(19)
(11)EP 3 397 590 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
17.06.2020 Bulletin 2020/25

(21)Application number: 16813176.1

(22)Date of filing:  29.11.2016
(51)International Patent Classification (IPC): 
C01B 32/174(2017.01)
C08J 3/20(2006.01)
C08K 3/04(2006.01)
B82Y 30/00(2011.01)
C08J 3/22(2006.01)
C09D 123/12(2006.01)
(86)International application number:
PCT/US2016/064008
(87)International publication number:
WO 2017/116592 (06.07.2017 Gazette  2017/27)

(54)

POLYMER COATED MULTIWALL CARBON NANOTUBES

POLYMERBESCHICHTETE MEHRWANDIGE KOHLENSTOFFNANORÖHRCHEN

NANOTUBES DE CARBONE À PAROIS MULTIPLES REVÊTUS D'UN POLYMÈRE


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 29.12.2015 US 201562272468 P
15.04.2016 US 201662323146 P
15.04.2016 US 201662323151 P

(43)Date of publication of application:
07.11.2018 Bulletin 2018/45

(73)Proprietors:
  • SABIC Global Technologies B.V.
    4612 PX Bergen op Zoom (NL)
  • Georgia Tech Research Corporation
    Atlanta, GA 30318 (US)

(72)Inventors:
  • WANG, Po-Hsiang
    Atlanta Georgia 30339 (US)
  • GHOSHAL, Sushanta
    Summerville South Carolina 29483 (US)
  • VERGHESE, Nikhil
    6167RD Geleen (NL)
  • KUMAR, Satish
    Atlanta Georgia 30345 (US)

(74)Representative: Lang, Johannes 
Bardehle Pagenberg Partnerschaft mbB Patentanwälte, Rechtsanwälte Prinzregentenplatz 7
81675 München
81675 München (DE)


(56)References cited: : 
US-A1- 2011 220 851
  
  • QINGLIANG HE ET AL: "Flame-Retardant Polypropylene/Multiwall Carbon Nanotube Nanocomposites: Effects of Surface Functionalization and Surfactant Molecular Weight", MACROMOLECULAR CHEMISTRY AND PHYSICS., vol. 215, no. 4, 13 February 2014 (2014-02-13), pages 327-340, XP55344841, DE ISSN: 1022-1352, DOI: 10.1002/macp.201300608
  • YANG B X ET AL: "Enhancement of the mechanical properties of polypropylene using polypropylene-grafted multiwalled carbon nanotubes", COMPOSITES SCIENCE AND TECHNOLOGY, ELSEVIER, AMSTERDAM, NL, vol. 68, no. 12, 1 September 2008 (2008-09-01), pages 2490-2497, XP025431667, ISSN: 0266-3538, DOI: 10.1016/J.COMPSCITECH.2008.05.001 [retrieved on 2008-05-08]
  • CAUSIN V ET AL: "Nucleation, structure and lamellar morphology of isotactic polypropylene filled with polypropylene-grafted multiwalled carbon nanotubes", EUROPEAN POLYMER JOURNAL, PERGAMON PRESS LTD. OXFORD, GB, vol. 45, no. 8, 1 August 2009 (2009-08-01) , pages 2155-2163, XP026336890, ISSN: 0014-3057, DOI: 10.1016/J.EURPOLYMJ.2009.05.026 [retrieved on 2009-05-27]
  
Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


Description

TECHNICAL FIELD



[0001] The present disclosure relates to polymer coated carbon nanotubes and methods of making same, more specifically polypropylene coated multiwall carbon nanotubes and methods of making same.

BACKGROUND



[0002] Carbon nanotubes (CNT), including multiwall carbon nanotubes (MWNT), have been incorporated into various polymer systems owing to their outstanding tensile modulus (270-950 GPa), tensile strength (11-63 GPa), as well as thermal (200-3000 W/m/K at 300 K) and electrical conductivity (102-107 S/m at 300 K). While interfacial stress transfer from nanotubes to polymer accounts for mechanical reinforcement, CNT can also act as a nucleating agent for polymer crystallization, as well as induce the formation of a highly ordered interphase polymer layer in many polymer/CNT composites.

[0003] Polypropylene (PP) is a widely used commercial polymer due to its excellent chemical stability, physical and mechanical properties, processability and low cost. PP has numerous industrial applications, such as fiber manufacturing, packaging, automotive components, construction, etc. Over the years, PP has been reinforced with fibrous fillers (e.g., carbon, Kevlar, natural fibers) and particulate fillers (e.g., talc, mica, clay), as well as by melt blending with other polymers to enhance its mechanical properties. Emergence of CNT has paved the way for new polymer composite applications in various fields, such as electromagnetic interference (EMI) shielding, enhanced oxygen barrier performance, and for antistatic purposes.

[0004] Although the benefits of introducing CNT into PP can be many fold, it is difficult to fully disperse CNT into the PP polymer matrix, since CNT tend to bundle together through van der Waals forces. Only a limited number of organic solvents, such as N,N-dimethylformamide (DMF), 1,2-dichlorobenzene (ODCB), N-methylpyrrolidinone (NMP), tetrahydrofuran (THF) and chloroform, are known to disperse CNT to some extent. Nanocomposites incorporating CNT can be successfully produced via a solution approach with conjugated polymers, aromatic polymers, and other polar polymers like pol(vinyl chloride), polyacrylonitrile, poly(methyl methacrylate), poly(vinyl alcohol) and poly (ethylene oxide), etc. However, PP, due to its non-polar nature, does not have sufficient solubility in these solvents.

[0005] Several approaches have been used for improving the dispersion of CNT in PP, for example chemical modification of CNT and/or the polymer through covalent functionalization and grafting; incorporation of a compatibilizer such as maleic anhydride grafted PP (MA-g-PP) and maleic anhydride grafted styrene-ethylene/butylenes-styrene copolymer (MA-SEBS); surfactants, such as sodium dodecyl sulfate (SDS) and sodium dodecylbenzene sulfonate (NaDDBS); master batch dilution; mechanical dispersion including ultra-sound assisted melt extrusion; and some combinations thereof.

[0006] PP coating of CNT has been reported via grafting of MA-g-PP or PP. One method stabilizes CNT in aqueous solution via non-covalent association between nanotubes and poly(vinyl pyrrolidone) (PVP), wherein the PVP wrapped CNT can be further dispersed in other polymers, e.g., in poly(vinyl alcohol). Another method produced PE wrapped CNT via crystallization in ODCB, wherein the MWNT were wrapped by a homogenous coating of PE, while a PP coating could not be achieved by the same procedure. In yet another method, CNT were encapsulated with MA-g-PP via a solution mixing approach by using butanol and xylene. Ball milling was also used for forming CNT polymer composites, and while some MA-g-PP chains adsorbed onto sidewalls of MWNT, PP did not exhibit the same behavior.

[0007] Q. He et al., "Flame-Retardant Polypropylene/Multiwall Carbon Nanotube Nanocomposites: Effects of Surface Functionalization and Surfactant Molecular Weight," Macromolecular Chem. and Phys., 2014, 215(4): 327-340, describe functionalized polypropylene coated multiwall carbon nanotubes with amino group functionalization, wherein 3-aminopropyl-triethoxysilane (APTES) was used to modify f-CNTs (functionalized carbon nanotubes), and maleic-anhydride-grafted PP (MAPP) with two molecular weights was used to further improve the dispersion of f-CNTs in the PP matrix. B.-X. Yang et al., "Enhancement of the mechanical properties of polypropylene using polypropylene-grafted multiwalled carbon nanotubes," Composites Sci. and Tech., 2008, 68(12): 2490-2497, studied PP composites, wherein PP was grafted onto multiwalled carbon nanotubes (MWNTs) by melt blending PP containing 0.6 wt% of maleic anhydride and amine-functionalized MWNTs. V. Causin et al., "Nucleation, structure and lamellar morphology of isotactic polypropylene filled with polypropylene-grafted multiwalled carbon nanotubes", European Polymer Journal, 2009, 45(8): 2155-2163, studied PP-based nanocomposites filled with PP-grafted multiwalled carbon nanotubes (PP-g-MWNT), wherein the materials were prepared using amino groups by grafting PP-MA to MWNT-NH2 by melt blending. US 2011/0220851 A1 discloses a method of dispersing nanotubes and/or nanoplatelets in a polyolefin. Thus, there is an ongoing need for the development of PP coated CNT (PP/CNT) and methods of making same, wherein the PP encapsulates the CNT via a non-perturbing PP coating (e.g., a PP coating via non-covalent means) to prevent nanotube re-aggregation.

BRIEF SUMMARY



[0008] The present invention provides a method of making polypropylene-coated functionalized multiwall carbon nanotubes (PP/f-MWNT), the method comprising (a) contacting pristine multiwall carbon nanotubes (p-MWNT) with nitric acid to produce functionalized multiwall carbon nanotubes (f-MWNT) comprising carboxylic acid groups, (b) contacting at least a portion of the f-MWNT with a first solvent to form a f-MWNT comprising carboxylic acid groups dispersion, (c) contacting polypropylene (PP) with a second solvent to form a PP solution, (d) contacting at least a portion of the f-MWNT comprising carboxylic acid groups dispersion with at least a portion of the PP solution to form a PP and f-MWNT comprising carboxylic acid groups suspension, and (e) drying at least a portion of the PP and f-MWNT comprising carboxylic acid groups suspension to form the PP/f-MWNT comprising carboxylic acid groups.

[0009] Disclosed herein are polypropylene-coated functionalized multiwall carbon nanotubes (PP/f-MWNT) produced by a process comprising (a) contacting pristine multiwall carbon nanotubes (p-MWNT) with nitric acid to produce functionalized multiwall carbon nanotubes (f-MWNT), (b) contacting at least a portion of the f-MWNT with a first solvent to form a f-MWNT dispersion. (c) contacting polypropylene (PP) with a second solvent to form a PP solution, (d) contacting at least a portion of the f-MWNT dispersion with at least a portion of the PP solution to form a PP and f-MWNT suspension, and (e) drying at least a portion of the PP and f-MWNT suspension to form the PP/f-MWNT.

[0010] The present invention further provides polypropylene-coated functionalized multiwall carbon nanotubes (PP/f-MWNT) comprising functionalized multiwall carbon nanotubes (f-MWNT) in an amount of from about 0.5 wt.% to about 80 wt.%, based on the total weight of the PP/f-MWNT; and polypropylene (PP) in an amount of from about 20 wt.% to about 99.5 wt.%, based on the total weight of the PP/f-MWNT, wherein the PP coats the f-MWNT via non-covalent interactions, and wherein the non-covalent interactions exclude hydrogen bonding.

[0011] Also disclosed herein are polypropylene-coated functionalized multiwall carbon nanotubes (PP/f-MWNT) comprising functionalized multiwall carbon nanotubes (f-MWNT) in an amount of from about 0.5 wt.% to about 10 wt.%, based on the total weight of the PP/f-MWNT, and polypropylene (PP) in an amount of from about 90 wt.% to about 99.5 wt.%, based on the total weight of the PP/f-MWNT; wherein the PP coats the f-MWNT via non-covalent interactions; wherein the PP is characterized by an isotacticity of from about 90% to 100%; wherein the f-MWNT have a diameter of from about 5 nm to about 20 nm, a length of from about 0.5 microns to about 20 microns, and from about 5 walls to about 15 walls; and wherein a PP coating has thickness of from about 1 nm to about 10 nm.

BRIEF DESCRIPTION OF THE DRAWINGS



[0012] For a detailed description of the preferred embodiments, reference will now be made to the accompanying drawings in which:

Figures 1A and 1B display a schematic illustration of multiwall carbon nanotubes (MWNT) functionalization to produce functionalized multiwall carbon nanotubes (f-MWNT), and polypropylene-coated functionalized multiwall carbon nanotubes (PP/f-MWNT) preparation;

Figures 2A and 2B display (a) Raman spectra and (b) wide angle X-ray diffraction (WAXD) of pristine MWNT (p-MWNT) and f-MWNT;

Figure 3 displays Fourier transform infrared spectroscopy (FTIR) spectra of p-MWNT and f-MWNT;

Figures 4A through 4H display transmission electron microscopy (TEM) images of p-MWNT and f-MWNT, as well as optical photographs of p-MWNT, f-MWNT, and PP/f-MWNT, dried and in suspensions and/or dispersions;

Figures 5A through 5F display scanning electron microscopy (SEM) images of PP/f-MWNT and maleic anhydride grafted PP (MA-g-PP) coated f-MWNT (MA-g-PP/f-MWNT);

Figures 6A through 6D display TEM images of (a,b) PP/f-MWNT and (c,d) MA-g-PP/f-MWNT master batches;

Figures 7A and 7B display thermogravimetric analysis (TGA) under nitrogen (a) for MA-g-PP and MA-g-PP/f-MWNT; and (b) for PP and PP/f-MWNT;

Figure 8 displays TGA under nitrogen for p-MWNT and f-MWNT;

Figures 9A and 9B display TGA under nitrogen for (a) PP/f-MWNT and (b) MA-g-PP/f-MWNT before and after xylene wash;

Figures 10A through 10D display SEM images of (a) f-MWNT, (b) PP/f-MWNT, (c) PP/f-MWNT washed in xylene at 70 °C, and (d) PP/f-MWNT washed in xylene at 120 °C;

Figure 11 displays FTIR spectra of PP, PP/f-MWNT, MA-g-PP, and MA-g-PP/f-MWNT;

Figure 12 displays FTIR spectra of PP, PP/f-MWNT, MA-g-PP, and MA-g-PP/f-MWNT, for the entire recorded wavenumber range;

Figure 13 displays Raman spectra of p-MWNT, f-MWNT, PP/f-MWNT, and MA-g-PP/f-MWNT;

Figures 14A and 14B display Raman spectra of p-MWNT, f-MWNT, PP/f-MWNT, and MAg-PP/f-MWNT;

Figures 15A and 15B display optical micrographs of PP/f-MWNT and MA-g-PP/f-MWNT;

Figure 16 displays WAXD curves for PP, PP/f-MWNT, and MA-g-PP/f-MWNT;

Figures 17A through 17D display DSC plots of PP, PP/f-MWNT, MA-g-PP, and MA-g-PP/f-MWNT; and

Figures 18A through 18C display optical micrographs of PP/MWNT nanocomposites at 0.1 wt.% MWNT loading using (a) a PP/f-MWNT master batch; (b) a MA-g-PP/f-MWNT master batch; and (c) p-MWNT.


DETAILED DESCRIPTION



[0013] The present invention refers to polypropylene-coated functionalized multiwall carbon nanotubes (PP/f-MWNT) and methods of making same. The PP/f-MWNT comprise functionalized multiwall carbon nanotubes (f-MWNT) in an amount of from about 0.5 wt.% to about 80 wt.%, based on the total weight of the PP/f-MWNT; and polypropylene (PP) in an amount of from about 20 wt.% to about 99.5 wt.%, based on the total weight of the PP/f-MWNT. The PP coats the f-MWNT via non-covalent interactions, and the non-covalent interactions exclude hydrogen bonding. In an embodiment, the non-covalent interactions can comprise intermolecular CH-π interactions.

[0014] A method of making PP/f-MWNT comprises the steps of (a) contacting pristine multiwall carbon nanotubes (p-MWNT) with nitric acid to produce f-MWNT comprising carboxylic acid groups; (b) contacting at least a portion of the f-MWNT with a first solvent to form a f-MWNT comprising carboxylic acid groups dispersion; (c) contacting PP with a second solvent to form a PP solution; (d) contacting at least a portion of the f-MWNT comprising carboxylic acid groups dispersion with at least a portion of the PP solution to form a PP and f-MWNT comprising carboxylic acid groups suspension; and (e) drying at least a portion of the PP and f-MWNT comprising carboxylic acid groups suspension to form the PP/f-MWNT. The step (e) of drying the PP and f-MWNT suspension can occur under agitating, stirring, magnetic stirring, or combinations thereof; at a temperature of from about from about 40 °C to about 80 °C; and at a pressure of from about 50 mbar to about 1,013 mbar.

[0015] Other than in the operating examples or where otherwise indicated, all numbers or expressions referring to quantities of ingredients, reaction conditions, and the like, used in the specification and claims are to be understood as modified in all instances by the term "about." Various numerical ranges are disclosed herein. Because these ranges are continuous, they include every value between the minimum and maximum values. The endpoints of all ranges reciting the same characteristic or component are independently combinable and inclusive of the recited endpoint. Unless expressly indicated otherwise, the various numerical ranges specified in this application are approximations. The endpoints of all ranges directed to the same component or property are inclusive of the endpoint and independently combinable. The term "from more than 0 to an amount" means that the named component is present in some amount more than 0, and up to and including the higher named amount.

[0016] The terms "a," "an," and "the" do not denote a limitation of quantity, but rather denote the presence of at least one of the referenced item. As used herein the singular forms "a," "an," and "the" include plural referents.

[0017] As used herein, "combinations thereof" is inclusive of one or more of the recited elements, optionally together with a like element not recited, e.g., inclusive of a combination of one or more of the named components, optionally with one or more other components not specifically named that have essentially the same function. As used herein, the term "combination" is inclusive of blends, mixtures, alloys, reaction products, and the like.

[0018] Reference throughout the specification to "an embodiment," "another embodiment," "other embodiments," "some embodiments," and so forth, means that a particular element (e.g., feature, structure, property, and/or characteristic) described in connection with the embodiment is included in at least an embodiment described herein, and may or may not be present in other embodiments. In addition, it is to be understood that the described element(s) can be combined in any suitable manner in the various embodiments.

[0019] As used herein, the terms "inhibiting" or "reducing" or "preventing" or "avoiding" or any variation of these terms, include any measurable decrease or complete inhibition to achieve a desired result.

[0020] As used herein, the term "effective," means adequate to accomplish a desired, expected, or intended result.

[0021] As used herein, the terms "comprising" (and any form of comprising, such as "comprise" and "comprises"), "having" (and any form of having, such as "have" and "has"), "including" (and any form of including, such as "include" and "includes") or "containing" (and any form of containing, such as "contain" and "contains") are inclusive or open-ended and do not exclude additional, unrecited elements or method steps.

[0022] Unless defined otherwise, technical and scientific terms used herein have the same meaning as is commonly understood by one of skill in the art.

[0023] Compounds are described herein using standard nomenclature. For example, any position not substituted by any indicated group is understood to have its valency filled by a bond as indicated, or a hydrogen atom. A dash ("-") that is not between two letters or symbols is used to indicate a point of attachment for a substituent. For example, -CHO is attached through the carbon of the carbonyl group.

[0024] A method of making PP/f-MWNT comprises a step of contacting pristine multiwall carbon nanotubes (p-MWNT) with nitric acid to produce functionalized multiwall carbon nanotubes (f-MWNT) comprising carboxylic acid groups. For purposes of the disclosure herein, the term "pristine multiwall carbon nanotubes" or "p-MWNT" refers to multiwall carbon nanotubes (MWNT) as synthesized, which MWNT could have been subjected to a purification and/or isolation step, but which have not been subjected to a chemical functionalization step. As used herein, "chemical functionalization" refers to a method or process of introducing a functional group in a given structure, for example introducing one or more carboxyl groups into a MWNT structure.

[0025] In an embodiment, the step of contacting p-MWNT with nitric acid can comprise contacting at least a portion of the p-MWNT with water to form a p-MWNT aqueous suspension. The p-MWNT aqueous suspension can be homogenized by agitating, stirring, magnetic stirring, sonicating, and the like, or combinations thereof, for a time period of from about 1 minute to about 4 hours, alternatively from about 5 minutes to about 2 hours, or alternatively from about 15 minutes to about 30 minutes. In an embodiment, p-MWNT aqueous suspension can be magnetically stirred. As will be appreciated by one of skill in the art, and with the help of this disclosure, MWNT (e.g., p-MWNT) have a tendency to clump together and settle in solution, and as such a solution or suspension containing MWNT has to be agitated by any suitable methodology to be homogenized.

[0026] In an embodiment, at least a portion of p-MWNT aqueous suspension can be contacted with nitric acid to form a p-MWNT acidic suspension, wherein the p-MWNT acidic suspension can have a nitric acid concentration of from about 8 molar (mol/L or M) to about 12 M, alternatively from about 9 M to about 11 M, or alternatively from about 9.5 M to about 10.5 M.

[0027] In an embodiment, at least a portion of the p-MWNT acidic suspension can be dispersed to form a p-MWNT acidic dispersion. In an embodiment, dispersing at least a portion of the p-MWNT acidic suspension to form a p-MWNT acidic dispersion can comprise agitating, stirring, magnetic stirring, sonicating, and the like, or combinations thereof, for a time period of from about 5 minutes to about 4 hours, alternatively from about 10 minutes to about 2 hours, or alternatively from about 15 minutes to about 45 minutes. In an embodiment, the p-MWNT acidic suspension can be sonicated to form the p-MWNT acidic dispersion.

[0028] In an embodiment, at least a portion of the p-MWNT acidic dispersion can be refluxed to produce the functionalized multiwall carbon nanotubes (f-MWNT). Generally, refluxing can provide for maintaining a substantially constant temperature (e.g., reaction temperature, such as a temperature needed for chemical functionalization of MWNT). The p-MWNT acidic dispersion can be refluxed at a temperature of from about 100 °C to about 140 °C, alternatively from about 110 °C to about 130 °C, or alternatively from about 115 °C to about 125 °C. The p-MWNT acidic dispersion can be refluxed for a time period of from about 12 hours to about 48 hours, alternatively from about 16 hours to about 42 hours, or alternatively from about 18 hours to about 36 hours.

[0029] A method of making PP/f-MWNT comprises a step of contacting at least a portion of the f-MWNT with a first solvent to form an f-MWNT comprising carboxylic acid groups dispersion. In an embodiment, at least a portion of the f-MWNT comprising carboxylic acid groups can be washed with water to produce water washed f-MWNT.

[0030] In some embodiments, washing at least a portion of the f-MWNT with water to produce water washed f-MWNT can comprise repeatedly centrifuging f-MWNT suspended in water and re-suspending the f-MWNT, as many times as necessary to remove substantially all acid from the f-MWNT. For example, a refluxing mixture comprising the f-MWNT can be centrifuged to produce isolated f-MWNT (e.g., as a precipitate) by decanting or otherwise removing the supernatant formed during centrifuging a refluxing mixture comprising the f-MWNT. The isolated f-MWNT can be re-suspended or re-dispersed in water, for example by shaking the f-MWNT in water, vortexing, stirring, and the like, or combinations thereof, and the resulting mixture can be centrifuged to isolate the f-MWNT. As will be appreciated by one of skill in the art and with the help of this disclosure, repeatedly centrifuging and re-suspending the f-MWNT removes acid traces from the f-MWNT, as such acid could interfere with the intended use for f-MWNT. In an embodiment, the f-MWNT can be suspended in water and centrifuged as many times as it is necessary or effective for the supernatant to have a neutral pH. For purposes of the disclosure herein a neutral pH refers to a value of about 7, and/or the pH of the water used for re-suspending the f-MWNT.

[0031] In other embodiments, washing at least a portion of the f-MWNT with water to produce water washed f-MWNT can comprise washing the f-MWNT on a filter. For example, a refluxing mixture comprising the f-MWNT can be filtered to produce isolated f-MWNT (e.g., as a precipitate on the filter) by removing a filtrate. The isolated f-MWNT can be washed on the filter with water, until the filtrate reaches a neutral pH. As will be appreciated by one of skill in the art and with the help of this disclosure, repeatedly washing the f-MWNT on the filter can remove acid traces from the f-MWNT, as such acid could interfere with the intended use for f-MWNT.

[0032] In yet other embodiments, washing at least a portion of the f-MWNT with water to produce water washed f-MWNT can comprise any suitable combination of (i) repeatedly centrifuging f-MWNT suspended in water and re-suspending the f-MWNT in water and (ii) washing the f-MWNT on a filter, as necessary to remove substantially all acid from the f-MWNT.

[0033] In an embodiment, at least a portion of the water washed f-MWNT can be washed with the first solvent to produce first solvent washed f-MWNT. In an embodiment, the first solvent can comprise any suitable polar solvent. Nonlimiting examples of polar solvents suitable for use as a first solvent in the present disclosure include an alcohol, methanol, ethanol, propanol, isopropanol, butanol, pentanol, a mild acid, acetic acid, lactic acid, oxalic acid, formic acid, succinic acid, acetone, and the like, or combinations thereof. As will be appreciated by one of skill in the art, and with the help of this disclosure, functionalizing the MWNT introduces carboxylic groups in the structure of the MWNT, thereby enhancing their solubility (e.g., ability to form a stable suspension or dispersion) in polar solvents. In an embodiment, the first solvent comprises butanol.

[0034] In an embodiment, washing at least a portion of the water washed f-MWNT with the first solvent to produce first solvent washed f-MWNT can comprise any suitable combination of (i) repeatedly centrifuging f-MWNT suspended in the first solvent and re-suspending the f-MWNT in the first solvent and (ii) washing the f-MWNT on a filter with the first solvent, as necessary to remove substantially all water from the f-MWNT. As will be appreciated by one of skill in the art, and with the help of this disclosure, the f-MWNT are more soluble in the first solvent than in water, and as such it is important to remove the water from the f-MWNT, to improve the solubility of the f-MWNT in the first solvent.

[0035] In an embodiment, washing at least a portion of the water washed f-MWNT with the first solvent to produce first solvent washed f-MWNT can comprise washing the f-MWNT on a filter with the first solvent.

[0036] In an embodiment, at least a portion of the first solvent washed f-MWNT can be contacted with the first solvent to form an f-MWNT suspension. The first solvent washed f-MWNT can be suspended in the first solvent by shaking the f-MWNT in the first solvent, vortexing, stirring, and the like, or combinations thereof.

[0037] In an embodiment, at least a portion of the f-MWNT suspension can be dispersed to form the f-MWNT comprising carboxylic acid groups dispersion. In an embodiment, dispersing at least a portion of the f-MWNT suspension to form the f-MWNT dispersion can comprise agitating, stirring, magnetic stirring, sonicating, and the like, or combinations thereof, for a time period of from about 24 hours to about 72 hours, alternatively from about 36 hours to about 60 hours, or alternatively from about 42 hours to about 56 hours. In an embodiment, the f-MWNT suspension can be sonicated to form the f-MWNT dispersion.

[0038] In an embodiment, the f-MWNT dispersion can have a concentration of f-MWNT in the first solvent of from about 5 mg/liter to about 100 mg/liter, alternatively from about 20 mg/liter to about 80 mg/liter, or alternatively from about 40 mg/liter to about 60 mg/liter, based on the volume of the first solvent. In an embodiment, the f-MWNT dispersion can be stable for a time period of from about 1 month to about 1 year, alternatively from about 2 months to about 10 months, or alternatively from about 3 months to about 9 months.

[0039] A method of making PP/f-MWNT comprises a step of contacting polypropylene (PP) with a second solvent to form a PP solution. In an embodiment, contacting PP with a second solvent can comprise heating the PP in the second solvent under agitating, stirring, magnetic stirring, and the like, or combinations thereof. The second solvent can be heated to a temperature effective to allow for substantially complete dissolution of PP in the second solvent. As will be appreciated by one of skill in the art, and with the help of this disclosure, PP does not dissolve in solvents under regular conditions, e.g., ambient temperature. Further, as will be appreciated by one of skill in the art, and with the help of this disclosure, the solvent can be heated up to a temperature that is just below the boiling point of the solvent. Further, as will be appreciated by one of skill in the art, and with the help of this disclosure, the solvent can be heated up to a temperature that is just below the melting point of the polymer, when the melting point of the polymer is lower than the boiling point of the solvent.

[0040] In some embodiments, the second solvent can be heated to a temperature in a range of from about 80 °C to about 130 °C, alternatively from about 90 °C to about 125 °C, or alternatively from about 100 °C to about 120 °C.

[0041] In an embodiment, the second solvent can comprise an aromatic hydrocarbon solvent, a cycloalkane, and the like, or combinations thereof. Nonlimiting examples of second solvent suitable for use in the present disclosure include xylene, o-xylene, m-xylene, p-xylene, ethylbenzene, toluene, tetralin, chlorobenzene, cyclohexane, decalin, and the like, or combinations thereof.

[0042] In an embodiment, the PP solution can have a concentration of PP in the second solvent of from about 0.5 g/liter to about 5 g/liter, alternatively from about 1 g/liter to about 4 g/liter, or alternatively from about 1.5 g/liter to about 2.5 g/liter, based on the volume of the second solvent.

[0043] A method of making PP/f-MWNT comprises a step of contacting at least a portion of the f-MWNT comprising carboxylic acid groups dispersion with at least a portion of the PP solution to form a PP and f-MWNT comprising carboxylic acid groups suspension.

[0044] In an embodiment, the f-MWNT comprising carboxylic acid groups dispersion can be heated to a first temperature prior to contacting at least a portion of the f-MWNT dispersion with at least a portion of the PP solution. As will be appreciated by one of skill in the art, and with the help of this disclosure, if the temperature of the f-MWNT dispersion is too low (as compared to the temperature of the PP solution), the PP could precipitate upon contact with the f-MWNT dispersion (as opposed to uniformly dispersing into the forming solvent mixture, to facilitate coating the f-MWNT).

[0045] In an embodiment, the PP solution can be characterized by a second temperature in a range of from about 80 °C to about 130 °C, alternatively from about 90 °C to about 125 °C, or alternatively from about 100 °C to about 120 °C. In some embodiments, the second temperature can be the same as the temperature at which the second solvent was heated to in order to facilitate the dissolution of PP in the second solvent. In some embodiments, the second temperature can be different than the temperature at which the second solvent was heated to in order to facilitate the dissolution of PP in the second solvent. For example, the PP solution can be cooled or allowed to cool to the second temperature, wherein the second temperature is lower than the heating temperature of the second solvent by equal to or greater than about 1 °C, alternatively equal to or greater than about 5 °C, or alternatively equal to or greater than about 10 °C.

[0046] In an embodiment, the second temperature can be greater than the first temperature. In an embodiment, the second temperature can be greater than the first temperature by equal to or greater than about 30 °C, alternatively equal to or greater than about 40 °C, or alternatively equal to or greater than about 50 °C.

[0047] In an embodiment, the PP solution can be added to the f-MWNT dispersion to form the PP and f-MWNT suspension, wherein the f-MWNT dispersion can be characterized by a first temperature, wherein the PP solution can be characterized by a second temperature, and wherein the first temperature can be lower than the second temperature. In an embodiment, the PP solution can be added dropwise to the f-MWNT dispersion to form the PP and f-MWNT suspension. For purposes of the disclosure herein, the term "dropwise" refers to adding the PP solution to the f-MWNT dispersion discontinuously, intermittently, slowly, via discrete or separate aliquots, to prevent the precipitation of the PP upon contact with the f-MWNT dispersion (as opposed to uniformly dispersing into the forming mixture, to facilitate coating the f-MWNT).

[0048] In an embodiment, the PP solution can be added to the f-MWNT dispersion at a flow rate of from about 20 mL/minute to about 40 mL/minute, alternatively from about 22.5 mL/minute to about 37.5 mL/minute, or alternatively from about 25 mL/minute to about 35 mL/minute.

[0049] In an embodiment, the PP solution can be added to the f-MWNT dispersion under agitating, stirring, magnetic stirring, and the like, or combinations thereof, to form the PP and f-MWNT suspension.

[0050] In an embodiment, the PP and f-MWNT suspension can have a volumetric ratio of the second solvent to the first solvent of from about 1:1 to about 1:5, alternatively from about 1.2:1 to about 1:4, or alternatively from about 1.5:1 to about 1:3. As will be appreciated by one of skill in the art, and with the help of this disclosure, the PP solution and the f-MWNT dispersion can be combined in any amount effective to produce a desired volumetric ratio of the second solvent to the first solvent in the PP and f-MWNT suspension.

[0051] In an embodiment, the PP and f-MWNT suspension can have a weight ratio of f-MWNT to PP of from about 0.5:99.5 to about 80:20, alternatively from about 1:99 to about 60:40, or alternatively from about 10:90 to about 50:50. Without wishing to be limited by theory, a weight ratio of f-MWNT to PP of about 80:20 can be achieved when a single polymer molecule is coating a single f-MWNT.

[0052] A method of making PP/f-MWNT comprises a step of drying at least a portion of the PP and f-MWNT comprising carboxylic acid groups suspension to form the PP/f-MWNT comprising carboxylic acid groups. In an embodiment, drying at least a portion of the PP and f-MWNT suspension can occur under agitating, stirring, magnetic stirring, and the like, or combinations thereof, to provide for uniform solvent evaporation.

[0053] In an embodiment, drying at least a portion of the PP and f-MWNT suspension can occur at a temperature of from about from about 40 °C to about 80 °C, alternatively from about from about 45 °C to about 75 °C, or alternatively from about from about 50 °C to about 70 °C.

[0054] In some embodiments, drying at least a portion of the PP and f-MWNT suspension can occur under vacuum. In other embodiments, drying at least a portion of the PP and f-MWNT suspension can occur at ambient pressure (e.g., without vacuum). In an embodiment, drying at least a portion of the PP and f-MWNT suspension can occur at a pressure of from about 50 mbar to about 1,013 mbar, alternatively from about 100 mbar to about 900 mbar, or alternatively from about 200 mbar to about 800 mbar.

[0055] In an embodiment, a method of making PP/f-MWNT can further comprise subjecting the PP/f-MWNT to grinding, crushing, milling, chopping, and the like, or combinations thereof, to form a PP/f-MWNT powder. As will be appreciated by one of skill in the art, and with the help of this disclosure, evaporating the solvent(s) from PP and f-MWNT suspension can produce rather non-uniform PP/f-MWNT particles (which can be clumped together), and as such these particles can be further converted to a powder of more uniform particle size, as might be desirable for further use of the PP/f-MWNT.

[0056] In an embodiment, the PP/f-MWNT powder is characterized by an average powder particle size of from about 10 µm to about 1 mm, alternatively from about 50 µm to about 750 µm, or alternatively from about 100 µm to about 500 µm.

[0057] The PP/f-MWNT comprises f-MWNT in an amount of from about 0.5 wt.% to about 80 wt.%, alternatively from about 1 wt.% to about 60 wt.%, or alternatively from about 10 wt.% to about 50 wt.%, based on the total weight of the PP/f-MWNT; and PP in an amount of from about 20 wt.% to about 99.5 wt.%, alternatively from about 40 wt.% to about 99 wt.%, or alternatively from about 50 wt.% to about 90 wt.%, based on the total weight of the PP/f-MWNT.

[0058] The PP coats the f-MWNT via non-covalent interactions, and the non-covalent interactions exclude hydrogen bonding. In some embodiments, the non-covalent interactions can comprise intermolecular CH-π interactions. Generally, non-covalent adsorption of electron-rich chemical compounds, such as compounds that are highly aromatic in nature, on the sidewall of CNT occurs most commonly through π-π interactions. However, non-covalent interactions can also occur between carbon-hydrogen groups and a π system, for example CH-π interactions (e.g., CH stretching, CH bending vibration, CH2 asymmetry bending vibration, CH3 asymmetry bending vibration, CH2 wagging, CH3 symmetry bending vibration, CH2 torsion motion, etc.), which can be identified through peak shifts in Fourier transform infrared spectroscopy (FTIR), as well as D band wavelength shifts in Raman spectroscopy. As will be appreciated by one of skill in the art, and with the help of this disclosure, CH-π interactions are relatively weak, are comparable to van der Waals forces, and have about one-tenth the strength of the hydrogen bond. Further, as will be appreciated by one of skill in the art, and with the help of this disclosure, CH-π interactions are characterized by a peak upshift in FTIR. Further, as will be appreciated by one of skill in the art, and with the help of this disclosure, CH-π interactions are characterized by a D band downshift in Raman spectroscopy.

[0059] In an embodiment, the PP can coat the f-MWNT via non-covalent interactions comprising intermolecular CH-π interactions, wherein the intermolecular CH-π interactions can be characterized by an upshift in the CH2 torsion motion, when compared to the CH2 torsion motion of the same PP used for coating the f-MWNT but in the absence of the f-MWNT; and wherein the upshift is an increase in the wavenumber of from about 4 cm-1 to about 10 cm-1, alternatively from about 4 cm-1 to about 9 cm-1, or alternatively from about 5 cm-1 to about 8 cm-1, as determined by FTIR.

[0060] In an embodiment, the PP can coat the f-MWNT via non-covalent interactions comprising intermolecular CH-π interactions, wherein the intermolecular CH-π interactions can be characterized by a downshift of D band, when compared to the D band of the same f-MWNT that have not been coated with PP; and wherein the downshift is a decrease in the wavenumber of from about 4 cm-1 to about 10 cm-1, alternatively from about 4 cm-1 to about 9 cm-1, or alternatively from about 5 cm-1 to about 8 cm-1, as determined by Raman spectroscopy. Without wishing to be limited by theory, when f-MWNT are coated by a polymer sheath (e.g., PP coating), strain is developed within the graphitic lattice of the MWNT that affects the vibration motion of the C-C bond due to the CH-π interactions, as suggested by the downshift in the D band.

[0061] In an embodiment, the f-MWNT of the PP/f-MWNT can have a diameter of from about 5 nm to about 200 nm, alternatively from about 10 nm to about 150 nm, or alternatively from about 20 nm to about 100 nm. As will be appreciated by one of skill in the art, and with the help of this disclosure, the dimensions (e.g., physical structure) of the f-MWNT are substantially the same as the dimensions of the p-MWNT, as the functionalization with nitric acid is performed under mild enough conditions to not alter the physical structure of the MWNT, while introducing carboxylic acid groups in the chemical structure.

[0062] In an embodiment, the f-MWNT of the PP/f-MWNT can have a length of from about 0.5 microns to about 1 mm, alternatively from about 1 micron to about 750 microns, or alternatively from about 5 microns to about 500 microns.

[0063] In an embodiment, the f-MWNT of the PP/f-MWNT can have from about 3 walls to about 100 walls, alternatively from about 5 walls to about 75 walls, or alternatively from about 8 walls to about 50 walls.

[0064] In an embodiment, the f-MWNT can comprise more carboxylic acid groups (-COOH) than the p-MWNT. Generally, the relative degree of functionalization of the MWNT can be estimated by Raman spectroscopy, for example by analyzing the intensity ratio of D-band (ID) at about 1300 cm-1 (due to disorder in the carbon lattice) to that of the G-band (IG) at about 1590 cm-1 (due to sp2 longitudinal vibration of graphitic structure) in the Raman spectra. As will be appreciated by one of skill in the art, and with the help of this disclosure, a higher Raman ID/IG ratio suggests a less perfect graphitic structure in the f-MWNT compared to that of p-MWNT due to the presence of -COOH groups on an f-MWNT side wall.

[0065] In an embodiment, the f-MWNT can be characterized by a ratio of intensity of D band to intensity of G band (ID/IG) that is increased by equal to or greater than about 20%, alternatively by equal to or greater than about 30%, or alternatively by equal to or greater than about 40%, when compared to an ID/IG for p-MWNT that have not been treated with nitric acid, as determined by Raman spectroscopy.

[0066] In an embodiment, the PP of the PP/f-MWNT can be isotactic, syndiotactic, atactic, or combinations thereof. Tacticity is a property of polymers comprising regular substituents (originating in the monomer(s) used for forming the polymer) on the polymer chain. When the substituents are arranged in an irregular, random fashion, the polymer is atactic. When the substituents are all on the same side of the chain, the polymer is isotactic. When the substituents alternate regularly from one side of the chain to the other, the polymer is syndiotactic. Isotactic and syndiotactic polymers are referred to as stereoregular, that is, polymers having an ordered arrangement of pendant groups along the chain. For example, in isotactic PP, all the methyl (-CH3) groups are arranged along the same side of the polymer chain. Generally, stereoregular polymers are usually high-strength materials owing to an uniform structure leading to close packing of the polymer chains, which can result in a high degree of crystallinity.

[0067] In an embodiment, the PP of the PP/f-MWNT can be characterized by an isotacticity of from about 0% to 100%, alternatively from about 90% to 100%, alternatively from about 95% to 100%, alternatively from about 96% to about 99%, or alternatively from about 92% to about 96%, as measured by 13C nuclear magnetic resonance (13C NMR) spectroscopy. For example, for high stiffness applications (e.g., pipe extrusion, injection molding, thin wall injection molding) the PP can be characterized by an isotacticity of from about 95% to 100%, or alternatively from about 96% to about 99%. As another example, for film applications, the PP can be characterized by an isotacticity of from about 92% to about 96%.

[0068] In an embodiment, the PP of the PP/f-MWNT can be characterized by a melt flow index (MFI) of from about 0.1 dg/min to about 250 dg/min, alternatively from about 0.1 dg/min to about 200 dg/min, alternatively from about 0.1 dg/min to about 1 dg/min, alternatively from about 1 dg/min to about 10 dg/min, or alternatively from about 10 dg/min to about 200 dg/min, as determined in accordance with ISO 1133 under a load of 2.16 kg. For example, for pipe extrusion applications the PP can be characterized by an MFI of from about 0.1 dg/min to about 1 dg/min; while for injection molding, the PP can be characterized by an MFI of from about 10 dg/min to about 200 dg/min.

[0069] In an embodiment, the PP of the PP/f-MWNT can be characterized by a molecular weight distribution (MWD) of from about 1 to about 10, alternatively from about 2 to about 8, alternatively from about 2 to about 4, or alternatively from about 4 to about 8, as determined in accordance with size exclusion chromatography/differential viscometry (SEC/DV). Generally, MWD, also known as polydispersity index, is a measure of the distribution of molecular mass in a given polymer sample. MWD can be calculated by dividing the weight average molecular weight by the number average molecular weight. As an example, for fibers applications the PP can be characterized by a MWD of from about 2 to about 4; while for injection molding, the PP can be characterized by a MWD of from about 4 to about 8.

[0070] In an embodiment, the PP/f-MWNT can have a PP coating thickness of from about 1 nm to about 10 nm, alternatively from about 1.5 nm to about 9.5 nm, or alternatively from about 2 nm to about 9 nm. In some embodiments, the PP coating can have an uniform thickness for a given discrete (e.g., individual) MWNT. In other embodiments, the PP coating can have a varying thickness for a given discrete MWNT.

[0071] In an embodiment, the PP coating can be characterized by a solubility in aromatic hydrocarbon solvents (e.g., second solvent) at 70 °C that is decreased by equal to or greater than about 25%, alternatively by equal to or greater than about 30%, or alternatively by equal to or greater than about 35%, when compared to a solubility in aromatic hydrocarbon solvents at 70 °C of the same PP used for coating the f-MWNT but in the absence of the f-MWNT. As will be appreciated by one of skill in the art, and with the help of this disclosure, due to the small size of the PP/f-MWNT, it would be expected that the PP coating would more soluble in aromatic hydrocarbon solvents, owing to an increase surface contact area between the PP coating of the PP/f-MWNT and the aromatic hydrocarbon solvent. Without wishing to be limited by theory, the non-covalent interactions (e.g., CH-π interactions) between the PP and the f-MWNT lead to an increased chemical stability of the PP coating (e.g., decrease the solubility of the PP in aromatic hydrocarbon solvents, increased thermal decomposition temperature, etc.). When comparing a property of the PP used for coating the f-MWNT but in the absence of the f-MWNT, a comparison is made between a quantification of a designated property of the PP polymer prior to being used as a coating on the f-MWNT (e.g., the PP prior to being placed in solution) and a quantification of the same property under the same testing conditions for the PP after the PP has been applied as a coating to the f-MWNT (e.g., the PP as present in the final PP/f-MWNT product), and such comparison may indicate a difference or change in the quantified property.

[0072] In an embodiment, the PP of the PP/f-MWNT can be characterized by a thermal decomposition temperature that is increased by equal to or greater than about 10 °C, alternatively equal to or greater than about 15 °C, or alternatively equal to or greater than about 20 °C when compared to a thermal decomposition temperature of the same PP used for coating the f-MWNT but in the absence of the f-MWNT, as determined by thermogravimetric analysis (TGA) under a nitrogen atmosphere. Generally, the thermal decomposition temperature of a substance is the temperature at which the substance chemically decomposes.

[0073] In an embodiment, the PP of the PP/f-MWNT can be characterized by a crystallization temperature that is increased by equal to or greater than about 2 °C, alternatively equal to or greater than about 3 °C, or alternatively equal to or greater than about 4 °C when compared to a crystallization temperature of the same PP used for coating the f-MWNT but in the absence of the f-MWNT, as determined by differential scanning calorimetry (DSC) thermal analysis in accordance with ASTM E794-06. Generally, the crystallization temperature of a polymer refers to the temperature at which polymer crystals form.

[0074] In an embodiment, the PP of the PP/f-MWNT can be characterized by a melting temperature that is increased by equal to or greater than about 1 °C, alternatively equal to or greater than about 2 °C, or alternatively equal to or greater than about 3 °C when compared to a melting temperature of the same PP used for coating the f-MWNT but in the absence of the f-MWNT, as determined by DSC thermal analysis in accordance with ASTM E794-06. Generally, the melting temperature of a polymer refers to a temperature where the polymer transition from a crystalline or semi-crystalline phase to a solid amorphous phase.

[0075] In an embodiment, the PP/f-MWNT can comprise discrete f-MWNT coated with PP (e.g., discrete PP/f-MWNT). For purposes of the disclosure herein, the term "discrete f-MWNT" refers to an individual f-MWNT (as opposed to two or more f-MWNT touching each other or adjacent to each other under a PP coating) that does not contact any other f-MWNT under a PP coating. In a discrete f-MWNT, no uncoated portion of a given f-MWNT is in direct contact with an uncoated portion of another f-MWNT. The PP/f-MWNT can comprise non-discrete f-MWNT coated with PP (non-discrete PP/f-MWNT), for example two or more f-MWNT touching each other or adjacent to each other under a PP coating (e.g., an uncoated portion of a given f-MWNT is in direct contact with an uncoated portion of another f-MWNT).

[0076] In an embodiment, the PP/f-MWNT can comprise equal to or greater than about 50 wt.%, alternatively equal to or greater than about 60 wt.%, or alternatively equal to or greater than about 75 wt.% discrete f-MWNT coated with PP (e.g., discrete PP/f-MWNT), based on the total weight of the f-MWNT. In an embodiment, a discrete PP/f-MWNT can have a diameter of from about 6 nm to about 210 nm, alternatively from about 15 nm to about 175 nm, or alternatively from about 25 nm to about 150 nm.

[0077] In an embodiment, PP/f-MWNT can be produced by a process comprising the steps of (a) contacting pristine multiwall carbon nanotubes (p-MWNT) with nitric acid to produce f-MWNT, wherein the p-MWNT are refluxed in nitric acid, and wherein the f-MWNT have a diameter of from about 10 nm to about 30 nm; (b) contacting at least a portion of the f-MWNT with butanol to form a f-MWNT suspension; (c) sonicating at least a portion of the f-MWNT suspension to form a f-MWNT dispersion; (d) contacting PP with xylene to form a PP solution, under agitating, stirring, magnetic stirring, and the like, or combinations thereof, and at a temperature of about 120 °C; (e) adding dropwise at least a portion of the PP solution to at least a portion of the f-MWNT dispersion under agitating, stirring, magnetic stirring, and the like, or combinations thereof, to form a PP and f-MWNT suspension; and (f) drying at least a portion of the PP and f-MWNT suspension under agitating, stirring, magnetic stirring, and the like, or combinations thereof; at a temperature of from about from about 40 °C to about 80 °C; and at a pressure of from about 50 mbar to about 1,013 mbar; to form the PP/f-MWNT. In such embodiment, the PP/f-MWNT can comprise f-MWNT and PP, wherein the PP coats the f-MWNT via non-covalent interactions, wherein the non-covalent interactions comprise intermolecular CH-π interactions, and wherein the non-covalent interactions exclude hydrogen bonding.

[0078] In an embodiment, PP/f-MWNT can comprise f-MWNT in an amount of from about 0.5 wt.% to about 10 wt.%, based on the total weight of the PP/f-MWNT, and PP in an amount of from about 90 wt.% to about 99.5 wt.%, based on the total weight of the PP/f-MWNT; wherein the PP coats the f-MWNT via non-covalent interactions; wherein the PP is characterized by an isotacticity of from about 90% to 100%; wherein the f-MWNT have a diameter of from about 5 nm to about 20 nm, a length of from about 0.5 microns to about 20 microns, and from about 5 walls to about 15 walls; and wherein a PP coating has thickness of from about 1 nm to about 10 nm. In an embodiment, the PP/f-MWNT can be used for modifying PP.

[0079] In an embodiment, the PP/f-MWNT comprising f-MWNT and PP, wherein the PP coats the f-MWNT via non-covalent interactions, and methods of making same, as disclosed herein can advantageously display improvements in one or more composition characteristics when compared to an otherwise similar composition comprising PP and MWNT, wherein the PP coats the MWNT via interactions other than non-covalent interactions.

[0080] In an embodiment, the PP/f-MWNT comprising f-MWNT and PP, wherein the PP coats the f-MWNT via non-covalent interactions, can advantageously display an increased thermal degradation temperature of the PP coating, when compared to a thermal degradation temperature of the same PP used for coating the f-MWNT but in the absence of the f-MWNT.

[0081] In an embodiment, the PP/f-MWNT comprising f-MWNT and PP, wherein the PP coats the f-MWNT via non-covalent interactions, can advantageously display increased solvent resistance (e.g., lower solubility) of the PP coating when compared to a solvent resistance of the same PP used for coating the f-MWNT but in the absence of the f-MWNT.

[0082] In an embodiment, the PP/f-MWNT comprising f-MWNT and PP, wherein the PP coats the f-MWNT via non-covalent interactions, can advantageously display both increased crystallization temperature and increased melting temperature of the PP coating, when compared to a crystallization temperature and a melting temperature, respectively, of the same PP used for coating the f-MWNT but in the absence of the f-MWNT.

[0083] In an embodiment, the PP/f-MWNT comprising f-MWNT and PP, wherein the PP coats the f-MWNT via non-covalent interactions, can advantageously allow for improved f-MWNT dispersion in PP-MWNT nanocomposites, when compared to dispersion of p-MWNT in otherwise similar PP-MWNT nanocomposites, as shown in Figure 18A vs. Figure 18C. In Figure 18A, a polymeric nanocomposite (0.1 wt.% f-MWNT) was prepared by micro-compounding PP with PP/f-MWNT. In Figure 18C, a polymeric nanocomposite (0.1 wt.% p-MWNT) was prepared by micro-compounding PP with p-MWNT. The former displayed better MWNT dispersion in the PP matrix. Additional advantages of the PP/f-MWNT comprising f-MWNT and PP, wherein the PP coats the f-MWNT via non-covalent interactions, and methods of making same, as disclosed herein can be apparent to one of skill in the art viewing this disclosure.

EXAMPLES



[0084] The subject matter having been generally described, the following examples are given as particular embodiments of the disclosure and to demonstrate the practice and advantages thereof. It is understood that the examples are given by way of illustration and are not intended to limit the specification of the claims to follow in any manner.

[0085] Materials. MWNT (SMW200) used in this study were obtained from SouthWest NanoTechnologies, Inc. (SWeNT), OK. Average number of walls (9 to 10) and average diameter (12 ± 3 nm) were determined from full width at half maximum (FWHM) of ∼25.8° integrated peak from wide angle X-ray diffraction (WAXD) and scanning electron microscopy (SEM), respectively. Impurity content in MWNT was about 2% as determined by thermogravimetric analysis (TGA) in air and a length of the tubes was about 4 µm according to the supplier. For functionalization and dispersion of MWNT, nitric acid (ACS reagent, 70% purchased from Sigma-Aldrich) and butanol (99.9 % purchased from Sigma-Aldrich) were used, respectively. Isotactic PP homopolymer (isotacticity: 97% and polydispersity index: 5) was provided by SABIC, Geleen, Netherlands. Maleic anhydride grafted PP (MA-g-PP) (Epolene E-43 polymer, Mw∼9100 g/mole, acid number of 45 mg KOH/g) was purchased from Westlake Chemical Corporation, TX. Xylene (99.9 % purchased from Sigma-Aldrich) was used as aromatic hydrocarbon solvent.

[0086] Characterization. Scanning electron microscopy (SEM) was performed on a Zeiss Ultra 60 FE-SEM at an accelerating voltage of 2 kV. Average diameter of p-MWNT and polymer coated MWNT was measured using ImageJ software from 40-50 measurements. For transmission electron microscopy (TEM) characterization, a few drops of f-MWNT/polymer solution mixture slurry were put on a holey carbon coated copper grid. TEM images were obtained using a probe corrected scanning/transmission electron microscope JEOL JEM-ARM200cF (JEOL, Ltd, Tokyo, Japan) operated at 80kV. WAXD was performed using a Rigaku MicroMax-002 beam generator (Cu Kα λ= 0.1542 nm, operating voltage and current 45 kV and 0.65 mA) equipped with R-axis IV++ detector. Raman spectra were collected using a HORIBA XploRA ONE (λ=785 nm) spectrometer. FTIR spectra of p-MWNT, f-MWNT, PP, MA-g-PP, and PP/f-MWNT mixed with potassium bromide (KBr) pellets were recorded using a PerkinElmer Spectrum One FTIR spectrometer with a resolution of 4 cm-1. Dynamic frequency sweep test was performed at 200 °C in the range of 0.1 to 500 rad/s using parallel-plate geometry (plate diameter 25 mm and the gap between the plates is 1 mm). For studying thermal degradation, TGA study was carried out at a heating rate of 10 °C/min under nitrogen using a TA Instrument Q500. For DSC study (using TA Instrument Q100), heating rate was 10 °C /min or 2.5 °C /min, and samples were heated from room temperature to 220 °C and then cooled and re-heated at the same rate. Crystallization temperature (Tc) and melt temperature (Tm) were derived from the 1st cooling cycle and the 2nd heating cycles, respectively, in accordance with ASTM E794-06. Crystallinity was calculated from enthalpy of melting assuming the enthalpy of melting for 100 % crystalline PP to be 207 J/g. Baselines for integration under crystallization and melting peaks were chosen in the range of 90 to 140 °C and 105 to 180 °C, respectively.

EXAMPLE 1



[0087] f-MWNT were prepared as follows. MWNT were functionalized using nitric acid. Pristine MWNT (p-MWNT) were homogenized in deionized water (DI water) for 20 min at 7000 rpm followed by sonication (Branson bath sonicator 3510R-MT, 100 W, 42 kHz) in 10 M nitric acid for 30 min. The mixture was refluxed at 120 °C (oil-bath temperature) for 24 hours and then repeatedly centrifuged and washed in deionized (DI) water until the pH value reached that of the DI water. The resulting f-MWNT suspension was filtered and washed using butanol followed by 48 hours of sonication at 5 mg/dl concentration, to produce a f-MWNT dispersion. Figures 1A and 1B summarize the MWNT functionalization, and PP/f-MWNT preparation: (a) p-MWNT was treated with 10 M HNO3 at 120 °C for 24 hours; and (b) f-MWNT was sonicated in butanol for 48 hours after which MA-g-PP/xylene or PP/xylene solution was added drop-by-drop into the f-MWNT/butanol dispersion at 60 °C followed by drying. For purposes of the disclosure herein, a MWNT that can be used for preparing polymer nanocomposites can also be referred to as "master batch," such as p-MWNT master batch, f-MWNT master batch, PP/f-MWNT master batch, MA-g-PP/f-MWNT master batch, etc.

[0088] Generally, carboxyl groups (-COOH) can be introduced on a carbon nanotube surface through nitric acid treatment to promote its solubility in polar solvents such as butanol. While increasing the treatment time, temperature, or other harsher reaction conditions can introduce more functional groups on MWNT, the nanotubes can also be fragmented or unzipped under such harsher treatment conditions. A relative degree of functionalization of the MWNT can be estimated via Raman spectroscopy, by the intensity ratio of D-band (ID) at ∼1300 cm-1 (due to disorder in the carbon lattice) to that of the G-band (IG) at ∼1590 cm-1 (due to sp2 longitudinal vibration of graphitic structure) in the Raman spectra (Fig. 2A). Table 1 displays ID/IG ratios from Raman spectra, crystal sizes derived from WAXD (002) integrated peak using Scherrer equation, and the corresponding number of MWNT walls assuming 0.34 nm interlayer separation.
Table 1
SampleID/IG (average of 5 different measurements)(002) Crystal size (nm)Number of walls
p-MWNT 1.69 ± 0.05 3.17 9.2
f-MWNT 2.32 ± 0.05 3.30 9.6


[0089] Higher Raman ID/IG ratio (Table 1) suggests a less perfect graphitic structure in f-MWNT compared to that of p-MWNT due to the presence of -COOH groups on f-MWNT side wall. The presence of carboxylic acid C=O (∼1700 cm-1) and OH stretch (∼2800-3000 cm-1) in f-MWNT also suggests the successful functionalization from nitric acid treatment, as I can be seen from the FTIR spectra in Fig. 3. Average number of walls in p-MWNT and f-MWNT were determined from the WAXD (002) FWHM using the Scherrer equation (Fig. 2B and Table 1) and the average number of walls in p-MWNT and f-MWNT were found to be the same within experimental error. This shows that the process of nitric acid treatment and the introduction of the functional groups in the current experiments have not destroyed even a single wall of the MWNT. Figs. 4A through 4H display TEM images of (a,b) p-MWNT, (c,d) f-MWNT; photographs of (e) f-MWNT/butanol, and (f) p-MWNT/butanol dispersions in vials after 48 hours of sonication; photographs of PP/f-MWNT (master batch) prepared (g) via gradual evaporation of solvents (xylene and butanol) and (h) via precipitation using methanol. A comparison of the TEM images of p-MWNT (Fig. 4A and B) to those of the f-MWNT (Fig. 4C and D) also confirms that there is no significant damage on MWNT sidewall upon nitric acid treatment under conditions used herein. Sonicated f-MWNT/butanol dispersions (at 5 mg/dl) were found to be very stable (there was no noticeable phase separation), when kept at room temperature over several months (Fig. 4E). By comparison, similarly sonicated p-MWNT/butanol system did not exhibit good dispersion (Fig. 4F).

EXAMPLE 2



[0090] PP/f-MWNT or MA-g-PP/f-MWNT were prepared from the f-MWNT of Example 1 as follows. PP and MA-g-PP master batches containing 5 wt.% f-MWNT were prepared in butanol/xylene solvent mixture. A f-MWNT/butanol dispersion (5 mg/dl) was heated to 60 °C while PP or MA-g-PP was dissolved in xylene at 120 °C (190 mg/dl) and added dropwise into the former with a final xylene to butanol ratio equaled to 1:2. The solution was dried at 60 °C under vacuum while stirring in the reactor to obtain PP/f-MWNT or MA-g-PP/f-MWNT master batches containing 5 wt. % f-MWNT. The two master batches were converted to powders using mortar and pestle.

[0091] Figs. 5A through 5F show SEM images of PP and MA-g-PP coated f-MWNT. Figs. 5A through 5F displays SEM images of MA-g-PP/f-MWNT and PP/f-MWNT master batches at various stages of solvent evaporation: (a) and (b) right after the mixing of polymer solution in f-MWNT dispersion (stage 1), (c) and (d) when 80% of the solvent had been removed by evaporation (stage 2), (e) and (f) when all solvent had been removed by evaporation (stage 3). Scale bar represents 30 nm in Figures 5A through 5F. The solvent evaporation refers to the timing of when the sample was removed from the reactor. As will be appreciated by one of skill in the art, and with the help of this disclosure, for SEM observation, ultimately all solvent was removed. However, after the sample removal from the reactor, the solvent removal was without any stirring. Thus, during stage 1 and stage 2, there was lower probability of polymer coating on the carbon nanotubes than during stage 3.

[0092] The average diameter of PP coated f-MWNT was 23 nm, and that of MA-g-PP coated f-MWNT was 26 nm, as displayed in Table 2.
Table 2
SampleDiameter (nm)
p-MWNT: 12 ±3
PP/f-MWNT master batch (stage1) 16 ± 6
PP/f-MWNT master batch (stage2) 19 ± 4
PP/f-MWNT master batch (stage3) 23 ± 5
MA-g-PP /f-MWNT master batch (stage1) 20 ± 3
MA-g-PP /f-MWNT master batch (stage2) 22 ± 4
MA-g-PP /f-MWNT master batch (stage3) 26 ± 6
Note: Various sample stages as defined for Figures 5A through 5F.
Table 3
SampleAverage Diameter (nm)
f-MWNT 15 ±3
PP/f-MWNT master batch 23 ± 5
PP/f-MWNT master batch washed with xylene at 70 °C 20 ± 3
PP/f-MWNT master batch washed with xylene at 120 °C 17 ± 4


[0093] Through SEM and TEM imaging, a 4 to 5 nm thick layer of PP and MA-g-PP polymer coating was observed on the MWNT sidewall in the two master batches. Based on a 15 nm diameter of the f-MWNT (Table 3), the average coating thickness was about 4 nm for PP and about 5 nm for MA-g-PP. This coating was achieved while the solvent was slowly evaporated at a controlled temperature while stirring. TEM images (Figs. 6A through 6D) also confirmed the presence of polymer coating on f-MWNT and showed that there was no gap between nanotubes and the polymer, and that f-MWNT were fully wetted and encapsulated by the two polymers, PP or MA-g-PP, used experimentally. Figs. 6A through 6D displays TEM images of (a,b) PP/f-MWNT and (c,d) MA-g-PP/f-MWNT master batches. Both PP and MA-g-PP form continuous coatings on f-MWNT, suggesting interaction between nanotubes and the polymers. There appears to be no gap between polymer and f-MWNT. Images (6A) and (6C) as well as the arrow in (6B) demonstrate the ability of polymer coating on separating adjacent MWNT.

[0094] The resulting PP/f-MWNT master batch was a black powder (Fig. 4G). In an alternative procedure, when polymer (PP or MA-g-PP)/f-MWNT/butanol/xylene system was precipitated by introducing methanol (rather than removing the solvent by slow evaporation), f-MWNT and the polymers were phase separated. This could be easily seen by white powder (polymer) and black particles (f-MWNT) (Fig. 4H). Such coagulation precipitation is one of the common solution-based approaches for preparing PP composites, however, the fast dissolution of CNT-PP precipitants cannot provide enough time for the development of a homogenous PP layer on CNT.

EXAMPLE 3



[0095] The stability of the interfacial polymer layer on polymer coated MWNT was investigated for both PP/f-MWNT and MA-g-PP/f-MWNT, which were prepared as described in Example 2.

[0096] Thermal stability of MWNT, PP/f-MWNT and MA-g-PP/f-MWNT was investigated by TGA in nitrogen (Figs. 7A and 7B, Fig. 8). The weight loss from 150 to 550 °C in the case of f-MWNT can be attributed to the loss of functional groups, and the loss of the nanotubes catalyzed by the loss of functional groups. Above 550 °C, combustion of f-MWNT can be facilitated by the defects generation through breaking of the carbon double bonds. PP and MA-g-PP powders samples (without nanotubes), that underwent similar solution preparation and drying process as the two master batches (e.g., PP/f-MWNT and MA-g-PP/f-MWNT) were used as the control samples for studying the thermal degradation behaviors of the two master batches. The degradation temperatures (Td) of the PP and MA-g-PP without nanotubes were at 331 and 341 °C, respectively (Fig. 7A and B). In the MA-g-PP/f-MWNT master batch, Td was 21 °C higher (at 362 °C) than that in MA-g-PP without nanotubes (Fig. 7A). Similarly, enhancement in Td was also observed in PP/f-MWNT master batch where a shoulder peak in the derivative plot was observed at 349 °C as compared to the peak degradation temperature of 331 °C for PP without nanotubes (Fig. 7B). Increase in thermal stability of polymer-CNT composite can be attributed to number of factors. Without wishing to be limited by theory, the barrier effect of CNT network in the nanocomposite can hinder the diffusion of the degradation products from the bulk polymer to the gas phase. Further, without wishing to be limited by theory, the interfacial interaction between CNT and polymer can restrict the thermal motion of macromolecules that increases the degradation activation energy. Further, without wishing to be limited by theory, CNT can demonstrate antioxidant effect due to their strong radical accepting ability that can decelerate the degradation process. Therefore, the enhanced Td of PP/f-MWNT and MA-g-PP/f-MWNT compared with the control samples can be attributed to the combined effect of well dispersed f-MWNT in the polymer matrix as well as to the interphase polymer layer on f-MWNT.

[0097] The polymer chain adsorbed onto the f-MWNT sidewalls also displayed enhanced chemical stability. While PP is fully soluble in xylene above 70 °C, the PP/f-MWNT master batch had lower solubility than the control PP under the same treatment conditions. After washing at 70 °C in xylene for two hours, dissolved polymer in the master batch was filtered. The remaining weight of the master batch was about 69% of the original weight, suggesting that 31% polymer dissolved. From scanning electron micrographs, it was determined that the average f-MWNT diameter of PP/f-MWNT after 70 °C xylene washing and filtering, decreased from 23 nm to 20 nm (Table 3). The remaining sample, after washing in xylene at 70 °C showed further increase in Td from 348 °C (before xylene treatment) to 380 °C (Figs. 9A and 9B). Figs. 9A and 9B display TGA under N2 of (a) PP/f-MWNT, and (b) MA-g-PP/f-MWNT master batches before and after xylene wash at 70 °C for two hours. Similarly, for MA-g-PP/f-MWNT master batch, about 57 % residual weight was observed after 70 °C xylene washing for two hours. After treatment in xylene, the peak degradation temperature did not change significantly (Figs. 9A and 9B). When the xylene washing temperature was increased to 120 °C, almost all PP in the PP/f-MWNT was washed away, and the average f-MWNT diameter decreased close to the value of the uncoated f-MWNT (Table 3).

[0098] Figs. 10A through 10D display SEM images of (a) f-MWNT, (b) PP/f-MWNT master batch, (c) PP/f-MWNT master batch washed in xylene at 70 °C, and (d) PP/f-MWNT master batch washed in xylene at 120 °C. The data in Figures 10A through 10D show that the polymer chains adsorbed on MWNT are not easily washed away. The data in Figures 10A through 10D further supports the idea of good interaction between the polymer and f-MWNT. Scale bar in Figures 10A through 10D represents 30 nm.

[0099] As compared to the control PP and MA-g-PP, the thermal degradation temperature of the two master batches was about 20 °C higher (under nitrogen atmosphere). After washing the PP/f-MWNT master batch in xylene at 70 °C, thermal degradation temperature of the remaining PP in this xylene washed sample was 50 °C higher than that of the control PP. The two master batches also exhibited better solvent resistance than the respective control polymers. These observations provide further evidence of interaction (e.g., non-covalent interaction) between the interfacial polymers and the f-MWNT.

EXAMPLE 4



[0100] The polymer coating interaction with the MWNT was investigated for both PP/f-MWNT and MA-g-PP/f-MWNT, which were prepared as described in Example 2. Evidence of CH-π interaction between PP and f-MWNT, MA-g-PP and MWNT, as well as hydrogen bonding between MA-g-PP and f-MWNT was obtained via FTIR spectroscopy.

[0101] Presence of CH-π interactions can be identified through peak shifts in FTIR. Examples of these include shifts corresponding to CH stretching (3266 cm-1 in acetylene) or CH bending (1450 cm-1 in polybutadiene) vibration. Fig. 11 shows FTIR spectra of PP/f-MWNT and MA-g-PP/MWNT master batches and FTIR spectra of the two control polymers (PP and MA-g-PP). While there is no change in resonance frequency of the CH2, CH3 asymmetry bending vibration (1460 cm-1, 1458 cm-1), and CH2 wagging/CH3 symmetry bending (1377 cm-1) vibration when either PP or MA-g-PP interact with the f-MWNT, a slight upshift (from 1256 to 1262 cm-1) in the CH2 torsion motion was observed in both cases (Fig. 11). This upshift indicates the presence of intermolecular CH-π interaction between f-MWNT and PP, as well as between f-MWNT and MA-g-PP. In addition, in MA-g-PP/f-MWNT, hydrogen bonding between anhydride group in MA-g-PP and carbonyl groups in f-MWNT was also observed through down shift in anhydride stretch from 1783 to 1774 cm-1 (Fig. 11). The CH-π interaction is relatively weak and is comparable to van der Waals forces, and it is about one-tenth the strength of the hydrogen bond. Without wishing to be limited by theory, it can be concluded that MA-g-PP interacts more strongly (via the formation of hydrogen as well as CH-π interaction) with f-MWNT than PP, which only displays CH-π interactions with f-MWNT. A thicker MA-g-PP coating was observed on f-MWNT than for PP, further demonstrating the difference of interaction between the two different polymers (PP and MA-g-PP) with f-MWNT (Table 2). Figure 12 displays FTIR spectra in the entire wave number range for PP, PP/f-MWNT master batch, MA-g-PP, and MA-g-PP/f-MWNT master batch.

[0102] Fig. 13 shows the Raman spectra of p-MWNT, f-MWNT, PP/f-MWNT and MA-g-PP/f-MWNT where a more pronounced peak shift is observed in D band rather than G and D* bands (Figs. 14A and 14B). Without wishing to be limited by theory, after functionalization, the upshift of D band from 1301 to 1313 cm-1 can be related to the direct electron charge transfer from the nanotube to acceptor carbonyl groups. When f-MWNT are encapsulated by the polymer sheath, strain can be developed within the graphitic lattice that can affect the vibration motion of C-C bond due to the CH-π interactions or hydrogen bonds. Further, without wishing to be limited by theory, a downshift of D band from 1313 to 1307 cm-1 in both PP/f-MWNT and MA-g-PP/f-MWNT master batches suggests a strain induced in the f-MWNT (Fig. 13). Similarly, downshift of both D and G bands in CNT have been previously reported due to the stretching and weakening of carbon-carbon (C-C) bond in CNT during tensile deformation or uniaxial bending. Interestingly, although MA-g-PP interacts more strongly with f-MWNT through hydrogen bonds and CH-π interaction compared with PP where only CH-π interaction exists, the D band resonance frequency exhibits the same shift of 6 cm-1 in f-MWNT coated with either PP or MA-g-PP.

EXAMPLE 5



[0103] The dispersion of the f-MWNT in the polymer coated f-MWNT was investigated for both PP/f-MWNT and MA-g-PP/f-MWNT, which were prepared as described in Example 2.

[0104] The f-MWNT dispersion in both PP and MA-g-PP based master batches was investigated under molten state using optical microscopy (Figs. 15A and 15B). Figures 15A and 15B display optical micrographs of (a) PP/f-MWNT, and (b) MA-g-PP/f-MWNT master batches, wherein the scale bar represents 100 µm. As compared to PP/f-MWNT master batch, MA-g-PP/f-MWNT master batch exhibits greater homogeneity (Fig 15A and B) in terms of f-MWNT dispersion in the polymer matrix. Dark regions in PP/f-MWNT master batch in Fig. 15A are regions with high f-MWNT concentration.

EXAMPLE 6



[0105] The melting and crystallization behavior of the f-MWNT in the polymer coated f-MWNT was investigated for both PP/f-MWNT and MA-g-PP/f-MWNT, which were prepared as described in Example 2.

[0106] Table 4 displays differential scanning calorimetry (DSC) melting and crystallization data of the PP/f-MWNT and MA-g-PP/f-MWNT master batches along with the respective control samples, for 10 °C/min ramping rate.
Table 4
SampleTo1 (°C)Tc(°C)FWHM of Tc peakTm (°C)Crystallinity (%)
MA-g-PP 119.2 115.5 5.4 147/155 --2
MA-g-PP/f-MWNT master batch 120.5 117.5 4.9 146/154 --2
PP 123.6 119.0 5.7 160 51
PP/f-MWNT master batch 125.0 123.0 3.4 162 48
Notes: 1 - onset of crystallization temperature (To), Crystallization temperature (Tc), and melting temperature (Tm); 2 - Enthalpy of melting for 100% crystalline MA-g-PP was not available.


[0107] To ensure comparable control samples for the DSC experiments, PP and MA-g-PP samples were dissolved in xylene and then xylene was evaporated by vacuum drying. The vacuum dried polymer samples were grounded using mortar and pestle. WAXD shows only α-form crystal in both PP/f-MWNT and MA-g-PP/f-MWNT master batches (Fig. 16). Addition of f-MWNT resulted in increased crystallization temperature (Tc) and decreased FWHM of the crystallization peak as compared to that of the unfilled polymer in both PP and MA-g-PP systems. Increased crystallization temperature suggests enhanced nucleation rate while a decreased FWHM of the crystallization peak suggests narrower crystal size distribution. The effect is more evident in PP/f-MWNT where a 4 °C increase of Tc was observed as compared to a 2 °C increase in MA-g-PP/f-MWNT, when compared to their respective control samples (Fig. 17A and B, Table 4).

[0108] In the case of PP master batch, Tm shifted from 160 to 162 °C (Table 4), suggesting higher crystal perfection and/or larger crystals in PP/f-MWNT containing nanocomposite than in the control. Double melting endotherm peak is observed in the MA-g-PP based samples (Fig. 17C). Smaller and imperfect crystals melt at lower temperature, and then recrystallize into more perfect and/or larger crystals upon further heating. These more perfect or larger crystals melt at higher temperature and contribute to the double melting peaks in the DSC curve (Fig 17C).

[0109] A more pronounced enhancement of both the crystallization (Tc) and melting (Tm) temperatures as compared to the respective control samples was observed in the PP/f-MWNT master batch, as compared to the Tc and Tm enhancement for the MA-g-PP/f-MWNT master batch, although f-MWNT dispersion was better in the latter case.

[0110] For the purpose of any U.S. national stage filing from this application, all publications and patents mentioned in this disclosure are incorporated herein by reference in their entireties, for the purpose of describing and disclosing the constructs and methodologies described in those publications, which might be used in connection with the methods of this disclosure. Any publications and patents discussed herein are provided solely for their disclosure prior to the filing date of the present application. Nothing herein is to be construed as an admission that the inventors are not entitled to antedate such disclosure by virtue of prior invention.

[0111] In any application before the United States Patent and Trademark Office, the Abstract of this application is provided for the purpose of satisfying the requirements of 37 C.F.R. § 1.72 and the purpose stated in 37 C.F.R. § 1.72(b) "to enable the United States Patent and Trademark Office and the public generally to determine quickly from a cursory inspection the nature and gist of the technical disclosure." Therefore, the Abstract of this application is not intended to be used to construe the scope of the claims or to limit the scope of the subject matter that is disclosed herein. Moreover, any headings that can be employed herein are also not intended to be used to construe the scope of the claims or to limit the scope of the subject matter that is disclosed herein. Any use of the past tense to describe an example otherwise indicated as constructive or prophetic is not intended to reflect that the constructive or prophetic example has actually been carried out.

[0112] The present disclosure is illustrated by the above examples, which are not to be construed in any way as imposing limitations upon the scope thereof. On the contrary, it is to be clearly understood that resort can be had to various other aspects, embodiments, and modifications thereof which, after reading the description herein, can be suggest to one of ordinary skill in the art without departing from the scope of the appended claims.

[0113] While embodiments of the disclosure have been shown and described, modifications thereof can be made without departing from the teachings of the invention. The embodiments and examples described herein are exemplary only, and are not intended to be limiting. Many variations and modifications of the invention disclosed herein are possible and are within the scope of the invention.


Claims

1. A method of making polypropylene-coated functionalized multiwall carbon nanotubes (PP/f-MWNT), the method comprising:

(a) contacting pristine multiwall carbon nanotubes (p-MWNT) with nitric acid to produce functionalized multiwall carbon nanotubes (f-MWNT) comprising carboxylic acid groups;

(b) contacting at least a portion of the f-MWNT with a first solvent to form a f-MWNT comprising carboxylic acid groups dispersion;

(c) contacting polypropylene (PP) with a second solvent to form a PP solution;

(d) contacting at least a portion of the f-MWNT comprising carboxylic acid groups dispersion with at least a portion of the PP solution to form a PP and f-MWNT comprising carboxylic acid groups suspension; and

(e) drying at least a portion of the PP and f-MWNT comprising carboxylic acid groups suspension to form the PP/f-MWNT comprising carboxylic acid groups.


 
2. The method of claim 1, wherein the step (a) of contacting p-MWNT with nitric acid comprises (i) contacting at least a portion of the p-MWNT with water and nitric acid to form a p-MWNT acidic suspension; and (ii) dispersing at least a portion of the p-MWNT acidic suspension to form a p-MWNT acidic dispersion.
 
3. The method of claim 2 further comprising (iii) refluxing at least a portion of the p-MWNT acidic dispersion at a temperature of from 100 °C to 140 °C, and for a time period of from 2 hours to 48 hours, to produce the f-MWNT comprising carboxylic acid groups.
 
4. The method of any one of claims 1 to 3, wherein the step (b) of contacting at least a portion of the f-MWNT with a first solvent comprises (i) washing at least a portion of the f-MWNT comprising carboxylic acid groups with water to produce water washed f-MWNT comprising carboxylic acid groups; (ii) washing at least a portion of the water washed f-MWNT with the first solvent to produce first solvent washed f-MWNT comprising carboxylic acid groups; and (iii) contacting at least a portion of the first solvent washed f-MWNT comprising carboxylic acid groups with the first solvent to form a f-MWNT comprising carboxylic acid groups suspension.
 
5. The method of claim 4, wherein the step (b) of contacting at least a portion of the f-MWNT comprising carboxylic acid groups with a first solvent further comprises (iv) dispersing at least a portion of the f-MWNT comprising carboxylic acid groups suspension to form the f-MWNT comprising carboxylic acid groups dispersion.
 
6. The method of any one of claims 1 to 5, wherein the first solvent comprises a polar solvent, an alcohol, methanol, ethanol, propanol, isopropanol, butanol, pentanol, a mild acid, acetic acid, lactic acid, oxalic acid, formic acid, succinic acid, acetone, or combinations thereof; and wherein the second solvent comprises an aromatic hydrocarbon solvent, xylene, o-xylene, m-xylene, p-xylene, ethylbenzene, toluene, tetralin, chlorobenzene, cycloalkanes, cyclohexane, decalin, or combinations thereof.
 
7. The method of any one of claims 1 to 6, wherein the f-MWNT comprising carboxylic acid groups dispersion has a concentration of f-MWNT comprising carboxylic acid groups in the first solvent of from 5 mg/liter to 100 mg/liter, based on the volume of the first solvent; wherein the PP solution has a concentration of PP in the second solvent of from 0.5 g/liter to 5 g/liter, based on the volume of the second solvent; and wherein the PP and f-MWNT comprising carboxylic acid groups suspension has a volumetric ratio of the second solvent to the first solvent of from 1:1 to 1:5, and a weight ratio of f-MWNT comprising carboxylic acid groups to PP of from 0.5:99.5 to 80:20.
 
8. The method of any one of claims 1 to 7, wherein the step (c) of contacting PP with a second solvent comprises heating the PP in the second solvent to a temperature in a range of from 80 °C to 130 °C under agitating, stirring, magnetic stirring, or combinations thereof.
 
9. The method of any one of claims 1 to 8, wherein the step (d) of contacting the f-MWNT comprising carboxylic acid groups dispersion with the PP solution comprises (i) heating the f-MWNT comprising carboxylic acid groups dispersion to a first temperature; (ii) adding the PP solution to the f-MWNT comprising carboxylic acid groups dispersion to form the PP and f-MWNT comprising carboxylic acid groups suspension, wherein the PP solution is characterized by a second temperature, and wherein the first temperature is lower than the second temperature.
 
10. The method of any one of claims 1 to 9, wherein the step (e) of drying the PP and f-MWNT comprising carboxylic acid groups suspension occurs under agitating, stirring, magnetic stirring, or combinations thereof; at a temperature of from 40 °C to 80 °C; and at a pressure of from 50 mbar to 1,013 mbar.
 
11. Polypropylene-coated functionalized multiwall carbon nanotubes (PP/f-MWNT) comprising functionalized multiwall carbon nanotubes (f-MWNT) in an amount of from 0.5 wt.% to 80 wt.%, based on the total weight of the PP/f-MWNT; and polypropylene (PP) in an amount of from 20 wt.% to 99.5 wt.%, based on the total weight of the PP/f-MWNT, wherein the PP coats the f-MWNT via non-covalent interactions, and wherein the non-covalent interactions exclude hydrogen bonding.
 
12. The PP/f-MWNT of claim 11, wherein the non-covalent interactions comprise intermolecular CH-π interactions, and optionally.
the intermolecular CH-π interactions are characterized by an upshift in CH2 torsion motion, when compared to the CH2 torsion motion of the same PP used for coating the f-MWNT but in the absence of the f-MWNT; and wherein the upshift is an increase in the wavenumber of from 4 cm-1 to 10 cm-1, as determined by Fourier transform infrared spectroscopy (FTIR); and
wherein the intermolecular CH-π interactions are characterized by a downshift of D band, when compared to the D band of the same f-MWNT that have not been coated with PP; and wherein the downshift is a decrease in the wavenumber of from 4 cm-1 to 10 cm-1, as determined by Raman spectroscopy.
 
13. The PP/f-MWNT of any one of claims 11 to 12, wherein the f-MWNT have a diameter of from 5 nm to 200 nm; a length of from 0.5 microns to 1 mm; and from 3 walls to 100 walls.
 
14. The PP/f-MWNT of any one of claims 11 to 13, wherein the PP of the PP/f-MWNT is characterized by a thermal decomposition temperature that is increased by equal to or greater than about 10 °C when compared to a thermal decomposition temperature of the same PP used for coating the f-MWNT but in the absence of the f-MWNT, as determined by thermogravimetric analysis (TGA) under a nitrogen atmosphere;
wherein the PP of the PP/f-MWNT is characterized by a crystallization temperature that is increased by equal to or greater than 2 °C when compared to a crystallization temperature of the same PP used for coating the f-MWNT but in the absence of the f-MWNT, as determined by differential scanning calorimetry (DSC) thermal analysis in accordance with ASTM E794-06; and
wherein the PP of the PP/f-MWNT is characterized by a melting temperature that is increased by equal to or greater than about 1 °C when compared to a melting temperature of the same PP used for coating the f-MWNT but in the absence of the f-MWNT, as determined by differential scanning calorimetry (DSC) thermal analysis in accordance with ASTM E794-06.
 
15. The PP/f-MWNT of any one of claims 11 to 14, wherein the PP/f-MWNT comprise equal to or greater than 50 wt.% discrete f-MWNT coated with PP (discrete PP/f-MWNT), based on the total weight of the f-MWNT; and wherein the discrete PP/f-MWNT have a diameter of from 6 nm to 210 nm.
 


Ansprüche

1. Verfahren zur Herstellung von Polypropylen-beschichteten funktionalisierten mehrwandigen Kohlenstoff-Nanoröhren (PP/f-MWNT), wobei das Verfahren umfasst:

(a) In-Kontakt-Bringen von unberührten mehrwandigen Kohlenstoff-Nanoröhren (p-MWNT) mit Salpetersäure, um funktionalisierte mehrwandige Kohlenstoff-Nanoröhren (f-MWNT), die Carbonsäuregruppen umfassen, herzustellen;

(b) In-Kontakt-Bringen wenigstens eines Teils der f-MWNT mit einem ersten Lösungsmittel, um eine Dispersion von Carbonsäuregruppen umfassendem f-MWNT zu bilden;

(c) In-Kontakt-Bringen von Polypropylen (PP) mit einem zweiten Lösungsmittel, um eine PP-Lösung zu bilden;

(d) In-Kontakt-Bringen wenigstens eines Teils der Dispersion von Carbonsäuregruppen umfassendem f-MWNT mit wenigstens einem Teil der PP-Lösung, um eine Suspension von PP und Carbonsäuregruppen umfassendem f-MWNT zu bilden; und

(e) Trockenen wenigstens eines Teils der Suspension von PP und Carbonsäuregruppen umfassendem f-MWNT, um das PP/Carbonsäuregruppen umfassende f-MWNT zu bilden.


 
2. Verfahren nach Anspruch 1, wobei der Schritt (a) eines In-Kontakt-Bringens von p-MWNT mit Salpetersäure (i) In-Kontakt-Bringen wenigstens eines Teils des p-MWNT mit Wasser und Salpetersäure umfasst, um eine saure p-MWNT-Suspension zu bilden; und (ii) Dispergieren wenigstens eines Teils der sauren p-MWNT-Suspension, um eine saure p-MWNT-Dispersion zu bilden.
 
3. Verfahren nach Anspruch 2, weiterhin umfassend (iii) Refluxieren wenigstens eines Teils der sauren p-MWNT-Dispersion bei einer Temperatur von 100 °C bis 140 °C und für eine Zeitdauer von 12 Stunden bis 48 Stunden, um das Carbonsäuregruppen umfassende f-MWNT herzustellen.
 
4. Verfahren nach irgendeinem der Ansprüche 1 bis 3, wobei der Schritt (b) eines In-Kontakt-Bringens wenigstens eines Teils des f-MWNT mit einem ersten Lösungsmittel umfasst (i) Waschen wenigstens eines Teils des Carbonsäuregruppen umfassenden f-MWNT mit Wasser, um mit Wasser gewaschenes, Carbonsäuregruppen umfassendes f-MWNT herzustellen; (ii) Waschen wenigstens eines Teils des mit Wasser gewaschenen f-MWNT mit dem ersten Lösungsmittel, um ein mit dem ersten Lösungsmittel gewaschenes, Carbonsäuregruppen umfassendes f-MWNT herzustellen; und (iii) In-Kontakt-Bringen wenigstens eines Teils des mit dem ersten Lösungsmittel gewaschenen, Carbonsäuregruppen umfassenden f-MWNT mit dem ersten Lösungsmittel, um eine Suspension von Carbonsäuregruppen umfassendem f-MWNT zu bilden.
 
5. Verfahren nach Anspruch 4, wobei der Schritt (b) eines In-Kontakt-Bringens wenigstens eines Teils des Carbonsäuregruppen umfassenden f-MWNT mit einem ersten Lösungsmittel weiterhin umfasst (iv) Dispergieren wenigstens eines Teils der Suspension von Carbonsäuregruppen umfassendem f-MWNT, um die Dispersion von Carbonsäuregruppen umfassendem f-MWNT zu bilden.
 
6. Verfahren nach irgendeinem der Ansprüche 1 bis 5, wobei das erste Lösungsmittel ein polares Lösungsmittel, einen Alkohol, Methanol, Ethanol, Propanol, Isopropanol, Butanol, Pentanol, eine milde Säure, Essigsäure, Milchsäure, Oxalsäure, Ameisensäure, Bernsteinsäure, Aceton oder Kombinationen davon umfasst; und wobei das zweite Lösungsmittel ein aromatisches Kohlenwasserstofflösungsmittel, Xylol, o-Xylol, m-Xylol, p-Xylol, Ethylbenzol, Toluol, Tetralin, Chlorbenzol, Cycloalkane, Cyclohexan, Decalin oder Kombinationen davon umfasst.
 
7. Verfahren nach irgendeinem der Ansprüche 1 bis 6, wobei die Dispersion von Carbonsäuregruppen umfassendem f-MWNT eine Konzentration an Carbonsäuregruppen umfassendem f-MWNT in dem ersten Lösungsmittel von 5 mg/Liter bis 100 mg/Liter aufweist, bezogen auf das Volumen des ersten Lösungsmittels; wobei die PP-Lösung eine Konzentration an PP in dem zweiten Lösungsmittel von 0,5 g/Liter bis 5 g/Liter aufweist, bezogen auf das Volumen des zweiten Lösungsmittels; und wobei die Suspension von PP und Carbonsäuregruppen umfassendem f-MWNT ein volumetrisches Verhältnis des zweiten Lösungsmittels zu dem ersten Lösungsmittel von 1:1 bis 1:5 und ein Gewichtsverhältnis von Carbonsäuregruppen umfassendem f-MWNT zu PP von 0,5:99,5 bis 80:20 aufweist.
 
8. Verfahren nach irgendeinem der Ansprüche 1 bis 7, wobei der Schritt (c) eines In-Kontakt-Bringens von PP mit einen zweiten Lösungsmittel Erwärmen des PP in dem zweiten Lösungsmittel auf eine Temperatur in einem Bereich von 80 °C bis 130 °C unter Bewegen, Rühren, Magnetrühren oder Kombinationen davon umfasst.
 
9. Verfahren nach irgendeinem der Ansprüche 1 bis 8, wobei der Schritt (d) eines In-Kontakt-Bringens der Dispersion von Carbonsäuregruppen umfassendem f-MWNT mit der PP-Lösung umfasst (i) Erwärmen der Dispersion von Carbonsäuregruppen umfassendem f-MWNT auf eine erste Temperatur; (ii) Hinzufügen der PP-Lösung zu der Dispersion von Carbonsäuregruppen umfassendem f-MWNT, um die Suspension von PP und Carbonsäuregruppen umfassendem f-MWNT zu bilden, wobei die PP-Lösung durch eine zweite Temperatur gekennzeichnet ist, und wobei die erste Temperatur niedriger als die zweite Temperatur liegt.
 
10. Verfahren nach irgendeinem der Ansprüche 1 bis 9, wobei der Schritt (e) eines Trocknens der Suspension von PP und Carbonsäuregruppen umfassendem f-MWNT unter Bewegen, Rühren, Magnetrühren oder Kombinationen davon erfolgt; bei einer Temperatur von 40 °C bis 80 °C; und bei einem Druck von 50 mbar bis 1,013 mbar.
 
11. Polypropylen-beschichtete funktionalisierte mehrwandige Kohlenstoff-Nanoröhren (PP/f-MWNT), umfassend funktionalisierte mehrwandige Kohlenstoff-Nanoröhren (f-MWNT) in einer Menge von 0,5 Gew.-% bis 80 Gew.-%, bezogen auf das Gesamtgewicht des PP/f-MWNT; und Polypropylen (PP) in einer Menge von 20 Gew.-% bis 99,5 Gew.-%, bezogen auf das Gesamtgewicht des PP/f-MWNT, wobei das PP das f-MWNT über nicht-kovalente Wechselwirkungen beschichtet, und wobei die nicht-kovalenten Wechselwirkungen Wasserstoffbindung bzw. Wasserstoffbrückenbindung ausschließen.
 
12. PP/f-MWNT nach Anspruch 11, wobei die nicht-kovalenten Wechselwirkungen intermolekulare CH-π-Wechselwirkungen umfassen, und gegebenenfalls die intermolekularen CH-π-Wechselwirkungen durch einen Upshift in der CH2-Torsionsbewegung gekennzeichnet sind, im Vergleich zu der CH2-Torsionsbewegung des gleichen PP, das zum Beschichten des f-MWNT verwendet wurde, jedoch in Abwesenheit des f-MWNT; und wobei der Upshift eine Zunahme in der Wellenzahl von 4 cm-1 bis 10 cm-1 ist, wie durch Fourier-Transformations-Infrarot-Spektroskopie (FTIR) bestimmt; und wobei die intermolekularen CH-π-Wechselwirkungen durch einen Downshift der D-Bande im Vergleich zu der D-Bande des gleichen f-MWNT, das nicht mit PP beschichtet worden ist, gekennzeichnet sind; und wobei der Downshift eine Abnahme in der Wellenzahl von 4 cm-1 bis 10 cm-1 ist, wie durch Raman-Spektroskopie bestimmt.
 
13. PP/f-MWNT nach irgendeinem der Ansprüche 11 bis 12, wobei die f-MWNT einen Durchmesser von 5 nm bis 200 nm; eine Länge von 0,5 Mikron bis 1 mm; und von 3 Wänden bis 100 Wänden haben.
 
14. PP/f-MWNT nach irgendeinem der Ansprüche 11 bis 13, wobei das PP des PP/f-MWNT durch eine thermische Zersetzungstemperatur gekennzeichnet ist, die um gleich oder größer als etwa 10 °C erhöht ist, im Vergleich zu einer thermischen Zersetzungstemperatur des gleichen PP, das zum Beschichten des f-MWNT verwendet wurde, jedoch in Abwesenheit des f-MWNT, wie durch thermogravimetrische Analyse (TGA) unter einer Stickstoffatmosphäre bestimmt;
wobei das PP des PP/f-MWNT durch eine Kristallisationstemperatur gekennzeichnet ist, die um gleich oder größer als 2 °C erhöht ist, im Vergleich zu einer Kristallisationstemperatur des gleichen PP, das zum Beschichten des f-MWNT verwendet wurde, jedoch in Abwesenheit des f-MWNT, wie durch dynamische Differenzkalorimetrie bzw. Differential Scanning Calorimetry (DSC)-Thermoanalyse gemäß ASTM E794-06 bestimmt; und
wobei das PP des PP/f-MWNT durch eine Schmelztemperatur gekennzeichnet ist, die um gleich oder größer als etwa 1 °C erhöht ist, im Vergleich zu einer Schmelztemperatur des gleichen PP, das zum Beschichten des f-MWNT verwendet wurde, jedoch in Abwesenheit des f-MWNT, wie durch dynamische Differenzkalorimetrie bzw. Differential Scanning Calorimetry (DSC)-Thermoanalyse gemäß ASTM E794-06 bestimmt.
 
15. PP/f-MWNT nach irgendeinem der Ansprüche 11 bis 14, wobei das PP/f-MWNT gleich oder größer als 50 Gew .-% diskretes f-MWNT umfasst, das mit PP (diskretes PP/f-MWNT) beschichtet ist, bezogen auf das Gesamtgewicht des f-MWNT; und wobei das diskrete PP/f-MWNT einen Durchmesser von 6 nm bis 210 nm aufweist.
 


Revendications

1. Procédé de fabrication de nanotubes de carbone multifeuillets fonctionnalisés revêtus de polypropylène (PP/f-MWNT), le procédé comprenant :

(a) la mise en contact de nanotubes de carbone multifeuillets vierges (p-MWNT) avec de l'acide nitrique pour produire des nanotubes de carbone multifeuillets fonctionnalisés (f-MWNT) comprenant des groupes acide carboxylique ;

(b) la mise en contact d'au moins une portion des f-MWNT avec un premier solvant pour former un f-MWNT comprenant une dispersion de groupes acide carboxylique ;

(c) la mise en contact de polypropylène (PP) avec un deuxième solvant pour former une solution de PP ;

(d) la mise en contact d'au moins une portion des f-MWNT comprenant la dispersion de groupes acide carboxylique avec au moins une portion de la solution de PP pour former un PP et un f-MWNT comprenant une suspension de groupes acide carboxylique ; et

(e) le séchage d'au moins une portion du PP et du f-MWNT comprenant la suspension de groupes acide carboxylique pour former le PP/f-MWNT comprenant des groupes acide carboxylique.


 
2. Procédé selon la revendication 1, dans lequel l'étape (a) de mise en contact du p-MWNT avec l'acide nitrique comprend (i) la mise en contact d'au moins une portion du p-MWNT avec de l'eau et de l'acide nitrique pour former une suspension acide de p-MWNT ; et (ii) la dispersion d'au moins une portion de la suspension acide de p-MWNT pour former une dispersion acide de p-MWNT.
 
3. Procédé selon la revendication 2, comprenant en outre (iii) le reflux d'au moins une portion de la dispersion acide de p-MWNT à une température de 100 °C à 140 °C, pendant un laps de temps de 2 heures à 48 heures, pour produire le f-MWNT comprenant des groupes acide carboxylique.
 
4. Procédé selon l'une quelconque des revendications 1 à 3, dans lequel l'étape (b) de mise en contact d'au moins une portion du f-MWNT avec un premier solvant comprend (i) le lavage d'au moins une portion du f-MWNT comprenant des groupes acide carboxylique avec de l'eau pour produire un f-MWNT lavé à l'eau et comprenant des groupes acide carboxylique ; (ii) le lavage d'au moins une portion du f-MWNT lavé à l'eau avec le premier solvant pour produire un premier f-MWNT lavé au solvant, comprenant des groupes acide carboxylique ; et (iii) la mise en contact d'au moins une portion du premier f-MWNT lavé au solvant, comprenant des groupes acide carboxylique, avec le premier solvant pour former un f-MWNT comprenant une suspension de groupes acide carboxylique.
 
5. Procédé selon la revendication 4, dans lequel l'étape (b) de mise en contact d'au moins une portion du f-MWNT comprenant des groupes acide carboxylique avec un premier solvant comprend en outre (iv) la dispersion d'au moins une portion du f-MWNT comprenant une suspension de groupes acide carboxylique pour former le f-MWNT comprenant une dispersion de groupes acide carboxylique.
 
6. Procédé selon l'une quelconque des revendications 1 à 5, dans lequel le premier solvant comprend un solvant polaire, un alcool, le méthanol, l'éthanol, le propanol, l'isopropanol, le butanol, le pentanol, un acide faible, l'acide acétique, l'acide lactique, l'acide oxalique, l'acide formique, l'acide succinique, de l'acétone, ou des combinaisons de ceux-ci ; et dans lequel le deuxième solvant comprend un solvant hydrocarbure aromatique, le xylène, l'o-xylène, le m-xylène, le p-xylène, l'éthylbenzène, le toluène, la tétraline, le chlorobenzène, des cycloalcanes, le cyclohexane, de la décaline, ou des combinaisons de ceux-ci.
 
7. Procédé selon l'une quelconque des revendications 1 à 6, dans lequel le f-MWNT comprenant une dispersion de groupes acide carboxylique a une concentration de f-MWNT comprenant des groupes acide carboxylique dans le premier solvant de 5 mg/litre à 100 mg/litre, rapportée au volume du premier solvant ; dans lequel la solution de PP a une concentration de PP dans le deuxième solvant de 0,5 g/litre à 5 g/litre, rapportée au volume du deuxième solvant ; et dans lequel le PP et le f-MWNT comprenant une suspension de groupes acide carboxylique présentent un rapport en volume du deuxième solvant au premier solvant de 1:1 à 1:5, et un rapport en poids du f-MWNT comprenant des groupes acide carboxylique au PP de 0,5:99,5 à 80:20.
 
8. Procédé selon l'une quelconque des revendications 1 à 7, dans lequel l'étape (c) de mise en contact du PP avec un deuxième solvant comprend le chauffage du PP dans le deuxième solvant à une température comprise dans la plage de 80 °C à 130 °C, sous agitation, agitation mécanique, agitation magnétique, ou des combinaisons de ces techniques.
 
9. Procédé selon l'une quelconque des revendications 1 à 8, dans lequel l'étape (d) de mise en contact du f-MWNT comprenant une dispersion de groupes acide carboxylique avec la solution de PP comprend (i) le chauffage du f-MWNT comprenant une dispersion de groupes acide carboxylique à une première température ; (ii) l'ajout de la solution de PP au f-MWNT comprenant une dispersion de groupes acide carboxylique pour former le PP et le f-MWNT comprenant une suspension de groupes acide carboxylique, la solution de PP étant caractérisée par une deuxième température, et la première température étant inférieure à la deuxième température.
 
10. Procédé selon l'une quelconque des revendications 1 à 9, dans lequel l'étape (c) de séchage du PP et du f-MWNT comprenant une suspension de groupes acide carboxylique a lieu sous agitation, agitation mécanique, agitation magnétique ou par des combinaisons de ces techniques ; à une température de 40 °C à 80 °C ; et sous une pression de 50 mbar à 1013 mbar.
 
11. Nanotubes de carbone multifeuillets fonctionnalisés revêtus de polypropylène (PP/f-MWNT) comprenant des nanotubes de carbone multifeuillets fonctionnalisés (f-MWNT) en une quantité de 0,5 % en poids à 80 % en poids, rapportée au poids total du PP/f-MWNT ; et du polypropylène (PP) en une quantité de 20 % en poids à 99,5 % en poids, rapportée au poids total du PP/f-MWNT, le PP revêtant le f-MWNT par des interactions non covalentes, et les interactions non covalentes excluant une liaison hydrogène.
 
12. PP/f-MWNT selon la revendication 11, dans lequel les interactions non covalentes comprennent des interactions CHπ intermoléculaires, et en option les interactions CHπ intermoléculaires sont caractérisées par décalage vers le haut du mouvement de torsion du CH2, par comparaison avec le mouvement de torsion du CH2 du même PP utilisé pour revêtir le f-MWNT mais en l'absence de f-MWNT ; et dans lequel le décalage vers le haut est une augmentation du nombre d'onde de 4 cm-1 à 10 cm-1, telle que déterminée par spectroscopie infrarouge à transformée de Fourier (FTIR) ; et dans lequel les interactions CH-π intermoléculaires sont caractérisées par un décalage vers le bas de la bande D, par comparaison avec la bande D du même f-MWNT qui n'a pas été revêtue de PP, le décalage vers le bas étant une diminution du nombre d'onde de 4 cm-1 à 10 cm-1, telle que déterminée par spectroscopie Raman.
 
13. PP/f-MWNT selon l'une quelconque des revendications 11 à 12, dans lequel les f-MWNT ont un diamètre de 5 nm à 200 nm ; une longueur de 0,5 micromètre à 1 mm ; et de 3 feuillets à 100 feuillets.
 
14. PP/f-MWNT selon l'une quelconque des revendications 11 à 13, dans lesquels le PP des PP/f-MWNT est caractérisé par une température de décomposition thermique qui est d'une quantité supérieure ou égale à environ 10 °C supérieure à une température de décomposition thermique du même PP utilisé pour revêtir les f-MWNT mais en l'absence des f-MWNT, telle que déterminée par analyse thermogravimétrique (ATG) sous atmosphère d'azote ;
dans lesquels le PP des PP/f-MWNT est caractérisé par une température de cristallisation qui est d'une quantité supérieure ou égale à 2 °C supérieure à la température de cristallisation du même PP utilisé pour revêtir les f-MWNT mais en l'absence des f-MWNT, telle que déterminée par analyse thermique par calorimétrie différentielle à balayage (DSC), conformément à ASTM D794-06 ; et
dans lesquels le PP des PP/f-MWNT est caractérisé par une température de fusion qui est d'une quantité supérieure ou égale à environ 1 °C supérieure à une température de fusion du même PP utilisé pour revêtir les f-MWNT mais en l'absence de f-MWNT, telle que déterminée par analyse thermique par calorimétrie différentielle à balayage (DSC) conformément à ASTM D794-06.
 
15. PP/f-MWNT selon l'une quelconque des revendications 11 à 14, dans lesquels les PP/f-MWNT comprennent une quantité supérieure ou égale à 50 % en poids de f-MWNT discrets revêtus de PP (PP/f-MWNT discrets), par rapport au poids total des f-MWNT ; et dans lesquels les PP/f-MWNT ont un diamètre de 6 nm à 210 nm.
 




Drawing



























































Cited references

REFERENCES CITED IN THE DESCRIPTION



This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

Patent documents cited in the description




Non-patent literature cited in the description