasse 4
81925 München
81925 München (DE)


(56)References cited: : 
EP-A- 0 628 985
JP-A- 5 029 285
JP-A- 6 151 362
JP-A- 7 086 242
JP-A- 8 176 854
JP-A- 1 032 631
JP-A- 5 291 194
JP-A- 6 283 484
JP-A- 7 115 085
US-A- 5 433 258
  
  • PATENT ABSTRACTS OF JAPAN vol. 095, no. 008, 29 September 1995 (1995-09-29) & JP 07 115085 A (SONY CORP), 2 May 1995 (1995-05-02)
  • PATENT ABSTRACTS OF JAPAN vol. 095, no. 006, 31 July 1995 (1995-07-31) & JP 07 086242 A (FUJITSU LTD;OTHERS: 01), 31 March 1995 (1995-03-31) & US 5 620 526 A
  • HWANG H H ET AL: "REGIMES OF PARTICLE TRAPPING IN INDUCTIVELY COUPLED PLASMA PROCESSING REACTORS" APPLIED PHYSICS LETTERS, vol. 68, no. 26, 24 June 1996 (1996-06-24), pages 3716-3718, XP000599590 ISSN: 0003-6951
  • JAPANESE JOURNAL OF APPLIED PHYSICS, Vol. 30, No. 8, (August 1991), p. 1887-1892.
  
Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


Description

Field of the Invention



[0001] The present invention relates to a plasma processing method for performing a plasma process upon an object to be processed, such as a semiconductor wafer.

Background of the Invention



[0002] During the fabrication of a semiconductor device, a plasma is often used to subject a semiconductor wafer (hereinafter called a wafer) to a process such as film-formation or etching. This processing is performed by introducing a processing gas into a vacuum vessel which is provided with a mounting stand for a wafer, then supplying energy such as electromagnetic energy to that processing gas to create a plasma therefrom. Various methods are known as methods of supplying this electromagnetic energy, such as electron cyclotron resonance (ECR), which makes use of the interaction between microwaves and a magnetic field, and a method known as inductive coupled plasma (ICP) in which an electric field and a magnetic field from a coil surrounding a dome-shaped vessel are applied to a processing gas.

[0003] A high-density plasma is established in a zone corresponding to the wafer, but a thin plasma is also present throughout the entire interior of the vacuum vessel. This deteriorates an O-ring that acts as a sealing material and also causes peeling of a film that has adhered to the walls of the vessel due the reactions of the processing gas. It is therefore not possible to avoid the generation of particles within the vacuum vessel. Particularly with plasma processing, the speed of movement of electrons within the plasma is greater than that of ions, so a large number of electrons adhere to surfaces such as the walls and internal members of the vessel, as well as the wafer, and are negatively charged, Thus the potential gradient in the vicinity of these surfaces destroys the neutral characteristics of the plasma in the vicinity of the surfaces, without allowing the electrons to approach, thus forming a zone called a sheath of a thickness of a few mm.

[0004] Since the particles are negatively charged, they cannot pass through the sheath zone and are pushed back towards the plasma. As seen from a certain point in time, it occurs that these particles appear to be trapped at the boundary between the plasma and the sheath zone. However, when the microwave power and wafer biasing power are cut, the particles trapped at positions floating above the wafer will tend to adhere to the wafer. There is therefore a demand for a method of suppressing the generation of these particles as far as possible, especially since circuitry patterns will continue to become finer in the future.

[0005] US-A-5 433 258 discloses a plasma process with magnetic coils located on either side of the wafer in the horizontal direction; EP-A-628 985 discloses magnets which do not operate during wafer processing.

[0006] The present invention was devised in the light of the above problems with the conventional art and has as an objective thereof the provision of a plasma processing method that is capable of suppressing the creation of particles, thus increasing the yield.

Summary of the Invention



[0007] In order to achieve the above described objective, an aspect of the present invention disclosed in a first claim herein relates to a plasma processing method comprising the steps of:

forming a magnetic field by a first coil (27) and a second coil (28) in such a manner that magnetic lines of force thereof run from a zone corresponding to a surface to be processed of an object (10) to be processed towards said object (10) to be processed, said object (10) being provided in a film-formation chamber (22);
   forming a plasma from a processing gas that is supplied into a plasma chamber (21), based on the interaction between an electrical field and said magnetic field;
   using said plasma to perform a plasma process on said object (10) to be processed, said first coil (27) and said second coil (28) being disposed so as to surround a central axis of said object (10) to be processed, whereby said first coil (27) being provided above said object (10) to be processed and said second coil (28) being provided either beside or below said object (10) to be processed and being energised during said plasma process;
   subsequently forming a plasma that does not promote processing instead of said plasma of said processing gas,
   adjusting said magnetic field in such a manner that said magnetic lines of force thereof in the vicinity of said object (10) to be processed fan out further than during said plasma processing by either reducing a current flowing through said second coil (28) to less than that during said plasma processing (including a reduction to zero) or reversing said current; and
   conveying said object (10) to be processed out of said film-formation chamber (22).



[0008] In another aspect of this invention disclosed in a second claim herein, the plasma processing method comprising the steps of:

attracting the object (10) to be processed by electrostatic attraction to a mounting stand (3) that is provided within a film-formation chamber (22) and includes an electrostatic chuck (32),

subsequently separating said object (10) to be processed from said mounting stand (3) and applying a negative voltage to a chuck electrode (33) of said electrostatic chuck (32); and

placing another object to be processed on said mounting stand (3) and performing plasma processing thereon.



[0009] In a further aspect of this invention disclosed in a third claim herein, the film-formation gas comprises SiF4 and the plasma gas comprises Ar and O2 for forming a film of SiOF.

Brief Description of the Drawings



[0010] 

Fig. 1 is a vertical cross-sectional view of an example of a plasma processing apparatus for implementing the method of this invention;

Fig. 2 illustrates an example of the method of this invention;

Fig. 3 illustrates a situation wherein a sheath zone is formed when a plasma is established;

Fig. 4A shows a state of particles when a conventional-art method is used, whereas Fig. 4B shows the effect of the action of the embodiment of Fig. 2;

Fig. 5 is a graph of the relationship between microwave power applied after a film has been formed and the number of particles;

Fig. 6 illustrates a Miller magnetic field and a divergent magnetic field;

Fig. 7 illustrates another example,

Fig. 8 illustrates an example of a method of forming a magnetic field;

Fig. 9 is a graph of the relationship between the current passing through the auxiliary electromagnetic coil after the film has been formed and the number of particles;

Fig. 10 illustrates a further example;

Fig. 11 is a graph of the relationship between the bias voltage applied to the mounting stand after the film has been formed and the number of particles;

Fig. 12 illustrates a still further example and

Fig. 13 is a graph of the relationship between the current passing through the auxiliary electromagnetic coil and the number of particles.



[0011] The description below relates to methods applied to plasma processing performed by using an electron cyclotron resonance (ECR) type of plasma processing apparatus. The structure of a plasma processing apparatus 1 will first be described with reference to Fig. 1. This plasma processing apparatus 1 has a vacuum vessel 2 made of a material such as aluminum. The vacuum vessel 2 consists of a cylindrical plasma chamber 21, which is positioned at the top of the vacuum vessel 2 and in which a plasma is generated, and a cylindrical film-formation chamber 22 of a larger diameter of that of the plasma chamber 21, which is positioned therebelow and communicating therewith. Note that the vacuum vessel 2 is grounded and is thus at zero potential.

[0012] An upper edge of this vacuum vessel 2 is open but is sealed hermetically with a transparent window 23 formed of a material that is transparent to microwaves, such as quartz, so as to maintain the vacuum state of the vacuum vessel 2. On the outer side of this transparent window 23 is provided a wave guide 25 connected to a high-frequency power source 24 which is a high-frequency supply means for generating a plasma at, for example, 2.46 GHz. The configuration is such that microwaves M generated in the high-frequency power source 24 are guided by the wave guide 25 and are introduced into the plasma chamber 21 through the transparent window 23.

[0013] Plasma gas nozzles 26 are provided in a side wall that defines the plasma chamber 21 at, for example, regular intervals around the periphery thereof. In addition, the configuration is such that a plasma gas source, such as a source of Ar or O2, (not shown in the figure) is connected thereto so that a plasma gas such as Ar or O2 is supplied to an upper portion within the plasma chamber 21 uniformly and without interruptions. Note that only two of the nozzles 26 are shown in the figure, to avoid over-complexity of the drawing, but in practice a larger number will be provided.

[0014] An annular main electromagnetic coil 27 is disposed about the outer periphery of the side wall that, defines the plasma chamber 21 in close contact therewith, as a means for forming a magnetic field. In addition, an annular auxiliary electromagnetic coil 28 is disposed on a lower side of the film-formation chamber 22 in such a manner that a magnetic field B of, for example, 875 Gauss, is formed extending from the plasma chamber 21 above, downward towards the film-formation chamber 22. The ECR plasma conditions are satisfied thereby. Note that permanent magnets could be used instead of magnetic coils.

[0015] The above described ECR plasma is generated by the interaction caused by the formation of the microwaves M and the magnetic field B within the thus configured plasma chamber 21, where the frequency of the microwaves M is controlled. At this point, resonance is induced in the introduced gas at this frequency so that a plasma of a high density is formed. In other words, this apparatus is configured as an electron cyclotron resonance (ECR) plasma processing apparatus.

[0016] An annular film-formation gas supply portion 30 is provided in an upper portion of the film-formation chamber 22, in other words, in the portion thereof communicating with the plasma chamber 21, in such a manner that a film-formation gas is ejected from an inner peripheral surface thereof. A mounting stand 3 is also provided in the film-formation chamber 22 in a elevatable manner. This mounting stand 3 is provided with an electrostatic chuck 32, which has an internal heater, on top of a main unit 31 of a material such as aluminum. A chuck electrode 33 within the electrostatic chuck 32 also acts as an electrode for applying a bias voltage in order to draw ions towards the wafer W, and it is connected to a power supply such as a high-frequency power supply portion 34. An exhaust pipe 35 is connected to a base portion of the film-formation chamber 22.

[0017] The description now turns to the use of the above described apparatus in a method of forming an inter-layer insulating film on a wafer 10 that is the object to be processed. It is assumed in this case that aluminum wiring has been formed on the surface of this wafer 10 and the inter-layer insulating film is to be an SiOF film, by way of example. First of all, a gate valve provided in a side wall of the vacuum vessel 2, but not shown in the figure, is opened then the wafer 10 is conveyed thereinto by a conveyor arm (not shown in the figure) from a load-lock chamber (also not shown in the figure).

[0018] After the gate valve has been closed, sealing the interior of the apparatus, the internal atmosphere is exhausted from the exhaust pipe 35 to evacuate the apparatus to a predetermined degree of vacuum, then gases for generating a plasma, such as O2 and Ar, are introduced into the plasma chamber 21 from the plasma gas nozzles 26 at flow rates of 200 sccm and 350 sccm, respectively. In addition, a film-formation gas such as SiF4 is introduced into the film-formation chamber 22 from the film-formation gas supply portion 30 at a flow rate of 140 sccm. The interior of the vacuum vessel 2 is then maintained at a processing pressure of, for example, 0.4 Pa; biasing power at 13.56 MHz and 2500 W is applied to the wafer 10; and also the surface temperature of the mounting stand 3 is set to 200°C.

[0019] High-frequency power (microwaves) at 2.45 GHz from the high frequency power source 24 for plasma generation is transmitted through the wave guide 25 towards the ceiling portion of the vacuum vessel 2, passes through the transparent window 23 provided therein, and is introduced into the plasma chamber 21 as the microwaves M. The magnetic field B generated by the electromagnetic coils 27 and 28, from above and directed downward, is applied within the plasma chamber 21 at a strength of, for example, 875 Gauss. The interaction between this magnetic field B and the microwaves M induces an electrical field E as well as the magnetic field B, which generates electron cyclotron resonance, and this resonance causes the Ar to become a plasma.

[0020] The plasma flowing from the plasma chamber 21 and into the film-formation chamber 22 activates the SiF4 gas supplied thereto to form active seeds, and an SiOF film is formed by the reaction between SiF4 and O2 to fill concavities on the wafer 10. During this time, the Ar ions are drawn towards the wafer 10 by the bias voltage for attracting the plasma, and the corners of the SiOF film formed in the pattern (concavities) on the surface of the wafer 10 are shaved off by the sputter-etching action thereof, and thus the Ar ions fulfil the role of broadening the apertures in the pattern.

[0021] This method affects the subsequent processing. In other words, at a time t1, immediately after the film formation is completed, the supply of the plasma gases Ar and O2 continues without changes but the supply of film-formation gas is halted and also the microwave power is reduced from 2500 W to 1000 W, as shown in Fig. 2. A certain time later, such as 10 seconds later, the supply of the microwave power and the biasing power are stopped.

[0022] This makes it possible to reduce the number of particles on the wafer. The reason for this can be considered to be as described below. In other words, as discussed in the section on the conventional-art technique, the speed of movement of the electrons within the plasma move is greater than that of the ions, so large numbers of electrons adhere in the vicinity of the surfaces of the materials or the wafer, as shown in Fig. 3. Thus the neutral characteristics of the plasma in a plasma zone Z are destroyed to form a sheath zone S. The depth D of this sheath zone S increases with decreasing electron density. This is because the magnitude of the charge of electrons adhering to a material is determined, and thus the magnitude of the positive charge inherent to the sheath zone S is also determined. Therefore, if the electron density is low (if the plasma density is low), the number of ions within the sheath zone S is small. With a small number of ions, the ion layer necessary for maintaining a certain charge becomes thicker and, as a result, the sheath zone S also becomes thicker.

[0023] If, therefore, this sheath zone S is formed above the surface of the wafer 10 during the film formation, as shown in Fig. 4A, and the microwave power and biasing power are cut in that state, particles P will adhere to the wafer 10. Since the particles are extremely small at no more than 1 µm, they are moved around freely by external influences such as air current, rather than fall under gravity, so any particles that are in the vicinity of the wafer 10 will strike it and adhere thereto. In this case, if the microwave power is reduced after the film is formed, the electron density drops and as a result the thickness D of the sheath zone S becomes larger, as shown in Fig. 4B.

[0024] Since the particles P appear to be trapped between the sheath zone S and the plasma zone Z, increasing the thickness D of the sheath zone S ensures that the particles P are moved away from the surface of the wafer 10. If the microwave power and biasing power are both cut at this point, the number of particles adhering to the wafer 10 will be small.

[0025] Experiments were performed with the microwave power set to 2500 W during the formation of the film. After a film had been formed on the surface of the wafer 10 under the previously described processing conditions, the microwave power was reduced in the sequence shown in Fig. 2, this microwave power was changed in various ways, and the numbers of particles between 0.25 µm and 1 µm out of those on each 8-inch wafer were counted, with the results being as shown in Fig. 5. If the period between the times t1 and t2 in Fig. 2 during which the microwave power is reduced is called "power reduction processing", the horizontal axis shows the microwave power during this power reduction. It is clear from these results that the number of particles on the wafer 10 is reduced by lowering the microwave power after the film is formed, and this will improve the yield. Note that "reducing the microwave power" also includes cases in which the microwave power is reduced gradually. This method is not limited to film-formation processing; it can also be applied to etching, in which case the supply of etching gas can be changed to Ar gas, and the microwave power reduced.

[0026] Another way of increasing the thickness of this sheath could be to increase the biasing power so that it is at a setting such as 3500 W during the power reduction period. This would also make it possible to reduce the number of particles. The reason why increasing the biasing power increases the thickness of the sheath is discussed below. If the biasing power increases, the bias voltage also increases, and moreover the frequency of that voltage is 13.56 MHz, which is high enough that the ions cannot follow. Therefore, the sheath thickness increases at the instant that a negative bias voltage is applied. Since the potential of the plasma is always higher than that of the outer walls, the sheath thickness does not become too small, even if a positive bias voltage is applied. Therefore, the average sheath thickness increases. It should be noted, however, that if the biasing power becomes too great, sputter-etching will occur on the surface of the wafer, so it is preferable to adjust the microwave power instead.

[0027] It should be noted that this method is not limited to use in an ECR plasma processing apparatus; it can also be used in the above mentioned ICP apparatus, in which case the configuration could be such that the current of coil is reduced so that the electromagnetic energy drops after the film-formation processing, thus reducing the electron density.

[0028] The method described below is also effective for reducing the number of particles adhering to the wafer surface even further. Power is passed through the main electromagnetic coil 27 and the auxiliary electromagnetic coil 28 during the formation of the film, but when the film formation is completed the current in the auxiliary electromagnetic coil 28 is lowered or made to be zero so that the field changes from a Miller electromagnetic field M1 to a dispersed electromagnetic field M2, as shown in Fig. 6. Alternatively, the direction R of the current flowing through the auxiliary electromagnetic coil 28 could be made to be opposite to the direction L of the current flowing through the main electromagnetic coil 27 to form a cusped electromagnetic field M3, as shown in Fig. 8. In this power reduction process, the supply of film-formation gas stops but the supply of Ar and O2 continues, in a similar manner to the previous embodiment. This causes the plasma zone to expand, as shown in Fig. 7, so that the groups of particles that were trapped as described previously are moved towards the sides, the number of particles corresponding to the wafer 10 is thereby reduced, and therefore the number of particles adhering to the wafer 10 is reduced. Note that the configuration could also be such that the direction of flow of current in the auxiliary electromagnetic coil 28 is reversed to form a cusped magnetic field, as shown in Fig. 8.

[0029] After a film was formed on an 8-inch wafer as described above, power-reduction processing was performed in which the current in the auxiliary electromagnetic coil 28 was changed in various ways, and the numbers of particles between 0.25 µm and 1 µm on the wafer surface were counted, with the results being as shown in Fig. 9. It is clear from this graph that the number of particles decreases as the current in the auxiliary electromagnetic coil 28 decreases. Note that the current in the auxiliary electromagnetic coil 28 was 120 A during the film formation.

[0030] The present invention relates to a method for preventing particle contamination of wafers during plasma processing, but this method can also have other embodiments. One of these embodiments is intended to reduce the number of particles adhering to the surface of the mounting stand 3. If particles adhere to the surface of the mounting stand, those particles may transfer to the rear surface of the wafer so that, when the wafer is accommodated within a cassette, the particles may fall off and adhere to the surface of a wafer in a lower stage, which will deteriorate the yield.

[0031] In this embodiment, a negative voltage of -1000 V, for example, is applied by a power source 4 to the chuck electrode 33 of the electrostatic chuck 32, as shown in Fig. 10. The timing at which this voltage is applied could be immediately after a film has been formed on the wafer 10 and the wafer 10 has been removed from the mounting stand 3 by the conveyor arm, for example. The transfer of the wafer to the conveyor arm could be done by pushing the wafer upward by projecting pins incorporated within the mounting stand 3, then inserting the arm into the lower-surface side of the wafer.

[0032] The thickness of the dielectric member above the chuck electrode 33 is extremely thin, on the order of 0.4 mm, and moreover an ordinary conductive material is mixed into the material such as alumina or aluminum nitride of the dielectric member used in the electrostatic chuck, to ensure that the residual charge is small when the electrostatic chuck is switched off. This means that the surface layer portion of the dielectric member (the portion above the chuck electrode 33) is slightly conductive. There is therefore a voltage drop in this surface layer portion, so the surface of the mounting stand 3 is at a negative potential even when the negative voltage of the power source 4 is not present. Since the particles within the plasma remain negatively charged within a high degree of vacuum, it is difficult for these particles to come close to the surface of the mounting stand 3, and thus the adhesion of such particles to the mounting stand 3 is suppressed. This method can also be applied to etching.

[0033] Experiments were performed wherein an SiOF film was formed on a wafer under the above described conditions then that wafer was removed from the mounting stand 3 by the conveyor arm, various different voltages were applied to the chuck electrode 33 of the mounting stand 3, the next wafer was then placed on the mounting stand 3, that wafer was removed and placed in a cassette, and the numbers of particles between 0.25 µm and 1 µm that adhered to the surface of the unconveyed wafer immediately therebelow were counted. The results are shown in Fig. 11. It can be seen from these results that the number of particles is reduced by applying a negative voltage to the chuck electrode 33 of the mounting stand 3.

[0034] The description now turns to a further embodiment of the present invention. The configuration of this embodiment is such that, after the film-formation processing, a first cleaning step is performed with a cleaning gas 41 comprising a halogen gas, such as NF3, CF4, or ClF3, then a second cleaning step is performed with a cleaning gas 42 comprising at least O2, such as a mixture of O2 and Ar, as shown in Fig. 12. The cleaning gases 41 and 42 are supplied from the plasma gas nozzles 26 of the apparatus, as shown in Fig. 1. To ensure that a plasma zone Z that is wider than the plasma zone used during the film formation is created for the cleaning steps, a dispersed magnetic field is formed by, for example, reducing the current in the auxiliary electromagnetic coil 28 to less than that during the film formation, or to zero, as previously described with reference to Fig. 6.

[0035] Use of this method makes it is possible to reduce particles in an apparatus for forming a film of a material such as SiOF, SiO2, or polysilicon. The reason therefor will now be discussed. After films have been formed on a certain number of wafers, such as 13 wafers, the interior of the vacuum vessel 2 is cleaned with a halogen type of gas. However, when the present inventors investigated more closely, they found that some particles will adhere to the next wafer to be processed, albeit a very small number thereof, even after this cleaning, and carbon is comprised within these particles. In other words, they determined that previous fragments remain on surfaces such as the inner walls of the vessel and the side surfaces of the mounting stand 3, even when cleaning is done with a halogen gas.

[0036] The inventors considered that this carbon is dispersed from the O-ring used to provide a hermetic seal for the vacuum vessel. This is considered to be because the O-ring is made of a resin and active seeds of the plasma that enter into crevices in the walls will penetrate the O-ring. Therefore, the reaction between carbon and oxygen when subjected to an oxygen plasma will cause fragments to form CO2 and CO and scatter.

[0037] If the plasma zone is broadened by a dispersed magnetic field when cleaning is performed, the cleaning gases are projected over all the surfaces of the mounting stand 3 and also all the walls of the vacuum vessel 2. In this case, the dispersed magnetic field could be formed in either the first cleaning step or the second cleaning step, or in both cleaning steps. Note that it is also possible to form the cusped magnetic field described previously with reference to Fig. 8, to broaden the plasma zone.

[0038] Experiments were performed by forming a film of SiOF on each of 13 wafers then executing the first and second cleaning steps, and subsequently forming a film of SiOF on a further wafer. The numbers of particles between 0.25 µm and 1 µm on the surface of that wafer were counted, with the results being as shown in Fig. 13 which shows the relationship between different currents in the auxiliary electromagnetic coil 28 during the second cleaning step and the numbers of particles.

[0039] It should be noted that NF3 gas was supplied at 1000 sccm during the first cleaning step, the pressure was 500 Pa, the microwave power was 1200 W, the biasing power was zero, the current in the auxiliary electromagnetic coil 28 was 200 A, and cleaning was performed for ten minutes. During the second cleaning step. O3 and Ar were supplied at 200 sccm and 300 sccm, respectively, the pressure was 0.3 Pa, the microwave power was 1700 W, the biasing power was zero, and the cleaning was performed for one minute.

[0040] As a result, it was shown that performing the second cleaning step made it possible to reduce the particles, and broadening the magnetic field made it possible to reduce them even further.

[0041] Thus the present invention makes it possible to suppress contamination of an object to be processed by particles, and also enables an improvement in the yield.


Claims

1. A plasma processing method comprising the steps of:

forming a magnetic field by a first coil (27) and a second coil (28) in such a manner that magnetic lines of force thereof run from a zone corresponding to a surface to be processed of an object (10) to be processed towards said object (10) to be processed, said object (10) being provided in a film-formation chamber (22);

forming a plasma from a processing gas that is supplied into a plasma chamber (21), based on the interaction between an electrical field and said magnetic field;

using said plasma to perform a plasma process on said object (10) to be processed, said first coil (27) and said second coil (28) being disposed so as to surround an axis passing centrally through of said object (10) to be processed, whereby said first coil (27) is provided above said object (10) to be processed and said second coil (28) is provided either beside or below said object (10) to be processed and both coils are energised during said plasma process;

subsequently forming a plasma that does not promote processing instead of said plasma of said processing gas,

adjusting said magnetic field in such a manner that said magnetic lines of force thereof in the vicinity of said object (10) to be processed fan out further than during said plasma processing by either reducing a current flowing through said second coil (28) to less than that during said plasma processing, including a reduction to zero, or reversing said current; and

conveying said object (10) to be processed out of said film-formation chamber (22).


 
2. A method as claimed in claim 1 comprising the steps of:

attracting the object (10) to be processed by electrostatic attraction to a mounting stand (3) that is provided within a film-formation chamber (22) and includes an electrostatic chuck (32),

subsequently separating said object (10) to be processed from said mounting stand (3) and applying a negative voltage to a chuck electrode (33) of said electrostatic chuck (32); and

placing another object to be processed on said mounting stand (3) and performing plasma processing thereon.


 
3. A method as claimed in claim 2, wherein the film-formation gas comprises SiF4 and the plasma gas comprises Ar and O2 for forming a film of SiOF.
 


Ansprüche

1. Ein Plasmabearbeitungsverfahren, umfassend die Schritte:

Bilden eines magnetischen Feldes durch eine erste Spule (27) und eine zweite Spule (28) derart, dass die magnetischen Kraftlinien derselben von einem Bereich, der einer zu bearbeitenden Oberfläche eines zu bearbeitenden Gegenstands (10) entspricht, zu dem zu bearbeitenden Gegenstand (10) hin verlaufen, wobei der Gegenstand (10) in einer Filmformationskammer (22) vorgesehen ist;

Bilden eines Plasmas aus einem Bearbeitungsgas, das in eine Plasmakammer (21) zugeführt wird, basierend auf der Wechselwirkung zwischen einem elektrischen Feld und dem magnetischen Feld;

Verwenden des Plasmas, um eine Plasmabearbeitung an dem zu bearbeitenden Gegenstand (10) durchzuführen, wobei die erste Spule (27) und die zweite Spule (28) derart angeordnet sind, um eine Achse, die mittig durch den zu bearbeitenden Gegenstand (10) verläuft, zu umgeben, und wobei die erste Spule (27) oberhalb des zu bearbeitenden Gegenstands (10) und die zweite Spule (28) entweder neben oder unterhalb des zu bearbeitenden Gegenstands (10) vorgesehen ist, und beide Spulen während der Plasmabearbeitung mit Energie beaufschlagt sind;

anschließendem Bilden eines Plasmas, das die Bearbeitung nicht steigert, anstelle des Plasmas des Bearbeitungsgases;

Einstellen des magnetischen Feldes derart, dass die magnetischen Kraftlinien desselben in der Umgebung des zu bearbeitenden Gegenstands (10) sich weiter während der Plasmabearbeitung ausbreiten, entweder durch Reduzieren eines durch die zweite Spule (28) fließenden Stroms auf weniger als den während der Plasmabearbeitung (einschließlich einer Reduzierung auf Null) oder durch Umkehren des Stroms; und

Befördern des zu bearbeitenden Gegenstands (10) aus der Filmformationskammer (22).


 
2. Ein Verfahren nach Anspruch 1, umfassend die Schritte:

Anziehen des zu bearbeitenden Gegenstands (10) durch elektrostatische Anziehung an einem Befestigungsstand (3), der innerhalb einer Filmformationskammer (22) vorgesehen ist und eine elektrostatische Einspannvorrichtung (32) umfasst,

anschließendem Trennen des zu bearbeitenden Gegenstands (10) von dem Befestigungsstand (3) und Anlegen einer negativen Spannung an die Einspannvorrichtungselektrode (33) der elektrostatischen Einspannvorrichtung (32); und

Stellen eines weiteren zu bearbeitenden Gegenstands auf den Befestigungsstand (3) und Durchführen der Plasmabearbeitung an diesem.


 
3. Ein Verfahren nach Anspruch 2, wobei das Filmformationsgas SiF4 aufweist, und das Plasmagas Ar und O2 zum Bilden eines Films aus SiOF aufweist.
 


Revendications

1. Procédé de traitement par plasma comprenant les étapes consistant à:

former un domaine magnétique au moyen d'une première bobine (27) et d'une seconde bobine (28) de telle sorte que des lignes de force de champ magnétique de ces bobines s'étendent depuis une zone correspondant à une surface devant être traitée d'un objet à traiter (10) en direction dudit objet à traiter (10), ledit objet (10) étant pourvu d'une chambre (22) de formation de film;

former un plasma à partir d'un gaz de traitement qui est envoyé dans une chambre à plasma (21), sur la base de l'interaction entre un champ électrique et ledit champ magnétique;

utiliser ledit plasma pour exécuter un traitement plasmatique dudit objet à traiter (10), ladite première bobine (27) et ladite seconde bobine (28) étant disposées de manière à entourer l'axe passant au centre dudit objet à traiter (10), ladite première bobine (27) étant prévue au-dessus dudit objet à traiter (10) et ladite seconde bobine (28) étant prévue soit à côté, soit au-dessous dudit objet à traiter (10) et les deux bobines étant excitées pendant ledit processus plasmatique;

former ultérieurement un plasma qui ne favorise pas le traitement à la place dudit plasma dudit gaz de traitement,

ajuster ledit champ magnétique de telle sorte que lesdites lignes de force du champ magnétique à proximité dudit objet à traiter (10) se déploient d'une manière plus conséquente que pendant ledit traitement plasmatique soit par réduction d'un courant circulant dans ladite seconde bobine (28) à une valeur plus faible que pendant ledit traitement plasmatique, y compris une réduction à zéro, soit par inversion dudit courant; et

convoyer ledit objet à traiter (10) hors de ladite chambre (22) de formation du film.


 
2. Procédé selon la revendication 1, comprenant les étapes consistant à:

attirer l'objet à traiter (10), par attraction électrostatique sur un support de montage (3) qui est prévu dans une chambre (22) de formation du film et inclut un mandrin électrostatique (32);

séparer ensuite ledit objet à traiter (10) dudit support de montage (3) et appliquer une tension négative à une électrode (33) dudit mandrin électrostatique (32); et

disposer un autre objet à traiter sur ledit support de montage (3) et appliquer un traitement plasmatique à l'objet.


 
3. Procédé selon la revendication 2, selon lequel le gaz de formation du film comprend du SiF4 et le gaz de plasma comprend du Ar et du O2. pour former un film de SiOF.
 