(19)
(11)EP 2 574 186 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
26.06.2019 Bulletin 2019/26

(21)Application number: 11775495.2

(22)Date of filing:  26.04.2011
(51)International Patent Classification (IPC): 
C03C 3/062(2006.01)
C03C 8/08(2006.01)
C04B 35/00(2006.01)
C03C 3/093(2006.01)
C03C 8/14(2006.01)
(86)International application number:
PCT/US2011/033895
(87)International publication number:
WO 2011/137098 (03.11.2011 Gazette  2011/44)

(54)

ENAMEL AND GROUND COAT COMPOSITIONS

EMAIL- UND BODENBESCHICHTUNGSZUSAMMENSETZUNGEN

COMPOSITIONS D'ÉMAIL ET DE COUCHE DE FOND


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 27.04.2010 US 768213

(43)Date of publication of application:
03.04.2013 Bulletin 2013/14

(73)Proprietor: Ferro Corporation
Ohio 44124 (US)

(72)Inventors:
  • BENFORD, Albert, L.
    Bedford Heights, OH 44146 (US)
  • GORECKI, Andrew
    Brunswick, OH 44212 (US)
  • GAZO, Louis, J.
    Independence, OH 44131 (US)
  • BALDWIN, Charles, A.
    Brooklyn, OH 44144 (US)

(74)Representative: Reinhardt, Markus 
Patentanwaltskanzlei Reinhardt Postfach 11 65
83225 Aschau
83225 Aschau (DE)


(56)References cited: : 
EP-A1- 0 049 041
US-A- 4 110 487
US-A- 5 382 552
US-A1- 2004 018 932
US-B1- 6 251 810
WO-A2-2006/124415
US-A- 5 264 287
US-A- 5 725 919
US-A1- 2005 014 625
  
      
    Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


    Description

    CROSS REFERENCES TO RELATED APPLICATIONS



    [0001] This application claims priority upon US patent application serial No. 12/768,213 filed April 27, 2010.

    FIELD OF THE INVENTION



    [0002] The present invention provides enamel compositions and ground coat compositions. More particularly, the present invention provides compositions for use in forming an acid resistant and chip resistant enamel cover coating from which baked-on foods can be removed without the need for pyrolysis or highly alkaline cleaners. Also provided are methods for forming the enamel coating, enamel coated substrates, ground coat, and multilayer coated substrates.

    BACKGROUND OF THE INVENTION



    [0003] An oven can be one of the most difficult kitchen appliances to clean. Food that splatters onto the interior surfaces of an oven during cooking usually becomes baked-on, making the removal thereof particularly difficult. If the oven is not frequently cleaned, the amount of baked-on food can build up rapidly, thereby increasing the cleaning difficulty.

    [0004] Coatings used for the interiors of ovens are primarily one of three types: (1) self-cleaning pyrolytic ground coats, (2) non-self-cleaning ground coats, and (3) catalytic continuous clean enamels.

    [0005] The first type of coatings, i.e. self-cleaning pyrolytic ground coats, enable food residue to be reduced to ash by exposure to temperatures between 850 and 1000°F (455 and 538°C). However, there are several concerns associated with heating oven coatings to such temperatures. First, high temperatures are required, necessitating extra insulation around the oven chamber and safety interlocks for oven operation. Second, producing such high temperatures requires relatively large amounts of energy consumption. Third, depending upon the materials exposed to such high temperatures, concerns exist as to the possible release of toxic fumes. Fourth, the cleaning cycle used in association with these coatings takes up to three hours to complete and potentially reduces the overall service life of the oven. Further, in order to withstand multiple cleaning cycles, such enamel coatings generally contain hard, chemically-resistant frits that, without high-temperature exposure, have inherently poor release properties, thereby compounding the difficulty in removing baked-on residues.

    [0006] The second type of coating, i.e. non-self-cleaning ground coats, requires significant cleaning efforts by the consumer and/or harsh alkaline saponifying cleaners that have a pH of approximately 14. As will be appreciated, significant safety concerns exist when using, handling, and storing such hazardous and often toxic cleaners. In addition, producing various oven models each with potentially different interior coatings can increase manufacturing complexity and thus costs. In order to provide a lower cost appliance, Original Equipment Manufacturers (OEMs) generally use the same pyrolytic enamel as used in self-cleaning ovens, but do not equip the oven with a self-clean cycle. Thus, although satisfactory, many ovens such as those lacking a self-cleaning cycle, utilize coatings that are not optimally designed for the oven.

    [0007] The third type of coating, i.e. catalytic continuous clean enamels, fire out with a porous microstructure, enabling the reduction of food residue to ash at normal cooking temperatures. Although satisfactory in many regards, these coatings have largely fallen out of use in North America but are still in use in other markets.

    [0008] The patent literature has described enamel cover coatings. US Patent 7,005,396 describes enamel formulas that include mixtures of low softening point alkali aluminophosphate frit with a high softening point zirconia phosphate frit. The soft frit fluxes the hard frit, creating workability within typical oven enamel firing conditions of 1520 to 1600°F (827 to 871°C). The fired coating sheds baked-on foodstuffs upon exposure to a moist environment. The soil release mechanism is hypothesized to be due to relatively weakly bonded surface absorbed water rather than the significantly stronger bonds otherwise occurring on conventional enamels. When applied to an oven cavity, this surface creates a fourth option for soil removal through relatively brief exposure to water or steam at much lower temperatures than used with the pyrolytic enamels and without the use of harsh alkaline cleaners.

    [0009] However, the glasses discussed in US Patent 7,005,396 have certain characteristics that preclude their use in oven applications using ground coats or that render them difficult to apply with dry electrostatic methods to oven surfaces. The thermal expansion of the glasses is too high relative to ground coats typically used in ovens. This difference in thermal expansion characteristics would lead to cracking or other distortions in an oven coating using such glasses. In addition, the glass temperature of the glasses is below 750°F (400°C). On hidden bake ovens in which an oven floor covers the heating element, the floor can exceed these temperatures. Foods baked-on above the glass temperature would then not necessarily release upon exposure to moisture. As for their application characteristics, a soft and hard frit with mill-added raw materials described in that patent would tend to segregate on recirculation through an automatic spray booth and thus this characteristic detracts from application of the glass mixture via spraying.

    [0010] Accordingly, there exists a need for a composition that can be applied to the interior surfaces of oven cavities and other articles from which baked-on foods can be easily removed without the need for pyrolysis or highly alkaline cleaners.

    SUMMARY OF THE INVENTION



    [0011] The difficulties and drawbacks associated with previously known systems are addressed in the present compositions, methods, and coated substrates involving enamel cover coatings and ground coats that enable baked-on foods to be easily removed.

    [0012] Generally, the present invention provides a composition adapted for forming an enamel coating. Also provided are methods of forming enamel coatings on substrates by use of these compositions. And, the present invention additionally provides various enamel coated substrates.

    [0013] More specifically, and in one aspect, the present invention provides a composition adapted for forming an enamel coating. The composition prior to firing, comprises (i) a glass component that includes from 7.1% to 7.9% Na2O, from 7.0% to 7.7% K2O, from 0.6% to 1.0% ZnO, from 2.7% to 3.3% BaO, from 19.3% to 20.7% Al2O3, from 10.8% to 11.8% SiO2, from 0.7% to 1.2% TiO2, from 14.4% to 15.6% ZrO2, from 29.2% to 31.3% P2O5, and from 0.1% to 5.2% Co2O3.

    [0014] In another aspect, the invention provides a method of forming an enamel coating on a substrate. The method comprises providing a substrate and providing a composition. The composition includes (i) a glass component. The method also comprises depositing a layer of the composition on the substrate. And, the method comprises firing the layer to thereby form an enamel coating on the substrate.

    [0015] Specifically and in another aspect, the present invention provides a method for forming an enamel coating on a substrate. The method comprises providing a substrate for receiving the coating. The method also comprises providing a composition that includes (i) a glass component. The glass component includes from 7.1% to 7.9% Na2O, from 7.0% to 7.7% K2O, from 0.6% to 1.0% ZnO, from 2.7% to 3.3% BaO, from 19.3% to 20.7% Al2O3, from 10.8% to 11.8% SiO2, from 0.7% to 1.2% TiO2, from 14.4% to 15.6% ZrO2, from 29.2% to 31.3% P2O5, and from 0.1% to 5.2% Co2O3. The method also comprises depositing a layer of the composition on the substrate. And, the method additionally comprises firing the layer to thereby form an enamel coating on the substrate.

    [0016] The present invention also provides in another aspect, an enamel coated substrate. The enamel coating prior to firing comprises (i) a glass component and (ii) an effective amount of at least one additive.

    [0017] Specifically and in yet another aspect, the present invention provides an enamel coated substrate. The enamel coating has a composition prior to firing that comprises (i) a glass component. The glass component includes from 7.1% to 7.9% Na2O, from 7.0% to 7.7% K2O, from 0.6% to 1.0% ZnO, from 2.7% to 3.3% BaO, from 19.3% to 20.7% Al2O3, from 10.8% to 11.8% SiO2, from 0.7% to 1.2% TiO2, from 14.4% to 15.6% ZrO2, from 29.2% to 31.3% P2O5, and from 0.1% to 5.2% Co2O3.

    [0018] As will be realized, the invention is capable of other and different embodiments and its several details are capable of modifications in various respects, all without departing from the invention. Accordingly, the description is to be regarded as illustrative and not restrictive.

    DETAILED DESCRIPTION OF THE EMBODIMENTS



    [0019] The present invention provides compositions for use in forming an enamel cover coating from which baked-on foods can be removed without the need for pyrolysis or highly alkaline cleaners. The enamel cover coating produced using the compositions according to the invention exhibits no chipping or other surface defects after cleaning and removal of baked-on foods. Coated substrates according to the invention exhibit excellent food removal characteristics and do not require pyrolysis or use of caustic cleaners. The present invention also provides compositions for use in forming ground coatings or "ground coats" on substrates, and which coatings are well suited for receiving the enamel cover coats described herein.

    Enamel Compositions



    [0020] The enamel compositions of the present invention are preferably provided in the form of a dry powder. This promotes storage and enables the composition to be applied to substrates by well known powder coating processes. However, the compositions can also be provided and applied in a wet state such as a water-based slurry.

    [0021] The enamel compositions of the invention include a glass component and an effective amount of one or more additives such as fluorine and/or NO2. The glass component includes one or more oxides selected from the group consisting of P2O5, Al2O3, ZrO2, SiO2, Na2O, K2O, BaO, TiO2, ZnO, Co2O3, NiO, Cr2O3, MnO2, CuO, and combinations thereof. The compositions may also include one or more additional components such as but not limited to Li2O, Rb2O, Cs2O, MgO, CaO, SrO, ZnO, CeO2, LaO2, B2O3, FeO, Fe2O3, and Fe3O4.

    [0022] The glass component of the enamel compositions preferably comprises a combination of one or more alkali oxides represented as R2O, one or more alkaline earth oxides represented as RO, and one or more various transition metal oxides represented herein as MO, MO2, and M2O3. Preferably, RO includes any transition metal oxide (an oxide of any metallic element with D shell electrons such as but not limited to Sc, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Y, Zr, Nb, Mo, Tc, Ru, Rh, Pd, Ag, Cd...etc.). In certain embodiments, RO includes oxides typically used in enamels that do not have hazardous or scarcity issues such as for example Ti, Cr, Mn, Fe, Co, Ni, Cu, Zn, Y, La, Ce, Zr, Nb, Mo, Ag, W, and Au.

    [0023] The formula R2O represents alkali oxides, preferably selected from the group consisting of Li2O, Na2O, and K2O. The formula RO represents alkaline earth oxides, preferably selected from the group consisting of MgO, CaO, SrO, and BaO.

    [0024] The formulas MO, MO2, and M2O3 represent transition metal oxides. MO includes ZnO, NiO, and CuO for example. MO2 includes TiO2 and ZrO2 for example. And, M2O3 includes Co2O3 and Cr2O3 for example. It will be understood that M can be any transition metal as known in the art.

    [0025] Preferably and more specifically, the enamel compositions prior to firing, comprise (i) a glass component that includes from 7.1% to 7.9% Na2O, from 7.0% to 7.7% K2O, from 0.6% to 1.0% ZnO, from 2.7% to 3.3% BaO, from 19.3% to 20.7% Al2O3, from 10.8% to 11.8% SiO2, from 0.7% to 1.2% TiO2, from 14.4% to 15.6% ZrO2, from 29.2% to 31.3% P2O5, and from 0.1% to 5.2% Co2O3, and (ii) an effective amount of at least one additive. The term "" as used herein includes amounts or proportions of the noted component, agent, element or the like that are substantially the same as the noted amount.

    [0026] Typical, preferred and most preferred ranges for components in the glassy portion of the compositions are set forth below in Table 1 as follows (all values are in weight percent unless indicated otherwise).
    Table 1 - Glass Component Formulation Ranges
    ComponentMost PreferredMore PreferredPreferredTypical
    Na2O 7.32 - 7.72 7.2 - 7.8 7.1 - 7.9 6.0 - 9.0
    K2O 7.15 - 7.54 7.1 - 7.6 7.0 - 7.7 6.0 - 9.0
    ZnO 0.77 - 0.83 0.7 - 0.9 0.6 - 1.0 0.1 - 2.0
    BaO 2.92 - 3.12 2.8 - 3.2 2.7 - 3.3 1.5 - 5.0
    Al2O3 19.50 - 20.45 19.3 - 20.7 19.0 - 21.0 17.0 - 23.0
    SiO2 11.00 - 11.63 10.8 - 11.8 10.5 - 12.0 9.0 - 14.0
    TiO2 0.90 - 1.00 0.8 - 1.1 0.7 - 1.2 0.1 - 2.0
    ZrO2 14.60 - 15.41 14.5 - 15.5 14.4 - 15.6 13.5 - 17.0
    P2O5 29.50 - 31.15 29.2 - 31.3 29.0 - 31.0 27.0 - 33.0
    NiO 0 - 0.93 0 - 1.0 0 - 1.1 0 - 2.0
    CuO 0 - 0.51 0 - 0.6 0 - 0.7 0 - 2.0
    Co2O3 0.34 - 4.90 0.2 - 5.0 0.1 - 5.2 0 - 7.0
    MnO2 0 - 0.59 0 - 0.7 0 - 0.8 0 - 2.0
    Cr2O3 0 - 0.90 0 - 1.0 0 - 1.1 0 - 2.0


    [0027] The present invention provides several preferred compositions set forth below in Table 2. These preferred compositions are designated as preferred compositions A, B, C, D, E, F, and G.



    [0028] In addition to the components set forth in Tables 1 and 2, it is also preferred to include an additive such as fluorine in an amount typically from 0.78% to 1.50%, preferably from 0.88% to 1.35%, and most preferably from 0.91% to 1.25% of the glass component. And, it is also preferred to include another additive such as NO2 in an amount of typically from 1.50% to 4.71%, preferably from 2.00% to 4.61%, and most preferably from 2.40% to 4.56% of the glass component. These formulation ranges for the noted additives are set forth below in Table 3. Typically, after firing, one-half of the fluorine remains in the resulting layer. Typically, all of the nitrogen dioxide is released or decomposed during firing.
    Table 3 - Additive Component Formulation Ranges
    ComponentMost PreferredPreferredTypical
    F 0.91 - 1.25 0.88 - 1.35 0.78 - 1.50
    NO2 2.40 - 4.56 2.00 - 4.61 1.50 - 4.71


    [0029] The glass frits comprising the glass component of the compositions according to the invention are preferably milled prior to application. Any of the conventional milling techniques can be employed. Milling fineness is not critical, but a fineness of 2 grams being retained from a 50 gram sample using a 74 µm (200 mesh) sieve is presently considered optimal. Other particle size distributions may also be utilized. In certain embodiments, either prior to or during milling, additional oxides may be added. For example, an additional 1% oxide may be added to adjust the color of the final composition. After milling, it may be desired to subject the milled composition to a post heat treatment such as exposure to temperatures of 200 °F (93°C) for 18 hours.

    [0030] It will be appreciated that the compositions according to the invention can further comprise up to 20% by weight of one or more mill additions. Suitable mill additions include, for example, clay, bentonite, magnesium carbonate, potassium nitrate, sodium aluminate, boric acid, and pigments. Inorganic materials, such as zirconia, alumina, alumina metaphosphate, spodumene, and feldspar, can also be added to the composition in order to modify the texture and/or to adjust the roughness of the fired enamel. Furthermore, one or more mill additives may be added to adjust or improve sprayability properties of the material.

    [0031] The compositions according to the invention are intended for use as a cover coating. The compositions can be applied like any of the known cover coat enamels for use on sheet steel. For example, the compositions can be applied directly onto pickled, nickel-coated steel. The compositions can be applied onto aluminum substrates. The compositions can be applied over fired enamel ground coated substrates using known two-coat/two-fire processes. And, the compositions can be applied over unfired ground coats using any of the known two-coat/one-fire processes (e.g., wet/wet, wet/dry, and dry/dry).

    Methods



    [0032] The enamel compositions according to the present invention can be applied by any of the known wet application processes such as spraying, dipping, flow coating, and electrodeposition. Preferably, the compositions are dried prior to firing when the compositions are applied using a wet application process. Drying is typically accomplished using heating lamps. The drying time and temperature are not critical. The application rate of the compositions by wet application processes will vary depending upon the desired thickness of the resulting fired enamel cover coat. For example, a fired enamel cover coat having a thickness of 140 µm can be obtained when the application rate of the wet enamel composition is 400 g/m2.

    [0033] The enamel compositions can also be applied using conventional dry electrostatic application processes. In such instances, an organopolysiloxane is typically added to the compositions to facilitate electrostatic application. The application rate of the compositions by dry electrostatic processes will vary widely according to the desired thickness of the resultant enamel cover coat. Typical application rates are from 200 g/m2 to 600 g/m2.

    [0034] The enamel compositions according to the present invention are typically fired at a temperature of from 770°C to 870°C for 2 to 8 minutes. More preferably, the compositions are fired at a temperature of from 800°C to 850°C for 3 to 6 minutes. The optimal firing conditions are 820°C for 3.5 minutes. It will be appreciated that firing times and temperatures are not critical, and a range of firing schedules could be used.

    [0035] Upon firing, the enamel compositions according to the present invention form an enamel cover coat from which baked-on foods can be removed without the need for pyrolysis or highly alkaline cleaners. The enamel compositions according to the invention are particularly well-suited for application on the interior surfaces of oven cavities, dripping pans, cookware, and other articles that are exposed to the risk of baked-on food soiling. The compositions are also expected to find wide application in microwave ovens. The fired enamel cover coats can be produced in a wide range of colors, including bright colors such as blue and green, by varying the pigments included as mill additions.

    [0036] The fired cover coat enamels according to the invention are scratch resistant, stain resistant, and maintain their easy-to-clean properties over many heating cycles. In addition, baked-on food can be easily removed from the fired cover coat enamels without the need for high temperature heating cycles or highly alkaline chemical cleaners. Most baked-on foods can be removed from the fired enamel cover coats using warm water. In a particularly preferred cleaning technique, surfaces in accordance with the invention having baked-on food residue are exposed to warm water vapor, such as having a temperature of at least 150 °F (66°C), and most preferably steam having a temperature of 212 °F (100°C) for at least 3 minutes, more preferably at least 5 minutes, and more preferably at least 10 minutes. Such surfaces can also be exposed to liquid water which is preferably warm and more preferably at the noted temperatures for the noted time periods. After such exposure, the food or food residue can be easily cleaned off the surface. As noted, the cleaning efforts do not require the use of harsh or caustic cleaning agents or exposure to much greater temperatures such as associated with pyrolysis.

    [0037] In accordance with the invention, multilayer coated substrates are provided. In a preferred embodiment, a substrate receives a ground coat as described herein and then also receives an enamel cover coat as described herein. The ground coat is preferably disposed between and in contact with the substrate and the enamel cover coat. However, it will be appreciated that the invention includes a wide array of other configurations.

    [0038] When utilized in conjunction with one another, the ground coat and the enamel cover coat can be applied, dried, and fired in a variety of different strategies. For example, a ground coat and an enamel cover coat can be applied via a two-coat/two-fire dry process in which a dry ground coat is applied and then fired, followed by application of a dry enamel cover coat to the fired ground coat. The enamel cover coat is then fired. A two-coat/one-fire dry process can be used in which a dry ground coat is applied and then a dry enamel cover coat is applied onto the unfired ground coat. The two layers are then collectively fired. Another method involves a two-coat/two-fire wet/wet process in which a wet ground coat is applied, dried, and then fired. A wet enamel cover coat is then applied onto the fired ground coat, dried, and then fired. Yet another process is referred to as a two-coat/one-fire wet/dry process involving application of a wet ground coat, drying and then application of a dry enamel cover coat on the dried ground coat. The resulting layers are then collectively fired. In still another technique, referred to as a two-coat/one-fire wet/wet process, a wet ground coat is applied followed by application of a wet enamel coat onto the undried ground coat. A single firing is performed.

    Examples


    Example 1. Two-Coat/Two-Fire Application



    [0039] Glass frit according to the preferred composition D from Table 2 was milled into an electrostatic powder composition as shown in Table 7. This powder is designated as "Powder Enamel 1."
    Table 7 - Powder Enamel 1 Powder Formulation
    Raw MaterialPowder Enamel 1
    Frit D 99.5
    Spinel Black Oxide 0.5
    Siloxane 0.18
    Fineness 1-2%/200 M Sieve
    Screening 149 µm (100 mesh)
    Post Milling Heat Treatment 200°F (93°C) for 18 hours


    [0040] Powder Enamel 1 was applied to a steel substrate as follows. First, 33 to 40 g/ft2 (355 to 430 g/m2) of electrostatic ground coat was applied over cleaned-only ASTM A424-compliant enameling grade steel. Electrostatic ground coats suitable for pyrolytic self-cleaning ovens are preferred, but any ground coat that creates adhesion on steel could be used. If a pyrolytic self-cleaning ground coat is used, such coating is fired at 1560°F (850°C) for 90 seconds at peak metal temperature. The ground coat was allowed to cool, and Powder Enamel 1 was applied at a coating density of 34 to 40 g/ft2 (366 to 430 g/m2) and fired at 1560°F (850°C) for 90 seconds at peak metal temperature.

    [0041] Test plates were prepared by a two-coat/two-fire dry electrostatic process. 34 to 40 g/ft2 (366 to 430 g/m2) of flecked blue pyrolytic ground coat were applied electrostatically to 5.5 inch by 5.5 inch (14 cm by 14 cm) cleaned Type 1 enameling steel plates. The ground coat was fired at 1560°F (850°C) for 4.0 minutes in the hot zone in an electric continuous furnace. Powder Enamel 1 was applied at a coating density of 33 to 47 g/ft2 (355 to 506 g/m2) and fired at 1560°F (850°C) for 4.0 minutes. Powder Enamel 1 fired out into a smooth glossy gray finish free from defects. It will be noted that although flecked blue pyrolytic ground coats were prepared, in many applications it may be preferred to prepare and/or provide a flecked gray pyrolytic ground coat.

    [0042] Cleanability was tested against a reference standard self-cleaning pyrolytic standard, preferably the ground coat used for the water-clean enamel.

    [0043] Six foodstuffs to be tested were prepared as follows:
    1. 1. AHAM mixture
    2. 2. Cherry pie filling
    3. 3. Lemon juice
    4. 4. Beef gravy
    5. 5. Ketchup
    6. 6. Egg whites (or egg beaters)


    [0044] The recipe for AHAM is shown in Table 8.
    Table 8 - AHAM Mixture Recipe
    AHAM MixtureU.S.Metric
    75% Lean ground beef 4 oz. 113 g
    Grated cheddar cheese ½ cup 119 mL
    Whole milk ½ cup 119 mL
    Granulated white sugar ½ cup 119 mL
    Canned sour pie cherries ½ cup 119 mL
    Dry, uncooked instant tapioca pudding mix 2 tbsp. 30 mL
    Large raw egg 1 1
    All-purpose flour 2 tbsp. 30 mL
    Tomato juice ½ cup 119 mL


    [0045] First, the panels were placed in a conventional free-standing electric range that was then preheated to 450°F (232°C). Second, the oven was turned off, and 0.5 teaspoon (2.5 ml) of each of the noted foodstuffs was applied to the panels. Next, the soils were baked-on at 450°F (232°C) for 1 hour.

    [0046] The oven was allowed to cool for 15 minutes. A traditional pyrolytic enamel was soiled as a reference sample. To rate the cleanability of the coatings, the soiled panels were placed in an enameled broiler pan. To the broiler pan was added 3 to 4 cups (700 to 1000 ml) of water. The broiler pan with water and the soiled panels were then heated in the oven at 250°F (121°C) for 30 minutes and allowed to cool for 30 minutes.

    [0047] Using a Scotch-Brite scouring sponge, it was first attempted to remove all the soils with a light rub. After evaluating and recording, the attempt was changed to a hard rub to finalize scoring. Each soil received a score according to the rating system shown in Table 9 set forth below.
    Table 9 - Rating System Per Soil
    Force and ResidueScore
    Light Rub Full Cleaning 5
    Light Rub Some Residue 4
    Hard Rub Full Cleaning 3
    Hard Rub Some Residue 2
    Ingredients Can't Be Removed 1


    [0048] The score for each soil was summed and the totals were assigned ratings according to the criteria in Table 10.
    Table 10 - Cleanability Ratings
    Cleanability ScoreClass
    25-30 A
    20-24 B
    15-19 C
    10-14 D
    0-9 E


    [0049] Using this testing method, Powder Enamel 1 exhibited the cleanability characteristics shown in Table 11.
    Table 11 - Cleanability of Powder Enamel 1 Applied With a Two-Coat/Two-Fire Process
    SoilPyrolyticPowder Enamel 1
    AHAM 0 5
    Cherry Pie Filling 0 4
    Lemon Juice 5 5
    Beef Gravy 1 5
    Ketchup 1 4
    Egg Whites or Egg Beaters 1 5
    Total Score 8 28
    Rating E A


    [0050] As evident from the data in Table 11, a coating prepared from a two-coat/two-fire application of Powder Enamel 1 exhibited significantly better cleanability characteristics as compared to a standard self-cleaning pyrolytic coating.

    Example 2. Two-Coat/One-Fire Application



    [0051] Test plates were prepared by a two-coat/one-fire dry electrostatic process. A base coat was applied at a coating density of 5 to 7 g/ft2 (54 to 75 g/m2) followed by an application of Powder Enamel 1 at a coating density of 33 to 47 g/ft2 (355 to 506 g/m2). Test plates were fired at 1560°F (850°C) for 4.0 minutes.

    [0052] The cleanability was tested using the procedure described in Example 1. The results are shown in Table 12.
    Table 12 - Cleanability of Powder Enamel 1 Applied With a Two-Coat/One-Fire Process
    SoilPyrolyticPowder Enamel 1
    AHAM 0 5
    Cherry Pie Filling 0 4
    Lemon Juice 5 5
    Beef Gravy 1 5
    Ketchup 1 4
    Egg Whites or Egg Beaters 1 5
    Total Score 8 28
    Rating E A


    [0053] As evident from Table 12, a coating prepared from a two-coat/one-fire application of Powder Enamel 1 exhibited significantly better cleanability characteristics as compared to the noted self-cleaning pyrolytic coating.

    Example 3. Blue Color



    [0054] This is an example of a frit formulation for forming a blue version of the coating. Glass frit according to preferred composition E from Table 2 was milled into electrostatic powder composition using the formula shown in Table 13. This powder is designated as "Powder Enamel 2."
    Table 13 - Powder Enamel 2 Powder Formulation
    Raw MaterialPowder Enamel 2
    Frit E 99.5
    Cobalt Aluminate Blue Oxide 0.25
    Siloxane 0.18
    Fineness 1-2%/200 M Sieve
    Screening 149 µm (100 mesh)
    Post Milling Heat Treatment 200°F (93°C) for 18 hours


    [0055] Test plates were prepared by a two-coat/two-fire dry electrostatic process. 34 to 40 g/ft2 (366 to 430 g/m2) of flecked blue pyrolytic ground coat were applied electrostatically to 5.5 inch by 5.5 inch (14 cm by 14 cm) cleaned Type 1 enameling steel plates. The ground coat was fired at 1560°F (850°C) for 4.0 minutes in the hot zone in an electric continuous furnace. Powder Enamel 2 was applied at a coating rate of 33 to 47 g/ft2 (355 to 506 g/m2) and fired at 1560°F (850°C) for 4.0 minutes. Powder Enamel 2 fired out into a smooth glossy blue-gray finish free from defects.

    [0056] The cleanability was tested using the procedure described in Example 1. The results are shown in Table 14.
    Table 14 - Cleanability of Powder Enamel 2 Applied With a Two-Coat/Two-Fire Process
    SoilPyrolyticPowder Enamel 2
    AHAM 0 5
    Cherry Pie Filling 0 4
    Lemon Juice 5 5
    Beef Gravy 1 5
    Ketchup 1 4
    Egg Whites or Egg Beaters 1 5
    Total Score 8 28
    Rating E A


    [0057] As evident from the data in Table 14, a coating prepared from a two-coat/two-fire application of Powder Enamel 2 exhibited significantly better cleanability characteristics as compared to a standard self-cleaning pyrolytic coating.

    Example 4. Gray Color



    [0058] This is an example of a frit formulation for forming a gray version of the coating. Glass frit according to preferred composition G from Table 2 was milled into electrostatic powder composition using the formula shown in Table 15. This powder is designated as "Powder Enamel 3."
    Table 15 - Powder Enamel 3 Powder Formulation
    Raw MaterialPowder Enamel 3
    Frit G 100
    Cobalt Black Oxide 1.00
    Siloxane 0.18
    Fineness 1-2%/200 M Sieve
    Screening 100 mesh
    Post Milling Heat Treatment 200°F (93°C) for 18 hours


    [0059] Test plates were prepared by a two-coat/two-fire dry electrostatic process. 34 to 40 g/ft2 (366 to 430 g/m2) of flecked gray pyrolytic ground coat were applied electrostatically to 5.5 inch by 5.5 inch (14 cm by 14 cm) cleaned Type 1 enameling steel plates. The ground coat was fired at 1560°F (850°C) for 4.0 minutes in the hot zone in an electric continuous furnace. Powder Enamel 3 was applied at a coating rate of 33 to 47 g/ft2 (355 to 506 g/m2) and fired at 1560°F (850°C) for 4.0 minutes. Powder Enamel 3 fired out into a smooth glossy gray finish free from defects.

    [0060] The cleanability was tested using the procedure described in Example 1. The results are shown in Table 16.
    Table 16 - Cleanability of Powder Enamel 3 Applied With a Two-Coat/Two-Fire Process
    SoilPyrolyticPowder Enamel 3
    AHAM 0 5
    Cherry Pie Filling 0 4
    Lemon Juice 5 5
    Beef Gravy 1 5
    Ketchup 1 4
    Egg Whites or Egg Beaters 1 5
    Total Score 8 28
    Rating E A


    [0061] As evident from the data in Table 16, a coating prepared from a two-coat/two-fire application of Powder Enamel 3 exhibited significantly better cleanability characteristics as compared to a standard self-cleaning pyrolytic coating.

    Example 5. Two-Coat/Two-Fire, Wet/Wet



    [0062] Preferred glass composition D from Table 2 can also be ground with conventional additives known to the industry for wet spray, dip, or flow coat application. Frit D was milled into a slurry according to the formula shown in Table 17 (values in parts by weight). This slurry is designated as Enamel 3. This is a recipe typically used for flow coating or dipping enamels, and other combinations of enamel raw materials could also be used.
    Table 17 - Slurry Formulation
    Raw MaterialSlurry Enamel 3
    Frit D 100
    Spinel Black Oxide 1
    Ball Clay 4
    Aluminum Oxide 4
    Aluminum Phosphate 2
    Bentonite 0.45
    Magnesium Carbonate 0.4
    Potassium Carbonate 0.35
    Sodium Aluminate 0.031
    Potassium Nitrite 0.15
    Gum Arabic 0.01
    Seqlene 0.018
    Water 47


    [0063] The slurry was applied at a coating density of 33 to 47 g/ft2 (355 to 506 g/m2) to a previously wet-applied and fired ground coated steel and fired at 1560°F (850°C) for 4.0 minutes. The enamel slurry fired out into a smooth glossy gray finish free from defects.

    [0064] The cleanability of the resulting enamel coating was tested using the procedure described in Example 1. Results are shown in Table 18.
    Table 18 - Cleanability of Enamel 3 Applied Wet With a Two-Coat/Two-Fire Process
    SoilPyrolyticEnamel 3
    AHAM 0 5
    Cherry Pie Filling 0 3
    Lemon Juice 5 5
    Beef Gravy 1 4
    Ketchup 1 3
    Egg Whites or Egg Beaters 1 5
    Total Score 8 25
    Rating E A


    [0065] As evident from the data in Table 18, a coating prepared from a wet version of Enamel 3 exhibited significantly better cleanability characteristics as compared to a standard self-cleaning pyrolytic coating.

    Example 6. Two-Coat/One-Fire, Wet/Dry



    [0066] A coated substrate could be formed by appropriately applying a wet ground coat composition as described herein. The ground coat would then be subjected to a drying operation. After sufficient drying, a dry enamel composition is then applied onto the dried and un-fired ground coat. The dry enamel composition can be applied in a variety of different fashions, including for example by powder coat techniques. After application of the enamel composition, the multilayer laminate is then subjected to a firing operation to collectively fire the ground coat and the enamel coat.

    Example 7. Two-Coat/One-Fire, Wet/Wet



    [0067] Using this method, a coated substrate could be formed by appropriately applying a wet ground coat composition onto a substrate. Prior to drying of the ground coat, a wet enamel composition is applied thereon. The resulting layered assembly is then subjected to firing conditions whereby the ground coat and the enamel coat are both collectively fired.

    [0068] Many other benefits will no doubt become apparent from future application and development of this technology.

    [0069] It will be understood that any one or more feature or component of one embodiment described herein can be combined with one or more other features or components of another embodiment. Thus, the present invention includes any and all combinations of components or features of the embodiments described herein.

    [0070] As described hereinabove, the present invention solves many problems associated with previous type compositions, methods, and coatings. However, it will be appreciated that various changes in the details, materials and arrangements, which have been herein described and illustrated in order to explain the nature of the invention, may be made by those skilled in the art without departing from the principle and scope of the invention, as expressed in the appended claims.


    Claims

    1. A composition adapted for forming an enamel coating on a metal substrate, the composition prior to firing, comprising in weight % with respect to the glass component formulation range:

    (i) a glass component including:

    from 7.1% to 7.9% Na2O;

    from 7.0% to 7.7% K2O;

    from 0.6% to 1.0% ZnO;

    from 2.7% to 3.3% BaO;

    from 19.3% to 20.7% Al2O3;

    from 10.8% to 11.8% SiO2;

    from 0.7% to 1.2% TiO2;

    from 14.4% to 15.6% ZrO2;

    from 29.2% to 31.3% P2O5, and

    from 0.1% to 5.2% Co2O3.


     
    2. Composition of claim 1, wherein the glass component (i) further includes:

    from 0% to 1.1% NiO;

    from 0% to 0.7% CuO;

    from 0% to 0.8% MnO2; and

    from 0% to 1.1% Cr2O3.


     
    3. Composition of claim 1, further including an additive selected from the group consisting of 0.78-1.5% F and 1.5-4.71 % NO2.
     
    4. A method of forming an enamel coating on a substrate, the method comprising:

    providing a substrate;

    providing a composition comprising:

    (i) a glass component including in weight % with respect to the glass component formulation range:

    from 7.1% to 7.9% Na2O,

    from 7.0% to 7.7% K2O,

    from 0.6% to 1.0% ZnO,

    from 2,7% to 3.3% BaO,

    from 19.3% to 20.7% Al2O3,

    from 10.8% to 11.8% SiO2,

    from 0.7% to 1.2% TiO2,

    from 14.4% to 15.6% ZrO2,

    from 29.20% to 31.3% P2O5, and

    from 0.1% to 5.2% Co2O3.

    depositing a layer of the composition on the substrate, and

    firing the layer to thereby form an enamel coating on the substrate.


     
    5. Method according to claim 4, wherein the composition further including an additive selected from the group consisting of 0.78-1.5% F and 1.5-4.71% NO2.
     
    6. Method of claim 4, wherein the firing is performed at a temperature of from 770°C to 870°C.
     
    7. Method of claim 4, wherein firing is performed at the temperature for 2 to 8 minutes.
     
    8. Method of claim 4, wherein the firing is performed at a temperature of from 800°C to 850°C.
     
    9. Method of claim 4, wherein firing is performed at the temperature for 3 to 6 minutes.
     
    10. Method of claim 4, wherein the substrate is selected from the group consisting of steel and aluminum.
     
    11. Method of claim 4, wherein the composition is disposed on a ground coat.
     
    12. A coated substrate made by the method of claim 4.
     


    Ansprüche

    1. Zusammensetzung, geeignet für die Bildung einer Emaille-Beschichtung auf einem Metallsubstrat, wobei die Zusammensetzung vor dem Brennen in Gewichts-% in Bezug auf den Glasbestandteilformulierungsbereich umfasst:

    (i) einen Glasbestandteil, umfassend:

    von 7,1% bis 7,9% Na2O;

    von 7,0% bis 7,7% K2O;

    von 0,6% bis 1,0% ZnO;

    von 2,7% bis 3,3% BaO;

    von 19,3% bis 20,7% Al2O3;

    von 10,8% bis 11,8% SiO2;

    von 0,7% bis 1,2% TiO2;

    von 14,4 % bis 15,6% ZrO2;

    von 29,2% bis 31,3% P2O5, und

    von 0,1% bis 5,2% Co2O3.


     
    2. Zusammensetzung nach Anspruch 1, wobei der Glasbestandteil (i) ferner umfasst:

    von 0% bis 1,1% NiO;

    von 0% bis 0,7% CuO;

    von 0% bis 0,8% MnO2; und

    von 0% bis 1,1% Cr2O3.


     
    3. Zusammensetzung nach Anspruch 1, ferner umfassend ein Additiv, das aus der Gruppe ausgewählt ist, die aus 0,78-1,5% F und 1,5-4,71 % NO2 besteht.
     
    4. Verfahren zur Bildung einer Emaillebeschichtung auf einem Substrat, wobei das Verfahren umfasst:

    Bereitstellen eines Substrats;

    Bereitstellen einer Zusammensetzung, umfassend:

    (i) einen Glasbestandteil, umfassend in Gewichts-% in Bezug auf den Glasbestandteilformulierungsbereich:

    von 7,1% bis 7,9% Na2O,

    von 7,0% bis 7,7% K2O,

    von 0,6% bis 1,0% ZnO,

    von 2,7% bis 3,3% BaO,

    von 19,3% bis 20,7% Al2O3,

    von 10,8% bis 11,8% SiO2,

    von 0,7% bis 1,2% TiO2,

    von 14,4% bis 15,6% ZrO2,

    von 29,20% bis 31,3% P2O5, und

    von 0,1% bis 5,2% Co2O3,

    Abscheiden einer Schicht der Zusammensetzung auf dem Substrat und

    Brennen der Schicht, um dadurch eine Emaille-Beschichtung auf dem Substrat zu bilden.


     
    5. Verfahren nach Anspruch 4, wobei die Zusammensetzung ferner ein Additiv umfasst, das aus der Gruppe ausgewählt ist, die aus 0,78-1,5% F und 1,5-4,71% NO2 besteht.
     
    6. Verfahren nach Anspruch 4, wobei das Brennen bei einer Temperatur von 770 °C bis 870 °C durchgeführt wird.
     
    7. Verfahren nach Anspruch 4, wobei das Brennen bei der Temperatur für 2 bis 8 Minuten durchgeführt wird.
     
    8. Verfahren nach Anspruch 4, wobei das Brennen bei einer Temperatur von 800 °C bis 850 °C durchgeführt wird.
     
    9. Verfahren nach Anspruch 4, wobei das Brennen bei der Temperatur für 3 bis 6 Minuten durchgeführt wird.
     
    10. Verfahren nach Anspruch 4, wobei das Substrat aus der Gruppe ausgewählt wird, die aus Stahl und Aluminium besteht.
     
    11. Verfahren nach Anspruch 4, wobei die Zusammensetzung auf einer Grundierung angebracht wird.
     
    12. Beschichtetes Substrat, hergestellt durch das Verfahren nach Anspruch 4.
     


    Revendications

    1. Composition destinée à former un revêtement d'émail sur un substrat métallique, la composition, avant la cuisson, comprenant en % en poids en ce qui concerne la plage de formulation du composant vitreux :

    (i) un composant vitreux comprenant :

    de 7,1 % à 7,9 % de Na2O ;

    de 7,0 % à 7,7 % de K2O ;

    de 0,6 % à 1,0 % ZnO ;

    de 2,7 % à 3,3 % de BaO ;

    de 19,3 % à 20,7 % d'Al2O3 ;

    de 10,8 % à 11,8 % de SiO2 ;

    de 0,7 % à 1,2 % de TiO2 ;

    de 14,4 % à 15,6 % de ZrO2 ;

    de 29,2 % à 31,3 % de P2O5 ; et

    de 0,1 % à 5,2 % de Co2O3.


     
    2. Composition selon la revendication 1, dans laquelle le composant vitreux (i) comprend en outre :

    de 0 % à 1,1 % de NiO ;

    de 0 % à 0,7 % de CuO ;

    de 0 % à 0,8 % de MnO2 ; et

    de 0 % à 1,1 % de Cr2O3.


     
    3. Composition selon la revendication 1, comprenant en outre un additif choisi dans le groupe consistant en 0,78-1,5 % de F et 1,5-4,71 % de NO2.
     
    4. Procédé de formation d'un revêtement d'émail sur un substrat, le procédé comprenant :

    prendre un substrat ;

    prendre une composition comprenant :

    (i) un composant vitreux comprenant en % en poids en ce qui concerne la plage de formulation du composant vitreux :

    de 7,1 % à 7,9 % de Na2O ;

    de 7,0 % à 7,7 % de K2O ;

    de 0,6 % à 1,0 % de ZnO ;

    de 2,7 % à 3,3 % de BaO ;

    de 19,3 % à 20,7 % d'Al2O3 ;

    de 10,8 % à 11,8 % de SiO2 ;

    de 0,7 % à 1,2 % de TiO2 ;

    de 14,4 % à 15,6 % de ZrO2 ;

    de 29,20 % à 31,3 % de P2O5 ; et

    de 0,1 % à 5,2 % de Co2O3 ;

    déposer une couche de la composition sur le substrat ; et

    cuire la couche pour former de cette façon un revêtement d'émail sur le substrat.


     
    5. Procédé selon la revendication 4, dans lequel la composition comprend en outre un additif choisi dans le groupe consistant en 0,78-1,5 % de F et 1,5-4,71 % de NO2.
     
    6. Procédé selon la revendication 4, dans lequel la cuisson est effectuée à une température de 770°C à 870°C.
     
    7. Procédé selon la revendication 4, dans lequel la cuisson est effectuée à la température pendant 2 à 8 minutes.
     
    8. Procédé selon la revendication 4, dans lequel la cuisson est effectuée à une température de 800°C à 850°C.
     
    9. Procédé selon la revendication 4, dans lequel la cuisson est effectuée à la température pendant 3 à 6 minutes.
     
    10. Procédé selon la revendication 4, dans lequel le substrat est choisi dans le groupe consistant en acier et aluminium.
     
    11. Procédé selon la revendication 4, dans lequel la composition est disposée sur une couche de fond.
     
    12. Substrat revêtu obtenu par le procédé selon la revendication 4.
     






    Cited references

    REFERENCES CITED IN THE DESCRIPTION



    This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

    Patent documents cited in the description