(51)International Patent Classification (IPC): 
H01M 2/02(2006.01)
H01M 10/0525(2010.01)
H01M 10/058(2010.01)
H01M 2/36(2006.01)
H01M 10/0566(2010.01)
(86)International application number:
PCT/JP2015/075162
(87)International publication number:
WO 2016/052074 (07.04.2016 Gazette  2016/14)

(54)

LITHIUM-ION SECONDARY BATTERY AND METHODS FOR MANUFACTURING THE SAME

LITHIUM-IONEN-SEKUNDÄRBATTERIE UND VERFAHREN ZUR HERSTELLUNG DERSELBEN

BATTERIE SECONDAIRE LITHIUM-ION ET SES PROCÉDÉS DE FABRICATION


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 30.09.2014 JP 2014199839
18.11.2014 JP 2014233944

(43)Date of publication of application:
09.08.2017 Bulletin 2017/32

(73)Proprietor: Envision AESC Energy Devices Ltd.
Sagamihara-shi, Kanagawa (JP)

(72)Inventors:
  • OHTA, Tomoyuki
    Sagamihara-shi Kanagawa 252-5298 (JP)
  • YANAGISAWA, Ryota
    Sagamihara-shi Kanagawa 252-5298 (JP)
  • SUZUKI, Takayuki
    Sagamihara-shi Kanagawa 252-5298 (JP)

(74)Representative: Vossius & Partner Patentanwälte Rechtsanwälte mbB 
Siebertstrasse 3
81675 München
81675 München (DE)


(56)References cited: : 
EP-A1- 2 503 634
JP-A- H0 785 889
JP-A- 2002 184 462
JP-A- 2007 328 952
JP-A- 2013 045 759
JP-A- 2013 164 915
CN-U- 202 678 453
JP-A- S5 918 580
JP-A- 2007 165 111
JP-A- 2008 091 065
JP-A- 2013 058 377
US-A1- 2009 191 457
  
      
    Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


    Description

    Technical Field



    [0001] The present invention relates to a lithium ion secondary battery and a method for manufacturing the same.

    Background Art



    [0002] Secondary batteries are widely used as a power source for portable devices such as cellular phones, digital cameras, and laptop computers, and are becoming common as a power source for vehicles and household use in recent years. Especially, lithium ion secondary batteries, which have high energy density and are lightweight, have become an energy storage device essential for life.

    [0003] A lithium ion secondary battery has a structure in which a positive electrode sheet and a negative electrode sheet as electrode elements are separated by a separator. Each of the positive electrode sheet and the negative electrode sheet includes a portion with an electrode coating, formed by applying a combined agent containing an active material, a binder, and a conductive aid, etc., onto a current collector, and a portion with no electrode coating, onto which a combined agent has not been applied to be connected to an electrode terminal. These are contained together with an electrolytic solution in an outer case and the outer case is sealed. A positive electrode terminal and a negative electrode terminal are electrically connected at one end to the portion with no electrode coating of the positive electrode sheet and the portion with no electrode coating of the negative electrode sheet, respectively, and the other ends of the positive electrode terminal and the negative electrode terminal are extracted to the outside of the outer case.

    [0004] For the outer case, flexible films including an aluminum sheet or the like with a thickness of tens to hundreds microns are frequently employed as a means for weight saving for a battery. Although flexible films are excellently lightweight, it is disadvantageous that they have strength lower than metal can cases with a large thickness and are vulnerable to an impact from the outside, and in addition the outer case swells significantly when a gas is generated from the battery element or electrolytic solution contained in the container.

    [0005] Accordingly, techniques to remove NH3 or H2 present in an electrolytic solution in a step of manufacturing an electrolytic solution have been proposed.

    [0006] For example, Patent Literature 1 describes removal of a residual impurity (an unreacted material and a by-product) in a method for manufacturing an electrolytic solution containing LiPF6, and discloses that, in the case that the residual impurity is a volatile substance or a gas, the impurity is removed through flowing an inert gas or vacuum treatment.

    Citation List


    Patent Literature



    [0007] Patent Literature 1: JP7-85889A

    [0008] CN 202678453 U refers to a vacuum liquid injection device for a cylindrical lithium battery. EP 2 503 634 A1 refers to a lithium ion secondary battery exhibiting a high capacity retention rate over a long period. US 2009/191457A1 refers to a method of manufacturing a lithium-ion secondary battery including an electrolytic solution making step of making an electrolytic solution by mixing at least an organic solvent and an electrolytic salt together, an electrode insertion step of inserting an anode and a cathode into an outer case, and a liquid injection step of injecting the electrolytic solution into the outer case; wherein the electrolytic solution making step or the liquid injection step adds a compound having an alkyl group with a carbon number of 10 or greater and an epoxy, vinyl, or silanol group at a terminal to the electrolytic solution. JP S 59 18580 A refers to a dope-undope type battery, which, in order to decrease self discharge, is manufactured by blowing inactive gas in an electrolyte solution in which an electrode is immersed. JP 2008-091065 A refers to a method, by which it is evacuated into a prescribed vacuum degree in the battery case, a temporary liquid storing chamber of an injection hopper in which a prescribed amount of an organic electrolytic solution is evacuated into the vacuum degree that a pressure difference higher by a prescribed value to a pressure in the battery case is generated, and by opening an injection port of the injection hopper, the organic electrolytic solution of the temporary liquid storing chamber is injected into the battery case via the injection port and the injection nozzle by the pressure difference. JP 2007-165111 A refers to a layered lithium manganese oxide of 5 wt.% to 40 wt.% being mixed with the spinel manganese oxide of the positive electrode to thereby suppress degradation from storage at high temperatures and also achieve safety under overcharge. JP 2007-328952 A refers to a non-aqueous electrolyte battery being equipped with an outer package material, non-aqueous electrolyte, positive electrode layer, positive electrode current collector, positive electrode tab in which a part of the positive electrode current collector is extended, positive electrode reed of which one end is connected to the positive electrode tab and the other end is extended to the outside of the outer package material, negative electrode layer including a negative electrode active material of which lithium storage and release potential is richer than 0.4 V (vs Li/Li+), negative electrode current collector, negative electrode tab in which a part of the negative electrode current collector is extended, and negative electrode reed of which one end is connected to the negative electrode tab and the other end is extended to the outside of the outer package material. JP 2002-184462 A refers to a nonaqueous electrolyte secondary battery including a jacket with a thickness X of not more than 0.3 mm and a nonaqueous electrolyte containing a nonaqueous solvent and an electrolyte.

    Summary of Invention


    Technical Problem



    [0009] If a technique to remove an impurity is used in a step of manufacturing an electrolytic solution, as described in Patent Literature 1, impurities such as NH3 and H2 in an electrolytic solution can be temporarily removed. However, moisture, nitrogen, carbon dioxide, or the like in a gas contacting with an electrolytic solution thus obtained dissolves in the electrolytic solution before injecting the electrolytic solution into a battery. Thus, it was difficult to prevent the occurrence of problems such as the swelling of a battery due to an impurity in an electrolytic solution only by removal of an impurity in a step of manufacturing an electrolytic solution.

    [0010] In transporting an electrolytic solution contained in a container, the container is typically filled with nitrogen gas to prevent moisture contamination, and particularly in this case, a large amount of nitrogen disadvantageously dissolves in the electrolytic solution. If an electrolytic solution containing dissolved nitrogen is used in manufacturing a battery, the dissolved nitrogen becomes into bubbles to cause the cell to swell in high temperature aging, and lowering of safety is expected to be caused. When the electrodes are vacuum-impregnated with an electrolytic solution after injection into a cell, the dissolved nitrogen to generate bubbles in the electrolytic solution by degassing, and the bubbles may attach to a sealing portion to degrade the sealing properties.

    [0011] An object of the present invention is to provide a lithium ion secondary battery to solve the above problems, and a method for manufacturing the lithium ion secondary battery.

    Solution to Problem



    [0012] The invention is defined in the independent claims. Dependent claims refer to preferred embodiments.

    [0013] A method for manufacturing a lithium ion secondary battery according to one aspect of the present invention is a method for manufacturing a lithium ion secondary battery, the lithium ion secondary battery including a positive electrode and a negative electrode disposed with a separator sandwiched therebetween and contained together with an electrolytic solution in an outer case including a flexible film, wherein
    the quantity of dissolved nitrogen in the electrolytic solution in injecting the electrolytic solution into the outer case is 100 µg/mL or less.

    [0014] A lithium ion secondary battery according to another aspect of the present invention is a lithium ion secondary battery including a positive electrode and a negative electrode disposed with a separator sandwiched therebetween and contained together with an electrolytic solution in an outer case including a flexible film, wherein the quantity of dissolved nitrogen in the electrolytic solution is 100 µg/mL or less.

    Advantageous Effects of Invention



    [0015] The present invention enables effective suppression of the swelling of a battery at a high temperature through setting the quantity of dissolved nitrogen in an electrolytic solution to a predetermined quantity or less; and prevention of bubble generation in an electrolytic solution to improve sealing properties in vacuum-impregnating electrodes with an electrolytic solution after injecting the electrolytic solution into a cell in manufacture of a lithium ion secondary battery.

    Brief Description of Drawings



    [0016] 

    [Figure 1] Figure 1 is a schematic cross-sectional view to illustrate the inner structure of a laminate lithium ion secondary battery according to an exemplary embodiment.

    [Figure 2] Figure 2 is a schematic perspective view to illustrate a battery element of a laminate lithium ion secondary battery according to an exemplary embodiment.

    [Figure 3] Figure 3 is a schematic to illustrate an outer case of a laminate lithium ion secondary battery according to an exemplary embodiment.

    [Figure 4A] Figure 4A is a schematic to illustrate how a battery element is contained in an outer case in manufacture of a laminate lithium ion secondary battery according to an exemplary embodiment.

    [Figure 4B] Figure 4B is a schematic plan view of the laminate lithium ion secondary battery obtained in Figure 4A.

    [Figure 5A] Figure 5A is a schematic to illustrate how a battery element is contained in an outer case in manufacture of a laminate lithium ion secondary battery according to another exemplary embodiment.

    [Figure 5B] Figure 5B is a schematic plan view of the laminate lithium ion secondary battery obtained in Figure 5A.


    Description of Embodiments



    [0017] A method for manufacturing a lithium ion secondary battery according to an exemplary embodiment is a method for manufacturing a lithium ion secondary battery, the lithium ion secondary battery including a positive electrode and a negative electrode disposed with a separator sandwiched therebetween and contained together with an electrolytic solution in an outer case including a flexible film, wherein the quantity of dissolved nitrogen in the electrolytic solution in injecting the electrolytic solution into the outer case is 100 µg/mL or less.

    [0018] Such a manufacturing method enables effective suppression of the swelling of a resulting battery at a high temperature; and prevention of bubble generation in an electrolytic solution to improve sealing properties in vacuum-impregnating electrodes with an electrolytic solution after injecting the electrolytic solution into a cell in manufacture of a battery.

    [0019] In the above manufacturing method, it is preferred to subject the electrolytic solution to decompression treatment (degas treatment) before injecting the electrolytic solution into the outer case so that the quantity of dissolved nitrogen in the electrolytic solution becomes 100 µg/mL or less, and inject the electrolytic solution after being subjected to the decompression treatment into the outer case.

    [0020] Then, the less the quantity of dissolved nitrogen in the electrolytic solution in injecting the electrolytic solution into the outer case is, the more preferable in principle. However, the more vigorous the degassing step is, the more frequently other adverse factors may be caused. Specifically, too much vacuum degassing, which is preferred in that the quantity of dissolved nitrogen is decreased, allows the solvent to evaporate, nevertheless, and the concentration or composition of the electrolytic solution may change to increase the viscosity, and as a result the performance of a battery may be degraded. Accordingly, the quantity of dissolved nitrogen is preferably 5 µg/mL or more, and more preferably 10 µg/mL or more as a rough value.

    [0021] Although it is desirable that the quantity of dissolved nitrogen in the electrolytic solution in injecting the electrolytic solution into the outer case is 100 µg/mL or less, the quantity is more preferably 80 µg/mL or less, and even more preferably 75 µg/mL or less from the viewpoint of achieving a more sufficient swelling-suppressing effect and foaming-preventing effect. The quantity of dissolved nitrogen may be set to 60 µg/mL or less, even to 50 µg/mL or less, and even to 40 µg/mL or less from the viewpoint of achieving a higher effect.

    [0022] Thus, the quantity of dissolved oxygen in the electrolytic solution in a lithium ion secondary battery manufactured is preferably 100 µg/mL or less, more preferably 80 µg/mL or less, and even more preferably 75 µg/mL or less. From the viewpoint of achieving a higher effect, the quantity of dissolved oxygen may be set to 60 .µg/mL or less, even to 50 µg/mL or less, and even to 40 µg/mL or less. From the viewpoint of ensuring a desired performance of a battery, the quantity of dissolved oxygen is preferably 5 µg/mL or more, and more preferably 10 µg/mL or more.

    [0023] The decompression treatment may be performed, for example, in 1 to 5 cycles, preferably in 1 to 3 cycles each of which includes decompression and opening. In the case that much dissolved nitrogen is present in the electrolytic solution, it is preferred to perform the decompression treatment in a plurality of cycles, preferably in 2 to 5 cycles, more preferably in 2 to 3 cycles. The decompression treatment in a plurality of cycles enables reduction of decompression duration per cycle and efficient removal of dissolved nitrogen. If the decompression treatment is performed in too many cycles, the components of the electrolytic solution tend to evaporate, and thus the decompression treatment is preferably performed in 5 or fewer cycles, more preferably in 3 or fewer cycles.

    [0024] The pressure in the decompression treatment may be set, for example, to -70 kPa to -99 kPa relative to the atmospheric pressure (a pressure lower than the atmospheric pressure by 70 to 99 kPa). If the degree of decompression is too low, dissolved nitrogen cannot be removed sufficiently; and if the degree of decompression is too high, the components of the electrolytic solution tend to evaporate. From the viewpoint of sufficient removal of dissolved nitrogen, the pressure is preferably -80 kPa to -99 kPa, and more preferably -90 kPa to -99 kPa.

    [0025] The duration to maintain a predetermined state of decompression in the decompression treatment may be set, for example, to 10 minutes or shorter from the viewpoint of reduction of the evaporation of the components of the electrolytic solution and treatment efficiency, and the duration is preferably 5 minutes or shorter, and more preferably 2 minutes or shorter, and the duration is preferably 0.5 minutes or longer, and more preferably 1 minute or longer from the viewpoint of sufficient removal of dissolved nitrogen.

    [0026] The decompression treatment may be performed at normal temperature, and may be set, for example, to 5 to 35°C, and may be performed preferably at 10 to 35°C, more preferably at 10 to 30°C. If the temperature of the electrolytic solution is low, less dissolved nitrogen is removed off; however, the evaporation of the components of the electrolytic solution can be reduced. If the temperature of the electrolytic solution is high, more dissolved nitrogen is removed off; however, the evaporation of the components of the electrolytic solution is promoted.

    [0027] The quantity of the electrolytic solution to be treated in one decompression treatment may be set, for example, to 200 to 1000 mL, and may be appropriately set even to a quantity of 1000 mL or more in accordance with the scale or performance of a treatment apparatus.

    [0028] The electrolytic solution after being subjected to the decompression treatment may be injected into the outer case, for example, in a dry air atmosphere (e.g., dew point: -40°C or lower). A shorter period is preferred for the period from the termination of the decompression treatment to injection, although the period depends on the state of storage of the electrolytic solution after being subjected to the decompression treatment, from the viewpoint of preventing increase of the quantity of dissolved nitrogen, and the period is preferably 1 week or shorter, for example. The electrolytic solution after being subjected to the decompression treatment is preferably stored in a sealed container during the period before injection. The space other than the space for the electrolytic solution in the sealed container is preferably small, and dry air may be used for a gas to fill the space.

    [0029] The above manufacturing method preferably includes a step of maintaining a battery obtained after injecting the electrolytic solution into the outer case at a temperature of 35°C or higher and 60°C or lower (preferably, 40°C or higher and 60°C or lower, more preferably 50°C or higher and 60°C or lower) for 48 hours or longer and shorter than 480 hours (or 480 hours or shorter). Then, a predetermined voltage is preferably applied to bring into a charging state. According to an exemplary embodiment, gas generation during such high temperature aging can be prevented. In addition, a step of degassing can be simplified or omitted.

    [0030] The above manufacturing method is particularly effective if the thickness of the flexible film is 5 µm or larger and 150 µm or smaller.

    [0031] A lithium ion secondary battery according to another exemplary embodiment is a lithium ion secondary battery including a positive electrode and a negative electrode disposed with a separator sandwiched therebetween and contained together with an electrolytic solution in an outer case including a flexible film, wherein the quantity of dissolved nitrogen in the electrolytic solution is 100 µg/mL or less.

    [0032] The thickness of the flexible film is preferably 5 µm or larger and 150 µm or smaller.

    [0033] A lithium ion secondary battery according to an exemplary embodiment can be obtained by using the above manufacturing method.

    [0034] According to an exemplary embodiment, swelling, which is a problem inherent in a lithium ion secondary battery with an outer case including a flexible film, can be suppressed and in particular swelling under a high temperature environment can be suppressed.

    [0035] Now, an exemplary embodiment will be further described.

    [0036] Figure 1 schematically illustrates an example of the configuration of a stacked lithium ion secondary battery, as a laminate lithium ion secondary battery according to an exemplary embodiment.

    [0037] A lithium ion secondary battery 100 according to an exemplary embodiment includes an electrode laminate in which positive electrodes 1 and negative electrodes 6 are alternately laminated with a separator 20 sandwiched therebetween in a plurality of layers, and the electrode laminate is contained together with an electrolytic solution in an outer case (container) 30 including a flexible film. To the electrode laminate, a positive electrode terminal 11 and a negative electrode terminal 16 are electrically connected, and the end portion of each of the positive electrode terminal 11 and the negative electrode terminal 16 is partially or totally extracted to the outside of the outer case 30.

    [0038] The positive electrode 1 includes a portion with a coating (positive electrode active material layer) 2, formed by applying a slurry containing a positive electrode active material onto the both sides of a positive electrode current collector followed by drying, and a portion with no coating, onto which the slurry has not been applied respectively. The negative electrode includes a portion with a coating (negative electrode active material layer) 7, formed by applying a slurry containing a negative electrode active material onto the both sides of a negative electrode current collector 8 followed by drying, and a portion with no coating, onto which the slurry has not been applied respectively.

    [0039] The portion with no coating of a positive electrode active material on the positive electrode current collector serves as a positive electrode tab 3 to connect to the positive electrode terminal 11, and the portion with no coating of a negative electrode active material on the negative electrode current collector serves as a negative electrode tab 8 to connect to the negative electrode terminal 16. A plurality of the positive electrode tabs 3 are brought together onto the positive electrode terminal 11 and the positive electrode tabs 3 are connected to each other together with the positive electrode terminal 11 through ultrasonic welding or the like. A plurality of the negative electrode tabs 8 are brought together onto the negative electrode terminal 16 and the negative electrode tabs 8 are connected to each other together with the negative electrode terminal 16 through ultrasonic welding or the like. One end of the positive electrode terminal 11 connected to the positive electrode tabs 3 is extracted to the outside of the outer case 30, and one end of the negative electrode terminal 16 connected to the negative electrode tabs 8 is extracted to the outside of the outer case 30. In the boundary portion 4 between the portion with a coating of the positive electrode active material 2 and the portion with no coating of the positive electrode active material 2, an insulating member is formed to prevent a short circuit to the negative electrode terminal.

    [0040] Examples of the positive electrode active material include layered oxide materials such as LiCoO2, LiNiO2, LiNi1-xCoxO2, LiNix(CoAl)1-xO2, Li2MO3-LiMO2 (M denotes metal element such as Ni, Co, and Mn), and LiNi1/3Co1/3Mn1/3O2; spinel-type oxide materials such as LiMn2O4, LiMn1.5Ni0.5O4, and LiMn2-xMxO4 (M denotes metal element such as Ni, Co, Cr, and Fe); olivine-type materials such as LiMPO4 (M denotes, for example, Ni, Co, Fe, or Mn); fluorinated olivine-type materials such as Li2MPO4F and Li2MSiO4F (M denotes, for example, Ni, Co, Fe, or Mn); and vanadium oxide materials such as V2O5. One of these positive electrode active materials may be used singly, or two or more thereof may be used in a mixture. In the above compositional formulas, x denotes any positive integer.

    [0041] Examples of the negative electrode active material which can be used include carbon materials such as graphite, amorphous carbon, diamond-like carbon, fullerene, carbon nanotubes, and carbon nanohorns; lithium metal materials; metal materials capable of alloying with Li such as silicon and tin; oxide materials such as Nb2O5 and TiO2; and composites of them.

    [0042] To each of the positive electrode active material and the negative electrode active material, a binder or a conductive aid, etc., may be appropriately added. Examples of the conductive aid include carbon black, carbon fibers, and graphite, and one of them may be used singly, or two or more thereof may be used in combination. For the binder, polyvinylidene fluoride, polytetrafluoroethylene, carboxymethyl cellulose, a modified acrylonitrile rubber particle, or the like may be used.

    [0043] For the positive electrode current collector, aluminum, a stainless steel, nickel, titanium, or an alloy thereof may be used, and aluminum is particularly preferred. For the negative electrode current collector, copper, a stainless steel, nickel, titanium, or an alloy thereof may be used. Examples of the shape of the current collector include a foil, a sheet, and a mesh.

    [0044] For the electrolytic solution, a nonaqueous electrolytic solution with a lithium salt dissolved therein may be used. Examples of the nonaqueous solvent include, but not particularly limited to, cyclic carbonates such as ethylene carbonate, propylene carbonate, vinylene carbonate, and butylene carbonate; linear carbonates such as ethyl methyl carbonate (EMC), diethyl carbonate (DEC), dimethyl carbonate (DMC), and dipropyl carbonate (DPC); aliphatic carboxylates such as methyl formate, methyl acetate, and ethyl propionate; lactones such as γ-butyrolactone; linear ethers such as 1,2-ethoxyethane (DEE) and ethoxymethoxyethane (EME); and cyclic ethers such as tetrahydrofuran and 2-methyltetrahydrofuran. Alternatively, an aprotic organic solvent may be used for the nonaqueous solvent, and examples of the aprotic organic solvent include dimethylsulfoxide, 1,3-dioxolane, dioxolane derivatives, formamide, acetamide, dimethylformamide, acetonitrile, propionitrile, nitromethane, ethyl monoglyme, triphosphates, trimethoxymethane, sulfolane, methylsulfolane, 1,3-dimethyl-2-imidazolidinone, 3-methyl-2-oxazolidinone, propylene carbonate derivatives, tetrahydrofuran derivatives, ethyl ether, 1,3-propanesultone, anisole, and N-methylpyrrolidone. One of the nonaqueous solvents may be used singly, or two or more thereof may be used in a mixture.

    [0045] Examples of the lithium salt to be dissolved in the nonaqueous solvent include, but not particularly limited to, LiPF6, LiAsF6, LiAlCl4, LiClO4, LiBF4, LiSbF6, LiCF3SO3, LiCF3CO2, Li(CF3SO2)2, LiN(CF3SO2)2, and lithium bis(oxalate)borate. One of these lithium salts may be used singly, or two or more thereof may be used in combination. In addition, a polymer component may be contained as a nonaqueous electrolyte.

    [0046] An additive may be added to the electrolytic solution. Examples of the additive which can be used include compounds having a sulfo group, fluorinated solvents such as fluoroethylene carbonate, and unsaturated cyclic carbonates such as vinylene carbonate. In particular, additives having low volatility, which are less affected by decompression, are preferred as the additive.

    [0047] For the separator, a porous membrane, a woven fabric, a nonwoven fabric, or the like may be used. Examples of a material constituting the separator include polyolefin resins such as polypropylenes and polyethylenes, polyester resins, acrylic resins, styrenic resins, and nylon resins. In particular, polyolefin microporous membranes are preferred because of being excellent in ion conductivity and physical separation between a positive electrode and a negative electrode. Further, a layer containing an inorganic particle may be formed on the separator, as necessary. Examples of the inorganic particle include insulating oxides, nitrides, sulfides, and carbides, and among them, TiO2 or Al2O3 is preferably contained.

    [0048] For the container, an outer case including a flexible film, a can case with a small thickness, or the like may be used. An outer case including a flexible film is preferably used from the viewpoint of weight saving for a battery. The thickness of the flexible film is preferably 5 µm or larger and 150 µm or smaller. If the thickness is smaller than 5 µm, it is difficult to endure an impact from the outside and pressure increase in the case. The thickness is more preferably 10 µm or larger, and even more preferably 50 µm or larger from the viewpoint of achieving a sufficient strength, durability, etc. Although the case that the thickness is larger than 150 µm is advantageous in that swelling due to pressure increase in the case is suppressed, it is disadvantageous from the viewpoint of weight saving. For the flexible film, a film in which a resin layer is provided on each surface of a metal layer serving as a base material may be used. For the metal layer, a metal layer having barrier properties to prevent leakage of the electrolytic solution and moisture intrusion from the outside, for example, may be selected, and aluminum, a stainless steel, or the like may be used, and aluminum is particularly preferred. A heat-sealable resin layer of a modified polyolefin or the like is preferably provided on at least one surface of the metal layer. The electrode laminate is contained in such a way that the heat-sealable resin layers of the flexible film face each other, and the periphery of the portion containing the electrode laminate is heat-sealed, and thus an outer case can be formed. On the surface opposite to the surface with a heat-sealable resin layer formed thereon, a resin layer relatively excellent in heat resistance such as a nylon film and a polyester film may be provided.

    [0049] A positive electrode terminal of aluminum or an aluminum alloy may be used for the positive electrode terminal, and a negative electrode terminal of copper, a copper alloy, or copper or a copper alloy with a nickel plating, or the like may be used for the negative electrode terminal. A heat-sealable resin may be provided in advance on each of the positive electrode terminal and the negative electrode terminal at a part corresponding to a portion of the flexible film to be heat-sealed when the electrode terminal is extracted to the outside of the outer case.

    [0050] A polyimide, a glass fiber, a polyester, a polypropylene, or an insulating member including them in its structure may be used for the insulating member to be formed in the boundary portion between the portion with a coating of an active material and the portion with no coating of an active material, and the insulating member can be formed by heating a tape-shaped member to fuse on the boundary portion or by applying a gelled resin onto the boundary portion followed by drying.

    [0051] Figure 2 schematically illustrates a battery element (electrode laminate) in which a positive electrode and a negative electrode are repeatedly laminated with a separator sandwiched therebetween. The positive electrode tabs 3 are brought together and connected to the positive electrode terminal 11, and the negative electrode tabs 8 are brought together and connected to the negative electrode terminal 16, and a resin to strengthen the adhesion is formed in a portion of each terminal to contact with an outer case.

    [0052] Figure 3 schematically illustrates an outer case to contain the battery element therein. Although an outer case obtained by pasting together two sheets each having a concave portion corresponding to the shape of the battery element is illustrated, the concave portion may be formed in only one sheet, or one sheet may be folded and pasted together.

    [0053] As shown in Figure 4A, the battery element is contained in the concave portions provided in the flexible films, and three peripheral edges are heat-sealed while any one edge among edges with no extrusion of an electrode terminal, for example, 300a in Figure 4B, is left unsealed. The one edge left unfused is for injection of the electrolytic solution. As long as an area which allows for injection is left unfused in the one edge left unfused, the rest of the one edge may be fused.

    [0054] After injection of the electrolytic solution, the portion left unfused is additionally heat-sealed to seal the outer case.

    [0055] Although a battery is formed in such a way that the electrode terminals are extracted from opposing edges in the example illustrated in Figure 4A and Figure 4B, a battery can be formed in the same manner in such a way that the electrode terminals are extracted from one edge as illustrated in Figure 5A and Figure 5B.

    [0056] Subsequently, a resulting battery may be evaluated to determine whether the battery contains a foreign matter in the composite electrode material. By performing such evaluation and excluding batteries containing a foreign matter in the composite electrode material, a battery excellent in heat resistance can be provided. In the evaluation, a resulting battery is applied with a voltage at a high temperature, specifically, applied with a voltage at a temperature of 25°C or higher and 60°C or lower, preferably at a temperature of 35°C or higher and 60°C or lower, more preferably at a temperature of 40°C or higher and 60°C or lower, and is maintained in the state, for example, for 48 hours or longer and shorter than 480 hours (or 480 hours or shorter). Here, a short circuit occurs in a battery containing a metal foreign matter in the composite electrode material due to a needle-like precipitate of the metal foreign matter. Since such a short-circuited battery undergoes voltage drop due to self-discharge, batteries with voltage drop can be discriminated and excluded.

    [0057] Here, voltage drop due to a foreign matter can be detected in a shorter time as the temperature is higher. If a battery does not swell even under such a temperature environment, the battery is proven to be a battery capable of operating satisfactorily even under a high temperature environment, for example, in a tropical region.

    Examples


    (Examples 1 to 3)



    [0058] A mixed active material of LiMn2O4 and LiNi0.8Co0.1Al0.1O2 was used as a positive electrode active material, and carbon black as a conductive aid and polyvinylidene fluoride (PVdF) as a binder for positive electrodes were used. The positive electrode active material, conductive aid, and binder were dispersed in a solvent to prepare a slurry, and the slurry was applied onto a positive electrode current collector made of aluminum, dried, and pressed to obtain a positive electrode sheet of a predetermined size.

    [0059] Graphite having an amorphous surface was used as a negative electrode active material, and PVdF was used as a binder for negative electrodes. The negative electrode active material and binder were dispersed in a solvent to prepare a slurry, and the slurry was applied onto a negative electrode current collector made of copper, dried, and pressed to obtain a negative electrode sheet of a predetermined size.

    [0060] As described above with reference to Figures 1 to 4, the resultant positive electrode sheet 5 and negative electrode sheet 6 were laminated with a separator having a thickness of 25 µm and made of polypropylene sandwiched therebetween, and a negative electrode terminal and a positive electrode terminal were provided thereto, and the resultant was contained in an outer case made of a flexible aluminum laminate film (thickness: about 100 µm), and an electrolytic solution was injected thereinto and the outer case was sealed to obtain a stacked laminate battery.

    [0061] The electrolytic solution used was an electrolytic solution obtained by adding a lithium salt (LiPF6) and an additive (vinylene carbonate) to a mixed carbonate solvent containing ethylene carbonate and diethyl carbonate.

    [0062] Here, before injection of the electrolytic solution, the electrolytic solution was subjected to decompression treatment with a vacuum pump in two steps at 25°C each of which includes leaving to stand at a reduced pressure of -99 kPa relative to the atmospheric pressure (a pressure lower than the atmospheric pressure by 99 kPa) for 2 minutes followed by opening to the atmospheric pressure. The gas used in opening to the atmospheric pressure was dry air (dew point: -40°C or lower). In this example, 200 to 1000 mL of the electrolytic solution was subjected to the decompression treatment.

    [0063] Through the decompression treatment, the quantity of dissolved nitrogen in 1 mL of the electrolytic solution was controlled to 5 µg.

    [0064] Through changing the duration of leaving to stand after decompression (the duration between the opening to the atmospheric pressure after the second decompression and the injection) among the vacuuming conditions, the quantity of dissolved nitrogen in 1 mL of the electrolytic solution was controlled to 5 µg (Example 1), 35 µg (Example 2), 80 µg (Example 3), and 100 µg (Example 4).

    [0065] The quantity of dissolved nitrogen in the electrolytic solution was measured by using gas chromatography (detector: ICD).

    (Comparative Example 1)



    [0066] A lithium ion secondary battery was produced in the same manner as in Examples except that the quantity of dissolved nitrogen in 1 mL of the electrolytic solution was controlled to 110 µg through changing the duration of leaving to stand after decompression among the vacuuming conditions in Examples.

    (Reference Example 1)



    [0067] A lithium ion secondary battery was produced in the same manner as in Examples except that the quantity of dissolved nitrogen in 1 mL of the electrolytic solution was controlled to 3 µg through changing the duration of leaving to stand after decompression among the vacuuming conditions in Examples.

    (Evaluation)



    [0068] Evaluations on the presence or absence of the swelling of the outer case and cycle characteristics were performed for the batteries obtained in Examples, Comparative Example, and Reference Example. Table 1 shows the results.

    [0069] In the evaluation on the presence or absence of the swelling of the outer case, a battery was retained at a predetermined temperature (30°C, 45°C, 60°C) for 240 hours and the presence or absence of the swelling of the outer case was determined by using Archimedes' Method.

    [0070] In the evaluation on cycle characteristics, the capacity retention rate after 500 cycles relative to the initial capacity was determined, and a capacity retention rate of 90% or more was rated as "O", a capacity retention rate of 85% or more and less than 90% was rated as "Δ", and a capacity retention rate of less than 85% was rated as "×".
    [Table 1]
     Quantity of dissolved N2 [µg/mL]Presence or absence of swelling (240 Hr)Cycle characteristics (45°C, after 500 cycles)Component analysis of electrolytic solution
    30°C45°C60°C
    Reference Example 1 3 absent absent absent × reduction of solvent component
    Example 1 5 absent absent absent no change
    Example 2 35 absent absent absent no change
    Example 3 80 absent absent present no change
    Example 4 100 absent absent present Δ no change
    Comparative Example 1 110 absent present present Δ no change


    [0071] As shown in Table 1, swelling did not occur at a temperature of 30 to 45°C in the case that the quantity of dissolved N2 was 100 µg/mL or less. In the case that the quantity of dissolved N2 was 5 to 80 µg/mL (Examples 1 to 3), swelling did not occur at a temperature of 30 to 45°C and in addition the cycle characteristics were satisfactory. In the case that the quantity of dissolved N2 was 5 to 35 µg/mL (Examples 1 and 2), swelling did not occur even at 60°C and in addition the cycle characteristics were satisfactory.

    [0072]  In the case that the quantity of dissolved N2 was 3 µg/mL (Reference Example 1), swelling did not occur, but the cycle characteristics were degraded. Although the reason is not clear, the degradation is presumably because the solvent in the electrolytic solution volatilized to increase the viscosity of the electrolytic solution and as a result the resistance increased. In the case that the quantity of dissolved N2 was 110 µg/mL (Comparative Example 1), on the other hand, the outer case swelled due to aging at 45°C or higher and the cycle characteristics were degraded.

    [0073] In the foregoing, the present invention has been described with reference to the exemplary embodiments and the Examples; however, the present invention is not limited to the exemplary embodiments and the Examples.

    Industrial Applicability



    [0074] The present invention is useful for lithium ion secondary batteries, capacitor devices such as lithium ion capacitors, and methods for manufacturing them.

    Reference Signs List



    [0075] 
    1
    positive electrode
    2
    portion with coating of positive electrode active material
    3
    positive electrode tab
    4
    boundary portion
    6
    negative electrode
    7
    portion with coating of negative electrode active material
    8
    negative electrode tab
    11
    positive electrode terminal
    16
    negative electrode terminal
    20
    separator
    30
    outer case (flexible film)
    100
    lithium ion secondary battery



    Claims

    1. A method for manufacturing a lithium ion secondary battery, the lithium ion secondary battery comprising a positive electrode and a negative electrode disposed with a separator sandwiched therebetween and contained together with an electrolytic solution in an outer case including a flexible film, the method comprising:

    injecting the electrolytic solution into the outer case, and

    maintaining a battery obtained after injecting the electrolytic solution into the outer case, at a temperature of 35°C or higher and 60°C or lower for 48 hours or longer and shorter than 480 hours, wherein

    a quantity of dissolved nitrogen in the electrolytic solution in injecting the electrolytic solution into the outer case is 100 µg/mL or less.


     
    2. A method for manufacturing a lithium ion secondary battery, the lithium ion secondary battery comprising a positive electrode and a negative electrode disposed with a separator sandwiched therebetween and contained together with an electrolytic solution in an outer case including a flexible film, the method comprising:

    conducting decompression treatment of the electrolytic solution before injecting the electrolytic solution into the outer case so that a quantity of dissolved nitrogen in the electrolytic solution becomes 100 µg/mL or less, and

    injecting the electrolytic solution into the outer case after the decompression treatment, wherein

    a quantity of dissolved nitrogen in the electrolytic solution in injecting the electrolytic solution into the outer case is 100 µg/mL or less.


     
    3. The method for manufacturing a lithium ion secondary battery according to claim 1 or 2, wherein a quantity of dissolved nitrogen in the electrolytic solution in injecting the electrolytic solution into the outer case is 5 µg/mL or more.
     
    4. The method for manufacturing a lithium ion secondary battery according to claim 1 or 2, wherein a quantity of dissolved nitrogen in the electrolytic solution in injecting the electrolytic solution into the outer case is 10 µg/mL or more.
     
    5. The method for manufacturing a lithium ion secondary battery according to any one of claims 1 to 4, wherein a quantity of dissolved nitrogen in the electrolytic solution in injecting the electrolytic solution into the outer case is 80 µg/mL or less.
     
    6. The method for manufacturing a lithium ion secondary battery according to claim 2, further comprising a step of maintaining a battery obtained after injecting the electrolytic solution into the outer case, at a temperature of 35°C or higher and 60°C or lower for 48 hours or longer and shorter than 480 hours.
     
    7. The method for manufacturing a lithium ion secondary battery according to any one of claims 1 to 6, wherein a thickness of the flexible film is 5 µm or larger and 150 µm or smaller.
     
    8. A lithium ion secondary battery obtained by the method of any one of claims 1 to 6, the lithium ion secondary battery comprising a positive electrode and a negative electrode disposed with a separator sandwiched therebetween and contained together with an electrolytic solution in an outer case including a flexible film, wherein a quantity of dissolved nitrogen in the electrolytic solution is 100 µg/mL or less.
     
    9. The lithium ion secondary battery according to claim 8, wherein a thickness of the flexible film is 5 µm or larger and 150 µm or smaller.
     


    Ansprüche

    1. Verfahren zur Herstellung einer Lithium-Ionen-Sekundärbatterie, wobei die Lithium-Ionen-Sekundärbatterie eine positive Elektrode und eine negative Elektrode aufweist, die mit einem dazwischen liegenden Separator angeordnet sind und zusammen mit einer Elektrolytlösung in einem Außengehäuse, das eine flexible Folie aufweist, enthalten sind, wobei das Verfahren aufweist:

    Injizieren der Elektrolytlösung in das Außengehäuse, und

    Halten einer durch Injizieren der Elektrolytlösung in das Außengehäuse gewonnenen Batterie bei einer Temperatur von 35° oder höher und 60°C oder niedriger für 48 Stunden oder länger und kürzer als 480 Stunden, wobei

    eine Menge von gelöstem Stickstoff in der Elektrolytlösung beim Injizieren der Elektrolytlösung in das Außengehäuse 100µg/mL oder weniger ist.


     
    2. Verfahren zur Herstellung einer Lithium-Ionen-Sekundärbatterie, wobei die Lithium-Ionen-Sekundärbatterie eine positive Elektrode und eine negative Elektrode aufweist, die mit einem dazwischen liegenden Separator angeordnet sind und zusammen mit einer Elektrolytlösung in einem Außengehäuse, das eine flexible Folie aufweist, enthalten sind, wobei das Verfahren aufweist:

    Durchführen einer Dekompressionsbehandlung der Elektrolytlösung vor Injizieren der Elektrolytlösung in das Außengehäuse, so dass eine Menge von gelöstem Stickstoff in der Elektrolytlösung 100µg/mL oder weniger wird, und

    Injizieren der Elektrolytlösung in das Außengehäuse nach der Dekompressionsbehandlung, wobei

    eine Menge von gelöstem Stickstoff in der Elektrolytlösung beim Injizieren der Elektrolytlösung in das Außengehäuse 100µg/mL oder weniger ist.


     
    3. Verfahren zur Herstellung einer Lithium-Ionen-Sekundärbatterie nach Anspruch 1 oder 2, wobei eine Menge von gelöstem Stickstoff in der Elektrolytlösung beim Injizieren der Elektrolytlösung in das Außengehäuse 5µg/mL oder mehr ist.
     
    4. Verfahren zur Herstellung einer Lithium-Ionen-Sekundärbatterie nach Anspruch 1 oder 2, wobei eine Menge von gelöstem Stickstoff in der Elektrolytlösung beim Injizieren der Elektrolytlösung in das Außengehäuse 10µg/mL oder mehr ist.
     
    5. Verfahren zur Herstellung einer Lithium-Ionen-Sekundärbatterie nach einem der Ansprüche 1 bis 4, wobei eine Menge von gelöstem Stickstoff in der Elektrolytlösung beim Injizieren der Elektrolytlösung in das Außengehäuse 80µg/mL oder weniger ist.
     
    6. Verfahren zur Herstellung einer Lithium-Ionen-Sekundärbatterie nach Anspruch 2, ferner aufweisend einen Schritt eines Haltens einer nach Injizieren der Elektrolytlösung in das Außengehäuse gewonnenen Batterie bei einer Temperatur von 35° oder höher und 60°C oder niedriger für 48 Stunden oder länger und kürzer als 480 Stunden.
     
    7. Verfahren zur Herstellung einer Lithium-Ionen-Sekundärbatterie nach einem der Ansprüche 1 bis 6, wobei eine Dicke der flexiblen Folie 5µm oder größer und 150µm oder kleiner ist.
     
    8. Lithium-Ionen-Sekundärbatterie, hergestellt durch ein Verfahren nach einem der Ansprüche 1 bis 6, wobei die Lithium-Ionen-Sekundärbatterie eine positive Elektrode und eine negative Elektrode aufweist, die mit einem dazwischen liegenden Separator angeordnet sind und zusammen mit einer Elektrolytlösung in einem Außengehäuse, das eine flexible Folie aufweist, enthalten sind, wobei eine Menge von gelöstem Stickstoff in der Elektrolytlösung 100µg/mL oder weniger ist.
     
    9. Lithium-Ionen-Sekundärbatterie nach Anspruch 8, wobei eine Dicke der flexiblen Folie 5µm oder größer und 150µm oder kleiner ist.
     


    Revendications

    1. Procédé de fabrication d'une batterie secondaire au lithium-ion, la batterie secondaire au lithium-ion comprenant une électrode positive et une électrode négative disposées avec un séparateur intercalé entre elles et contenues ensemble avec une solution électrolytique dans un boîtier externe incluant un film flexible, le procédé comprenant :

    l'injection de la solution électrolytique dans le boîtier externe, et

    le maintien d'une batterie obtenue après l'injection de la solution électrolytique dans le boîtier externe, à une température de 35 °C ou plus et 60 °C ou moins pendant 48 heures ou plus et moins de 480 heures, dans lequel

    une quantité d'azote dissous dans la solution électrolytique lors de l'injection de la solution électrolytique dans le boîtier externe est de 100 µg/mL ou moins.


     
    2. Procédé de fabrication d'une batterie secondaire au lithium-ion, la batterie secondaire au lithium-ion comprenant une électrode positive et une électrode négative disposées avec un séparateur intercalé entre elles et contenues ensemble avec une solution électrolytique dans un boîtier externe incluant un film flexible, le procédé comprenant :

    la mise en œuvre d'un traitement de décompression de la solution électrolytique avant l'injection de la solution électrolytique dans le boîtier externe de façon qu'une quantité d'azote dissous dans la solution électrolytique soit de 100 µg/mL ou moins, et

    l'injection de la solution électrolytique dans le boîtier externe après le traitement de décompression, dans lequel

    une quantité d'azote dissous dans la solution électrolytique lors de l'injection de la solution électrolytique dans le boîtier externe est de 100 µg/mL ou moins.


     
    3. Procédé de fabrication d'une batterie secondaire au lithium-ion selon la revendication 1 ou 2, dans lequel une quantité d'azote dissous dans la solution électrolytique lors de l'injection de la solution électrolytique dans le boîtier externe est de 5 µg/mL ou plus.
     
    4. Procédé de fabrication d'une batterie secondaire au lithium-ion selon la revendication 1 ou 2, dans lequel une quantité d'azote dissous dans la solution électrolytique lors de l'injection de la solution électrolytique dans le boîtier externe est de 10 µg/mL ou plus.
     
    5. Procédé de fabrication d'une batterie secondaire au lithium-ion selon l'une quelconque des revendications 1 à 4, dans lequel une quantité d'azote dissous dans la solution électrolytique lors de l'injection de la solution électrolytique dans le boîtier externe est de 80 µg/mL ou moins.
     
    6. Procédé de fabrication d'une batterie secondaire au lithium-ion selon la revendication 2, comprenant en outre une étape de maintien d'une batterie obtenue après l'injection de la solution électrolytique dans le boîtier externe, à une température de 35 °C ou plus et 60 °C ou moins pendant 48 heures ou plus et moins de 480 heures.
     
    7. Procédé de fabrication d'une batterie secondaire au lithium-ion selon l'une quelconque des revendications 1 à 6, dans lequel une épaisseur du film flexible est de 5 µm ou plus et 150 µm ou moins.
     
    8. Batterie secondaire au lithium-ion obtenue par le procédé selon l'une quelconque des revendications 1 à 6, la batterie secondaire au lithium-ion comprenant une électrode positive et une électrode négative disposées avec un séparateur intercalé entre elles et contenues ensemble avec une solution électrolytique dans un boîtier externe incluant un film flexible, dans lequel une quantité d'azote dissous dans la solution électrolytique est de 100 µg/mL ou moins.
     
    9. Batterie secondaire au lithium-ion selon la revendication 8, dans laquelle une épaisseur du film flexible est de 5 µm ou plus et 150 µm ou moins.
     




    Drawing














    Cited references

    REFERENCES CITED IN THE DESCRIPTION



    This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

    Patent documents cited in the description