(19)
(11)EP 3 346 020 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
29.07.2020 Bulletin 2020/31

(21)Application number: 16842041.2

(22)Date of filing:  05.09.2016
(51)International Patent Classification (IPC): 
C22C 38/60(2006.01)
C21D 9/52(2006.01)
C22C 38/02(2006.01)
C22C 38/06(2006.01)
C22C 38/20(2006.01)
C22C 38/24(2006.01)
C22C 38/28(2006.01)
C22C 38/34(2006.01)
C21D 1/25(2006.01)
C22C 38/00(2006.01)
F16F 1/02(2006.01)
C21D 9/02(2006.01)
C22C 38/04(2006.01)
C22C 38/18(2006.01)
C22C 38/22(2006.01)
C22C 38/26(2006.01)
C22C 38/32(2006.01)
C21D 1/48(2006.01)
C21D 8/06(2006.01)
C21D 6/00(2006.01)
(86)International application number:
PCT/JP2016/075961
(87)International publication number:
WO 2017/039012 (09.03.2017 Gazette  2017/10)

(54)

SPRING STEEL WIRE AND SPRING

STAHLDRAHT FÜR FEDERN UND FEDER

FIL EN ACIER À RESSORT ET RESSORT


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 04.09.2015 JP 2015174730

(43)Date of publication of application:
11.07.2018 Bulletin 2018/28

(73)Proprietor: Nippon Steel Corporation
Tokyo (JP)

(72)Inventors:
  • TERAMOTO Shinya
    Tokyo 100-8071 (JP)
  • YARITA Hiroshi
    Tokyo 100-0005 (JP)
  • SUZUKI Shouichi
    Tokyo 100-0005 (JP)

(74)Representative: Vossius & Partner Patentanwälte Rechtsanwälte mbB 
Siebertstrasse 3
81675 München
81675 München (DE)


(56)References cited: : 
EP-A1- 2 058 411
WO-A2-2008/156295
JP-A- 2005 220 392
WO-A1-2011/004913
JP-A- 2004 143 482
JP-A- 2011 214 118
  
      
    Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


    Description

    [Technical Field of the Invention]



    [0001] The present invention relates to a spring steel wire used for high strength springs such as valve springs, clutch damper springs, and suspension springs which are mainly used for automobiles, and particularly relates to a high strength spring steel wire having excellent settling resistance after coiliing, and a spring including the steel wire.

    [0002] Priority is claimed on Japanese Patent Application No. 2015-174730, filed on September 4, 2015.

    [Related Art]



    [0003] As automobiles progress in weight reduction and high performance, increase of design stress for springs used for various purposes as described above are also aimed at. In this case, since spring load stress increases, springs having excellent fatigue strength and settling resistance is required. Settling denotes plastic deformation under a stress load. Therefore, in a case where the settling resistance is low, there is a problem that the settling amount of a spring increases under a high-stress load and restoring force of the spring is degraded.

    [0004] As the springs used for various purposes as described above, cold formed springs are mainly employed. The cold formed springs are manufactured by carrying out cold coiliing with high strength steel wires in which steel has been subjected to quenching and tempering in advance. Generally, as a technique of improving fatigue strength and settling resistance of such springs, the measure, in which tensile strength after quenching and tempering is enhanced, is well known.

    [0005] In addition, as disclosed in Patent Documents 1 and 2, technologies of improving fatigue strength and settling resistance have been proposed. In the technologies, tensile strength of a steel wire is enhanced by containing a large amount of an alloying element as a chemical composition such as Si. However, when tensile strength of a steel wire is enhanced using such a technique, there is concern that ductility and toughness are remarkably degraded such that coiliing cannot be carried out, or an obtained spring cannot bear use as a spring.

    [0006] In addition to that described above, in the related art, various techniques of improving settling resistance have been proposed. For example, Patent Document 3 proposes a technology of improving settling resistance of a spring by causing fine cementite of 100 nm or smaller to be dispersed in steel. However, in Patent Document 3, in order to restrain this fine cementite from decomposing and dissipating during heat treatment, there is a need to cause Cr and V to be concentrated in the cementite such that the concentration of Cr and the concentration of V reach a predetermined concentration or higher. The fine cementite in which alloying elements such as Cr and V are concentrated has remarkably low ductility and toughness. Therefore, in the technology of Patent Document 3, there is concern that coiliing for obtaining a spring from a steel wire cannot be carried out, or an obtained spring cannot bear use as a spring.

    [0007] In addition, Patent Document 4 has proposed a technology of improving settling resistance of a suspension spring. In the technology, steel mainly including a structure of martensite and bainite is subjected to cold working. Thereafter, quenching and tempering are performed. Then, prior austenite grains are refined, and undissolved carbide is reduced as much as possible. However, in the technology of Patent Document 4, there is a need to carry out cold working for spring steel mainly including the structure of martensite and bainite. The structure of martensite and bainite in high carbon steel such as spring steel is brittle so that it is difficult to carry out cold working.

    [0008] Furthermore, Patent Documents 5 to 8 have also proposed technologies of improving fatigue properties or settling resistance by reducing the amount of undissolved carbide (cementite). However, in such technologies, the effect of improving fatigue properties or settling resistance is small.

    [0009] Patent Document 9 discloses a high strength heat treated steel wire for a spring characterized by comprising, by mass%, C: 0.5 to 0.9%, Si: 1.0 to 3.0%, Mn: 0.1 to 1.5%, Cr: 1.0 to 2.5%, V: over 0.15 to 1.0%, and Al: 0.005% or less, controlling N to 0.007% or less, further containing one or two of Nb: 0.001 to less than 0.01% and Ti: 0.001 to less 0.005%, and having a tensile strength of 2000 MPa or more, having cementite-based spheroidal carbides and alloy-based spheroidal carbides in a microscopic visual field satisfying an area percentage of carbides with a circle equivalent diameter of 0.2 µm or more of 7% or less and a density of carbides with a circle equivalent diameter of 1 grain/µm2 or less, having a prior austenite grain size number of # 10 or more, and having retained austenite of 15 mass% or less.

    [0010] Patent Document 10 discloses a steel wire rod having excellent cold workability and producing a spring with excellent fatigue life, the steel wire comprising (wt.%) carbon (0.5-0.7), silicon(1.5-3.0), manganese(0.3-1.0),chromium (0.01-1.5), molybdenum (0.01-1.0), nickel (0.01-1.0), boron (0.005-0.015), oxygen (<= 0.0015), aluminum (<= 0.01), phosphorus (<= 0.02), sulfur (<= 0.02), and nitrogen (<= 0.02).

    [0011] As described above, the technologies of improving settling resistance which have been proposed in the related art are still insufficient and high strength spring steel wires which can cope with recent demands for high strengthening of springs and can improve settling resistance of springs have not been realized at present.

    [Prior Art Document]


    [Patent Document]



    [0012] 

    [Patent Document 1] Japanese Patent No. 2613601

    [Patent Document 2] Japanese Unexamined Patent Application, First Publication No. H2-57637

    [Patent Document 3] Japanese Patent No. 4868935

    [Patent Document 4] Japanese Patent No. 3764715

    [Patent Document 5] Japanese Patent No. 3233188

    [Patent Document 6] Japanese Unexamined Patent Application, First Publication No. H11-246943

    [Patent Document 7] Japanese Patent No. 3971571

    [Patent Document 8] Japanese Patent No. 3851095

    [Patent Document 9] European Patent EP 2058411 A1

    [Patent Document 10] International Application WO2008/156295 A2.


    [Disclosure of the Invention]


    [Problems to be Solved by the Invention]



    [0013] The present invention has been made based on the foregoing circumstances. An object of the present invention is to provide a high strength spring steel wire which has favorable workability, in which the amount of plastic deformation is small even when being used under a high-stress load after coiliing, and which has excellent settling resistance to the extent of being able to sufficiently cope with recent demands for high strengthening, and a spring including the spring steel wire.

    [Means for Solving the Problem]



    [0014] In order to achieve the object, the inventors have intensively examined measures for realizing a high strength spring steel wire having excellent settling resistance after coiliing. The following (a) to (e) are results of the acquired knowledge.
    1. (a) In order to improve settling resistance, it is effective to cause the structure of a spring steel wire (metallographic structure) to be a structure having tempered martensite as a main constituent (specifically, a structure, by area ratio, having tempered martensite of 90% or more), and at the same time to refine the structure, particularly to refine prior austenite grains. Generally, in a process of manufacturing a spring steel wire, pearlitic transformation treatment such as lead patenting is performed with respect to steel having a structure including austenite after hot rolling. Thereafter, cold wire-drawing is performed, and then quenching and tempering are performed. If the structure after quenching and tempering is a structure having tempered martensite as a main constituent, particularly, a structure, by area ratio, having tempered martensite of 90% or more, excellent settling resistance can be ensured.
    2. (b) In order to improve settling resistance, it is effective to refine the structure, particularly to refine prior austenite grains. If austenite grains before transformation are refined, the size of martensite blocks in a structure having tempered martensite as a main constituent is refined. In addition, due to the refined martensite block size, yield strength is improved and settling resistance is improved. These effects are particularly maximized when the size of prior austenite grains matches that of No. 12.5 or higher in the grain size numbers regulated by JIS G 0551.
    3. (c) In order to achieve refinement of prior austenite grains, it is effective to cause a large amount of iron-based carbide represented by cementite (Fe3C), particularly comparatively large iron-based carbide (iron-based carbide having undissolved iron-based carbide as a main constituent, as described below) having a grain size of a certain degree or larger to be dispersed. In the related art, it has been considered that it is favorable to have no coarse carbide. However, when a large amount of comparatively large iron-based carbide is dispersed, austenite grains before transformation can be refined due to the pinning effect of the iron-based carbide. When the austenite grains before transformation are refined, martensite, which has been formed by transformation in a cooling process thereafter, is refined, so that yield strength is improved without having workability degraded. Therefore, settling resistance is improved.
    4. (d) In the iron-based carbide described above, its grain size is important. It is difficult to sufficiently exhibit the effects described above in fine iron-based carbide having an equivalent circle diameter less than 0.15 µm and coarse iron-based carbide having an equivalent circle diameter exceeding 0.50 µm. Therefore, in order to achieve the effect, there is a need to cause a predetermined amount or more of iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm to be present. In the process of manufacturing a spring steel wire, there are cases where a part of carbide such as cementite generated through pearlitic transformation treatment such as lead patenting after hot rolling remains undissolved without being completely dissolved even after quenching and tempering thereafter. Such undissolved iron-based carbide is often present as carbide having an equivalent circle diameter of approximately 0.15 µm or larger. Meanwhile, iron-based carbide is precipitated even during tempering after quenching. However, carbide which is precipitated during tempering is fine, and the equivalent circle diameter is less than 0.15 µm, particularly, the equivalent circle diameter is mostly less than 0.10 µm. Therefore, in order to refine austenite grains before transformation and to improve settling resistance, it is effective to utilize iron-based carbide which remains undissolved even after quenching and tempering.
    5. (e) In order to improve settling resistance, controlling the presence density of iron-based carbide is also important. That is, if an amount of iron-based undissolved carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm is small, since the effect of refining grains is not sufficient, settling resistance is not improved. Particularly, when its presence density is less than 0.40 pieces/µm2, the effect of improving settling resistance is scarcely recognized. Meanwhile, in a case where iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm is excessively present, since strength after quenching and tempering is degraded, settling resistance is degraded, on the contrary. In addition, in this case, since ductility is also degraded, workability is remarkably degraded. Particularly, when its presence density exceeds 2.00 pieces/µm2, these problems are likely to occur. Therefore, in order to reliably improve settling resistance without impairing workability, the presence density of iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm needs to be within a range of 0.40 pieces/µm2 to 2.00 pieces/µm2.


    [0015] Based on the knowledge described above as in (a) to (e), the inventors have found that settling resistance after coiliing can be reliably and sufficiently improved without impairing workability, when a structure of a steel wire includes, by area ratio, tempered martensite of 90% or more, when at the same time, the prior austenite grain size number is No. 12.5 or higher, and when furthermore, the presence density of iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm ranges from 0.40 pieces/µm2 to 2.00 pieces/µm2, and have attained the present invention.

    [0016]  The present invention is as stated in the appended claims.
    1. (1) According to an aspect of the present invention, there is provided a spring steel wire including, by mass%, C: 0.40% to 0.75%, Si: 1.00% to 5.00%, Mn: 0.20% to 2.00%, P: 0.0001% to 0.0500%, S: 0.0001% to 0.0500%, Cr: 0.50% to 3.50%, Al: 0.0005% to 0.0500%, N: 0.0020% to 0.0100%, Mo: 0% to 2.00%, V: 0% to 0.50%, W: 0% to 0.50%, Nb: 0% to 0.100%, Ti: 0% to 0.100%, Ca: 0% to 0.0100%, Mg: 0% to 0.0100%, Zr: 0% to 0.1000%, B: 0% to 0.0100%, Cu: 0% to 1.00%, Ni: 0% to 3.00%, and a remainder of Fe and impurities. A structure includes, by area ratio, a tempered martensite of 90% or more. The prior austenite grain size number is No. 12.5 or higher. The presence density of iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm is 0.40 pieces/µm2 to 2.00 pieces/µm2.
    2. (2) In the spring steel wire according to (1), the spring steel wire may include, by mass%, at least one of Mo: 0.01% to 2.00%, V: 0.01% to 0.50%, W: 0.01% to 0.50%, Nb: 0.005% to 0.100%, and Ti: 0.001% to 0.100%.
    3. (3) In the spring steel wire according to (1) or (2), the spring steel wire may include, by mass%, at least one of Ca: 0.0002% to 0.0100%, Mg: 0.0002% to 0.0100%, Zr: 0.0005% to 0.1000%, B: 0.0005% to 0.0100%, Cu: 0.05% to 1.00%, and Ni: 0.05% to 3.00%.
    4. (4) According to another aspect of the present invention, there is provided a spring including the spring steel wire according to any one of (1) to (3).

    [Effects of the Invention]



    [0017]  According to the present invention, it is possible to provide a high strength spring steel wire having excellent settling resistance after coiliing while favorable workability is ensured, and a spring including the spring steel wire.

    [Brief Description of the Drawings]



    [0018] 

    FIG. 1 is a graph showing a relationship between presence density of iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm, and a residual shear strain amount which is an index for settling resistance.

    FIG. 2 is a graph showing a relationship between presence density of iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm, and reduction in area which is an index for workability.


    [Embodiment of the Invention]



    [0019] Hereinafter, a spring steel wire according to an embodiment of the present invention (hereinafter, a spring steel wire according to the present embodiment) and a spring according to an embodiment of the present invention (hereinafter, according to a spring of the present embodiment) will be described.

    <Chemical Composition>



    [0020] First, the reasons for limiting the chemical composition of the spring steel wire in the present invention will be described. Hereinafter, the percentage sign "%" of the amount of each component indicates "mass%".

    C: 0.40% to 0.75%



    [0021] C is an important element determining strength of steel. In order to obtain sufficient strength, the lower limit is set to 0.40%, is preferably set to 0.45% or more, and is more preferably set to 0.50% or more. Since the alloying cost of C is low compared to other strengthening elements, if a large amount of C can be contained, high strength can be obtained at a low alloying cost. However, when C is excessively contained, the ductility and toughness are degraded so that the workability is remarkably degraded. Therefore, the upper limit for the C content is set to 0.75%. The C content is preferably set to 0.67% or less and is more preferably set to 0.65% or less.

    Si: 1.00% to 5.00%



    [0022] Si is an element having deoxidizing action. In addition, since Si is element which significantly suppresses softening of steel after heat treatment, Si is an element effective in improving settling resistance. In order to sufficiently obtain such an effect, the lower limit is set to 1.00%. The Si content is preferably set to 1.20% or more. Meanwhile, when Si is excessively contained, ductility and toughness of steel are degraded so that workability is remarkably degraded. Therefore, the upper limit for the Si content is set to 5.00%. The Si content is preferably set to 3.50% or less.

    Mn: 0.20% to 2.00%



    [0023] Mn is an element which fixes S in steel as MnS and is effective in enhancing hardenability such that hardness after heat treatment is sufficiently improved. In order to achieve these effects, the Mn content is set to 0.20% or more, is preferably set to 0.25% or more, and is more preferably set to 0.30% or more. Meanwhile, when Mn content exceeds 2.00%, hardness of the base (matrix) increases and steel becomes brittle, so that workability is remarkably degraded. Therefore, the Mn content is set to 2.00% or less. The Mn content is preferably set to 1.50% or less and is more preferably set to 1.20% or less.

    P: 0.0001% to 0.0500%



    [0024] Generally, P is included in steel by 0.0001% or more as impurities. Therefore, the lower limit is set to 0.0001%. P is an element being segregated in prior austenite grain boundaries and the like, so that steel becomes prominently brittle and workability is remarkably degraded. When the P content exceeds 0.0500%, the adverse influence becomes prominent. Therefore, the upper limit for the P content is set to 0.0500%. The P content is preferably 0.0300% or less, is more preferably set to 0.0200% or less, and is still more preferably set to 0.0150% or less.

    S: 0.0001% to 0.0500%



    [0025] Generally, similar to P, S is also included in steel by 0.0001% or more as impurities. Therefore, the lower limit for the S content is set to 0.0001%. S is an element causing steel to be brittle. Accordingly, it is desirable that the S content is reduced as much as possible. Particularly, when the S content exceeds 0.0500%, the adverse influence becomes prominent. Therefore, the upper limit for the S content is set to 0.0500%. The amount of S is preferably set to 0.0300% or less, is more preferably set to 0.0200% or less, and is still more preferably set to 0.0150% or less.

    Cr: 0.50% to 3.50%



    [0026] Cr is an element effective in improving settling resistance due to its effect of suppressing softening after heat treatment. In order to reliably obtain this effect, the Cr content is set to 0.50% or more, is preferably set to 0.60% or more, and is more preferably set to 0.70% or more. However, Cr is solid-solubilized in iron-based carbide and stabilizes the carbide. Therefore, when there is an excessive amount of Cr, iron-based undissolved carbide increases more than necessary, so that strength after heat treatment is degraded. In this case, settling resistance is degraded, on the contrary. When there is an excessive amount of Cr, ductility is degraded, and the workability is remarkably degraded. From these viewpoint, the Cr content is set to 3.50% or less, is preferably set to 3.00% or less, and is more preferably set to 2.75% or less.

    Al: 0.0005% to 0.0500%



    [0027] Generally, A1 is included in steel by 0.0005% or more as impurities. Therefore, the lower limit for the A1 content is set to 0.0005%. A1 is an element forming oxide such as Al2O3, such that ductility and toughness of steel are degraded and workability is remarkably degraded. Therefore, the Al content is set to 0.0500% or less. It is desirable that the Al content is reduced as much as possible. The Al content is preferably set to 0.0100% or less.

    N: 0.0020% to 0.0100%



    [0028] N is an element which combines with Al, V, Ti, and/or Nb in steel and forms nitride. This nitride has an effect of refining prior austenite grains. In order to achieve this effect, the N content is set to 0.0020% or more and is preferably set to 0.0030% or more. Meanwhile, when there is an excessive amount of N, the nitride is coarsened. As a result, ductility of steel is degraded and workability is remarkably degraded. Therefore, the N content is set to 0.0100% or less and is preferably set to 0.0070% or less.

    [0029] Basically, the spring steel wire according to the present embodiment includes the elements described above, and the remainder includes Fe and impurities. However, in order to further improve the characteristics, in place of a part of Fe, at least one of Mo: 0.01% to 2.00%, V: 0.01% to 0.50%, W: 0.01% to 0.50%, Nb: 0.005% to 0.100%, and Ti: 0.001% to 0.100%; and/or at least one of Ca: 0.0002% to 0.0100%, Mg: 0.0002% to 0.0100%, Zr: 0.0005% to 0.1000%, B: 0.0005% to 0.0100%, Cu: 0.05% to 1.00%, and Ni: 0.05% to 3.00% may be contained. However, all of Mo, V, W, Nb, Ti, Ca, Mg, Zr, B, Cu, and Ni are not necessarily contained, and their lower limits are 0%.

    <At Least One of Mo: 0.01% to 2.00%, V: 0.01% to 0.50%, W: 0.01% to 0.50%, Nb: 0.005% to 0.100%, and Ti: 0.001% to 0.100%>



    [0030] Mo, V, W, Nb, and Ti are elements contributing to improvement of settling resistance by suppressing softening after heat treatment. In order to achieve this effect, the amounts of Mo, V, and Ware preferably set to 0.01% or more. The amount of Nb is preferably set to 0.005% or more. In addition, the amount of Ti is preferably set to 0.001% or more. Meanwhile, when there are excessive amounts of these elements, metal carbonitride increases and strength after heat treatment is degraded. Accordingly, settling resistance is degraded, on the contrary. In addition, since ductility is degraded, workability is remarkably degraded. Therefore, even in a case where these elements are contained, it is preferable that the upper limit for the Mo content is set to 2.00%, the upper limit for the V content is set to 0.50%, the upper limit for the W content is set to 0.50%, the upper limit for the Nb content is set to 0.100%, and the upper limit for the Ti content is set to 0.100%. It is more preferable that the Mo content ranges from 0.05% to 0.60%, the V content ranges from 0.05% to 0.35%, the W content ranges from 0.05% to 0.35%, the Nb content ranges from 0.005% to 0.050%, and the Ti content ranges from 0.010% to 0.080%.

    <At Least One of Ca: 0.0002% to 0.0100%, Mg: 0.0002% to 0.0100%, Zr: 0.0005% to 0.1000%, B: 0.0005% to 0.0100%, Cu: 0.05% to 1.00%, and Ni: 0.05%. to 3.00%>



    [0031] All of Ca, Mg, and Zr are elements having an effect of improving hardness of steel after heat treatment by forming oxide, becoming crystallized nuclei of MnS, causing the MnS to be finely dispersed in a uniform manner, and enhancing hardenability by means of the MnS. In addition, all of B, Cu, and Ni are elements having an effect of improving hardness after heat treatment by being solid-solubilized in steel and enhancing hardenability. In order to exhibit these effects, it is preferable that the lower limits for the amounts of Ca and Mg are set to 0.0002%, the lower limit for the amount of Zr is set to 0.0005%, the lower limit for the amount of B is set to 0.0005%, the lower limit for the amount of Cu is set to 0.05%, and the lower limit for the amount of Ni is set to 0.05%. Meanwhile, if the Ca content and the Mg content exceed 0.0100% and if the Zr content exceeds 0.1000%, hard inclusions such as oxide, sulfide, and the like are excessively formed, so that ductility of steel is degraded and workability is remarkably degraded. In addition, when the B content exceeds 0.0100%, when the Cu content exceeds 1.00%, and the Ni content exceeds 3.00%, ductility of steel is degraded and workability is remarkably degraded. Therefore, even in a case where these elements are contained, it is preferable that the upper limits for the Ca content and the Mg content are set to 0.0100%, the upper limit for the Zr content is set to 0.1000%, the upper limit for the B content is set to 0.0100%, the upper limit for the Cu content is set to 1.00%, and the upper limit for the Ni content is set to 3.00%.

    [0032] The spring steel wire according to the present embodiment includes a chemical composition containing the essential elements and a remainder including Fe and impurities, or a chemical composition containing the optional elements described above in addition to the essential elements, and a remainder of Fe and impurities. As impurities other than those described above, O and the like are considered, and their amounts are preferably set to 0.05% or less in total.

    [0033] Next, the reasons for limiting the structure of the spring steel wire according to the present embodiment will be described.

    <Tempered Martensite of 90% or More by Area Ratio>



    [0034] When the structure of the spring steel wire is a structure having tempered martensite as a main constituent, excellent settling resistance can be obtained. As phases other than the tempered martensite (remainder structures), there are ferrite, pearlite, bainite, residual austenite, and the like. When the total area ratio of these structures (remainder structures) increases, settling resistance is degraded. On the contrary, when the remainder structures are further reduced, settling resistance is further improved.

    [0035] Particularly, when the total area ratio of the remainder structures exceeds 10%, settling resistance is remarkably degraded. Therefore, the remainder structures are set to less than 10% by total area ratio. That is, the area ratio of the tempered martensite is regulated to 90% or higher. The residual shear strain amount that is an index value for settling resistance can be set to 0.029% or less by setting the area ratio of the tempered martensite to 90% or more and controlling the prior austenite grain size, the iron-based carbide size, and the distribution state, which will be described below. The area ratio of the tempered martensite may be 100%.

    [0036] The area ratio of the tempered martensite needs only to be 90% or more by average area ratio when a cross section (C-cross section) of a spring steel wire orthogonal to the length direction after quenching and tempering is observed and image analysis is performed. Actually, for example, as seen in Examples described below, the area ratio of the tempered martensite may be represented by a value measured at a 1/4 position of a diameter D from a location on the outer circumferential surface of a steel wire in the C-cross section of the steel wire. For example, the area ratio of martensite may be obtained by collecting a sample from a 1/4 portion of the diameter D from the outer circumferential surface in the C-cross section of the steel wire, performing etching using a nital etching solution, capturing five photographs of the structure of 1,000-fold using an optical microscope, and performing image analysis.

    <No. 12.5 or Higher as Prior Austenite Grain Size Number>



    [0037] When prior austenite grains are refined, the size of martensite blocks is refined. Accordingly, yield strength is improved. As a result, settling resistance is improved. These effects get larger particularly through refinement in which the prior austenite grain size number is No. 12.5 or higher. Therefore, the prior austenite grain size number is set to No. 12.5 or higher. The prior austenite grain size number is preferably set to No. 13.5 or higher, is more preferably set to No. 14.0 or higher, and is still more preferably set to No. 14.5 or higher. Since it is preferable for the prior austenite grain size to be small, there is no need to provide an upper limit for the grain size number.

    [0038] The prior austenite grain size number needs only to be measured by observing prior austenite grain boundaries which are revealed through etching using an appropriate etching solution such as a picric acid saturated aqueous solution using an optical microscope or the like. Representatively, the measurement may be performed in accordance with JIS G 0551. In addition, the prior austenite grain size needs only to be measured in a cross section (C-cross section) of a spring steel wire orthogonal to the length direction after quenching and tempering. Actually, for example, as seen in Examples described below, the prior austenite grain size number may be represented by a value measured at a 1/4 position of the diameter D from a location on the outer circumferential surface of a steel wire in the C-cross section of the steel wire after quenching and tempering.

    < Presence Density of Iron-based Carbide Having Equivalent Circle Diameter Ranging from 0.15 µm to 0.50 µm is 0.40 Pieces/µm2 to 2.00 Pieces/µm2>



    [0039] In order to refine the prior austenite grains, it is effective to suppress grain growth of austenite before martensite transformation by means of an pinning effect of precipitates. In order to refine austenite before transformation such that the prior austenite grain size number becomes No. 12.5 or higher, without impairing workability, it is effective when precipitates having an equivalent circle diameter ranging from 0.10 µm to 0.50 µm, particularly among thereof, precipitates having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm are present in a dispersed manner at a density ranging from 0.40 pieces/µm2 to 2.00 pieces/µm2.

    [0040] Here, when the equivalent circle diameter is less than 0.15 µm or exceeds 0.50 µm, or when the presence density of precipitates is less than 0.40 pieces/µm2, the pinning effect of grain growth of austenite is small and sufficient refinement of austenite grains cannot be obtained. Therefore, the effect of improving settling resistance cannot be sufficiently obtained. In accordance with an increase of the presence density of precipitates, the prior austenite grain size number increases and settling resistance are improved. However, when the presence density of precipitates exceeds 2.00 pieces/µm2, strength after quenching and tempering is degraded, so that settling resistance is degraded, on the contrary. In addition, since ductility is also degraded, workability is remarkably degraded. Therefore, there is a need for precipitates having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm to be dispersed at a density ranging from 0.40 pieces/µm2 to 2.00 pieces/µm2.

    [0041] Furthermore, when there are 0.50 pieces/µm2 or more of precipitates having equivalent circle diameters ranging from 0.15 µm to 0.50 µm, the prior austenite grain size number becomes No. 13.5 or higher, which is more preferable.

    [0042] In order to obtain precipitates having the size and the amount as described above, it is necessary that precipitates is iron-based carbide such as cementite (Fe3C). However, even though precipitates are iron-based carbide, iron-based carbide precipitated during tempering is fine, and the foregoing conditions are not often satisfied. Therefore, it is preferable that iron-based carbide satisfying the foregoing conditions has comparatively large iron-based undissolved carbide as a main constituent which has remained undissolved during heating before quenching. In addition, for example, since nitride and the like are drastically smaller than the size described above, a sufficient pinning effect cannot be obtained compared to iron-based carbide.

    [0043] As described above, when the spring steel wire according to the present embodiment simultaneously satisfies three conditions, such as the spring steel wire includes, as a structure, by area ratio, a structure of tempered martensite of 90% or more, the prior austenite grain size number is No. 12.5 or higher, and the presence density of iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm is 0.40 pieces/µm2 to 2.00 pieces/µm2, excellent settling resistance can be obtained without impairing workability.

    [0044] The spring according to the present embodiment includes the spring steel wire according to the present embodiment. Specifically, the spring according to the present embodiment is obtained by carrying out cold coiliing with the spring steel wire according to the present embodiment. Even though coiliing is carried out, there is no change in the chemical composition and the presence state of carbide. Therefore, the chemical composition and the presence state of carbide in the spring according to the present embodiment including the spring steel wire according to the present embodiment are the same as those in the spring steel wire according to the present embodiment.

    [0045] Next, preferable methods of manufacturing the spring steel wire according to the present embodiment and the spring according to the present embodiment will be described.

    [0046] The spring steel wire according to the present embodiment can achieve the foregoing effects as long as the spring steel wire has the features described above. Therefore, the manufacturing method is not particularly limited. However, for example, when pearlitic transformation treatment such as lead patenting is performed with respect to a steel wire rod obtained through casting and hot rolling in accordance with the routine procedure, at a temperature higher than a general temperature range (patenting process), then, cold drawing is performed to a predetermined diameter, and thereafter, the heating temperature before quenching is controlled and quenching and tempering are performed (quenching and tempering process), the spring steel wire can be stably obtained, which is preferable.

    [0047] Hereinafter, preferable conditions for the patenting process and the quenching and tempering process will be described.

    <Patenting Process>



    [0048] Pearlitic transformation treatment such as lead patenting is performed with respect to a steel wire rod obtained through casting and hot rolling. Generally, in consideration of productivity and the like, pearlitic transformation treatment is performed at a temperature (approximately from 550°C to 600°C) in the vicinity of a pearlite nose in an isothermal transformation diagram (TTT curve). However, in a case where the spring steel wire according to the present embodiment is manufactured, it is preferable that patenting is performed within a range from 650°C to 750°C. When the patenting temperature is set to 650°C or higher, Cr and Mn are concentrated in cementite, so that iron-based carbide is unlikely to be dissolved during quenching and tempering. As a result, the main constituent of iron-based carbide becomes undissolved carbide, so that iron-based carbide having desired size and presence density can be obtained.

    <Quenching and Tempering Process>



    [0049] Quenching and tempering are performed with respect to a steel wire rod which has been subjected to cold drawing to a predetermined diameter after pearlitic transformation treatment such as patenting is performed. In order to realize the structure as described above, it is preferable to appropriately control the heating temperature before quenching. In order to have tempered martensite of 90% or more after quenching and tempering, it is preferable that the heating temperature before quenching is 870°C or higher.

    [0050] In addition, in the related art, since undissolved carbide has been considered to cause deterioration of characteristics, the heating temperature before quenching has been set near the temperature at which cementite (iron-based carbide) formed through pearlitic transformation treatment is solid-solubilized completely. However, in the spring steel according to the present embodiment, it is preferable that undissolved carbide remains. In order to satisfy the structure conditions as described above, it is preferable that the heating temperature before quenching is set lower than that in the related art, specifically lower than a temperature at which iron-based carbide is solid-solubilized completely, by a range approximately from 10°C to 40°C.

    [0051] The temperature at which iron-based carbide is solid-solubilized completely varies depending on the chemical composition of steel. Therefore, the temperature at which iron-based carbide is solid-solubilized completely can be obtained in advance using a sample having a similar chemical composition, and a temperature lower than the obtained temperature by a range from 10°C to 40°C may be set as the heating temperature before quenching.

    [0052] In addition, tempering may be performed under known conditions.

    [0053] Next, the method of manufacturing the spring according to the present embodiment will be described.

    [0054] As long as the spring according to the present embodiment is manufactured using the spring steel wire according to the present embodiment obtained as described above, its manufacturing conditions and the like are not particularly limited and need only to follow the routine procedure. For example, after cold spring forming is performed with a spring steel wire which is obtained through quenching and tempering as described above, annealing or nitriding may be performed as necessary.

    [0055] The present invention will be described below in detail with reference to Examples. These Examples are for describing the technical significance and the effects of the present invention and do not limit the scope of the present invention as set forth in the appended claims.

    [Examples]



    [0056] Pieces of ingot steel melted in converter having compositions indicated as kinds of steel A to Z in Table 1 and kinds of steel AA to AV in Table 2 were continuously cast and were made into 162 mm-square rolling materials via a soaking process and a blooming process as necessary. Thereafter, the rolling materials were heated to 1,150°C and were made into steel wire rods of φ8.0 mm through hot rolling. The steel wire rods were subjected to surface scalping to φ7.4 mm and were heated to 950°C. Thereafter, lead patenting treatment was performed at temperatures indicated in Tables 3 and 4. After cold wire-drawing was performed to φ4.0 mm, quenching and tempering were performed. The iron-based carbide size and the presence density in each steel wire were changed by varying the heating temperature before quenching within the ranges indicated in Tables 3 to 4. In addition, the structures were changed by adjusting the degree of agitation (0 cm/sec to 50 cm/sec) using a water soluble quenching solution (solution temperature of 40°C) and varying the cooling rate. Thereafter, tempering was performed for 90 seconds within a temperature range from 430°C to 500°C. Table 3 and Table 4 shows the conditions for quenching and tempering which are performed with respect to each kind of steel.
    [Table 1]
    Kind of steelChemical composition (mass%) *Remainder of Fe and impurities
    CSiMnPSCrAlMoVWNbTiCaMgZrBCuNiN
    A 0.61 2.75 0.89 0.003 0.004 1.32 0.0029 - - - - - - - - - - - 0.0045
    B 0.64 2.10 0.67 0.004 0.003 2.73 0.0023 - - - - - - - - - - - 0.0052
    C 0.43 1.24 0.77 0.003 0.004 2.11 0.0041 0.57 - - - - - - - - - - 0.0040
    D 0.58 2.23 0.85 0.005 0.004 1.02 0.0023 - 0.28 - - - - - - - - - 0.0069
    E 0.61 2.08 0.92 0.003 0.005 1.23 0.0028 - - 0.45 - - - - - - - - 0.0032
    F 0.61 1.98 0.87 0.004 0.006 1.19 0.0019 - - - 0.042 - - - - - - - 0.0057
    G 0.63 2.24 0.75 0.005 0.005 1.16 0.0032 - - - - 0.04 - - - - - - 0.0056
    H 0.58 3.42 0.65 0.005 0.003 1.25 0.0031 0.15 0.12 - - - - - - - - - 0.0064
    I 0.55 2.14 1.02 0.003 0.005 0.98 0.0024 0.17 - 0.14 - - - - - - - - 0.0041
    J 0.62 2.08 0.84 0.007 0.007 1.37 0.0010 0.18 - - 0.011 - - - - - - - 0.0048
    K 0.61 2.12 1.12 0.006 0.004 1.10 0.0021 0.21 - - - 0.05 - - - - - - 0.0058
    L 0.58 2.54 1.17 0.006 0.006 1.14 0.0026 - 0.19 0.17 - - - - - - - - 0.0046
    M 0.60 2.18 0.53 0.003 0.004 1.27 0.0019 - 0.23 - 0.023 - - - - - - - 0.0046
    N 0.60 1.98 0.87 0.005 0.005 1.28 0.0028 - 0.21 - - 0.05 - - - - - - 0.0042
    O 0.57 1.94 0.83 0.005 0.005 1.31 0.0021 - - 0.22 0.018 - - - - - - - 0.0058
    P 0.58 2.31 0.95 0.004 0.003 1.34 0.0024 - - 0.19 - 0.04 - - - - - - 0.0061
    Q 0.57 2.12 0.91 0.006 0.005 1.27 0.0038 - - - 0.021 0.06 - - - - - - 0.0052
    R 0.54 2.26 0.74 0.006 0.004 1.57 0.0023 - - - - - 0.0012 - - - - - 0.0037
    S 0.61 2.06 0.93 0.005 0.004 1.97 0.0037 - - - - - - 0.0011 - - - - 0.0042
    T 0.63 2.00 0.86 0.005 0.003 1.43 0.0011 - - - - - - - 0.0027 - - - 0.0051
    U 0.58 2.08 0.76 0.005 0.006 1.19 0.0020 - - - - - - - - 0.0022 - - 0.0054
    V 0.59 2.18 0.94 0.006 0.004 1.27 0.0033 - - - - - - - - - 0.12 0.27 0.0043
    W 0.60 1.97 1.12 0.006 0.005 0.75 0.0028 - - - - - 0.0031 0.0022 - - - - 0.0037
    X 0.59 1.91 0.94 0.004 0.003 1.35 0.0022 - - - - - 0.0018 - 0.0021 - - - 0.0061
    Y 0.60 2.23 0.78 0.005 0.006 1.34 0.0032 - - - - - 0.0024 - - 0.0034 - - 0.0038
    Z 0.61 2.37 0.88 0.005 0.005 1.21 0.0038 - - - - - 0.0028 - - - 0.18 0.21 0.0054
    [Table 2]
    Kind of steelChemical composition (mass%) *Remainder of Fe and impurities
    CSiMnPSCrAlMoVWNbTiCaMg ZrBCuNiN
    AA 0.54 2.34 0.72 0.003 0.004 1.52 0.0017 - - - - - - 0.0013 0.0014 - - - 0.0052
    AB 0.57 2.11 0.94 0.004 0.006 1.08 0.0022 - - - - - - 0.0018 - 0.0041 - - 0.0049
    AC 0.59 1.95 0.87 0.006 0.005 1.24 0.0040 - - - - - - 0.0021 - - 0.23 0.54 0.0034
    AD 0.62 2.07 1.03 0.006 0.004 1.28 0.0034 - - - - - - - 0.0048 0.0028 - - 0.0046
    AE 0.61 2.16 0.94 0.007 0.003 1.34 0.0028 - - - - - - - 0.0024 - 0.31 0.37 0.0054
    AF 0.59 2.07 0.87 0.003 0.006 1.02 0.0029 - - - - - - - - 0.0031 0.27 0.44 0.0046
    AG 0.62 2.17 0.98 0.005 0.005 1.24 0.0019 - - - - - 0.0016 0.0018 0.0031 - - - 0.0032
    AH 0.60 2.40 0.75 0.004 0.003 1.15 0.0042 0.12 - - - - 0.0021 - 0.0057 0.0025 - - 0.0067
    AI 0.62 1.94 1.18 0.003 0.006 0.94 0.0033 - 0.25 - - - 0.0025 0.0009 - - 0.28 0.52 0.0054
    AJ 0.54 1.87 0.74 0.007 0.003 1.25 0.0011 - - 0.16 - - - 0.0014 0.0016 - - - 0.0040
    AK 0.58 2.23 0.62 0.005 0.005 1.31 0.0020 - - - 0.017 - - - 0.0018 0.0038 - - 0.0048
    AL 0.58 2.06 0.97 0.003 0.005 0.87 0.0017 0.22 0.15 - - - 0.0014 - - - - - 0.0044
    AM 0.75 2.21 0.86 0.006 0.004 1.21 0.0012 - - - - - - - - - - - 0.0052
    AN 0.59 2.32 0.81 0.005 0.003 3.48 0.0018 - - - - - - - - - - - 0.0054
    AO 0.58 1.03 0.84 0.006 0.005 1.05 0.0020 - - - - - - - - - - - 0.0046
    AP 0.60 4.97 0.84 0.005 0.004 1.30 0.0026 - - - - - - - - - - - 0.0060
    AQ 0.58 2.17 0.21 0.006 0.005 1.25 0.0023 - - - - - - - - - - - 0.0057
    AR 0.59 2.22 0.80 0.005 0.004 0.51 0.0017 - - - - - - - - - - - 0.0055
    AS 0.59 2.14 0.83 0.005 0.004 1.32 0.0495 - - - - - - - - - - - 0.0047
    AT 0.58 2.08 0.83 0.004 0.005 1.28 0.0025 - - - - - - - - - - - 0.0097
    AU 0.60 2.26 1.98 0.005 0.006 1.18 0.0028 - - - - - - - - - - - 0.0054
    AV 0.59 2.17 0.87 0.005 0.004 4.02 0.0015 - - - - - - - - - - - 0.0049
    [Table 3]
    Test No.Kind of steelPatenting conditionsQuenching and tempering conditionsTemperature for complete solid-solution of cementite (°C)
    Temperature (°C)Heating temperature (°C)Agitation of quenching solution (cm/sec)Tempering temperature (°C)
    1 A 710 890 50 455 920
    2 B 710 940 50 475 970
    3 C 710 910 50 455 940
    4 D 710 880 50 455 910
    5 E 710 890 50 450 920
    6 F 710 890 50 440 920
    7 G 710 890 50 440 920
    8 H 710 890 50 480 920
    9 I 710 880 50 445 910
    10 J 710 895 50 450 925
    11 K 710 880 50 450 910
    12 L 710 890 50 465 920
    13 M 710 890 50 455 920
    14 N 710 890 50 455 920
    15 O 710 895 50 440 925
    16 P 710 890 50 445 920
    17 Q 710 890 50 440 920
    18 R 710 900 50 445 930
    19 S 710 910 50 455 940
    20 T 710 895 50 445 925
    21 U 710 890 50 435 920
    22 V 710 890 50 440 920
    23 W 710 880 50 430 910
    24 X 710 895 50 440 925
    25 Y 710 890 50 445 920
    26 Z 710 890 50 445 920
    27 AA 710 900 50 445 930
    28 AB 710 885 50 435 915
    29 AC 710 890 50 435 920
    30 AD 710 890 50 445 920
    31 AE 710 890 50 445 920
    32 AF 710 885 50 435 915
    33 AG 710 890 50 445 920
    [Table 4]
    Test No.Kind steelPatenting conditionsQuenching and tempering conditionsTemperature for complete solid-solution of cementite (°C)
    Temperature (°C)Heating temperature (°C)Agitation of quenching solution (cm/sec)Tempering temperature (°C)
    34 AH 710 885 50 450 915
    35 AI 710 880 50 450 910
    36 AJ 710 890 50 435 920
    37 AK 710 895 50 440 925
    38 AL 710 880 50 450 910
    39 AM 710 890 50 445 920
    40 AN 710 970 50 490 1000
    41 AO 710 885 50 430 915
    42 AP 710 890 50 490 920
    43 AQ 710 890 50 440 920
    44 AR 710 875 50 435 905
    45 AS 710 890 50 445 920
    46 AT 710 890 50 440 920
    47 AU 710 890 50 445 920
    48 AV 710 1010 50 500 1040
    49 A 630 890 50 455 900
    50 A 710 890 0 455 920
    51 H 710 890 0 480 920
    52 M 710 890 0 455 920
    53 W 710 885 0 430 910
    54 AK 710 895 0 440 925
    55 B 710 970 50 475 970
    56 C 710 935 50 455 940
    57 I 710 905 50 445 910
    58 AA 710 925 50 445 930
    59 AH 710 910 50 450 915
    60 A 710 875 50 455 920
    61 H 710 870 50 480 920
    62 M 710 870 50 455 920
     
    64 AK 710 870 50 440 925


    [0057] A sample was collected from a 1/4 portion of the diameter D from the outer circumferential surface in the C-cross section of each of the quenched and tempered steel wires, and etching was performed using a nital etching solution. Then, ten photographs of the structure of 10,000-fold were captured using an electronic scanning microscope, and the presence density of iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm was obtained through image analysis (Luzex). In addition, five photographs of the structure of 1,000-fold were captured using an optical microscope, and the area ratio of martensite was obtained through image analysis (Luzex). The prior austenite grain size was measured by performing etching with a picric acid saturated aqueous solution in accordance with JIS G 0551, causing prior austenite grain boundaries to be revealed, and observing the result using an optical microscope. JIS No. 2 tensile test pieces were prepared using the quenched and tempered steel wires, and tensile tests were executed in accordance with JIS Z 2241 and tensile strength, yield strength, and reduction in area were measured.

    [0058] In addition, after the quenched and tempered steel wires were subjected to cold spring forming (coil having an average diameter of 20.2 mm, and effective number of winding of 5.0), annealing treatment was performed at 400°C for 30 min. Both ends were subjected to end polishing, and shot-peening treatment was performed. Thereafter, low-temperature annealing treatment was performed at 230°C for 20 min. Lastly, cold setting was performed, and springs for settling resistance evaluation were prepared. The springs prepared under the conditions described above were heated to 120°C and were fastened at 1,300 MPa for 50 hours. Thereafter, the residual shear strain amounts were measured in order to evaluate the settling resistance. A spring having a residual shear strain amount of 0.029% or less was evaluated as a spring having excellent settling resistance.

    [0059]  Table 5 and Table 6 indicate the area ratio of the tempered martensite, the prior austenite grain size number, the presence density of iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm, and the results of the tensile tests and the settling resistance evaluation tests. The remainder structure was at least one of ferrite, pearlite, bainite, and residual austenite. In addition, based on the results, FIG. 1 shows a relationship between the presence density of iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm and the residual shear strain amount, and FIG. 2 shows a relationship between the presence density of iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm and a reduction in area.
    [Table 5]
    Test No.classificationArea ratio of tempered martensite (%)Prior austenite grain size numberPresence density of iron-based carbide having equivalent circle diameter ranging from 0.15 µm to 0.50 µm (pieces/µm2)Tensile strength (MPa)Yield strength (MPa)Reduction in area %)Residual shear strain amount (%)
    1   92 13.7 0.56 2253 2031 57 0.025
    2   91 14.0 0.97 2232 2021 56 0.023
    3   97 15.1 1.95 2248 2045 56 0.018
    4   94 14.1 1.03 2249 2034 58 0.027
    5   93 14.6 1.53 2221 2018 55 0.018
    6   91 15.1 1.87 2263 2059 53 0.018
    7   91 14.3 1.51 2255 2042 52 0.024
    8   94 14.0 0.42 2210 2007 59 0.028
    9   93 14.5 1.24 2219 2008 53 0.022
    10   92 13.8 0.75 2237 2017 57 0.026
    11   93 14.6 1.50 2204 2001 58 0.028
    12   92 14.2 1.34 2241 2024 55 0.020
    13   95 14.1 1.57 2230 2013 53 0.018
    14   92 14.2 0.78 2267 2047 60 0.023
    15   92 14.6 1.71 2254 2041 53 0.018
    16   94 13.7 0.55 2234 2012 61 0.024
    17 Examples of Invention 95 14.8 1.43 2239 2034 56 0.024
    18 92 14.3 1.16 2263 2053 52 0.018
    19 93 14.7 1.63 2231 2020 58 0.017
    20   91 14.3 1.41 2220 2007 58 0.025
    21   94 14.5 1.26 2269 2059 57 0.018
    22   93 14.1 1.08 2254 2038 56 0.022
    23   95 14.5 1.54 2208 1994 58 0.021
    24   93 14.8 1.78 2214 2010 55 0.021
    25   93 13.9 0.87 2231 2014 57 0.026
    26   92 14.4 1.19 2258 2046 54 0.025
    27   94 14.5 1.41 2262 2049 56 0.023
    28   93 14.6 1.37 2241 2029 52 0.020
    29   93 13.8 0.67 2227 2008 58 0.028
    30   94 14.6 1.08 2260 2043 54 0.019
    31   92 14.0 1.28 2250 2034 52 0.021
    32 33   93 13.8 0.67 2271 2047 56 0.027
      92 14.8 1.84 2247 2043 52 0.016
    34   95 14.2 1.48 2271 2064 55 0.024
    35   93 14.2 1.08 2258 2044 54 0.025
    [Table 6]
    Test No.classificationArea ratio of tempered martensite (%)Prior austenite grain size numberPresence density of iron-based carbide having equivalent circle diameter ranging from 0.15 µm to 0.50 µm (pieces/µm2)Tensile strength (MPa)Yield Strength (MPa)Reduction in area (%)Residual shear strain amount (%)
    36 Examples of Invention 92 14.4 1.42 2239 2027 58 0.021
    37 92 14.2 0.94 2224 2011 59 0.027
    38 91 14.6 1.04 2256 2050 57 0.023
    39 91 14.2 1.06 2222 2010 56 0.024
    40 92 14.0 1.03 2228 2014 58 0.023
    41 96 14.9 1.88 2252 2033 58 0.016
    42 94 14.2 0.51 2233 2022 53 0.026
    43 95 13.9 0.55 2241 2038 55 0.022
    44 92 14.1 1.23 2245 2029 54 0.020
    45 93 13.7 0.61 2238 2017 56 0.025
    46 95 14.3 1.28 2249 2034 52 0.018
    47 94 14.5 1.26 2238 2026 55 0.014
    48 Comparative Examples 92 11.7 1.48 2220 1905 53 0.066
    49 93 11.0 0.08 2238 1924 60 0.075
    50 88 13.7 0.87 2209 1951 61 0.042
    51 85 14.2 0.95 2227 1944 55 0.054
    52 82 14.5 1.51 2156 1874 51 0.060
    53 87 13.8 1.10 2184 1899 58 0.04 8
    54 81 14.4 1.43 2176 1843 52 0.053
    55 91 11.0 0.00 2287 1933 58 0.073
    56 97 12.1 0.37 2253 1950 57 0.071
    57 94 11.5 0.23 2223 1901 58 0.065
    58 92 11.3 0.13 2267 1935 57 0.070
    59 92 11.4 0.28 2217 1942 63 0.068
    60 94 14.3 2.12 2264 2037 43 0.016
    61 92 15.0 2.97 2211 2027 28 0.015
    62 95 14.8 2.64 2220 2023 37 0.017
       
    64 92 14.9 2.72 2204 2014 34 0.015


    [0060] As is clear from Table 5 and Table 6, the test No. 1 to 47 were Examples of the present invention satisfying the requirements regulated in the present invention. In these examples, it had been found that excellent settling resistance such as the residual shear strain amount of 0.029% or less were obtained while workability of reduction in area of 50% or more was maintained.

    [0061] In contrast, in the test No.48 to 64 which were Comparative Examples, either workability or settling resistance was not sufficient.

    [0062] In the test No.50 to 54, the prior austenite grain size or the presence density of iron-based carbide satisfied the range of the regulation of the present invention. However, since the area ratio of the tempered martensite was less than 90%, the residual shear strain amount was large and the settling resistance was low.

    [0063] In addition, in the test No.48, the prior austenite grain size number was less than 12.5. As a result, the residual shear strain amount was large and the settling resistance was low.

    [0064] In addition, in the test No.49 and 55 to 59, the area ratio of the tempered martensite satisfied the range of the regulation of the present invention. However, since the prior austenite grain size number was less than 12.5, the presence density of iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm was less than 0.40 pieces/µm2. As a result, the residual shear strain amount was large and the settling resistance was low.

    [0065] Furthermore, in the test No.60 to 64, the area ratio of the tempered martensite and the prior austenite grain size satisfied the range of the regulation of the present invention. However, the presence density of iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm exceeded 2.00 pieces/µm2. As a result, the reduction in area, that is, the workability was low.

    [0066]  Accordingly, from Examples described above, it is clear that while favorable workability is maintained, excellent settling resistance can be ensured by satisfying the conditions regulated in the present invention, particularly the structure conditions.

    [0067] Hereinabove, a preferable embodiment and Examples of the present invention have been described. Each of the embodiment and Examples is merely an example within the scope of the present invention, and addition, replacement and other changes of the configuration can be made within a range not departing from the present invention. That is, the present invention is not limited by the description above and is only limited by the accompanying Claims. Naturally, the present invention can be suitably changed within the scope thereof.

    [Industrial Applicability]



    [0068] According to the present invention, it is possible to provide a high strength spring steel wire having excellent settling resistance after coiliing while favorable workability is ensured, and a spring including the spring steel wire.


    Claims

    1. A spring steel wire comprising, by mass%,
    C: 0.40% to 0.75%,
    Si: 1.00% to 5.00%,
    Mn: 0.20% to 2.00%,
    P: 0.0001% to 0.0500%,
    S: 0.0001% to 0.0500%,
    Cr: 0.50% to 3.50%,
    Al: 0.0005% to 0.0500%,
    N: 0.0020% to 0.0100%,
    Mo: 0% to 2.00%,
    V: 0% to 0.50%,
    W: 0% to 0.50%,
    Nb: 0% to 0.100%,
    Ti: 0% to 0.100%,
    Ca: 0% to 0.0100%,
    Mg: 0% to 0.0100%,
    Zr: 0% to 0.1000%,
    B: 0% to 0.0100%,
    Cu: 0% to 1.00%,
    Ni: 0% to 3.00%, and
    a remainder of Fe and impurities,
    wherein a structure includes, by area ratio, a tempered martensite of 90% or more,
    wherein a prior austenite grain size number is No. 12.5 or higher,
    wherein a presence density of iron-based carbide having an equivalent circle diameter ranging from 0.15 µm to 0.50 µm is 0.40 pieces/µm2 to 2.00 pieces/µm2, and wherein the prior austenite grain size number and the presence density of iron-based carbide are measured by the methods disclosed in the present application.
     
    2. The spring steel wire according to Claim 1,
    wherein the spring steel wire includes, by mass%, at least one of
    Mo: 0.01% to 2.00%,
    V: 0.01% to 0.50%,
    W: 0.01% to 0.50%,
    Nb: 0.005% to 0.100%, and
    Ti: 0.001% to 0.100%.
     
    3. The spring steel wire according to Claim 1 or 2,
    wherein the spring steel wire includes, by mass%, at least one of
    Ca: 0.0002% to 0.0100%,
    Mg: 0.0002% to 0.0100%,
    Zr: 0.0005% to 0.1000%,
    B: 0.0005% to 0.0100%,
    Cu: 0,05% to 1.00%, and
    Ni: 0.05% to 3.00%.
     
    4. A spring including the spring steel wire according to any one of Claims 1 to 3.
     


    Ansprüche

    1. Ein Federstahldraht, umfassend, in Massen-%,
    C: 0,40% bis 0,75%,
    Si: 1,00% bis 5,00%,
    Mn: 0,20% bis 2,00%,
    P: 0,0001 % bis 0,0500%,
    S: 0,0001 % bis 0,0500%,
    Cr: 0,50% bis 3,50%,
    Al: 0,0005% bis 0,0500%,
    N: 0,0020% bis 0,0100%,
    Mo: 0% bis 2,00%,
    V: 0% bis 0,50%,
    W: 0% bis 0,50%,
    Nb: 0% bis 0,100%,
    Ti: 0% bis 0,100%,
    Ca: 0% bis 0,0100%,
    Mg: 0% bis 0,0100%,
    Zr: 0% bis 0,1000%,
    B: 0% bis 0,0100%,
    Cu: 0% bis 1,00%,
    Ni: 0% bis 3,00%, und
    einen Rest aus Fe und Verunreinigungen,
    wobei eine Struktur, im Flächenverhältnis, einen getemperten Martensit von 90% oder mehr enthält,
    wobei eine Korngrößennummer des vorherigen Austenits Nr. 12,5 oder höher beträgt,
    wobei eine Anwesenheitsdichte von auf Eisen basiertem Carbid mit einem äquivalenten Kreisdurchmesser im Bereich von 0,15 µm bis 0,50 µm 0,40 Stücke/µm2 bis 2,00 Stücke/µm2 beträgt, und
    wobei die Korngrößennummer des vorherigen Austenits und die Anwesenheitsdichte von auf Eisen basiertem Carbid durch die in der vorliegenden Anmeldung offenbarten Verfahren gemessen werden.
     
    2. Der Federstahldraht nach Anspruch 1,
    wobei der Federstahldraht, in Massen-%, mindestens eines aus
    Mo: 0,01% bis 2,00%
    V: 0,01% bis 0,50%,
    W: 0,01% bis 0,50%,
    Nb: 0,005% bis 0,100%, und
    Ti: 0,001% bis 0,100% enthält.
     
    3. Der Federstahldraht nach Anspruch 1 oder 2,
    wobei der Federstahldraht, in Massen-%, mindestens eines aus
    Ca: 0,0002% bis 0,0100%,
    Mg: 0,0002% bis 0,0100%,
    Zr: 0,0005% bis 0,1000%,
    B: 0,0005% bis 0,0100%,
    Cu: 0,05% bis 1,00%, und
    Ni: 0,05% bis 3,00% enthält.
     
    4. Eine Feder, welche den Federstahldraht nach einem der Ansprüche 1 bis 3 enthält.
     


    Revendications

    1. Fil en acier à ressort comprenant, en % en masse,
    C : 0,40 % à 0,75 %,
    Si: 1,00 % à 5,00 %,
    Mn : 0,20 % à 2,00 %,
    P : 0,0001 % à 0,0500 %,
    S : 0,0001 % à 0,0500 %,
    Cr : 0,50 % à 3,50 %,
    Al : 0,0005 % à 0,0500 %,
    N : 0,0020 % à 0,0100 %,
    Mo : 0 % à 2,00 %,
    V : 0 % à 0,50 %,
    W : 0 % à 0,50 %,
    Nb: 0% à 0,100%,
    Ti : 0 % à 0,100 %,
    Ca : 0% à 10,0100%,
    Mg 0 % à 0,0100 %,
    Zr : 0 % à 0,1000 %,
    B : 0 % à 0,0100 %,
    Cu : 0 % à 1,00 %,
    Ni : 0 % à 3,00 %, et
    pour le reste, du Fe et des impuretés,
    dans lequel la structure comprend, en proportion en surface, une martensite revenue à raison de 90 % ou plus,
    dans lequel la taille antérieure des grains d'austénite est un N° 12,5 ou plus,
    dans lequel la densité de présence du carbure à base de fer ayant un diamètre équivalent au cercle allant de 0,15 µm à 0,50 µm est de 0,40 pièce/µm2 à 2,00 pièce/µm2, et
    dans lequel la taille antérieure des grains d'austénite et la densité de présence du carbure à base de fer sont mesurées par les méthodes divulguées dans la présente demande.
     
    2. Fil en acier à ressort selon la revendication 1,
    dans lequel l'acier à ressort contient, en % en masse, au moins l'un parmi :

    Mo : 0,01 % à 2,00 %,

    V: 0,01 % à 0,50 %,

    W: 0,01 % à 0,50 %,

    Nb: 0,005 % à 0,100 %, et

    Ti: 0,001 % à 0,100 %.


     
    3. Fil en acier à ressort selon la revendication 1 ou 2,
    dans lequel l'acier à ressort contient, en % en masse, au moins l'un parmi :

    Ca: 0,0002 % à 0,0100 %,

    Mg : 0,0002 % à 0,0100 %,

    Zr : 0,0005 % à 0,1000 %,

    B : 0,0005 % à 0,0100 %,

    Cu: 0,05 % à 1,00 %, et

    Ni: 0,05 % à 3,00 %.


     
    4. Ressort contenant le fil en acier à ressort selon l'une quelconque des revendications 1 à 3.
     




    Drawing








    Cited references

    REFERENCES CITED IN THE DESCRIPTION



    This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

    Patent documents cited in the description