(19)
(11)EP 2 716 709 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
11.09.2019 Bulletin 2019/37

(21)Application number: 12793016.2

(22)Date of filing:  29.05.2012
(51)International Patent Classification (IPC): 
C08L 63/00(2006.01)
C08K 3/00(2018.01)
C08K 3/36(2006.01)
C08L 79/04(2006.01)
C08J 5/24(2006.01)
C08K 3/22(2006.01)
C08K 5/3445(2006.01)
(86)International application number:
PCT/JP2012/063740
(87)International publication number:
WO 2012/165423 (06.12.2012 Gazette  2012/49)

(54)

RESIN COMPOSITION, PREPREG AND LAMINATE

HARZZUSAMMENSETZUNG, PREPREG UND LAMINAT

COMPOSITION DE RÉSINE, PRÉIMPRÉGNÉ ET STRATIFIÉ


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 31.05.2011 JP 2011121923

(43)Date of publication of application:
09.04.2014 Bulletin 2014/15

(73)Proprietor: Mitsubishi Gas Chemical Company, Inc.
Tokyo 100-8324 (JP)

(72)Inventors:
  • OGASHIWA Takaaki
    Tokyo 125-8601 (JP)
  • TAKAHASHI Hiroshi
    Tokyo 125-8601 (JP)
  • MIYAHIRA Tetsuro
    Tokyo 125-8601 (JP)
  • KATO Yoshihiro
    Tokyo 125-8601 (JP)

(74)Representative: Hoffmann Eitle 
Patent- und Rechtsanwälte PartmbB Arabellastraße 30
81925 München
81925 München (DE)


(56)References cited: : 
EP-A1- 1 961 554
WO-A1-2010/109861
JP-A- 2003 502 484
JP-A- 2009 035 728
WO-A1-2010/098037
JP-A- 63 033 472
JP-A- 2003 531 941
JP-A- 2010 100 803
  
      
    Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


    Description

    Technical Field



    [0001] The present invention relates to a resin composition. In particular, the present invention relates to a resin composition which can be suitably used in a printed wiring board. Furthermore, the present invention relates to a prepreg, a laminate, and a metal foil-clad laminate which are produced using the resin composition.

    Background Art



    [0002] With increasing high functionalization and miniaturization of semiconductor packages which are widely used for electronic equipment, communication apparatuses, and personal computers or the like, in recent years, high integration and high-density packaging have been increasingly accelerated. As a result, requirements to a laminate used for the semiconductor package are also various, and characteristics such as flame retardance and low water absorption according to standardization of halogen-phosphorus free, lead free of solder are required from consideration to environmental problems.

    [0003] It has been known that a coefficient of thermal expansion in the plane direction of the laminate at a temperature higher than a glass transition point is different from that at a temperature lower than the glass transition point, and the coefficient of thermal expansion is decreased immediately after exceeding the glass transition point. Because a plastic package is heated to 260°C or more by solder reflow processing or the like in a producing process, the difference between the coefficients of thermal expansion in the plane direction is increased between the laminate and a sealing resin or the like by the declination of the coefficient of thermal expansion described above when the glass transition temperature of the laminate is low, which causes production faults such as warpage. Therefore, a high glass transition temperature is required for the laminate. In order to suppress a shape change caused by the coefficient of thermal expansion of the sealing resin, a high elastic modulus at high temperature is also required.

    [0004] In a technique of raising the glass transition temperature of the laminate, an ingredient having a high glass transition temperature is used for a resin composition for the laminate (for example, see Patent Literature 1). Novolac-based bismaleimide is used as the resin ingredient raising the glass transition temperature in Patent Literature 1. However, because the glass transition temperature of other resin ingredient is low, it is difficult to attain the glass transition temperature of 260°C or more. In order to attain the glass transition temperature of 260°C or more, it is necessary to increase the amount of an inorganic filler used. In this case, the moldability is easily predicted to be poor.

    [0005] As another technique, the blending of a cyanate ester resin and bismaleimide has been known. Many case examples using a novo lac-based cyanate ester resin particularly as a cyanate ester compound can be found (for example, see Patent Literature 2). However, the novolac-based cyanate ester resin is apt to be insufficiently cured in a normal curing condition. The obtained cured product disadvantageously has a large water absorption ratio.

    Citation List


    Patent Literature



    [0006] 

    Patent Literature 1: Japanese Patent Laid-Open No. 2010-100803

    Patent Literature 2: Japanese Patent Laid-Open No. 11-124433


    Summary of Invention


    Technical Problem



    [0007] It is an object of the present invention to provide, without using a halogenated compound or a phosphorus compound, a resin composition for printed wiring boards which has high-degree flame retardance, has a low water absorption ratio and a high glass transition temperature, and has a high elastic modulus at high temperature, a prepreg containing the resin composition, and a laminate and a metal foil-clad laminate which contain the prepreg.

    Solution to Problem



    [0008] The present inventors have found that a metal foil-clad laminate obtained by blending a maleimide compound having a specific structure, a cyanate ester compound, an epoxy resin, and an inorganic filler as a resin composition for printed wiring boards, or by blending an epoxy resin, an inorganic filler, and a BT resin obtained by prepolymerizing a maleimide compound having a specific structure and a cyanate ester compound has excellent flame retardance, low water absorption, a high glass transition temperature, and an excellent elastic modulus at high temperature. On the basis of these findings, the present inventors have completed the present invention.

    [0009] The present invention is defined in the appended claims.

    Advantageous Effect of Invention



    [0010] A metal foil-clad laminate according to the present invention has excellent flame retardance, low water absorption, a high glass transition temperature, and an excellent elastic modulus at high temperature, and is suitable for a material for printed wiring boards requiring high heat resistance and high reliability.

    Description of Embodiment



    [0011] Hereinafter, an embodiment of the present invention will be described. The following embodiment is exemplified to describe the present invention, and the present invention is not limited only to the embodiment.

    Resin Composition



    [0012] A resin composition according to the present invention contains a specific maleimide compound (A), a specific cyanate ester compound (B), a non-halogen epoxy resin (C), an inorganic filler (D), and an imidazole compound (F), wherein the imidazole compound (F) is 2,4,5-triphenyl imidazole. In another aspect, a resin composition contains a non-halogen epoxy resin (C), an inorganic filler (D), and a bismaleimide triazine (BT) resin (E) obtained by prepolymerizing the specific maleimide compound (A) and the specific cyanate ester compound (B), and optionally an imidazole compound (F). The resin composition may further contain other ingredients such as a silane coupling agent, and a wetting dispersing agent. The resin composition according to the present invention is suitably used for a cured product having a glass transition temperature of 260 to 360°C, and preferably 265 to 320°C. Hereinafter, individual ingredients constituting the resin composition will be described.

    Maleimide Compound (A)



    [0013] The maleimide compound (A) used in the present invention is represented by general formula (1):

    wherein R represents a hydrogen atom or a methyl group, and n represents an integer of 1 to 10 on average. Prepolymers thereof, and prepolymers of the maleimide compounds and the amine compounds, or the like can be used. Product examples include BMI-2300 manufactured by Daiwakasei Industry Co., Ltd. Because the compound has a novolac structure, the compound has many crosslinking points, and has an effect of raising the glass transition temperature of the cured product.

    [0014] The content of the maleimide compound (A) is not particularly limited. However, from the viewpoint of a glass transition temperature and a water absorption ratio, the content is preferably in the range of 10 to 50 parts by mass based on 100 parts by mass in total of the maleimide compound (A), the cyanate ester compound (B), and the non-halogen epoxy resin (C), and more preferably in the range of 15 to 40 parts by mass.

    Cyanate Ester Compound (B)



    [0015] Any common publicly known cyanate ester compound can be used as the cyanate ester compound (B) used in the present invention. Examples thereof include a naphthol aralkyl-based cyanate ester compound, a novolac-based cyanate ester compound, 1,3-dicyanatobenzene, 1,4-dicyanatobenzene, 1,3,5-tricyanatobenzene, bis(3,5-dimethyl-4-cyanatophenyl)methane, 1,3-dicyanatonahthalene, 1,4-dicyanatonahthalene, 1,6-dicyanatonahthalene, 1,8-dicyanatonahthalene, 2,6-dicyanatonahthalene, 2,7-dicyanatonahthalene, 1,3,6-tricyanatonahthalene, 4,4'-dicyanatobiphenyl, bis(4-cyanatophenyl)methane, 2,2'-bis(4-cyanatophenyl)propane, bis(4-cyanatophenyl)ether, bis(4-cyanatophenyl)thioether, bis(4-cyanatophenyl)sulfone, 2,2'-bis(4-cyanatophenyl)propane, bis(3,5-dimethyl-4-cyanatophenyl)methane, and a phenol novo lac-based cyanate ester compound. Of these, from the viewpoint of flame retardance, the naphthol aralkyl-based cyanate ester compound and/or the novolac-based cyanate ester compound are preferable. Furthermore, from the viewpoint of a water absorption ratio, a naphthol aralkyl-based cyanate ester compound represented by the following general formula (2) is more preferable.

    wherein R represents a hydrogen atom or a methyl group, and m represents an integer of 1 to 10 on average.

    [0016] The naphthol aralkyl-based cyanate ester compound can be selected from naphthol aralkyl-based cyanate ester compounds obtained by condensation of a cyanic acid and a naphthol aralkyl resin which is obtained by a reaction of a naphthol such as α-naphthol or β-naphthol with p-xylyleneglycol, α,α'-dimethoxy-p-xylene, 1,4-di(2-hydroxy-2-propyl)benzene or the like.

    [0017] The method of producing the cyanate ester compound is not particularly limited. The cyanate ester compound may be produced by any of methods known as a cyanate ester synthesis. Specifically, for example, the cyanate ester compound can be obtained by reacting a naphthol aralkyl resin represented by general formula (4) with a cyanogen halide in an inactive organic solvent in the presence of a basic compound. It is possible to adopt a method in which a salt of a similar naphthol aralkyl resin and a basic compound is formed in a solution containing water and then the salt is reacted with a cyanogen halide in a two-phase interface reaction, thereby synthesizing the cyanate ester compound.

    wherein R represents a hydrogen atom or a methyl group, and m represents an integer of 1 to 50 on average.

    [0018] The content of the cyanate ester compound (B) is not particularly limited. From the viewpoint of flame retardance, a glass transition temperature, a water absorption ratio, and an elastic modulus, the content of the cyanate ester compound (B) is preferably in the range of 10 to 50 parts by mass based on 100 parts by mass in total of the maleimide compound (A), the cyanate ester compound (B), and the non-halogen epoxy resin (C), and more preferably in the range of 20 to 40 parts by mass.

    [0019] The content of the cyanate ester compound (B) is not particularly limited. However, from the viewpoint of heat resistance, flame retardance, and a water absorption ratio, the cyanate ester compound (B) is preferably contained in an amount that meets a requirement of a ratio (CN/Ep) of 0.7 to 2.5, wherein CN represents the number of cyanate groups in the cyanate ester compound; and Ep represents the number of epoxy groups of an epoxy resin in the resin composition.

    Non-Halogen Epoxy Resin (C)



    [0020] The non-halogen epoxy resin (C) used in the present invention is not particularly limited so long as it is a compound which has two or more epoxy groups per molecule and does not have a halogen atom in a molecule structure. Examples thereof include a bisphenol A-based epoxy resin, a bisphenol F-based epoxy resin, a phenol novolac-based epoxy resin, a cresol novo lac-based epoxy resin, a bisphenol A novo lac-based epoxy resin, a trifunctional phenol-based epoxy resin, a tetrafunctional phenol-based epoxy resin, a naphthalene-based epoxy resin, an anthracene-based epoxy resin, a biphenyl-based epoxy resin, an aralkyl novolac-based epoxy resin, an alicyclic epoxy resin, a polyol-based epoxy resin, glycidyl amine, glycidyl ester, a compound obtained by epoxidation of a double bond of butadiene or the like, and a compound obtained by a reaction of a hydroxyl-group-containing silicon resin with epichlorohydrin.

    [0021] Of these, a phenol biphenyl aralkyl-based epoxy resin, a phenol novolac-based epoxy resin, a cresol novolac-based epoxy resin, a polyoxynaphthylene-based epoxy resin, a tetrafunctional naphthalene-based epoxy resin, and an anthracene-based epoxy resin are preferable to particularly improve flame retardance. A phenol phenyl aralkyl novolac-based epoxy resin represented by general formula (5), a phenol biphenyl aralkyl-based epoxy resin represented by general formula (6), a naphthol aralkyl-based epoxy resin represented by general formula (7), and a polyoxynaphthylene-based epoxy resin are more preferable. The non-halogen epoxy resins (C) can be used alone or in a mixture of two or more of them, as required.



    wherein R represents a hydrogen atom or a methyl group, and x represents an integer of 1 to 10 on average.

    wherein R represents a hydrogen atom or a methyl group, and y represents an integer of 1 to 50 on average.

    wherein R represents a hydrogen atom or a methyl group, and z represents an integer of 1 to 50 on average.

    [0022] Furthermore, when flame retardance is particularly required, phosphorus-containing epoxy resins or brominated epoxy resins may be used in a combination with the non-halogen epoxy resin depending upon applications. The brominated epoxy resin means a bromine atom-containing compound having two or more epoxy groups per molecule. Specific examples include a brominated bisphenol A-based epoxy resin and a brominated phenol novo lac-based epoxy resin.

    [0023] The content of the non-halogen epoxy resin (C) is not particularly limited. However, from the viewpoint of flame retardance, a glass transition temperature, a water absorption ratio, and an elastic modulus, the content is preferably in the range of 5 to 50 parts by mass based on 100 parts by mass in total of the maleimide compound (A), the cyanate ester compound (B), and the non-halogen epoxy resin (C), and more preferably in the range of 10 to 40 parts by mass. When the BT resin (E) is used, the content of the non-halogen epoxy resin (C) is not particularly limited. However, the content is preferably in the range of 5 to 50 parts by mass based on 100 parts by mass in total of the non-halogen epoxy resin (C) and the BT resin (E), and more preferably in the range of 10 to 40 parts by mass.

    [0024] The content of the non-halogen epoxy resin (C) is not particularly limited. However, from the viewpoint of flame retardance and curability or the like, it is preferable that the cyanate ester compound (B) and the non-halogen epoxy resin (C) are blended in the resin composition such that the ratio (CN/Ep) of the number of cyanate groups of the cyanate ester compound (B) and the number of epoxy groups of the non-halogen epoxy resin (C) is 0.7 to 2.5.

    Inorganic Filler (D)



    [0025] As the inorganic filler (D) used in the present invention, an inorganic filler generally used for the resin composition for electric wiring boards can be used. Specific examples thereof include silica such as natural silica, fused silica, amorphous silica, and hollow silica, metal hydrates such as aluminum hydroxide, a heat-treated product of aluminum hydroxide (obtained by heat-treating aluminum hydroxide and decreasing crystal water partially), boehmite, and magnesium hydroxide, molybdenum compounds such as molybdenum oxide and zinc molybdate, zinc borate, zinc stannate, alumina, clay, kaolin, talc, calcined clay, calcined kaolin, calcined talc, mica, short glass fiber (fine powders of glasses such as E glass or D glass), hollow glass, and spherical glass. The inorganic fillers (D) can be used alone or in a mixture of two or more of them, as required. Of these, from the viewpoint of a coefficient of thermal expansion and burning resistance, the silica, the boehmite, the magnesium hydroxide, the alumina, and the talc are preferable, and the boehmite and the silica are more preferable.

    [0026] The mean particle diameter (D50) of the inorganic filler (D) is not particularly limited. However, from the viewpoint of dispersibility, the mean particle diameter (D50) is preferably 0.2 to 5 µm. Herein, D50 means a median diameter, and is a particle diameter at which, when the particle size distribution of the measured powder is divided into two parts, particles larger than the particle diameter and particles smaller than the particle diameter, the number or mass of the larger side of the particles or the number or mass of the smaller side of the particles accounts for 50% of that of the whole powder. The D50 of the inorganic filler is generally measured by a wet laser diffraction scattering method.

    [0027] The content of the inorganic filler (D) is not particularly limited. However, the content is preferably 50 to 400 parts by mass based on 100 parts by mass in total of the maleimide compound (A), the cyanate ester compound (B), and the non-halogen epoxy resin (C). Furthermore, the content is particularly preferably 80 to 300 parts by mass. When the BT resin (E) is used, the content of the inorganic filler (D) is not particularly limited. However, the content is preferably 50 to 400 parts by mass based on 100 parts by mass in total of the non-halogen epoxy resin (C) and the BT resin (E). Furthermore, the content is particularly preferably 80 to 300 parts by mass. This is because the flame retardance can be further improved if the content of the inorganic filler is 50 parts by mass or more, and moldability and drilling workability are better if the content is 400 parts by mass or less.

    BT Resin (E)



    [0028] The BT resin (bismaleimide triazine resin) (E) used in the present invention is obtained by heat melting and mixing of the maleimide compound (A) represented by general formula (1) and the cyanate ester compound (B) in the absence of a solvent, or heat mixing after dissolution of the maleimide compound (A) and the cyanate ester compound (B) in an organic solvent such as methyl ethyl ketone, N-methyl pyrrodoline, dimethylformamide, dimethylacetamide, toluene, or xylene, and prepolymerizing the mixture.

    [0029] When the BT resin (E) is produced, the content of the maleimide compound (A) is not particularly limited. However, from the viewpoint of a glass transition temperature, flame retardance, and curability, the content is preferably in the range of 5 to 75 parts by mass based on 100 parts by mass of the BT resin (E), and particularly preferably in the range of 10 to 70 parts by mass. The range of the molecular weight of the BT resin (E) is not particularly limited. However, from the viewpoint of handleability, a glass transition temperature, and curability, the number average molecular weight is preferably in the range of about 100 to 100000.

    [0030] The content of the BT resin (E) is not particularly limited. However, from the viewpoint of heat resistance and a water absorption ratio, the content is preferably in the range of 20 to 80 parts by mass based on 100 parts by mass in total of the non-halogen epoxy resin (C) and the BT resin (E), more preferably in the range of 25 to 75 parts by weight, and particularly preferably 30 to 70 parts by mass.

    Imidazole Compound (F)



    [0031] The imidazole compound (F) present in the resin composition comprising the maleimide compound (A) and the cyantate ester compound (B) as defined in claim 1 is 2,4,5-triphenyl imidazole. In the resin composition comprising the BT resin as defined in claim 7, the presence of an imidazole compound (F) is optional. If present, it is represented by general formula (3):

    wherein Ar is a phenyl group, a naphthalene group, a biphenyl group, an anthracene group or, a hydroxyl group modified substance thereof, and R is a hydrogen atom, an alkyl group, an aryl group, or a hydroxyl group modified substance thereof. The imidazole compound (F) is added to the resin composition, and thereby the curing can be promoted, and the glass transition temperature of the cured product can be raised. The elastic modulus of the cured product can also be raised. In general formula (3), the imidazole substituent Ar is preferably the phenyl group, the naphthalene group, the biphenyl group, the anthracene group or, the hydroxyl group modified substance thereof or the like, and more preferably the phenyl group. The imidazole substituent R is preferably the hydrogen atom, the alkyl group, the aryl group, or the hydroxyl group modified substance thereof, and more preferably the aryl group such as the phenyl group. Furthermore, both the Ar group and the R group are particularly preferably the phenyl group.

    [0032] The content of the imidazole compound (F) 2,4,5-triphenyl imidazole in the resin composition comprising the maleimide compound (A) and the cyanate ester compound (B) is not particularly limited. However, from the viewpoint of the storage stability of a prepreg, and moldability when the prepreg is processed to a copper-clad laminate, the content is preferably in the range of 0.01 to 10 parts by mass based on 100 parts by mass in total of the maleimide compound (A), the cyanate ester compound (B), and the non-halogen epoxy resin (C), and more preferably in the range of 0.1 to 5 parts by mass. When the BT resin (E) is used, the content of the imidazole compound (F) is not particularly limited. However, the content is preferably in the range of 0.01 to 10 parts by mass based on 100 parts by mass in total of the non-halogen epoxy resin (C) and the BT resin (E), and more preferably in the range of 0.1 to 5 parts by mass.

    Other Ingredients



    [0033] The resin composition according to the present invention may further contain other ingredients such as a silane coupling agent and a wetting dispersing agent. The dispersibility of the inorganic filler, and the adhesive strength of the resin and the inorganic filler or the glass cloth can be improved by jointly using the silane coupling agent and the wetting dispersing agent in addition to the inorganic filler (D).

    [0034] The silane coupling agent is not particularly limited so long as it is selected from silane coupling agents which are generally used for surface-treating inorganic substances. Specific examples thereof include aminosilane coupling agents such as γ-aminopropyltriethoxysilane and N-β-(aminoethyl)-γ-aminopropyltrimethoxysilane, epoxysilane coupling agents such as γ-glycidoxypropyltrimethoxysilane, vinylsilane coupling agents such as γ-methacryloxypropyltrimethoxysilane, cationic silane coupling agents such as N-β-(N-vinylbenzylaminoethyl)-γ-aminopropyltrimethoxysilane hydrochloride, and phenylsilane coupling agents. The silane coupling agents can be used alone or in a combination of two or more of them, as required.

    [0035] The wetting dispersing agent is not particularly limited so long as it is selected from dispersion stabilizers which are used for coatings. Examples thereof include wetting dispersing agents such as Disperbyk-110, 111, 180, and 161, and BYK-W996, W9010, and W903 manufactured by BYK-Chemie Japan K.K.

    [0036] The resin composition according to the present invention may further contain a maleimide compound having a structure other than the structure represented by general formula (1), so long as the desired properties of the resin composition are not impaired. Any compound having one or more maleimide groups per molecule may be used as the maleimide compound without particular limitation. Examples thereof include N-phenylmaleimide, N-hydroxyphenylmaleimide, bis(4-maleimidophenyl)methane, 2,2-bis{4-(4-maleimidophenoxy)-phenyl}propane, bis(3,5-dimethyl-4-maleimidophenyl)methane, bis(3-ethyl-5-methyl-4-maleimidophenyl)methane, bis(3,5-diethyl-4-maleimidophenyl)methane, prepolymers of these maleimide compounds, or prepolymers of maleimide compounds and amine compounds. The maleimide compounds can be used in a mixture of two or more of them, as required.

    [0037] The resin composition according to the present invention may further contain a cyanate ester compound having a structure other than the structure represented by general formula (2), so long as the desired properties of the resin composition are not impaired. Any common publicly known cyanate ester resin may be used as the cyanate ester compound. Examples thereof include 1,3-dicyanatobenzene, 1,4-dicyanatobenzene, 1,3,5-tricyanatobenzene, bis(3,5-dimethyl-4-cyanatophenyl)methane, 1,3-dicyanatonahthalene, 1,4-dicyanatonahthalene, 1,6-dicyanatonahthalene, 1,8-dicyanatonahthalene, 2,6-dicyanatonahthalene, 2,7-dicyanatonahthalene, 1,3,6-tricyanatonahthalene, 4,4'-dicyanatobiphenyl, bis(4-cyanatophenyl)methane, 2,2'-bis(4-cyanatophenyl)propane, bis(4-cyanatophenyl)ether, bis(4-cyanatophenyl)thioether, bis(4-cyanatophenyl)sulfone, 2,2'-bis(4-cyanatophenyl)propane, bis(3,5-dimethyl-4-cyanatophenyl)methane, and phenol novolac-based cyanate esters. Those cyanate ester compounds can be used in a mixture of two or more of them, as required.

    [0038] The resin composition according to the present invention may further contain other curing accelerators in addition to the imidazole compound (F), so long as the desired properties of the resin composition are not impaired. Examples of the compounds include organic peroxides such as benzoyl peroxide, lauroyl peroxide, acetyl peroxide, parachlorobenzoyl peroxide, and di-tert-butyl-di-perphthalate; azo compounds such as azobisnitrile; tertiary amines such as N,N-dimethylbenzylamine, N,N-dimethylaniline, N,N-dimethyltoluidine, 2-N-ethylanilinoethanol, tri-n-butylamine, pyridine, quinoline, N-methylmorpholine, triethanolamine, triethylenediamine, tetramethylbutanediamine, and N-methylpiperidine; phenols such as phenol, xylenol, cresol, resorcin, and catechol; organic metal salts such as lead naphthenate, lead stearate, zinc naphthenate, zinc octylate, tin oleate, dibutyltin maleate, manganese naphthenate, cobalt naphthenate, and acetylacetone iron; a substance obtained by dissolving any one of these organic metal salts in a hydroxyl-group-containing compound such as phenol or bisphenol; inorganic metal salts such as tin chloride, zinc chloride, and aluminum chloride; and organotin compounds such as dioctyltin oxide, other alkyltin, and alkyltin oxide.

    [0039] The resin composition according to the present invention may further contain a silicone powder. The silicone powder retards a combustion time and functions as a flame retardant assistant which increases a flame resistant effect. The silicone powder includes a fine powder of polymethylsilsesquioxane where a siloxane bond is three-dimensionally reticulately cross-linked; a fine powder of an addition polymer of a vinyl-group-containing dimethylpolysiloxane and methylhydrogenpolysiloxane; a powder obtained by coating the surface of a fine powder of an addition polymer of a vinyl-group-containing dimethylpolysiloxane and methylhydrogenpolysiloxane with polymethylsilsesquioxane where a siloxane bond is three-dimensionally reticulately cross-linked; and a powder obtained by coating the surface of an inorganic support with polymethylsilsesquioxane where a siloxane bond is three-dimensionally reticulately cross-linked; or the like.

    [0040] The mean particle diameter (D50) of the silicone powder is not particularly limited. However, the mean particle diameter (D50) is preferably 1 to 15 µm in view of dispersibility.

    [0041] The content of the silicone powder is not particularly limited. However, from the viewpoint of moldability and dispersibility, the content is preferably in the range of 3 to 120 parts by mass based on 100 parts by mass in total of the maleimide compound (A), the cyanate ester compound (B), and the non-halogen epoxy resin (C), and particularly preferably in the range of 3 to 60 parts by mass.

    [0042] The resin composition according to the present invention may further contain a variety of high polymer compounds such as a different thermosetting resin, a thermoplastic resin, and oligomers thereof, and elastomers; a different flame retardant compound; and an additive or the like, so long as the desired properties of the resin composition are not impaired. These compounds and additive are not particularly limited so long as these compounds and additive are selected from those which are generally used. Examples of the flame retardant compound include a nitrogen-containing compound such as melamine or benzoguanamine, and an oxazine-ring-containing compound. Examples of the additive include an ultraviolet absorber, an antioxidant, a photopolymerization initiator, a fluorescent brightener, a photosensitizer, a dye, a pigment, a thickener, a lubricant, an antifoamer, a dispersing agent, a leveling agent, a brightener, and a polymerization inhibitor. These can be used in a combination as required.

    Prepreg



    [0043] The prepreg according to the present invention is produced by impregnating or coating the base material with the resin composition. A method for producing the prepreg according to the present invention is not particularly limited so long as it is selected from methods for impregnating or coating the base material with the resin composition containing the resin ingredient in the present invention to produce the prepreg. The prepreg may be produced, for example, by a method for producing a prepreg comprising impregnating or coating the base material with a resin varnish comprising the resin composition containing the maleimide compound (A), the cyanate ester compound (B), the non-halogen epoxy resin (C), and the inorganic filler (D), and an organic solvent, and then heating the impregnated or coated base material in a drier of 100 to 200°C for 1 to 60 minutes to semi-cure the resin. The amount of the resin composition deposited on the base material (F) is preferably in the range of 20 to 90% by mass based on the whole prepreg.

    [0044] The base material used in the prepreg of the present invention can be selected from known base materials which are used for a variety of printed wiring board materials. Examples thereof include glass fibers such as E glass, D glass, S glass ,NE glass, T glass, and Q glass, inorganic fibers other than glass, and organic fibers such as polyimide, polyamide and polyester. It is possible to select the base material in accordance with intended use or performance as required. Examples of the form of the base material include a woven fabric, a nonwoven fabric, roving, a chopped strand mat, or a surfacing mat. The thickness of the base material is not particularly limited. However, the thickness of the base material to be used is generally about 0.01 to 0.30 mm. Among these base materials, the E-glass fiber is particularly preferably used from the viewpoint of a balance between the coefficient of thermal expansion in a plane direction and the drilling workability. The woven fabric is preferably used as the form.

    [0045] The organic solvent is used to lower the viscosity of the resin composition, improve the handleability, and, at the same time, enhance the impregnation of the resin composition into the glass cloth. The organic solvent is not particularly limitated so long as the maleimide compound (A), the cyanate ester compound (B), and the non-halogen epoxy resin (C) can be dissolved therein. Specific examples thereof include ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone, and cyclohexanone; aromatic hydrocarbons such as benzene, toluene, and xylene; and amides such as dimethylformamide and dimethylacetamide.

    Laminate



    [0046] The laminate according to the present invention is obtained by laminate-molding the above-mentioned prepreg. The metal foil-clad laminate according to the present invention is obtained by laminate-molding the above-mentioned prepreg and a metal foil. Specifically, the laminate or metal-foil-clad laminate is produced by providing one prepreg mentioned above or stacking two or more prepregs, disposing a metal foil such as copper or aluminum on one surface or both surfaces of the prepreg or the stack of the prepregs, as required, and laminate-molding the resultant set. The metal foil to be used is not particularly limited so long as it is selected from metal foils which are used as a printed wiring board material. General technical skills for laminates and multilayer boards for printed wiring boards can be applied with regard to molding conditions. For example, a multiplaten press, a multiplaten vacuum press, continuous molding, and an autoclave molding machine or the like are generally used. The temperature is generally in the range of 100 to 300°C. The pressure is generally in the range of 2 to 100 kgf/cm2. The heating time is generally in the range of 0.05 to 5 hours. The laminate is preferably cured and molded at a temperature of 120 to 280°C for 0.1 to 4 hours, and more preferably at a temperature of 150 to 250°C for 0.5 to 3 hours. A multilayer board can be produced by combining the prepreg of the present invention and a wiring board, prepared separately, for an internal layer, and laminate-molding the prepreg and the wiring board.

    [0047] Hereinafter, the present invention is specifically described according to Synthesis Examples and Examples. However, the present invention is not limited to these Examples.

    Examples


    Synthesis Example 1


    Synthesis of α-Naphthol Aralkyl-Based Cyanate Ester Compound



    [0048] A reactor equipped with a thermometer, a stirrer, a dropping funnel, and a reflux condenser was preliminarily cooled with brine to 0 to 5°C. 7.47 g (0.122 mol) of Cyanogen chloride, 9.75 g (0.0935 mol) of 35% hydrochloric acid, 76 ml of water, and 44 ml of methylene chloride were charged into the reactor. The temperature within the reactor and pH were kept at -5 to +5°C and 1 or less, respectively, and, while stirring, a solution of 20 g (0.0935 mol) of an α-naphthol aralkyl resin in which all R's in general formula (4) were hydrogen atoms (SN485, OH group equivalent: 214 g/eq., softening point: 86°C, manufactured by Nippon Steel Chemical Co., Ltd.), and 14.16 g (0.14 mol) of triethylamine dissolved in 92 ml of methylene chloride was added dropwise to the contents in the reactor through a dropping funnel over a time period of 1 hour. After the completion of the dropwise addition, 4.72 g (0.047 mol) of triethylamine was further added dropwise thereto over a time period of 15 minutes.

    [0049] After the completion of the dropwise addition of the triethylamine, the mixture was stirred at the same temperature for 15 minutes, followed by separation of the reaction solution, thereby obtaining an organic layer. The obtained organic layer was washed twice with 100 ml of water. Methylene chloride was then removed by distillation under the reduced pressure with an evaporator, and the residue was finally concentrated to dryness at 80°C for 1 hour, thereby obtaining 23.5 g of a cyanate ester compound of an α-naphthol aralkyl resin (α-naphthol aralkyl-based cyanate ester resin).

    Synthesis Example 2


    Synthesis of BT Resin (1)



    [0050] 36 parts by mass of the α-naphthol aralkyl-based cyanate ester resin (cyanate equivalent: 261 g/eq.) prepared in Synthesis Example 1 and 24 parts by mass of a maleimide compound in which all R's were hydrogen atoms and n was 0 to 1 in general formula (1) (BMI-2300, manufactured by Daiwakasei Industry Co., Ltd.) were dissolved in dimethylacetamide. The resultant solution was reacted at 150°C while stirring, thereby obtaining a BT resin.

    Synthesis Example 3


    Synthesis of BT Resin (2)



    [0051] 30 parts by mass of the α-naphthol aralkyl-based cyanate ester resin (cyanate equivalent: 261 g/eq.) prepared in Synthesis Example 1 and 30 parts by mass of the maleimide compound (BMI-2300, manufactured by Daiwakasei Industry Co., Ltd.) used in Synthesis Example 2 were dissolved in dimethylacetamide. The resultant solution was reacted at 150°C while stirring, thereby obtaining a BT resin.

    Example 1 (Reference Example - not part of the claimed invention)



    [0052] 36 parts by mass of the α-naphthol aralkyl-based cyanate ester resin (cyanate equivalent: 261 g/eq.) prepared in Synthesis Example 1, 24 parts by mass of the maleimide compound (BMI-2300, manufactured by Daiwakasei Industry Co., Ltd.) used in Synthesis Example 2, and 40 parts by mass of a phenol biphenyl aralkyl-based epoxy resin (NC-3000-FH, epoxy equivalent: 321 g/eq., manufactured by Nippon Kayaku Co., Ltd.) were dissolved and mixed in methyl ethyl ketone. 1 part by mass of a wetting dispersing agent (disperbyk-w903, manufactured by BYK-Chemie Japan K.K.), 120 parts by mass of boehmite (APYRAL AOH60, manufactured by Nabaltec), and 0.02 part by mass of zinc octylate (NIKKA OCTHIX zinc, manufactured by Nihon Kagaku Sangyo Co., Ltd.) were further mixed, thereby obtaining a varnish. The varnish was diluted with methyl ethyl ketone. The diluted varnish was impregnated into and coated on a 0.1 mm-thick E-glass woven fabric. The impregnated and coated E-glass woven fabric was dried under heat at 160°C for 4 minutes, thereby obtaining a prepreg having a resin content of 50% by mass.

    Example 2



    [0053] 1 part by mass of 2,4,5-triphenyl imidazole (manufactured by Wako Pure Chemical Industries, Ltd.) was mixed with the varnish prepared in Reference Example 1. The varnish was diluted with methyl ethyl ketone. The diluted varnish was then impregnated into and coated on a 0.1 mm-thick E-glass woven fabric. The impregnated and coated varnish was dried under heat at 160°C for 4 minutes, thereby obtaining a prepreg having a resin content of 50% by mass.

    Example 3 (Reference Example - not part of the claimed invention)



    [0054] A prepreg was obtained in the same manner as in Reference Example 1 except that 40 parts by mass of the phenol biphenyl aralkyl-based epoxy resin was replaced with 36 parts by mass, and 4 parts by mass of a tetrafunctional naphthalene-based epoxy resin (EPICLON EXA-4710, epoxy equivalent: 170 g/eq., manufactured by DIC) and 10 parts by mass of a silicone rubber powder having a surface coated with a silicone resin (KMP-600, manufactured by Shin-Etsu Chemical Co., Ltd.) were added.

    Example 4



    [0055] 1 part by mass of 2,4,5-triphenyl imidazole used in Example 2 was mixed with the varnish prepared in Reference Example 3. The varnish was diluted with methyl ethyl ketone. The diluted varnish was then impregnated into and coated on a 0.1 mm-thick E-glass woven fabric. The impregnated and coated varnish was dried under heat at 160°C for 4 minutes, thereby obtaining a prepreg having a resin content of 50% by mass.

    Example 5 (Reference Example - not part of the claimed invention)



    [0056] A prepreg was obtained in the same manner as in Reference Example 1 except that 0.02 part by mass of manganese octylate (NIKKA OCTHIX manganese, manufactured by Nihon Kagaku Sangyo Co., Ltd.) was used instead of zinc octylate.

    Example 6



    [0057] 1 part by mass of 2,4,5-triphenyl imidazole used in Example 2 was mixed with the varnish prepared in Reference Example 5. The varnish was diluted with methyl ethyl ketone. The diluted varnish was then impregnated into and coated on a 0.1 mm-thick E-glass woven fabric. The impregnated and coated varnish was dried under heat at 160°C for 4 minutes, thereby obtaining a prepreg having a resin content of 50% by mass.

    Example 7 (Reference Example - not part of the claimed invention)



    [0058] A prepreg was obtained in the same manner as in Reference Example 1 except that 36 parts by mass of the α-naphthol aralkyl-based cyanate ester resin was replaced with 32 parts by mass; 40 parts by mass of the phenol biphenyl aralkyl-based epoxy resin was replaced with 36 parts by mass; and 24 parts by mass of the maleimide compound was replaced with 32 parts by mass.

    Example 8



    [0059] 1 part by mass of 2,4,5-triphenyl imidazole used in Example 2 was mixed with the varnish prepared in Reference Example 7. The varnish was diluted with methyl ethyl ketone. The diluted varnish was then impregnated into and coated on a 0.1 mm-thick E-glass woven fabric. The impregnated and coated varnish was dried under heat at 160°C for 4 minutes, thereby obtaining a prepreg having a resin content of 50% by mass.

    Example 9 (Reference Example - not part of the claimed invention)



    [0060] A prepreg was obtained in the same manner as in Reference Example 1 except that 36 parts by mass of the α-naphthol aralkyl-based cyanate ester resin was replaced with 39 parts by mass; 40 parts by mass of the phenol biphenyl aralkyl-based epoxy resin was replaced with 20 parts by mass; 24 parts by mass of the maleimide compound was replaced with 26 parts by mass; and 15 parts by mass of a phenol novo lac-based epoxy resin (N770, epoxy equivalent: 190 g/eq., manufactured by DIC) was used.

    Example 10



    [0061] 1 part by mass of 2,4,5-triphenyl imidazole used in Example 2 was mixed with the varnish prepared in Reference Example 9. The varnish was diluted with methyl ethyl ketone. The diluted varnish was then impregnated into and coated on a 0.1 mm-thick E-glass woven fabric. The impregnated and coated varnish was dried under heat at 160°C for 4 minutes, thereby obtaining a prepreg having a resin content of 50% by mass.

    Example 11 (Reference Example - not part of the claimed invention)



    [0062] A prepreg was obtained in the same manner as in Reference Example 1 except that 36 parts by mass of the α-naphthol aralkyl-based cyanate ester resin was replaced with 39 parts by mass; 40 parts by mass of the phenol biphenyl aralkyl-based epoxy resin was replaced with 20 parts by mass; 24 parts by mass of the maleimide compound was replaced with 26 parts by mass; and 15 parts by mass of a cresol novolac-based epoxy resin (N680, epoxy equivalent: 285 g/eq., manufactured by DIC) was used.

    Example 12



    [0063] 1 part by mass of 2,4,5-triphenyl imidazole used in Example 2 was mixed with the varnish prepared in Reference Example 11. The varnish was diluted with methyl ethyl ketone. The diluted varnish was then impregnated into and coated on a 0.1 mm-thick E-glass woven fabric. The impregnated and coated varnish was dried under heat at 160°C for 4 minutes, thereby obtaining a prepreg having a resin content of 50% by mass.

    Example 13 (Reference Example - not part of the claimed invention)



    [0064] A prepreg was obtained in the same manner as in Reference Example 1 except that 40 parts by mass of the phenol biphenyl aralkyl-based epoxy resin was replaced with 20 parts by mass, and 20 parts by mass of a polyoxynaphthylene-based epoxy resin (EXA-7311, epoxy equivalent: 277 g/eq., manufactured by DIC) was used.

    Example 14



    [0065] 1 part by mass of 2,4,5-triphenyl imidazole used in Example 2 was mixed with the varnish prepared in Reference Example 13. The varnish was diluted with methyl ethyl ketone. The diluted varnish was then impregnated into and coated on a 0.1 mm-thick E-glass woven fabric. The impregnated and coated varnish was dried under heat at 160°C for 4 minutes, thereby obtaining a prepreg having a resin content of 50% by mass.

    Example 15 (Reference Example - not part of the claimed invention)



    [0066] A prepreg was obtained in the same manner as in Reference Example 1 except that 40 parts by mass of the phenol biphenyl aralkyl-based epoxy resin was replaced with 36 parts by mass, and 4 parts by mass of the tetrafunctional naphthalene-based epoxy resin used in Reference Example 3 was used.

    Example 16



    [0067] 1 part by mass of 2,4,5-triphenyl imidazole used in Example 2 was mixed with the varnish prepared in Reference Example 15. The varnish was diluted with methyl ethyl ketone. The diluted varnish was then impregnated into and coated on a 0.1 mm-thick E-glass woven fabric. The impregnated and coated varnish was dried under heat at 160°C for 4 minutes, thereby obtaining a prepreg having a resin content of 50% by mass.

    Example 17



    [0068] 60 parts by mass of the BT resin (bismaleimide triazine resin) obtained in Synthesis Example 2 and 40 parts by mass of the phenol biphenyl aralkyl-based epoxy resin used in Example 1 were dissolved and mixed in methyl ethyl ketone. 1 part by mass of the wetting dispersing agent used in Example 1, 120 parts by mass of the boehmite, and 0.02 part by mass of the zinc octylate were further mixed, thereby obtaining a varnish. The varnish was diluted with methyl ethyl ketone. The diluted varnish was impregnated into and coated on a 0.1 mm-thick E-glass woven fabric. The impregnated and coated E-glass woven fabric was dried under heat at 160°C for 4 minutes, thereby obtaining a prepreg having a resin content of 50% by mass.

    Example 18



    [0069] 60 parts by mass of the BT resin (bismaleimide triazine resin) prepared in Synthesis Example 3 and 40 parts by mass of the phenol biphenyl aralkyl-based epoxy resin were dissolved and mixed in methyl ethyl ketone. 1 part by mass of the wetting dispersing agent used in Example 1, 120 parts by mass of the boehmite, 0.02 part by mass of the zinc octylate, and 1 part by mass of 2,4,5-triphenyl imidazole were further mixed, thereby obtaining a varnish. The varnish was diluted with methyl ethyl ketone. The diluted varnish was impregnated into and coated on a 0.1 mm-thick E-glass woven fabric. The impregnated and coated E-glass woven fabric was dried under heat at 160°C for 4 minutes, thereby obtaining a prepreg having a resin content of 50% by mass.

    Example 19



    [0070] 10% by mass of a silicone resin powder (Tospearl 120, manufactured by Momentive Performance Materials Japan LLC) was mixed with the varnish prepared in Example 16. The varnish was diluted with methyl ethyl ketone. The diluted varnish was impregnated into and coated on a 0.1 mm-thick E-glass woven fabric. The impregnated and coated E-glass woven fabric was dried under heat at 160°C for 4 minutes, thereby obtaining a prepreg having a resin content of 50% by mass.

    Example 20



    [0071] A prepreg was obtained in the same manner as in Example 2 except that 120 parts by mass of spherical fused silica (SC2500-SQ, manufactured by Admatex) was used instead of the boehmite.

    Example 21 (Reference Example - not part of the claimed invention)



    [0072] A prepreg was obtained in the same manner as in Reference Example 9 except that 120 parts by mass of the spherical fused silica used in Example 20 was used instead of the boehmite.

    Example 22 (Reference Example - not part of the claimed invention)



    [0073] A prepreg was obtained in the same manner as in Reference Example 15 except that 120 parts by mass of the spherical fused silica used in Example 20 was used instead of the boehmite.

    Example 23 (Reference Example - not part of the claimed invention)



    [0074] A prepreg was obtained in the same manner as in Reference Example 22 except that 40 parts by mass of a polyoxynaphthylene-based epoxy resin (EXA-7311, epoxy equivalent: 277 g/eq., manufactured by DIC) was used instead of the phenol biphenyl aralkyl-based epoxy resin, and 10 parts by mass of the silicone rubber powder used in Reference Example 3 was added.

    Example 24 (Reference Example - not part of the claimed invention)



    [0075] A prepreg was obtained in the same manner as in Reference Example 23 except that 120 parts by mass of the spherical fused silica was replaced with 250 parts by mass.

    Example 25 (Reference Example - not part of the claimed invention)



    [0076] A prepreg was obtained in the same manner as in Reference Example 23 except that 120 parts by mass of the spherical fused silica was replaced with 200 parts by mass, and 10 parts by mass of a silicone rubber powder used in Example 3 was replaced with 40 parts by mass.

    Example 26 (Comparative Example)



    [0077] A prepreg was obtained in the same manner as in Reference Example 1 except that 24 parts by mass of bis(3-ethyl-5-methyl-4-maleimidophenyl)methane (BMI-70, manufactured by K.I Chemical Industry Co., Ltd.) was used instead of the maleimide compound.

    Example 27 (Comparative Example) A prepreg was obtained in the same manner as in Reference Example 1 except that the boehmite was not used.


    Example 28 (Reference Example - not part of the claimed invention)



    [0078] A prepreg was obtained in the same manner as in Reference Example 1 except that 36 parts by mass of a prepolymer of 2,2-bis(4-cyanatophenyl)propane (CA210, cyanate equivalent: 139, manufactured by Mitsubishi Gas Chemical Co., Inc.) was used instead of the α-naphthol aralkyl-based cyanate ester resin.

    Example 29



    [0079] A prepreg was obtained in the same manner as in Example 2 except that the prepolymer of 2,2-bis(4-cyanatophenyl)propane used in Reference Example 28 was used instead of the α-naphthol aralkyl-based cyanate ester resin.

    Example 30 (Reference Example - not part of the claimed invention)



    [0080] A prepreg was obtained in the same manner as in Reference Example 28 except that 36 parts by mass of the prepolymer of 2,2-bis(4-cyanatophenyl)propane was replaced with 24 parts by mass, and 24 parts by mass of the maleimide compound was replaced with 36 parts by mass.

    Example 31 (Reference Example - not part of the claimed invention)



    [0081] A prepreg was obtained in the same manner as in Reference Example 1 except that 36 parts by mass of a novolac-based cyanate ester resin (Primaset PT-30, manufactured by LONZA JAPAN, cyanate equivalent: 254 g/eq.) was used instead of the α-naphthol aralkyl-based cyanate ester resin.

    Example 32 (Reference Example - not part of the claimed invention)



    [0082] The prepreg obtained in Reference Example 31 was laminate-pressed, and then heated at 220°C in a thermostatic chamber for 4 hours.

    Example 33 (Reference Example - not part of the claimed invention)



    [0083] A prepreg was obtained in the same manner as in Reference Example 1 except that 30 parts by mass of the novolac-based cyanate ester resin used in Example 31 was used instead of the α-naphthol aralkyl-based cyanate ester resin, and 24 parts by mass of the maleimide compound was replaced with 30 parts by mass.

    Example 34 (Comparative Example)



    [0084] A prepreg was obtained in the same manner as in Reference Example 1 except that 24 parts by mass of bis(3-ethyl-5-methyl-4-maleimidophenyl)methane (BMI-70, manufactured by K.I Chemical Industry Co., Ltd.) was used instead of the maleimide compound, and 120 parts by mass of the spherical fused silica used in Example 20 was used instead of the boehmite.

    Example 35 (Reference Example - not part of the claimed invention)



    [0085] A prepreg was obtained in the same manner as in Reference Example 1 except that 36 parts by mass of the prepolymer of 2,2-bis(4-cyanatophenyl)propane used in Example 28 was used instead of the α-naphthol aralkyl-based cyanate ester resin, and 120 parts by mass of the spherical fused silica used in Example 20 was used instead of the boehmite.

    Preparation of Metal Foil-Clad Laminate



    [0086] For each of the prepregs obtained in Examples 1 to 35, four sheets of the prepreg were superimposed on each other to constitute a stack. A 12 µm-thick electrolytic copper foil (3EC-III, manufactured by MITSUI MINING & SMELTING CO., LTD.) was disposed on the upper surface and the lower surface of the stack, followed by laminate-molding under conditions of a pressure of 30 kg/cm2, a temperature of 220°C, and a time of 120 minutes, thereby obtaining a metal foil-clad laminate having a 0.4 mm-thick insulating layer.

    [0087] Tables 1 and 2 show the results obtained by evaluating flame retardance, a glass transition temperature, a water absorption ratio, and an elastic modulus for the obtained metal foil-clad laminates.

    Evaluation Method of Physical Properties of Metal Foil-Clad Laminate



    [0088] The copper foil was removed by etching the metal foil-clad laminate before the flame retardance, the glass transition temperature, the water absorption ratio, and the elastic modulus (250°C) were evaluated by the following method. Flame retardance: evaluated according to a UL94 vertical combustion testing method. Glass transition temperature: measured with a dynamic viscoelasticity analyzer (manufactured by TA INSTRUMENTS) according to JIS C 6481. Water absorption ratio: a sample which has a size of 50 × 50 mm and has been previously dried in a drier at 125°C for 2 hours was allowed to stand under conditions of 121°C and 2 atm for 5 hours with a pressure cooker testing apparatus (manufactured by HIRAYAMA PRODUCING CORPORATION), and a change in weight of the sample was then measured.
    Bending elastic modulus (250°C): measured at a temperature of 250°C using Shimadzu Autograph (Model: AG-5kNIS, manufactured by Shimadzu Corporation) according to JIS C6481.
    [Table 1]
     Example 1*Example 2Example 3*Example 4Example 5*Example 6Example 7*
    Flame retardance V-0 V-0 V-0 V-0 V-0 V-0 V-0
    Glass transition temperature 270 284 280 294 276 285 281
    Water absorption ratio 0.49 0.51 0.51 0.53 0.49 0.51 0.53
    Bending elastic modulus (250°C) 16.4 17.0 16.0 16.5 17.0 18.0 17.0
     Example 8Example 9*Example 10Example 11*Example 12Example 13*Example 14
    Flame retardance V-0 V-0 V-0 V-0 V-0 V-0 V-0
    Glass transition temperature 296 274 287 267 273 274 288
    Water absorption ratio 0.55 0.52 0.53 0.52 0.53 0.54 0.55
    Bending elastic modulus (250°C) 18.2 16.7 17.8 16.3 16.8 16.7 17.8
     Example 15*Example 16Example 17Example 18Example 19Example 20Example 21*
    Flame retardance V-0 V-0 V-0 V-0 V-0 V-0 V-0
    Glass transition temperature 282 296 269 286 295 286 269
    Water absorption ratio 0.50 0.51 0.49 0.50 0.54 0.49 0.53
    Bending elastic modulus (250°C) 17.2 18.1 16.4 17.2 16.2 17.6 16.4
     Example 22*Example 23*Example 24*Example 25*   
    Flame retardance V-0 V-0 V-0 V-0      
    Glass transition temperature 281 302 301 302      
    Water absorption ratio 0.52 0.57 0.52 0.51      
    Bending elastic modulus (250°C) 17.0 18.4 18.0 17.8      
    Unit glass transition temperature: °C; water absorption ratio: % by weight; elastic modulus: GPa;* Reference Example - not part of the claimed invention
    [Table 2]
     Comp. Example 26Comp. Example 27Example 28*Example 29Example 30*Example 31*Example 32*Example 33*Comp. Example 34Example 35*
    Flame retardance V-0 burnout V-1 V-1 V-1 V-0 V-0 V-0 V-0 V-1
    Glass transition temperature 249 250 224 232 242 240 289 252 248 228
    Water absorption ratio 0.47 0.59 0.60 0.64 0.65 0.62 0.66 0.63 0.50 0.62
    Bending elastic modulus (250°C) 15.4 12.1 13.6 14.3 14.7 14.7 17.9 15.4 15.3 14.3
    unit glass transition temperature: °C; water absorption ratio: % by weight; elastic modulus: GPa; *Reference Example - not part of the claimed invention



    Claims

    1. A resin composition comprising:

    a maleimide compound (A) represented by general formula (1):

    wherein R represents a hydrogen atom or a methyl group, and n represents an integer of 1 to 10 on average;

    a cyanate ester compound (B);

    a non-halogen epoxy resin (C);

    an inorganic filler (D); and

    an imidazole compound (F);

    wherein the imidazole compound (F) is 2,4,5-triphenyl imidazole


     
    2. The resin composition according to claim 1, wherein a content of the maleimide compound (A) is 10 to 50 parts by mass based on 100 parts by mass in total of the maleimide compound (A), the cyanate ester compound (B), and the non-halogen epoxy resin (C).
     
    3.  The resin composition according to any one of claims 1 to 2, wherein a content of the cyanate ester compound (B) is 10 to 50 parts by mass based on 100 parts by mass in total of the maleimide compound (A), the cyanate ester compound (B), and the non-halogen epoxy resin (C).
     
    4. The resin composition according to any one of claims 1 to 3, wherein a content of the non-halogen epoxy resin (C) is 5 to 50 parts by mass based on 100 parts by mass in total of the maleimide compound (A), the cyanate ester compound (B), and the non-halogen epoxy resin (C).
     
    5. The resin composition according to any one of claims 1 to 4, wherein a content of the inorganic filler (D) is 50 to 400 parts by mass based on 100 parts by mass in total of the maleimide compound (A), the cyanate ester compound (B), and the non-halogen epoxy resin (C).
     
    6. The resin composition according to any one of claims 1 to 5, wherein a content of the imidazole compound (F) is 0.01 to 10 parts by mass based on 100 parts by mass in total of the maleimide compound (A), the cyanate ester compound (B), and the non-halogen epoxy resin (C).
     
    7. A resin composition comprising:

    a non-halogen epoxy resin (C);

    an inorganic filler (D); and

    a bismaleimide triazine resin (E) obtained by prepolymerizing a maleimide compound (A) and a cyanate ester compound (B), the maleimide compound (A) represented by general formula (1):

    wherein R represents a hydrogen atom or a methyl group, and n represents an integer of 1 to 10 on average.


     
    8. The resin composition according to claim 7, further comprising an imidazole compound (F) represented by general formula (3):

    wherein Ar is a phenyl group, a naphthalene group, a biphenyl group, an anthracene group, or a hydroxyl group modified substance thereof, and R is a hydrogen atom, an alkyl group, an aryl group, or a hydroxyl group modified substance thereof.
     
    9.  The resin composition according to claim 7 or 8, wherein a content of the non-halogen epoxy resin (C) is 5 to 50 parts by mass based on 100 parts by mass in total of the non-halogen epoxy resin (C) and the bismaleimide triazine resin (E).
     
    10. The resin composition according to any one of claims 7 to 9, wherein a content of the inorganic filler (D) is 50 to 400 parts by mass based on 100 parts by mass in total of the non-halogen epoxy resin (C) and the bismaleimide triazine resin (E).
     
    11. The resin composition according to any one of claims 7 to 10, wherein a content of the bismaleimide triazine resin (E) is 20 to 80 parts by mass based on 100 parts by mass in total of the non-halogen epoxy resin (C) and the bismaleimide triazine resin (E).
     
    12. The resin composition according to any one of claims 7 to 11, wherein a content of the maleimide compound (A) is 5 to 75 parts by mass based on 100 parts by mass of the bismaleimide triazine resin (E) when the bismaleimide triazine resin (E) is produced.
     
    13. The resin composition according to any one of claims 8 to 12, wherein a content of the imidazole compound (F) is 0.01 to 10 parts by mass based on 100 parts by mass in total of the non-halogen epoxy resin (C) and the bismaleimide triazine resin (E).
     
    14. The resin composition according to any one of claims 8 to 13, wherein the imidazole compound (F) is 2,4,5-triphenyl imidazole.
     
    15. The resin composition according to any one of claims 1 to 14 wherein the inorganic filler (D) is at least one selected from the group consisting of silica, boehmite, magnesium hydroxide, alumina, and talc.
     
    16. The resin composition according to any one of claims 1 to 15, wherein the inorganic filler (D) is the boehmite and/or the silica.
     
    17. The resin composition according to any one of claims 1 to 16, wherein the non-halogen epoxy resin (C) is at least one selected from the group consisting of a phenol biphenyl aralkyl-based epoxy resin, a phenol novo lac-based epoxy resin, a cresol novolac-based epoxy resin, a polyoxynaphthylene-based epoxy resin, a tetrafunctional naphthalene-based epoxy resin, and an anthracene-based epoxy resin.
     
    18. The resin composition according to any one of claims 1 to 17, wherein the cyanate ester compound (B) is a naphthol aralkyl-based cyanate ester compound and/or a novolac-based cyanate ester compound.
     
    19.  The resin composition according to any one of claims 1 to 18, wherein the cyanate ester compound (B) is a naphthol aralkyl-based cyanate ester compound represented by general formula (2):

    wherein R represents a hydrogen atom or a methyl group, and m represents an integer of 1 to 10 on average.
     
    20. The resin composition according to any one of claims 1 to 19 used for a cured product having a glass transition temperature of 260 to 360°C.
     
    21. A cured product comprising a resin composition according to any one of claims 1 to 20.
     
    22. A prepreg comprising:

    a base material; and

    a resin composition according to any one of claims 1 to 20 impregnated into or coated on the base material.


     
    23. A laminate obtained by laminate-molding a prepreg according to claim 22.
     
    24. A metal foil-clad laminate obtained by laminate-molding a prepreg according to claim 22 and a metal foil.
     
    25. A laminate obtained by laminating a prepreg according to claim 22, and curing the prepreg at a temperature of 100 to 300°C for 0.05 to 5 hours.
     
    26. A metal foil-clad laminate obtained by laminating a prepreg according to claim 22 and a metal foil, and curing the prepreg and the metal foil at a temperature of 100 to 300°C for 0.05 to 5 hours.
     
    27. A method for producing a laminate comprising the steps of:

    laminating a prepreg according to claim 22; and

    heating the prepreg at a temperature of 100 to 300°C for 0.05 to 5 hours.


     
    28. A method for producing a metal foil-clad laminate comprising the steps of:

    laminating a prepreg according to claim 22 and a metal foil; and

    heating the prepreg and the metal foil at a temperature of 100 to 300°C for 0.05 to 5 hours.


     


    Ansprüche

    1. Harzzusammensetzung, umfassend:

    eine durch die allgemeine Formel (1) dargestellte Maleimidverbindung (A):

    worin R ein Wasserstoffatom oder eine Methylgruppe darstellt und n eine ganze Zahl von 1 bis 10 im Mittel darstellt;

    eine Cyanatesterverbindung (B);

    ein Nicht-Halogen-Epoxyharz (C);

    einen anorganischen Füllstoff (D); und

    eine Imidazolverbindung (F);

    worin die Imidazolverbindung (F) 2,4,5-Triphenylimidazol ist.


     
    2. Harzzusammensetzung gemäß Anspruch 1, worin der Gehalt der Maleimidverbindung (A) 10 bis 50 Masseteile beträgt, bezogen auf 100 Masseteile der Gesamtheit der Maleimidverbindung (A), der Cyanatesterverbindung (B) und des Nicht-halogen-Epoxyharzes (C).
     
    3. Harzzusammensetzung gemäß irgendeinem der Ansprüche 1 bis 2, worin der Gehalt der Cyanatesterverbindung (B) 10 bis 50 Masseteile beträgt, bezogen auf 100 Masseteile der Gesamtheit der Maleimidverbindung (A), der Cyanatesterverbindung (B) und des Nicht-Halogen-Epoxyharzes (C).
     
    4. Harzzusammensetzung gemäß irgendeinem der Ansprüche 1 bis 3, worin der Gehalt des Nicht-Halogen-Epoxyharzes (C) 5 bis 50 Masseteile beträgt, bezogen auf 100 Masseteile der Gesamtheit der Maleimidverbindung (A), der Cyanatesterverbindung (B) und des Nicht-Halogen-Epoxyharzes (C).
     
    5. Harzzusammensetzung gemäß irgendeinem der Ansprüche 1 bis 4, worin der Gehalt des anorganischen Füllstoffs (D) 50 bis 400 Masseteile beträgt, bezogen auf 100 Masseteile der Gesamtheit der Maleimidverbindung (A), der Cyanatesterverbindung (B) und des Nicht-Halogen-Epoxyharzes (C).
     
    6. Harzzusammensetzung gemäß irgendeinem der Ansprüche 1 bis 5, worin der Gehalt der Imidazolverbindung (F) 0,01 bis 10 Masseteile beträgt, bezogen auf 100 Masseteile der Gesamtheit der Maleimidverbindung (A), der Cyanatesterverbindung (B) und des Nicht-Halogen-Epoxyharzes (C).
     
    7. Harzzusammensetzung, umfassend:

    ein Nicht-Halogen-Epoxyharz (C);

    einen anorganischen Füllstoff (D); und

    ein Bismaleimid-Triazin-Harz (E), erhalten durch Vorpolymerisieren einer Maleimidverbindung (A) und einer Cyanatesterverbindung (B), wobei die Maleimidverbindung (A) durch die allgemeine Formel (1) dargestellt wird:

    worin R ein Wasserstoffatom oder eine Methylgruppe darstellt und n eine ganze Zahl von 1 bis 10 im Mittel darstellt.


     
    8. Harzzusammensetzung gemäß Anspruch 7, ferner umfassend eine durch die allgemeine Formel (3) dargestellte Imidazolverbindung (F):

    worin Ar eine Phenylgruppe, eine Naphthalingruppe, eine Biphenylgruppe, eine Anthracengruppe oder eine Hydroxylgruppe-modifizierte Substanz hiervon ist, und R ein Wasserstoffatom, eine Alkylgruppe, eine Arylgruppe oder eine Hydroxylgruppe-modifizierte Substanz hiervon ist.
     
    9. Harzzusammensetzung gemäß Anspruch 7 oder 8, worin der Gehalt des Nicht-Halogen-Epoxyharzes (C) 5 bis 50 Masseteile beträgt, bezogen auf 100 Masseteile der Gesamtheit des Nicht-Halogen-Epoxyharzes (C) und des Bismaleimid-Triazin-Harzes (E).
     
    10. Harzzusammensetzung gemäß irgendeinem der Ansprüche 7 bis 9, worin der Gehalt des anorganischen Füllstoffs (D) 50 bis 400 Masseteile beträgt, bezogen auf 100 Masseteile der Gesamtheit des Nicht-Halogen-Epoxyharzes (C) und des Bismaleimid-Triazin-Harzes (E).
     
    11. Harzzusammensetzung gemäß irgendeinem der Ansprüche 7 bis 10, worin der Gehalt des Bismaleimid-Triazin-Harzes (E) 20 bis 80 Masseteile beträgt, bezogen auf 100 Masseteile der Gesamtheit des Nicht-Halogen-Epoxyharzes (C) und des Bismaleimid-Triazin-Harzes (E).
     
    12. Harzzusammensetzung gemäß irgendeinem der Ansprüche 7 bis 11, worin der Gehalt der Maleimidverbindung (A) 5 bis 75 Masseteile beträgt, bezogen auf 100 Masseteile des Bismaleimid-Triazin-Harzes (E), wenn das Bismaleimid-Triazin-Harz (E) hergestellt wird.
     
    13. Harzzusammensetzung gemäß irgendeinem der Ansprüche 8 bis 12, worin der Gehalt der Imidazolverbindung (F) 0,01 bis 10 Masseteile beträgt, bezogen auf 100 Masseteile der Gesamtheit des Nicht-Halogen-Epoxyharzes (C) und des Bismaleimid-Triazin-Harzes (E).
     
    14. Harzzusammensetzung gemäß irgendeinem der Ansprüche 8 bis 13, worin die Imidazolverbindung (F) 2,4,5-Triphenylimidazol ist.
     
    15. Harzzusammensetzung gemäß irgendeinem der Ansprüche 1 bis 14, worin der anorganische Füllstoff (D) zumindest einer ist, ausgewählt aus der Gruppe bestehend aus Silika, Böhmit, Magnesiumhydroxid, Aluminiumoxid und Talk.
     
    16. Harzzusammensetzung gemäß irgendeinem der Ansprüche 1 bis 15, worin der anorganische Füllstoff (D) Böhmit und/oder Silika ist.
     
    17. Harzzusammensetzung gemäß irgendeinem der Ansprüche 1 bis 16, worin das Nicht-Halogen-Epoxyharz (C) zumindest eines ist, ausgewählt aus der Gruppe bestehend aus einem Phenol-Biphenyl-Aralkyl-basierten Epoxyharz, einem Phenol-Novolak-basierten Epoxyharz, einem Kresol-Novolak-basierten Epoxyharz, einem Polyoxynaphthylenbasierten Epoxyharz, einem tetrafunktionellen Naphthalin-basierten Epoxyharz und einem Anthracenbasierten Epoxyharz.
     
    18. Harzzusammensetzung gemäß irgendeinem der Ansprüche 1 bis 17, worin die Cyanatesterverbindung (B) eine Naphthol-Aralkyl-basierte Cyanatesterverbindung und/oder eine Novolak-basierte Cyanatesterverbindung ist.
     
    19. Harzzusammensetzung gemäß irgendeinem der Ansprüche 1 bis 18, worin die Cyanatesterverbindung (B) eine Naphthol-Aralkyl-basierte Cyanatesterverbindung ist, dargestellt durch die allgemeine Formel (2):

    worin R ein Wasserstoffatom oder eine Methylgruppe darstellt und m eine ganze Zahl von 1 bis 10 im Mittel darstellt.
     
    20. Harzzusammensetzung gemäß irgendeinem der Ansprüche 1 bis 19, die für ein gehärtetes Produkt mit einer Glasübergangstemperatur von 260 bis 360°C verwendet wird.
     
    21. Gehärtetes Produkt, umfassend die Harzzusammensetzung gemäß irgendeinem der Ansprüche 1 bis 20.
     
    22. Prepreg, umfassend:

    ein Basismaterial; und

    eine Harzzusammensetzung gemäß irgendeinem der Ansprüche 1 bis 20, die in das Basismaterial imprägniert oder hierauf beschichtet ist.


     
    23. Laminat, erhalten durch Laminat-Formen eines Prepregs gemäß Anspruch 22.
     
    24. Metallfolien-verkleidetes Laminat, erhalten durch Laminat-Formen eines Prepregs gemäß Anspruch 22 und einer Metallfolie.
     
    25. Laminat, erhalten durch Laminieren eines Prepregs gemäß Anspruch 22 und Härten des Prepregs bei einer Temperatur von 100 bis 300°C für 0,05 bis 5 Stunden.
     
    26. Metallfolien-verkleidetes Laminat, erhalten durch Laminieren eines Prepregs gemäß Anspruch 22 und einer Metallfolie, und Härten des Prepregs und der Metallfolie bei einer Temperatur von 100 bis 300°C für 0,05 bis 5 Stunden.
     
    27. Verfahren zur Herstellung eines Laminats, umfassend die Schritte:

    Laminieren eines Prepregs gemäß Anspruch 22; und

    Erwärmen des Prepregs bei einer Temperatur von 100 bis 300°C für 0,05 bis 5 Stunden.


     
    28. Verfahren zur Herstellung eines mit Metallfolie verkleideten Laminats, umfassend die Schritte:

    Laminieren eines Prepregs gemäß Anspruch 22 und einer Metallfolie; und

    Erwärmen des Prepregs und der Metallfolie bei einer Temperatur von 100 bis 300°C für 0,05 bis 5 Stunden.


     


    Revendications

    1. Composition de résine comprenant :

    un composé maléimide (A) représenté par la formule générale (1) :

    dans laquelle R représente un atome d'hydrogène ou un groupe méthyle, et n représente un nombre entier de 1 à 10 en moyenne ;

    un composé ester de cyanate (B) ;

    une résine époxy non halogénée (C) ;

    une charge inorganique (D) ; et

    un composé imidazole (F) ;

    dans laquelle le composé imidazole (F) est le 2,4,5-triphényl-imidazole


     
    2. Composition de résine selon la revendication 1, dans laquelle une teneur du composé maléimide (A) va de 10 à 50 parties en masse sur la base de 100 parties en masse au total du composé maléimide (A), du composé ester de cyanate (B) et de la résine époxy non halogénée (C).
     
    3. Composition de résine selon l'une quelconque des revendications 1 à 2, dans laquelle une teneur du composé ester de cyanate (B) va de 10 à 50 parties en masse sur la base de 100 parties en masse au total du composé maléimide (A), du composé ester de cyanate (B) et de la résine époxy non halogénée (C).
     
    4. Composition de résine selon l'une quelconque des revendications 1 à 3, dans laquelle une teneur de la résine époxy non halogénée (C) va de 5 à 50 parties en masse sur la base de 100 parties en masse au total du composé maléimide (A), du composé ester de cyanate (B) et de la résine époxy non halogénée (C).
     
    5. Composition de résine selon l'une quelconque des revendications 1 à 4, dans laquelle une teneur de la charge inorganique (D) va de 50 à 400 parties en masse sur la base de 100 parties en masse au total du composé maléimide (A), du composé ester de cyanate (B) et de la résine époxy non halogénée (C).
     
    6. Composition de résine selon l'une quelconque des revendications 1 à 5, dans laquelle une teneur du composé imidazole (F) va de 0,01 à 10 parties en masse sur la base de 100 parties en masse au total du composé maléimide (A), du composé ester de cyanate (B) et de la résine époxy non halogénée (C).
     
    7. Composition de résine comprenant :

    une résine époxy non halogénée (C) ;

    une charge inorganique (D) ; et

    une résine bismaléimide triazine (E) obtenue par prépolymérisation d'un composé maléimide (A) et d'un composé ester de cyanate (B), le composé maléimide (A) représenté par la formule générale (1) :

    dans laquelle R représente un atome d'hydrogène ou un groupe méthyle, et n représente un nombre entier de 1 à 10 en moyenne.


     
    8. Composition de résine selon la revendication 7, comprenant en outre un composé imidazole (F) représenté par la formule générale (3) :

    dans laquelle Ar est un groupe phényle, un groupe naphtalène, un groupe biphényle, un groupe anthracène ou une substance de ceux-ci modifiée par un groupe hydroxyle, et R est un atome d'hydrogène, un groupe alkyle, un groupe aryle ou une substance de ceux-ci modifiée par un groupe hydroxyle.
     
    9. Composition de résine selon la revendication 7 ou 8, dans laquelle une teneur de la résine époxy non halogénée (C) va de 5 à 50 parties en masse sur la base de 100 parties en masse au total de la résine époxy non halogénée (C) et de la résine bismaléimide triazine (E).
     
    10. Composition de résine selon l'une quelconque des revendications 7 à 9, dans laquelle une teneur de la charge inorganique (D) va de 50 à 400 parties en masse sur la base de 100 parties en masse au total de la résine époxy non halogénée (C) et de la résine bismaléimide triazine (E).
     
    11. Composition de résine selon l'une quelconque des revendications 7 à 10, dans laquelle une teneur de la résine bismaléimide triazine (E) va de 20 à 80 parties en masse sur la base de 100 parties en masse au total de la résine époxy non halogénée (C) et de la résine bismaléimide triazine (E).
     
    12. Composition de résine selon l'une quelconque des revendications 7 à 11, dans laquelle une teneur du composé maléimide (A) va de 5 à 75 parties en masse sur la base de 100 parties en masse de la résine bismaléimide triazine (E) lorsque la résine bismaléimide triazine (E) est produite.
     
    13. Composition de résine selon l'une quelconque des revendications 8 à 12, dans laquelle une teneur du composé imidazole (F) va de 0,01 à 10 parties en masse sur la base de 100 parties en masse au total de la résine époxy non halogénée (C) et de la résine bismaléimide triazine (E).
     
    14. Composition de résine selon l'une quelconque des revendications 8 à 13, dans laquelle le composé imidazole (F) est le 2,4,5-triphényl-imidazole.
     
    15. Composition de résine selon l'une quelconque des revendications 1 à 14 dans laquelle la charge inorganique (D) est au moins l'une choisie dans le groupe constitué de la silice, la boehmite, l'hydroxyde de magnésium, l'alumine et le talc.
     
    16. Composition de résine selon l'une quelconque des revendications 1 à 15, dans laquelle la charge inorganique (D) est la boehmite et/ou la silice.
     
    17. Composition de résine selon l'une quelconque des revendications 1 à 16, dans laquelle la résine époxy non halogénée (C) est au moins l'une choisie dans le groupe constitué d'une résine époxy à base de phénol-biphényl-aralkyle, une résine époxy à base de phénol-novolac, une résine époxy à base de crésol-novolac, une résine époxy à base de polyoxynaphtylène, une résine époxy à base de naphtalène tétrafonctionnelle et une résine époxy à base d'anthracène.
     
    18. Composition de résine selon l'une quelconque des revendications 1 à 17, dans laquelle le composé ester de cyanate (B) est un composé ester de cyanate à base de naphtol aralkyle et/ou un composé ester de cyanate à base de novolac.
     
    19. Composition de résine selon l'une quelconque des revendications 1 à 18, dans laquelle le composé ester de cyanate (B) est un composé ester de cyanate à base de naphtol aralkyle représenté par la formule générale (2) :

    dans laquelle R représente un atome d'hydrogène ou un groupe méthyle, et m représente un nombre entier de 1 à 10 en moyenne.
     
    20. Composition de résine selon l'une quelconque des revendications 1 à 19 utilisée pour un produit durci ayant une température de transition vitreuse de 260 à 360 °C.
     
    21. Produit durci comprenant une composition de résine selon l'une quelconque des revendications 1 à 20.
     
    22. Préimprégné comprenant :

    un matériau de base ; et

    une composition de résine selon l'une quelconque des revendications 1 à 20 imprégnée dans ou revêtue sur le matériau de base.


     
    23. Stratifié obtenu par moulage de stratifié d'un préimprégné selon la revendication 22.
     
    24. Stratifié plaqué d'une feuille de métal obtenu par moulage de stratifié d'un préimprégné selon la revendication 22 et d'une feuille de métal.
     
    25. Stratifié obtenu par stratification d'un préimprégné selon la revendication 22, et durcissement du préimprégné à une température de 100 à 300 °C pendant 0,05 à 5 heures.
     
    26. Stratifié plaqué d'une feuille de métal obtenu par stratification d'un préimprégné selon la revendication 22 et d'une feuille de métal, et durcissement du préimprégné et de la feuille de métal à une température de 100 à 300 °C pendant 0,05 à 5 heures.
     
    27. Procédé de production d'un stratifié comprenant les étapes consistant à :

    stratifier un préimprégné selon la revendication 22 ; et

    chauffer le préimprégné à une température de 100 à 300 °C pendant 0,05 à 5 heures.


     
    28. Procédé de production d'un stratifié plaqué d'une feuille de métal comprenant les étapes consistant à :

    stratifier un préimprégné selon la revendication 22 et une feuille de métal ; et

    chauffer le préimprégné et la feuille de métal à une température de 100 à 300 °C pendant 0,05 à 5 heures.


     






    Cited references

    REFERENCES CITED IN THE DESCRIPTION



    This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

    Patent documents cited in the description