(19)
(11)EP 2 819 835 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
14.08.2019 Bulletin 2019/33

(21)Application number: 13713526.5

(22)Date of filing:  11.02.2013
(51)International Patent Classification (IPC): 
B29C 70/46(2006.01)
B29K 105/08(2006.01)
B29C 70/44(2006.01)
B29K 307/04(2006.01)
B29K 101/10(2006.01)
B29C 70/54(2006.01)
B29C 70/34(2006.01)
B29L 31/30(2006.01)
C08J 5/24(2006.01)
(86)International application number:
PCT/IB2013/051115
(87)International publication number:
WO 2013/128312 (06.09.2013 Gazette  2013/36)

(54)

PROCESS FOR MANUFACTURING ARTICLES IN CARBON FIBER

VERFAHREN ZUR HERSTELLUNG VON KOHLEFASERARTIKELN

PROCÉDÉ DE FABRICATION D'ARTICLES EN FIBRE DE CARBONE


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 28.02.2012 IT MI20120307

(43)Date of publication of application:
07.01.2015 Bulletin 2015/02

(73)Proprietor: Automobili Lamborghini S.P.A.
40019 Sant'Agata Bolognese (IT)

(72)Inventor:
  • MASINI, Attilio
    I-40050 Monteveglio BO (IT)

(74)Representative: Puggioli, Tommaso 
Bugnion S.p.A. Via di Corticella, 87
40128 Bologna
40128 Bologna (IT)


(56)References cited: : 
US-A- 4 855 097
US-B2- 6 797 379
US-B1- 6 454 893
  
      
    Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


    Description


    [0001] The present invention relates to the field of manufacturing articles in composite materials. More particularly, the invention relates to a heat compression molding process for the manufacture of articles in composite materials comprising carbon fibers and an article manufactured with this process.

    [0002] Known processes for manufacturing articles in composite materials use the technology of heat compression molding, in which measured quantities of materials comprising a heat-hardening matrix reinforced with fibers of rigid materials are inserted into molds made of steel or aluminum suitable to a confer a predetermined shape to the article. This technology, created for molding articles reinforced with glass fibers but today increasingly used also for articles reinforced with carbon fibers, allows to obtain components characterized by low weight and excellent mechanical properties, as well as good dimensional tolerances.

    [0003] The heat compression molding technology is very suitable for the manufacture of articles substantially free from undercut details, obtainable with molds made up of two overlapping parts inside which the shape of the article is formed in negative and in two portions.

    [0004] In a typical process of heat compression molding for articles of composite material based on carbon fibers, semi-finished products made of heat-hardening resins and carbon fibers are used. These semi-finished products, manufactured in processes separate from the compression molding process, are in the form of pre-impregnated sheets known in the industry with the English acronym "SMC" (Sheet Molding Compound).

    [0005] The SMC semi-finished products generally comprise a plurality of pre-impregnated sheets superimposed so as to form a single block. Before being loaded into the mold, an SMC semi-finished products can be advantageously subjected to a heating treatment, for example by means of infrared rays, which facilitates its arrangement in the mold and allows to reduce the curing time of the heat-hardening resin.

    [0006] In order to control features such as the dimensional shrinkage during the hot crosslinking phase, the surface finishing, the ease of detachment from the molds and the behavior in fire, the heat-hardening resins are usually charged with mineral charges, lubricants, release agents, flame retardants and the like. Calcium carbonate, kaolin, stearates, oxides and hydrates of calcium, magnesium, aluminum are some of the most used additives.

    [0007] Thanks to the low weights and the high mechanical characteristics, the articles in composite materials with carbon fibers made with the heat compression molding technology starting from SMC semi-finished products have been used for some years in the automotive industry for the production of structural components such as, for example, supports for lights, windscreen frames and supporting elements of bodywork parts.

    [0008] Nevertheless, these articles are not generally used for the manufacture of aesthetic elements of a vehicle, such as, for example, bodywork parts and details of the passenger compartment, due to their rather coarse surface finishing. In particular, an article of composite material made starting from SMC semi-finished products has surface defects such as, for example, porosity and undulations that are even visible to the naked eye and that therefore, despite the excellent mechanical characteristics, make it unsuitable for a use also or exclusively aesthetic.

    [0009] US 4855097 describes a method for making an exterior automotive body panel by compression molding in which a charge containing a curable resin covers from 40% to 80% of the surface area of the molding surface. According to this known document coverages higher than 80% do not permit sufficient flow of charge necessary to provide a slight movement of the same.

    [0010] The object of the present invention is therefore to provide a process for the manufacture of articles in composite materials comprising carbon fibers, which is free from said drawbacks. Said object is achieved with a process whose main features are specified in claim 1, while other features are specified in the remaining claims.

    [0011] An idea of solution underlying the present invention is to minimize the sliding of the material of the SMC semi-finished products in order to minimize the formation of surface defects. The inventors have found that the presence of surface defects such as porosity and undulations is strongly influenced by the flow of the composite material loaded into the mold, which determines different orientations of the carbon fibers in different areas of the finished article. In particular, it has been observed that in an article of composite material based on carbon fibers made according to known heat compression molding processes, the surface portions with less surface defects are those in which the fiber orientation is substantially identical to the one of the SMC semi-finished product introduced into the mold.

    [0012] To obtain an article free from surface defects, according to the invention the loading of the SMC semi-finished product in the mold is done by calculating both the weight suitable to allow the complete filling of the shape corresponding to the shape of the article, and the surface development of the shape formed in the mold and by making sure that the surfaces of the semi-finished product cover the surfaces of the shape in a percentage higher than 80% and less than or equal to 99%. Thanks to these characteristics it is possible to minimize the sliding of the composite material in the mold, and thus of the carbon fibers, thereby significantly reducing the formation of surface defects, in particular porosity and undulations. Consequently, the articles made according to the process of the invention are suitable for both structural and aesthetic uses, as for example for the manufacture of bodywork components for motor vehicles and/or covering elements for passenger compartments, which particulars were not achievable so far with the known heat compression molding processes of SMC articles.

    [0013] According to a preferred embodiment, the process of the invention comprises a step of adding at least one layer of a pre-impregnated fabric with unidirectional carbon fibers, in which step said at least one layer is arranged in contact with one or both surfaces of the SMC semi-finished product which are intended to come into contact with the surfaces of the shape of the article formed in the mold.

    [0014] To facilitate the evacuation of air and any other volatile substances trapped between the SMC semi-finished product and the one or more layers of pre-impregnated fabric superimposed to it, it is advantageous to produce cuts on the unidirectional fibers. This makes it possible to avoid the formation of bubbles and thus to further improve the surface finishing of the article.

    [0015] In order not to weaken the layer of pre-impregnated fabric of unidirectional fibers, the cuts are preferably inclined with respect to the fiber direction and misaligned with each other in the same direction. Furthermore, the cuts have a predetermined length and relative distance.

    [0016] As an alternative to the layer of pre-impregnated fabric of unidirectional carbon fibers, it is possible to use a sheet of nonwoven fabric made of carbon fiber, fiberglass or acrylic material which, as in the previous case, can be arranged in contact with one or both surfaces of the SMC semi-finished product intended to come into contact with the surfaces of the shape formed in the mold.

    [0017] The use of one or more layers of pre-impregnated fabric of unidirectional fibers or of one or more sheets of a nonwoven carbon fabric is advantageous since it allows to further improve the surface finishing, thereby obtaining a product essentially free from surface defects. In fact, such layers or sheets have surface finishing features even higher than those of the SMC semi-finished products.

    [0018] It is also possible to provide the combined use of at least one layer of a pre-impregnated fabric of unidirectional carbon fibers and at least one sheet of nonwoven carbon fabric.

    [0019] Another advantage offered by the invention is that the heat compression molding process does not entail increased costs compared to a heat compression molding process of the traditional type.

    [0020] Further advantages and characteristics of the process for manufacturing composite material comprising carbon fibers according to the present invention will become apparent to those skilled in the art from the following detailed description of an embodiment thereof with reference to the accompanying drawings in which:
    • Figures 1 to 3 show schematically the main steps of a heat compression molding process of an article made of composite material according to the invention; and
    • Figure 4 is a diagram showing the progress in time of the pressure during the molding process according to the invention.


    [0021] Figures 1 to 3 show schematically the main steps of a heat compression molding process of an article made of composite material according to the invention.

    [0022] An SMC semi-finished product 10 comprising one or more sheets of composite material comprising a matrix of heat-hardening resin and carbon fibers is inserted into a mold 20 in which the shape of an article 30 to be manufactured in formed in negative. As it is known, the shape of the article is divided into two portions along an opening plane P of the mold to allow the insertion of the SMC semi-finished product and the extraction of the finished article. The surfaces forming the shape in negative of the article 30 are indicated with the reference numbers 31, 32, and are formed in a first portion 21 and a second portion 22, respectively, of the mold 20.

    [0023] The heat-hardening resin used in the SMC semi-finished product is preferably selected from the group comprising vinyl-ester, phenolic, epoxy, polyester, polyamide, cyano-ester resins or combinations thereof.

    [0024] The carbon used is in the form of filaments of length comprised between 5 and 200 mm, preferably equal to 1 inch (25.4 mm). Each carbon filament is composed of a number of carbon fibers comprised between 3000 and 24000 fibers, preferably equal to about 12000 fibers. The amount of carbon fibers varies from 25% to 75% by weight of the heat-hardening resin, and is preferably equal to 50% by weight.

    [0025] To obtain an article, the mold 20 is preheated to a suitable temperature to allow the crosslinking of the heat-hardening resin that constitutes the matrix of the SMC semi-finished product. In the case of the above mentioned heat-hardening resins, this temperature is for example comprised between 120 and 150° C, and preferably equal to 130° C.

    [0026] The amount of SMC semi-finished product introduced into the mold is calculated by weighing on the basis of the volume of the article to be manufactured.

    [0027] According to the present invention, in addition to the calculation of the weight of the SMC semi-finished product, the dimensions of the surfaces of the SMC semi-finished product intended to come into contact with the surfaces 31, 32 of the shape formed in the mold 20 are calculated so as to cover these surfaces in a percentage higher than 80% and less than or equal to 99%. Thanks to these characteristics, the sliding of the material during the closing phase of the mold and the subsequent stages of compression is extremely limited, allowing to maintain substantially unaltered the isotropic arrangement of the fibers of the SMC semi-finished product. The article 30 resulting from the molding process according to the invention will therefore be characterized by a surface finishing substantially free from defects.

    [0028] In the calculation of the surface of coverage the entire development of the surfaces 31, 32 of the shape is considered, including flat portions, protrusions and depressions, not the frontal area resulting, for example, on the opening plane P of the mold. However, it has been experimentally verified that in the calculation of the coverage surface it is possible to disregard details having thin thickness, such as the ribs.

    [0029] It will be understood that during the molding process there will be a greater sliding of the material for lower percentages of coverage, i.e. close to 80%, and a sliding substantially zero for the highest percentages of coverage, namely close to 99%. Through experimental tests it has been verified that the lowest percentages of coverage are more suitable for articles having thicknesses in the order of 2 mm, where the sliding of the material is in any case very limited, while higher percentages of covering are more suitable to articles having thicknesses in the order of 4 mm, where instead there is a greater sliding of the material during the molding process.

    [0030] According to a preferred embodiment of the invention, the process can include a step of adding one or more layers of a pre-impregnated fabric of unidirectional carbon fibers, arranged in contact with one or both surfaces of the SMC semi-manufactured product 10 intended to come into contact with the surfaces 31, 32 of the shape, thus intended to form the outer surfaces of the article.

    [0031] The pre-impregnated material which is used can for example comprise a matrix of heat-hardening resin, for example epoxy, in which a plurality of carbon fibers arranged in parallel are immersed. The use of one or more additional layers comprising unidirectional carbon fibers allows to further improve the surface finishing, thereby obtaining a product essentially free from surface defects.

    [0032] The overlap of one or more layers of pre-impregnated fabric with unidirectional carbon fibers also advantageously allows to improve the mechanical characteristics of the article, for example being able to choose a fiber orientation according to the direction of the loads which will stress it in operation. This feature is very important in the manufacture of articles intended for a use both aesthetic and structural.

    [0033] The material used in this step can for example be a pre-impregnated fabric of unidirectional fibers having a carbon content comprised between 20 and 140 g/m2, preferably equal to about 40 g/m2.

    [0034] To facilitate the evacuation of air and other volatile substances trapped between the layers, so as to avoid the formation of bubbles and further improve the surface finishing, it is advantageous to make cuts on the unidirectional fibers.

    [0035] The cuts are preferably inclined with respect to the fiber direction and arranged so that consecutive cuts in such direction are partially misaligned with each other, namely involving only in part the same fibers.

    [0036] In particular, the angle of inclination of the cuts compared to the fibers is between 30° and 60°, for example 45°, and the consecutive cuts in the direction of the carbon fibers have in common at most 50% of the fibers. These features allow the elimination of air and other volatile substances without weakening the layer of pre-impregnated fabric of unidirectional fibers.

    [0037] Moreover, always with the aim of allowing the removal of air and other volatile substances without weakening the layer of pre-impregnated fabric of unidirectional fibers, the cuts have a length comprised between 1 and 20 mm, for example 5 mm, and are spaced from each other by an interval of between 5 and 100 mm, for example 50 mm.

    [0038] As an alternative to the pre-impregnated fabric of unidirectional carbon fibers, it is possible to use one or more sheets of nonwoven carbon, fiber glass or acrylic fabric, which, as in the previous case, can be arranged in contact with one or both surfaces of the SMC semi-finished product intended to come into contact with the front and rear shapes. The material used can have a carbon content comprised between 40 and 200 g/m2, preferably equal to about 100 g/m2.

    [0039] Figures 1 to 3 show for example a single layer 40 of a pre-impregnated fabric arranged on the surface of the SMC semi-finished product intended to come into contact with the surface 31 of the shape formed in the mold 20.

    [0040] It is also possible to provide the combined use of at least one layer of a fabric pre-impregnated unidirectional carbon fibers and at least one sheet of nonwoven carbon fabric, fiber glass or acrylic material, on one or both surfaces of the SMC semi-finished product intended to come into contact with the front and rear shapes. In this case, thanks to the improved aesthetic characteristics, the layers of nonwoven fabric are preferably arranged in contact with the surfaces 31, 32 of the shape and are therefore intended to constitute the outer surfaces of the article.

    [0041] The loading of the SMC semi-finished product 10 in the mold 20 is carried out at atmospheric pressure and requires a time comprised between 10 and 60 seconds. The mold 20, preheated to a temperature between 120 and 150° C, is then closed by starting a cycle of compression in an autoclave according to a predetermined time-pressure law.

    [0042] With reference to the diagram of Figure 4, the pressure is increased, for example according to a linear law, to a value comprised between 15 and 25 bar, preferably equal to about 18 bar, in a time equal to about 30 seconds. This pressure condition is maintained for a time comprised between about 10 and 20 seconds, for example 15 seconds, after which the pressure is rapidly increased to values between 70 and 90 bar, for example 80 bar. Also in this case the increase in pressure can follow a linear law.

    [0043] The article is then maintained in these conditions of pressure and temperature for about 300 seconds, after which the pressure is reduced to environmental values, the mold 20 is opened and the article 30 is extracted, being cooled on special shapes suitable for preventing deformation and finally subjected to the finishing workings such as, for example, the removal of the molding burrs.

    [0044] Always with the object of minimizing the displacements of the carbon fibers and, more generally, the flows of material inside the mold, in the manufacture of strongly asymmetric pieces with the same percentage of coverage it is possible to provide a shaping step of the SMC semi-finished product according to the plan shape of the article to be manufactured.


    Claims

    1. A heat compression molding process for the manufacturing of composite material articles, said process comprising the steps of:

    i) Providing a mold (20) in which the negative shape (31, 32) of an article (30) to be manufactured is formed;

    ii) Inserting into said mold (20) an SMC semi-finished product (10) comprising one or more sheets of composite material comprising a matrix of a heat-hardening resin and carbon fibers, the mold being pre-heated at a temperature suitable to allow the cure of said heat-hardening resin;

    iii) Closing the mold (20) and carrying out a compression cycle in an autoclave according to a predefined time-pressure law; and

    iv) Extracting the article (30),

    wherein the amount of SMC semi-finished product (10) inserted in the mold (20) is calculated by weighing on the basis of the volume of the article (30) to be manufactured, and wherein the size of the surfaces of the SMC semi-finished product (10) intended to contact the surfaces of the shape (31, 32) are calculated so as to cover said surfaces in a percentage higher than 80% and less than or equal to 99% of the whole development of the surfaces of the shape (31, 32).
     
    2. A molding process according to claim 1, characterized in that the heat-hardening resin forming the SMC semi-finished product is preferably chosen in the group comprising vinyl-ester, phenolic, epoxy, polyester, polyamide, cyano-ester resins or combinations thereof.
     
    3. A molding process according to claim 1 or 2, characterized in that the carbon used is in the form of filaments having a length comprised between 5 and 200 mm, each filament being made of a number of carbon fibers comprised between 3000 and 24000.
     
    4. A molding process according to any one of claims 1 to 3, characterized in that the amount of carbon fibers varies from 25% to 75% by weight of the heat-hardening resin.
     
    5. A molding process according to any one of claims 1 to 4, characterized by further comprising a step of adding one or more layers (40) of a pre-impregnated fabric with unidirectional carbon fibers and/or one or more sheets of a carbon nonwoven fabric, said layers and/or sheets being arranged in contact with one or both surfaces of the SMC semi-finished product (10) intended to contact the surfaces (31, 32) of the shape formed in the mold (20).
     
    6. A molding process according to claim 5, characterized in that said pre-impregnated fabric comprises a heat-hardening resin matrix in which a plurality of carbon fibers arranged parallel to each other are immersed.
     
    7. A molding process according to claim 6, characterized in that the pre-impregnated fabric has a carbon content comprised between 20 and 140 g/m2.
     
    8. A molding process according to any one of claims 5 to 7, characterized in that said nonwoven fabric has a carbon content comprised between 40 and 200 g/m2.
     
    9. A molding process according to any one of claims 5 to 8, characterized by further comprising a step of cutting said one or more layers of pre-impregnated fabric with unidirectional carbon fibers.
     
    10. A molding process according to claim 9, characterized in that said cuts are inclined with respect to the direction of the carbon fibers by an angle comprised between 30° and 60° and in that subsequent cuts along the direction of the carbon fibers are partially misaligned and arranged so as to share a maximum of 50% of the fibers.
     
    11. A molding process according to claim 9 or 10, characterized in that the cuts have a length comprised between 1 and 20 mm and their relative distance is comprised between 5 and 100 mm.
     


    Ansprüche

    1. Wärmeformpressverfahren zur Herstellung von Artikeln aus Verbundmaterial, wobei das Verfahren die Schritte umfasst:

    i) Bereitstellen eines Werkzeugs (20), in dem die Negativform (31, 32) eines herzustellenden Artikels (30) gebildet wird;

    ii) Einfügen eines SMC-Halbzeugs (10) in das Werkzeug (20) umfassend eine oder mehrere Platten aus Verbundmaterial, umfassend eine Matrix aus einem wärmehärtenden Harz und Kohlefasern, wobei das Werkzeug bei einer geeigneten Temperatur vorgewärmt wird, um das Aushärten des wärmehärtenden Harzes zu ermöglichen;

    iii) Schließen des Werkzeugs (20) und Ausführen eines Kompressionszyklus in einem Autoklaven nach einem vordefinierten Zeitdruckgesetz; und

    iv) Extrahieren des Artikels (30),

    wobei die Menge des in das Werkzeug (20) eingesetzten SMC-Halbzeugs (10) durch Wiegen auf der Grundlage des Volumens des herzustellenden Artikels (30) berechnet wird und wobei
    die Größe der Oberflächen des SMC-Halbzeugs (10), die dazu bestimmt sind, die Oberflächen der Form (31, 32) zu berühren, so berechnet wird, dass sie die Oberflächen in einem Prozentsatz höher als 80% und weniger als oder gleich wie 99% der Gesamtentwicklung der Oberflächen der Form (31, 32) bedecken.
     
    2. Formungsverfahren nach Anspruch 1, dadurch gekennzeichnet, dass das wärmehärtende Harz, das das SMC-Halbzeug bildet, vorzugsweise aus der Gruppe umfassend Vinylester-, Phenol-, Epoxy-, Polyester-, Polyamid-, Cyanester-Harze oder Kombinationen davon ausgewählt wird.
     
    3. Formungsverfahren nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass der verwendete Kohlenstoff in Form von Filamenten aufweisend eine Länge zwischen 5 und 200 mm ist, wobei jedes Filament aus einer Anzahl an Kohlenstofffasern besteht, die zwischen 3000 und 24000 liegen.
     
    4. Formungsverfahren nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, dass die Menge an Kohlenstofffasern von 25 bis 75 Gew .-% des wärmehärtenden Harzes variiert.
     
    5. Formungsverfahren nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass es ferner einen Schritt zum Zugeben einer oder mehrerer Schichten (40) eines vorimprägnierten Gewebes mit unidirektionalen Kohlenstofffasern und/oder einer oder mehreren Platten eines Kohlenstoff-Vliesstoffs umfasst, wobei die Schichten und/oder Platten in Kontakt mit einer oder beiden Oberflächen des SMC-Halbzeugs (10) angeordnet sind, die dazu bestimmt sind, die Oberflächen (31, 32) der im Werkzeug (20) gebildeten Form zu berühren.
     
    6. Formungsverfahren nach Anspruch 5, dadurch gekennzeichnet, dass das vorimprägnierte Gewebe eine wärmehärtende Harzmatrix umfasst, in der eine Vielzahl an parallel zueinander angeordneten Kohlenstofffasern eingetaucht sind.
     
    7. Formungsverfahren nach Anspruch 6, dadurch gekennzeichnet, dass das vorimprägnierte Gewebe einen Kohlenstoffgehalt zwischen 20 und 140 g/m2 aufweist.
     
    8. Formungsverfahren nach einem der Ansprüche 5 bis 7, dadurch gekennzeichnet, dass der Vliesstoff einen Kohlenstoffgehalt zwischen 40 und 200 g/m2 aufweist.
     
    9. Formungsverfahren nach einem der Ansprüche 5 bis 8, dadurch gekennzeichnet, dass es ferner einen Schritt zum Schneiden der einen oder mehrerer Schichten eines vorimprägnierten Gewebes mit unidirektionalen Kohlenstofffasern umfasst.
     
    10. Formungsverfahren nach Anspruch 9, dadurch gekennzeichnet, dass die Schnitte in Bezug auf die Richtung der Kohlenstofffasern um einen Winkel zwischen 30° und 60° geneigt sind und dass nachfolgende Schnitte entlang der Richtung der Kohlenstofffasern teilweise versetzt und so angeordnet sind, dass maximal 50% der Fasern geteilt wird.
     
    11. Formungsverfahren nach Anspruch 9 oder 10, dadurch gekennzeichnet, dass die Schnitte eine Länge zwischen 1 und 20 mm aufweisen und deren relativer Abstand zwischen 5 und 100 mm liegt.
     


    Revendications

    1. Procédé de moulage par compression de chaleur pour la fabrication d'articles en matériau composite, ledit procédé comprenant les étapes de:

    i) Prévoir un moule (20) dans lequel est formée la forme négative (31, 32) d'un article (30) à fabriquer;

    ii) Introduire dans ledit moule (20) un produit semi-fini préimprégné en feuille (10) comprenant une ou plusieurs feuilles de matériau composite comprenant une matrice d'une résine thermodurcissable et de fibres de carbone, le moule étant préchauffé à une température adaptée pour permettre le séchage de ladite résine thermodurcissable;

    iii) Fermer le moule (20) et effectuer un cycle de compression dans un autoclave selon une loi de pression temporelle prédéfinie; et

    iv) Extraire l'article (30),

    dans lequel la quantité de produit semi-fini préimprégné en feuille (10) introduite dans le moule (20) est calculée par la pesée sur la base du volume de l'article (30) à fabriquer, et dans lequel
    la dimension des surfaces du produit semi-fini préimprégné en feuille (10) prévue pour se mettre en contact avec les surfaces de la forme (31, 32) est calculée de manière à couvrir lesdites surfaces dans un pourcentage supérieur à 80% et inférieur ou égal à 99% du développement global des surfaces de la forme (31, 32).
     
    2. Procédé de moulage selon la revendication 1, caractérisé en ce que la résine thermodurcissable formant le produit semi-fini préimprégné en feuille est de préférence choisie dans le groupe comprenant des résines d'ester vinylique, phénoliques, époxy, polyester, polyamide, cyano-ester ou leurs combinaisons.
     
    3. Procédé de moulage selon la revendication 1 ou 2, caractérisé en ce que le carbone utilisé se présente sous forme de filaments ayant une longueur comprise entre 5 et 200 mm, chaque filament étant constitué d'un nombre de fibres de carbone compris entre 3000 et 24000.
     
    4. Procédé de moulage selon l'une quelconque des revendications de 1 à 3, caractérisé en ce que la quantité de fibres de carbone varie de 25 à 75% en poids de la résine thermodurcissable.
     
    5. Procédé de moulage selon l'une quelconque des revendications de 1 à 4, caractérisé en ce qu'il comprend de plus une étape consistant à ajouter une ou plusieurs couches (40) d'un tissu préimprégné à fibres de carbone unidirectionnelle et/ou une ou plusieurs feuilles d'un tissu non tissé en carbone, lesdites couches et/ou feuilles étant disposées en contact avec une ou deux surfaces du produit semi-fini préimprégné en feuille (10) prévu pour se mettre en contact avec les surfaces (31, 32) de la forme formée dans le moule (20).
     
    6. Procédé de moulage selon la revendication 5, caractérisé en ce que ledit tissu préimprégné comprend une matrice de résine thermodurcissable dans laquelle une pluralité de fibres de carbone, disposées parallèlement les unes aux autres, sont immergées.
     
    7. Procédé de moulage selon la revendication 6, caractérisé en ce que le tissu préimprégné a une teneur en carbone comprise entre 20 et 140 g/m2.
     
    8. Procédé de moulage selon l'une quelconque des revendications de 5 à 7, caractérisé en ce que ledit tissu non tissé a une teneur en carbone comprise entre 40 et 200 g/m2.
     
    9. Procédé de moulage selon l'une quelconque des revendications de 5 à 8, caractérisé en ce qu'il comprend de plus une étape consistant à inciser lesdites une ou plusieurs couches de tissu préimprégné avec des fibres de carbone unidirectionnelles.
     
    10. Procédé de moulage selon la revendication 9, caractérisé en ce que lesdites incisions sont inclinées par rapport à la direction des fibres de carbone selon un angle compris entre 30 et 60° et en ce que des incisions subséquentes le long de la direction des fibres de carbone sont partiellement décalées et disposées de sorte à partager un maximum de 50 % des fibres.
     
    11. Procédé de moulage selon la revendication 9 ou 10, caractérisé en ce que les incisions ont une longueur comprise entre 1 et 20 mm et leur distance relative est comprise entre 5 et 100 mm.
     




    Drawing











    Cited references

    REFERENCES CITED IN THE DESCRIPTION



    This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

    Patent documents cited in the description