(19)
(11)EP 3 212 303 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
15.09.2021 Bulletin 2021/37

(21)Application number: 15790508.4

(22)Date of filing:  30.10.2015
(51)International Patent Classification (IPC): 
B01D 39/16(2006.01)
B01D 39/20(2006.01)
B01D 39/18(2006.01)
(52)Cooperative Patent Classification (CPC):
B01D 2239/1233; B01D 39/2024; B01D 39/163; B01D 2239/04; B01D 2239/086; B01D 2239/1216; B01D 39/18
(86)International application number:
PCT/EP2015/075318
(87)International publication number:
WO 2016/066825 (06.05.2016 Gazette  2016/18)

(54)

SELF SUPPORTING PLEATED OIL FILTER

SELBSTTRAGENDER PLISSIERTER ÖLFILTER

FILTRE À HUILE PLISSÉ AUTOPORTANT


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 31.10.2014 US 201462073066 P
28.11.2014 FI 20146043

(43)Date of publication of application:
06.09.2017 Bulletin 2017/36

(73)Proprietor: Ahlstrom-Munksjö OYJ
00100 Helsinki (FI)

(72)Inventors:
  • SHIM, Jesse
    Daegu Metropolitan City (KR)
  • KIM, Kevin
    Daegu Metropolitan City (KR)
  • KWON, Ryan
    Daegu (KR)
  • KIM, Jinny
    Daegu Metropolitan City (KR)
  • BYEON, Jamie
    Daegu (KR)
  • TOPOLENSKI, David, Alan
    Madisonville, KY 42431 (US)
  • TOWNSEND, Kevon, Ray
    Providence, KY 42450 (US)

(74)Representative: Vossius & Partner Patentanwälte Rechtsanwälte mbB 
Siebertstrasse 3
81675 München
81675 München (DE)


(56)References cited: : 
WO-A1-2012/054672
US-A1- 2006 242 933
US-A1- 2002 148 776
  
  • None
  
Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


Description

Technical Field



[0001] The present invention relates to self-supporting pleated oil filters incorporating filter media formed from synthetic fibers, optionally at least one additive and at least one thermoset binder and/or at least one binder fiber, wherein the synthetic fibers comprise up to 30 wt.-%, preferably up to 20 wt.-%, glass fibers, based on the total weight of the fibers, wherein the fibers are bonded with the thermoset binder and/or the at least one binder fiber to form a fibrous medium.

Background



[0002] Oil filters intended for use in combustion engines conventionally comprise filter media with fibers obtained from wood pulp. Such wood pulp fibers are typically 1 to 7 millimeters long and 15 to 45 microns in diameter. Natural wood pulp has largely been the preferred raw material for producing filtration media due to its relatively low cost, processability, various mechanical and chemical properties, and durability in the end application.

[0003] The filter media are pleated to increase filtration surface area transversally to the direction of the oil flow.

[0004] US Patent Specification No. 3,288,299 discloses a dual type of oil filter cartridge wherein part of the flow is through a surface type of filter element, such as pleated paper, and the rest of the flow is through a depth type of filter element such as a thick fibrous mass. An oil filter and adapter is disclosed in US Patent No. 3,912,631.

[0005] A typical prior art oil filter is shown in Figure 1. Reference numeral 1 refers to the pleated filter media (or filtration media) and 2 to a backing structure. A conventional filter media exhibits low stiffness and has poor mechanical strength in terms of tensile strength and burst strength. The filter media 1 is therefore used together with a metal mesh or other type of support means 2, which forms a backing for the filter media and assists in maintaining the pleat shape when used in the end application.

[0006] Nevertheless, in view of the low mechanical strength the filter media tend to burst over time on exposure to engine oil at the temperatures encountered in a combustion engine, such as 125-135°C.

[0007] Although filter media products that are produced largely with wood pulp are still an excellent choice for most automotive and heavy duty oil filtration applications, there is a growing market demand for oil filtration products that exhibit increased strength and durability over time as the media is exposed to the various chemical, thermal, and mechanical stresses of the end application environment. This demand stems from both harsher end application conditions that the media is exposed to as well as increasing demand for filter media that can be safely used in the end application for increasingly longer amounts of time without rupturing or failing.

[0008] The long-standing and widely applied solution to this demand has been to incorporate some minor quantity of synthetic fiber, typically PET polyester, in the amount of about 5 - 20%. The result of fortifying the fiber furnish in this way is higher media strength as well as enhanced chemical and mechanical durability when the media is exposed to the end application environment, due to the superior chemical, thermal, and mechanical durability of the synthetic fibers themselves.

[0009] For air filters there are alternative technical solutions primarily based on non-natural fibers described in the art.

[0010] US Patent No. 7,608,125 discloses a MERV filter composed of a wet laid fibrous mat comprising about 20-60 wt-% of glass fibers, about 15-60 wt-% of polymer fibers, and about 15-40 wt-% of a binder for bonding of the fibers. The binder of this disclosure is latex modified with melamine formaldehyde.

[0011] Published US Patent Application No. 2012/0175298 discloses a HEPA filter comprising a nonwoven web of two different fiber components. The first fiber component is formed by fibers of polyesters, polyamides, polyolefin, polylactide, cellulose esters, polycaprolactone, polyactides, polyurethane, polyvinylchloride, and combinations thereof. The first fibers make up at least 20 % of the weight of web. The second fiber can be composed of either cellulosic fibres (Lyocell) or glass or combination of the two. There is further a binder component formed by acrylic polymers, styrenic polymers, vinyl polymers polyurethanes, and combinations thereof.

[0012] Published US Patent Application No. 2013/0233789 discloses a glass-free non-woven fuel filtration media that is comprised of a blend of a staple synthetic fibers and fibrillated cellulosic fibers.

[0013] US Patents Nos. 7,488,365, 8,236,082 and 8,778,047 disclose further filtration media containing 50 to 100 % of synthetic fibers of the weight of the fibrous web.

[0014] None of the references to air filters and fuel filter media discloses a filter medium capable of forming a self-supporting oil filter when configured into a pleated structure and which would be capable of working properly at the harsh conditions in connection with a combustion engine.

[0015] US 2002/148776 A1 discloses a fibrous filtration media for water filtration, which comprises a mixture of between about 10 to about 50 wt. % glass fibers and between about 25 to about 65 wt. % synthetic polymeric fibers. It further comprises between about 10 to about 20 wt. % staple binder fibers.

[0016] In fact, the known filtration media containing a high percentage of synthetic fibers are not pleateable or self-supporting as such, and they have to be co-pleated and reinforced with some sort of additional mechanical support layer, such as a plastic or wire mesh backing. Media made with high levels of synthetic fiber typically tend to exhibit drape and they lack sufficient stiffness and rigidity causing the pleats to collapse without an additional support. A 100 % synthetic media as disclosed in the art cannot maintain a grooving pattern like corrugation or a pleated structure due to the thermal and mechanical properties of the synthetic fibers.

Summary



[0017] The following presents a simplified summary in order to provide a basic understanding of some aspects of various embodiments of the invention.

[0018] The summary is not an extensive overview of the invention. It is neither intended to identify key or critical elements of the invention nor to delineate the scope of the invention. The following summary merely presents some concepts of the invention in a simplified form as a prelude to a more detailed description of exemplifying embodiments of the invention.

[0019] It is an aim of the present invention to eliminate at least some of the problems related to the art and to provide a novel oil filter for use in combustion engines.

[0020] According to one aspect the present disclosure concerns a self-supporting pleated oil filter according to claim 1. The media incorporated in said oil filter is capable of retaining pleats upon contact with oil having a temperature in the range typically encountered in a combustion engine, such as 125-135°C (257-275°F).

[0021] Said filtration media can be produced by forming a wet laid web from a fibrous slurry comprised of synthetic fibers and optionally at least one binder fiber and/or at least one additive; drying the web to a low moisture content; contacting the dried web with a composition of a thermoset binding agent in a liquid phase to bond the fibers together with the thermoset binder; removing the liquid phase to form a media, optionally corrugating and/or pre-curing the obtained media and pleating the obtained media, followed by an optional final curing step.

[0022] The use of the present oil filter is characterized by what is stated in claim 15.

[0023] Considerable advantages are obtained by the present invention: The used fibrous media will give rise to self-supporting (i.e. stand-alone or unsupported) filters when pleated, optionally corrugated and shaped into the proper form of an oil filter, and do not require the use of a mesh backing in the finished filter device. Therefore they can be manufactured and supplied without the need of pairing with a mesh or other type of secondary material backing.

[0024] The fibrous media used in the oil filter according to the present invention exhibit good burst strength over time on exposure to hot engine oil.

[0025] Said fibrous media have lower degradation rates when exposed to hot engine oil than conventional filtration media that contain natural wood pulps.

[0026] As will be discussed below in more detail, synthetic materials for example comprising prior art fiber mixtures of the kind discussed above, would be vulnerable to glycol assisted disintegration which prevails at the conditions in, for example heavy duty diesel engines. Upon decomposition, such materials may disintegrate into the oil and even give rise to engine seizure and contamination of moving parts. By contrast, the present fibrous media have improved resistance to such disintegration and this provides extended operation times for the filters.

[0027] The fibrous media used in the present invention is readily groovable, i.e. corrugatable, and pleatable. And the material is capable of maintaining most of its original groove depth (or corrugation depth) even after long exposure times in hot engine oil having e.g. a temperature of 140°C. This feature also contributes to extended operation life of the present fibrous media.

[0028] The fibrous web produced as such also has sufficient strength such that it can be readily produced on typical style production equipment without undue inefficiencies such as those that may arise from web breaks, linting, wrinkling, etc.

[0029] In summary, the present invention eliminates the use of expensive backing materials, the obtained fibrous media are easily groovable (or corrugatable) and are easily pleatable. The end result is the ability to produce a filter with the present fibrous media without a support backing material while also achieving significantly higher burst strength than possible with traditional style oil filtration media that contain wood pulps, excellent resistance to glycol assisted disintegration and excellent dust filtration capacity and particle removal efficiency.

Brief Description of Drawings



[0030] 

Figure 1 shows an oil filter system according to prior art which includes two supporting structures for maintaining the pleats during use in e.g. a combustion engine;

Figure 2 shows the natural logarithm (In) of the hot oil burst strength of a non-limiting exemplary fibrous medium of the present invention (◆) and typical wood pulp containing media (■, ×, X), as a function of time, thereby demonstrating the beneficial hot oil durability of the fibrous media used in the invention (the conditions for this hot oil ageing are described in the test methods below);

Figure 3 shows an exemplary non-limiting pleated self-supporting medium used in the present invention;

Figure 4 shows a non-corrugated pleated filter medium (left) and a corrugated pleated filter medium (right), thereby illustrating the improved flow through the pleats when using a corrugated pleated filter medium; and

Figure 5 shows the relation between caliper, total thickness and corrugation depth of a non-limiting exemplary fibrous medium of the present invention.


Embodiments



[0031] A number of exemplifying and non-limiting embodiments of the invention are described in the accompanied dependent claims.

[0032] The verbs "to comprise" and "to include" are used in this document as open limitations that neither exclude nor require the existence of also un-recited features. The features recited in depending claims are mutually freely combinable unless otherwise explicitly stated. Furthermore, it is to be understood that the use of "a" or "an", i.e. a singular form, throughout this document does not exclude a plurality.

[0033] The term "consisting essentially of' has the meaning that specific further components may be present, namely those not materially affecting the essential characteristics of the fibers/composition in question.

[0034] As discussed above, according to the invention, a self-supporting pleated filter is described in claim 1. The used fibrous media in said oil filter is capable of forming a self-supporting, pleated oil filter which is capable of retaining pleats and corrugations upon contact with oil having a temperature in the range encountered in a combustion engine such as e.g. 125 to 135°C.

[0035] Generally, the concentration of the thermoset binder is preferably in the range of 15 to 50 wt-% by weight of the fibrous web, in particular 15 to 30 % by weight of the fibrous web. At a concentration of 15 wt-% or greater, excellent properties in terms of pleatability and self-supportability are achieved. At concentrations up to about 30 %, efficiency of the filter as a filtering media is still unimpaired, although greater concentrations can still be used.

[0036] "Synthetic" is herein used to differentiate the present fibers from natural fibers obtainable directly from natural raw-materials. Thus, for the purpose of the invention, "synthetic" fibers include fibers of polymeric materials produced by polymerization of monomeric entities as well as fibers obtained by drawing of melt material and fibers obtained by regenerating natural fibers e.g. after dissolution of them in a solvent.

[0037] The fibrous media typically comprises synthetic fibers selected from the group of thermoplastic polymers, silicious fibers, such as glass fibers, regenerated cellulosic fibers and mixtures thereof.

[0038] In one embodiment, synthetic fibers of only one kind are used in the fibrous web.

[0039] In one embodiment, it is particularly preferred to use at least two different synthetic fibers.

[0040] In a further embodiment, at least 30 wt.-%, preferably at least 50 wt.-% of the fibers are thermoplastic polymers, based on the total weight of fibers.

[0041] The fibrous media may comprise
  • a first fiber component consisting of fibers selected from the group of synthetic thermoplastic fibers;
  • a second fiber component consisting of fibers selected from a group of silicious fibers and optionally further comprising regenerated cellulosic fibers, and combinations thereof;
  • optionally a third fiber component consisting of binder fibers;
    the fibers of the first and the second and optionally the third fiber components being mixed together, and
  • a thermoset binder wherein the thermoset binder is being capable of bonding together the first, the second and optionally the third fiber components.


[0042] In one embodiment, the first fiber is preferably a synthetic thermoplastic fiber, such as polyester, and forming 30 to 99.5 %, in particular 40 to 99 %, for example 43 to 98 % by weight of the fibers of the fibrous web.

[0043] The second fiber is selected from a group of glass fibers, optionally mixed with Lyocell, regenerated cellulose and combinations thereof. The amount of the second fiber is preferably 0.1 to 70 %, in particular 1 to 60 %, for example 2 to 57 % by weight of the fibers of the fibrous web.

[0044] As defined herein, the term "self-supporting pleatable web" or self-supporting pleated filter media" is a web or a filter media whose pleats have sufficient stiffness so that they do not collapse or bow excessively when subjected to oil pressure typically encountered in combustion engines. In one preferred embodiment, the media can be provided with pleats having a sharp angle of less than 30°, in particular less than 25° (see also Figure 3). Typically, a "pleatable" media will be capable of taking up pleats and retaining them. Preferably, the pleated media will retain pleats over the whole operation time of the filter.

[0045] As defined herein, the term "corrugation" or "grooving" has the meaning commonly used in the art. Specifically, it can be preferably defined as relating to a surface structure of alternate ridges or grooves and is typically applied in a direction perpendicular to the pleat direction in order to further increase the effective surface area of the media without the necessity of increasing the outer dimensions of the media. Preferably, the corrugation depth (or grooving depth) is about 0.1-0.6 mm. The "corrugation depth" relates to the difference between the caliper (or thickness) of the flat sheet of medium and the thickness of the sheet after corrugating the medium (see also Figure 5). Corrugation is particularly important in coiled filter arrangements of pleated filters in which the pleats extend parallel to the central axis of the coiled filter arrangement. As the number of pleats increases within a given volume, the pleats come to lie in close abutment against one another, in particular on the outflow side of the filter, thereby reducing the flowrate of the medium to be filtered and consequently increasing flow resistance of the filter arrangement (see also Figure 4, right side showing a corrugated filter system according to the invention). Thus, corrugation allows for an undisturbed, more uniform flow of the medium to be filtered by increasing the rate of flow compared to a non-corrugated filter as e.g. shown in Figure 4, left side.

[0046] As defined herein, the term "fibrous" means a material that is composed predominantly of fiber and/or staple fiber.

[0047] In the present context, the term "thermoplastic" means a plastic which becomes pliable or moldable above a specific temperature and returns to a solid state upon cooling. Exemplary thermoplastic fibers suitable for the present disclosure are polyesters (e.g., polyalkylene terephthalates such as polyethylene terephthalate (PET), polybutylene terephthalate (PBT) and the like), polyalkylenes (e.g., polyethylenes, polypropylenes and the like), poyacrylonitriles (PAN), and polyamides (nylons, for example, nylon-6, nylon 6,6, nylon-6,12, and the like).

[0048] Preferred are PET fibers which exhibit good chemical and thermal resistance which are properties of importance for the use of the media as oil filters.

[0049] In an embodiment, the thermoplastic synthetic fibers are selected from fibers having an average diameter from 0.1 µm to 15 µm, such as 0.1 µm to 10 µm, and an average length from 1 to 50 mm, such as 1 to 20 mm. In general, fibers having a length greater than 5 mm, in particular greater than 10 mm, are preferred for good burst strength.

[0050] In the present context, "silicious fibers" primarily stands for "glass" fibers such as microglass fibers. Such fibers generally have an aspect ratio (ratio of length to diameter) of 1,000 to 1.

[0051] In one embodiment, the glass fibers have an average diameter from 0.1 µm to 5 µm, and an aspect ratio of 1,000 to 1. In particular, the glass fibers may have an average fiber diameter of 0.4 to 2.6 µm.

[0052] Glass fibers are preferably included in a sufficient amount to improve efficiency of the fibrous media as a filter. In one embodiment, the synthetic fibers comprise up to 30 wt.-%, preferably up to 20 wt.-%, based on the total weight of the fibers, of glass fibers. Although the synthetic fibers comprise only up to 30 wt.-% or up to 20 wt.-% of glass fibers, based on the total weight of the fibers, this amount is sufficient to prepare a fibrous media for a filter having excellent particle removal efficiency and hot oil burst strength as shown in the examples. Typically, synthetic filter media of the prior art include a high amount of glass fibers for achieving a sufficient filtration efficiency of a gas or a liquid, even under high temperature conditions such as e.g. 150°C. However, by using less glass fibers in the fibrous media as set forth in the claims, fibrous media may be provided that have excellent filtration properties in terms of particle removal efficiency and hot oil burst strength.

[0053] In particularly preferred embodiments, there are at least two kinds of glass fibers present, viz. a first group of fibers having an average fiber diameter of less than 1 µm and a second group which having an average fiber diameter of 2 µm or more. The weight ratio of the two groups of fibers is typically 1:100 to 100:1, in particular about 1:10 to 10:1.

[0054] The synthetic fibers may also include up to 40 % by weight, preferably up to 30 % by weight, based on the total weight of the fibers, of a regenerated cellulosic material, such as Lyocell or viscose or combinations thereof.

[0055] The fibrous media used in an oil filter may comprise a fibrous web formed from, or comprising,
  • a first fibrous component consisting of synthetic thermoplastic fibers, the synthetic fibers having an average diameter from 0.1 um to 10 um and an average length from 1 to 20 mm; and
  • a second fibrous component consisting of silicious fibers; the fibers of the first fibrous component forming a majority of the fibers of the fibrous web such as up to 70 % by weight, based on the total weight of the fibrous components; and
  • a thermoset binder present at a concentration of at least 15 %, by weight of the fibrous web.


[0056] The fibrous web may comprise a combination of first and second fibrous components, wherein
  • the first fibrous component forms 70 % to 88 % of the fibrous web by weight;
  • the second fibrous components, of for example glass fibers, forms 12 % to 30 % of the fibrous web by weight.


[0057] In preferred embodiments, the synthetic fibers may also include undrawn synthetic fibers such as undrawn thermoplastic synthetic fibers. Undrawn fibers are common in the art. Although undrawn fibers typically do not have the mechanical properties such as tensile strength and modulus that are required for practical use, it was surprisingly found out that undrawn fibers may improve the web's capability for retaining not only pleats but also corrugation upon contact with oil having a temperature in the range encountered in a combustion engine such as 125 to 135°C. They may also contribute to improve the filter efficiency of the filter as defined herein.

[0058] Undrawn fibers may be comprised up to 50 % by weight, preferably up to 45 % by weight, such as from 20 to 50 % by weight or from 20 to 40 % by weight, based on the total weight of the fibers.

[0059] Preferred are undrawn PET fibers. The undrawn fibers may preferably have an average fiber length of about 1 to 10 mm, such as about 5 to 10 mm.

[0060] By using undrawn synthetic fibers and by e.g. calendering the resulting wet-laid fibrous web under heat (e.g. up to 220°C) and pressure using both top and bottom hot smooth rolls, the void fraction of the obtained fibrous web may be preferably adjusted in the range of approximately 70-95 %, such as 80-90 % which may be particularly beneficial for corrugation. This is because if, on the one hand, the void fraction is too low, the corrugation is easily embossed, but the filter properties of the resulting corrugated fibrous web are not sufficient. If, on the other hand, the void fraction is too high, then the fibrous web cannot be corrugated in the most preferred corrugation depth such as 0.1-0.6 mm. Moreover, the calendering may add strength for the further processing steps such as the corrugation, impregnation with the thermoset binder and/or pleating.

[0061] Without being bound by this theory, it is believed that the undrawn fibers may basically act as additional binder fibers, since they contract after being heated under the manufacturing conditions as described below in example 1.

[0062] The used media further includes a binder, in particular a thermoset binder, which preferably has a concentration of 15 % to 50 % by weight of the fibrous web or a binder fiber as defined below. The thermoset binder is preferably selected from phenolic resin, acrylic resin and/or epoxy resin and melamine resin or acrylic resins, or mixtures thereof. The concentration of the thermoset binder is selected such that effectively most of the fibers of the fibrous mixture are coated with the thermoset binder.

[0063] The fibrous media may comprise a coating made of thermoset binder, selected from the group of phenolic resins, acrylic resins, epoxy resins, melamine formaldehyde resins and combinations thereof.

[0064] Preferably the thermoset binder has a concentration of from 15 % to 30 % of the fibrous web by weight.

[0065] To further improve internal bonding between the fibers of the media, for example between the first and second fibers, bicomponent thermoplastic fibers (as specific binder fibers) can be employed. Such fibers typically comprise a thermoplastic core fiber surrounded by a meltable surface layer of a thermoplastic polymer which as a lower melting point than the material forming the core. The low melting point thermoplastic polymer may act as a thermoplastic binding agent when softened or partially melted during processing of the fibrous web by heating, thereby adhering to the fibers of the web. The higher melting material forming the core may act as a structural material. The average fiber diameter of these bicomponent thermoplastic fibers may be preferably in the range of about 2 to 20 µm such as 10 µm and the average fiber length of these bicomponent thermoplastic fibers may be preferably in the range of about 2 to 12 mm, such as about 6 mm. The amount of such fibers is 0.1 to 20 % by weight, preferably about 0.5 to 5 % by weight, based on the total weight of fibers.

[0066] Moreover, to further improve internal bonding between the fibers of the web, for example between the first and second fibers, other binder fibers can be employed. Such binder fibers are preferably thermoplastic binder fibers such as PET binder fibers or polyvinyl alcohol (PVOH) binder fibers. These binder fibers have typically a lower melting point than the synthetic fibers, thereby acting as a binding agent when softened or partially surface-melted during processing of the fibrous web by heating. Alternatively, these binder fibers do not melt, but begin to partially dissolve in the solvent used for the manufacturing process (i.e. water) and become tacky. The tacky or softened binder fibers are therefore capable of internally binding the fibers of the web by adhering to the fibers and structurally strengthening the thus obtained fiber web. The average fiber diameter of these binder fibers may preferably be in the range of about 2 to 20 µm such as 10 µm and the average fiber length of these binder fibers may preferably be in the range of about 2 to 12 mm, such as about 6 mm. The amount of such fibers may be 0.1 to 25 % by weight, preferably about 0.5 to 20 % by weight, such as 2 % by weight, based on the total weight of fibers.

[0067] The present web optionally includes at least one additive which is common in the art. The at least one additive may be selected from a flame-retardant agent, a coloring agent, a hydrophobic agent, a hydrophilic agent, a wetting agent, an antimicrobial agent or an antistatic agent.

[0068] In an embodiment, the fibrous media may further comprise a nanofiber coating made of nanofibers, in particular electrospun nanofibers such as those selected from polyethersulfone (PES) or polyamide (PA) nanofibers. The nanofiber coating may preferably have a thickness of about 50 to 1000 nm. The nanofiber coating may preferably have a loading of about 0.5 to 5.0 g/m2. The nanofibers may preferably have an average fiber diameter of about 50 to 500 nm such as about 100 to 300 nm. Preferably, the nanofiber coating may be applied on top of the fibrous web being impregnated with the thermoset binder.

[0069] The fibrous media is prepared generally by mixing fibers of at least one first fibrous component, optionally with at least one binder fiber and/or at least one additive, to form a fibrous web. The process is disclosed in more detail in example 1.

[0070] According to a preferred embodiment the fibrous web of the present disclosure further has the following properties:
  • the basic weight between 50 and 400 gsm;
  • an air permeability for oil application of between 2 and 600 cfm/sf; and
  • a burst strength after 500 hours in hot oil having e.g. a temperature of 140°C of at least 20 psi.


[0071] Unless otherwise indicated, all parameters of the fibrous web described herein were determined according to the tests methods described below in the examples.

[0072] In the test methods below, 1 psi = 6.89 kPa, 1 mils = 0.0254 mm , 1 mg/in2 = 0.155 mg/cm2.

[0073] Furthermore, typical properties of the fibrous media are the following at a caliper (TMI) of 20 to 60 mils:
  • burst strength, dry (saturated and dried web, SD) typically 25 to 90 psi, in particular 28.5 to 85.0 psi;
  • burst strength, wet (saturated and dried web, SD) typically 10 to 90 psi, in particular 12 to 82.0 psi;
  • 500 hour hot oil burst 20 to 50 psi.


[0074] Furthermore, typical properties of the fibrous media are the following at a caliper (TMI) of 20 to 60 mils:
  • burst strength, dry (saturated, dried and cured web, SDC) typically 30 to 80 psi;
  • burst strength, wet (saturated, dried and cured web, SDC) typically 30 to 90 psi.


[0075] In an embodiment, stiffness (machine direction, MD, saturated and dried, SD) of a filter media having a caliper of 20 to 60 mils is typically 3,300 to 10,000 mg, in particular about 5,000 to 8,000 mg.

[0076] In an embodiment, stiffness (machine direction, MD, saturated, dried and cured, SDC) of a filter media having a caliper of 20 to 60 mils is typically 3,200 to 16,800 mg.

[0077] In an embodiment, filtering efficiency of a web having a caliper of 20 to 60 mils against particles having a particle size of 15 microns is: 20 to 99%, in particular about 25 to 98%. Dirt holding capacity: 70 to 150 mg/in2, in particular 95 to 145 mg/in2.

[0078] "Saturated and dried" stands for a medium having a total content of volatiles of less than 7 % by weight at room temperature, based on the total weight of the medium.

[0079] "Saturated, dried and cured" stands for a medium having a total content of volatiles of less than 7 % by weight at room temperature, based on the total weight of the medium which has been fully cured.

[0080] A method of making a filter media of any of the above-discussed embodiments comprises typically the steps of
  • forming a wet laid web from a fibrous slurry comprised of synthetic fibers and optionally at least one additive and/or at least one binder fiber in water;
  • drying the web to a low moisture content, preferably a moisture content of 2 % or less;
  • contacting the dried web with a composition of a thermoset binding agent in a liquid phase to bond the fibers together with the thermoset binder;
  • removing the liquid phase to form a web;
  • optionally pre-curing and/or corrugating the web; and
  • pleating the web, optionally followed by a final curing step.


[0081] The concentration (solid matter) of the binding agent in the liquid phase composition is suitably about 10 to 50 % by weight, based on the total weight of the liquid phase composition.

[0082] In the step of contacting the dried web with a binding agent, the dried web is preferably saturated with a liquid composition of the thermoset binding agent on one or both sides. After the saturation step, the liquid phase, i.e. the solvent or dispersing agent, of the composition is removed. For removing the liquid phase the medium is preferably heated.

[0083] Optionally, the dried medium may be pre-cured by an additional heating step prior to pleating and/or corrugation. "Pre-curing" refers to a partial curing of the thermoset binder resin up to e.g. 65 % or 100 %.

[0084] The liquid phase of the binding agent composition is, in one embodiment, removed such that the volatiles content is reduced to less than 10 wt.-%, in particular less than 8 wt.-%, calculated from the total weight of the treated web prior to optional corrugation.

[0085] The content of volatiles refers to the amount of volatile components left in the web at ambient (room) temperature.

[0086] The media can be optionally corrugated. In one embodiment, the corrugation may be formed after impregnation of the fibrous web with a thermoset binder by heating (or drying) the fibrous web to approximately 180-220°C between resin coating rolls and corrugation rolls, followed by heating (or drying) the thus obtained corrugated fibrous media below 80°C in order to prevent the collapse of the corrugation by high heating. Corrugation techniques are commonly known in the art.

[0087] The manufacturing method is examined in more detail in connection with Example 1.

[0088] The media can be pleated and optionally fully cured as described in more detail in Example 3.

[0089] A fibrous media according to the present technology is capable of forming a self-supporting oil filter media which retains its pleats and corrugations during periods of normal operation.

[0090] Typically, the present media is capable of retaining the pleats and optionally corrugations even upon a contact with oil, in particular oil having a temperature of up to about 140°C. Thus, the self-supporting, pleated and optionally corrugated oil filter media is capable of retaining pleats and optional corrugations upon contact with oil having a temperature in the range encountered in a combustion engine such as 125 to 135°C.

[0091] As preliminarily discussed above, it is known that e.g. heavy duty diesel engines may have internal cracks in the gaskets within their cooling system which gives rise to a leaking of the ethylene glycol of the coolant into the lube oil of the lubrication system. The combination of glycol with hot oil may have a dramatic influence on synthetic filter media, i.e. these media may lose their integrity and may even dissolve completely in the oil glycol mixture at elevated engine operating temperature.

[0092] By contrast, in the present invention it was observed that the solubility of the fiber media according to the invention in glycol oil mixture is reduced or completely eliminated when the fibers are impregnated or coated with a binder selected from the group of thermoset binder resins like melamine-based resins, such as melamine formaldehyde.

[0093] According to an embodiment, the present disclosure concerns an oil filter according to the present invention comprising corrugated fibrous media. The filter according to the present disclosure is especially suitable for use in lube oil systems because of its high temperature integrity. A "filter" refers to a filter device (or filter arrangement) comprising the filter media as defined above being pleated and optionally corrugated and being disposed between a pair of end plates in such a manner so as to form a hollow cylinder.

[0094] The web of the present disclosure may be used in a laminated media product. Since the fibrous media according to the present disclosure contains a very high percentage of synthetic fibers, it is bondable to other materials in a lamination process using heat bonding, ultrasonic bonding, etc. It may also be laminated using standard water-based or hot-melt glues.

[0095] The examples below discuss the production of filter media used in the invention.

[0096] Figure 2 shows the natural logarithm (In) of the hot oil burst strength of (i) an exemplary web of the present disclosure and (ii) standard oil media as a function of time. The slope of the natural logarithm (In) burst graph shown in Figure 2 is considered to be the degradation rate of the media. The slope of the media according to the present disclosure is half of that of wood pulp-containing prior art media. Accordingly, the media according to the present disclosure has higher burst strength for a significantly longer period of time on exposure to hot engine oil when compared to a wood pulp-containing media.

[0097] It was observed that the groove depth (or corrugation depth) of the media according to the present disclosure is stable in hot engine oil and is directly comparable to the groove depth retention in a typical wood pulp-containing media. It is also observed that the relatively heavy basis weight of the fibrous media according to the present disclosure, coupled with the relatively high % resin content of the sheet (e.g. at least 15 % or 25% resin content) and the use of a phenolic resin system all combined to give the media excellent grooving and pleating characteristics as well as high durability in hot oil.

Examples


Test methods



[0098] Basis Weight: The basis weight is measured according to TAPPI Standard T 410 om-02 and reported in grams per square meter (gsm).

[0099] Caliper or Thickness: The caliper or thickness of the media is determined according to TAPPI Standard T 411 om-05 using a Thwing Albert 89-100 Thickness Tester.

[0100] Corrugation Depth is the difference between the caliper of the flat sheet of media and the thickness of the sheet after corrugating the media.

[0101] Air Permeability: The air permeability, or "air perm", of the media is measured according to TAPPI Standard T 251 cm-85 ("Air Permeability of Porous Paper, Fabric and Pulp Handsheets) with 0.5 inch (2.7 mm) water differential using a Textest AG (model FX3300) and reported as the rate of the flow of air in cubic feet per square foot of sample area per minute (cfm/sf), sometimes referred to as cfm. Air Perm may also be referred to porosity, Frazier or Textest 1 cfm/sf = 5.08 1/m2/s.

[0102] Burst Strength: The wet and dry burst strength is measured according to TAPPI Standard T 403 om-22 ("Bursting Strength of Paper") and reported in kgf/cm2.

[0103] Stiffness of the media was determined according to TAPPI T 489 om-92 using a Gurley bending resistance tester MOD 4171D (Gurley Precision Instruments).

[0104] Pore Size: The size of the pores in the media was determined using a bubble point method according to ASTM 316-03 (2011) utilizing a Porometer G3 Series (Quantachrome Instruments) and reported in microns (µm).

[0105] Void fraction was determined by an imbibition method by immersing the filter to be analyzed, under vacuum, in n-butyl alcohol that wets the pores (filter size: 40mm × 40mm; vacuum pump: 0.133 Pa (ultimate pressure), 50L/min exhaust rate; use a direct-reading balance having a resolution of at least 0.1 mg).

[0106] Dust Holding Capacity/Particle Removal Efficiency: Following ISO 4548-12 for lube oil filtration using a Multipass system, the DHC (Dust Holding Capacity) and particle removal efficiency was determined for the media. The media is tested as a flat sheet with a test flow of 0.5 L/min, particle injection flow of 250 mL/min, BUGL (Basic Upstream Gravimetric Level) of 60 mg/L (ISO Medium Test Dust), a terminal pressure drop of 12.3 psi, a circular shaped sample test diameter of 6.375 inches, and a face velocity of 3.624 inches per minute.

[0107] Hot Oil Ageing, in order to determine the hot oil burst strength, is done by placing a media sample (size: 14 x 10 cm) into an oil bath of typical engine oil (e.g. Mobil 1) maintained at 140 C +/- 0.1°C for 500 hr. "Hot oil burst strength" of a media sample is defined as the maximum hydrostatic pressure required to result in rupture of the media sample when a controlled and constantly increasing pressure is applied through a rubber diaphragm to an area of 7.07 cm2. The media sample is then removed, cooled for about 5 minutes, and excess oil is blotted from the sample. Then, the moisture free sample is tested using a Mullen burst strength tester. The results are reported in force per unit area at failure (e.g. kg/cm2 or psi).

[0108] Unless otherwise indicated, the unit "um" corresponds to "µm" or micron.

Manufacture of filter material (Example 1)



[0109] The production process for making a filtration media comprises for example a wet-laid process. In such a process, the fibrous material is first disintegrated for example in a hydropulper optionally in the presence of a fiber dispersant chemical additive such as a surfactant for keeping the fibers separated when added and to prevent the fibers from entangling during handling. If microglass is being disintegrated, the pH of the hydropulper may also be adjusted to a pH in the range of 2 to 5 using an acid in order to prevent the microglass fibers from clumping together and to promote even dispersion of the microglass fibers. Fibers of each desired variety are then added to the hydropulper in their respective correct proportion according to the furnish recipe. A consistency (fiber weight to water volume) of about 1 to 10 %, in particular about 5 % is preferred at the mixing stage.

[0110] After an optional refining stage, the fiber furnish is then diluted down to a consistency of about 0.01 - 0.02 % and formed into a web on a paper machine wire. A single layer or multiple layer headbox design may be employed. If a multiple layer headbox design in employed, more than one designed furnish blend may be deposited in series onto the paper machine wire, thereby creating a multi-layer wet-laid composite.

[0111] Once on the paper machine wire, the water content of the wet-laid furnish is drained through the moving paper machine wire by a series of hydrofoils and vacuum boxes until the percent solids content of the sheet is approximately 30 to 40 wt-%. In a subsequent dryer section, the web is dried to approximately a moisture content of 2 % or less.

[0112] The binder resin is then introduced to the sheet, preferably at a saturator machine. The resin may be applied on either one or both sides of the sheet. The process may be adjusted to achieve either 1- or 2-sided saturation of the sheet. The solids content of the resin bath applied to the sheet is typically between 20 to 40 wt-%. The resin bath solids content is chosen based on multiple processing (equipment) and application (into the web) considerations. Besides the solids content, the balance of the resin bath composition is a solvent such as methanol, water, and/or other solvent components.

[0113] After the resin is applied to the sheet, the solvent is liberated by heating the web to an elevated temperature such that the solvent evaporates at a rate fast enough to accommodate the desired production throughput. Heating may involve the use of steam cans, ovens, a combination of both, and/or other heating technologies. The obtained media may be referred to as being "saturated and dried (SD)".

[0114] After the solvent removal, the media may be pre-cured by heating to an elevated temperature such that the binder resin partially (e.g. to 25-65 %) and/or completely cures. Heating may involve the use of steam cans, ovens, a combination of both, and/or other heating technologies. The thus obtained media being completely cured may be referred to as being "saturated, dried and cured (SDC)".

[0115] During this drying process groove patterns (corrugation), if applicable, can be also imparted on the sheet. This may be most preferably done by calendering the resulting wet-laid fibrous sheet under heat (up to 220°C) and pressure using both top and bottom hot smooth rolls, thereby preferably adjusting the obtained sheet's void fraction in the range of approximately 70-95 %, such as 80-90 % which is beneficial for corrugation. The percent volatiles content is reduced in the drying process to a predetermined level of about 1 to 10 %, in particular to about 4 to 6 %, by weight of the web.

[0116] Compositions of exemplary media (Samples 1 and 2) according to the present disclosure are shown in Table 1.
Table 1. Summary of furnish compositions Samples 1 and 2
FiberSample 1Sample 2
4mm "PVOH fiber", average fiber diameter: 10 µm (binder fiber) 2.0% by weight -
glass fibers, average fiber diameter: 0.65 µm 4.0% by weight 10.0% by weight
glass fibers, average fiber diameter: 2.44 µm 16.5% by weight 10.0% by weight
PET 0.3D*5mm, average fiber diameter: 5.5 µm 16.4% by weight 30.3% by weight
PET 0.8D*5mm - 11.0% by weight
PET 0.8D*6mm, average fiber diameter: 9.06 µm 6.6% by weight -
Lyocell 1.7Dt*4mm, unfibrillated, average fiber diameter: 11.5 µm 34.5% by weight -
Undrawn PET 1.6D*5mm 20.0% by weight 38.7% by weight
Resin content 25 % by weight phenolic (phenol formaldehyde resin) 25 % by weight melamine
Cellulosic content 34.5 % by weight -
Glass content 20.5 % by weight 20.0 % by weight
Total content of thermoplastic fibers 45.0 % by weight 80.0 % by weight


[0117] Properties of the exemplary webs according to the present disclosure are shown in Table 2.
Table 2. Properties of exemplary webs (Samples 1 and 2)
 UnitSample 1Sample 2
Basis weight (SD) lb/3000 ft2 162.0 114.7
g/m2 263.6 186.6
Basis weight (SDC) lb/3000 ft2 150.8 109.3
g/m2 245.4 177.8
Textest air permeability cfm 39.8 28.8
TMI Caliper (or thickness) mils 52.3 36.2
mm 1.33 0.92
Groove (or corrugation) depth (see Figure 5) mils 18.0 5.0
mm 0.46 0.13
Mean pore (manual) µm 18.2 15.6
Burst - dry, SD psi 28.5 80.0
Burst - wet, SD psi 18.5 65.0
Burst - dry, SDC psi 36.0 74.0
Burst - wet, SDC psi 48.0 67.0
Stiffness, MD SD mg 4 900 7 900
Stiffness, MD SDC mg 9 100 6 800
Particle removal efficiency against particles having a particle size of 15 microns % 81.9 96.2
Dirt holding capacity (DHC) mg/in2 144.1 100.9
mg/cm2 22.3 15.6
500 hour hot oil burst (Hot Oil Ageing) psi 23.3 43.0
kPa 160.9 297
kgf/cm2 1.64 3.02
1 cfm/sf = 5.08 1/m2/s

Example 2 (Samples 3-6):



[0118] Using the method described in Example 1, filter media impregnated with melamine resin were produced (Samples 3-6). For Samples 5 and 6, an additional calendaring step for adjusting the void fraction to a range of about 70-95 %, as discussed above, was used for preparing the corrugated filter media. Corrugation on the sheet was imparted during the drying process at a temperature of about 180-220°C, followed by a temperature below 80°C after the corrugation was completed. The compositions of Samples 3-6 are given in Table 2a below.

[0119] The properties of the filter media thus obtained are indicated in Tables 3 and 4. The medium of Sample 3 is suitable for, e.g., motorcycle fuel media filters. The medium of Sample 4 is self-supporting, washable and plain e.g. flat. It is suitable for, e.g., lube (oil) and air applications. The medium of Sample 5 is self-supporting, washable and corrugated and suitable for, e.g., lube (oil) and air applications.
Table 2a. Summary of furnish compositions Samples 3, 4, 5 and 6
FiberSample 3Sample 4Sample 5Sample 6
Glass fibers, average fiber diameter: 0.65 µm 8.0% by weight 10.0% by weight 10.0% by weight -
Glass fibers; average fiber diameter: 0.53 µm; - - - 8.0% by weight
Glass fibers, average fiber diameter: 2.44 µm - 10.0% by weight 10.0% by weight 13.3% by weight
PET 0.05D*6mm 8.9% by weight - - -
PET 0.3D*5mm, average fiber diameter: 5.5 µm 17.8% by weight 30.3% by weight 30.3% by weight 43.7% by weight
PET 0.8D*5mm 17.8% by weight 11.0% by weight 11.0% by weight -
PET 1.4D*6mm 8.9% by weight - - -
PET 3.0D*5mm 8.9% by weight - - -
Undrawn PET 1.6D*5mm 29.7% by weight 38.7% by weight 38.7% by weight 35.0% by weight
Resin content (= amount of resin based on the total weight of the fibrous media) 18.5% by weight melamine 21.9 % by weight melamine 17 % by weight melamine 23% by weight melamine
Glass content 8.0 % by weight 20.0 % by weight 20.0 % by weight 20.0 % by weight
Total content of thermoplastic fibers 92.0 % by weight 80.0 % by weight 80.0 % by weight 80.0 % by weight
Table 3. Properties of Filter Media (Samples 3, 4 and 5).
Physical properties Sample 3Sample 4Sample 5
Mass per unit area (basis weight)   g/m2 SD 216.8 199.8 187.2
  SDC 208.3 193.2 181.7
Thickness 20 kPa mm Total - - 1.008
Caliper 1.334 1.098 0.893
Corrugation depth   mm   - - 0.115
Air permeability 125 Pa cfm/sq .ft   32.1 30.8 28.5
Burst Strength, dry   kgf/cm2 SD 3.19 4.87 4.22
  psi 45.4 69.3 60.0
Pore Size   µm Max 63.9 44.0 47.4
  Mean 54.6 39.7 41.8
Stiffness   mg SD 5957 9778 4801
Dirt holding capacity   mg/in2   74.1 73.7 90.8
  (mg/cm2)   (11.48) (11.42) (14.07)


[0120] The properties of the filter medium of Sample 6 are indicated in Table 4. The medium is self-supporting, pleatable and corrugated.
Table 4. Properties of exemplary Filter Medium (Sample 6).
Overall filtration efficiency (ISO 4548-12) against particles having the following particle size:
>10 µm 96.6%
>12 µm 99.1%
>15 µm 99.9 %
>17 µm 100,0 %
>20 µm 100,0 %
>25 µm 100,0 %
>30 µm 99.9 %
>40 µm 99.9 %
Corrugation depth 0.15-0.6 mm

Example 2a:



[0121] Using the method described in Example 1, a filter medium comprising a binder fiber and being impregnated with melamine resin (Sample 7) or a filter medium comprising a binder fiber (Samples 8 to 9) was produced. The compositions of Samples 7-9 and Comparative Samples 1-3 are given in Tables 5 and 6 below.
Table 5. Summary of furnish compositions Sample 7 and Comparative Samples 1-3 (see also Figure 2)
FiberSample 7Comparative Sample 1Comparative Sample 2Comparative Sample 3
Softwood fibers - 57.0 % by weight 70.7 % by weight 31.7% by weight
Hardwood fibers - 13.3 % by weight 3.0% by weight 50.7 % by weight
Glass fibers, average fiber diameter: 2.44 µm 15.5% by weight - 2.3% by weight -
Glass fiber, average fiber diameter: 0.65 µm - - 6.0% by weight 3.3% by weight
PET 0.3D*5mm, average fiber diameter: 5.5 µm 33.2% by weight - - -
PET 0.8D*6mm 10.3% by weight - - -
Reliance 1.5d x 1/4" polyester - 30.0% by weight 18.0% by weight 14.3% by weight
Lyocell 1.7Dt*4mm, unfibrillated, average fiber diameter: 11.5 µm 31.5% by weight - - -
Binder PET 2.0D*6mm (binder fiber) 9.5% by weight - - -
Resin content (= amount of resin based on the total weight of the fibrous media) 25 % by weight phenolic 26.0 % by weight phenolic 22.0 % by weight phenolic 18.0 % by weight phenolic
Cellulosic pulp content - 60.0% by weight 73.7% by weight 82.4% by weight
Glass content 15.5 % by weight - 8.3% by weight 3.3% by weight
Total content of thermoplastic fibers 84.5 % by weight 30.0% by weight 18.0% by weight 14.3% by weight


[0122] The hot oil burst strength properties of the filter media thus obtained (Sample 7 and Comparative Samples 1-3) are shown in Figure 2.
Table 6. Summary of furnish compositions Samples 8-9.
FiberSample 8Sample 9
PET 0.06 Dt*3mm 14.8% by weight 14.8% by weight
PET 03D*5mm, average fiber diameter: 5.5 µm 65.6% by weight 65.6% by weight
Binder 4.0D*6mm (bicomponent binder fiber) 19.7% by weight 19.7% by weight
Nanofiber coating PES PA
(thermoplastic, 50-1000 nm) (thermoplastic, 50-1000 nm)
Resin content acrylic resin, 7% by weight acrylic resin, 7% by weight
Glass content - -
Total content of thermoplastic fibers 100.0 % by weight 100.0 % by weight

Example 3: Pleating of material



[0123] The material can be pleated to provide a suitable self-supporting, pleated, stand-alone structure.

[0124] In the pleating process the media is loaded between two rollers. The nip gap between the roller and the scoring head between the nip gap helps to form the fold mark for the pleat. The pleat is formed by the forward movement of the media post fold mark. The fold is then made to move through a preheating zone at 150 to 160 °C with a very short residence time 15-120 sec.

[0125] The folded media can then be allowed to pass through an oven to complete residual cure at 180 °C or higher for a residence time of 5-10 min. The curing oven is optional and used only if the media is uncured or partially cured at the previous stage.

[0126] The pleatability of a material can be assessed by the pleat angle which will reflect the extent or ease of forming a pleat.

[0127] On the other hand, an important feature of the present invention is the combination of ease of pleat forming during manufacturing of the fibrous media and pleat-retention upon contact with hot oil.

[0128] An exemplary pleated self-supporting web according to present disclosure processed as described above is shown in Figure 3, wherein reference numeral 11 refers to the pleated material.


Claims

1. A pleated, self-supporting oil filter comprising a pleated
fibrous media comprising a fibrous web formed from

- synthetic fibers;

- optionally at least one additive; and

- a thermoset binder present at a concentration of at least 15 wt-% by weight of the fibrous web and/or at least one binder fiber;

wherein the synthetic fibers comprise up to 30 wt.-%, preferably up to 20 wt.-%, glass fibers, based on the total weight of the fibers;

wherein the synthetic fibers are bonded with the thermoset binder and/or the at least one binder fiber to form the fibrous web; and the fibrous media is capable of forming said self-supporting, pleated oil filter which is capable of retaining pleats upon contact with oil having a temperature in the range encountered in a combustion engine; and

wherein the filter comprises the fibrous media without a support backing material.


 
2. The oil filter according to claim 1, wherein the fibrous web comprises synthetic fibers selected from the group of thermoplastic polymers, silicious fibers, such as glass fibers, regenerated cellulosic fibers and mixtures thereof, at least 30 wt.-%, preferably at least 50 wt.-% of the fibers being thermoplastic polymers.
 
3. The oil filter according to claim 1 or 2, wherein the fibrous web contains (i) at least 70 wt.-% fibers of thermoplastic polymer(s) and up to 40 or up to 30 wt.-% regenerated cellulosic fibers; (ii) at least 70 wt.-% fibers of thermoplastic polymer(s); or (iii) no regenerated cellulosic fibers such as Lyocell or viscose or combinations thereof.
 
4. The oil filter according to any of the preceding claims, wherein the fibrous web is impregnated with the thermoset binder which is preferably selected from thermoset resins, such as phenolic resins, epoxy resins or melamine-based polymers, such as melamine formaldehyde, or acrylic resins, or combinations thereof.
 
5. The oil filter according to any of the preceding claims, wherein the binder fiber is selected from a bicomponent binder fiber, a polyethylene terephthalate (PET) binder fiber or a polyvinyl alcohol (PVOH) binder fiber; and/or wherein the at least one additive is selected from a flame-retardant agent, a coloring agent, a hydrophobic agent, a hydrophilic agent, a wetting agent, an antimicrobial agent or an antistatic agent.
 
6. The oil filter according to any of the preceding claims, wherein the fibrous media comprises 15 to 30 %, in particular 20 to 25 %, of the thermoset binder, the concentration of which is calculated based on the total weight of the fibers.
 
7. The oil filter according to any of the preceding claims, wherein the synthetic fibers comprise first fibers, having a first average diameter such 2 µm or more, and second fibers, having a second average diameter less than 1 µm, the first average length being greater than the second average length.
 
8. The oil filter according to any of the preceding claims, wherein the synthetic fibers comprise undrawn fibers such as undrawn thermoplastic polyethylene terephthalate fibers, preferably in an amount of 15 to 50% by weight, more preferably 20 to 40% by weight, based on the total weight of fibers; and/or wherein the synthetic fibers are thermoplastic fibers selected from the group of polyesters, for example polyalkylene terephthalates, such as polyethylene terephthalate (PET), polybutylene terephthalate (PBT) and the like, polyalkylenes, for examples polyethylenes, polypropylenes and the like, polyacrylonitriles (PAN), and polyamides, for example nylons, such as nylon-6, nylon-6,6, nylon-6,12, and the like, and combinations thereof.
 
9. The oil filter according to any of the preceding claims, wherein the synthetic fibers comprise thermoplastic synthetic fibers having an average diameter from 0.1 µm to 15 µm, preferably 0.1 µm to 10 µm and an average length from 1 to 50 mm such as 1 to 20 mm; and/or wherein the glass fibers have an average fiber diameter of 0.4 to 2.6 µm.
 
10. The oil filter according to any of the preceding claims, wherein the synthetic fibers include up to 40 % by weight, preferably up to 30 % by weight, based on the total weight of the fibers, of a regenerated cellulosic material, such as Lyocell or viscose or combinations thereof.
 
11. The oil filter according to any of the preceding claims, wherein the fibrous web has an average thickness of 0.6 to 1.5 mm, in particular 0.7 to 1.4 mm and/or wherein the fibrous web is corrugated, preferably by a corrugation depth of about 0.1 to 0.5 mm.
 
12. The oil filter according to any of the preceding claims, wherein the fibrous media further comprises a nanofiber coating, wherein the nanofiber coating includes electrospun nanofibers, such as polyethersulfone (PES) or polyamide (PA) nanofibers, and preferably has a thickness of 50 to 1000 nm; and/or wherein the fibrous web is wet-laid.
 
13. The oil filter according to any of the preceding claims, wherein

- the fibers of the thermoplastic polymer form 60 % to 88 % of the fibrous web by weight;

- the glass fibers form 2 % to 30 % of the fibrous web by weight; and

- the fibrous web further comprises a coating made of the thermoset binder composed of a phenolic resin, an acrylic resin, an epoxy resin or a melamine formaldehyde, wherein the amount of the binder is from 15 % to 30 wt.-% by weight of the fibrous web.


 
14. The oil filter according to any of the preceding claims, wherein the fibrous media is corrugated.
 
15. Use of the oil filter according to any of the preceding claims for the filtration of oil in an internal combustion engine.
 


Ansprüche

1. Ein plissierter, selbsttragender Ölfilter, umfassend ein plissiertes Fasermedium, umfassend ein Faservlies, gebildet aus

- synthetischen Fasern;

- gegebenenfalls mindestens einem Additiv; und

- einem duroplastischen Bindemittel in einer Konzentration von mindestens 15 Gew.-% bezogen auf das Gewicht des Faservlieses und/oder mindestens eine Bindemittelfaser;

wobei die synthetischen Fasern bis zu 30 Gew.-%, bevorzugt bis zu 20 Gew.-%, Glasfasern umfassen, bezogen auf das Gesamtgewicht der Fasern;

wobei die synthetischen Fasern mit dem duroplastischen Bindemittel und/oder der mindestens einen Bindemittelfaser gebunden sind, um das Faservlies zu bilden; und das Fasermedium in der Lage ist, den selbsttragenden, plissierten Ölfilter zu bilden, der in der Lage ist, Plisseefalten bei Kontakt mit Öl beizubehalten, das eine Temperatur in dem Bereich aufweist, der in einem Verbrennungsmotor vorkommt; und

wobei der Filter das Fasermedium ohne ein unterstützendes Trägermaterial umfasst.


 
2. Der Ölfilter gemäß Anspruch 1, wobei das Faservlies synthetische Fasern, ausgewählt aus der Gruppe aus thermoplastischen Polymeren, siliziumdioxidhaltige Fasern wie etwa Glasfasern, regenerierten Cellulosefasern und Gemischen davon umfasst, wobei mindestens 30 Gew.-%, bevorzugt mindestens 50 Gew.-%, der Fasern thermoplastische Polymere sind.
 
3. Der Ölfilter gemäß Anspruch 1 oder 2, wobei das Faservlies (i) mindestens 70 Gew.-% Fasern (eines) thermoplastischen/-er Polymers/-e und bis zu 40 oder bis zu 30 Gew.-% regenerierte Cellulosefasern; (ii) mindestens 70 Gew.-% Fasern (eines) thermoplastischen/-er Polymers/-e; oder (iii) keine regenerierten Cellulosefasern wie etwa Lyocell oder Viskose oder Kombinationen davon enthält.
 
4. Der Ölfilter gemäß einem der vorhergehenden Ansprüche, wobei das Faservlies mit dem duroplastischen Bindemittel imprägniert ist, das bevorzugt ausgewählt ist aus duroplastischen Harzen wie etwa Phenolharzen, Epoxidharzen oder Polymeren auf Melaminbasis wie etwa Melaminformaldehyd oder Acrylharzen oder Kombinationen davon.
 
5. Der Ölfilter gemäß einem der vorhergehenden Ansprüche, wobei die Bindemittelfaser ausgewählt ist aus einer Zweikomponenten-Bindemittelfaser, einer Polyethylenterephthalat (PET)-Bindemittelfaser oder einer Polyvinylalkohol (PVOH)-Bindemittelfaser; und/oder wobei das mindestens eine Additiv ausgewählt ist aus einem flammhemmenden Mittel, einem farbgebenden Mittel, einem hydrophoben Mittel, einem hydrophilen Mittel, einem Benetzungsmittel, einem antimikrobiellen Mittel oder einem antistatischen Mittel.
 
6. Der Ölfilter gemäß einem der vorhergehenden Ansprüche, wobei das Fasermedium 15 bis 30 %, insbesondere 20 bis 25 %, des duroplastischen Bindemittels umfasst, wobei dessen Konzentration bezogen auf das Gesamtgewicht der Fasern berechnet ist.
 
7. Der Ölfilter gemäß einem der vorhergehenden Ansprüche, wobei die synthetischen Fasern erste Fasern mit einem ersten durchschnittlichen Durchmesser wie 2 µm oder mehr und zweite Fasern mit einem zweiten durchschnittlichen Durchmesser von weniger als 1 µm umfassen, wobei die erste durchschnittliche Länge größer als die zweite durchschnittliche Länge ist.
 
8. Der Ölfilter gemäß einem der vorhergehenden Ansprüche, wobei die synthetischen Fasern ungestreckte Fasern umfassen wie etwa ungestreckte thermoplastische Polyethylenterephthalat-Fasern, bevorzugt in einer Menge von 15 bis 50 Gew.-%, stärker bevorzugt 20 bis 40 Gew.-%, bezogen auf das Gesamtgewicht der Fasern; und/oder wobei die synthetischen Fasern thermoplastische Fasern sind, ausgewählt aus der Gruppe aus Polyestern, beispielsweise Polyalkylenterephthalaten wie etwa Polyethylenterephthalat (PET), Polybutylenterephthalat (PBT) und dergleichen, Polyalkylenen, beispielsweise Polyethylenen, Polypropylenen und dergleichen, Polyacrylonitrilen (PAN) und Polyamiden, beispielsweise Nylon wie etwa Nylon-6, Nylon-6,6, Nylon-6,12 und dergleichen und Kombinationen davon.
 
9. Der Ölfilter gemäß einem der vorhergehenden Ansprüche, wobei die synthetischen Fasern thermoplastische synthetische Fasern mit einem durchschnittlichen Durchmesser von 0,1 µm bis 15 µm, bevorzugt 0,1 µm bis 10 µm, und einer durchschnittlichen Länge von 1 bis 50 mm, wie etwa 1 bis 20 mm, umfassen; und/oder wobei die Glasfasern einen durchschnittlichen Faserdurchmesser von 0,4 bis 2,6 µm aufweisen.
 
10. Der Ölfilter gemäß einem der vorhergehenden Ansprüche, wobei die synthetischen Fasern bis zu 40 Gew.-%, bevorzugt bis zu 30 Gew.-%, bezogen auf das Gesamtgewicht der Fasern, eines regenerierten Cellulosematerials wie etwa Lyocell oder Viskose oder Kombinationen davon beinhalten.
 
11. Der Ölfilter gemäß einem der vorhergehenden Ansprüche, wobei das Faservlies eine durchschnittliche Dicke von 0,6 bis 1,5 mm, insbesondere 0,7 bis 1,4 mm aufweist und/oder wobei das Faservlies gewellt ist, bevorzugt mit einer Wellentiefe von etwa 0,1 bis 0,5 mm.
 
12. Der Ölfilter gemäß einem der vorhergehenden Ansprüche, wobei das Fasermedium ferner eine Nanofaser-Beschichtung umfasst, wobei die Nanofaser-Beschichtung elektrogesponnene Nanofasern wie etwa Polyethersulfon (PES) oder Polyamid (PA) Nanofasern beinhaltet und bevorzugt eine Dicke von 50 bis 1000 nm aufweist; und/oder wobei das Faservlies nassgelegt ist.
 
13. Der Ölfilter gemäß einem der vorhergehenden Ansprüche, wobei

- die Fasern des thermoplastischen Polymers 60 % bis 88 % bezogen auf das Gewicht des Faservlieses bilden;

- die Glasfasern 2 % bis 30 % bezogen auf das Gewicht des Faservlieses bilden; und

- das Faservlies ferner eine Beschichtung umfasst, hergestellt aus dem duroplastischen Bindemittel, bestehend aus einem Phenolharz, einem Acrylharz, einem Epoxidharz oder einem Melamin-Formaldehyd, wobei die Menge des Bindemittels von 15 Gew.-% bis 30 Gew.-% bezogen auf das Gewicht des Faservlieses beträgt.


 
14. Der Ölfilter gemäß einem der vorhergehenden Ansprüche, wobei das Fasermedium gewellt ist.
 
15. Verwendung des Ölfilters gemäß einem der vorhergehenden Ansprüche für die Filtration von Öl in einem Verbrennungsmotor.
 


Revendications

1. Filtre à huile autoportant plissé, comprenant un milieu fibreux plissé comprenant un voile fibreux formé à partir de :

- fibres synthétiques ;

- éventuellement au moins un additif ; et

- un liant thermodurcissable présent en une concentration d'au moins 15 % en poids du voile fibreux et/ou d'au moins une fibre de liaison ;

dans lequel les fibres synthétiques comprennent jusqu'à 30 % en poids, de préférence jusqu'à 20 % en poids de fibres de verre, sur la base du poids total des fibres ;

dans lequel les fibres synthétiques sont liées au liant thermodurcissable et/ou à la au moins une fibre de liaison pour former le voile fibreux ; et le milieu fibreux est capable de former ledit filtre à huile autoportant plissé, qui est capable de conserver des plis au contact de l'huile ayant une température dans la plage rencontrée dans un moteur à combustion interne ; et

ledit filtre comprenant le milieu fibreux sans matériau support de renfort.


 
2. Filtre à huile selon la revendication 1, dans lequel le voile fibreux comprend des fibres synthétiques choisies dans le groupe des polymères thermoplastiques, des fibres siliceuses, comme des fibres de verre, des fibres cellulosiques régénérées et des mélanges de celles-ci, au moins 30 % en poids, de préférence au moins 50 % en poids des fibres étant des polymères thermoplastiques.
 
3. Filtre à huile selon la revendication 1 ou 2, dans lequel le voile fibreux contient (i) au moins 70 % en poids de fibres de polymère(s) thermoplastique(s) et jusqu'à 40 ou jusqu'à 30 % en poids de fibres cellulosiques régénérées ; (ii) au moins 70 % en poids de fibres de polymère(s) thermoplastique(s) ; ou (iii) aucune fibre cellulosique régénérée telle que Lyocell ou la viscose ou des combinaisons de celles-ci.
 
4. Filtre à huile selon l'une quelconque des revendications précédentes, dans lequel le voile fibreux est imprégné avec le liant thermodurcissable qui est de préférence choisi parmi les résines thermodurcissables, comme les résines phénoliques, les résines époxy ou les polymères à base de mélamine, comme le mélamine- formaldéhyde, ou les résines acryliques, ou des combinaisons de celles-ci.
 
5. Filtre à huile selon l'une quelconque des revendications précédentes, dans lequel la fibre de liaison est choisie parmi une fibre de liaison bicomposante, une fibre de liaison de polyéthylène téréphtalate (PET) ou une fibre de liaison d'alcool polyvinylique (PVOH) ; et/ou dans lequel le au moins un additif est choisi parmi un agent ignifuge, un agent colorant, un agent hydrophobe, un agent hydrophile, un agent mouillant, un agent antimicrobien ou un agent antistatique.
 
6. Filtre à huile selon l'une quelconque des revendications précédentes, dans lequel le milieu fibreux comprend 15 à 30 %, en particulier 20 à 25 % du liant thermodurcissable, sa concentration étant calculée sur la base du poids total des fibres.
 
7. Filtre à huile selon l'une quelconque des revendications précédentes, dans lequel les fibres synthétiques comprennent des premières fibres, ayant un premier diamètre moyen tel que 2 µm ou plus, et des secondes fibres, ayant un second diamètre moyen inférieur à 1 µm, la première longueur moyenne étant supérieure à la seconde longueur moyenne.
 
8. Filtre à huile selon l'une quelconque des revendications précédentes, dans lequel les fibres synthétiques comprennent des fibres non étirées telles que des fibres de polyéthylène téréphtalate thermoplastiques non étirées, de préférence en une quantité de 15 à 50 % en poids, de manière mieux préférée de 20 à 40 % en poids, sur la base du poids total des fibres ; et/ou dans lequel les fibres synthétiques sont des fibres thermoplastiques choisies dans le groupe des polyesters, par exemple des polyalkylène téréphtalates, comme le polyéthylène téréphtalate (PET), le polybutylène téréphtalate (PBT), et similaires, des polyalkylènes, par exemple des polyéthylènes, polypropylènes et similaires, des polyacrylonitriles (PAN), et des polyamides, par exemple des nylons, tels que le nylon-6, le nylon-6,6, le nylon-6,12 et similaires, et des combinaisons de ceux-ci.
 
9. Filtre à huile selon l'une quelconque des revendications précédentes, dans lequel les fibres synthétiques comprennent des fibres synthétiques thermoplastiques ayant un diamètre moyen de 0,1 µm à 15 µm, de préférence 0,1 µm à 10 µm, et une longueur moyenne de 1 à 50 mm telle que 1 à 20 mm ; et/ou dans lequel les fibres de verre ont un diamètre moyen de fibres de 0,4 à 2,6 µm.
 
10. Filtre à huile selon l'une quelconque des revendications précédentes, dans lequel les fibres synthétiques comprennent jusqu'à 40 % en poids, de préférence jusqu'à 30 % en poids, sur la base du poids total des fibres, d'une matière cellulosique régénérée, telle que Lyocell ou la viscose ou des combinaisons de celles-ci.
 
11. Filtre à huile selon l'une quelconque des revendications précédentes, dans lequel le voile fibreux a une épaisseur moyenne de 0,6 à 1,5 mm, en particulier 0,7 à 1,4 mm et/ou dans lequel le voile fibreux est ondulé, de préférence par une profondeur d'ondulation d'environ 0,1 à 0,5 mm.
 
12. Filtre à huile selon l'une quelconque des revendications précédentes, dans lequel le milieu fibreux comprend en outre un revêtement de nanofibres, dans lequel le revêtement de nanofibres comprend des nanofibres électrofilées, telles que des nanofibres de polyéthersulfone (PES) ou de polyamide (PA), et a de préférence une épaisseur de 50 à 1000 nm ; et/ou dans lequel le voile fibreux est déposé par voie humide.
 
13. Filtre à huile selon l'une quelconque des revendications précédentes, dans lequel

- les fibres du polymère thermoplastique forment 60 à 88 % du voile fibreux en poids ;

- les fibres de verre forment 2 % à 30 % du voile fibreux en poids ; et

- le voile fibreux comprend en outre un revêtement fait du liant thermodurcissable constitué d'une résine phénolique, d'une résine acrylique, d'une résine époxy, ou d'un mélamine-formaldéhyde, la quantité de liant allant de 15 % à 30 % en poids sur le poids du voile fibreux.


 
14. Filtre à huile selon l'une quelconque des revendications précédentes, dans lequel le milieu fibreux est ondulé.
 
15. Utilisation du filtre à huile selon l'une quelconque des revendications précédentes pour la filtration de l'huile dans un moteur à combustion interne.
 




Drawing














Cited references

REFERENCES CITED IN THE DESCRIPTION



This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

Patent documents cited in the description