(19)
(11)EP 2 576 636 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
26.06.2019 Bulletin 2019/26

(21)Application number: 11720388.5

(22)Date of filing:  12.05.2011
(51)International Patent Classification (IPC): 
C08F 10/00(2006.01)
C08F 10/08(2006.01)
C08F 210/16(2006.01)
C08F 2/34(2006.01)
C08F 10/14(2006.01)
(86)International application number:
PCT/EP2011/002386
(87)International publication number:
WO 2011/147539 (01.12.2011 Gazette  2011/48)

(54)

OLEFIN GAS PHASE POLYMERISATION

OLEFINGASPHASENPOLYMERISATION

POLYMÉRISATION D'OLÉFINE EN PHASE GAZEUSE


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 27.05.2010 EP 10075226

(43)Date of publication of application:
10.04.2013 Bulletin 2013/15

(73)Proprietor: Saudi Basic Industries Corporation
Riyadh 11422 (SA)

(72)Inventors:
  • BANAT, Yahya
    Riyadh 11422 (SA)
  • AL-OBAIDI, Fahad
    Riyadh 11422 (SA)
  • MALEK, Abul Kader
    Riyadh 11422 (SA)

(74)Representative: Sabic Intellectual Property Group 
Sabic Intellectual Property Department P.O. Box 3008
6160 GA Geleen
6160 GA Geleen (NL)


(56)References cited: : 
WO-A1-2011/072850
US-A- 5 352 749
US-A1- 2005 182 207
US-A- 4 588 790
US-A- 5 436 304
US-B1- 6 759 489
  
      
    Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


    Description


    [0001] The invention relates to a process for the polymerisation of olefin monomers, preferably ethylene monomers, in a gas phase polymerization process in a fluidised bed reactor.

    [0002] Olefin polymerization is a very exothermic reaction. Heat needs to be removed continuously so as to keep the temperature in the reactor at the desired level. Such removal may be effected via the gas stream which leaves the reactor at a higher temperature than that at which it is supplied to the reactor. In gas phase polymerization the removal of heat from the bed of growing polymer tends to be a rate limiting step.

    [0003] Conventionally, gas phase polymerization processes typically run continuously, therefore the temperature of the fluidized bed reactor is controlled to an essentially isothermal level through continuously removing the heat of polymerization by circulating the gas exiting from the fluidized bed to a condenser/heat exchanger outside the reactor and recirculating the cooled gas stream back into the reactor. When the temperature of the recirculating stream introduced or recycled into the fluidized bed polymerization reactor is above the dew point temperature, substantially no liquid is present. This process is known as the "dry mode" process. One method to maximize the ability of heat removal is, throughout the operation, to reduce to the lowest possible value the temperature of the gaseous feed stream into the reactor.

    [0004] According to the "condensed mode" process a two phase mixture is directed into the fluidized bed as a fluidizing medium, the liquid portion of which vaporizes when it is exposed to the heat of the reactor. Fluid is formed by cooling the recycle stream below the dew point temperature, thereby converting a portion of the gas into a liquid, and the cooled recycle stream is introduced into the fluidized bed polymerization reactor. The objective is to take advantage of the cooling effect brought about by the vaporization, i.e., by bringing the temperature of the fluidized bed down to a point where degradation of the polymer and the catalyst are avoided and agglomeration of the polymer and chunking are prevented. The liquid phase is provided by a portion of the recycle gases, which includes monomers and low boiling liquid hydrocarbons, inert to the reaction conditions needed for polymerization, and condensation. Condensed mode fluidized bed reactor polymerization processes are disclosed in for example US 4543399 and US 4588790. These publications describe the introduction of an inert liquid into the recycle stream to increase the dew point temperature of the recycle stream and allowing the process to operate at levels of up to 17.4% liquid by weight, based on the total weight of the cooled recycle stream. A condensed mode process is advantageous because its ability to remove greater quantities of heat generated by polymerization increases the polymer production capacity of a fluidized bed polymerization reactor. A commonly used liquid hydrocarbon is isopentane, which boils at about 27 °C., and consequently becomes a vapor in the recycle line in view of the heat present in the recycle gases. The recycle gases leave the reactor, are cooled, and then condensed to the extent that a vapor phase and liquid phase are formed. The velocity of the recycled gas/liquid mixture should be sufficient to support the fluidized bed, but slow enough to avoid excessive entrainment of fines. The cooling capacity should be sufficient to improve the production rate in terms of space/time/yield.

    [0005] "Super condensed mode" fluidized bed reactor polymerization processes operate with above 17.4% liquid by weight in the cooled recycle stream as described for example in US 5352749. These must be confined under certain more specific and restrictive conditions within a limited range of operating conditions to avoid destabilizing the fluidized bed, thereby halting the process.

    [0006] Condensed and super condensed mode processes have been limited due to several factors including only an estimate of the amount of liquid entering the bed was controlled /monitored. The negatives reside in the limit placed upon the production rate, i.e., space/time/yield, which is influenced by the maximum rate at which heat can be removed from the reactor; the introduction of hydrocarbons other than monomers, which, although considered inert, can affect the polymer morphology and the static, chunking, and sheeting, which plague many polymerization runs; flooding and frothing at the bottom of the reactor due to too much liquid; and the requirement for additional cooling and condensing equipment for converting the recycle stream to the gas/liquid mixture.

    [0007] Fraser et al. discloses in "Manufacturing efficiencies from metallocene catalysis in gas phase polyethylene production" (1997, Univation Technologies) the general concept of the olefin gas phase process. Generally in gas phase polymerization of olefins the feed stream passes through a fluidized or stirred bed of growing polymer particles. The growing polymer particles are fluidised by a recycle gas stream of monomer, co-monomer, hydrogen, nitrogen and inert condensing gas. The cycle gas flow provides monomer and co-monomer for polymerization, agitates the bed and also removes the heat of polymerization. The cycle gas exits the top of the reactor and is then compressed through a compressor and cooled via a heat exchanger before being fed into the bottom of the fluidised bed. The recycle stream is made up with additional feed stream and returned to the bed of growing polymer. The monomer in the feed stream contacts the catalyst in the growing polymer particles and is polymerized.

    [0008] A preferred reactor system to be applied for this gas phase polymerisation is a vertical elongated reactor in which a bed of polymer particles is maintained in fluidised condition with the aid of an ascending gas feed stream which contains the gaseous monomer(s) to be polymerised. The reactor comprises a reaction zone which is confined at the underside by a gas distribution plate and at the top side by a virtual end surface, in which the fluidised bed is maintained between the underside and the top side and in which at least part of the gaseous stream withdrawn from the top of the reactor is cooled to a point where the stream partially condenses into a liquid, and in which at least part of the resulting two-phase stream is recycled to the reactor via an inlet which terminates in the reactor below the gas distribution plate.

    [0009] The ascending gas stream may contain an inert gas and for example hydrogen as a chain length regulator. The inert gas is added to control the dew point of the gas mixture. Suitable inert gases include for example nitrogen and inert hydrocarbons such as (iso)butane, (iso)pentane and (iso)hexane. The inert gas may be added to the gas stream as a gas or, in condensed form, as a liquid. The gas stream is discharged through the top of the reactor and, after certain processing operations, fresh monomer is added to it to make up for the monomer(s) consumed in the polymerisation, and then the gas stream is again supplied to the reactor as (a portion of) the ascending gas stream in order to maintain the bed. A catalyst is also added to the bed.

    [0010] It is a disadvantage of the known processes to promote the levels of condensation in the recycle stream that are required to enter the super-condensed regimen requires such amounts of non-volatile constituents that may harm the stable operation of the reactor. In order to reach higher production rates, the attainment of higher heat removal ability is not sufficient, since it is also essential to keep a stable operation. In case the stable operation cannot be kept as such, the heat removal ability is no longer the limiting factor for the production rate, while the advantage of the operation in the condensed and super-condensed modes is lost. The difficulties in keeping the process stability in the super-condensed mode as well as the ways of keeping pace with those drawbacks are discussed in US 5352749 and US 5436304.

    [0011] In further variations of the gas phase polymerization process, where co-monomers of longer chains and consequently lower volatility such as 1-pentene, 1-hexene or 1-octene are applied in relatively high amounts for copolymerizing with the primary monomer, due to problems related to the suitable heat removal and to the stability of the reactor bed; the combination of the process conditions with the features of such monomers may lead to the partial condensation of said co-monomers and to the consequent impossibility to operate the process under high production rates.

    [0012] EP1196238 discloses a process for the gas phase polymerisation of one or more olefin monomers in a fluidised bed reactor, which reactor comprises a reaction zone which is confined at the underside by a gas distribution plate and at the top side by a virtual end surface, in which a fluidised bed is maintained between the underside and the top side, and in which at least part of the gaseous stream withdrawn from the top of the reactor is cooled and in which at least part of the resulting two-phase stream is recycled to the reactor and wherein the gas stream comprises an inert gas.

    [0013] In general, the conventional fluidized bed reactors used in gas-phase olefin polymerization may have a cylindrical shaped fluidized bed section and an enlarged conical entrainment disengaging section. During the course of polymerization, fresh polymer particles are produced by catalytic polymerization of olefin, eg ethylene. Such polymer particles are projected upward into the disengaging section through the flowing gas and most of these particles return to the fluidized bed by gravity as their velocity decreases in the disengaging section. However, some of fine particles "fines" are elutriated out of the projected particles and do not return to the fluidized bed by gravity. Such fines either leave with the flowing gas through the reactor outlet or accumulate in the disengaging section. Consequently, high levels of fines in the reactor may cause significant operating difficulties either within the reactor itself, or outside the reactor represented by piping system, heat exchangers, compressors, and reactor inlet gas distribution grid. Within the fluidized bed section, fines are considered the major reason for the formation of wall sheeting.

    [0014] US2005/182207 describes a continuous gas fluidized bed polymerization process for the production of a polymer from a monomer including continuously passing a gaseous stream comprising the monomer through a fluidized bed reactor in the presence of a catalyst under reactive conditions; withdrawing a polymeric product and a stream comprising unreacted monomer gases; cooling said stream comprising unreacted monomer gases to form a mixture comprising a gas phase and a liquid phase and reintroducing said mixture into said reactor with sufficient additional monomer to replace that monomer polymerized and withdrawn as the product, wherein said liquid phase is vaporized, and wherein the stream comprises at least two inert condensing agents selected from the group consisting of alkanes, cycloalkanes, an mixtures thereof, each of the inert condensing agents having a normal boiling point less than 40 °C.

    [0015] US6759489 discloses a continuous gas fluidized bed method for making a polymer featuring a condensing agent in a recycle stream; and also to methods for monitoring and providing continuity in a gas fluidized bed method for making a polymer featuring a condensing agent in a recycle stream.

    [0016] US5436304 is directed toward polymerizing or copolymerizing alpha-olefins either alone or in combination with one or more other alpha-olefins in a gas phase reactor having a fluidized bed and a fluidizing medium such that the fluidizing medium entering the reactor comprises a gas and a liquid phase.

    [0017] US5352749 is directed toward polymerizing or copolymerizing alpha-olefins either alone or in combination with one or more other alpha-olefins in a gas phase reactor having a fluidized bed and a fluidizing medium such that the fluidizing medium entering the reactor comprises a gas and a liquid phase.

    [0018] US4588790 discloses a continuous gas fluidized bed process for the production of polymer from monomer wherein a gaseous stream comprising monomer is passed through a fluidized bed in a reaction zone in the presence of catalyst under reactive conditions, withdrawing from the reaction zone polymeric product and a stream comprising unreacted gases and solid particles, cooling the stream an recycling the cooled stream to the reaction zone together with sufficient additional monomer to replace monomer polymerized and withdrawn as polymer product, and wherein at least a part of the recycle stream is cooled to condense a portion thereof and form a liquid-containing mixture wherein the weight ratio of liquid to solid particles is not less than about two to one and introducing the mixture into the reaction zone wherein the liquid in the mixture is vaporized.

    [0019] WO2011/072850 describes a process for the polymerization of olefins a temperatures of from -20 to 200 °C and pressures of from 0.1 to 20 MPa in the presence of a polymerization catalyst and an anti-static agent, wherein the antistatic agent is an antistatically acting composition comprising a polysulfone copolymer, a polymeric compound comprising basic nitrogen atoms, an oil-soluble sulfonic acid an optionally a solvent and the polysulfone copolymer, the polymeric compound comprising basic nitrogen atoms and the oil soluble sulfonic acid constitute together at least 1 wt.-% of the antistatically acting composition.

    [0020] It is the object of the present invention to provide a process for the polymerisation of one or more olefin monomers in a gas phase polymerization process in a fluidised bed reactor that combines running the fluidized bed reactor with cooling capacity sufficient to improve the production rate of dry mode and (super-)condensed mode fluidized bed reactor polymerization processes.

    [0021] Furthermore the desired polymer properties for example a high polymer particle density, a high polymer bulk density, a high catalyst productivity and improved polymer morphology should be obtained.

    [0022] This object is achieved with a process for the gas phase polymerisation of one or more olefin monomers in a fluidised bed reactor in a dry mode or in a (super) condensed mode with a gas stream comprising an inert gas, characterised in that the inert gas comprises a mixture of inert components:
    1. (1) 5-60 % by mol of nitrogen
    2. (2) 10-90 % by mol of a gas heat capacity increasing agent which regulates the dew point and at the same time improves the vapor stream heat capacity
    3. (3) 1-50 % by mol of a sorption promoting agent which acts as promoting agent of the ethylene and alpha olefins local concentrations at the growing polymer micro-particle level where sorption of such components into the polyethylene increases the local concentration of ethylene and/or alpha-olefins in terms of micro-conditions surrounding the catalyst active sites and
    4. (4) 0.1- 10 % by mol of a polymer swelling agent which acts as a polymer physical and viscoelastic properties modifying agent, developed instantaneously during polymer growth, by swelling and plasticizing the polymer formed during growth and which agent influences the characteristics of the crystalline phase, wherein the gas heat capacity increasing agent is a saturated (C2-C3) hydrocarbon or a mixture of these hydrocarbons, the sorption promoting agent is (C4) hydrocarbon n-butane and the polymer swelling agent is a saturated (C5-C20) hydrocarbon or a mixture of at least two different saturated (C5-C20) hydrocarbons and wherein the total amount of the inert components (1), (2), (3) and (4) is 100%.


    [0023] According to a preferred embodiment of the invention the process takes place in a reactor which comprises a reaction zone which is confined at the underside by a gas distribution plate and at the top side by a virtual end surface, in which a fluidised bed is maintained between the underside and the top side, and in which at least part of the gaseous stream withdrawn from the top of the reactor is cooled and in which at least part of the resulting two-phase stream is recycled to the reactor and wherein the gas stream comprises an inert gas, comprising a mixture of inert components:
    1. (1) nitrogen
    2. (2) a gas heat capacity increasing agent
    3. (3) a sorption promoting agent and
    4. (4) a polymer swelling agent.


    [0024] The recycle stream is made up with additional feed stream and returned to the bed of growing polymer. The feed stream in the recycle stream comprises olefin monomers and the mixture of inert components.

    [0025] According to a preferred embodiment the olefin is ethylene. In case the olefin is ethylene, the amount of ethylene in the feed stream ranges between 50 % by weight and 95% by weight of the total amount of olefin monomers. Suitable co-monomers include for example 1-butene, 1-hexene and propylene.

    [0026] The process according to the invention results in an improved process especially in terms of space/time/yield and at the same time enabling a broader range of operating conditions of the fluidized bed reactor polymerization process.

    [0027] According to a preferred embodiment of the invention the gas phase polymerisation takes place via the (super) condensed mode process.

    [0028] Preferably the inert components are saturated compounds.

    [0029] The gas heat capacity increasing agent in the feed stream to a gas phase reactor regulates the dew point and at the same time improves the vapour stream heat capacity.

    [0030] Preferably the gas heat capacity increasing agent is ethane.

    [0031] The sorption promoting agent acts as promoting agent of the ethylene and alpha olefins local concentrations at the growing polymer micro-particle level where sorption of such components into the polyethylene increases the local concentration of ethylene and/or alpha-olefins in terms of micro-conditions surrounding the catalyst active sites. This physical phenomenon is known as co-solubility.

    [0032] It is an advantage of the present invention that the sorption of the hydrocarbons into the growing polymer particles permits promoting catalyst activity.

    [0033] The polymer swelling agent acts as a polymer physical and viscoelastic properties modifying agent, developed instantaneously during polymer growth by swelling and plasticizing the polymer formed during growth. Furthermore the polymer swelling agent influences the characteristics of the crystalline phase, such as crystallinity, lamellar thickness, and the interfacial structure of the crystallites. Additionally the polymer swelling agent functions as a delaying agent for the crystallization kinetics during polymer growth. Accordingly the swelling agent reduced the production of fines during polymerization and additionally the swelling agent increases the particle density through controlling the catalyst fragmentation. Generally the applied swelling agents have a normal boiling point higher than 40 °C.

    [0034] Preferably the polymer swelling agent is n-pentane or iso-pentane.

    [0035] It is possible to apply for example iso-pentane as the sorption promoting agent and also as swelling promoting agent. In this case iso-pentane may be present in an amount between for example 1.1 and 60 % by mole.

    [0036] According to a further preferred embodiment of the invention the mixture comprises
    1. (1) nitrogen
    2. (2) ethane
    3. (3) n-butane and
    4. (4) n-pentane or iso-pentane
      wherein the total amount of the inert components (1), (2), (3) and (4) is 100%.


    [0037] Preferably the mixture comprises
    1. (1) 5-60 % by mol of nitrogen
    2. (2) 10-90 % by mol of ethane
    3. (3) 1-50 % by mol of n-butane and
    4. (4) 0.1-10 % by mol of n-pentane or iso-pentane
      wherein the total amount of the inert components (1), (2), (3) and (4) is 100%.


    [0038] More preferably the mixture comprises
    1. (1) 10-50 % by mol of nitrogen
    2. (2) 25-80 % by mol of ethane
    3. (3) 5-45 % by mol of n-butane and
    4. (4) 0.1-45 % by mol of n-pentane or iso-pentane
      wherein the total amount of the inert components (1), (2), (3) and (4) is 100%.


    [0039] The polymerization process according to the present invention combines running the fluidized bed reactor with cooling capacity sufficient to improve the production rate in terms of space/time/yield and at the same time enabling a broader range of operating conditions of a dry and condensed mode fluidized bed reactor polymerization method regardless of the type of catalyst used and polymer properties with high polymer particle density, polymer bulk density, promoted catalyst productivity and improved polymer morphology process for the reduction of powder fines in a fluid bed polyethylene process.

    [0040] It is another advantage that the process according to the invention results in a reduction of fines to a low level in for example the polyethylene production process of a fluid bed reactor through the introduction of promoting agents of the ethylene and alpha olefins local concentrations at the growing polymer micro-particle level and through the introduction at the same time agents of instantaneous viscoelastic local properties improving agents while furthermore at the same time the maintenance of the operation without stability problems in the reactor bed or of entrainment of polymer particles is secured.

    [0041] The process according to the present invention comprises (co)polymerizing a feed of gaseous olefin monomers under polymerization conditions, in gas phase reactors, in the condensed or non condensed mode where a specific mole fraction of the recycle stream is made up of inert components, admixed in specific amounts, said compositions maximize the heat transport properties both microscopically (at the particle level) and macroscopically (at the reactor level). Macroscopic implies the total volume of the reactor whereas microscopic refers to the immediate vicinity around the catalytic sites where polymerization takes place. When cooling improves, catalyst productivity and polymer properties will improve. At the same time, reactor operability becomes more robust since hot spotting, sheeting, and chunking are reduced.

    [0042] The use of the swelling agent results in improved viscoelastic properties in addition to better heat removal through all components and consequently the process according to the present invention results in a reduced amount of fines.

    [0043] The process according to the present invention is suitable for the manufacture of polyolefins in the gas phase by the polymerisation of one or more olefin monomers.The polymers may be homopolymers and copoymers of ethylene and/or propylene or copolymers of ethylene or propylene with one or more C2-C8 alpha-olefins such as for example ethylene, propylene, butene-1, pentene-1, hexene-1, 4-methylpentene-1, and octene-1. Higher olefins for example decene-1 or dienes for example 1,4-butadiene, 1,6-hexadiene, dicyclopentadiene, ethylidene norbornene and vinyl norbornene may also be applied.

    [0044] Preferably the process is an ethylene homo polymerization or an ethylene - alpha-olefin co-polymerization process.

    [0045] Preferably the pressure of the polymerisation process ranges between 0.5 and 10 MPa and the temperature ranges between 30°C and 130°C.

    [0046] A catalyst is also added to the bed. During the process, under the influence of the catalyst present, fresh polymer is continuously formed and at the same time polymer that has formed is withdrawn from the bed, with the bed volume and mass being kept substantially constant.

    [0047] It is another advantage of the present invention that the object is obtained regardless of the applied type of catalyst.

    [0048] The polymerisation reaction may be carried out in the presence of any known suitable catalyst system for the gas phase polymerisation for example a catalyst system of the Ziegler-Natta type, a chromium based catalyst system and a metallocene based catalyst system.

    [0049] The catalyst may also be in the form of a prepolymer powder prepared in a prepolymerisation stage with the aid of a catalyst system described above. The prepolymerisation may be carried out by any known process, for example, polymerisation in a liquid hydrocarbon diluent or in the gas phase using a batch process, a semi-continuous process or a continuous process.

    [0050] US2005/182207 discloses a continuous gas fluidized bed polymerization process for the production of a polymer from a monomer including continuously passing a gaseous stream comprising the monomer through a fluidized bed reactor in the presence of a catalyst under reactive conditions; withdrawing a polymeric product and a stream comprising unreacted monomer gases; cooling said stream comprising unreacted monomer gases to form a mixture comprising a gas phase and a liquid phase and reintroducing said mixture into said reactor with sufficient additional monomer to replace that monomer polymerized and withdrawn as the product, wherein said liquid phase is vaporized, and wherein the stream comprises at least two inert condensing agents selected from the group consisting of alkanes and cycloalkanes. US 2005/0182207 applies at least two inert condensing agents of normal boiling point less than 40 °C. Technically this means that the inert component condenses at the inlet conditions below the distributor plate. Therefore, ethane is not used since it does not condense by itself in the absence of other induced condensing agent. Ethane is not an induced condensing agent. Additionally, ethane with low concentration (0 mol% - 4 mol%) will be present in any gas phase ethylene polymerization process as impurity with ethylene feedstock or being generated in the reactor due to hydrogenation of ethylene or even as a by product of metal alkyls reaction with traces of water in the reactor. Furthermore, in contrast to US 2005/0182207 in the present patent application swelling agents are applied which have generally a normal boiling point higher than 40 °C.

    [0051] US6759489 discloses a continuous gas fluidized bed methods for making a polymer featuring a condensing agent in a recycle stream and also to methods for monitoring and providing continuity in a gas fluidized bed method for making a polymer featuring a condensing agent in a recycle stream.

    [0052] US5436304 relates to a process for polymerizing alpha-olefins in a gas phase reactor at significantly higher production rates than herefore envisaged. The invention is directed toward a process for polymerizing alpha-olefins in a gas phase reactor having a fluidized bed and a fluidizing medium where the level of liquid in the fluidizing medium is greater than 15 weight percent based on the total weight of the fluidizing medium. Further US5436304 relates to a method for determining stable operating conditions of a gas phase fluidized bed polymerization reactor by identifying a property useful to determine stability of a fluidized bed and controlling the composition of a fluidizing medium or recycle stream to establish a range of values for the property to maintain the stable operating condition.

    [0053] US5352749 discloses a process for polymerizing alpha-olefin(s) in a gas phase reactor having a fluidized bed and a fluidizing medium wherein the fluidizing medium serves to control the cooling capacity of said reactor, the improvement comprising employing a level of liquid in the fluidizing medium entering the reactor which is in the range of from 17.4 to 50 weight percent based on the total weight of the fluidizing medium and maintaining the ratio of fluidized bulk density to settled bulk density above 0.59.

    [0054] US2005/182207, US6759489, US5436304 and US5352749 do not describe the use of a mixture of inert components comprising nitrogen, a gas heat capacity increasing agent, a sorption promoting agent and a polymer swelling agent.

    [0055] US2005/182207, US6759489, US5436304 and US5352749 do not describe the specific mixture comprising 5-60 % by mol nitrogen; 10- 90 % by mol of the gas heat capacity increasing agent; 1-50 % by mol of the sorption promoting agent and 0.1-10 % by mol of the polymer swelling agent.

    [0056] US2005/182207, US6759489, US5436304 and US5352749 do not describe the specific mixture comprising 5-60 % by mol of nitrogen; 10-90 % by mol of ethane; 1-50 % by mol of n-butane and 0.1-10 % by mol of n-pentane or iso-pentane.

    [0057] The invention will be elucidated by means of the following non-limiting examples.

    Example II and Comparative Examples I and A



    [0058] A polymerization process in fluidized bed was used to carry out the polymerization of ethylene and 1-hexene in the non condensed dry mode in accordance with the conditions as disclosed in Example 9 of US 4588790.

    [0059] In comparative example I iso-pentane was replaced partially (about 25 %) by n-pentane. n-pentane has a higher solubility than iso-pentane in polyethylene by about 12% and n-pentane has higher heat transfer capabilities than iso-pentane by about 4 %.

    [0060] In Example II iso-pentane was replaced by a mixture of n-butane and n-pentane. n-pentane has higher solubility than iso-pentane in polyethylene by about 12% and n-butane has a lower solubility by about 40 % Further, n-pentane has higher heat transfer capabilities than iso-pentane by about 4 % , n-butane has much lower boiling point of -0.6 °C compared to a boiling point of 27.8 °C for iso-pentane and with approximately similar heat transfer capabilities as iso-pentane.

    [0061] Comparing comparative example I and comparative Example A, an increase in the production rate of about 24 percent was obtained by replacing more than 70% of nitrogen by ethane and use of n-pentane and iso pentane.

    [0062] Comparing comparative Example A and Example II, an improvement in the production rate of about 28 percent was obtained by replacing more than 70% of nitrogen by ethane and n-butane to maximize the heat transport properties both microscopically at the particle level and macroscopically at the reactor level.
    TABLE 1
    ExampleAIII
    internal Reactor diameter (m) 3.5 3.5 3.5
    Recycle Gas Superficial Velocity (m/s) 0.673 0.673 0.673
    Recycle Gas Composition (mole fraction):      
    Ethylene 0.393 0.393 0.393
    1-Hexene (co-monomer) 0.047 0.047 0.047
    Hydrogen 0.062 0.062 0.062
    Nitrogen 0.358 0.1 0.085
    Ethane (gas heat capacity increasing agent) 0.126 0.384 0.38
    iso-pentane (sorption promoting and polymer swelling promoting agent) 0.014 0.010 0
    n-Butane (sorption promoting agent) - - 0.03
    n-Pentane (polymer swelling agent) - 0.004 0.003
    Recycle Gas Density (kg/m3) 22.84 24.12 24.55
    Reactor Temperature (°C) 94.9 94.9 94.9
    Reactor Inlet Temperature (°C) 61.6 61.6 61.6
    Reactor Pressure (psig) 309.2 309.2 309.2
    Reactor inlet Pressure (psig) 323.5 323.5 323.5
    Inlet Dew Point Temperature (°C) 59.0 59.9 60.0
    Operation Mode dry dry dry
    Condensed Liquid in Recycle Stream (% weight) - - -
    Production Rate (ton/h) 9.87 12.26 12.60

    Example IV and comparative examples III and B



    [0063] A polymerization process in fluidized bed was carried out in accordance with the disclosure of Example 9 in US 4588790.

    [0064] The examples show an increase in the production rate of about 8 and 11 percent, respectively, obtained in condensed mode of operation by replacing more than 40% of nitrogen by ethane (comparative example III) and more than 90% of nitrogen by ethane (Example IV).
    TABLE 2
    ExampleBIIIIV
    internal Reactor diameter (m) 3.5 3.5 3.5
    Recycle Gas Superficial Velocity (m/s) 0.64 0.64 0.64
    Recycle Gas Composition (mole fraction):      
    Ethylene 0.474 0.474 0.393
    1-Hexene 0.056 0.056 0.047
    Hydrogen 0.074 0.074 0.062
    Nitrogen 0.27 0.164 0.085
    Ethane (gas heat capacity increasing agent) 0.114 0.222 0.38
    iso-pentane (sorption promoting and polymer swelling promoting agent) 0.012 0.0075 0
    n-Butane (sorption promoting agent) - - 0.03
    n-Pentane (polymer swelling agent) - 0.0025 0.003
    Recycle Gas Density (kg/m3) 22.95 23.39 23.71
    Reactor Temperature (°C) 94.7 94.7 94.7
    Reactor Inlet Temperature (°C) 56.1 56.1 56.1
    Reactor Pressure (psig) 306.8 306.8 306.8
    Reactor inlet Pressure (psig) 321.1 321.1 321.1
    Inlet Dew Point Temperature (°C) 62.6 62.7 62.8
    Operation Mode Condensed Condensed Condensed
    Condensed Liquid in Recycle Stream (% weight) 4.0 4.1 4.1
    Production Rate (ton/h) 12.34 13.39 13.77

    Comparative examples V-VIII and C



    [0065] The polymerization process of ethylene and 1-butene in the dry mode in fluidized bed was carried out in accordance with the conditions as disclosed in Example 10 of US 4588790.

    [0066] Comparing the comparative example C and comparative example V an increase in the production rate of about 11 percent was obtained in dry mode by replacing more than 60% of nitrogen by ethane without impacting the dew point of the inlet recycle stream.

    [0067] Comparing the comparative example C and comparative example VI an increase in the production rate of about 26 % was obtained by replacing about 50% of nitrogen by ethane, and the use of about 25% of iso-pentane as n-pentane.

    [0068] In comparative example VI the use of about 68% of isopentane (compared to comparative example C) resulted in a remarkable reduction in the dew point of the inlet recycle stream which enabled lowering the recycle stream inlet temperature which contributed to further improvement of the production rate.

    [0069] Comparative example VII shows an increase in the production rate by replacing about 50% of nitrogen by ethane.

    [0070] Comparative example VIII shows an increase in the production rate of about 70 percent by replacing more than 50% of nitrogen by ethane, and the use of about 39% of isopentane (compared to comparative example C) with about 25% of iso-pentane as n-pentane.
    TABLE 3
    ExampleCVVIVIIVIII
    internal Reactor diameter (m) 2.44 2.44 2.44 2.44 2.44
    Recycle Gas Superficial Velocity (m/s) 0.78 0.78 0.78 0.78 0.78
    Recycle Gas Composition (mole fraction):          
    Ethylene 0.4236 0.4236 0.427 0.427 0.427
    1-Butene 0.1558 0.1558 0.157 0.157 0.157
    Hydrogen 0.0694 0.0694 0.070 0.07 0.07
    Nitrogen 0.1915 0.0724 0.096 0.096 0.09
    Ethane (gas heat capacity increasing 0.0228 0.1419 0.137 0.147 0.183
    iso-pentane (sorption promoting and polymer swelling promoting agent) 0.1319 0.1319 0.090 0.075 0.052
    n-Butane (sorption promoting agent) 0.0020 0.0020 - - -
    n-Pentane (polymer swelling agent) - - 0.020 0.025 0.018
    Recycle Gas Density (kg/m3) 26.50 27.32 26.26 25.88 24.77
    Reactor Temperature (°C) 85.1 85.1 85.1 85.1 85.1
    Reactor Inlet Temperature (°C) 68.6 67.1 63.5 61.5 53.8
    Reactor Pressure (psig) 269.4 269.4 269.4 269.4 269.4
    Reactor inlet Pressure (psig) 284.5 284.5 284.5 284.5 284.5
    Inlet Dew Point Temperature (°C) 66.2 65.4 61.7 59.8 52.2
    Operation Mode Dry Dry Dry Dry Dry
    Condensed Liquid in Recycle Stream (% weight) - - - - -
    Production Rate (ton/h) 3.6 4.0 4.54 4.88 6.15

    Example X and comparative examples IX and D



    [0071] A polymerization process in fluidized bed was used to polymerize ethylene and 1-butene in the condensed mode in accordance with the disclosure of example 10.a in US 4588790. Table 4 shows that when comparing the comparative example D, with comparative example IX and Example X an increase in the production rate of about 11 and 37 percent, respectively, was obtained.
    TABLE 4
    ExampleDIXX
    internal Reactor diameter (m) 2.44 2.44 2.44
    Recycle Gas Superficial Velocity (m/s) 0.49 0.49 0.49
    Recycle Gas Composition (mole fraction):      
    Ethylene 0.4377 0.446 0.446
    1-Butene 0.1590 0.162 0.162
    Hydrogen 0.0883 0.09 0.090
    Nitrogen 0.1600 0.09 0.080
    Ethane (gas heat capacity increasing agent) 0.0236 0.112 0.090
    iso-pentane (sorption and polymer swelling promoting agent) 0.1266 0.1 -
    n-Butane (sorption promoting agent) 0.0020 - 0.120
    n-Pentane (polymer swelling agent) - - 0.012
    Recycle Gas Density (kg/m3) 25.58 25.02 24.78
    Reactor Temperature (°C) 85.1 85.1 85.1
    Reactor Inlet Temperature (°C) 53.5 48.0 41
    Reactor Pressure (psig) 264.9 264.9 264.9
    Reactor inlet Pressure (psig) 276.2 276.2 276.2
    Inlet Dew Point Temperature (°C) 63.3 58.0 49.5
    Operation Mode Condensed Condensed Condensed
    Condensed Liquid in Recycle Stream (% weight) 14.4 14.3 14.5
    Production Rate (ton/h) 5.83 6.50 7.40

    Example XII and comparative examples XI, XIII and E



    [0072] A polymerization process in fluidized bed for the polymerization of ethylene and 1-butene in the condensed mode was carried out in accordance with the disclosure of Example 6.2 from US 6759489 B1.

    [0073] Comparing the comparative example E and the comparative examples XI and XII as well as Example XII an increase in the production rate of about 16, 16, and 21 percent, respectively, was obtained.
    TABLE 5
    ExampleEXIXIIXIII
    Internal Reactor diameter (m) 4.42 4.42 4.42 4.42
    Recycle Gas Superficial Velocity (m/s) 0.77 0.77 0.77 0.77
    Recycle Gas Composition (mole fraction):        
    Ethylene 0.3292 0.3292 0.3269 0.3269
    1-Butene 0.1319 0.1319 0.1310 0.1310
    Hydrogen 0.0687 0.0687 0.0682 0.0682
    Nitrogen 0.3433 0.1822 0.0820 0.0850
    Ethane (gas heat capacity increasing 0.0343 0.1954 0.2599 0.3119
    Iso-pentane (sorption promoting and polymer swelling promoting agent) 0.0925 0.0925   0.0770
    n-Butane (sorption promoting agent) - - 0.1200 -
    n-Pentane (polymer swelling agent) - - 0.0120 -
    Recycle Gas Density (kg/m3) 26.85 27.88 28.61 27.93
    Reactor Temperature (°C. 88 88 88 88
    Reactor Inlet Temperature (°C) 39.0 39.0 39.0 39.0
    Reactor Pressure (psig) 305 305 305 305
    Reactor Inlet Pressure (psig) 320 320 320 320
    Inlet Dew Point Temperature (°C) 57.7 58.9 52.6 55.6
    Operation Mode Condensed Condensed Condensed Condensed
    Condensed Liquid in Recycle Stream (% weight) 21.0 22.0 21.2 20.1
    Production Rate (ton/h) 45.6 52.9 55.6 52.7

    Examples XV-XVI and comparative examples XIV and F



    [0074] A polymerization process in fluidized bed was carried out to polymerize ethylene and 1-hexene in the condensed mode in accordance with the reaction conditions as disclosed in Example 3 in WO 99/06451.

    [0075] Comparing the comparative example F and the comparative example XIV as well as the Examples XV and XVI in Table 6 shows an increase in the production rate of about 22, 32 and 43 percent, respectively was obtained.
    TABLE 6
    ExampleFXIVXVXVI
    internal Reactor diameter (m) 4.42 4.42 4.42 4.42
    Recycle Gas Superficial Velocity (m/s) 0.77 0.77 0.77 0.77
    Recycle Gas Composition (mole fraction):        
    Ethylene 0.333 0.333 0.333 0.333
    1-Hexene 0.047 0.047 0.047 0.047
    Hydrogen 0.06 0.06 0.06 0.06
    Nitrogen 0.458 0.158 0.1 0.09
    Ethane (heat capacity increasing agent) 0 0.3 0.273 0.327
    Iso-pentane (sorption promoting and polymer swelling promoting agent) 0.093 0.093 - -
    n-Hexane 0.009 0.009 - -
    n-Butane (sorption swelling agent) - - 0.17 0.13
    n-Pentane (polymer swelling agent) - - 0.017 0.013
    Recycle Gas Density (kg/m3) 25.33 27.07 28.55 27.33
    Reactor Temperature (°C) 87.0 87.0 87.0 87.0
    Reactor Inlet Temperature (°C) 51.0 51.0 51.0 43.0
    Reactor Pressure (psig) 310 310 310 310
    Reactor Inlet Pressure (psig) 325 325 325 325
    Inlet Dew Point Temperature (°C) 77.6 78.1 74.4 70.5
    Operation Mode Condensed Condensed Condensed Condensed
    Condensed Liquid in Recycle Stream (% weight) 18.8 14.3 14.5 14.5
    Production Rate (ton/h) 34.8 42.6 45.9 49.7



    Claims

    1. Process for the gas phase polymerisation of one or more olefin monomers in a fluidised bed reactor in a dry mode or in a (super) condensed mode with a gas stream comprising an inert gas characterised in that the inert gas comprises a mixture of inert components:

    (1) 5-60 % by mol of nitrogen

    (2) 10- 90 % by mol of a gas heat capacity increasing agent which regulates the dew point and at the same time improves the vapor stream heat capacity

    (3) 1-50 % by mol of a sorption promoting agent which acts as promoting agent of the ethylene and alpha olefins local concentrations at the growing polymer micro-particle level where sorption of such components into the polyethylene increases the local concentration of ethylene and/or alpha-olefins in terms of micro-conditions surrounding the catalyst active sites and

    (4) 0.1-10 % by mol of a polymer swelling agent which acts as a polymer physical and viscoelastic properties modifying agent, developed instantaneously during polymer growth, by swelling and plasticizing the polymer formed during growth and which agent influences the characteristics of the crystalline phase, wherein the gas heat capacity increasing agent is a saturated (C2-C3) hydrocarbon or a mixture of these hydrocarbons, the sorption promoting agent is (C4) hydrocarbon n-butane and the polymer swelling agent is a saturated (C5-C20) hydrocarbon or a mixture of at least two different saturated (C5-C20) hydrocarbons, the polymer swelling agent being n-pentane or iso-pentane, and wherein the total amount of the inert components (1), (2), (3) and (4) is 100%..


     
    2. Process for the gas phase polymerisation of one or more olefin monomers in a fluidised bed reactor according to Claim 1 wherein the reactor comprises a reaction zone which is confined at the underside by a gas distribution plate and at the top side by a virtual end surface, in which a fluidised bed is maintained between the underside and the top side, and in which at least part of the gaseous stream withdrawn from the top of the reactor is cooled and in which at least part of the resulting two-phase stream is recycled to the reactor and wherein the gas stream comprises an inert gas comprising a mixture of inert components:

    (1) nitrogen

    (2) a gas heat capacity increasing agent

    (3) a sorption promoting agent, and

    (4) a polymer swelling agent.


     
    3. Process according to any one of Claims 1-2 characterised in that the mixture comprises

    (1) 10-50 % by mol of nitrogen

    (2) 25- 80 % by mol of a (C2-C3) hydrocarbon

    (3) 1-45 % by mol of a (C4) hydrocarbon and

    (4) 0.2-7 % by mol of a (C5-C20) hydrocarbon

    wherein the total amount of the inert components (1), (2), (3) and (4) is 100%.
     
    4. Process according to any one of Claims 1-3 characterised in that the gas heat capacity increasing agent is ethane.
     
    5. Process according to any one of Claims 1-4 characterised in that the polymer swelling agent is n-pentane.
     
    6. Process according to any one of Claims 1-5 characterised in that the olefin monomer is an ethylene monomer wherein the amount of ethylene in the feed stream ranges between 50 % by weight and 95% by weight of the total amount of olefin monomers.
     


    Ansprüche

    1. Verfahren zur Gasphasenpolymerisation eines oder mehrerer Olefinmonomere in einem Wirbelschichtreaktor in einem Trockenmodus oder in einem (super)kondensierten Modus mit einem Gasstrom, der ein Inertgas umfasst, dadurch gekennzeichnet, dass das Inertgas ein Gemisch von inerten Komponenten umfasst:

    (1) 5-60 mol-% Stickstoff,

    (2) 10-90 mol-% an einem die Gas-Wärmekapazität erhöhenden Mittel, das den Taupunkt reguliert und zugleich die Dampfstrom-Wärmekapazität verbessert,

    (3) 1-50 mol-% an einem sorptionsfördernden Mittel, das als förderndes Mittel der lokalen Konzentrationen von Ethylen und alpha-Olefinen auf der Ebene der wachsenden Polymermikropartikel wirkt, wobei Sorption derartiger Komponenten in das Polyethylen die lokale Konzentration von Ethylen und/oder alpha-Olefinen hinsichtlich der Mikrobedingungen, die die aktiven Katalysatozentren umgeben, erhöht, und

    (4) 0,1-10 mol-% an einem Polymerquellmittel, das als physikalische und viskoelastische Eigenschaften des Polymers modifizierendes Mittel, sofort während des Polymerwachstums entwickelt, durch Quellen und Plastifizieren des während des Wachstums gebildeten Polymers wirkt, wobei das Mittel die Eigenschaften der kristallinen Phase beeinflusst, wobei das die Gas-Wärmekapazität erhöhende Mittel ein gesättigter (C2-C3)-Kohlenwasserstoff oder ein Gemisch derartiger Kohlenwasserstoffe ist, das sorptionsfördernde Mittel der (C4)-Kohlenwasserstoff n-Butan ist und das polymerquellende Mittel ein gesättigter (C5-C20)-Kohlenwasserstoff oder ein Gemisch wenigstens zwei verschiedener gesättigter (C5-C20)-Kohlenwasserstoffe ist, wobei das polymerquellende Mittel n-Pentan oder isoPentan ist und wobei die Gesamtmenge der inerten Komponenten (1), (2), (3) und (4) 100 % beträgt.


     
    2. Verfahren zur Gasphasenpolymerisation eines oder mehrerer Olefinmonomere in einem Wirbelschichtreaktor gemäß Anspruch 1, wobei der Reaktor eine Reaktionszone umfasst, die an der Unterseite durch eine Gasverteilerplatte und an der Oberseite durch eine virtuelle Endoberfläche beschränkt ist, wobei eine Wirbelschicht zwischen der Unterseite und der oberen Seite aufrechtgehalten wird, und wobei wenigstens ein Teil des an der Oberseite des Reaktors entnommenen gasförmigen Stroms abgekühlt wird, und wobei wenigstens ein Teil des erhaltenen Zweiphasenstroms zu dem Reaktor rückgeführt wird und wobei der Gasstrom ein Inertgas umfasst, das ein Gemisch von inerten Komponenten umfasst:

    (1) Stickstoff,

    (2) ein die Gas-Wärmekapazität erhöhendes Mittel,

    (3) ein sorptionsförderndes Mittel und

    (4) ein Polymerquellmittel.


     
    3. Verfahren gemäß einem der Ansprüche 1-2, dadurch gekennzeichnet, dass das Gemisch umfasst:

    (1) 10-50 mol-% Stickstoff,

    (2) 25-80 mol-% an einem (C2-C3)-Kohlenwasserstoff,

    (3) 1-45 mol-% an einem (C4)-Kohlenwasserstoff und

    (4) 0,2-7 mol-% an einem (C5-C20)-Kohlenwasserstoff,
    wobei die Gesamtmenge der inerten Komponenten (1), (2), (3) und (4) 100 % beträgt.


     
    4. Verfahren gemäß einem der Ansprüche 1-3, dadurch gekennzeichnet, dass das die Gas-Wärmekapazität erhöhende Mittel Ethan ist.
     
    5. Verfahren gemäß einem der Ansprüche 1-4, dadurch gekennzeichnet, dass das Polymerquellmittel n-Pentan ist.
     
    6. Verfahren gemäß einem der Ansprüche 1-5, dadurch gekennzeichnet, dass das Olefin-Monomer ein Ethylenmonomer ist, wobei die Menge an Ethylen in dem Einsatzstrom in dem Bereich zwischen 50 Gew.-% und 95 Gew.-% der Gesamtmenge an Olefinmonomeren liegt.
     


    Revendications

    1. Procédé pour la polymérisation en phase gazeuse d'un ou plusieurs monomères oléfiniques dans un réacteur à lit fluidisé en mode sec ou en mode (super)condensé avec un flux de gaz comprenant un gaz inerte, caractérisé en ce que le gaz inerte comprend un mélange de composants inertes :

    (1) 5-60 % en mole d'azote

    (2) 10-90 % en mole d'un agent augmentant la capacité calorifique du gaz qui ajuste le point de rosée et en même temps améliore la capacité calorifique du flux de vapeur

    (3) 1-50 % en mole d'un agent promoteur de sorption qui sert d'agent promoteur des concentrations locales d'éthylène et d'alpha-oléfines au niveau de microparticules de polymère en train de croître, la sorption de tels composants dans le polyéthylène augmentant la concentration locale d'éthylène et/ou d'alpha-oléfines en termes de micro-conditions entourant les sites actifs du catalyseur, et

    (4) 0,1-10 % en mole d'un agent de gonflement de polymère qui sert d'agent modificateur de propriétés physiques et viscoélastiques du polymère, développé instantanément pendant la croissance du polymère, par gonflement et plastification du polymère formé pendant la croissance et lequel agent a une incidence sur les caractéristiques de la phase cristalline,
    l'agent augmentant la capacité calorifique du gaz étant un hydrocarbure en C2-C3 saturé ou un mélange de ces hydrocarbures, l'agent promoteur de sorption étant l'hydrocarbure en C4 n-butane et l'agent de gonflement de polymère étant un hydrocarbure en C5-C20 saturé ou un mélange d'au moins deux hydrocarbures en C5-C20 saturés différents, l'agent de gonflement de polymère étant le n-pentane ou l'isopentane, et
    la quantité totale des composants inertes (1), (2), (3) et (4) étant de 100 %.


     
    2. Procédé pour la polymérisation en phase gazeuse d'un ou plusieurs monomères oléfiniques dans un réacteur à lit fluidisé selon la revendication 1, le réacteur comprenant une zone de réaction qui est délimitée du coté inférieur par une plaque de distribution de gaz et du côté supérieur par une surface d'extrémité virtuelle, un lit fluidisé étant maintenu entre le côté inférieur et le côté supérieur et au moins une partie du flux gazeux soutiré à partir de la partie supérieure du réacteur étant refroidi et au moins une partie du flux à deux phases résultant étant recyclé vers le réacteur et le flux de gaz comprenant un gaz inerte comprenant un mélange de composants inertes :

    (1) de l'azote

    (2) un agent augmentant la capacité calorifique du gaz

    (3) un agent promoteur de sorption et

    (4) un agent de gonflement de polymère.


     
    3. Procédé selon l'une quelconque des revendications 1-2 caractérisé en ce que le mélange comprend

    (1) 10-50 % en mole d'azote

    (2) 25-80 % en mole d'un hydrocarbure en C2-C3

    (3) 1-45 % en mole d'un hydrocarbure en C4 et

    (4) 0,2-7 % en mole d'un hydrocarbure en C5-C20,
    la quantité totale des composants inertes (1), (2), (3) et (4) étant de 100 %.


     
    4. Procédé selon l'une quelconque des revendications 1-3 caractérisé en ce que l'agent augmentant la capacité calorifique du gaz est l'éthane.
     
    5. Procédé selon l'une quelconque des revendications 1-4 caractérisé en ce que l'agent de gonflement de polymère est le n-pentane.
     
    6. Procédé selon l'une quelconque des revendications 1-5 caractérisé en ce que le monomère oléfinique est un monomère de type éthylène, la quantité d'éthylène dans le flux d'alimentation étant comprise entre 50 % en poids et 95 % en poids de la quantité totale de monomères oléfiniques.
     






    Cited references

    REFERENCES CITED IN THE DESCRIPTION



    This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

    Patent documents cited in the description




    Non-patent literature cited in the description