(19)
(11)EP 3 084 047 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
18.03.2020 Bulletin 2020/12

(21)Application number: 14827209.9

(22)Date of filing:  19.12.2014
(51)International Patent Classification (IPC): 
C25D 11/02(2006.01)
C25D 11/06(2006.01)
C25D 11/12(2006.01)
C25D 11/24(2006.01)
C25D 11/04(2006.01)
C25D 11/08(2006.01)
C25D 11/16(2006.01)
(86)International application number:
PCT/EP2014/078700
(87)International publication number:
WO 2015/091932 (25.06.2015 Gazette  2015/25)

(54)

METHOD FOR FORMING A MULTI-LAYER ANODIC COATING

VERFAHREN ZUR HERSTELLUNG EINER MEHRSCHICHTIGEN ANODISCHEN SCHICHT

PROCÉDÉ DE FORMATION D'UN REVÊTEMENT ANODIQUE MULTICOUCHE


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 20.12.2013 GB 201322745

(43)Date of publication of application:
26.10.2016 Bulletin 2016/43

(73)Proprietor: Technological University Dublin
Dublin D07 EWV4 (IE)

(72)Inventors:
  • DUFFY, Brendan
    Co. Kildare (IE)
  • WHELAN, Michael
    Co. Kildare (IE)

(74)Representative: Appleyard Lees IP LLP 
15 Clare Road
Halifax HX1 2HY
Halifax HX1 2HY (GB)


(56)References cited: : 
JP-A- 2006 328 467
US-A- 4 278 737
US-A- 4 687 551
US-A- 5 820 740
US-A- 3 962 049
US-A- 4 566 952
US-A- 5 486 283
  
  • WHELAN M ET AL: "Sol-gel sealing characteristics for corrosion resistance of anodised aluminium", SURFACE AND COATINGS TECHNOLOGY, vol. 235, 13 July 2013 (2013-07-13), pages 86-96, XP028749518, ISSN: 0257-8972, DOI: 10.1016/J.SURFCOAT.2013.07.018
  • A. Pakes ET AL: "Development of porous anodic films on 2014-T4 aluminium alloy in tetraborate electrolyte", CORROSION SCIENCE., vol. 45, no. 6, 1 June 2003 (2003-06-01), pages 1275-1287, XP055475344, GB ISSN: 0010-938X, DOI: 10.1016/S0010-938X(02)00216-0
  
Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


Description

Field



[0001] The present invention relates to a method for forming a multi-layer anodic coating, in particular, a duplex anodic layer, on an anodisable metal.

Background



[0002] Aluminium is used extensively for lightweight structures such as automotive and aerospace components where a combination of strength and corrosion resistance is essential. Aluminium owes its inherent corrosion resistance to a naturally occurring passive oxide which forms on the metal when exposed to the atmosphere. The thickness of the oxide layer is in the nanometre range which limits the performance of the metal against extreme mechanical and chemical attack. Electrochemical processes have been investigated with a view to producing coatings on such metals to enhance the strength and corrosion resistance of the metals.

[0003] Anodising is a well known electrochemical process for coating metals whereby a metal component, such as an aluminium work piece, for example, is submerged in a bath of an electrolytic solution. The work piece to be coated acts as a positive electrode and a direct current is applied. This results in an anodic coating comprising a porous layer of aluminium oxide being formed on the work piece. The thickness of the aluminium oxide is increased by the anodising process through an electrochemical reaction in acidic electrolytes such as sulphuric, phosphoric or oxalic acids. The process is commonly used to increase corrosion resistance and adhesion properties of the aluminium surface for a variety of applications.

[0004] The anodised aluminium oxide layer is nanoporous in structure with a self-assembled, hexagonal array of pores extending from the surface of the oxide to a thin barrier layer at the metal - metal oxide interface. The oxide growth and nanopore formation mechanism is a result of flow of anodic alumina in the barrier layer region due to the combination of growth stresses and field assisted plasticity. The stresses that drive the flow of material are due to electrostriction of the oxide layer which is plasticised under the electric field. The flow of material proceeds from the barrier layer into the pore walls forming Al2O3 columns in a self-assembled structure.

[0005] The anodic coating forms part of the metal but it has a porous structure which enables further treatments to be applied. For example, top coats and lacquers may be incorporated in the coating. Following the anodising process, the pores of the anodic layer need to be closed. If the pores are not sealed, the surface could have poor corrosion resistance.

[0006] For anti-corrosion applications, sulphuric acid anodising (SAA) is most commonly employed. A known significant advantage of SAA anodic layers is, for example, the ability of the pores of the anodic layer to close by surface hydration resulting in improved barrier properties thereby providing corrosion resistance. Hydration on the SAA surface proceeds rapidly after anodising and can be accelerated by hydrothermal treatment to achieve increased corrosion protection while also entrapping any applied inhibitors or dyes. Both natural and hydrothermally induced hydration results in pore blocking near the surface of the anodised layer. Hydration continues naturally over time as the pore closing effects move down the pore channel towards the metal surface. This continued hydration, termed "auto-sealing", results in an increase in the barrier properties of the anodic layers even during exposure to aggressive environments. Such a feature is responsible for the excellent long term and accelerated corrosion resistance of sulphuric acid anodised layers on copper- free wrought alloys.

[0007] However, in the case of copper-containing alloys, the protective properties provided by anodic layers formed by sulphuric acid anodising is reduced by the inclusion of copper ions within the oxide network. The presence of copper, as well as the random orientation of the pores, leads to difficulties with hydration sealing. To improve the corrosion protection on copper containing alloys, anodising processes have been developed including boric-sulphuric (BSAA) and tartaric-sulphuric (TSAA) acid anodising for corrosion and adhesive bonding applications.

[0008] Chromate based anodising processes and sealing processes are generally regarded as the target performance benchmarks for any developed anodising technology. However, due to the carcinogenic nature of these materials, the use of chromate based processes are currently restricted or being eliminated from anodising industries.

[0009] Anodising procedures currently used in the art include the use of mixed tartaric sulphuric acid (TSA) which has been shown to produce corrosion resistance and fatigue resistance equivalent to chromic acid anodising. However, on the other hand, due to surface hydration and small pore size of the resulting oxide layer, the adhesion of top coats and lacquers has been found to be inferior to that achieved using chromic acid anodising.

[0010] The conventional phosphoric acid anodising process is well known as having excellent adhesion properties, comparable to chromic acid anodising. However, this treatment imparts extremely poor corrosion resistance to the metal.
In order to achieve a balance of adhesion and corrosion resistance, duplex anodic layers have been investigated.

[0011] International Publication No. WO 2006/072804 relates to a method for the formation of anodic oxide films on aluminium or aluminium alloys. The anodic oxide coating disclosed in WO 2006/072804 is suitable for adhesive bonding of aluminium alloy structures. A duplex anodising procedure is described which involves the use of a mixed sulphuric phosphoric acid anodising step followed by a sulphuric acid treatment. The mixed bath is used to achieve a balance between hydration resistance and anodising voltage. However, in the process disclosed, the voltage used for the first anodising step is limited due to the mixture of acids used. In particular, when anodising in the presence of sulphuric acid, a lower voltage must be used compared to that used when anodising in the presence of phosphoric acid. The voltage used in the anodising step described in WO 2006/072804 is limited due to the mixture of sulphuric acid and phosphoric acid. The process disclosed in WO 2006/072804 also suffers from the disadvantage that the duplex anodic layer formed is not optimised for adhesion as the pore size is relatively small. In order to prevent pore closure due to hydration and accordingly to retain the adhesion properties of the surface, a system comprising pores having a large diameter is required.

[0012] A technology similar to that disclosed in WO 2006/072804 is described in US20050150771 in which, again, the initial anodising procedure requires a mixed sulphuric phosphoric acid anodising electrolyte to achieve lower forming voltage. It is notable that the forming voltages are limited to below 25V. However, optimum surface adhesion is not achieved as this can only be provided by sulphate free anodised layers formed under larger potentials. Thus, again, the duplex anodic layer formed is not optimised. US 4278737 discloses a method of anodizing aluminium and US 5486283 discloses a method for anodizing aluminium and product formed. JP2006 328467 discloses an anodic oxidation film applied aluminium substrate and method of manufacturing the same.

[0013] Thus, despite the development of anodising treatments for copper rich aluminium alloys, the corrosion protection afforded by the anodic layers is limited and does not provide the desired corrosion resistance.

[0014] In addition, many aerospace and automotive companies are utilising sol-gel chemistries as a replacement for hexavalent chrome anodising and conversion coatings. For corrosion resistance of anodised aluminium using sol-gel based sealers, the combination of both natural hydration of the surface as well as penetration of the sol-gel into the pores of the anodic is required for full performance. However, there are some inherent problems associated with the combination of sol-gel chemistry and current anodising processes. Migration of sol-gel materials into the aluminium oxide pores can also be limited.

[0015] Accordingly, there is a need for an improved method for the production of anodic coatings which are capable of imparting desirable corrosion resistance as well as the desirable adhesion and abrasion properties to an anodisable metal. Furthermore, the anodic layer requires optimisation in order to achieve full encapsulation of materials applied to the anodic layer(s) such as sol-gel sealers without affecting the desired properties of the anodic layers. Such optimised corrosion resistance; and optimised adhesion and abrasion properties as well as optimised for achieving full encapsulation of applied materials is not achieved by the known processes.

Summary of the present invention



[0016] Accordingly, the present invention provides a method for producing a multi-layer anodic coating on aluminium or an alloy thereof according to claim 1.

[0017] It will be understood that reducing the applied current does not equate to removing the applied current entirely.

[0018] The applied current in step (ii) may be reduced by an amount up to 50 % of the steady state current. The reduction in current results in a reduction in the steady state voltage.

[0019] The method according to the present invention suitably comprises the step of repeating step (ii) sequentially for a period of time such that a steady state voltage is obtained.

[0020] Steps (i) and (ii) of the method of the present invention comprise a first anodising process having a final forming voltage and step (iii) comprises a second anodising process having an initial forming voltage; wherein following step (ii), the final forming voltage of the first anodising process is less than the initial forming voltage of the second anodising process.

[0021] The thickness of the coating is determined by the level of electrical current and the length of time it is applied. The process described herein provides a barrier layer thinning technique. The term "barrier layer thinning" as used herein means a technique whereby the anodising current in the first anodising process is suddenly reduced to a lower value. This lower value may be half the value of the anodising current prior to the reduction. This reduction in steady state anodising current takes the system out of its first steady state anodising voltage and progressively lower voltages are achieved until the system reaches a second steady state. As the thickness of the barrier layer is dependent on the anodising voltage, the reduction in current effectively causes a thinning of the barrier layer. The method according to the present invention utilises this barrier layer thinning technique at the end of the first anodising step. This results in a lowering of the forming voltage and allows for a subsequent low forming voltage, second anodising step to be conducted.

[0022] The final forming voltage of the first anodising process is in the range 2V to 10V.

[0023] The method according to the present invention has the advantage that it is more flexible than those processes of the prior art due to the fact that the initial or first anodising step can be carried out using large voltages (for example, in the region of hundreds of volts) and fast anodising rates (for example, 0.05-1µm/min), while the second anodising step can still be conducted as a low voltage process. Another advantage of the present invention is that the second anodising step achieves growing a protective oxide layer as distinct from reducing the thickness of the barrier layers as in the prior art. Furthermore, the films produced using the method of the present invention have markedly different chemical and structural features from those achieved by the processes of the prior art. These chemical and structural features will be described further hereinbelow.

[0024] The method according to the present invention utilises a duplex anodising process which achieves the optimisation of the anodic layers and hence, the surface preparation of an anodisable metal, for example aluminium. The method of the present invention has the advantage that it overcomes the limitations between the respective forming voltages for the phosphoric acid anodising (PAA) and sulphuric acid anodising (SAA) treatments so that the parameters of each step may be chosen independently.

[0025] The first and second anodising steps can be carried out using any electrochemical process that forms an appropriate porous oxide layer on the metal. The formation of the oxide can be conducted simultaneously with an additional surface electrochemical process. For instance, the formation of the oxide can be accompanied simultaneously by an electrobrightening process. Electrobrightening of aluminium in acidic electrolytes is known to produce a porous oxide film similar to the anodising process. The parameters of the electrobrightneing process can be tailored to achieve reduction in surface roughness, to increase surface reflectance, while simultaneuously forming the anodic oxide required for the duplex anodic structure.

[0026] Another example of a simultaneous electrochemical process is the tailoring of the anodising procedure to form the porous oxide while simultaneously consuming the native oxide formed on the aluminium surface. Additionally, the parameters can be tailored to remove intermetallics from the aluminium matrix that oxidising at a slower rate than the aluminium metal. Such intermetallics can cause defect in the formed anodic layers which is problematic when optimum corrosion protection is required. In one embodiment of the present invention, the first anodic electrochemical treatment is used to prepare the aluminium surface and remove any intermetallics; and the second electrochemical process is then be conducted with the formed oxide thereby exhibiting optimum protection properties.

[0027] An advantage of the process according to the present invention is that it reduces the number of process steps therefore needed to prepare a metal surface. As the initial anodising treatment consumes the metal surfaces and any intermetallics, the surface is sufficiently prepared for the second treatment. The integrity and barrier properties achiveved by the first anodising step are not particularly important, as the resulting first anodic layer is used as an adhesion and abrasion promoter; the integrity of the second anodic layer formed by the second anodising step being aided by the first anodic layer pre-treatment. This feature has the advantage of removing the requirement for up to six chemical treatments from a typical known anodising and electrobrightening cycle.

[0028] The multi-layer anodic coating according to the present invention suitably comprises a duplex anodic layer. The duplex anodic layer structure is formed by the double anodising process described herein which is conducted in two different electrolytes under conditions such that optimisation of the structure of the respective layers and of the overall duplex layer is achieved for optimised corrosion resistance together with optimised adhesion and abrasion properties as well as optimised for achieving full encapsulation of applied materials such as additional treatments that may be added to the exposed surface of the multi-layer anodic coating, such treatments possibly being formulated in the form of sol-gels.

[0029] Multi-acid systems comprising two or more acids such as tartaric sulphuric acid, boric sulphuric acid or any other suitable mixed acid electrolytes may also be used. Additional ions such as tartrates or borates, for example, can be included to impart better corrosion resistance and physical properties in the aluminium oxide matrix. Furthermore, the low film thickness, suitably in the region of approximately 2 to 3 microns produced from these systems have been shown to be advantageous for corrosion resistance and fatigue resistance.

[0030] The first anodising solution for carrying out the first anodising step of the method of the present invention comprises phosphoric acid.

[0031] The second anodising solution for carrying out the second anodising step of the method of the present invention comprises a suitable acid be selected from the group consisting of sulphuric acid solution, oxalic acid solution, tartaric acid solution, boric acid solution and mixtures thereof.

[0032] The first and second anodising solutions may be kept at a temperature in the range 0°C to 90°C; ideally, in the range 0°C to 70°C; preferably, 5°C to 40°C, more preferably, 15°C to 25°C, most preferably about 20°C.

[0033] The method according to the present inventionhas the significant advantage of allowing the incorporation of the anticorrosion and fatigue resistance properties of tartaric sulphuric acid anodising (TSA) as well as the adhesion and abrasion properties of the phosphoric acid anodising (PAA) treatment on the same surface.

[0034] In one aspect of the present invention, the first anodising solution comprises from 1 to 20% phosphoric acid and the second anodising solution comprises from 1 to 30% sulphuric acid.

[0035] The first anodic layer may comprise a phosphoric acid anodic layer comprising pores that are referred to as relatively large pore diameters i.e. having a diameter in the range 50 to 150 nm, preferably in the range 50 to 100 nm, most preferably in the range 75 to 100nm.

[0036] The second anodic layer may comprise a sulphuric acid anodic layer comprising pores that are referred to as relatively small pore diameters i.e. having a diameter in the range 10 to 25nm preferably in the range 15 to 25nm.

[0037] The two layers comprising the first anodic layer and the second anodic layer, with the first anodic layer comprising pores having relatively large pore diameter size; and the second anodic layer comprising pores having relatively small pore diameter size is referred to herein as a duplex layer or duplex anodic layer or duplex structure.

[0038] This duplex layer structure allows impregnation of dyes or other compounds into the relatively smaller pores of the SAA while the surface of the SAA allows the required hydration layer. The larger pores of the PAA are advantageous for encapsulating the sol-gel materials, or any other applied coatings or adhesives for enhanced adhesion and corrosion protection.

[0039] In one aspect of the present invention, step (i) of the method is conducted at a voltage of 10 to 200V preferably 30 to 50V, more preferably 40V. This is a preferred voltage for carrying out the first anodising step which is carried out in phosphoric acid to form a phosphoric anodised layer.
It will be appreciated that the time required for the first step may vary with voltage and other parameters but a suitable time is between 1 to 240 minutes. The method may further comprise the step of sealing an interface between the first anodic layer and the second anodic layer. In a preferred aspect, the first anodic layer comprises a phosphoric acid (PAA) layer and the second anodic layer comprises a sulphuric acid (SAA) layer. The sealing creates a barrier at the interface that separates the two anodic layers. This advantageous sealing is discussed in more detail hereinbelow.

[0040] The method according to the present invention may also improve the process for the application of sol-gels or other top coats to anodic layers. The anti-corrosion properties of the top coat material is therefore not as critical because enhanced corrosion resistance is provided by the bottom anodic layer of the duplex structure. For example, the level of protection of provided by a Si-Zr sol-gel sealed anodic layer is appropriate to be considered as a replacement for Chromium based anodising and sealing technologies.

[0041] The sol-gel process can be used to form nanostructured inorganic films (typically 200nm to 10µm in overall thickness) that can be tailored to be more resistant than metals to oxidation, corrosion, erosion and wear while also possessing good thermal and electrical properties.

[0042] The surface of the phosphoric acid layer is compatible for coating or adhesive bonding as per conventional processes.

[0043] Preferably, the coating comprises a sol-gel. The sol-gel coating may be selected from the group consisting of an inorganic, organic or hybrid precursors such a metal oxides and organically functionalised silanes. The sol-gel coating may also contain active corrosion inhibitors such as nitrogen based heterocycles. An example of a suitable Si-Zr sol-gel is provided in WO/2009/069111, the entire contents of which are hereby incorporated by reference.

[0044] The method may further comprise the step of applying a sealing or corrosion inhibiting treatment to the sulphuric acid layer. The sealing treatment may include hydrothermal, nickel acetate, nickel fluoride, sodium silicate or other conventional sealing treatments. Corrosion inhibitors may also be included in the sulphuric acid layer. Examples of suitable corrosion inhibitors may be selected from the group consisting nitrogen heterocycles triazoles, triazines and tetrazines.

[0045] In another aspect, the present invention provides a multi-layer anodic coating comprising a duplex anodic structure comprising a phosphoric acid anodic layer and a sulphuric acid anodic layer, wherein said phosphoric acid layer is a surface layer and comprises pores having a diameter in the range 75 to 100nm; and said sulphuric acid layer comprising pores having a diameter in the range 10 to 25 nm, preferably 15 to 25nm.

[0046] The method of the present invention has the advantage that it achieves a structure within the first anodic layer (preferably, the anodic layer formed in the the phosphoric acid (ie. the phosphoric acid anodic layer) has a structure of pores having openings formed at intervals along the longitudinal axis of the pore such that adjacent pores are in fluid connecection thereby allowing a material such as a sol-gel to flow laterally between one columnar pore and a neighbouring columnar pore such that lateral porosity is achieved where heretofore only longitudinally porous structure was achieved. This structure has the highly desirable effect of enabling full encapsulation of a material such as a sol-gel throughout the first anodic (PAA) layer. Thus, a highly desirable and advantageous feature of the phosphoric acid anodising process conducted in the method according to the present invention is the lateral interporosity produced in the aluminium oxide network in addition to the longitudinal porosity. Thus, a 3D network of pores is formed in the first anodic layer (preferably, comprising PAA) which aids penetration, encapsulation and adhesion of any applied coatings or adhesives.

[0047] The duplex anodic structure formed by the method described herein enables encapsulation of sol-gel materials while the surface hydration is unaltered. The phosphoric acid layer in the duplex structure may further comprise a sol-gel.

1. Advantageous Features of the optimised multi-layer anodic layer of the present invention:



[0048] The oxide layers provided by the present invention achieve optimised adhesion to any applied liquids, adhesives or coatings.
  • For optimum adhesion, the surface oxide must be comprised of sulphate free anodic alumina. The presence of sulphate ions results in an increase in the hydration rate of the surface which can cause the pores to close and inhibit adhesion to the oxide. Additionally, application of coatings to sulphuric acid anodised layers can delaminate when exposed to humid conditions. Anodic layers comprising phosphate ions only have shown to provide excellent adhesion to a range of coating materials.
  • Anodic layers with pore diameter characteristic of phosphoric acid anodised layers for instance at least 50-150 nm. The large pore diameters allow better penetration of coatings and adhesives into the alumina matrix.
  • For encapsulation purposes, the layers would be required to be at least 3-5 µm for thin film coatings such as sol-gel. For larger coating thickness, such as those with paints the required anodic layer thickness may be up to 50 µm.

Additional features of the structure of the anodic layers of the present invention produced by the method of the present invention:


Selective sealing of duplex layers



[0049] The ability to apply sealing treatments to the base oxide of the duplex structure without closing the pores of the (top) surface oxide is a key element of the developed technology. Traditional treatments such as hydrothermal treatment or nickel based sealing can be conducted to increase the corrosion resistance of the base anodic layer while retaining the open pore and adhesion properties to the surface anodic layer. This can only be achieved by ensuring that the pore diameters of the surface oxide are appropriately large and that this layer is formed in electrolytes that are sulphate free.

Three dimensional porosity of formed layers



[0050] By selecting appropriate anodising conditions, the oxide film can be grown to produce pores that exhibit openings or channels in the pore walls as shown in Fig 9 of the attached drawings. The combination of acid concentration, temperature and anodising voltage results in a nanoporous three dimensional aluminium oxide network. Pore wall voids are visible throughout the layer leading to interconnectivity between adjoining pores.
By achieving this lateral porosity, a three dimensional porous network is formed. This network can be used as a host matrix for any applied coatings. This encapsulation method has shown particular application with sol-gel coatings. The sol-gel materials can easily migrate through the aluminium oxide network resulting in a dense oxide-sol-gel composite layer as seen in Figure 10.

[0051] The sulphuric acid anodic layer in the duplex structure may further comprise a corrosion inhibitor.

[0052] In a further aspect, the present invention provides an aluminium component comprising a multi-layer anodic coating produced by the method of the present invention. The aluminium component suitably comprises a multi-layer anodic coating comprising a duplex anodic structure comprising a phosphoric acid anodic layer which is a surface layer and comprising pores having a diameter in the range 75 to 100 nm; and a sulphuric acid anodic layer comprising pores having a diameter in the range 10 to 25 nm; preferably in the range 15 to 25 nm.

[0053] The multilayer, in paricular, duplex anodic layer structure produced by the process according to the present invention allows any coating material to be successfully incorporated into the anodic layer, retaining all the natural properties of both the coating and anodised surfaces. This combination can be used commercially in aerospace, automotive and architectural applications, amongst others.

[0054] It is to be understood that while the following description refers to duplex layer structure and method of formation of a duplex layer, it is to be understood that the method of the invention can be employed to form a multi-layer structure and is not limited to duplex layers.

Brief Description Of The Drawings



[0055] The present application will now be described more particularly with reference to the accompanying drawings in which a duplex anodic layer structure, and its method of formation, will be described by way of example only:

Figure 1 is an electron microscope image showing a duplex anodic layer formed on a clad Aluminium alloy (AA2024-T3);

Figures 2(a), 2(b) and 2(c) show a schematic of the anodic layer structural change during the duplex anodising cycle;

Figures 3(a) and 3(b) are electron microscope images showing the results of a barrier layer thinning process to 10V and 2V;

Figure 4 shows pore penetration of sol-gel materials into anodised layers on AA2024-T3;

Figure 5 is a graph showing rain erosion performance of anodised and sol-gel sealed systems on clad 2024-T3.;

Figures 6(a) and 6(b) show 0 h impedance and phase plots for PhTEOSand Si-Zr sealed anodic layers on AA2024-T3;

Figure 7 shows theTime to First Detection of Corrosion during Neutral Salt Spray Testing;

Figure 8 shows photographs of Phosphoric acid and Duplex Anodising Sealed with Phenyltriethoxysilane based Sol-gel after NSS salt spray intervals

Figure 9 is an electron microscope image showing an exploded view of the 3D network having lateral porosity (interporosity) structure of the first anodic layer (the PAA layer) of the duplex anodic layer formed on a clad Aluminium alloy (3003--H13); and

Figure 10 is an electron microscope image showing an exploded view of the 3D network having lateral porosity (interporosity) structure of the first anodic layer (the PAA layer) of the duplex anodic layer formed on a clad Aluminium alloy (3003-H13) and with sol-gel encapsulated in the first anodic layer.


Detailed Description



[0056] The present invention describes a method of forming a multilayer, in particular, duplex, porous structure on an anodisable metal. The method utilises an anodising process which is suitable for producing multilayer, in particular, duplex, anodic structures on the surface of a metal. The multilayer, in particular, duplex anodic structure optimises the surface preparation of a metal or alloy surface. The method described herein is particularly suitable for use as a surface preparation technique prior to sol-gel coating deposition on a metal or alloy, for example aluminium.

[0057] The method according to the present invention enables the production of a duplex anodic layer structure which enables a combination of adhesion and corrosion resistance to be achieved. The duplex structure comprises first and second anodic layers having a variable pore size. The process for the production of the duplex anodic structure involves treating an anodisable metal in two separate anodising baths to form firstly, a porous anodic oxide layer having a large diameter pore system, for example 75-100nm, and secondly, a second anodic layer having a smaller diameter pore system. The large diameter pore system exhibits a low level of hydration. This results in a surface treatment that has excellent adhesion and abrasion properties and a desirable hydration resistance. It will be appreciated that any suitable electrolyte may be used as the first anodising solution. An example of a suitable electrolyte is phosphoric acid. The incorporation of phosphate ions into the anodic layer results in a minimal rate of hydration. A second anodic layer may then be formed between the initial anodisation layer and the base metal. This layer may be tailored to achieve optimum corrosion resistance. A small pore size (10-20nm) is necessary for the second anodic layer and it enables a fast rate of hydration. The skilled person will appreciate that any suitable electrolytic solution may be used for the second anodising step. An example of a suitable electrolyte is sulphuric acid.

[0058] The smaller diameter pore system of the second anodic layer can be sealed by conventional processes such as hydrothermal sealing which converts aluminium oxide to aluminium hydroxide. The more volumous aluminium hydroxide results in a swelling closed of the pores increasing barrier protection of the anodised layer. Other methods of sealing based on heavy metal compounds or silicates can also be utilised. In all cases the open pore structure of the first anodised layer remains open.

[0059] It will be appreciated that the features and properties of the anodic oxides produced are dependent on many parameters including the aluminium alloy, electrolyte type and anodising conditions, for example, temperature and current density. Many structural changes to anodic layers can be conducted by altering the electrochemical parameters. For example lower electrolyte concentration results in better fatigue resistance as the film thickness is lower, lowering electrolyte temperature generally results in a harder oxide layer produced, and additional ions such a tartrates or borates can be introduced to the electrolytes to impart better corrosion resistance and physical properties.

[0060] For corrosion resistance of anodised aluminium using sol-gel based sealers, the combination of both natural hydration of the surface as well as penetration of the sol-gel into the pores of the anodic is generally required for full performance. As some sol-gel chemistries can inhibit hydration of anodic layers the natural protection properties of anodic layers is prevented. In addition some sol-gel chemistries do not penetrate the pores of sulphuric acid anodised (SAA) aluminium due to large particle size. Phosphoric acid anodised (PAA) aluminium with a larger pore size will allow penetration of such sol-gel however it does not allow hydration due to the chemical nature of the anodic finish.

[0061] In order to achieve both hydration and sol-gel penetration the duplex anodising process is utilised. The interface between the dual layers can be sealed by the hydration process. The duplex structure can be used as a standalone treatment for the metal for combined corrosion and adhesion properties. For optimum corrosion protection a coating can be applied to the duplex structure and encapsulated in the top anodic coatings. Suitable coatings include primers, topcoats and lacquers. Sol-gel derived coatings are particularly convenient as the entire sol-gel coating thickness can be encapsulated in the top anodic layer. Suitable sol-gel materials include any water or solvent based sol-gel formulation synthesised from silicon alkoxides or any other metal alkoxides.

[0062] Examples of components which may be treated with the process according to the present invention include generally aluminium components to be employed in an outdoor environment where a degree of corrosion resistance is required. These would include for example components used in the aerospace industry, automotive industry and building components, such as scaffolding, exterior trim and window frames.

[0063] The duplex structure may be tailored to suit particular applications, end uses. The following is an example of an application of the process according to the present invention wherein a duplex anodic layer was produced and sol-gel encapsulated into the structure thereof to enhance the properties thereof. The duplex anodising process according to the present inventiong utilises the natural corrosion resistance properties of sulphuric acid anodising with the adhesion and hosting properties of phosphoric acid anodising. The anodising process and sol-gel sealed surfaces produced in the following example were characterised using field emission scanning electron microscopy, energy dispersive x-ray spectroscopy. Performance of the sol-gel treated anodic layers was evaluated by neutral salt spray testing, electrochemical impedance spectroscopy and rain erosion testing.

[0064] Aspects will now be discussed in more detail below with reference to the following non limiting examples. The Si-Zr sol-gel referred to below in the Example(s) is the subject of International patent application no. WO2009069111 A2, the disclosure of which is incorporated herein.

Example 1



[0065] Two sol-gel coatings were synthesised and used as sealers for the anodic layers.

Phenyl Functionalised Sol-gel



[0066] The silane precursor Phenyltriethoxysilane (PhTEOS 98%) (VWR International Ltd (Irl), 98%) was hydrolysed under acidic conditions by adding 5.2ml of 0.04M HNO3 to 50.6ml of silane precursor. 30.6ml of absolute ethanol was immediately added to the mixture and left to stir for 45 minutes. 13.6ml of de-ionised water was then added dropwise and the solution was left to stir for 24 h before use. The final molar ratio for the formulation was Silane: Ethanol: Water - 1:2.5:3.5.

Silane-Zirconium Hybrid Sol-gel



[0067] The silane precursor, 3-(trimethoxysilyl) propylmethacrylate (MAPTMS) (Sigma Aldrich, Irl, Assay (99%) was pre-hydrolysed using 0.01 N HNO3 for 45 min (A). Simultaneously, zirconium (IV) n-propoxide (TPOZ) (Sigma Aldrich, Ireland, Assay ∼70% in propanol) was chelated using Methacrylic acid (MAAH)(Sigma Aldrich), at a 1:1 molar ratio for 45 minutes (B) to form a zirconium complex. Solution A was slowly added to solution B over ten minutes. Following another 45 min, water (pH 7) was added to this mixture. The molar ratio of Si/Zr in the final sol is 4:1 and Si/H20 is 1:2. After 24 hours of stirring 3,6-Di-2-pyridyl-1,2,4,5-tetrazine (DPTZ) was added as a corrosion inhibitor at a concentration of 0.3% w/v of MAPTMS precursor.

1.1 Pre-treatment and Anodising



[0068] AA2024-T3 (Si 0.5%, Fe 0.5%, Cu 0.8-4.9%, Mg 1.2-1.8%, Mn 0.3-0.9%, Cr 0.1%, Zn 0.25%, Ti 0.15% other 0.15%, Al remainder) aluminium panels (150mm x 100mm x 0.6mm) were sourced from Amari (Irl). The panels were degreased in acetone, etched in Novaclean® 104 for 45 secs, rinsed and etched in Novox® 302 for 90 seconds. Novaclean and Novox were purchased from Henkel (Ger). Clad 2024-T3 aluminium panels (150mm x 75mm x 0.6mm) were provided from industrial sources. Acetone, NaOH, HNO3, H2SO4 and H3PO4 were purchased from Sigma Aldrich IRL. The panels were degreased in acetone, etched in 10% NaOH at 40°C for 50 seconds and rinsed in de-ionised water. The panels were then treated in 50% HNO3 at room temperature for 90 seconds to remove any intermetallics from the surface prior to anodising.

[0069] Anodising solutions were prepared by diluting 98% H2SO4 w/v and 95% H3PO4 in deionised water to a concentration of 25% w/v and 10% w/v respectively. Three anodising procedures were conducted:
  1. 1) Phosphoric Acid Anodising (PAA) - 60 minute phosphoric acid anodising at constant 40V.
  2. 2) Sulphuric Acid Anodising (SAA) - 20 minute sulphuric acid anodising at 1.5A d/m2 of aluminium surface area.
  3. 3) Duplex Anodising (DA) - PAA process was conducted as per procedure 1). At the end of the PAA cycle the anodising current was immediately reduced to half of its steady state value. As a result the anodising potential gradually decreased. Once the anodising voltage decreased to 10V the power was turned off. The surfaces were then rinsed in de-ionised water for 10 minutes to remove any residual electrolyte from the pores. The parts were then immersed in the sulphuric acid electrolyte. AA2024-T3 and Clad AA2024-T3 were anodised for 5 and 2 min respectively at 1.5A d/m2 of aluminium surface area. All anodised samples were rinsed for 20 min in de-ionised water and air dried prior to sol-gel application and testing.


[0070] For the PAA and SAA surfaces the sol-gel solution applied immediately after rinsing and drying by a dip coating process. The DA surface was hydrothermally sealed in de-ionised water at 95 °C ±5 for 5 min prior to sol-gel dip coating. In all cases the dip cycle consisted of a 20 minute immersion step in the sol-gel solution following withdrawal at a rate of 10mm.min-1. The panels were then cured in an oven at 110°C for 16 hours.

[0071] The pore dimensions and penetration of the sol-gel sealers into the anodic layers was determined by electron microscopy using a Hitachi SU 70 Field Emission Scanning Electron Microscope (FESEM). Anodic film cross sections were prepared by bending the aluminium sample over 180° to induce microcracks in the oxide layer. The cross section of the crack face exhibits the pore structure of the anodic alumina for imaging at 3 - 5keV. For imaging purposes the samples were sputter coated with a 4nm layer of Pt/Pd using a Cressington 208HR sputter coater.
Dot Map energy dispersive X-ray spectroscopy was conducted using an Oxford Instruments INCA X-MAX Energy Dispersive X-ray Spectrometer attached to the FESEM. Cross sections were prepared by mounting samples in epoxy resin before grinding and polishing to a mirror finish using progressive grades of carbide paper and polished to a 1µm finish with a diamond solution. The polished cross sections were coated with 5nm of carbon using a Cressington 208C Carbon evaporation coating unit. The Si and Al species are presented on a mixed DOT MAP to show the location of the sol-gel sealer in relation to the anodic oxide and aluminium substrate.

[0072] Electrochemical Impedance Spectroscopy (EIS) was conducted on the anodised and sealed AA2024-T3 and clad AA2024-T3 samples. EIS was carried out using a Solartron SI 1287/1255B system comprising of a frequency analyser and potentiostat operated by CorrView® and Z Plot® software. EIS electrochemical cells were made by mounting bottom-less plastic vials on to the exposed surface of the coated panel with amine hardened epoxy adhesive (Araldite®). The exposure electrolyte used was 3.5% w/v solution of NaCl(aq). The area of the coating exposed was 4.9 cm2. All measurements were made at the open circuit potential (Eoc) with an applied 10mV sinusoidal perturbation in the frequency range 1×106 to 1×10-1 Hz (10 points per decade). EIS was performed with the anodised and sealed metal surface acting as the working electrode, silver/silver chloride (Ag/AgCl 3M KCl) electrode as the reference electrode and platinum mesh being used as a counter electrode.

[0073] To simulate the effect of rain erosion on the anodised and sol-gel sealed surface a Whirling Arm Rain Erosion test Rig (WARER) was used. Circular test samples were produced from the anodised and sol-gel treated samples by punch and die. The initial sample mass recorded. Mass measurements were repeated 3 times and taken using an Ohaus Explorer analytical balance with an accuracy of 0.1 mg. Inspection was also carried out for scratches and surface imperfections before testing. An individual test sample was then mounted at the end of the whirling arm. Tests were carried out at 178 ms-1 and weight loss was recorded at four test durations; 15, 30, 45, and 60 min. The total test duration is based on the length of time the droplet system is active. The rainfall rate was 25 mmh-1 and was monitored by a flowmeter. A cooling system was used to keep the ambient temperature constant during testing. After each test, the coupons were dried with compressed air and the mass recorded again.

[0074] In the example above, the duplex anodic structure produced by the method according to the present invention was utilised for sol-gel deposition. However it will be appreciated that it can be used for any applications requiring combined corrosion resistance of SAA layers with the adhesion properties of PAA.

[0075] The duplex oxides produced in accordance with the process according to the present invention are markedly different in structure from known duplex anodic structures. The current process produces duplex layers of unique structures as seen in the electron micrograph in Fig 1. The duplex structure consists of a SAA layer approximately 1µm next to the base metal. This layer exhibits all the natural features of conventional sulphuric acid anodising such as a small pore diameter as well as hydration and auto-sealing. As shown in Fig. 1, attached to the surface of the SAA is approximately 2 µm of oxide produced from the PAA process. The oxide exhibits a large pore diameter with a high level of interporosity. This interconnectivity between pores aids the penetration of liquids into the oxide network as the pressure increase within the pores due to the impinging liquid is easily dissipated.

[0076] Conventionally the forming voltage of the phosphoric acid anodising (PAA) process is larger than the sulphuric acid anodising (SAA) process. PAA can be conducted up to 200V while SAA processes generally do not exceed 25V. Due to this difference in forming voltages, burning and rapid dissolution of the metal can occur during the SAA cycle due to the high insulative effect of the previously formed PAA layer. The predominant structural effect of the forming voltage is the relative barrier layer thickness with nano-layers formed at approximately 1nm/V. The barrier layer has been shown to be a significant feature in the electrochemical response of anodised layers. The critical requirement for the formation of a duplex anodic layer without burning of the surfaces is the reduction of the barrier layer thickness of the PAA layer prior to the SAA anodising.

[0077] As shown in Fig 2 (a), after conducting the initial PAA process a porous layer with a relatively thick barrier layer is formed. The barrier layer formed at the base of the pores is approximately 40nm in thickness. It is known that the charge transfer across the barrier is due to ionic conduction of the anodising electrolyte ions. If the barrier layer is not decreased in thickness prior to the SAA process the application of the second lower steady state anodising potential is not sufficient to allow ionic transfer across the barrier layer. Rather than distributing uniformly across the metal surface the current will conduct through the point of least resistance. The process of in-situ electrochemical thinning of the barrier layer prior to the second anodising process as used in the method according to the present invention is critical to prevent burning and dissolution of the metal surface due to large build up of current density at weak spots in the first anodic layer.

[0078] Barrier layer thinning (BLT) utilises the self-regulating nature of the anodising process. By rapidly limiting current at the end of the PAA process to half of the steady state anodising current the voltage will gradually decrease from the set 40V to a lower value. As shown in Fig 2(b), during this decrease in voltage the self-regulating characteristic of the anodising process results in a corresponding thinning of the barrier layer Once a second steady state anodising voltage is reached the anodising current can again be halved which results in a further voltage drop and continued barrier layer thinning This step can be further repeated and by sequentially limiting the current in this way a final steady state voltage of the first anodising process can be lowered below the initial anodising voltage of the second anodising process. The results of conducting two rounds of current limiting procedure and three rounds of current limiting procedure on barrier layer thickness can be seen in Figures 3(a) and 3(b). Figure 3(a) shows the results of a BLT process to 10V and Figure 3(b) shows the results of a BLT process to 2V.

[0079] By lowering the forming voltage to 2V, it can be seen that the barrier is almost completely removed. Complete removal of the barrier may however compromise the interfacial adhesion between the anodised layers. Barrier layer thinning to a forming voltage of 10V is sufficient to allow the second anodising process to proceed. Once the BLT is achieved to an appropriate voltage the secondary sulphuric acid treatment can be conducted. Figure 4 shows the duplex anodic structure formed. The top anodic layer (PAA) has a large pore diameter desirable for the encapsulation of applied top coatings such as paint, lacquers or sol-gels. As the PAA layer does not hydrate the pores do not close over time and adhesion is retained. As any applied top coating will be encapsulated in an aluminium oxide matrix the abrasion resistance will be greatly increased.

[0080] Once the BLT PAA anodised aluminium is immersed in the SAA electrolyte and a potential above 10V is applied ionic conduction across the barrier layer will occur. This results in a thickening of the barrier layer and SAA layer pore nucleation initiates. The SAA layer growth then proceeds in uninhibited. By applying an intermediate BLT step between the first and second anodising processes the parameters for each treatment can be chosen independently. This allows a great deal of flexibility in the thickness, pore features and chemical nature of the possible duplex structures that can be formed.

[0081] The bottom SAA layer contains all the conventional properties of an anodised layer and can be hydrated and sealed to achieve elevated corrosion resistance. This layer can also be used to encapsulate corrosion inhibitors, organic dyes or metal electrodeposits.

[0082] There are many factors that can determine if the sol-gel coating penetrates the porous anodic layers. PAA layer offer the best probability of penetration due to the large pore diameter however if the particle size is sufficiently small the sol-gel colloids can also migrate into the SAA layers. In order to determine the penetration properties of the sol-gel coatings on each anodic finish EDX dot map analysis was used to plot the Si and Al distributions. Fig 4 exhibits the dot maps for the PhTEOS and Si-Zr sol-gel sealed SAA, PAA and DA films. The PhTEOS exhibits penetration into all surfaces. On the SAA layer, which contains the smallest pore diameter it is clear that the PhTEOS sealer has significant penetration into the oxide with Si intensity deteriorating rapidly at approximately 75% of the oxide thickness. The PAA is known to act as an excellent host for sol-gel materials and penetration can be seen throughout the layer. For the DA layer penetration occurs in the PAA layer without any migration into the SAA base layer due to the forced hydration and pore closing between the PAA and SAA layers. In the case of the Si-Zr sol-gel the large limited penetration into SAA network occurs. A surface coating only can be distinguished from Fig 1. Similarly to the PhTEOS the Si-Zr sol-gel penetrates the PAA networks of the single and duplex anodised layers.

[0083] Anodising is often used to increase the surface hardness and abrasion resistance of aluminium alloys. By incorporating the sol-gel coating into the aluminium oxide network the elevated mechanical properties are afforded to the sol-gel coating. This will improve the hardness, abrasion resistance and impact resistance of the sol-gel coatings. A significant advantage of increased mechanical performance for the aerospace industry is the decreased effect of rain erosion. Erosion of aerospace grade aluminium alloys by impinging water droplets is a significant issue especially during aircraft take-off and landing.

[0084] Whirling arm rain erosion evaluation of the Si-Zr sol-gel sealed clad 2024-T3 samples was conducted and the weight loss over the 60 min exposure was recorded as seen in Fig 5. The weight loss for the sol-gel applied on the SAA is significantly greater than any other surface tested. From the EDX analysis Fig 6 it is determined that the sol-gel forms a surface coating on the SAA surface with limited encapsulation in the porous anodic alumina. The rain erosion and weight loss of this system is of the sol-gel coating only which is mechanically inferior to the aluminium oxides produced from SAA, PAA and DA as well as the sol-gel/alumina composites produced from sol-gel encapsulation.

[0085] This indicates that the encapsulation of the sol-gel coatings in anodic alumina presents a significant improvement in rain erosion. The weight loss of the bare anodic layers or sol-gel encapsulated layers is minimal.

[0086] The electrochemical properties of the treated anodised aluminium panels can be used to estimate the potential long term performance in aggressive challenging environments. EIS is an AC technique used to estimate electrochemical interactions at the coating metal interface at a preset potential, usually the open circuit potential. The EIS analysis involved applying an AC voltage at the OCP, with sinusoidal amplitude of 10mV, from a frequency of 106 Hz down to 10-1 Hz across the sealed anodic layer. The films resistance to the AC signal, or impedance, varies according to the applied frequency and is graphically represented on a Bode frequency plot. The phase angle associated with the impedance gives valuable information on the film properties such as barrier performance and interfacial activity.

[0087] EIS analysis was conducted on the un-clad 2024-T3 as the electrochemical response is from the copper rich base metal which is more susceptible to corrosion than the clad material. The 0 hr impedance and phase plot for the PhTEOS sealed anodic layers can be seen in Fig 5. The PAA and DA layers exhibit a characteristic two time constant response corresponding to a sealed porous layer and a barrier layer contribution. Conversely the SAA PhTEOS layer exhibits a single time constant phase angle response. PhTEOS sol-gel sealed SAA anodic layers have been previously reported and have produced a similar single time constant response REF REF. From the EDX analysis it is known that this sealer penetrates the porous network and the EIS response is as a result of the sol-gel/oxide composite layer. The Si-Zr sol-gel where pore penetration is absent on the SAA layer exhibits a two time constant response as seen in Fig 5. These features correspond to the sol-gel coating and the barrier layer. The Si-Zr sealed PAA and DA layer exhibit a two time constant response similar to the PhTEOS sealed equivalents.

[0088] By plotting the impedance at 0.1 Hz over time the evolution of barrier properties can be determined. The protection properties of each sealer over time can be seen in Fig 6. For the PhTEOS sealed anodic layers, Fig 7(a), the SAA and DA layers appear stable up to 668 h while the impedance of the PAA layer drops rapidly at 168 h exposure. At this exposure time the PAA PhTEOS sealed layer exhibits extensive pitting and corrosion. The increased impedance of the SAA system compared to the DA is due to the longer anodising duration of the SAA system. The SAA and DA exhibit stable impedance up to 836 h.

[0089] In the case of the Si-Zr sol-gel sealed anodic layers all system experience a drop in impedance after 168 h however after this time the impedance stabilises. This initial drop is possibly due to uptake of electrolyte by the sol-gel coating. After this time the impedance stabilises.

[0090] Neutral salt spray exposure was also conducted on the anodised and sol-gel sealed samples. In unsealed form the SAA, PAA and DA surfaces offer little protection with corrosion occurring rapidly. The SAA and PAA layers exhibited pitting corrosion after 24 h exposure with the DA surface remaining clear of corrosion until 72 h exposure. Upon the onset of initial corrosion pitting increases rapidly for all of the unsealed anodised surfaces. Treating of the SAA and PAA surfaces with the PhTEOS sol-gel exhibits limited increase in protection. The presence of the sol-gel within the pores of the SAA layer appears to have a negative effect on corrosion prevention with a marginally higher level of pitting exhibited on the PhTEOS treated surface when compared to the unsealed SAA. This is possibly due to the effect on hydration due to the presence of the sol-gel within the aluminium oxide network. The sol-gel may retard the hydration of the surfaces as has been previously reported. In the case of the PhTEOS PAA layer there is a marginal reduction in pitting however the performance over the unsealed PAA is negligible. The PhTEOS sealed DA layer exhibited a marked increase in pitting prevention over the other anodising finishes.



[0091] The Si-Zr sol-gel presents enhanced pitting corrosion protection over the PhTEOS sol-gel sealed systems. The increased barrier properties as well as the inclusion of an active corrosion inhibitor results a significant level of protection on all anodising treatments. The SAA layer in particular exhibits remarkable corrosion resistance with no evidence of pitting at 3500 h. The absence of pore penetration of the Si-Zr sol ensures that the natural hydration properties of the SAA layer are retained. Furthermore the inclusion of an appropriate corrosion inhibitor may also have a positive effect on the integrity of the SAA layer. The tetrazine based inhibitor is known to bind to and chelate copper ions. The DA equivalent shows a higher degree of degradation, when compared to the SAA equivalent, possibly due to the decrease thickness of the SAA layer. The worst performing Si-Zr sealed layer is the PAA.

[0092] For many sol-gel coating additives there is a critical concentration after which the additive affects the film forming properties and integrity of the applied sol-gel film. Excess amounts of corrosion inhibitors have been shown to have a negative effect on film forming properties of sol-gel coatings. By utilising a duplex anodic oxide the active corrosion inhibitors can be incorporated in the SAA layer at a significantly higher concentration while the sol-gel can be encapsulated in the porous PAA network. DA allows addition of inhibitor into the SAA layer.

Further Examples


Example 2 (combined electropolishing and anodising)



[0093] Aluminium alloy 6063 is exposed to an aqueous electrolyte containing 40% H3PO4 at 70°C. The aluminium acts as an anode with a lead cathode. A current of approx 6 A/dm2 is applied. The applied potential is approximately 80V. This procedure results in a combined action of surface polishing as well as growth of a phosphate rich anodic layer on the surface of the metal. The process is conducted for 20 mins to achieve a high level of surface brightening. At the end of the combined polishing and anodising cycle the current is halved and the potential is allowed to float to achieve a lower steady state value. This current reduction process is repeated until a steady state voltage of 10V is achieved. The part is then removed from the phodpsoric acid bath and rinsed in de-ionised water. The part is then exposed to a room temperature electrolyte of 25% H2SO4 and a current of 1.5 A/dm2 is applied for 20 mins. This grows a protective anodic layer between the initial phosphate rich oxide and the brightened base metal.

Example 3 (Surface Conditioning Process)



[0094] Aluminium alloy 2024 is exposed to an aqueous electrolyte containing 10% H3PO4 at 40°C. The aluminium acts as an anode with a lead cathode. A potential of 30V is applied. The process is conducted for 10 mins. This procedure results in a combined action of growing a phosphate rich anodic layer while also conditioning the metal prior to a second anodisation. The process aides in the removal of intermetallics in the alloy that do not anodise at the same rate as the aluminium matrix. At the end of the combined conditioning and anodising cycle the current is halved and the potential is allowed to float to achieve a lower steady state value. This current reduction process is repeated until a steady state voltage of 10V is achieved. The part is then removed from the H3PO4 bath and rinsed in de-ionised water. The part is then exposed to a room temperature electrolyte of 25% H2SO4 and a current of 1.5 A/dm2 is applied for 20 mins. This grows a protective anodic layer between the initial phosphate rich oxide and the conditioned base metal.

Example 4 (High potential process)



[0095] A high voltage process can also be utilised for the first anodising step. A aluminium alloy 3003 is exposed to a 4% H3PO4 electrolyte at room temperature. The aluminium acts as an anode with a lead cathode. A potential of 120V is applied to the aluminium anode to grow a phosphate rich anodic layer. At the end of the combined polishing and anodising cycle the current is halved and the potential is allowed to float to achieve a lower steady state value. This current reduction process is repeated until a steady state voltage of 10V is achieved. The part is then removed from the phodpsoric acid bath and rinsed in de-ionised water. The part is then exposed to a room temperature electrolyte of 25% H2SO4 and a current of 1.5 A/dm2 is applied for 20 mins. This grows a protective anodic layer between the initial phosphate rich oxide and the base metal.

[0096] In summary, the method according to the present invention has the advantage that it can be utilised for adhesion and bonding applications while also retaining a significant level of corrosion resistance on aluminium alloys. The duplex anodic layer is particularly suitable for sol-gel sealing. Due to the low thickness of sol-gel coatings the PAA layer can be tailored to result in full encapsulation of the sol-gel coating within the anodic structure. Furthermore conventional sealing methods can be applied to the SAA base layer of the DA structure. This results in elevated corrosion resistance while also preventing the sol-gel material from migrating into the SAA pores. The natural hydration properties of SAA layer is therefore not affected by the presence of the sol-gel material while encapsulation in the PAA layer increases the mechanical properties of the sol-gel.

[0097] The words comprises/comprising when used in this specification are to specify the presence of stated features, integers, steps or components but does not preclude the presence or addition of one or more other features, integers , steps, components or groups thereof.


Claims

1. A method for producing a multi-layer anodic coating on aluminium or an alloy thereof which comprises the steps of

(i) placing the aluminium or alloy thereof in a first electrolytic solution and applying a current as a steady state current to form a first anodic layer having a barrier region, wherein the first electrolytic solution comprises phosphoric acid;

(ii) reducing the applied current to cause a reduction in thickness of the barrier region; and

(iii) placing the aluminium or alloy thereof in a second electrolytic solution and applying a current to form a second anodic layer, wherein the second electrolytic solution is selected from the group consisting of sulphuric acid solution, oxalic acid solution, tartaric acid solution, boric acid solution and mixtures thereof,

wherein the multi-layer anodic coating comprises a first anodic layer and a second anodic layer, with the first anodic layer comprising pores having a diameter in the range 50 to 150 nm, preferably in the range 50 to 100 nm, most preferably in the range 75 to 100 nm; and the second anodic layer comprising pores having a diameter in the range 10 to 25 nm, preferably in the range 15 to 25 nm, and wherein step (i) and step (ii) define a first anodising process having a final forming voltage and step (iii) defines a second anodising process having an initial forming voltage; wherein following step (ii), the final forming voltage of the first anodising process is less than the initial forming voltage of the second anodising process; and wherein the final forming voltage after step (ii) is in the range 2V to 10V.
 
2. A method according to claim 1 wherein the current in step (ii) is a reduction by an amount up to 50% from the steady state current in step (i); optionally further comprising the step of repeating step (ii) sequentially for a period of time.
 
3. A method according to any preceding claim wherein the multi-layer anodic coating comprises a duplex anodic layer.
 
4. A method according to claim 1 wherein the first anodic layer comprises a phosphoric acid anodic layer comprising pores having a diameter in the range 50 to 100 nm, preferably in the range 75 to 100 nm.
 
5. A method according to claim 1 or claim 4 wherein the second anodic layer comprises a sulphuric acid anodic layer.
 
6. A method according to any one of claims 1 to 5 wherein step (i) is conducted at 10 to 200V volts for 1 to 240 minutes; preferably,
wherein step (i) is conducted at between 30 to 50V;
most preferably wherein step (i) is conducted at about 40V.
 
7. A method according to any preceding claim, further comprising the step of sealing an interface between the first anodic layer and the second anodic layer;
optionally, wherein the first anodic layer comprises a phosphoric acid layer and the second anodic layer comprises a sulphuric acid layer.
 
8. A method as claimed in any preceding claim wherein the first anodic layer includes a structure of pores having openings formed at intervals along the longitudinal axis of the pore such that adjacent pores are in fluid connection so as to allow a material such as a sol-gel to flow laterally between one columnar pore and a neighbouring columnar pore such that lateral porosity is achieved so as to enable full encapsulation of a material such as a sol-gel throughout the first anodic layer, and wherein the first anodic layer comprises a phosphoric acid layer formed in phosphoric acid.
 
9. A method according to claim 8, further comprising the step of applying a coating or adhesive to the phosphoric acid layer; optionally wherein the coating comprises a sol-gel; and preferably,
wherein the sol-gel is selected from the group consisting of an inorganic, organic or hybrid precursors such a metal oxides and organically functionalised silanes.
 
10. A method according to any one of claims 5 to 9, further comprising the step of applying a sealing or corrosion inhibiting treatment to said sulphuric acid layer; optionally wherein the sealing treatment includes hydrothermal, nickel acetate, nickel fluoride, sodium silicate or other conventional sealing treatments; optionally, wherein said corrosion inhibitor is selected from the group consisting of nitrogen heterocycles triazoles, triazines and tetrazines.
 
11. A method according to any one of the preceding claims wherein the first and second anodising steps are carried out using any electrochemical process that forms an appropriate porous oxide layer on the aluminium or alloy thereof.
 
12. A method according to Claim 11 wherein the formation of the oxide is conducted simultaneously with an additional surface electrochemical process, optionally wherein the formation of the oxide can be accompanied simultaneously by an electrobrightening process.
 
13. A method according to claim 12 wherein the simultaneous electrochemical process comprises the tailoring of the anodising procedure to form the porous oxide while simultaneously consuming the native oxide formed on a surface of the aluminium or alloy thereof; optionally wherein the parameters can be tailored to remove intermetallics from a matrix of the aluminium or alloy thereof that oxidise at a slower rate than the aluminium or alloy thereof.
 
14. A method according to claim 11 wherein the first anodic electrochemical process is used to prepare a surface of the aluminium or alloy thereof and remove any intermetallics; and the second electrochemical process is then conducted with the formed oxide thereby exhibiting optimum protection properties.
 
15. A method according to any one of claims 1 to 14 wherein the first and second anodising solutions are maintained at a temperature in the range of between 0°C to 90°C; ideally, in the range of between 0°C to 70°C; preferably, 5°C to 40°C, more preferably, 15°C to 25°C, most preferably about 20°C.
 
16. A multi-layer anodic coating comprising duplex anodic structure comprising a phosphoric acid anodic layer and a sulphuric acid anodic layer, wherein said phosphoric acid layer is a surface layer and comprises pores having a diameter in the range 75 to 100 nm and said sulphuric acid layer comprising pores having a diameter in the range 10 to 25 nm.
 
17. A multi-layer anodic coating comprising a first anodic layer and a second anodic layer wherein the first anodic layer includes a structure of pores having openings formed at intervals along the longitudinal axis of the pore such that adjacent pores are in fluid connection so as to allow a material such as a sol-gel to flow laterally between one columnar pore and a neighbouring columnar pore such that lateral porosity is achieved so as to enable full encapsulation of a material such as a sol-gel throughout the first anodic layer, wherein the first anodic layer is a surface layer and comprises a phosphoric acid layer formed in a phosphoric acid electrolyte, wherein the phosphoric acid layer comprises pores having a diameter in the range 75 to 100 nm.
 
18. A multi-layer anodic coating according to claim 17 wherein said first anodic layer further comprises a sol-gel.
 
19. A multi-layer anodic coating according to claim 16 wherein said sulphuric acid anodic layer further comprises a corrosion inhibitor.
 
20. An aluminium component comprising a multi-layer anodic coating according to claim 16.
 


Ansprüche

1. Verfahren zur Herstellung einer mehrschichtigen anodischen Beschichtung auf Aluminium oder einer Legierung davon, umfassend die Schritte:

(i) Anordnen des Aluminiums oder der Legierung davon in einer ersten elektrolytischen Lösung und Anlegen eines Stroms als stationären Strom, um eine erste anodische Schicht, die einen Sperrbereich aufweist, zu bilden, wobei die erste elektrolytische Lösung Phosphorsäure umfasst;

(ii) Verringern des angelegten Stroms, um eine Dickenverringerung des Sperrbereichs zu bewirken; und

(iii) Anordnen des Aluminiums oder der Legierung davon in einer zweiten elektrolytischen Lösung und Anlegen eines Stroms, um eine zweite anodische Schicht zu bilden, wobei die zweite elektrolytische Lösung ausgewählt ist aus der Gruppe bestehend aus Schwefelsäurelösung, Oxalsäurelösung, Weinsäurelösung, Borsäurelösung und Gemischen davon,

wobei die mehrschichtige anodische Beschichtung eine erste anodische Schicht und eine zweite anodische Schicht umfasst, wobei die erste anodische Schicht Poren mit einem Durchmesser in dem Bereich von 50 bis 150 nm umfasst, vorzugsweise in dem Bereich von 50 bis 100 nm, höchst bevorzugt in dem Bereich von 75 bis 100 nm; und die zweite anodische Schicht Poren mit einem Durchmesser in dem Bereich von 10 bis 25 nm umfasst, vorzugsweise in dem Bereich von 15 bis 25 nm, und wobei Schritt (i) und Schritt (ii) ein erstes Anodisierungsverfahren mit einer End-Formierungsspannung definieren und Schritt (iii) ein zweites Anodisierungsverfahren mit einer Anfangs-Formierungsspannung definiert; wobei nach Schritt (ii) die End-Formierungsspannung des ersten Anodisierungsverfahrens kleiner als die Anfangs-Formierungsspannung des zweiten Anodisierungsverfahrens ist; und wobei die End-Formierungsspannung nach Schritt (ii) in dem Bereich von 2 V bis 10 V liegt.
 
2. Verfahren gemäß Anspruch 1, wobei der Strom bei Schritt (ii) eine Verringerung um eine Menge von bis zu 50 % von dem stationären Strom bei Schritt (i) darstellt; gegebenenfalls ferner umfassend den Schritt des aufeinanderfolgenden Wiederholens von Schritt (ii) für eine Zeitdauer.
 
3. Verfahren gemäß einem der vorstehenden Ansprüche, wobei die mehrschichtige anodische Beschichtung eine anodische Duplexschicht umfasst.
 
4. Verfahren gemäß Anspruch 1, wobei die erste anodische Schicht eine Phosphorsäure-anodische Schicht umfasst, die Poren mit einem Durchmesser in dem Bereich von 50 bis 100 nm, vorzugsweise in dem Bereich von 75 bis 100 nm, umfasst.
 
5. Verfahren gemäß Anspruch 1 oder Anspruch 4, wobei die zweite anodische Schicht eine Schwefelsäure-anodische Schicht umfasst.
 
6. Verfahren gemäß einem der Ansprüche 1 bis 5, wobei Schritt (i) bei 10 bis 200 V Volt für 1 bis 240 Minuten durchgeführt wird;
wobei Schritt (i) vorzugsweise bei zwischen 30 und 50 V durchgeführt wird;
wobei Schritt (i) höchst bevorzugt bei etwa 40 V durchgeführt wird.
 
7. Verfahren gemäß einem der vorstehenden Ansprüche, ferner umfassend den Schritt des Versiegelns einer Grenzfläche zwischen der ersten anodischen Schicht und der zweiten anodischen Schicht;
wobei gegebenenfalls die erste anodische Schicht eine Phosphorsäureschicht umfasst und die zweite anodische Schicht eine Schwefelsäureschicht umfasst.
 
8. Verfahren gemäß einem der vorstehenden Ansprüche, wobei die erste anodische Schicht eine Struktur von Poren aufweist, die Öffnungen aufweisen, die in Intervallen entlang der Längsachse der Pore gebildet sind, so dass benachbarte Poren in Fluidverbindung stehen, um zu erlauben, dass ein Material, wie z. B. ein Sol-Gel, seitwärts zwischen einer säulenförmigen Pore und einer benachbarten säulenförmigen Pore fließt, so dass seitliche Porosität erzielt wird, um vollständige Verkapselung eines Materials, wie z. B. eines Sol-Gels, in der gesamten ersten anodischen Schicht zu ermöglichen, und wobei die erste anodische Schicht eine Phosphorsäureschicht umfasst, die in Phosphorsäure gebildet ist.
 
9. Verfahren gemäß Anspruch 8, ferner umfassend den Schritt des Aufbringens einer Beschichtung oder eines Klebstoffs auf die Phosphorsäureschicht;
wobei die Beschichtung gegebenenfalls ein Sol-Gel umfasst; und
wobei das Sol-Gel vorzugsweise ausgewählt ist aus der Gruppe bestehend aus einem anorganischen, organischen oder hybriden Vorläufer, wie z. B. Metalloxiden und organisch funktionalisierten Silanen.
 
10. Verfahren gemäß einem der Ansprüche 5 bis 9, ferner umfassend den Schritt des Aufbringens einer Versiegelungs- oder Korrosionshemmungsbehandlung auf die Schwefelsäureschicht; wobei die Versiegelungsbehandlung gegebenenfalls hydrothermische, Nickelacetat, Nickelfluorid, Natriumsilicat oder andere herkömmliche Versiegelungsbehandlungen umfasst; wobei der Korrosionshemmer gegebenenfalls ausgewählt ist aus der Gruppe bestehend aus Stickstoffheterocyclischen Triazolen, Triazinen und Tetrazinen.
 
11. Verfahren gemäß einem der vorstehenden Ansprüche, wobei der erste und der zweite Anodisierungsschritt unter Verwendung eines beliebigen elektrochemischen Verfahrens durchgeführt werden, das eine geeignete poröse Oxidschicht auf dem Aluminium oder der Legierung davon bildet.
 
12. Verfahren gemäß Anspruch 11, wobei das Bilden des Oxids gleichzeitig mit einem zusätzlichen elektrochemischen Oberflächenverfahren durchgeführt wird, wobei das Bilden des Oxids gegebenenfalls gleichzeitig von einem Elektroaufhellungsverfahren begleitet sein kann.
 
13. Verfahren gemäß Anspruch 12, wobei das gleichzeitige elektrochemische Verfahren das Maßschneidern des Anodisierungsverfahrens umfasst, um das poröse Oxid zu bilden und gleichzeitig das native Oxid zu verbrauchen, das auf einer Oberfläche des Aluminiums oder der Legierung davon gebildet ist; wobei die Parameter gegebenenfalls dafür maßgeschneidert werden können, intermetallische Stoffe aus einer Matrix des Aluminiums oder der Legierung davon zu entfernen, die mit einer langsameren Rate als das Aluminium oder die Legierung davon oxidieren.
 
14. Verfahren gemäß Anspruch 11, wobei das erste anodische elektrochemische Verfahren verwendet wird, um eine Oberfläche des Aluminiums oder der Legierung davon vorzubereiten und jegliche intermetallischen Stoffe zu entfernen; und das zweite elektrochemische Verfahren anschließend mit dem gebildeten Oxid durchgeführt wird, um dadurch optimale Schutzeigenschaften aufzuweisen.
 
15. Verfahren gemäß einem der Ansprüche 1 bis 14, wobei die erste und die zweite Anodisierungslösung bei einer Temperatur in dem Bereich von zwischen 0 °C und 90 °C gehalten werden; idealerweise in dem Bereich zwischen 0 °C und 70 °C; vorzugsweise 5 °C bis 40 °C, bevorzugter 15 °C bis 25 °C, höchst bevorzugt etwa 20 °C.
 
16. Mehrschichtige anodische Beschichtung, umfassend eine anodische Duplexstruktur, die eine Phosphorsäure-anodische Schicht und eine Schwefelsäure-anodische Schicht umfasst, wobei die Phosphorsäureschicht eine Oberflächenschicht ist und Poren mit einem Durchmesser in dem Bereich von 75 bis 100 nm umfasst und die Schwefelsäureschicht Poren mit einem Durchmesser in dem Bereich von 10 bis 25 nm umfasst.
 
17. Mehrschichtige anodische Beschichtung, umfassend eine erste anodische Schicht und eine zweite anodische Schicht, wobei die erste anodische Schicht eine Struktur von Poren aufweist, die Öffnungen aufweisen, die in Intervallen entlang der Längsachse der Pore gebildet sind, so dass benachbarte Poren in Fluidverbindung stehen, um zu erlauben, dass ein Material, wie z. B. ein Sol-Gel, seitwärts zwischen einer säulenförmigen Pore und einer benachbarten säulenförmigen Pore fließt, so dass seitliche Porosität erzielt wird, um vollständige Verkapselung eines Materials, wie z. B. eines Sol-Gels, in der gesamten ersten anodischen Schicht zu ermöglichen, wobei die erste anodische Schicht eine Oberflächenschicht ist und eine Phosphorsäureschicht umfasst, die in einem Phosphorsäure-Elektrolyten gebildet ist, wobei die Phosphorsäureschicht Poren mit einem Durchmesser in dem Bereich von 75 bis 100 nm umfasst.
 
18. Mehrschichtige anodische Beschichtung gemäß Anspruch 17, wobei die erste anodische Schicht ferner ein Sol-Gel umfasst.
 
19. Mehrschichtige anodische Beschichtung gemäß Anspruch 16, wobei die Schwefelsäure-anodische Schicht ferner einen Korrosionshemmer umfasst.
 
20. Aluminiumkomponente, umfassend eine mehrschichtige anodische Beschichtung gemäß Anspruch 16.
 


Revendications

1. Procédé de production d'un revêtement anodique multicouche sur de l'aluminium ou un alliage de celui-ci qui comprend les étapes de

(i) positionnement de l'aluminium ou de l'alliage de celui-ci dans une première solution électrolytique et application d'un courant définissant un courant en régime permanent pour former une première couche anodique ayant une région barrière, la première solution électrolytique comprenant de l'acide phosphorique ;

(ii) réduction du courant appliqué pour provoquer une réduction d'épaisseur de la région barrière ; et

(iii) positionnement de l'aluminium ou de l'alliage de celui-ci dans une deuxième solution électrolytique et application d'un courant pour former une deuxième couche anodique, la deuxième solution électrolytique étant choisie dans le groupe constitué par une solution d'acide sulfurique, une solution d'acide oxalique, une solution d'acide tartrique, une solution d'acide borique et les mélanges de celles-ci,

dans lequel le revêtement anodique multicouche comprend une première couche anodique et une deuxième couche anodique, la première couche anodique comprenant des pores ayant un diamètre dans la gamme de 50 à 150 nm, de préférence dans la gamme de 50 à 100 nm, idéalement dans la gamme de 75 à 100 nm, et la deuxième couche anodique comprenant des pores ayant un diamètre dans la gamme de 10 à 25 nm, de préférence dans la gamme de 15 à 25 nm, et dans lequel l'étape (i) et l'étape (ii) définissent un premier traitement d'anodisation ayant une tension de formation finale et l'étape (iii) définit un deuxième traitement d'anodisation ayant une tension de formation initiale ; dans lequel, après l'étape (ii), la tension de formation finale du premier traitement d'anodisation est inférieure à la tension de formation initiale du deuxième traitement d'anodisation ; et dans lequel la tension de formation finale après l'étape (ii) se situe dans la gamme de 2 V à 10 V.
 
2. Procédé selon la revendication 1 dans lequel le courant à l'étape (ii) est une réduction d'une quantité allant jusqu'à 50 % du courant en régime permanent à l'étape (i) ; éventuellement, comprenant en outre l'étape de répétition séquentielle de l'étape (ii) pendant un laps de temps.
 
3. Procédé selon une quelconque revendication précédente dans lequel le revêtement anodique multicouche comprend une couche anodique duplex.
 
4. Procédé selon la revendication 1 dans lequel la première couche anodique comprend une couche anodique à l'acide phosphorique comprenant des pores ayant un diamètre dans la gamme de 50 à 100 nm, de préférence dans la gamme de 75 à 100 nm.
 
5. Procédé selon la revendication 1 ou la revendication 4 dans lequel la deuxième couche anodique comprend une couche anodique à l'acide sulfurique.
 
6. Procédé selon l'une quelconque des revendications 1 à 5 dans lequel l'étape (i) est conduite à 10 à 200 V volts pendant 1 à 240 minutes ; de préférence dans lequel l'étape (i) est conduite entre 30 et 50 V ; idéalement dans lequel l'étape (i) est conduite à environ 40 V.
 
7. Procédé selon une quelconque revendication précédente, comprenant en outre l'étape d'étanchéification d'une interface entre la première couche anodique et la deuxième couche anodique ;
éventuellement dans lequel la première couche anodique comprend une couche à l'acide phosphorique et la deuxième couche anodique comprend une couche à l'acide sulfurique.
 
8. Procédé selon une quelconque revendication précédente dans lequel la première couche anodique comporte une structure de pores ayant des ouvertures formées à des intervalles le long de l'axe longitudinal du pore de telle sorte que des pores adjacents sont en connexion fluidique de manière à permettre à un matériau tel qu'un sol-gel de s'écouler latéralement entre un pore colonnaire et un pore colonnaire voisin de telle sorte qu'une porosité latérale est obtenue de manière à permettre l'encapsulation complète d'un matériau tel qu'un sol-gel dans toute la première couche anodique, et dans lequel la première couche anodique comprend une couche à l'acide phosphorique formée dans de l'acide phosphorique.
 
9. Procédé selon la revendication 8, comprenant en outre l'étape d'application d'un revêtement ou d'un adhésif à la couche à l'acide phosphorique ; éventuellement dans lequel le revêtement comprend un sol-gel ; et de préférence dans lequel le sol-gel est choisi dans le groupe constitué par des précurseurs inorganiques, organiques ou hybrides tels que des oxydes métalliques et des silanes fonctionnalisés par voie organique.
 
10. Procédé selon l'une quelconque des revendications 5 à 9, comprenant en outre l'étape d'application d'un traitement d'étanchéification ou d'inhibition de la corrosion à ladite couche à l'acide sulfurique ; éventuellement dans lequel le traitement d'étanchéification comporte un traitement hydrothermique, à l'acétate de nickel, au fluorure de nickel, au silicate de sodium ou d'autres traitements d'étanchéification conventionnels ; éventuellement dans lequel ledit inhibiteur de corrosion est choisi dans le groupe constitué par les triazoles, triazines et tétrazines à hétérocycles azotés.
 
11. Procédé selon l'une quelconque des revendications précédentes dans lequel les première et deuxième étapes d'anodisation sont réalisées au moyen de n'importe quel traitement électrochimique qui forme une couche d'oxyde poreux approprié sur l'aluminium ou l'alliage de celui-ci.
 
12. Procédé selon la revendication 11 dans lequel la formation de l'oxyde est conduite simultanément à un traitement électrochimique de surface supplémentaire, éventuellement dans lequel la formation de l'oxyde peut être accompagnée simultanément par un traitement d'électrobrillantage.
 
13. Procédé selon la revendication 12 dans lequel le traitement électrochimique simultané comprend l'adaptation de la procédure d'anodisation pour former l'oxyde poreux tout en consommant simultanément l'oxyde natif formé sur une surface de l'aluminium ou de l'alliage de celui-ci ; éventuellement dans lequel les paramètres peuvent être adaptés pour retirer des intermétalliques d'une matrice de l'aluminium ou de l'alliage de celui-ci qui s'oxydent à une vitesse plus lente que l'aluminium ou l'alliage de celui-ci.
 
14. Procédé selon la revendication 11 dans lequel le premier traitement électrochimique anodique est utilisé pour préparer une surface de l'aluminium ou de l'alliage de celui-ci et retirer tous les intermétalliques ; et le deuxième traitement électrochimique est ensuite conduit avec l'oxyde formé présentant ainsi des propriétés de protection optimales.
 
15. Procédé selon l'une quelconque des revendications 1 à 14 dans lequel les première et deuxième solutions d'anodisation sont maintenues à une température dans la gamme entre 0 °C et 90 °C ; idéalement, dans la gamme entre 0 °C et 70 °C ; de préférence, de 5 °C à 40 °C, mieux encore de 15 °C et 25 °C, idéalement à environ 20 °C.
 
16. Revêtement anodique multicouche comprenant une structure anodique duplex comprenant une couche anodique à l'acide phosphorique et une couche anodique à l'acide sulfurique, dans lequel ladite couche à l'acide phosphorique est une couche de surface et comprend des pores ayant un diamètre dans la gamme de 75 à 100 nm et ladite couche à l'acide sulfurique comprend des pores ayant un diamètre dans la gamme de 10 à 25 nm.
 
17. Revêtement anodique multicouche comprenant une première couche anodique et une deuxième couche anodique, dans lequel la première couche anodique comporte une structure de pores ayant des ouvertures formées à des intervalles le long de l'axe longitudinal du pore de telle sorte que des pores adjacents sont en connexion fluidique de manière à permettre à un matériau tel qu'un sol-gel de s'écouler latéralement entre un pore colonnaire et un pore colonnaire voisin de telle sorte qu'une porosité latérale est obtenue de manière à permettre l'encapsulation complète d'un matériau tel qu'un sol-gel dans toute la première couche anodique, dans lequel la première couche anodique est une couche de surface et comprend une couche à l'acide phosphorique formée dans un électrolyte à l'acide phosphorique, dans lequel la couche à l'acide phosphorique comprend des pores ayant un diamètre dans la gamme de 75 à 100 nm.
 
18. Revêtement anodique multicouche selon la revendication 17 dans lequel ladite première couche anodique comprend en outre un sol-gel.
 
19. Revêtement anodique multicouche selon la revendication 16 dans lequel ladite couche anodique à l'acide sulfurique comprend en outre un inhibiteur de corrosion.
 
20. Composant en aluminium comprenant un revêtement anodique multicouche selon la revendication 16.
 




Drawing





























Cited references

REFERENCES CITED IN THE DESCRIPTION



This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

Patent documents cited in the description