(19)
(11)EP 2 852 568 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
17.08.2016 Bulletin 2016/33

(21)Application number: 13734202.8

(22)Date of filing:  22.05.2013
(51)International Patent Classification (IPC): 
C07C 68/04(2006.01)
B01J 27/16(2006.01)
C07C 69/96(2006.01)
(86)International application number:
PCT/IN2013/000331
(87)International publication number:
WO 2013/175510 (28.11.2013 Gazette  2013/48)

(54)

PROCESS FOR MAKING DIMETHYL CARBONATE

VERFAHREN ZUR HERSTELLUNG VON DIMETHYLCARBONAT

PROCÉDÉ POUR LA FABRICATION DE CARBONATE DE DIMÉTHYLE


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 22.05.2012 IN DE15592012

(43)Date of publication of application:
01.04.2015 Bulletin 2015/14

(73)Proprietor: Council of Scientific & Industrial Research
New Delhi 110 001 (IN)

(72)Inventors:
  • SRINIVAS, Darbha
    Pune 411008 Maharashtra (IN)
  • PULIKKEEL, Unnikrishnan
    Pune 411008 Maharashtra (IN)

(74)Representative: Nuss, Laurent et al
Cabinet Nuss 10, rue Jacques Kablé
67080 Strasbourg Cedex
67080 Strasbourg Cedex (FR)


(56)References cited: : 
  
  • K. TOMISHIGE ET AL.: "Promoting effect of phosphoric acid on zirconia catalysts in selective synthesis of dimethyl carbonate from methanoland carbon dioxide", CATALYSIS LETTERS, vol. 66, 2000, pages 59-62, XP002704871, ISSN: 1011-372X cited in the application
  • WANG J D ET AL: "Preparation of layered zirconium phosphonate/phosphate, zirconium phosphonate/phosphite and related compounds", MATERIALS CHEMISTRY AND PHYSICS, ELSEVIER SA, SWITZERLAND, TAIWAN, REPUBLIC OF CHINA, vol. 35, no. 3-4, 1 October 1993 (1993-10-01), pages 208-216, XP024148243, ISSN: 0254-0584, DOI: 10.1016/0254-0584(93)90133-7 [retrieved on 1993-10-01] cited in the application
  • ABRAHAM CLEARFIELD ET AL: "Synthesis and Stability of Mixed Ligand Zirconium Phosphonate Layered Compounds", JOURNAL OF SOLID STATE CHEMISTRY, vol. 117, no. 2, 1 July 1995 (1995-07-01), pages 275-289, XP055071916, ISSN: 0022-4596, DOI: 10.1006/jssc.1995.1274 cited in the application
  
Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


Description

FIELD OF THE INVENTION



[0001] The present invention relates to a process for making dimethyl carbonate in presence of a solid catalyst.

[0002] Particularly, the present invention relates to an improved, eco-friendly process for producing dimethyl carbonate comprising contacting methanol with carbon dioxide in presence of a solid calcined catalyst derived from zirconium phosphonate having molecular formula:

        Zr(X)2-nYn.mH2O

wherein X refers to phosphonate and Y refers to HPO42- or HPO32-. The value of n varies from 0.2 to 1.8 and the value of m varies from 0 to 5.

BACKGROUND OF THE INVENTION



[0003] Dimethyl carbonate, (CH3O)2CO, finds large industrial applications. It replaces toxic phosgene in the manufacture of polyurethanes and polycarbonates. It finds application as a "green" solvent and as an eco-friendly reagent in methylation, esterification, carbomethoxylation and carbonylation reactions. Dimethyl carbonate is also a potential oxygenate fuel additive replacement to MTBE. Three commercial methods of dimethyl carbonate production are known. Phosgenation of methanol is the route formerly used. Oxidative carbonylation of methanol in liquid or vapor phase using CuCl (US patent 5,536,864), nitric oxide (UBE) or copper supported on active carbon (US patents 5,183,920 and 5,543,548) catalysts is the second route. The third commercial method (also using CO + O2) developed by UBE industry employs a Pd2+ catalyst and an alkyl nitrite promoter. All these methods produce dimethyl carbonate in high yields but the chemicals used and vent discharges in the processes are toxic or corrosive.

[0004] Transesterification of cyclic carbonates with methanol is currently practiced at Asahi Corporation Ltd (US patent 5,847,189A and 6,479,689B1). Dimethyl carbonate is produced in good yields. This reaction with small exotherm is carried out in the liquid phase without any toxic or corrosive chemicals. But alkelene diol in equimolar amounts is cogenerated. The one-pot reaction of epoxide, carbon dioxide and methanol produces dimethyl carbonate in moderate yields (US patents 7,145,028; 6,607,279B1; 4,434,105 and 6,407279 B1). Even in this reaction alkelene diol is cogenerated. Reaction of methanol with urea in presence of catalyst leads to dimethyl carbonate. Ammonia is produced as co-product which can be recycled back into urea production (US patents 7,314,947 and 7,074,951). However, the reaction of dimethyl carbonate and ammonia leads to undesired carbamate and isocyanate products. All these processes of dimethyl carbonate synthesis are not atom-efficient. The co-products and their separation affect the economics of the process.

[0005] Direct synthesis of dimethyl carbonate by the reaction of methanol with carbon dioxide is the simplest and desirable route. Water is produced as a by-product in this reaction. This reaction is more atom-efficient than the above-said routes. However, yield of dimethyl carbonate is low in this reaction due to thermodynamic limitations. Development of more efficient catalysts that could activate simultaneously carbon dioxide and methanol and overcome the limitations is desirable. Moreover, utilizing carbon dioxide, a greenhouse emission gas, as a raw material in the production of a green chemical would possibly make some positive impact on reducing global warming and carbon dioxide levels in the atmosphere.

[0006] US patent 7,605,285 B2 provides a method and apparatus for simultaneous production of methanol and dimethyl carbonate. Methanol is synthesized by allowing the synthesis gas to react over a catalyst, and dimethyl carbonate is produced by adding carbon dioxide to the methanol, characterized in that carbon dioxide in combustion exhaust gas discharged from a combustion radiator section for heating a reaction tube of the reformer is recovered. Dimethyl carbonate yields are limited by thermodynamic limitations.

[0007] US patent 2011/0196167 A1 discloses a method for producing dimethyl carbonate, the method comprises providing effective amounts of methanol and carbon dioxide to a reaction vessel, reacting methanol and carbon dioxide in the presence of a heterogeneous catalyst in the reaction vessel to produce dimethyl carbonate wherein the heterogeneous catalyst provides both acidic sites and basic sites. The catalyst is selected from the group consisting of Rh/Al2O3, Pd/Al2O3, Pt/Al2O3, Ni/Al2O3, Rh/SiO2, Rh/ZSM-5, Rh-K/Al2O3, Ni/SiO2-Al2O3, Mo2C/Al2O3, Pd/V2O5, Pd/TiO2, Pd/V2O5-TiO2, Pd/TiO2-ZrO2, Pt/Al2O3, Re/Al2O3, MoO3/Al2O3, MoO3/ZSM-5, MoO3/SiO2 and combinations thereof. The reaction is performed at ambient temperature and at a temperature from about 80°C to about 280°C. At 80°C, dimethyl carbonate is the selective product but at higher temperature, formation of significant amount of undesired dimethyl ether was detected.

[0008] References may be made to the following literature. Fang and Fujimoto (Appl. Catal. A: Gen. Vol. 142, Year 1996, Page L1) synthesized dimethyl carbonate from methanol and carbon dioxide using methyl iodide and K2CO3 as promoters. Although this reaction was fast, its deactivation was very rapid. Zirconia-based materials with both acidic and basic properties have been used as heterogenous catalysts for this reaction (Tomishige et al., J. Catal. Vol. 192, Year 2000, page 355; Ikeda et al., J. Phys. Chem. B Vol. 105, Year 2001, page 10653; Jiang et al., Appl. Catal. A: Gen., Vol. 256, Year 2003, page 203). The yield of DMC formed was low over these catalysts.

[0009] Article titled," A novel method of direct synthesis of dimethyl carbonate from methanol and carbon dioxide catalyzed by zirconia" by Keiichi Tomishige, Tomohiro Sakaihori, Yoshiki Ikeda, Kaoru Fujimoto in Catalysis Letters, Year1999, Volume 58, Issue 4, pp 225-229 reports the synthesis of Dimethyl carbonate from methanol and CO2 with high selectivity using ZrO2 catalysts. In this reaction, the amount of dimethyl ether and CO was below the detection limit. Further it reports, the catalytic activity seems to be related to acid-base pair sites of the ZrO2 surface from the results of temperature -programmed desorption of NH3 and CO2. It also reports the selectivity of DMC formation on Zirconia catalyst as 100% under all the reaction conditions studied.

[0010] Article titled," Promoting effect of phosphoric acid on zirconia catalysts in selective synthesis of dimethyl carbonate from methanol and carbon dioxide" by Yoshiki Ikeda, Tomohiro Sakaihori, Keiichi Tomishige and Kaoru Fujimoto in Catalysis Letters 66 (2000) 59-62 reports the addition of phosphoric acid to zirconia catalysts promoted the activity for dimethyl carbonate synthesis from methanol and carbon dioxide with high selectivity, and the reactions proceeded at much lower temperature on H3PO4/ZrO2 than on zirconia catalysts. It also suggests that the surface acidity enhancement by phosphoric acid contributed to higher activity. The selectivity of DMC formation on H3PO4/ZrO2 is estimated 100%. The catalyst was optimized by employing calcinations temperature of 600 °C and P/Zr ratio of 0.05. However, even with this optimized catalyst the maximum yield of dimethyl carbonate produced at CH3OH : CO2 (milli molar ratio) = 192 : 200, catalyst weight = 0.5 g, reaction temperature = 170 °C and reaction time = 2 h was 0.85 mmol/g catalyst (0.0765 g. DMC/g. catalyst) only which is significantly low for possible commercialization.

[0011] In view of the importance of dimethyl carbonate in industrial applications and drawbacks of prior-art processes which include low yield of dimethyl carbonate, formation of undesired dimethyl ether and catalyst deactivation, it is desirable to have a more efficient solid catalyst and a process using the catalyst. The process of the present invention using zirconium phosphonate phosphite or zirconium phosphonate phosphate compound is highly efficient and overcomes the deficiencies of prior-art processes.

OBJECTIVES OF THE INVENTION



[0012] The prime object of present invention is to provide an efficient, eco-friendly process for making dimethyl carbonate in presence of a water-tolerant solid acid catalyst.

[0013] Another object of present invention is to provide a catalytic process for producing dimethyl carbonate wherein dimethyl carbonate is formed with 100% selectivity and catalyst is stable, reusable, active and selective over a broader range of temperatures and pressures.

[0014] Yet another object of the present invention is to provide a process wherein the solid catalyst is selectively gives dimethyl carbonate and no dimethyl ether.

SUMMARY OF THE INVENTION



[0015] Accordingly, present invention provides a process for making dimethyl carbonate in high yields and with 100 wt% selectivity wherein the said process comprises the steps of:
  1. (a) providing reusable, water-tolerant, solid, calcined catalyst derived from zirconium phosphonate having molecular formula:

            Zr(X)2-nYn.mH2O

    Wherein, X refers to phosphonate, Y refers to HPO42- or HPO32-, n varies from 0.2 to 1.8 and m varies from 0 to 5, prepared by the known method;
  2. (b) contacting methanol with carbon dioxide in the presence of catalyst as provided in step (a) wherein the amount of catalyst ranges from 0.5 to 5 % by weight of methanol, pressure of carbon dioxide ranges from 1 to 60 bar and molar ratio of methanol and carbon dioxide varies from 0.25:1 to 10:1;
  3. (c) subjecting the reaction mixture as obtained in step (b) to a temperature in the range of 80 to 200 °C and for a period in the range of 3 to 12 hrs followed by lowering the temperature, venting out or recycling unreacted carbon dioxide and separating product dimethyl carbonate from the left out methanol, by-product water and catalyst by known procedures.


[0016] In an embodiment of the present invention, the reaction is carried out optionally in the presence of solvent or water trapping agent or both.
In another embodiment of the present invention, solvent used is selected from the group consisting of N,N-dimethyl formamide, tetrahydrofuran and dimethylsulphoxide.

[0017] The process according to claim 1, wherein water trapping agent used is selected from the group consisting of molecular sieves, 2,2-dimethoxy propane and like material.

[0018] In yet another embodiment of the present invention, said solid catalyst is hydrophobic with water adsorption capacity of 0.1 - 5 wt%.

[0019] In yet another embodiment of the present invention, said solid catalyst is stable and reusable and contains both acidic and basic sites.

[0020] In yet another embodiment of the present invention, said solid catalyst has the overall acid site density in the range of 0.05 to 0.35 mmol/sq. meter, basicity in the range of 0.05 to 0.5 mmol/g.catalyst and surface area in the range of 20 - 200 m2/g.

[0021] In yet another embodiment of the present invention, carbon dioxide used in the reaction is 100% pure or a mixture of carbon dioxide and other gases wherein the other gases are carbon monoxide, hydrogen, hydrocarbons and water.

[0022] In yet another embodiment of the present invention, the composition of calcined solid catalyst comprises of zirconium pyrophosphate phase.

[0023] In yet another embodiment of the present invention, the yield of dimethyl carbonate is as high as or above 2.29 g/g. catalyst.

[0024] In still another embodiment of the present invention, the present invention provides a unique feature of the present invention wherein methanol is activated at both acidic and basic sites generating CH3+ and CH3O- intermediate ions. Carbon dioxide is activated at the basic sites. Simultaneous presence both the acidic and basic sites and hydrophobicity of the catalyst are responsible for its efficient catalytic activity and reusability.

[0025] In yet another embodiment of the present invention, the reaction can be conducted in a batch, or continuous fixed-bed reaction mode.

[0026] In still yet another embodiment of the present invention, when the process is conducted in a continuous fixed-bed mode the catalyst is shaped into pellets or extrudates and used.

[0027] In yet another embodiment of the present invention, the selectivity of dimethyl carbonate is 100% by weight.

[0028] In still another embodiment, the present invention doesn't lead to production of dimethyl ether.

[0029] In yet another embodiment of the present invention, Zr in the catalyst composition can be replaced with other metal or metalloic ion preferably taken from the group consisting of Zr, Zn, Cd, Al, Sn, La and Ce.

[0030] In still yet another embodiment of the present invention, the catalyst of the present invention is characterized by powder X-ray diffraction pattern as shown in Figure 1, infrared spectroscopic finger prints as shown in Figure 2, 31P magic angle spin nuclear magnetic resonance spectrum (31P MAS N MR) as shown in Figure 3, the overall acid site density in the range 0.05 to 0.35 mmol/sq. meter, basicity in the range 0.05 to 0.5 mmol/g.catalyst and surface area in the range 20 - 200 m2/g. In still another embodiment of the present invention, the process of present invention wherein the catalyst is a solid and the reaction takes place in a heterogeneous condition. The solid catalyst can be easily separated from products by centrifugation-filtration/decantation for further reuse. Also, the catalyst of present invention is stable in aqueous medium.

BRIEF DESCRIPTION OF THE DRAWINGS



[0031] 

Figure 1: X-ray diffraction pattern of the catalyst (Example 1).

Figure 2: FTIR spectrum of the catalyst.

Figure 3: 31P Magic angle spin nuclear magnetic resonance spectrum of catalyst.

Figure 4: Gas chromatograph of the product mixture (Example 10)


DETAILED DESCRIPTION OF THE INVENTION



[0032] The present invention discloses a process for making dimethyl carbonate in presence of a solid catalyst. The present invention discloses to an improved, eco-friendly process for producing dimethyl carbonate comprising contacting methanol with carbon dioxide in presence of a solid calcined catalyst derived from zirconium phosphonate having molecular formula:

        Zr(X)2-nYn.mH2O

where X refers to phosphonate and Y refers to HPO42- or HPO32-. The value of n varies from 0.2 to 1.8 and the value of m varies from 0 to 5.

[0033] In the investigations leading to the present invention, the solid, calcined zirconium phosphonate catalyst of present invention is highly efficient, high dimethyl carbonate yielding and could be easily separated from the products for further use. The prior-art catalysts are expensive due to presence of noble metals or less stable in water by-product medium. A highly stable and easily separable catalyst, for example, the catalyst of the present invention is advantageous.

[0034] The catalyst of the present invention is efficient in terms of the yield of dimethyl carbonate; 100% selectivity of dimethyl carbonate is obtained at a broader temperature and pressure range.

[0035] Present invention provides an improved process for making dimethyl carbonate in high yields with 100% selectivity wherein the said process comprises the steps of:
  1. (a) contacting methanol with carbon dioxide in the presence of a reusable, water-tolerant, solid, calcined catalyst derived from zirconium phosphonate having molecular formula:

            Zr(X)2-nYn.mH2O

    where X refers to phosphonate and Y refers to HPO42- or HPO32-. The value of n varies from 0.2 to 1.8 and the value of m varies from 0 to 5, wherein the amount of catalyst ranges from 0.5 to 5 % by weight of methanol, pressure of carbon dioxide ranges from 1 to 60 bar and the molar ration of methanol to carbon dioxide ranges from 0.25:1 to 10:1;
  2. (b) subjecting the reaction mixture obtained in step (a) to a temperature in the range of 80 to 200 °C and for a reaction time of 3 to 12 hrs to obtain dimethyl carbonate, and,
  3. (c) lowering the temperature, venting out or recycling unreacted carbon dioxide and separating product dimethyl carbonate from the left out methanol, by-product water and catalyst by known procedures.


[0036] The process of present invention is eco-friendly, and generates little waste products unlike in the prior art processes where dimethyl ether formed in large quantities.

[0037] The zirconium phosphonate catalysts are prepared by the known procedure as described in the references: A. Clearfield et al., J. Sold. State Chem. Vol. 117, Year 1995, pp. 275; J. Don Wang et al., Mater. Chem. Phys. Vol. 35, Year 1993, pp. 208; K. Nakamura et al., J. Incl. Phenom. Mol. Recog. Chem. Vol. 31, Year 1998, pp. 351.

EXAMPLES



[0038] Following examples are given by way of illustration therefore should not be construed to limit the scope of the invention.

EXAMPLE 1



[0039] This example illustrates the preparation of zirconium phenyl phosphonate phosphite catalyst of molecular composition: Zr(C6H5PO3)0.29(HPO3)1.71.0.02H2O. In a typical synthesis, solution A was prepared by dissolving 4 g of zirconyl oxychloride (ZrOCl2.8H2O) in 40 ml of water and 9 ml of conc. HF taken in a polyethylene beaker. Solution B was prepared by dissolving 1.06 g of phenyl phosphonic acid and 26.8 g of phosphorous acid in 100 ml of water. Solution A was added to the solution B. Beaker containing solution A was rinsed with 14 ml of water and the contents were added to the reaction mixture. The reaction mixture was heated at 70 °C for 34 hrs till it got dried. The material was washed with 2 liters of water and dried at 90 °C for 16 h. The catalyst was calcined at 550 °C for 2 h. Acid site density = 0.246 mmol/sq. meter, basicity = 0.32 mmol/g, specific surface area = 26 m2/g and water adsorption capacity = 0.2 wt%.

EXAMPLE 2



[0040] This example illustrates the preparation of zirconium phenyl phosphonate phosphite catalyst of molecular composition: Zr(C6H5PO3)0.99(HPO3)1.01.0.4H2O. In a typical synthesis, 1 g of phenyl phosphonic acid and 1.04 g of phosphorous acid were dissolved in 20 ml of water. To this, 2.04 g of zirconyl oxychloride dissolved in 5 ml of water was added. The mixture was then heated at 90 °C for 3 hrs and solid was recovered, washed with water and dried at 90 °C for 16 h. The catalyst was calcined at 550 °C for 2 h. Acid site density = 0.051 mmol/sq. meter, basicity = 0.15 mmol/g, specific surface area = 188 m2/g and water adsorption capacity = 0.8 wt%.

EXAMPLE 3



[0041] This example illustrates the preparation of zirconium phenyl phosphonate phosphite catalyst of molecular composition: Zr(C6H5PO3)0.97(HPO3)1.03.0.15H2O. In a typical synthesis, 1 g of phenyl phosphonic acid and 0.52 g of phosphorous acid were dissolved in 20 ml of water. To this, 2.04 g of zirconyl oxychloride (ZrOCl2.8H2O) dissolved in 5 ml of water was added. The mixture was then heated at 90 °C for 3 hrs and solid was recovered, washed with water and dried at 90 °C for 16 h. The catalyst was calcined at 550 °C for 2 h. Acid site density = 0.05 mmol/sq. meter, basicity = 0.17 mmol/g, specific surface area = 193 m2/g and water adsorption capacity = 2.1 wt%.

EXAMPLE 4



[0042] This example illustrates the preparation of zirconium phenyl phosphonate phosphate catalyst of molecular composition: Zr(C6H5PO3)0.8(HPO4)1.2.0.5H2O. In a typical synthesis, solution A was prepared by dissolving 5.43 g of zirconyl oxychloride in 30 ml of distilled water taken in a polyethylene beaker. To it 12.4 ml of 48% HF was added. Solution B was prepared by disallowing 2.16 g of phenyl phosphonic acid in 45 ml of water. To it 84.6 ml of conc. phosphoric acid was added. Solution A was added slowly at 25 °C to solution B over a period of 1 h. The empty beaker containing solution A was rinsed with 28 ml of water and the contents were added to the above reaction mixture. The combined volume of the reaction mixture was nearly 200 ml. The mixture was heated in oil bath at 70 °C for 2 days till all the solvent got evaporated and solid was formed. The solid was washed with 2 l of water, dried in an oven at 90 ° C for 16 h. The material was calcined at 550 °C for 2 h. Acid site density = 0.09 mmol/sq. meter, basicity = 0.20 mmol/g, specific surface area = 200 m2/g and water adsorption capacity = 0.7 wt%.

EXAMPLE 5



[0043] This example illustrates the preparation of dimethyl carbonate using the calcined catalyst described in Example 1. 5.2 g of methanol (164 mmol), 0.102 g of catalyst, 10 ml of N,N-dimethyl formamide (solvent) and 0.5 g of molecular sieves-3A were taken in a 100 ml stainless steel Parr autoclave. The reactor was pressurized with carbon dioxide (98 vol%; rest being CO, CH4, hydrogen and H2O) to 40 bar (164 mmol). Temperature of the reactor was raised to 170 °C and the reaction was conducted for 12 h. Later, unreacted gases were vented out. The catalyst was separated from the liquid product by filtration. The liquid product was analyzed by gas chromatography (Varian 3400). Nonane-1-ol was used an internal standard. Dimethyl carbonate yield = 2.29 g/g catalyst. Gas portion did not contain any detectable dimethyl ether or carbon monoxide compound. Mass balance > 95 wt%.

EXAMPLE 6



[0044] This example illustrates the preparation of dimethyl carbonate using the calcined catalyst described in Example 1. 5.2 g of methanol (164 mmol), 0.160 g of catalyst, 10 ml of N,N-dimethyl formamide (solvent) and 0.5 g of molecular sieves-3A were taken in a 100 ml stainless steel Parr autoclave. The reactor was pressurized with carbon dioxide (98 vol%; rest being CO, CH4, hydrogen and H2O) to 40 bar (164 mmol). Temperature of the reactor was raised to 170 °C and the reaction was conducted for 12 h. Later, unreacted gases were vented out. The catalyst was separated from the liquid product by filtration. The liquid product was analyzed by gas chromatography (Varian 3400). Nonane-1-ol was used an internal standard. Dimethyl carbonate yield = 1.62 g/g catalyst. Gas portion did not contain any detectable dimethyl ether or carbon monoxide compound. Mass balance > 95 wt%.

EXAMPLE 7



[0045] This example illustrates the preparation of dimethyl carbonate using the calcined catalyst described in Example 1 at CO2 pressure of 30 bar and methanol : CO2 molar ratio of 2:1. 8 g of methanol (250 mmol), 0.1602 g of catalyst, 10 ml of N,N-dimethyl formamide (solvent) and 0.5 g of molecular sieves-3A were taken in a 100 ml stainless steel Parr autoclave. The reactor was pressurized with carbon dioxide (98 vol%; rest being CO, CH4, hydrogen and H2O) to 30 bar (125 mmol). Temperature of the reactor was raised to 170 °C and the reaction was conducted for 12 h. Later, unreacted gases were vented out. The catalyst and molecular sieve were separated from the liquid product by filtration. The liquid product was analyzed by gas chromatography (Varian 3400). Nonane-1-ol was used an internal standard. Dimethyl carbonate yield = 1.12 g/g catalyst. Mass balance > 95 wt%.

EXAMPLE 8



[0046] This example illustrates the preparation of dimethyl carbonate using the calcined catalyst described in Example 1 at CO2 pressure of 30 bar, methanol : CO2 molar ratio of 4:1 and without employing a water trapping agent. 16.02 g of methanol (500 mmol), 0.1602 g of catalyst and 10 ml of N,N-dimethyl formamide (solvent) were taken in a 100 ml stainless steel Parr autoclave. The reactor was pressurized with carbon dioxide (98 vol%; rest being CO, CH4, hydrogen and H2O) to 30 bar. Temperature of the reactor was raised to 170 °C and the reaction was conducted for 12 h. Later, unreacted gases were vented out. The catalyst was separated from the liquid product by filtration. The liquid product was analyzed by gas chromatography (Varian 3400). Nonane-1-ol was used an internal standard. Dimethyl carbonate yield = 0.84 g/g catalyst. Mass balance > 95 wt%.

EXAMPLE 9



[0047] This example illustrates the preparation of dimethyl carbonate using the calcined catalyst described in Example 1 at CO2 pressure of 30 bar, methanol : CO2 molar ratio of 4:1 and without employing solvent and water trapping agent. 16.02 g of methanol (500 mmol), and 0.1602 g of catalyst were taken in a 100 ml stainless steel Parr autoclave. The reactor was pressurized with carbon dioxide (98 vol%; rest being CO, CH4, hydrogen and H2O) to 30 bar. Temperature of the reactor was raised to 170 °C and the reaction was conducted for 12 h. Later, unreacted gases were vented out. The catalyst was separated from the liquid product by filtration. The liquid product was analyzed by gas chromatography (Varian 3400). Nonane-1-ol was used an internal standard. Dimethyl carbonate yield = 0.72 g/g catalyst. Mass balance > 95 wt%.

EXAMPLE 10



[0048] This example illustrates the preparation of dimethyl carbonate using the calcined catalyst described in Example 1 at CO2 pressure of 30 bar, methanol : CO2 molar ratio of 4:1, without employing solvent but using a water trapping agent - molecular sieve. 16.02 g of methanol (500 mmol), 0.1602 g of catalyst and 0.5 g of molecular sieve-3A were taken in a 100 ml stainless steel Parr autoclave. The reactor was pressurized with carbon dioxide (98 vol%; rest being CO, CH4, hydrogen and H2O) to 30 bar. Temperature of the reactor was raised to 170 °C and the reaction was conducted for 12 h. Later, unreacted gases were vented out. The catalyst and molecular sieve were separated from the liquid product by filtration. The liquid product was analyzed by gas chromatography (Varian 3400). Nonane-1-ol was used an internal standard. Dimethyl carbonate yield = 0.91 g/g catalyst. Mass balance > 95 wt%.

EXAMPLE 11



[0049] This example illustrates the preparation of dimethyl carbonate using the calcined catalyst described in Example 1 at 20 bar CO2 pressure, 1 wt% of catalyst and without employing solvent and water trapping agent. 16.02 g of methanol (500 mmol) and 0.160 g of catalyst were taken in a 100 ml stainless steel Parr autoclave. The reactor was pressurized with carbon dioxide (98 vol%; rest being CO, CH4, hydrogen and H2O) to 20 bar (83 mmol). Temperature of the reactor was raised to 170 °C and the reaction was conducted for 8 h. Later, unreacted gases were vented out. The catalyst was separated from the liquid product by filtration. The liquid product was analyzed by gas chromatography (Varian 3400). Nonane-1-ol was used an internal standard. Dimethyl carbonate yield = 0.46 g/g catalyst. Mass balance = 99 wt%. Figure 4 shows the gas chromatograph of the product mixture.

EXAMPLE 12



[0050] This example illustrates the preparation of dimethyl carbonate using the calcined catalyst described in Example 2 at 20 bar CO2 pressure, 1 wt% of catalyst and without employing solvent and water trapping agent. 16.02 g of methanol (500 mmol) and 0.160 g of catalyst were taken in a 100 ml stainless steel Parr autoclave. The reactor was pressurized with carbon dioxide to 20 bar (83 mmol). Temperature of the reactor was raised to 170 °C and the reaction was conducted for 8 h. Later, unreacted gases were vented out. The catalyst was separated from the liquid product by filtration. The liquid product was analyzed by gas chromatography (Varian 3400). Nonane-1-ol was used an internal standard. Dimethyl carbonate yield = 0.045 g/g catalyst. Mass balance = 99 wt%.

EXAMPLE 13



[0051] This example illustrates the preparation of dimethyl carbonate using the calcined catalyst described in Example 3 at 20 bar CO2 pressure, 1 wt% of catalyst and without employing solvent and water trapping agent. 16.02 g of methanol (500 mmol) and 0.160 g of catalyst were taken in a 100 ml stainless steel Parr autoclave. The reactor was pressurized with carbon dioxide to 20 bar (83 mmol). Temperature of the reactor was raised to 170 °C and the reaction was conducted for 8 h. Later, unreacted gases were vented out. The catalyst was separated from the liquid product by filtration. The liquid product was analyzed by gas chromatography (Varian 3400). Nonane-1-ol was used an internal standard. Dimethyl carbonate yield = 0.05 g/g catalyst. Mass balance = 99 wt%. Figure 4 shows the gas chromatograph of the product mixture.

EXAMPLE 14



[0052] This example illustrates the preparation of dimethyl carbonate using the calcined catalyst described in Example 4 at 20 bar CO2 pressure, 1 wt% of catalyst and without employing solvent and water trapping agent. 16.02 g of methanol (500 mmol) and 0.160 g of catalyst were taken in a 100 ml stainless steel Parr autoclave. The reactor was pressurized with carbon dioxide to 20 bar (83 mmol). Temperature of the reactor was raised to 170 °C and the reaction was conducted for 8 h. Later, unreacted gases were vented out. The catalyst was separated from the liquid product by filtration. The liquid product was analyzed by gas chromatography (Varian 3400). Nonane-1-ol was used an internal standard. Dimethyl carbonate yield = 0.16 g/g catalyst. Mass balance = 99 wt%.

EXAMPLE 15



[0053] This example illustrates the reusability of the catalyst reported in example 1 in four recycling experiments. In this study 16.02 g of methanol (500 mmol), 0.1602 g of catalyst and 5 ml of N,N-dimethyl formamide (solvent) were taken in a 100 ml stainless steel Parr autoclave. The reactor was pressurized with carbon dioxide to 30 bar (125 mmol). Temperature of the reactor was raised to 170 °C and the reaction was conducted for 12 h. Later, unreacted gases were vented out. The catalyst was separated from the liquid product by filtration. The liquid product was analyzed by gas chromatography (Varian 3400). Nonane-1-ol was used an internal standard. The catalyst recovered after washing with acetone (5 ml) and drying at 250°C for 2 h was used in the recycling experiment conducted in the same manner as described above. Such recycling studies of the catalyst were done four times. Dimethyl carbonate yield = 0.805 g/g catalyst (Fresh or 0th recycle), 0.805 g/g catalyst (1st recycle), 0.803 g/g catalyst (2nd recycle), 0.804 g/g catalyst (3rd recycle) and 0.788 g/g catalyst (4th recycle).

EXAMPLE 16



[0054] This example compares the performance of calcined H3PO4/ZrO2 catalyst prepared as reported in the prior art by Yoshiki Ikeda, Tomohiro Sakaihori, Keiichi Tomishige and Kaoru Fujimoto (Catalysis Letters, Vol. 66, Year 2000, pp. 59-62) with that of the catalyst of present invention reported in Example 1. The comparative experiments were conducted under similar experimental conditions as reported in Example 6. 5.2 g of methanol (164 mmol), 0.160 g of calcined H3PO4/ZrO2 catalyst, 10 ml of N,N-dimethyl formamide (solvent) and 0.5 g of molecular sieves-3A were taken in a 100 ml stainless steel Parr autoclave. The reactor was pressurized with carbon dioxide (98 vol%; rest being CO, CH4, hydrogen and H2O) to 40 bar (164 mmol). Temperature of the reactor was raised to 170 °C and the reaction was conducted for 12 h. Later, unreacted gases were vented out. The catalyst was separated from the liquid product by filtration. The liquid product was analyzed by gas chromatography (Varian 3400). Nonane-1-ol was used an internal standard. DMC yield = 0.17 g/g catalyst. Gas portion did not contain any detectable dimethyl ether or carbon monoxide compound. Mass balance > 95 wt%. Under similar conditions the calcined catalyst of Example 1 provided Dimethyl carbonate yield of 1.62 g/g catalyst. Hence, the catalyst of present invention is nearly 10 times more active and efficient than the prior art catalyst.

ADVANTAGES OF THE INVENTION



[0055] Advantages of instant invention are as following:
1.
Heterogeneous, bi-functional, hydrophobic catalyst-based process
2.
Reusable catalyst process
3.
Eco-friendly process
4.
Dimethyl carbonate selectivity of 100% by weight.
5.
Reaction can be performed either in batch or continuous fixed-bed reaction mode.



Claims

1. A process for making dimethyl carbonate in yield greater than 40 wt% of catalyst and with 100 wt.% selectivity wherein the said process comprises the steps of:

(a) providing reusable, water-tolerant, solid, calcined catalyst comprising of zirconium pyrophosphate deprived from zirconium phosphonate having molecular formula:

        Zr(X)2-nYnmH2O

wherein, X is phenyl phosphonate, Y is HPO42- or HPO32-, n varies from 0.2 to 1.8 and m varies from 0 to 5

(b) contacting methanol with carbon dioxide in the presence of catalyst as provided in step (a) wherein the amount of catalyst ranges from 0.5 to 5 % by weight of methanol, pressure of carbon dioxide ranges from 1 to 60 bar und molar ratio of methanol and carbon dioxide varies from 0.25:1 to 10:1;

(c) subjecting the reaction mixture as obtained in step (b) to a temperature in the range of 80 to 200 °C and for a period in the range of 3 to 12 hrs followed by lowering the temperature, venting out or recycling unreacted carbon dioxide and separating product dimethyl carbonate from the left out methanol, by-product water and catalyst.


 
2. The process according to claim 1, wherein the reaction is carried out optionally in presence of solvent selected from the group of N,N-dimethyl formanide, tetrahydrofuran and dimethylsulphoxide.
 
3. The process according to claim 1, wherein the reaction is carried out optionally in the presence of water trapping agent selected from the group of molecular sieves, 2,2-dimethoxy propane and like material.
 
4. The process according to claim 1, wherein the reaction is carried out optionally either or in presence of both solvent and water trapping agent.
 
5. The process according to claim 1, wherein the solid catalyst is hydrophobic with water adsorption capacity in the range of 0.1 - 5 wt%.
 
6. The process according to claim 1, wherein the solid catalyst
is stable and reusable and contains both acidic and basic sites.
 
7. The process according to claim 6, wherein the overall acid site density of the solid catalyst is in the range of 0.05 to 0.35 mmol/sq. meter and basicity is in the range of 0.05 to 0.5 mmol/g catalyst
 
8. The process according to claim 1, wherein the surface area of the catalyst is in the range of 20 - 200 m2/g.
 
9. The process according to claim 1, wherein carbon dioxide used in the reaction is 100% pure or a mixture of carbon dioxide and other gases, wherein the other gases are carbon monoxide, hydrogen, hydrocarbons and water.
 
10. The process according to claim 1, wherein the yield of dimethyl carbonate is ≥ 2.29 g/g. catalyst or 229 wt% of catalyst.
 


Ansprüche

1. Verfahren zur Herstellung von Dimethylcarbonat mit einer höheren Ausbeute, als 40 Gewichtsprozent Katalysator und 100 Gewichtsprozent Selektivität, wobei das genannte Verfahren die folgenden Schritte umfasst:

(a) Bereitstellen eines wiederverwendbaren, wasserbeständigen, festen, kalzinierten Katalysators, umfassend Zirkoniumpyrophosphat, das aus Zirkoniumphosphonat gewonnen wurde und die Summenformel

        Zr(X)2-nYn·mH2O

wobei X für Phenylphosphonat steht, Y für HPO42- oder HPO32- steht, n zwischen 0,2 und 1,8 und m zwischen 0 und 5 liegt;

(b) Kontaktieren von Methanol mit Kohlendioxid in Anwesenheit des in Schritt (a) bereiteten Katalysators, wobei die Menge an Katalysator zwischen 0,5 und 5 Gewichtsprozent des Methanols beträgt, der Druck des Kohlendioxids zwischen 1 und 60 bar und das Molverhältnis von Methanol zu Kohlendioxid zwischen 0,25:1 und 10:1 liegt;

(c) Aussetzen des in Schritt (b) erhaltene Reaktionsgemischs einer Temperatur im Bereich von 80 bis 200°C für eine Dauer im Bereich von 3 bis 12 Stunden, gefolgt von Verringerung der Temperatur, Entgasen oder Rückführung des unverbrauchten Kohlendioxids und Trennung des Produkts Dimethylcarbonat von überschüssigem Methanol, als Nebenprodukt erzeugtem Wasser und Katalysator.


 
2. Verfahren nach Patentanspruch 1, bei dem die Reaktion optional in Anwesenheit eines aus der Gruppe N,N-Dimethylformamid, Tetrahydrofuran und Dimethylsulfoxid ausgewählten Lösungsmittels ausgeführt wird.
 
3. Verfahren nach Patentanspruch 1, bei dem die Reaktion optional in Anwesenheit eines aus der Gruppe Molekularsiebe, 2,2-Dimethoixypropan und Ähnlichem ausgewählten Wasser aufnehmenden Mittels ausgeführt wird.
 
4. Verfahren nach Patentanspruch 1, bei dem die Reaktion optional in Anwesenheit von entweder oder beiden, sowohl eines Lösungsmittels als auch eines Wasser aufnehmenden Mittels, ausgeführt wird.
 
5. Verfahren nach Patentanspruch 1, bei dem der feste Katalysator hydrophob ist mit einem Wasseradsorptionsvermögen im Bereich von 0,1 - 5 Gewichtsprozent.
 
6. Verfahren nach Patentanspruch 1, bei dem der feste Katalysator stabil und wiederverwendbar ist und sowohl saure, als auch basische aktive Stellen aufweist.
 
7. Verfahren nach Patentanspruch 6, bei dem die Gesamtdichte saurer aktiver Stellen des festen Katalysators im Bereich von 0,05 bis 0,35 mmol/m2 liegt und die Basisität im Bereich von 0,05 bis 0,5 mmol/(g Katalysator).
 
8. Verfahren nach Patentanspruch 1, bei dem die Oberfläche des Katalysators im Bereich von 20 - 200 m2/g liegt.
 
9. Verfahren nach Patentanspruch 1, bei dem das in der Reaktion verwendete Kohlendioxid 100% rein ist oder ein Gemisch aus Kohlendioxid und anderen Gasen, wobei die anderen Gase Kohlenmonoxid, Wasserstoff, Kohlenwasserstoffe und Wasser sind.
 
10. Verfahren nach Patentanspruch 1, bei dem die Ausbeute an Dimethylcarbonat ≥ 2,29 g/(g Katalysator) oder 229 Gewichtsprozent des Katalysators beträgt.
 


Revendications

1. Procédé de fabrication de carbonate de diméthyle avec un rendement supérieur à 40 % en poids de catalyseur et avec une sélectivité de 100 % en poids, ledit procédé comprenant les étapes de :

(a) fourniture d'un catalyseur réutilisable, tolérant à l'eau, solide, calciné constitué de pyrophosphate de zirconium dérivé de phosphonate de zirconium ayant la formule moléculaire :

        Zr(X)2-nYn.mH2O

dans laquelle, X est phénylphosphonate, Y est HPO42- ou HPO32-, n varie de 0,2 à 1,8 et m varie de 0 à 5,

(b) mise en contact de méthanol avec du dioxyde de carbone en présence d'un catalyseur tel que fourni dans l'étape (a) où la quantité de catalyseur est dans la plage de 0,5 à 5 % en poids de méthanol, la pression de dioxyde de carbone est dans la plage de 1 à 60 bar et le rapport molaire de méthanol et de dioxyde de carbone varie de 0,25:1 à 1,0:1 ;

(c) soumission du mélange de réaction tel qu'obtenu dans l'étape (b) à une température dans la plage de 80 à 200 °C et pendant une durée dans la plage de 3 à 12 h suivie par une diminution de la température, l'évacuation ou le recyclage du dioxyde de carbone n'ayant pas réagi et la séparation du produit de carbonate de diméthyle du méthanol résiduel, du sous-produit d'eau et du catalyseur.


 
2. Procédé selon la revendication 1, dans lequel la réaction est facultativement conduite en présence d'un solvant choisi dans le groupe du N,N-diméthylformamide, du tétrahydrofurane et du diméthylsulfoxyde.
 
3. Procédé selon la revendication 1, dans lequel la réaction est facultativement conduite en présence d'un agent de piégeage d'eau choisi dans le groupe de tamis moléculaires, du 2,2-diméthoxypropane et d'un matériau similaire.
 
4. Procédé selon la revendication 1, dans lequel la réaction est facultativement conduite en présence de solvant et/ou d'agent de piégeage d'eau.
 
5. Procédé selon la revendication 1, dans lequel le catalyseur solide est hydrophobe avec une capacité d'absorption d'eau dans la plage de 0,1 à 5 % en poids.
 
6. Procédé selon la revendication 1, dans lequel, le catalyseur solide est stable et réutilisable et contient à la fois des sites acides et basiques.
 
7. Procédé selon la revendication 6, dans lequel la densité totale de sites acides du catalyseur solide est dans la plage de 0,05 à 0,35 mmol/mètre carré et la basicité est dans la plage de 0,05 à 0,5 mmol/g de catalyseur.
 
8. Procédé selon la revendication 1, dans lequel la superficie du catalyseur est dans la plage de 20 à 200 m2/g.
 
9. Procédé selon la revendication 1, dans lequel le dioxyde de carbone utilisé dans la réaction est pur à 100 % ou un mélange de dioxyde de carbone et d'autres gaz, les autres gaz étant le monoxyde de carbone, l'hydrogène, des hydrocarbures et de l'eau.
 
10. Procédé selon la revendication 9, dans lequel le rendement de carbonate de diméthyle est ≥ 2,29 g/g de catalyseur ou 229 % en poids de catalyseur.
 




Drawing

















Cited references

REFERENCES CITED IN THE DESCRIPTION



This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

Patent documents cited in the description




Non-patent literature cited in the description