(11)EP 3 101 043 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
27.01.2021 Bulletin 2021/04

(21)Application number: 14868022.6

(22)Date of filing:  09.12.2014
(51)International Patent Classification (IPC): 
C08F 293/00(2006.01)
C08J 5/00(2006.01)
C08F 214/18(2006.01)
C08L 53/00(2006.01)
G03F 7/00(2006.01)
C08F 220/30(2006.01)
(86)International application number:
PCT/KR2014/012035
(87)International publication number:
WO 2015/084132 (11.06.2015 Gazette  2015/23)

(54)

BLOCK COPOLYMER

BLOCKCOPOLYMER

COPOLYMÈRE BLOC


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 20.12.2013 KR 20130159994
30.09.2014 KR 20140131964
08.12.2014 KR 20140175412

(43)Date of publication of application:
07.12.2016 Bulletin 2016/49

(73)Proprietor: LG Chem, Ltd.
Seoul 150-721 (KR)

(72)Inventors:
  • KIM, Jung Keun
    Daejeon 305-738 (KR)
  • LEE, Jeong Kyu
    Daejeon 305-738 (KR)
  • LEE, Je Gwon
    Daejeon 305-738 (KR)
  • LEE, Mi Sook
    Daejeon 305-738 (KR)
  • PARK, No Jin
    Daejeon 305-738 (KR)
  • KU, Se Jin
    Daejeon 305-738 (KR)
  • CHOI, Eun Young
    Daejeon 305-738 (KR)
  • YOON, Sung Soo
    Daejeon 305-738 (KR)

(74)Representative: Hoffmann Eitle 
Patent- und Rechtsanwälte PartmbB Arabellastraße 30
81925 München
81925 München (DE)


(56)References cited: : 
JP-B2- 4 625 901
KR-A- 20100 070 380
US-A- 5 234 604
KR-A- 20100 033 962
KR-A- 20110 097 707
  
  • DATABASE CAPLUS, CHEMICAL ABSTRACT [Online] 7 September 2011 (2011-09-07), ZOU YUE: "Fluorosurfactant capable of preventing unevenness in photoresist coating and its preparation by anionic polymerization", XP002771143, retrieved from CAPLUS; STN Database accession no. 2011:1148166 & CN 102 172 491 A (JIANGSU JOHNNY FLUORIN MATERIAL TECHNOLOGY CO LTD) 7 September 2011 (2011-09-07)
  • MORI H ET AL: "SYNTHESIS AND SURFACE CHARACTERIZATION OF HYDROPHILIC-HYDROPHOBIC BLOCK COPOLYMERS CONTAINING POLY(2,3-DIHYDROXYPROPYL METHACRYLATE)", MACROMOLECULES, AMERICAN CHEMICAL SOCIETY, US, vol. 27, no. 15, 18 July 1994 (1994-07-18) , pages 4093-4100, XP000456650, ISSN: 0024-9297, DOI: 10.1021/MA00093A010
  • KAGO K ET AL: "X-ray reflectivity study of polymer assembly at air-water interface", SUPRAMOLECULAR SCIENCE, BUTTERWORTH-HEINEMANN, OXFORD, GB, vol. 5, no. 3-4, 1 July 1998 (1998-07-01), pages 349-355, XP027388373, ISSN: 0968-5677 [retrieved on 1998-07-01]
  • LUTZ FUNK ET AL: "Novel Amphiphilic Styrene-Based Block Copolymers for Induced Surface Reconstruction", MACROMOLECULAR CHEMISTRY AND PHYSICS., vol. 209, no. 1, 4 January 2008 (2008-01-04), pages 52-63, XP055382259, DE ISSN: 1022-1352, DOI: 10.1002/macp.200700312
  • AKIBA, ISAMU ET AL.: 'Self-assembly of amphiphilic block copolymers containing poly(n- octadecyl actylate) block in aqueous solution' IOP CONFERENCE SERIES: MATERIALS SCIENCE AND ENGINEERING vol. 14, no. 1, 2010, XP055348355
 
Remarks:
The filing date of the international application is within two months from the date of expiration of the priority period (R. 26bis.3 PCT).
 
Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


Description

TECHNICAL FIELD



[0001] The present application relates to block copolymers and their application.

BACKGROUND



[0002] Block copolymers have molecular structures in which polymer subunits having chemically different structures from each other are linked by covalent bonds. Block copolymers are capable of forming periodically aligned structure such as the sphere, the cylinder or the lamella through phase separations. Sizes of domains of the structures formed by the self assemblies of block copolymers may be adjusted in a wide range, and various shapes of structures can be prepared. Therefore, they can be utilized in pattern-forming methods by lithography, various magnetic recording mediae or next generation nano devices such as metal dots, quantum dots or nano lines, high density magnetic storage mediae, and the like.

[0003] Block copolymers are disclosed in the following: Zou Yue, "fluorosurfactant capable of preventing unevenness in photoresist coating and its preparation by anionic polymerization", Chemical Abstract, 7 September 2011; Mori H et al, "Synthesis and surface characterization of hydrophilic-hydrophobic block copolymers containing poly(2,3-dihydroxypropyl methacrylate)", Macromolecules, American Chemical Society, vol. 27, no. 15, 18 July 1994, pages 4093-4100; Kago K et al, "X-ray reflectivity study of polymer assembly at air-water interface", Supramolecular Science, vol. 5, no. 3-4, 1 July 1998, pages 349-355; Lutz Funk et al, "Novel Amphiphilic styrene-based block copolymers for induced surface reconstruction", Macromolecular Chemistry and Physics, vol. 209, no. 1, 4 January 2008, pages 52-63; and US 5 234 604 A.

DESCRIPTION


TECHNICAL OBJECT



[0004] The present application provides a block copolymer, a polymer layer including the block copolymer, a method for forming the polymer layer and a pattern-forming method.

TECHNICAL SOLUTION



[0005] The block copolymer includes a first block represented by Formula 1 described below and a second block represented by Formula 3 described below.

[0006] The block copolymer may be a block copolymer that includes an additional block other than the first and second blocks.

[0007] The block copolymers may be phase-separated, since they comprise the two or more polymeric chains linked to each other via covalent bonds. In the present application, since the block copolymer satisfies at least one parameter as described below, the phase-separation can be very effectively occurred, and therefore it can form a nano-scaled structure by a microphase separation. According to the present application, by controlling sizes such as molecular weights or relative ratios between blocks, Sizes or shapes of the nano structure can be freely adjusted. By the above, the block copolymer can freely form various sizes of phase-separated structure such as the sphere, the cylinder, the gyroid, the lamella and the reversed structure and the like. The present inventors have found that, if block copolymers satisfy at least one parameter among ones described below, the self assembling properties and the phase separation properties as described above are largely improved. It is confirmed that it is possible to make the block copolymer to show a vertically aligning property by making the block copolymer to satisfy an appropriate parameter. The term "vertically aligning property" as used herein may refer to aligning property of the block copolymer and may refer to a case where the nano scaled structure formed by the block copolymer is aligned vertically to a direction of a substrate. Techniques controlling an aligning of a self assembled structure of a block copolymer to be vertical or parallel with respect to various substrates are a big part of practical application of a block copolymer. Conventionally, the aligning direction of the nano scaled structure in a layer of a block copolymer depends on what block among blocks forming the block copolymer is exposed to a surface or an air. Generally, since lots of substrates are polar and the air is non-polar, a block having more polarity than the other block in the block copolymer wets on the substrate and a block having less polarity than the other block in the block copolymer wets with respect to the interface between the air. Many techniques are proposed in order for blocks of a block copolymer having properties different from each other to wet simultaneously toward the substrate, and a most typical method is to control the aligning by preparing the neutral surface. However, in one embodiment, by controlling the parameters below, the block copolymer may be vertically aligned with respect to substrates, to which conventionally known treatment for accomplishing the vertical alignment including the neutral surface treatment is not performed. For example, block copolymers according to one embodiment of the present application can show the vertical aligning property on both of hydrophobic surfaces and hydrophilic surfaces, to which any pre-treatment is not performed. Further, in an additional embodiment, the vertical alignment may be accomplished with respect to a large area in a short time by a thermal annealing.

[0008] The block copolymer according to the present application exhibits a specific tendency in a XRD (X ray diffraction) analysis.

[0009] That is, as described below, the number (n) of the chain-forming atoms and the scattering vector (q) obtained from the XRD analysis satisfy the equation 1 below.



[0010] In the Equation 1, the "n" is the number of the chain-forming atoms, and the "q" is the smallest scattering vector among scattering vectors at which peaks are observed in the XRD analysis or a scattering vector at which a peak having the largest area is observed. Further, the π in the equation 1 is the ratio of the circumference of a circle to its diameter.

[0011] The term "chain-forming atoms" as used herein refers to atoms forming the side chain linked to the block copolymer and atoms forming a linear structure of the side chain. The side chain may have a linear or branched structure; however the number of the chain-forming atoms is calculated only by the number of atoms forming the longest linear chain. Therefore, other atoms such as, in a case where the chain-forming atom is the carbon atom, the hydrogen atom that is linked to the carbon atom and the like are not calculated as the number of the chain-forming atoms. Further, in case of the branched chain, the number of the chain-forming atoms is the number of atoms forming the longest chain. For example, the chain is n-pentyl, all of the chain-forming atoms are carbon atoms and the number thereof is 5. If the chain is 2-methylpentyl, all of the chain-forming atoms are also carbon atoms and the number thereof is 5. The chain-forming atoms may be the carbon, the oxygen, the sulfur or the nitrogen, and the like and appropriate chain-forming atoms may be the carbon, the oxygen or the nitrogen; or the carbon or the oxygen. The number of the chain-forming atoms may be 8 or more, 9 or more, 10 or more, 11 or more; or 12 or more. The number of the chain-forming atoms may be 30 or less, 25 or less, 20 or less or 16 or less.

[0012] The XRD analysis for confirming the equation 1 may be performed by passing X-ray through a sample of the block copolymer and then measuring a scattering intensity according to scattering vector. The XRD analysis may be performed with respect to a block copolymer without any specific pre-treatment, and, for example, it may be performed by drying the block copolymer under an appropriate condition and then passing X ray through it. As the X ray, X ray, a vertical size of which is 0.023 mm and a horizontal size of which is 0.3 mm can be used. By using a measuring device (for example, 2D marCCD), a 2D diffraction pattern scattered from the sample is obtained as an image, and then the above fitting is performed with respect to the obtained diffraction pattern so as to obtain the scattering vector and the FWHM, and the like.

[0013] The fitting of the diffraction pattern may be performed by a numerical analysis, in which the least square technique is used, with respect to results of the XRD analysis. In the above method, the Gaussian fitting is performed with respect to a profile of peaks in the XRD pattern under a state where a position at which a XRD diffraction pattern has a lowest intensity becomes a baseline and the lowest intensity is converted to zero, and then the scattering vector (q) and the FWHM are obtained from the result of the Gaussian fitting. The R square of the Gaussian fitting is at least 0.9 or more, 0.92 or more, 0.94 or more or 0.96 or more. The method obtaining the above information from the XRD analysis is known, and, for example, a numerical value analysis program such as the origin may be used.

[0014] The scattering value substituted with the value of the equation 1 may be a scattering value within a range from 0.5 nm-1 to 10 nm-1. In another embodiment, the scattering value substituted with the value of the equation 1 may be a scattering value within a range from 0.5 nm-1 to 10 nm-1. In another embodiment, the scattering value substituted with the value of the equation 1 may be 0.7 nm-1 or more, 0.9 nm-1 or more, 1.1 nm-1 or more, 1.3 nm-1 or more or 1.5 nm-1 or more. In another embodiment, the scattering value substituted with the value of the equation 1 may be 9 nm-1 or less, 8 nm-1 or less, 7 nm-1 or less, 6 nm-1 or less, 5 nm-1 or less, 4 nm-1 or less, 3.5 nm-1 or less or 3 nm-1 or less.

[0015] The equation 1 may represent a relation between the number of the chain-forming atoms and an interval (D) between blocks including the chains under a state where the block copolymer is self assembled and forms the phase separated structure. If the number of the chain-forming atoms of the block copolymer including the chains satisfies the equation 1, the crystallizability exhibited by the chain is improved, and therefore the phase separation property and the vertical aligning property may be largely improved. In another embodiment, the nq/(2×π) in the equation 1 may be 4.5 nm-1 or less. In the above, the interval (D, unit: nm) between blocks including the chains can be calculated by a numerical formula, D = 2×π/q. In the above, the "D" is the interval (D, unit: nm) between the blocks and the π and the q are the same as defined in the equation 1.

[0016] The above parameter may be realized by, for example, controlling the structure of the block copolymer.

[0017] Hereinafter, for the sake of convenient explanation, the block comprising the side chain may be referred to as the first block.

[0018] The block copolymer may include two or more blocks.

[0019] The term "aromatic structure" as used herein may refer to an aryl or arylene group, and may refer to a monovalent or a bivalent substituent derived from a compound including one benzene ring structure or a structure, in which at least two benzene rings are linked with sharing one or two carbon atoms or by an optional linker, or a derivative of the compound. The aryl or arylene group may be, unless defined otherwise, an aryl group having 6 to 30, 6 to 25, 6 to 21, 6 to 18, or 6 to 13 carbon atoms. As the aryl or arylene group, a monovalent or a bivalent substituent derived from benzene, naphthalene, azobenzene, anthracene, phenanthrene, tetracene, pyrene, benzopyrene, and the like may be illustrated.

[0020] For example, in order to control the parameter, the chain having 8 or more chain-forming atoms is linked, as a side chain, to first block of the block copolymer. In this document, the term "side chain" and the term "chain" may indicate to the same object. The first block includes the aromatic structure, and the chain is linked to the aromatic structure.

[0021] The side chain may be a chain linked to a main chain of polymer. As described, the side chain may be a chain including 8 or more, 9 or more, 10 or more, 11 or more or 12 or more chain-forming atoms. The number of the chain-forming atoms may be 30 or less, 25 or less, 20 or less or 16 or less. The chain-forming atom may be carbon, oxygen, nitrogen or sulfur, or appropriately carbon or oxygen.

[0022] The side chain may be a hydrocarbon chain such as an alkyl group, an alkenyl group or an alkynyl group. At least one carbon atom in the hydrocarbon chain may be replaced with the sulfur atom, the oxygen atom or the nitrogen atom.

[0023] The side chain is linked to the aromatic structure, and the chain may be directly linked to the aromatic structure or may be linked to the aromatic structure via a linker. The linker may be an oxygen atom, a sulfur atom, -NR1-, -S(=O)2-, a carbonyl group, an alkylene group, an alkenylene group, an alkynylene group, - C(=O)-X1- or -X1-C(=O)-. In the above, the R1 may be hydrogen, an alkyl group, an alkenyl group, an alkynyl group, an alkoxy group or an aryl group and the X1 may be a single bond, an oxygen atom, a sulfur atom, -NR2-, -S(=O)2-, an alkylene group, an alkenylene group or alkynylene group, and the R2 may be hydrogen, an alkyl group, an alkenyl group, an alkynyl group, an alkoxy group or an aryl group. An appropriate linker may the oxygen atom. The side chain may be linked to the aromatic structure via, for example, an oxygen atom or nitrogen.

[0024] An appropriate linker bonding the aromatic structure to the main chain may -C(=O)-O- or -O-C(=O)-, but is not limited thereto.

[0025] In another embodiment, the aromatic structure in the first block and/or the second block of the block copolymer may include 1 or more, 2 or more, 3 or more, 4 or more or 5 or more halogen atom(s). The number of the halogen atom(s) may be 30 or less, 25 or less, 20 or less, 15 or less or 10 or less. The halogen atom may be a fluorine or chlorine; and the fluorine may be used. The block comprising the aromatic structure including the halogen atom may effectively form the phase separation structure by an appropriate interaction with the other block.

[0026] For realizing appropriate phase separations, the first block may include an aromatic structure that does not include the halogen atom and the second block may include an aromatic structure that includes the halogen atom. Further, the aromatic structure of the first block may include the side chain that is linked directly or via the linker including the oxygen or nitrogen atom.

[0027] The first block is represented by Formula 1.





[0028] In Formula 1, R is hydrogen or an alkyl group having 1 to 4 carbon atom(s); X is a carbonyl group, -C(=O)-X1- or -X1-C(=O)-, wherein X1 is an oxygen atom, a sulfur atom or -S(=O)2-; and Y is a monovalent substituent including an aromatic structure which has 6 to 12 carbon atoms and to which a side chain having 8 or more chain-forming atoms is linked.

[0029] The term "single bond" as used herein may refer to a case where there is no atom in a corresponding site.

[0030] The term "alkyl group" as used herein may refer to, unless defined otherwise, a linear, a branched or a cyclic alkyl group having 1 to 20, 1 to 16, 1 to 12, 1 to 8, or 1 to 4 carbon atoms, and the alkyl group may be optionally substituted with at least one substituent. In case where the side chain is the alkyl group, the alkyl group may include 8 or more, 9 or more, 10 or more, 11 or more or 12 or more carbon atoms, and the number of the carbon atoms in the alkyl group may be 30 or less, 25 or less, 20 or less or 16 or less.

[0031] The term "alkenyl or alkynyl group" as used herein may refer to, unless defined otherwise, a linear, a branched or a cyclic alkenyl or alkynyl group having 2 to 20, 2 to 16, 2 to 12, 2 to 8, or 2 to 4 carbon atoms and the alkenyl or alkynyl group may be optionally substituted with at least one substituent. In case where the side chain is the alkenyl or alkynyl group, the alkenyl or the alkynyl group may include 8 or more, 9 or more, 10 or more, 11 or more or 12 or more carbon atoms, and the number of the carbon atoms in the alkenyl or the alkynyl group may be 30 or less, 25 or less, 20 or less or 16 or less.

[0032] The term "alkylene group" as used herein may refer to, unless defined otherwise, an alkylene group having 1 to 20, 1 to 16, 1 to 12, 1 to 8 or 1 to 4 carbon atoms. The alkylene group may have a linear, branched, or cyclic structure, and may be optionally substituted with at least one substituent.

[0033] The term "alkenylene or alkynylene group" as used herein may refer to, unless defined otherwise, an alkenylene or alkynylene group having 2 to 20, 2 to 16, 2 to 12, 2 to 8 or 2 to 4 carbon atoms. The alkenylene or alkynylene group may have a linear, branched, or cyclic structure, and may be optionally substituted with at least one substituent.

[0034] The X of the Formula 1 may be, in another embodiment, -C(=O)O- or - OC(=O)-.

[0035] The Y in the formula 1 is the substituent including the chain, it is a substituent including an aromatic structure having 6 to 12 carbon atoms. In the above, the chain may be an alkyl group having 8 or more, 9 or more, 10 or more, 11 or more or 12 or more carbon atoms. The alkyl group may include 30 or less, 25 or less, 20 or less or 16 or less carbon atom. The chain may be directly linked to the aromatic structure or be linked to the aromatic structure via the linker as described above.

[0036] The first block may be, in another embodiment, represented by the Formula 2 below.



[0037] In Formula 2, the R may be the hydrogen atom or the alkyl group having 1 to 4 carbon atom(s), the X may be -C(=O)-O-, the P may be the arylene group having 6 to 12 carbon atoms, the Q may be the oxygen atom, the Z is the chain having 8 or more chain-forming atoms.

[0038] In another embodiment of the Formula 2, the P may be a phenylene. Also, the Z may be a linear alkyl group having 9 to 20, 9 to 18 or 9 to 16. In case where the P is the phenylene, the Q may be linked to the para position of the phenylene. The alkyl group, arylene group, phenylene group and the chain may be optionally substituted with at least one substituent.

[0039] The second block is represented by Formula 3 below.





[0040] In Formula 3, X2 is a single bond, an oxygen atom, a sulfur atom or - S(=O)2-; and W is an aryl group which has 6 to 13 carbon atoms and which comprises at least one halogen atom.

[0041] In another embodiment of the Formula 3, the X2 may be the single bond.

[0042] In the Formula 3, the aryl group of the W may be an aryl group having 6 to 12 carbon atoms or a phenyl group. The aryl group or the phenyl group may include 1 or more, 2 or more, 3 or more, 4 or more or 5 or more halogen atom(s). The number of the halogen atom(s) may be 30 or less, 25 or less, 20 or less, 15 or less or 10 or less. As the halogen atom, fluorine atom may be used.

[0043] The block of the Formula 3 may be, in another embodiment, represented by Formula 4 below.





[0044] In Formula 4, the X2 is the same as defined in the Formula 3, and the R1 to R5 may be each independently hydrogen, an alkyl group, a haloalkyl group or a halogen atom. The number of the halogen atom included in the R1 to R5 is 1 or more.

[0045] In Formula 4, the R1 to R5 may be each independently hydrogen, an alkyl group having 1 to 4 carbon atom(s) or a haloalkyl group having 1 to 4 carbon atom(s) or the halogen atom, and the halogen atom may be the fluorine or chlorine.

[0046] In Formula 4, the R1 to R5 may include 1 or more, 2 or more, 3 or more, 4 or more, 5 or more or 6 or more halogen atom(s). The upper limit of the number of the halogen atom(s) is not particularly limited, and the number of the halogen atom(s) in the R1 to R5 may be, for example, 12 or less, 8 or less, or 7 or less.

[0047] The block copolymer may include only the above described two kinds of blocks or may include both of the above described two kinds of blocks along with another block.

[0048] A method for preparing the block copolymer is not particularly limited. For example, the block copolymer may be prepared by a living radical polymerization (LRP). For example, there are methods such as the anionic polymerization, in which block copolymers are synthesized in the presence of inorganic acid salts such as salts of alkali metal or alkali earth metal by using organic rare earth metal complexes or organic alkali metal compounds as polymerization initiators; the anionic polymerization, in which block copolymers are synthesized in the presence of organic aluminum compounds by using organic alkali metal compounds as polymerization initiators; the atom-transfer radical polymerization (ATRP) using an atom transfer radical polymerizer as a polymerization controller; the activators regenerated by electron transfer (ATGET) ATRP performing polymerization in the presence of an organic or inorganic reducing agent generating electrons using an atom transfer radical polymerizer as a polymerization controller; the initiators for continuous activator regeneration (ICAR) ATRP; the reversible addition-ring opening chain transfer (RAFT) polymerization using an inorganic reducing agent reversible addition-ring opening chain transfer agent; and the a method using an organic tellurium compound as an initiator, and an appropriate method may be selected among the above methods.

[0049] In one embodiment, the block copolymer may be prepared by a method including polymerizing a material comprising monomers capable of forming the block in the presence of radical initiators and living radical polymerization reagents by the living radical polymerization. The method for preparing the block copolymer may further include, for example, precipitating the polymerized product formed from the above process in non solvent.

[0050] A kind of the radical initiators may be suitably selected in consideration of polymerization efficiency without particular limitation, and an azo compound such as azobisisobutyronitrile (AIBN) or 2,2'-azobis-(2,4-dimethylvaleronitrile), or a peroxide compound such as benzoyl peroxide (BPO) or di-t-butyl peroxide (DTBP) may be used.

[0051] The LRP may be performed in a solvent such as methylenechloride, 1,2-dichloroethane, chlorobenzene, dichlorobenzene, benzene, toluene, acetone, chloroform, tetrahydrofuran, dioxane, monoglyme, diglyme, dimethylformamide, dimethylsulfoxide or dimethylacetamide.

[0052] As the non-solvent, for example, an alcohol such as methanol, ethanol, normal propanol or isopropanol, a glycol such as ethyleneglycol, or an ether compound such as n-hexane, cyclohexane, n-heptane or petroleum ether may be used without limitation.

[0053] The block copolymer as described above may exhibit an excellent phase separation property and self assembling property and its vertical aligning property is also excellent. The present inventor has confirmed that, if the block copolymer further satisfies at least one parameter among ones as described below, the above properties can be further improved.

[0054] For example, the block copolymer may form a layer showing an in-plane phase diffraction pattern of the grazing incidence small angle X ray scattering (GISAXS) on a hydrophobic surface. The block copolymer may form a layer showing an in-plane phase diffraction pattern of the grazing incidence small angle X ray scattering (GISAXS) on a hydrophilic surface.

[0055] The term "showing the in-plane phase diffraction pattern of the grazing incidence small angle X ray scattering (GISAXS)" as used herein may refer to a case where a peak vertical to the X coordinate is observed in the GISAXS diffraction pattern when the GISAXS analysis is performed. Such a peak may be confirmed by the vertical aligning property of the block copolymer. Therefore, the block copolymer showing the in-plane phase diffraction pattern shows the vertical aligning property. Further, if the above peaks are observed with a regular interval, the phase separation efficiency may be further improved.

[0056] The term "vertical" as used herein is a term considering errors and, for example, it may include errors within ±10 degrees, ±8 degrees, ±6 degrees, ±4 degrees or ±2 degrees.

[0057] A block copolymer capable of forming a layer showing the in-plane phase diffraction patterns on both of the hydrophobic and the hydrophilic surfaces can show the vertical aligning property on various surface to which any treatment for inducing the vertical aligning is not performed. The term "hydrophobic surface" as used herein may refer to a surface of which a wetting angle of purified water is in a range from 5 degrees to 20 degrees. Examples of the hydrophobic surface may include a surface of silicone treated with the piranha solution, sulfuric acid, or an oxygen plasma, but is not limited thereto. The term "hydrophilic surface" as used herein may refer to a surface of which a wetting angle of purified water is in a range from 50 degrees to 70 degrees. Examples of the hydrophilic surface may include a surface of silicone treated with hydrogen fluoride, silicone treated with hexamethyldisilazane or polydimethylsiloxane treated with oxygen plasma, but is not limited thereto.

[0058] Unless defined otherwise, in this document, a property such as a wetting angle that can be changed according to temperature is measured at room temperature. The term "room temperature" as used herein may refer to a temperature in its natural state that is not heated and cooled and may refer to a temperature in a range from about 10°C to 30°C, or of about 25°C or about 23°C.

[0059] The layer that is formed on the hydrophobic or hydrophilic surface and shows the in-plane phase diffraction pattern on the GISAXS may be a layer to which a thermal annealing is performed. In one embodiment, the layer for measuring the GISAXS is, for example, prepared by coating a coating solution, which is prepared by diluting the block copolymer in a solvent (for example, fluorobenzene) to a concentration of about 0.7 weight%, on a corresponding hydrophobic or hydrophilic surface so as for the coated layer to have a thickness of about 25 nm and an area of about 2.25 cm2 (a width: 1.5 cm, a length: 1.5 cm) and then performed the thermal annealing thereto. The thermal annealing may be performed by maintaining the layer for about 1 hour at a temperature of 160°C. The GISAXS may be measured by irradiating the above prepared layer with X ray so as for an incident angle thereof to be in a range from 0.12 to 0.23 degrees. Diffraction patterns scattered from the layer may be obtained by a conventional measuring device (for example, 2D marCCD). Techniques confirming the existence of the in-plane phase diffraction pattern from the above obtained diffraction pattern is known in the field.

[0060] The block copolymer showing the above peaks in the GISAXS can show excellent self assembling property and the property can be effectively controlled according to an object.

[0061] In another embodiment, the block copolymer may exhibit at least one peak within a predetermined range of the scattering vector (q) in the XRD (X ray diffraction) analysis as described above.

[0062] For example, in the XRD analysis, the block copolymer may show at least one peak within a range from 0.5 nm-1 to 10 nm-1 of the scattering vectors (the q values). In other embodiment, the range of the scattering vectors (the q values) within which the at least one peak is observed may be from 0.7 nm-1 or more, 0.9 nm-1 or more, 1.1 nm-1 or more, 1.3 nm-1 or more or 1.5 nm-1 or more. In other embodiment, the range of the scattering vectors (the q values) within which the at least one peak is observed may be from 9 nm-1 or less, 8 nm-1 or less, 7 nm-1 or less, 6 nm-1 or less, 5 nm-1 or less, 4 nm-1 or less, 3.5 nm-1 or less or 3 nm-1 or less.

[0063] The FWHM (full width at half maximum) of the peak observed within the above range of the scattering vectors (q) may be from 0.2 nm-1 to 0.9 nm-1. In another embodiment, the FWHM may be 0.25 nm-1 or more, 0.3 nm-1 or more or 0.4 nm-1 or more. The FWHM may be, in another embodiment, 0.85 nm-1 or less, 0.8 nm-1 or less or 0.75 nm-1 or less.

[0064] The term "FWHM (full width at half maximum)" as used herein may refer to a width (difference between scattering vectors (q's)) of a peak showing an intensity half times as large as the maximum intensity. The method forming the FWHM is as described above.

[0065] The block copolymer showing the peak having the above FWHM within the above range of scattering vectors (q's) may include a crystalline portion suitable for the self assembling. The block copolymer showing the peak having the above FWHM within the above range of scattering vectors (q's) may show an excellent self assembling property.

[0066] The method for performing the XRD analysis to confirm the above parameter is as above.

[0067] In one embodiment of the present application, an absolute value of a difference between surface energies of the first and the second blocks may be 10 mN/m or less, 9 mN/m or less, 8 mN/m or less, 7.5 mN/m or less or 7 mN/m or less. The absolute value of the difference between surface energies may be 1.5 mN/m or more, 2 mN/m or more or 2.5 mN/m or more. The structure in which the first and the second blocks, the absolute value of the difference between the surface energies of which is within the above range, are linked via the covalent bond may realize an effective microphase separation by a phase separation due to appropriate uncompatibilities. In the above, the first block may be the block having the chain as described above.

[0068] The surface energy may be measured by using a drop shape analyzer (DSA100 product manufactured in KRUSS, Co.). Specifically, the surface energy may be measured with respect to a layer prepared by coating a coating solution prepared by diluting a sample (a block copolymer or a homopolymer) to be measured in fluorobenzene to a solid content of about 2 weight% on a substrate so as for the coated layer to have a thickness of 50 nm and a coated area of 4 cm2 (a width: 2 cm, a length: 2 cm); drying the coated layer for about an hour at the room temperature; and then performing a thermal annealing for about an hour at 160°C. On the layer after the thermal annealing is performed, deionized water of which the surface tension is known is dropped and then the contact angle is measured. The above process for obtaining the contact angle of the deionized water is repeated 5 times, and the average value of the 5 obtained contact angles are calculated. Identically, on the layer after the thermal annealing is performed, diiodomethane of which the surface tension is known is dropped and then the contact angle is measured. The above process for obtaining the contact angle of the diiodomethane is repeated 5 times, and the average value of the 5 obtained contact angles are calculated. After that, the surface energy may be obtained by substituting a value (Strom value) regarding the surface tension of the solvent through the Owens-Wendt-Rabel-Kaelble method using the obtained average values of the contact angles of the deionized water and the diiodomethane. The surface energy of each block in the block copolymer may be obtained by using the above described method with respect to a homopolymer prepared by monomers forming the corresponding block.

[0069] In case where the block copolymer comprises the above described chain, the block comprising the chain may have a larger surface energy than the other block. For example, if the first block comprises the chain, the first block may have a larger surface energy than the second block. In this case, the surface energy of the first block may be in a range from about 20 mN/m to about 40 mN/m. In another embodiment, the surface energy of the first block may be about 22 mN/m or more, about 24 mN/m or more, about 26 mN/m or more or about 28 mN/m or more. The surface energy of the first block may be about 38 mN/m or less, about 36 mN/m or less, about 34 mN/m or less or about 32 mN/m or less. Such a block copolymer including the above first block and showing the above difference between surface energies of blocks may show an excellent self assembling property.

[0070] In the block copolymer, an absolute value of a difference between densities of the first and the second blocks may be 0.25 g/cm3 or more, 0.3 g/cm3 or more, 0.35 g/cm3 or more, 0.4 g/cm3 or more or 0.45 g/cm3 or more. The absolute value of the difference between the densities may be 0.9 g/cm3 or less, 0.8 g/cm3 or less, 0.7 g/cm3 or less, 0.65 g/cm3 or less or 0.6 g/cm3 or less. The structure in which the first and the second blocks, the absolute value of the difference between the densities of which is within the above range, are linked via the covalent bond may realize an effective microphase separation by a phase separation due to appropriate uncompatibilities.

[0071] The density of each block in the block copolymer may be obtained through a known buoyancy method. For example, it may be obtained by analyzing a mass of a block copolymer in solvent such as ethanol, of which a mass and a density in the air are known.

[0072] In case where the block copolymer comprises the above described side chain, the block comprising the chain may have a lower density than the other block. For example, if the first block comprises the chain, the first block may have a lower density than the second block. In this case, the density of the first block may be in a range from about 0.9 g/cm3 to about 1.5 g/cm3. In another embodiment, the density of the first block may be about 0.95 g/cm3 or more. The density of the first block may be about 1.4 g/cm3 or less, about 1.3 g/cm3 or less, about 1.2 g/cm3 or less, about 1.1 g/cm3 or less or about 1.05 g/cm3 or less. Such a block copolymer including the above first block and showing the above difference between the densities of blocks may show an excellent self assembling property. The surface energy and the density are measured at the room temperature.

[0073] The block copolymer may include a block, of which a volume fraction is from 0.4 to 0.8, and a block, of which a volume fraction is from 0.2 to 0.6. In case where the block copolymer comprises the chain, the block having the chain may have the volume fraction from 0.4 to 0.8. For example, the first block comprises the chain, the first block may have the volume fraction from 0.4 to 0.8 and the second block may have the volume fraction from 0.2 to 0.6. The sum of the volume fractions of the first and the second blocks may be 1. The block copolymer including each block in the above volume fractions may show an excellent self assembling property. The volume fraction of each block of the block copolymer may be obtained by using the density of each block and a molecular weight obtained by the Gel Permeation Chromatograph (GPC).

[0074] The block copolymer may have, for example, a number average molecular weight (Mn) in a range from approximately 3,000 to 300,000. The term "number average molecular weight" as used herein may refer to a converted value with respect to the standard polystyrene measured by the GPC (Gel Permeation Chromatography). Unless defined otherwise, the term "molecular weight" as used herein may refer to the number average molecular weight. The molecular weight (Mn), in another embodiment, may be, for example, 3000 or more, 5000 or more, 7000 or more, 9000 or more, 11000 or more, 13000 or more or 15000 or more. The molecular weight (Mn), in another embodiment, may be, for example, 250000 or less, 200000 or less, 180000 or less, 160000 or less, 140000 or less, 120000 or less, 100000 or less, 90000 or less, 80000 or less, 70000 or less, 60000 or less, 50000 or less, 40000 or less, 30000 or less, or 25000 or less. The block copolymer may have the polydispersity (Mw/Mn) in a range from 1.01 to 1.60. In another embodiment, the polydispersity may be about 1.1 or more, about 1.2 or more, about 1.3 or more, or about 1.4 or more.

[0075] In the above range, the block copolymer may exhibit an appropriate self assembling property. The number average molecular weight and the like of the block copolymer may be controlled considering the objected self assembled structure.

[0076] If the block copolymer at least includes the first and second blocks, a ratio of the first block, for example, the block including the chain in the block copolymer may be in a range of 10 mole% to 90 mole%.

[0077] The present application relates to a polymer layer including the block copolymer. The polymer layer may be used in various applications. For example, it can be used in a biosensor, a recording media such as a flash memory, a magnetic storage media or the pattern forming method or an electric device or an electronic device, and the like.

[0078] In one embodiment, the block copolymer in the polymer layer may be forming a periodic structure including a sphere, a cylinder, a gyroid, or a lamella by the self assembly. For example, in one segment of the first block or the second block or other block linked to the above block via a covalent bond in the block copolymer, other segment may be forming the regular structure such as lamella form, cylinder form and the like. And the above structure may be aligned vertically.

[0079] The polymer layer may show the above in-plane phase diffraction pattern, i.e., the peak vertical to the X coordinate in the GISAXS diffraction pattern of the GISAXS analysis. In further embodiment, two or more peaks may be observed in the X coordinate of the GISAXS diffraction pattern. In case where two or more peaks are observed, the scattering vectors (the q values) may be confirmed with having constant ratios.

[0080] The present application relates also to a method for forming a polymer layer by using the block copolymer. The method may include forming a polymer layer including the block copolymer on a substrate in a self-assembled state. For example, the method may include forming a layer of the block copolymer or a coating solution in which the block copolymer is diluted in suitable solvent on the substrate by a coating and the like, and if necessary, then aging or heat-treating the layer.

[0081] The aging or the heat treatment may be performed based on, for example, a phase transition temperature or glass transition temperature of the block copolymer, and for example, may be performed at a temperature higher than the glass transition temperature or phase transition temperature. A time for the heat treatment is not particularly limited, and the heat treatment may be performed for approximately 1 minute to 72 hours, but may be changed if necessary. In addition, the temperature of the heat treatment of the polymer layer may be, for example, 100°C to 250°C, but may be changed in consideration of the block copolymer used herein.

[0082] The formed layer may be aged in a non-polar solvent and/or a polar solvent at the room temperature for approximately 1 minute to 72 hours.

[0083] The present application relates also to a pattern-forming method. The method may include selectively removing the first or second block of the block copolymer from a laminate comprising a substrate and a polymer layer that is formed on a surface of the substrate and that includes a self-assembled block copolymer. The method may be a method for forming a pattern on the above substrate. For example, the method may include forming the polymer layer on the substrate, selectively removing one block or two or more blocks of the block copolymer that is in the polymer layer; and then etching the substrate. By the above method, for example, nano-scaled micropattern may be formed. Further, according to shapes of the block copolymer in the polymer layer, various shapes of pattern such as nano-rod or nanohole can be formed by the above method. If necessary, in order to form a pattern, the block copolymer may be mixed with another copolymer or homopolymer. A kind of the substrate applied to this method may be selected without particular limitation, and, for example, silicon oxide and the like may be applied.

[0084] For example, according to the method, a nano-scale pattern of silicon oxide having a high aspect ratio may be formed. For example, various types of patterns such as a nanorod or nanohole pattern may be formed by forming the polymer layer on the silicon oxide, selectively removing any one block of the block copolymer in a state where the block copolymer in the polymer layer is formed in a predetermined structure, and etching the silicon oxide in various methods, for example, reactive ion etching. In addition, according to the above method, a nano pattern having a high aspect ratio can be formed.

[0085] For example, the pattern may be formed to a scale of several tens of nanometers, and such a pattern may be applied in various uses including a next-generation information electronic magnetic recording medium.

[0086] For example, a pattern in which nano structures, for example, nanowires, having a width of approximately 3 to 40 nm are disposed at an interval of approximately 6 to 80 nm may be formed by the above-described method. In another embodiment, a structure in which nanoholes having a width, for example, a diameter of approximately 3 to 40 nm are disposed at an interval of approximately 6 to 80 nm can be implemented.

[0087] In addition, in this structure, nanowires or nanoholes may be formed to have a high aspect ratio.

[0088] In this method, a method of selectively removing any one block of the block copolymer is not particularly limited, and for example, a method of removing a relatively soft block by irradiating a suitable electromagnetic wave, for example, ultra violet rays to a polymer layer may be used. In this case, conditions for ultra violet radiation may be determined according to a type of the block of the block copolymer, and ultra violet rays having a wavelength of approximately 254 nm may be irradiated for 1 to 60 minutes.

[0089] In addition, followed by the ultra violet radiation, the polymer layer may be treated with an acid to further remove a segment degraded by the ultra violet rays.

[0090] In addition, the etching of the substrate using the polymer layer from which a block is selectively removed may be performed by reactive ion etching using CF4/Ar ions, and followed by the above process, and removing the polymer layer from the substrate by oxygen plasma treatment may be further performed.

BRIEF DESCRIPTION OF FIGURES



[0091] 

Figs. 3 to 8 show SEM images of polymer layers.

Fig. 1 and 2 show GISAXS diffraction pattern.

Fig. 9 to 11 show SEM images of polymer layers.


EFFECTS



[0092] The present application may provide the block copolymers that have excellent self assembling and phase separation properties and therefore that can be effectively used in various applications. The present application may also provide applications of the block copolymers.

ILLUSTRATIVE EMBODIMENTS



[0093] Hereinafter, the present application will be described in detail with reference to Examples and Comparative Examples, but the scope of the present application is not limited to the following examples.

1. NMR ANALYSIS



[0094] The NMR analysis was performed at the room temperature by using a NMR spectrometer including a Varian Unity Inova (500 MHz) spectrometer having a triple resonance 5 mm probe. A sample to be analyzed was used after diluting it in solvent (CDCl3) for the NMR analysis to a concentration of approximately 10 mg/ml and a chemical shift (δ) was expressed in ppm.

<Abbreviation>



[0095] br = wide signal, s = singlet, d = doublet, dd = double doublet, t = triplet, dt = double triplet, q = quadruplet, p = quintuplet, m = multiplet

2. GPC(Gel Permeation Chromatograph)



[0096] The number average molecular weight and the polydispersity were measured by the GPC (Gel Permeation Chromatograph). In a 5 mL vial, a block copolymer or a macroinitiator to be measured of Example or Comparative Example and then diluted to a concentration of about 1 mg/mL. Then, the standard sample for a calibration and a sample to be analyzed were filtered by a syringe filter (pore size: 0.45 µm) and then analyzed. ChemStation from the Agilent technologies, Co. was used as an analysis program. The number average molecular weight (Mn) and the weight average molecular weight (Mw) were obtained by comparing an elution time of the sample with a calibration curve and then the polydispersity (PDI) was obtained from their ratio (Mw/Mn). The measuring condition of the GPC was as below.

<GPC Measuring Condition>



[0097] Device: a 1200 series from Agilent technologies, Co.
Column: two of PLgel mixed B from Polymer laboratories, Co. were used
Solvent: THF
Temperature of the column: 35°C
Concentration of Sample: 1 mg/mL, 200L injection
Standard Sample: Polystyrene (Mp: 3900000, 723000, 316500, 52200, 31400, 7200, 3940, 485)

3. GISAXS (Grazing Incidence Small Angle X ray Scattering)



[0098] The GISAXS analysis was performed in a 3C beam line of the Pohang Light Source. A coating solution was prepared by dissolving a block copolymer to be evaluated in fluorobenzene so as for a solid content to be 0.7 weight%, the coating solution was spin coated on a substrate so as to having a thickness of about 5 nm. The coating area was controlled to be about 2.25 cm2 (coated area: width = 1.5 cm, length = 1.5 cm). The coated layer was dried for about 1 hour at the room temperature and then subjected to the thermal annealing at about 160°C for about 1 hour so as for the phase separation structure to be realized. Therefore, the layer in which the phase separation structure was realized was formed. The formed layer was irradiated with X ray so as for an incident angle to be from about 0.12 degrees to 0.23 degrees, which corresponded to an angle between a critical angle of the layer and a critical angle of the substrate, and then the X ray diffraction pattern scattered from the layer was obtained by using a 2D marCCD. At this time, a distance from the layer to the detector was selected so as for the self assembled pattern in the layer to be effectively observed within a range from about 2 m to 3 m. As the substrate, a substrate (a silicone substrate that was treated with piranha solution and that has a wetting angle of about 5 degrees with respect to purified water at the room temperature) having the hydrophilic surface or a substrate (a silicone substrate that was treated with HMDS (hexamethyldisilazane) and that has a wetting angle of about 60 degrees with respect to purified water at the room temperature) having the hydrophobic surface was used.

4. XRD analysis (Method A)



[0099] The XRD pattern was evaluated by measuring the scattering intensity according to the scattering vector (q) by passing X ray through a sample in a 4C beam line of the Pohang Light Source. As the sample, powder obtained from the block copolymer to which any specific pre-treatment was not performed by purifying it so as to remove impurities therefrom was used after putting it in a cell for measurement of the XRD. During the XRD pattern analysis, as the X ray, X ray, a vertical size of which is 0.023 mm and a horizontal size of which is 0.3 mm was used and, as the detector, the measuring device (for example, 2D marCCD) was used. A 2D diffraction pattern scattered from the sample was obtained as an image. Information such as the scattering vectors and the FWHMs was obtained by analyzing the obtained diffraction pattern by the numerical analysis using the least square technique. The analysis was performed by the origin program. A position at which the XRD diffraction pattern had the lowest intensity became the baseline and the lowest intensity was converted to zero, and then the Gaussian fitting was performed with respect to the profile of peaks in the XRD pattern, and then the scattering vector (q) and the FWHM were obtained from the result of the Gaussian fitting. The R square of the Gaussian fitting was set to be 0.96 or more.

5. Surface energies measurement



[0100] The surface energy was measured by using the drop shape analyzer (DSA 100 product from KRUSS, Co.). The surface energy was evaluated with respect to the polymer layer formed by spin-coating a coating solution, which was prepared by dissolving the material to be evaluated in fluorobenzene so as for a solid content to be 2 weight%, on a silicone wafer so as for the coated layer to have a thickness of 50 nm (coated area: width = 2 cm, length = 2 cm) and drying it for about 1 hour at the room temperature and then subjecting it to the thermal annealing at about 160°C for about 1 hour. A process, in which deinonized water of which the surface tension is known was dropped on the layer after the thermal annealing and then its contact angle was obtained, was repeated 5 times, and an average value of the obtained 5 contact angles was calculated. Identically, a process, in which diiodomethane of which the surface tension is known was dropped on the layer after the thermal annealing and then its contact angle was obtained, was repeated 5 times, and an average value of the obtained 5 contact angles was calculated. The surface energy was obtained by the Owens-Wendt-Rabel-Kaelble method by using the obtained average values of the contact angles of the deionized water and the diiodomethane and substituting a value (the Strom value) regarding the surface tension of solvent. The surface energy of each block of the block copolymer was obtained as above with respect to a homopolymer prepared only by monomers forming the block.

6. Volume fraction measurement



[0101] The volume fraction of each block of the block copolymer was calculated based on a molecular weight measured by a GPC (Gel Permeation Chromatogrph) and the density at the room temperature. In the above, the density was measured by the buoyancy method, specifically, was calculated by a mass of a sample to be measured in solvent (ethanol), of which a mass and a density in the air are known.

Preparation Example 1. Synthesis of a Monomer (A)



[0102] A compound (DPM-C12) of the Formula A below was synthesized by the below method. To a 250 mL flask, hydroquinone (10.0 g, 94.2 mmole) and 1-bromododecane (23.5 g, 94.2 mmole) were added and dissolved in 100 mL acetonitrile, an excessive amount of potassium carbonate was added thereto and then the mixture was reacted at 75°C for approximately 48 hours under nitrogen. After the reaction, remaining potassium carbonate and acetonitrile used for the reaction were removed. The work up was performed by adding a mixed solvent of dichloromethane (DCM) and water, and separated organic layers were collected and dehydrated through MgSO4. Subsequently, a white solid intermediate was obtained with a yield of approximately 37 % using DCM through column chromatography.

< NMR analysis result of the intermediate>



[0103] 1H-NMR(CDCl3): δ6.77(dd, 4H); δ4.45(s, 1H); δ3.89(t, 2H); δ1.75(p, 2H); δ1.43(p, 2H); δ1.33-1.26(m, 16H); δ0.88(t, 3H)

[0104] The synthesized intermediate (9.8 g, 35.2 mmole), methacrylic acid (6.0 g, 69.7 mmole), dicyclohexylcarbodiimide (DCC; 10.8 g, 52.3 mmole) and p-dimethylaminopyridine (DMPA; 1.7 g, 13.9 mmol) were put into a flask, 120 ml of methylenechloride was added, and a reaction was performed at the room temperature for 24 hours under nitrogen. After the reaction was completed, a urea salt produced in the reaction was removed through a filter, and remaining methylenechloride was also removed. Impurities were removed using hexane and DCM (dichloromethane) as mobile phases though column chromatography, and the obtained product was recrystallized in a mixed solvent of methanol and water (mixed in 1:1 weight ratio), thereby obtaining a white solid product (DPM-C12)(7.7 g, 22.2 mmol) with a yield of 63 %.

<NMR analysis result>



[0105] 1H-NMR(CDCl3): δ7.02(dd, 2H); δ6.89(dd, 2H); δ6.32(dt, 1H); δ5.73(dt, 1H); δ3.94(t, 2H); δ2.05(dd, 3H); δ1.76(p, 2H); δ1.43(p, 2H); 1.34-1.27(m, 16H); δ0.88(t, 3H)



[0106] In the above, the R is a linear alkyl having 12 carbon atoms.

Preparation Example 2. Synthesis of a Monomer (G)



[0107] A compound of the Formula G below was synthesized according to the method of Preparation Example 1, except that 1-bromobutane was used instead of the 1-bromododecane. The NMR analysis result with respect to the above compound is as below.

<NMR analysis result with respect to DPM-C4>



[0108] 1H-NMR(CDCl3): δ7.02(dd, 2H); δ6.89(dd, 2H); δ6.33(dt, 1H); δ5.73(dt, 1H); δ3.95(t, 2H); δ2.06(dd, 3H); δ1.76(p, 2H); δ1.49(p, 2H); δ0.98(t, 3H)



[0109] In the above, the R is a linear alkyl having 4 carbon atoms.

Preparative Example 3. Synthesis of a Monoer (B)



[0110] A compound of the Formula B below was synthesized according to the method of Preparation Example 1, except that 1-bromooctane was used instead of the 1-bromododecane. The NMR analysis result with respect to the above compound is as below.

<NMR analysis result with respect to DPM-C8>



[0111] 1H-NMR(CDCl3): δ7.02(dd, 2H); δ6.89(dd, 2H); δ6.32(dt, 1H); δ5.73(dt, 1H); δ3.94(t, 2H); δ2.05(dd, 3H); δ1.76(p, 2H); δ1.45(p, 2H); 1.33-1.29(m, 8H); δ0.89(t, 3H)



[0112] In the above, the R is a linear alkyl having 8 carbon atoms.

Preparation Example 4. Synthesis of a Monomer (C)



[0113] A compound (DPM-C10) of the Formula C below was synthesized according to the method of Preparation Example 1, except that 1-bromodecane was used instead of the 1-bromododecane. The NMR analysis result with respect to the above compound is as below.

<NMR analysis result with respect to DPM-C10>



[0114] 1H-NMR(CDCl3): δ7.02(dd, 2H); δ6.89(dd, 2H); δ6.33(dt, 1H); δ5.72(dt, 1H); δ3.94(t, 2H); δ2.06(dd, 3H); δ1.77(p, 2H); δ1.45(p, 2H); 1.34-1.28(m, 12H); δ0.89(t, 3H)



[0115] In the above, the R is a linear alkyl having 10 carbon atoms.

Preparation Example 5. Synthesis of a Monomer (D)



[0116] A compound of the Formula D below was synthesized according to the method of Preparation Example 1, except that 1-bromotetradecane was used instead of the 1-bromododecane. The NMR analysis result with respect to the above compound is as below.

<NMR analysis result with respect to DPM-C14>



[0117] 1H-NMR(CDCl3): δ7.02(dd, 2H); δ6.89(dd, 2H); δ6.33(dt, 1H); δ5.73(dt, 1H); δ3.94(t, 2H); δ2.05(dd, 3H); δ1.77(p, 2H); δ1.45(p, 2H); 1.36-1.27(m, 20H); δ0.88(t, 3H.)



[0118] In the above, the R is a linear alkyl having 14 carbon atoms.

Preparation Example 6. Synthesis of a Monomer (E)



[0119] A compound of the Formula E below was synthesized according to the method of Preparation Example 1, except that 1-bromohexadecane was used instead of the 1-bromododecane. The NMR analysis result with respect to the above compound is as below.

<NMR analysis result with respect to DPM-C16>



[0120] 1H-NMR(CDCl3): δ7.01(dd, 2H); δ6.88(dd, 2H); δ6.32(dt, 1H); δ5.73(dt, 1H); δ3.94(t, 2H); δ2.05(dd, 3H); δ1.77(p, 2H); δ1.45(p, 2H); 1.36-1.26(m, 24H); δ0.89(t, 3H)



[0121] In the above, the R is a linear alkyl having 16 carbon atoms.

Example 1



[0122] 2.0 g of the compound (DPM-C12) of Preparation Example 1, 64 mg of RAFT (Reversible Addition-Fragmentation chain transfer) reagent (cyanoisopropyl dithiobenzoate), 23 mg of AIBN (azobisisobutyronitrile) and 5.34 mL of benzene were added to a 10 mL flask and then were stirred at the room temperature for 30 minutes and then the RAFT (reversible addition fragmentation chain transfer) polymerization was performed at 70°C for 4 hours. After the polymerization, the reacted solution was precipitated in 250 mL of methanol that was an extraction solvent, was vacuum filtered and dried so as to obtain pink macroinitiator. The yield of the macroinitiator was about 86%, and its number average molecular weight (Mn) and polydispersity (Mw/Mn) were 9,000 and 1.16, respectively.

[0123] 0.3 g of the macroinitiator, 2.7174 g of pentafluorostyrene and 1.306 mL of benzene were added to a 10 mL Schlenk flask and then were stirred at the room temperature for 30 minutes and then the RAFT (reversible addition fragmentation chain transfer) polymerization was performed at 115°C for 4 hours. After the polymerization, the reacted solution was precipitated in 250 mL of methanol that was an extraction solvent, was vacuum filtered and dried so as to obtain light pink block copolymer. The yield of the block copolymer was about 18%, and its number average molecular weight (Mn) and polydispersity (Mw/Mn) were 16,300 and 1.13, respectively. The block copolymer includes the first block derived from the monomer (A) of Preparation Example 1 and the second block derived from the pentafluorostyrene.

Example 2



[0124] A block copolymer was prepared by the same method as in Example 1 except that a macroinitiator prepared by using the monomer (B) of Preparation Example 3 instead of the monomer (A) of Preparation Example 1 and pentafluorostyrene were used. The block copolymer includes the first block derived from the monomer (B) of Preparation Example 3 and the second block derived from the pentafluorostyrene.

Example 3



[0125] A block copolymer was prepared by the same method as in Example 1 except that a macroinitiator prepared by using the monomer (C) of Preparation Example 4 instead of the monomer (A) of Preparation Example 1 and pentafluorostyrene were used. The block copolymer includes the first block derived from the monomer (C) of Preparation Example 4 and the second block derived from the pentafluorostyrene.

Example 4



[0126] A block copolymer was prepared by the same method as in Example 1 except that a macroinitiator prepared by using the monomer (D) of Preparation Example 5 instead of the monomer (A) of Preparation Example 1 and pentafluorostyrene were used. The block copolymer includes the first block derived from the monomer (D) of Preparation Example 5 and the second block derived from the pentafluorostyrene.

Example 5



[0127] A block copolymer was prepared by the same method as in Example 1 except that a macroinitiator prepared by using the monomer (E) of Preparation Example 6 instead of the monomer (A) of Preparation Example 1 and pentafluorostyrene were used. The block copolymer includes the first block derived from the monomer (E) of Preparation Example 6 and the second block derived from the pentafluorostyrene.

Comparative Example 1



[0128] A block copolymer was prepared by the same method as in Example 1 except that a macroinitiator prepared by using the monomer (G) of Preparation Example 2 instead of the monomer (A) of Preparation Example 1 and pentafluorostyrene were used. The block copolymer includes the first block derived from the monomer (G) of Preparation Example 2 and the second block derived from the pentafluorostyrene.

Comparative Example 2



[0129] A block copolymer was prepared by the same method as in Example 1 except that a macroinitiator prepared by using 4-methoxyphenyl methacrylate instead of the monomer (A) of Preparation Example 1 and pentafluorostyrene were used. The block copolymer includes the first block derived from the 4-methoxyphenyl methacrylate and the second block derived from the pentafluorostyrene.

Comparative Example 3



[0130] A block copolymer was prepared by the same method as in Example 1 except that a macroinitiator prepared by using dodecyl methacrylate instead of the monomer (A) of Preparation Example 1 and pentafluorostyrene were used. The block copolymer includes the first block derived from the dodecyl methacrylate and the second block derived from the pentafluorostyrene.

[0131] The GPC results regarding the macroinitiator and the block copolymer of the Examples are stated in Table 1.
Table 1
 ExamplesCom. Examples
12345123
MI Mn 9000 9300 8500 8700 9400 9000 7800 8000
PDI 1.16 1.15 1.17 1.16 1.13 1.16 1.17 1.19
BCP Mn 16300 19900 17100 17400 18900 18800 18700 16700
PDI 1.13 1.20 1.19 1.17 1.17 1.22 1.25 1.18
MI: the macroinitiator
BCP: the block copolymer
Mn: the number average molecular weight
PDI: the polydispersity

Test Example 1. XRD analysis



[0132] The result of the XRD analysis performed regarding the block copolymer according to the above method is stated in Table 2 below (In case of the Comparative Example 3, no peak was observed in a range of the scattering vectors from 0.5 nm-1 to 10 nm-1).
Table 2
 Exs.Com. Exs.
12345123
Chain-forming atoms 12 8 10 14 16 4 1 12
n/D 3.75 3.08 3.45 4.24 4.44 2.82 1.98 -
the q value (unit: nm-1) 1.96 2.41 2.15 1.83 1.72 4.42 3.18 -
FWHM (unit: nm-1) 0.57 0.72 0.63 0.45 0.53 0.97 1.06 -
The q value: the scattering vector
The chain-forming atoms: the number of the chain-forming atoms in the first block n/D: the value calculated by the formula (nq/(2×π)) (n: the number of the chain-formingatoms, q is the scattering vector which is within a range from 0.5 nm-1 to 10 nm-1 at which and at which a peak having the largest area is observed within the above range of the scattering vectors)

Test Example 2. Self assembling property measurement



[0133] The self assembled polymer layer was obtained by spin coating a coating solution prepared by dissolving the block copolymer of Examples or Comparative Examples in fluorobenzene to a solid content of about 0.7 weight% on a silicone wafer so as for a coated thickness to be 5 nm (a coated area: a width×a length = 1.5cm×1.5cm), and drying it for 1 hour at the room temperature and then subjecting it to a thermal annealing for 1 hour at about 160°C. Then, a SEM (scanning electron microscope) image of the formed polymer layer was obtained. Figs. 3 to 7 are results of Examples 1 to 5, respectively. As confirmed from Figures, in case of the block copolymers of Examples, self assembled polymer layer having line patterns are effectively formed. However, an appropriate phase separation was not realized in Comparative Example. For example, Fig. 8 is the SEM result of Comparative Example 3, and it is confirmed that effective phase separation was not realized.

Test Example 2. GISAXS diffraction pattern confirmation



[0134] Fig. 1 shows the result of the GISAXS (Grazing Incident Small Angle X ray Scattering) analysis of the block copolymer of Example 1 performed with respect to the hydrophilic surface of which a contact angle at the room temperature with respect to the purified water was about 5 degrees, and Fig. 2 shows the result of the GISAXS (Grazing Incident Small Angle X ray Scattering) analysis of the block copolymer of Example 1 performed with respect to the hydrophobic surface of which a contact angle at the room temperature with respect to the purified water was about 60 degrees. From Figs. 1 and 2, it can be confirmed that the in-plane phase diffraction patterns are observed in any case. From the above, it can be confirmed that the block copolymer can show the vertical aligning properties with respect to various substrates.

[0135] Further, by using the block copolymer of Example 1, polymer layers were formed by the same method as described above. The polymer layers were formed on a silicone substrate that was treated with the piranha solution that had a contact angle of 5 degrees of the purified water at the room temperature, a silicone oxide substrate that had a contact angle of 45 degrees of the purified water at the room temperature and a HMDS (hexamethyldisilazane) treated silicone substrate that had a contact angle of 60 degrees of the purified water at the room temperature, respectively. Figs. 9 to 11 are the SEM images regarding the polymer layers on the surface having the contact angles of 5 degrees, 45 degrees and 60 degrees, respectively. From the Figures, it can be confirmed that the block copolymer forms the phase separation structure irrespective of surface properties of substrates.

Test Example 3. Properties measurement of block copolymers



[0136] The results of evaluations regarding each block copolymer measured as above method are stated in the below Table.
Table 3
 Exs.Com. Exs.Ref.
123451 23
The first Block SE 30.83 31.46 27.38 26.924 27.79 37.37 48.95 19.1 38.3
De 1 1.04 1.02 0.99 1.00 1.11 1.19 0.93 1.05
VF 0.66 0.57 0.60 0.61 0.61 0.73 0.69 0.76 -
The Second Block SE 24.4 24.4 24.4 24.4 24.4 24.4 24.4 24.4 41.8
De 1.57 1.57 1.57 1.57 1.57 1.57 1.57 1.57 1.18
VF 0.34 0.43 0.40 0.39 0.39 0.27 0.31 0.24 -
Difference of SE 6.43 7.06 2.98 2.524 3.39 12.98 24.55 5.3 3.5
Difference of De 0.57 0.53 0.55 0.58 0.57 0.46 0.38 0.64 0.13
SE: surface energy (unit: mN/m)
De: density (unit: g/cm3)
VF: volume fraction Difference of SE: the absolute value of the difference between the surface energies of the first and the second block Difference of De: the absolute value of the difference between the densities of the first and the second block Ref.: Polystyrene-polymethylmethacrylate block copolymer (the first block: polystyrene block, the second block: polymethylmethacrylate block)

Test Example 4.



[0137] Further, block copolymers having different volume fractions were prepared according to the same method as in Example 1, except that the molar ratios of the monomers and the macroinitiators were controlled.

[0138] The volume fractions are as below.
Table 4
 Volume fraction of the first blockVolume fraction of the second block
Sample 1 0.7 0.3
Sample 2 0.59 0.41
Sample 3 0.48 0.52


[0139] The volume fraction of each block of the block copolymer was calculated based on a molecular weight measured by a GPC (Gel Permeation Chromatogrph) and the density at the room temperature. In the above, the density was measured by the buoyancy method, specifically, was calculated by a mass in solvent (ethanol), of which a mass and a density in the air are known, and the GPC was performed according to the above described method.

[0140] The polymer layer was obtained by spin coating a coating solution prepared by dissolving the block copolymer of each sample in fluorobenzene to a solid content of about 0.7 weight% on a silicone wafer so as for a coated thickness to be 5 nm (a coated area: a width = 1.5 cm, a length = 1.5cm), and drying it for 1 hour at the room temperature and then subjecting it to a thermal annealing for 1 hour at about 160°C. Then, the GISAXS was performed, and it can be confirmed that the in-plane phase diffraction pattern is observed and the block copolymer has the vertical aligning property.


Claims

1. A block copolymer comprising a first block represented by Formula 1 below and a second block represented by Formula 3 below:

wherein R is hydrogen or an alkyl group having 1 to 4 carbon atoms; X is a carbonyl group, -C(=O)-X1- or -X1-C(=O)-, wherein X1 is an oxygen atom, a sulfur atom or -S(=O)2-; and Y is a monovalent substituent comprising an aromatic structure which has 6 to 12 carbons atoms and to which a side chain having 8 or more chain-forming atoms is linked,

wherein X2 is a single bond, an oxygen atom, a sulfur atom or -S(=O)2-; and W is an aryl group which has 6 to 13 carbon atoms and which comprises at least one halogen atom,
wherein the number (n) of chain-forming atoms of the side chain satisfies equation 1 below:

wherein "n" is the number of the chain-forming atoms, and "q" is the smallest scattering vector among scattering vectors at which peaks are observed in the X ray diffraction analysis or a scattering vector at which a peak having the largest area is observed, the X ray diffraction analysis being performed in accordance with method A as defined in the description.
 
2. A block copolymer according to Claim 1, wherein the scattering vector in equation 1 is from 1 nm-1 to 3 nm-1.
 
3. A block copolymer according to Claim 1, wherein a volume fraction of the first block is from 0.4 to 0.8, a volume fraction of the second block is from 0.2 to 0.6 and the sum of the volume fractions of the first and second blocks is 1.
 
4. A block copolymer according to Claim 1, wherein, in Formula 1, the side chain is a linear chain and is linked to the aromatic structure via an oxygen atom or a nitrogen atom.
 
5. A block copolymer according to Claim 1, wherein, in Formula 3, the halogen atom is a fluorine atom.
 
6. A block copolymer according to Claim 1, wherein, in Formula 1, the aromatic structure does not have a halogen atom and the side chain is a linear chain that is linked to the aromatic structure via an oxygen atom or a nitrogen atom.
 
7. A block copolymer according to Claim 1, wherein its number average molecular weight is from 3,000 to 300,000.
 
8. A block copolymer according to Claim 1, wherein its polydispersity (Mw/Mn) is from 1.01 to 1.60.
 
9. A polymer layer comprising a self assembled product of the block copolymer as defined in Claim 1.
 
10. A polymer layer according to Claim 9, wherein it exhibits an in-plane phase diffraction pattern in a grazing incidence small angle X ray scattering.
 
11. A method for forming a polymer layer, the method comprising forming the polymer layer comprising a self assembled product of the block copolymer as defined in Claim 1.
 
12. A pattern-forming method comprising selectively removing the first block or the second block of the block copolymer from a laminate comprising a substrate and a polymer layer that is formed on the substrate and that comprises a self-assembled product of the block copolymer as defined in Claim 1.
 


Ansprüche

1. Blockcopolymer, umfassend einen durch die nachstehende Formel 1 dargestellten ersten Block und einen durch die nachstehende Formel 3 dargestellten zweiten Block:

worin R Wasserstoff oder eine Alkylgruppe mit 1 bis 4 Kohlenstoffatomen ist, X eine Carbonylgruppe, -C(=O)-X1- oder -X1-C(=O)- ist, wobei X1 ein Sauerstoffatom, ein Schwefelatom oder -S(=O)2- ist, und Y ein monovalenter Substituent ist, der eine aromatische Struktur umfasst, die 6 bis 12 Kohlenstoffatomen aufweist und an die eine Seitenkette mit 8 oder mehr kettenbildenden Atomen geknüpft ist,

worin X2 eine Einfachbindung, ein Sauerstoffatom, ein Schwefelatom oder -S(=O)2- ist und W eine Arylgruppe ist, die 6 bis 13 Kohlenstoffatome aufweist und die mindestens ein Halogenatom umfasst,
wobei die Zahl (n) der kettenbildenden Atome der Seitenkette die nachstehende Gleichung 1 erfüllt:

worin "n" die Zahl der kettenbildenden Atome und "q" der kleinste Streuvektor unter Streuvektoren, bei denen Peaks in einer Röntgenbeugungsanalyse beobachtet werden, oder ein Streuvektor ist, bei dem ein Peak mit der größten Fläche beobachtet wird, wobei die Röntgenbeugungsanalyse gemäß dem in der Beschreibung definierten Verfahren A durchgeführt wird.
 
2. Blockcopolymer gemäß Anspruch 1, wobei der Streuvektor in Gleichung 1 1 nm-1 bis 3 nm-1 beträgt.
 
3. Blockcopolymer gemäß Anspruch 1, wobei ein Volumenanteils des ersten Blocks 0,4 bis 0,8 beträgt, ein Volumenanteil des zweiten Blocks 0,2 bis 0,6 beträgt und die Summe der Volumenanteile des ersten und zweiten Blocks 1 ist.
 
4. Blockcopolymer gemäß Anspruch 1, wobei in Formel 1 die Seitenkette eine lineare Kette ist und an die aromatische Struktur über ein Sauerstoffatom oder ein Stickstoffatom geknüpft ist.
 
5. Blockcopolymer gemäß Anspruch 1, wobei in Formel 3 das Halogenatom ein Fluoratom ist.
 
6. Blockcopolymer gemäß Anspruch 1, wobei in Formel 1 die aromatische Struktur kein Halogenatom aufweist und die Seitenkette eine lineare Kette ist, die an die aromatische Struktur über ein Sauerstoffatom oder ein Stickstoffatom geknüpft ist.
 
7. Blockcopolymer gemäß Anspruch 1, wobei sein zahlengemitteltes Molekulargewicht 3.000 bis 300.000 beträgt.
 
8. Blockcopolymer gemäß Anspruch 1, wobei seine Polydispersität (Mw/Mn) 1,01 bis 1,60 beträgt.
 
9. Polymerschicht, umfassend ein selbstorganisiertes Produkt des in Anspruch 1 definierten Blockcopolymers.
 
10. Polymerschicht gemäß Anspruch 9, die Beugungsmuster der In-Plane-Phase in einer Kleinwinkel-Röntgenstreuung unter streifendem Einfall aufweist.
 
11. Verfahren zur Bildung einer Polymerschicht, wobei das Verfahren die Bildung einer Polymerschicht umfasst, die ein selbstorganisiertes Produkt des in Anspruch 1 definierten Blockcopolymers umfasst.
 
12. Musterbildungsverfahren, umfassend die selektive Entfernung des ersten Blocks oder des zweiten Blocks des Blockcopolymers von einem Laminat, das ein Substrat und eine Polymerschicht umfasst, die auf dem Substrat gebildet ist und die ein selbstorganisiertes Produkt des in Anspruch 1 definierten Blockcopolymers umfasst.
 


Revendications

1. Copolymère séquencé comprenant une première séquence représentée par la formule 1 ci-dessous et une seconde séquence représentée par la formule 3 ci-dessous :

dans laquelle R est un hydrogène ou un groupe alkyle ayant 1 à 4 atomes de carbone ; X est un groupe carbonyle, -C(=O)-X1- ou -X1-C(=O)-, dans laquelle X1 est un atome d'oxygène, un atome de soufre ou -S(=O)2-; et Y est un substituant monovalent comprenant une structure aromatique qui a 6 à 12 atomes de carbone et à laquelle une chaîne latérale ayant 8 atomes de formation de chaîne ou plus est liée,

dans laquelle X2 est une liaison simple, un atome d'oxygène, un atome de soufre ou -S(=O)2- ; et W est un groupe aryle qui a 6 à 13 atomes de carbone et qui comprend au moins un atome d'halogène,
dans lequel le nombre (n) d'atomes de formation de chaîne de la chaîne latérale satisfait à l'équation 1 ci-dessous :

dans laquelle « n » est le nombre d'atomes de formation de chaîne, et « q » est le plus petit vecteur de diffusion parmi les vecteurs de diffusion auquel des pics sont observés dans l'analyse de diffraction des rayons X ou un vecteur de diffusion auquel un pic ayant la plus grande aire est observé, l'analyse de diffraction des rayons X étant réalisée conformément au procédé A tel que défini dans la description.
 
2. Copolymère séquencé selon la revendication 1, dans lequel le vecteur de diffusion dans l'équation 1 est de 1 nm-1 à 3 nm-1.
 
3. Copolymère séquencé selon la revendication 1, dans lequel une fraction volumique de la première séquence est de 0,4 à 0,8, et une fraction volumique de la seconde séquence est de 0,2 à 0,6, et la somme des fractions volumiques des première et seconde séquences est 1.
 
4. Copolymère séquencé selon la revendication 1, dans lequel, dans la formule 1, la chaîne latérale est une chaîne linéaire et est liée à la structure aromatique via un atome d'oxygène ou un atome d'azote.
 
5. Copolymère séquencé selon la revendication 1, dans lequel, dans la formule 3, l'atome d'halogène est un atome de fluor.
 
6. Copolymère séquencé selon la revendication 1, dans lequel, dans la formule 1, la structure aromatique n'a pas d'atome d'halogène et la chaîne latérale est une chaîne linéaire qui est liée à la structure aromatique via un atome d'oxygène ou un atome d'azote.
 
7. Copolymère séquencé selon la revendication 1, dans lequel le poids moléculaire moyen en nombre est de 3 000 à 300 000.
 
8. Copolymère séquencé selon la revendication 1, dans lequel sa polydispersité (Mw/Mn) est de 1,01 à 1,60.
 
9. Couche polymère comprenant un produit auto-assemblé du copolymère séquencé selon la revendication 1.
 
10. Couche polymère selon la revendication 9, dans laquelle elle présente un motif de diffraction de phase dans le plan en diffusion de rayons X aux petits angles en incidence rasante.
 
11. Procédé de formation d'une couche polymère, le procédé comprenant la formation de la couche polymère comprenant un produit auto-assemblé du copolymère séquencé selon la revendication 1.
 
12. Procédé de formation de motif comprenant le retrait sélectif de la première séquence ou de la seconde séquence du copolymère séquencé d'un stratifié comprenant un substrat et une couche polymère qui est formée sur le substrat et qui comprend un produit auto-assemblé du copolymère séquencé selon la revendication 1.
 




Drawing


























Cited references

REFERENCES CITED IN THE DESCRIPTION



This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

Patent documents cited in the description




Non-patent literature cited in the description