(19)
(11)EP 3 487 673 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
02.09.2020 Bulletin 2020/36

(21)Application number: 17751849.5

(22)Date of filing:  20.07.2017
(51)International Patent Classification (IPC): 
B28B 1/00(2006.01)
E04B 5/08(2006.01)
E04C 2/04(2006.01)
B28B 23/22(2006.01)
E04C 3/22(2006.01)
(86)International application number:
PCT/IB2017/054402
(87)International publication number:
WO 2018/015920 (25.01.2018 Gazette  2018/04)

(54)

STRUCTURE OF REINFORCED CEMENTITIOUS MATERIAL AND PROCESS OF MAKING THE SAME STRUCTURE BY A THREE-DIMENSIONAL PRINTING PROCESS

STRUKTUR AUS VERSTÄRKTEM ZEMENTMATERIAL UND VERFAHREN ZUR HERSTELLUNG DERSELBEN STRUKTUR DURCH EIN DREIDIMENSIONALES DRUCKVERFAHREN

STRUCTURE DE MATÉRIAU CIMENTAIRE RENFORCÉ ET PROCÉDÉ DE FABRICATION DE LA MÊME STRUCTURE PAR UN PROCÉDÉ D'IMPRESSION TRIDIMENSIONNEL


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 22.07.2016 IT 201600077424

(43)Date of publication of application:
29.05.2019 Bulletin 2019/22

(73)Proprietor: ETESIAS S.r.l.
80125 Napoli (IT)

(72)Inventors:
  • ASPRONE, Domenico
    80125 Napoli (IT)
  • AURICCHIO, Ferdinando
    20123 Milano (IT)
  • MENNA, Costantino
    80030 Carbonara di Nola (NA) (IT)

(74)Representative: PGA S.p.A. 
Via Mascheroni, 31
20145 Milano
20145 Milano (IT)


(56)References cited: : 
BE-A- 463 520
FR-A1- 2 918 396
DE-A1-102014 206 697
  
      
    Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


    Description

    Field of the invention



    [0001] The object of the present invention is a structure of reinforced cementitious material and a process of making the same by a three-dimensional printing process. The invention can be advantageously applied in the architectural, design and building fields, for example for erecting buildings and also in the construction engineering field.

    Background of the invention



    [0002] Nowadays, making components by 3D printers using the Additive Manufacturing technology has a blooming development and is substantially impacting different industrial manufacturing fields. The 3D printing process enables to deposit layers of a material on a base of a three-dimensional pattern for physically making this latter. With reference to the present description, the construction, building and design fields are particularly interesting. Recently, the Additive Manufacturing technology is used by 3D printers for supplying inorganic "pastes" (mainly clays) as printing material for making typically small artifacts having non-structural functions. The artifacts obtainable by the Additive Manufacturing technology are not useable as structural elements in the building and construction fields. Until now, the components of cementitious material used in the construction and building fields are made by two different technologies: the subtractive technology and the formative technology. The subtractive technology provides to take away a cementitious material from a rough preform in order to obtain a finished product. On the contrary, the formative technology provides to pour a cementitious material at the liquid (green) state inside adapted moulds (casings) wherein the material solidifies for defining the finished product: at the end of the solidifying step, the finished product is then extracted from the mould. These known technologies, while being widely used for making components and structural elements of cementitious materials, exhibits substantial limitations. De facto, such technologies do not enable to easily and economically make components different from each other by shape and size. Indeed, it is noted that when there is the need of making by the above described processes, different types of blocks of concrete, it will be necessary to differentiate - in case of the subtractive technology - the process of removing the material for each block, while - in case of the formative technology - it will be necessary to provide a different mould for each component; in this way, the actions at a processing level, necessary for making different types of blocks, will substantially increase the times and therefore the costs for manufacturing these latter. Moreover, it is noted that manufacturing blocks different from each other entails, with the subtractive technology, an additional step of processing the rough blocks which, besides increasing the processing times, impacts on the cost and the amount of scraps. Instead, the formative technology requires a greater investment in term of equipment; each type of blocks will require a dedicated mould. Moreover, it is noted that the known above described technologies (subtractive and formative for elements of cementitious material) do not enable to easily and economically make components of cementitious material exhibiting complicated shapes, for example defined by arcuate portions with varying cross-section.

    [0003] Therefore, the object of the present invention consists of substantially solving at least one of the inconveniencies and/or limitations of the previous solutions.

    [0004] Document BE463520 FR2918396 MAT4P1WO disclose some examples of prefabricated cementitious structures according to the prior art.

    [0005] DE102014206697 discloses a process of making a structure by a three-dimensional printing process of for example cementitious material.

    [0006] A first object of the present invention consists of providing a structure of reinforced cementitious material exhibiting excellent mechanical properties and, at the same time, easily and quickly manufacturable, in accordance with claim 6. Particularly, it is an object of the present invention to provide a structure of reinforced cementitious material exhibiting a suitable shape and size and adapted to ensure optimal structural characteristics. Moreover, it is an object of the present invention to provide a structure of reinforced cementitious material which exhibits a flexible use and which can be employed for making different types of constructions and structural elements. Then, it is an object of the present invention to provide a structure of reinforced cementitious material manufacturable with a limited amount of material, and capable anyway of maintaining excellent properties of mechanical strength to stresses. Moreover, it is an object of the present invention to provide a structure of reinforced cementitious material obtainable with limited manufacturing costs.

    [0007] Then, it is an object of the present invention to provide a fast and highly versatile process of making a structure of reinforced cementitious material which therefore can reduce at the minimum the manufacturing costs, in accordance with claim 1.

    [0008] A further object not part of the present invention consists of providing a cementitious composition adapted to be 3D-printed, particularly a cementitious composition being capable of being conveyed to the supplying head 101 of the 3D printer and to be extruded or pumped by the same, and therefore printable, through the supplying head.

    [0009] Moreover, a further object not part of the present invention consists of providing a cementitious composition wherein the layers thereof, after being printed, show the capability of remaining separated from each other, and of supporting the weight of the following layers deposited by the 3D printing process, of having a good setting and hardening kinetics, and compressive strength. Lastly, a further object not part of the present invention consists of providing a cementitious composition enabling to make shapes which are both structurally efficient and characterized by using a low quantity of the cementitious material. These and other objects, which will better appear in the following description, are substantially met by a structure of reinforced cementitious material and a process of making this latter according to what is disclosed in one or more of the attached claims, and/or of following aspects, considered alone or in any combination with each other or in a combination with any of the attached claims and/or in a combination of any of the further aspects or characteristics described in the following.

    Description of the drawings



    [0010] Some embodiments and some aspects of the invention will be described in the following with reference to the attached drawings, given only in an indicative and therefore non-limiting way, wherein:
    • Figure 1 is a schematic view of a first embodiment of a structure of reinforced cementitious material according to the present invention;
    • Figure 2 is a schematic view of a second embodiment of a structure of reinforced cementitious material according to the present invention;
    • Figure 3 is a schematic view of a third embodiment of a structure of reinforced cementitious material according to the present invention;
    • Figure 4 is a detailed view of the structure of reinforced cementitious material of Figure 3;
    • Figures 5 and 6 are respectively a top view and a front view of a structure of cementitious material according to the present invention;
    • Figure 7 is an exploded view of a connecting element of the reinforced cementitious material according to the present invention;
    • Figures 8 and 9 are respectively a perspective view and a front view of a module of a structure of reinforced cementitious material according to the present invention;
    • Figures 10 and 11 schematically illustrate a step of forming a module of a structure of reinforced cementitious material according to the present invention;
    • Figures from 12 to 16 schematically illustrate some steps of a process of making a structure of reinforced cementitious material according to the present invention;
    • Figure 17 is a perspective view of a fourth embodiment a structure of reinforced cementitious material according to the present invention;
    • Figure 18 is a perspective view of a step of an embodiment variant of a process of making a structure of reinforced cementitious material according to the present invention;
    • Figure 19 is a cross-section view of a cylindrical specimen used in the example 4.

    Detailed description



    [0011] It is noted that in the present detailed description, corresponding parts illustrated in the different figures are indicated by the same numeral references. The figures could illustrate the object of the invention by not-to-scale representations; therefore, parts and components illustrated in the figures regarding the object of the invention could refer only to schematic representations.

    [0012] The term "three-dimensional printing" or 3D printing means a process of making objects by a three-dimensional printer or 3D printer based on a material additive technology (known as Additive Manufacturing). The process provides making - by dedicated modelling software - a three-dimensional model which is delivered to a 3D printer configured for making the corresponding physical model of the digital mathematical model by depositing a material one layer on another, by advancing by cross-sections towards the top.

    [0013] The term "3D printer" means a device configured for making a three-dimensional physical model by means of an additive manufacturing 3D-printing process. Particularly, the 3D printer comprises at least one supplying head 101 configured for depositing a predetermined quantity of material. The 3D printer comprises a movement system 102 connected to the supplying head 101 which is configured for moving this latter according to a three-dimensional space.

    [0014] Moreover, the 3D printer can comprise a control unit 103 connected to the movement system 102 and to the supplying head 101; the control unit 103 is configured for receiving and processing a digital mathematical model and for commanding the activation of the movement system 102 and supplying head 101 for defining the stratification (layer-by-layer) of the processed model. The 3D printer is configured, starting from an object designed/drawn by software, for physically reproducing it by suitable materials.

    [0015] The term "control unit" 103 means an electronic-type component which can comprise at least one of: a digital processor (CPU), a memory (or memories), an analog-type circuit, or a combination of one or more digital processing units with one or more analog-type circuits. The control unit can be "configured" or "programmed" for executing some steps: this can be physically obtained by any means enabling to configure or program the control unit. For example, when a control unit comprises one or more CPUs and one or more memories, one or more programs can be stored in suitable memory banks connected to the CPU or CPUs; the program or programs contain instructions which, when are executed by the CPU or CPUs, program or configure the control unit for executing operations described with reference to the control unit. As an alternative, if the control unit is or comprises an analog-type circuitry, then the circuit of the control unit can be designed to include a configured circuitry, when used, for processing electric signals in order to execute the steps regarding the control unit.

    [0016] The term "cementitious material" means a material comprising at least partially a composition of cementitious material, or a cementitious material as specifically described in the following. Particularly, the term "cementitious material" means a material comprising fully, particularly exclusively, said composition of cementitious material or a cementitious composition. Particularly, the term "cementitious material" means a material obtained by a composition of cementitious material or a cementitious composition as specifically described in the following. Particularly, the cementitious material is obtained by 3D-printing a cementitious composition according to the hereinbelow description.

    1. Structure



    [0017] 1 generally indicates a structure of reinforced cementitious material, for example, useable in the architectural and building fields, for example for erecting buildings, and also in the construction engineering field. As it is visible for example in Figures from 1 to 3, the structure 1 comprises a plurality of modules of cementitious material each of them, as will be better described in the following, is manufacturable by a three-dimensional printing process. More particularly, the structure 1 comprises at least one first module 2 externally delimited by a lateral wall 3 which defines an outer lateral surface 3a of the first module 2. As it is for example visible in Figure 8, the lateral wall 3 of the first module 2 extends along a stratification direction D between a first and second ends; the stratification direction D, as will be better described in the following, is a direction along which the three-dimensional printing process deposits a plurality of layers L of cementitious material one on the other (Figures 10 and 11). In a preferred but non-limiting embodiment of the invention, the first module 2 exhibits, along the stratification direction D, a substantially constant cross-section essentially defining a profiled element. More particularly, the first module 2 exhibits, along a cross-section perpendicular to the stratification direction D, a closed outer perimeter having, for example, a polygonal shape (see Figure 9 for example). In a preferred but non-limiting embodiment of the invention, the first module 2 comprises an internally hollow body; particularly, the first module 2 comprises at least one seat defined inside the closed outer perimeter, which develops for all the extension of said first module 2 along the stratification direction D: the through seat extends between the first and second ends of the module 2. As it is visible in Figures from 1 to 4 and 12, for example, at least part of the outer lateral surface 3a of the first module 2 defines a reciprocal coupling surface 3b which, as will be better described in the following, is configured for abutting on a respective reciprocal coupling surface of a further module. As it is visible in Figures 1, 8 and 9, for example, at least part of the lateral surface 3a of the first module 2 can define a further reciprocal coupling surface 3c opposite to the reciprocal coupling surface 3b of the module 2 itself. In a preferred but non-limiting embodiment of the invention, the further reciprocal coupling surface 3c of the first module 2 exhibits the same shape and size as the reciprocal coupling surface 3b of the module 2 itself; the further reciprocal coupling surface 3c of the first module is configured for abutting on a reciprocal coupling surface and/or on a further reciprocal coupling surface of a further module. Moreover, the first module 2 comprises at least one hooking portion 4 defining at least one cavity 4a extending at least partially along the stratification direction D of the module 2 itself. In the configuration wherein the first module 2 comprises a closed outer outline lateral wall 3, the hooking portion 4 is defined inside said closed outer perimeter; optionally the portion 4 extends for all the development of the first module 2 along the stratification direction D, in other words from the first to the second ends of the first module 2. Figures 1, 3 and 4 illustrate in a non-limiting way a first module 2 exhibiting two hooking portions 4. Figure 2 illustrates an embodiment variant wherein the first module 2 exhibits only one hooking portion 4. However, it is not excluded the possibility of making a first module 2 exhibiting a number of hooking portions 4 greater than 2. Particularly, the first module 2 can exhibit a number of hooking portions 4 equal to or comprised between 1 and 10, particularly between 1 and 5, still more particularly between 1 and 4. Each hooking portion 4 can define only one cavity 4a or a plurality of cavities in a number for example comprised between 1 and 4. As it is visible in Figures 1, 3, 4, 8 and 9 for example, the first module 3 can comprise - inside the closed outer perimeter - a reinforcing portion 11 extending inside the closed outer perimeter between two sides substantially opposite to each other. Advantageously but in a non-limiting way, the reinforcing portion 11 of the first module 2 extends along the stratification direction D along all the development of the first module 2, particularly from the first to the second ends of the first module 2. The reinforcing portion 11 defines, cooperatively with the lateral wall 3 of the first module 2, at least one first and one second flanked through seats 12, 13 and both defined inside the closed outer perimeter of the first module 2 (see Figures 1 and 9 for example).

    [0018] From the dimensional point of view, the first module 2 can exhibit a height - defined along the stratification direction D - greater than 100 mm, particularly greater than 200 mm, still more particularly comprised between 250 and 1,000 mm. Moreover, the first module can exhibit a length and a width - measured perpendicular to the stratification D and perpendicular to each other - greater than 100 mm, particularly greater than 200 mm, still more particularly comprised between 250 and 3,000 mm.

    [0019] As it is visible in the attached figures, moreover the structure 1 comprises at least one module 5 externally delimited by a lateral wall 6 which defines an outer lateral surface 6a of the second module 5. The lateral wall 6 of the second module 5 extends along a stratification direction between a first and second ends; the stratification direction, as will be better described in the following, is a direction along which the three-dimensional printing process deposits a plurality of layers L of cementitious material one on the other (Figures 10 and 11). The stratification direction D of the first module 2 and the stratification direction of the second module 5 are parallel to each other. In a preferred but non-limiting embodiment of the invention, the second module 5 exhibits, along the stratification direction, a substantially constant cross-section essentially defining a profiled element. More particularly, the second module 5 exhibits, along a cross-section perpendicular to the stratification direction, a closed outer perimeter having a polygonal shape for example. In a preferred but non-limiting embodiment of the invention, the second module 5 comprises an internally hollow body; particularly, the second module 5 comprises at least one seat defined inside the closed outer perimeter which extends for all the extension of said second module along the stratification direction: the through seat extends between the first and second ends of the module 5. At least part of the outer lateral surface 6a of the second module 5 defines a reciprocal coupling surface 6b countershaped and in contact with the reciprocal coupling surface 3b of the first module 2. As it is visible in Figures from 1 to 3 for example, at least part of the lateral surface 6a of the second module 5 can define a further reciprocal coupling surface 6c opposite to the reciprocal coupling surface 6b of the module 5 itself. In a preferred but non-limiting embodiment of the invention, the further reciprocal coupling surface 6c of the second module 5 exhibits the same shape and size as the reciprocal coupling surface 6b of the module 5 itself; the further reciprocal coupling surface 6c of the second module 5 abuts on a reciprocal coupling surface and/or on a further reciprocal coupling surface of a further module. The second module 5 comprises at least one hooking portion 7 defining at least one cavity 7a extending at least partially along the stratification direction of the module 5. In the configuration wherein the second module 5 comprises the lateral wall 6 having a closed outer outline, the hooking portion 7 is defined inside said closed outer perimeter; optionally, the portion 7 extends for all the development of the second module 5 along the stratification direction, in other words from the first to the second ends of the second module 5. Figures 1 and 3 illustrate, in a non-limiting way, a second module 5 exhibiting two hooking portions 7. Figure 2 illustrates an embodiment variant wherein the second module exhibits three hooking portions 7. However, it is not excluded the possibility of making the second module 5 so that is has only one hooking portion 7 or a number of hooking portions 7 greater than three. Particularly, the second module 5 can exhibit a number of hooking portions 7 equal to or comprised between 1 and 10, particularly between 1 and 5, still more particularly between 1 and 4. Each hooking portion 7 can define only one cavity 7a or a plurality of cavities, for example in a number comprised between 1 and 4. As it is visible in Figures 1, 3, 13 and 14 for example, the second module 2 can comprise - inside the closed outer perimeter - a reinforcing portion 14 which extends inside the closed outer perimeter between two sides substantially opposite to each other. Advantageously, but in a non-limiting way, the reinforcing portion 14 of the second module 5 extends along the stratification direction for all the development of the second module 5, particularly from the first to the second ends of the module 5. The reinforcing portion 14 defines, cooperatively with the lateral wall 6 of the second module 5, at least one first and one second flanked through seats 15, 16 and both defined inside the closed outer perimeter of the second module 5 (see Figures 1 and 3, for example).

    [0020] From the dimensional point of view, the second module 5 can exhibit a height - defined along the stratification direction of the module 5 itself - greater than 100 mm, particularly greater than 200 mm, still more particularly comprised between 250 and 1,000 mm. In an embodiment illustrated in the attached figures, the first and second modules 2, 5 exhibit substantially the same height: the first and second ends of the first module are respectively disposed at the first and second ends of the second module 5. Moreover, the second module 5 can exhibit a length and width - measured perpendicularly to the stratification direction of the module 5 itself and perpendicular to each other - greater than 100 mm, particularly greater than 200 mm, still more particularly comprised between 250 and 3,000 mm. Figure 1 illustrates - in a non-limiting way - an embodiment of the structure 1 wherein the first and second modules 2, 5 are identical to each other by shape and size. As it is visible in the attached figures, the structure 1 can comprise, in a non-limiting way, at least one third module 18 externally delimited by a lateral wall 19 which defines an outer lateral surface 19a of the third module 18. The lateral wall 19 of the third module 18 extends along a stratification direction between a first and second ends; the stratification direction, as will be better described in the following, is a direction along which the three-dimensional printing process deposits a plurality of layers L of cementitious material one on the other. The stratification direction of the first and second modules 2, 5 is parallel to the stratification direction of the third module 18. In a preferred but non-limiting embodiment of the invention, the third module 18 exhibits, along the stratification direction, a substantially constant cross-section essentially defining a profiled element. More particularly, the third module 18 exhibits, along a cross-section perpendicular to the stratification direction, a closed outer perimeter having a polygonal shape for example. In a preferred but non-limiting embodiment of the invention, the third module 18 comprises an internally hollow body; particularly, the second third 18 comprises at least one seat defined inside the closed outer perimeter which extends for all the extension of said second module along the stratification direction: the through seat extends between the first and second ends of the module 18. At least part of the outer lateral surface 19a of the third module 18 defines a reciprocal coupling surface 19b countershaped to and in contact with the further reciprocal coupling surface 6c of the second module 5. As it is visible in Figures from 1 to 3, for example, at least part of the lateral surface 19a of the third module 18 can define a further reciprocal coupling surface 19c opposite to the reciprocal coupling surface 19b of the module 18 itself. In a preferred but non-limiting embodiment of the invention, the further reciprocal coupling surface 19c of the third module 18 exhibits the same shape and size as the reciprocal coupling surface 19b of the module 18 itself; the further reciprocal coupling surface 19c of the third module 18 abuts on a reciprocal coupling surface and/or a further reciprocal coupling surface of a further module. The third module 18 comprises at least one hooking portion 20 defining at least one cavity 20a extending at least partially along the stratification direction of the module 18. In the configuration wherein the third module 18 comprises a closed outer outline lateral wall 19, the hooking portion 20 is defined inside said closed outer perimeter; optionally the portion 20 extends for all the development of the third module 18 along the stratification direction, in other words from the first to the second ends of the third module 18. Figures 1 and 3 illustrate in a non-limiting way a third module 18 exhibiting two hooking portions 20. Figure 2 illustrates an embodiment variant wherein the third module exhibits three hooking portions 20. However, it is not excluded the possibility of making a third module 18 exhibiting only one hooking portion 20 or a number of hooking portions 20 greater than three. Particularly, the third module 18 can exhibit a number of hooking portions 20 equal to or comprised between 1 and 10, particularly between 1 and 5, still more particularly between 1 and 4. Each hooking portion 20 can define only one cavity 20a or a plurality of cavities, for example in a number comprised between 1 and 4. As it is visible in Figure 3 for example, the third module 18 can comprise - inside the closed outer perimeter - a reinforcing portion 21 extending inside the closed outer perimeter between two sides substantially opposite to each other. Advantageously, but in a non-limiting way, the reinforcing portion 21 of the third module 18 extends along the stratification direction for all the development of the third module 18, particularly from the first to the second ends of the module 18. The reinforcing portion 21 defines, cooperatively with the lateral wall 19 of the third module 18, at least one first and one second flanked through seats 22, 23 both defined inside the closed outer perimeter of the third module 18 (see Figure 3, for example). From the dimensional point of view, the third module 18 can exhibit a height - defined along the stratification direction of the module 18 itself - greater than 100 mm, particularly greater than 200 mm, still more particularly comprised between 250 and 3,000 mm. In an embodiment illustrated in the attached figures, the second and third modules 5, 18 exhibit substantially the same height (so that the third module exhibits substantially the same height as the first module) : the first and second ends of the second module are respectively disposed at the first and second ends of the first module 18. Moreover, the third module 18 can exhibit a length and width - measured perpendicularly to the stratification direction of the module 18 itself and perpendicularly to each other - greater than 100 mm, particularly greater than 200 mm, still more particularly comprised between 250 and 3,000 mm.

    [0021] Figure 1 illustrates an embodiment of the structure wherein the first and second modules 2, 5 are identical to each other by shape and size, while the third module exhibits a shape and size different from said modules 2 and 5. However, it is not excluded the possibility of making a structure 1 wherein the third module 18 is identical by shape and size to the first and second modules. As it is visible in the attached figures, the structure 1 can comprise a plurality of modules in contact with each other and aligned along a direction A (see Figure 14 for example) perpendicular to a stratification direction of each module. For example, the structure 1 can comprise a number of modules greater than 3; particularly the structure 1 can comprise a number of modules greater than 4, particularly greater than 5, still more particularly comprised between 5 and 20. At least part of the plurality of modules of the structure 1 can comprise a reciprocal coupling surface and a further reciprocal coupling surface opposite to each other with respect to the module itself; the reciprocal coupling surface of a module abuts on a reciprocal coupling surface and/or on a further reciprocal coupling surface of an immediately adjacent module (modules in contact with each other). The modules can be all different from each other by shape and size or can be at least partially identical to each other by shape and size. The shape and/or size of the above described modules can be determined by a process optimizing the topology, which maximizes the mechanical performance of the block. As it is visible in Figures from 1 to 3 and 6, for example, moreover the structure comprises at least one connecting element 8 engaged, on one side, inside the cavity 4a of the hooking portion 4 of the first module 2 and, on the other side, inside the cavity 7a of the hooking portion 7 of the second module 5: the connecting element 8 stably constrains the first and second modules 2, 5 and is configured for holding these latter in contact with each other. De facto, the connecting element acts as an outer reinforcing element providing the structure with strength to tensile loads.

    [0022] More particularly and as it is visible in the attached figures, the connecting element 8 comprises at least one reinforcing bar, optionally of metal material, extending along a longitudinal development direction between a first and second end portions 8a, 8b: the longitudinal development direction of the bar is transversal, particularly perpendicular, to the stratification direction of the first and second modules. The connecting element 8 comprises - at the first end portion 8a - a first engagement portion 9 emerging from the reinforcing bar transversally to the longitudinal development direction of the same and engaged inside the cavity 4a of the hooking portion 4 of the first module 2. Moreover, the connecting element 8 comprises - at the second end portion 8b - a second engagement portion 10 emerging from the reinforcing bar transversally to the longitudinal development direction of the same and engaged inside the cavity 7a of the hooking portion 7 of the second module 2. De facto, the portions 9 and 10 partially cross - along the height - the first and second modules 2, 5 while the reinforcing bar is disposed outside the lateral wall and the through seat of the respective modules. The reinforcing bar is essentially an outer connecting bar between the portions 9, 10 which are engaged inside the respective modules; the bar essentially acts as a tie in relation to the tensile stresses generated in the system. Moreover, the connecting element 8 can comprise only one reinforcing bar adapted to connect the engagement portions 9 and 10. Figures 5 and 6 illustrate a preferred embodiment of the connecting element 8 which exhibits a first and second engagement portions 9, 10 vertically crossing the first and second modules and exhibiting respective end portions emerging from the first and second ends of the respective modules (Figure 5). With such arrangement, the connecting element 8 exhibits two reinforcing bars disposed at the first and second ends of the module 2 and 5: the bars are disposed opposite to each other with respect to the modules 2 and 5. A first reinforcing bar is constrained to the first end portion of the portions 9 and 10 while a second bar is constrained to the second end portion of the portions 9 and 10. Both the reinforcing bars are disposed outside the modules 2, 5 and respectively at the first and second ends of these latter. Figure 2 illustrates an embodiment of the structure 1, comprising only one connecting element 8 adapted to constrain the first and second modules 2. Figure 1 illustrates a preferred but non-limiting embodiment of the invention wherein the structure comprises two connecting elements adapted to stably constrain the first and second modules 2, 5. However it is not excluded the possibility of defining a structure 1 comprising a number of connecting elements 8 equal to or greater than 3, particularly comprised between 3 and 10, still more particularly between 3 and 5. In a preferred but non-limiting embodiment of the invention illustrated in Figures 3, 4, 5 and 7 for example, the first and second engagement portions 9, 10 of the connecting element 8 are distinct and removably associable to the reinforcing bar. Particularly, the first and second engagement portions 9, 10 can for example comprise respective threaded bars: the reinforcing bar can comprise, for example, a bar exhibiting at the end portions 8a, 8b an engagement portion shaped as an eyelet or slot inside which part of the threaded bar of the portions 9 and 10 can be housed. The reinforcing bar can be fixed to the respective engagement portions by bolts engaging the threaded bars of the portions 9 and 10 and which therefore constrain the engagement portions of the reinforcing bar to the portions 9 and 10. Figure 18 illustrates an embodiment variant of the connecting element wherein the reinforcing bar and engagement portions 9, 10 are integrally joined for defining a single body having a substantially "C" shape. As it is visible in Figures from 1 to 3 for example, further the structure 1 can comprise at least one connecting element 24 engaging, on one side, inside the cavity 7a of the hooking portion 7 of the second module and, on the other side, inside the cavity 20a of the hooking portion 20 of the third module 18: the connecting element 24 stably constrains the second and third modules 5, 18, and is configured for holding these latter in contact with each other. More specifically and it is visible in the attached figures, the connecting element 24 comprises at least one reinforcing bar, optionally of metal material, extending along a longitudinal development direction between a first and second end portions 24a, 24b: the longitudinal development direction of the bar is transversal, particularly perpendicular, to the stratification direction of the first and second modules. The connecting element 24 comprises - at the first end portion 24a - a first engagement portion 25 emerging from the reinforcing bar transversally to the longitudinal development direction of the same and engaged inside the cavity 7a of the hooking portion 7 of the second module 5 (Figure 3). The connecting element 24 further comprises - at the second end portion 24b - a second engagement portion 26 emerging from the reinforcing bar transversally to the longitudinal development direction of the same and engaged inside the cavity 20a of the hooking portion 20 of the third module 18. De facto, the portions 25 and 26 vertically cross at least partially the second and third modules 5, 18 while the reinforcing bar is disposed outside the lateral wall and the through seat of the respective modules. The reinforcing bar of the element 24 is essentially an outer connecting bar between the portions 25, 26 which are engaged inside the respective modules. Moreover, the connecting element 24 can comprise only one reinforcing bar adapted to connect the engagement portions 25 and 26. In a preferred embodiment, the connecting element 24 exhibits a first and second engagement portions 25, 26 vertically crossing the second and third modules and exhibiting respective end portions emerging from the first and second ends of the respective modules. With such arrangement, the connecting element 24 exhibits two reinforcing bars disposed at the first and second ends of the modules 5 and 18: the bars are disposed opposite to each other with respect to the modules 5 and 18. A first reinforcing bar is constrained to the first end portions of the portions 25 and 26, while a second bar is constrained to the second end portion of the portions 25 and 26. Both the reinforcing bars are disposed outside the modules 5 and 18 and respectively at the first and second ends of these latter.

    [0023] The structure 1 can comprise only one connecting element 24 adapted to constrain the second and third modules 5, 18 (Figure 2). Figure 1 illustrates a preferred but non-limiting embodiment of the invention wherein the structure comprises two connecting elements 24 adapted to stably constrain the second and third modules 5, 18. However, it is not excluded the possibility of defining a structure 1 comprising a number of connecting elements 24 equal to or greater than 3, particularly comprised between 3 and 10, still more particularly between 3 and 5. In a preferred but non-limiting embodiment of the invention, the first and second engagement portions 25, 26 of the connecting element 24 are distinct and removably associable to the reinforcing bar. Particularly, the first and second engagement portions 25, 26 can for example comprise respective threaded bars: the reinforcing bar can for example comprise a bar exhibiting, at the end portions 24a, 24b, an engagement portion shaped as an eyelet or slot inside which part of the threaded part of the portions 25 and 26 can be housed. The reinforcing bar can be fixed to the respective engagement portions by bolts which engage the threaded bars of the portions 25 and 26 which constrain therefore the engagement portions of the reinforcing bar to the portions 25 and 26. In a preferred but non-limiting embodiment of the invention, moreover the structure 1 comprises at least one connecting element 27 engaged, on one side, inside the cavity 4a of the hooking portion 4 of the first module 2 and, on the other side, inside the cavity 20a of the hooking portion 20 of the third module 18; the connecting element 27 stably constrains the first module and third module 2, 18. As it is visible in Figure 3, advantageously the connecting element exhibits an arrangement (structure) similar to the connecting elements 8 and 24. As schematically shown in Figure 1, the structure 1 is configured for mainly opposing, under operative conditions of the same, a stress S directed perpendicularly to the stratification direction of the plurality of modules and perpendicularly to the alignment direction A of the same (the direction A is schematically shown in Figure 14).

    2. Process



    [0024] Moreover, it is an object of the present invention a process of making a structure 1 of reinforced cementitious material according to anyone of the attached claims and/or according to the above given description. The process comprises a step of making a plurality of modules of cementitious material by a three-dimensional printing process which comprises a step of depositing a plurality of layers L of cementitious material one on the other along a stratification direction D; the layers L exhibit substantially the same shape and size: each module can exhibit, along the stratification direction D, a substantially constant cross-section for essentially defining a profile. However, it is not excluded the possibility of making modules exhibiting - along the stratification direction D - a varying cross-section, obtainable, for example, by a "cantilevered" layer-by-layer printing process. Particularly, by the three-dimensional printing process, the first and second modules 2, 5 and optionally also the third module 18 are obtained. Figures 10 and 11 schematically illustrate the three-dimensional printing process of making the first module 2. The head 101 of the 3D printer deposits one layer L on another layer of cementitious material for defining a cross-section of the module. By the same process, the second module 5 (the configuration thereof is not illustrated in the attached figures) and optionally the third module 18 are made. After, the first and second modules 2, 5 are disposed in contact with each other so that the respective reciprocal coupling surfaces 3b, 6b of said modules abut on each other (Figure 12 illustrates a step of approaching the modules 2 and 5). Optionally, if the third module 18 is present, the process comprises a step of contacting the second and third modules so that the further reciprocal coupling surface 6c of the second module 5 abuts on the reciprocal coupling surface 19b of the third module 18 (Figure 13 illustrates a step of approaching the modules 5 and 18). After the step of contacting the first and second modules, the process comprises a step of engaging at least one connecting element 8, from one side, inside the cavity 4a of the hooking portion 4 of the first module 2 and, on the other side, inside the cavity 7a of the hooking portion 7 of the second module 5; the connecting element 8 stably constrains the first and second modules 2, 5 and is configured for holding these latter in contact with each other. More specifically, the step of engaging the connecting element 8 to the first and second modules 2, 5 comprises at least the following sub-steps:
    • stably engaging the first engagement portion 9 inside the cavity 4a of the hooking portion 4 of the first module 2,
    • stably engaging the second engagement portion 10 inside the cavity 7a of the hooking portion 7 of the second module 5.


    [0025] Figure 18 illustrates a step of inserting the connecting element 8 comprising the engagement portions 9, 10 integrally joined to the reinforcing bar.

    [0026] As hereinbefore described, the connecting element 8 can comprise engagement portions 9, 10 distinct and removable from the reinforcing bar; in such arrangement, the step of engaging the connecting element 8 comprises the following sub-steps:
    • inserting the first engagement portion 9 inside the cavity 4a of the hooking portion 4 of the first module 2,
    • filling at least partially the cavity 4a of the hooking portion 4 of the first module 2 with a cementitious material at least partially at a liquid state so that this latter can contact at least part of said first engagement portion 9,
    • constraining, by hardening the cementitious material inside the cavity 4a of the first module 2, said first engagement portion 9,
    • inserting the second engagement portion 10, for example before a step of hardening the cementitious material present in the cavity 4a, inside the cavity 7a of the hooking portion 7 of the second module 5,
    • filling at least partially the cavity 7a of the hooking portion 7 of the second module 5 with a cementitious material at least partially at a liquid state so that this latter can contact at least part of said second engagement portion 10,
    • constraining, by hardening the cementitious material inside the cavity 7a of the second module 5, said second engagement portion 10.


    [0027] After engaging the engagement portions 9, 10 with the modules 2 and 5, the process comprises a step of constraining (fixing) the reinforcing bar to said first and second engagement portions 9, 10. The process, simultaneously with or after the step of engaging the connecting element 8 with the first and second modules, can comprise at least one step of further fixing the first and second modules which comprises at least the following sub-steps:
    • providing between the reciprocal coupling surfaces of the first and second modules, a predetermined quantity of cementitious material at least partially at a liquid state,
    • further constraining, by hardening said cementitious material disposed between the reciprocal coupling surfaces, said first and second modules.


    [0028] If a third module 18 is present, moreover the process can comprise a step of engaging at least one connecting element 24, on one side, inside the cavity 7a of the hooking portion 7 of the second module 5 and, on the other side, inside the cavity 20a of the hooking portion 20 of the third module 18; the connecting element 24 stably constrains the second module 5 and third module 18 and is configured for holding these latter in contact with each other. More specifically, the step of engaging the connecting element 24 with the second and third modules comprises at least the following sub-steps:
    • stably engaging the first engagement portion 25 inside the cavity 7a of the hooking portion 7 of the second module 5,
    • stably engaging the second engagement portion 26 inside the cavity 20a of the hooking portion 20 of the third module 18.


    [0029] As hereinbefore described, the connecting element 24 can comprise engagement portions 25 distinct and removable from the reinforcing bar; in such arrangement, the step of engaging the connecting element 24 comprises the following sub-steps:
    • inserting the first engagement portion 25 inside the cavity 7a of the hooking portion 7 of the second module 5,
    • filling at least partially the cavity 7a of the hooking portion 7 of the second module 5 with a cementitious material at least partially at a liquid state so that this latter can contact at least part of said first engagement portion 25,
    • constraining, by hardening the cementitious material inside the cavity 7a of the second module 5, said first engagement portion 25,
    • inserting the second engagement portion 26 inside the cavity 20a of the hooking portion 20 of the third module 18,
    • filling at least partially the cavity 20a of the hooking portion 20 of the third module 18 with a cementitious material at least partially at a liquid state so that this latter can contact at least part of said second engagement portion 26,
    • constraining, by hardening the cementitious material inside the cavity 20a of the third module 18, said second engagement portion 26.


    [0030] After constraining the engagement portions 25, 26 with the modules 5 and 18, the process comprises a step of constraining (fixing) the reinforcing bar to said first and second engagement portions 25 and 26. The process, simultaneously with or after the step of engaging the connecting element 24 with the second and third modules, can comprise at least one step of further fixing the first and second modules which comprises at least the following sub-steps:
    • providing between the reciprocal coupling surfaces of second and third modules, a predetermined quantity of cementitious material at least partially at a liquid state,
    • further constraining, by hardening said cementitious material placed between the reciprocal coupling surfaces, said second and third modules.


    [0031] Moreover, the process can comprise a step of engaging at least one connecting element 27 (the structure thereof can be identical to the connecting elements 8 and/or 24, for example), on one side, inside the cavity 4a of the hooking portion 4 of the first module 2 and, on the other side, inside the cavity 20a of the hooking portion 20 of the third module 18: the connecting element 27 stably constrains the first module and third modules 2, 18.

    3. Cementitious composition



    [0032] The present inventors have found that a cementitious composition comprising cement, an inert aggregate, a polymeric fiber, a superfluidifying agent and water, characterized by specific quantities of the components, by the ratio between the water quantity and cement quantity, by the quantity of the superfluidifying agent and by the granulometry of the inert aggregate, is particularly adapted to make structures of reinforced cementitious material by the 3D printing process of the present invention. Particularly, the present inventors, starting from the water/cement ratio necessary to obtain the required mechanical performance and the required setting and hardening kinetics, have optimized the consistency of the mixture by using a fluidifying agent having a specific quantity in relation with the granulometry and capable of absorbing the inert aggregate. Therefore, a further aspect of the disclosure is a cementitious composition M comprising:
    1. (i) from 15 to 30% by weight of cement with respect to the total weight of the composition,
    2. (ii) from 60 to 80% by weight of at least one inert aggregate, alone or in a mixture with one or more other inert aggregates, with respect to the total weight of the composition,
    3. (iii) from 0.02 to 0.75% by weight of at least one polymeric fiber, alone or in a mixture with one or more other polymeric fibers, with respect to the total weight of the composition,
    4. (iv) from 0.03 to 0.1% by weight of at least one superfluidifying agent, alone or in mixture with one or more other superfluidifying agents, with respect to the total weight of the composition, and
    5. (v) water in a quantity sufficient to reach 100% by weight of the composition, optionally, it can be present:
    6. (vi) from 0.1 to 2.5% by weight of at least one viscosity modifying agent with respect to the total weight of the composition, wherein:
      • the weight ratio between water and cement is comprised between 0.3 and 0.45 or the ratio between water and the equivalent cement is comprised between 0.29 and 0.49; and
      • the maximum diameter of the at least one inert aggregate is less than 12.5 mm.


    [0033] According to a further aspect of the present disclosure (cementitious composition) a suitable cement is selected among those belonging to the types I, II, III, IV and V, established by the standard EN 197-1, accepted at a national level by the standard UNI EN 197/1. According to a further aspect of the present disclosure, a suitable cement is selected among those belonging to the types I, II, III, IV and V and having strength classes 42,5R and 52,5R according to the standard UNI EN 197/1. Preferably, according to a further aspect of the present disclosure (cementitious composition), a suitable cement is selected among the cements belonging to the classes CEM II/A-L (or A-LL) 42,5R and CEM II/A-L (or A-LL) 52,5R; more preferably selected among the cements belonging to the class CEM II/A-L (or A-LL) 42,5R according to the standard UNI EN 197/1. According to a further aspect of the present disclosure (cementitious composition), said suitable cement has a maximum diameter of the particles less than or equal to 100 microns, preferably less than 50 microns, still more preferably less than 30 microns. According to a further aspect of the present disclosure, the percentage by weight of cement is preferably greater than 18%, more preferably greater than 21%; and/or is preferably less than 27%, more preferably is less than 25%; and/or is preferably comprised between 18% and 27%, more preferably is comprised between 21% and 25% with respect to the total weight of the composition.

    [0034] Optionally, part of the cement can be substituted with II type additions according to the standard UNI EN 206-1:2006, and particularly with silica fume, or fly ashes, or blast furnace slag, or pozzolana both natural and industrial, comprised between 1 and 3% by weight with respect to the total weight of the composition, preferably silica fume comprised between 1 and 3% by weight with respect to the total weight of the composition; in this case such additions of II type substitute part of the cement by a percentage comprised between 7 and 11% by weight of the cement. In such cases, instead of the "weight ratio between water and cement", it is considered the "weight ratio between water and equivalent cement" as established by the standard UNI EN 206-1: 2006, according to the following formula:

    water/equivalent cement = water/(cement + k x II type addition),

    wherein k is a parameter specific according to the type of addition.



    [0035] Therefore, the water/cement ratio of the cementitious composition of the present disclosure wherein from 7 to 11% by weight of the cement is substituted with II type additions, is comprised between 0.29 and 0.49. According to the further aspect of the present disclosure, the at least one suitable inert aggregate is selected among fine aggregates, filler and mixtures thereof; preferably the filler is selected in case of I type additions according to the standard UNI EN 12620, more preferably the filler is selected between quartz sand, siliceous sand (microsilica) and calcareous filler (calcium carbonate). Preferably, according to a further aspect of the present disclosure, the composition comprises a mixture of inert aggregates; more preferably comprises sand and quartz sand and/or calcareous filler. According to a further aspect of the present disclosure, said sand is from 90% to 95% and said filler, preferably quartz sand or calcareous filler, is from 5% to 10% with respect to the total weight of the inert aggregates. According to a further aspect of the present disclosure, preferably said sand has a maximum diameter less than 10 mm, still more preferably less than 6 mm, still more preferably less than 4 mm, according to the standard UNI 8520-1 for the compliance, and according to the standard UNI 2332 for determining the granulometric distribution. According to the further aspect of the present disclosure, preferably said filler, preferably quartz sand or calcareous filler, has a maximum diameter less than 0.25 mm, preferably less than 0.125 mm, still more preferably less than 0.063 mm according to the standard UNI 8520-1 for the compliance and according to the standard UNI 2332 for determining the granulometric distribution. According to the further aspect of the present disclosure, the percentage by weight of the at least one inert aggregate, alone or in a mixture with one or more other inert aggregates, is preferably greater than 63%, more preferably greater than 65%, and/or is preferably less than 79%, more preferably is less than 77%; and/or is preferably comprised between 63% and 79%, more preferably is comprised between 65% and 77% with respect to the total weight of the composition.

    [0036] According to the further aspect of the present disclosure, said at least one polymeric fiber is selected among polyolefinic fibers, preferably polypropylene (PP); polyvinyl alcohol (PVA); polyesters; aliphatic polyamides (Nylon); and mixtures thereof. Preferably, said at least one polymeric fiber is a polypropylene fiber (PP). Preferably, said at least one polymeric fiber, more preferably polypropylene (PP), has a diameter or a maximum size of the cross-section comprised between 0.12 and 0.8 mm, more preferably comprised between 0.25 and 0.35 mm. Preferably, said at least one polymeric fiber, more preferably polypropylene (PP), has a length less than 60 mm, more preferably comprised between 10 and 57 mm, still more preferably between 40 and 55 mm.

    [0037] According to a further aspect of the present disclosure, the percentage by weight of the at least one polymeric fiber, alone or in a mixture with one or more other polymeric fibers, is preferably greater than 0.025%, more preferably greater than 0.03%; and/or is preferably less than 0.6%, more preferably is less than 0.5%; and/or is preferably comprised between 0.025% and 0.6%, more preferably is comprised between 0.03% and 0.5% with respect to the total weight of the composition. Suitable polymeric fibers can be selected among those commercially available, for example those of the MapeFibre series marketed by Mapei, for example MapeFibre CN54 or NS12; those of the series RUREDIL marketed by RUREDIL, for example RUREDIL X FIBER 19; those of the Polifer series marketed by Polifer, for example Polifer 420. Without wishing to be bound by any explicative theory, the present inventors deem that said polymeric fibers have the function of contributing to the continuity of the flow of said composition exiting the supplying head 101, of providing the not already hardened slurry with tenacity and of decreasing the shrinkage effect of the cementitious composition. According to a further aspect of the present disclosure, said at least one superfluidifying agent is selected among polymers optionally modified polycarboxylic polyethers, naphthalene sulfonic polyethers, polyphosphonics polyethers, acrylic polyethers, and polypropylene glycols, and mixtures thereof. Preferably, said at least one superfluidifying agent is a polymer possibly a modified polycarboxylic polyether.

    [0038] According to a further aspect of the present disclosure, said at least one fluidifying agent can be present as dust or in a liquid form, for example in an aqueous solution; preferably as dust, said dust has a density comprised between 50 and 80 g/100 cm3, preferably comprised between 30 and 60 g/100 cm3. Suitable superfluidifying agents are selected among those commercially available, for example among those of the Melflux® series marketed by BASF, such as for example Melflux® 2651F, and those of the series Dynamon® marketed by Mapei. According to a further aspect of the present disclosure (cementitious composition), the percentage by weight of the at least one superfluidifying agent, alone or in a mixture with one or more other fluidifying agents, is preferably greater than 0.035%; and/or is preferably less than 0.05%; and/or is preferably comprised between 0.035% and 0.05% with respect to the total weight of the composition. According to the further aspect of the present disclosure (cementitious composition), the percentage by mass of the at least one superfluidifying agent, alone or in a mixture with one or more other fluidifying agents, is preferably greater 0.02%, more preferably greater than 0.05%; and/or is preferably less than 0.15%, more preferably is less than 0.10%; and/or is preferably comprised between 0.02% and 0.15%, more preferably is comprised between 0.05% and 0.10% with respect to the total mass of the composition. According to the further aspect of the present disclosure, the percentage by mass of the at least one superfluidifying agent, alone or in a mixture with one or more other fluidifying agents, is preferably greater than 0.1%, more preferably greater than 0.2%, still more preferably greater than 0.25%; and/or less than 0.65%, more preferably less than 0.5%, still more preferably less than 0.40%; and/or is comprised between 0.1% and 0.65%, more preferably is comprised between 0.2% and 0.5%, still more preferably is comprised between 0.25% and 0.40% with respect to the total mass of the cement. Without wishing to be bound by any explicative theory, the present inventors deem that the superfluidifying agent, added with specific quantities at the end of the mixing step in a mixer, adjusts the rheology and thixotropy of the cementitious composition. Particularly, such superfluidifying agent determines a low viscosity during the supplying step by the supplying head 101, for ensuring the printability of the cementitious composition, at the same time determines a high viscosity after the deposition of the composition in order to ensure in this way to separate the layers and support the layers successively deposited by the printing process. Moreover, the present inventors have noted that the superfluidifying dust is better distributed in the mixture and exerts the fluidifying effect in very few minutes after introducing it in the mixer (the effect is visible since it makes homogeneous and "pasty" the mixture). According to a further aspect of the present disclosure preferably the weight ratio between water and cement is comprised between 0.33 and 0.40. According to the further aspect of the present disclosure, the cementitious composition can optionally comprise: natural or synthetic fibers besides those listed at the point (iii), for example short fibers of hemp, flax, jute; aerating agents, for example the Mapeair AE series marketed by Mapei; lightened inert aggregates having a maximum diameter less than 12.5 mm, such as for example Leca expanded (structural) clays; geopolymeric binders based on metakaolin and an aqueous solution of metal hydroxides (for example sodium hydroxide), such as for example setting accelerators, such as for example the Mapequick series of Mapei; hollow glass nanospheres. In a preferred embodiment, the cementitious composition - according to the further aspect of the present disclosure - comprises:
    1. (i) from 15 to 30% by weight of cement with respect to the total weight of the composition, selected among those belonging to the types I, II, III, IV and V and having strength classes 42,5R and 52,5R according to the standard UNI EN 197/1;
    2. (ii) from 60 to 80% by weight of at least one inert aggregate, alone or in a mixture with one or more other inert aggregates, with respect to the total weight of the composition, comprising sand and quartz sand or calcareous filler;
    3. (iii) from 0.02 to 0.75% by weight of at least one polymeric fiber, alone or in a mixture with one or more other polymeric fibers, with respect to the total weight of the composition, selected among polyolefinic fibers, preferably polypropylene (PP); polyvinyl alcohol (PVA); polyesters; and aliphatic polyamides (Nylon);
    4. (iv) from 0.03 to 0.1% by weight of at least one superfluidifying agent, alone or in mixture with one or more other superfluidifying agents, with respect to the total weight of the composition, selected among polymers optionally modified polycarboxylic polyethers, naphthalene sulfonic polyethers, polyphosphonics polyethers, and acrylic polyethers.


    [0039] In a more preferred embodiment, the cementitious composition, according to the further aspect of the present disclosure, comprises:
    1. (i) from 18 to 27% by weight of cement with respect to the total weight of the composition, selected among those belonging to the types I, II, III, IV and V and having strength classes 42,5R and 52,5R according to the standard UNI EN 197/1;
    2. (ii) from 63 to 79% by weight of at least one inert aggregate, alone or in a mixture with one or more other inert aggregates, with respect to the total weight of the composition, comprising sand and quartz sand or calcareous filler;
    3. (iii) from 0.025 to 0.6% by weight of at least one polymeric fiber, alone or in a mixture with one or more other polymeric fibers, with respect to the total weight of the composition, selected among polyolefinic fibers, preferably polypropylene (PP); polyvinyl alcohol (PVA); polyesters; and aliphatic polyamides (Nylon);
    4. (iv) from 0.035 to 0.05% by weight of at least one superfluidifying agent, alone or in a mixture with one or more other superfluidifying agents, with respect to the total weight of the composition, selected among polymers optionally modified polycarboxylic polyethers, naphthalene sulfonic polyethers, polyphosphonics polyethers, and acrylic polyethers.


    [0040] In a still more preferred embodiment, the cementitious composition comprises:
    1. (i) from 21 to 25% by weight of cement with respect to the total weight of the composition, selected among those belonging to the types I, II, III, IV and V and having strength classes 42,5R and 52,5R according to the standard UNI EN 197/1;
    2. (ii) from 65 to 77% by weight of at least one inert aggregate, alone or in a mixture with one or more other inert aggregates, with respect to the total weight of the composition, comprising sand and quartz sand;
    3. (iii) from 0.03 to 0.5% by weight of at least one polymeric fiber, alone or in a mixture with one or more other polymeric fibers, with respect to the total weight of the composition, selected among polyolefinic fibers, preferably polypropylene (PP); polyvinyl alcohol (PVA); polyesters; and aliphatic polyamides (Nylon); preferably polypropylene (PP) fibers;
    4. (iv) from 0.035 to 0.05% wt. of at least one superfluidifying agent, alone or in a mixture with one or more other superfluidifying agents, with respect to the total weight of the composition, selected among polymers optionally modified polycarboxylic polyethers, naphthalene sulfonic polyethers, polyphosphonics polyethers, and acrylic polyethers; preferably modified polycarboxylic polyether polymers. As an alternative, the cementitious composition of the present disclosure can be defined based on the quantity expressed by kg of the components from (i) to (v) present in a cubic meter of said composition. The cementitious composition of the present disclosure comprises:
      1. (i) from 300 to 650 kg of cement per cubic meter of the composition,
      2. (ii) from 1,000 to 2,000 kg of at least one inert aggregate per cubic meter of the composition,
      3. (iii) from 0.5 to 2 kg of at least one polymeric fiber per cubic meter of the composition,
      4. (iv) from 0.5 to 2.8 kg of at least one superfluidifying agent per cubic meter of the composition,
      5. (v) from 100 to 200 liters of water per cubic meter of the composition.


    [0041] The cementitious composition, according to the present disclosure, falls into a consistency class S1. De facto, said composition in a green state, has a value of the Abrams cone slump test (SLUMP), measured according to the standard EN 12350-2:2009, comprised between 10 and 40 mm, preferably comprised between 30 and 40 mm. The cementitious composition according to the present disclosure, hardened after curing for 28 days, has an average cubic strength value Rcm and an average cylindrical strength fcm, measured according to the standard EN 12390, comprised respectively between 50 and 60 MPa and between 40 and 48 MPa. A further aspect of the present disclosure comprises a method of preparing the cementitious composition according to the present disclosure, comprising:
    1. a) mixing the at least one inert aggregate (i) with the cement (ii),
    2. b) adding water to the obtained mixture and mixing in order to form a slurry,
    3. c) adding to the obtained slurry the at least one polymeric fiber (iii) and mixing,
    4. d) adding the at least one fluidifying agent (iv) and mixing.


    [0042] According to a further aspect of the present disclosure (method of preparing the cementitious composition), a suitable cement is selected among those belonging to the types I, II, III, IV and V, established by the standard EN 197-1, accepted at a national level by the standard UNI EN 197/1.

    [0043] According to a further aspect of the present disclosure, a suitable cement is selected among those belonging to the types I, II, III, IV and V and having strength classes 42, 5R and 52,5R according to the standard UNI EN 197/1. Preferably, according to the further aspect of the present disclosure, (cementitious composition), a suitable cement is selected among those cements belonging to the classes CEM II/A-L (or A-LL) 42,5R and CEM II/A-L (or A-LL) 52,5R; more preferably selected among the cements belonging to the class CEM II/A-L (or A-LL) 42,5R according to the standard UNI EN 197/1. Said suitable cement has a maximum diameter of the particles less than or equal to 100 microns, preferably less than 50 microns, still more preferably less than 30 microns. According to the method of preparing the composition according to the present disclosure the at least one suitable inert aggregate is selected among sand, filler and mixtures thereof, preferably the filler is selected in the family of the I-type additives according to the standard UNI EN 12620, more preferably the filler is selected among quartz sand, silica sand (microsilica), and calcareous filler. According to the method of preparing the composition according to the present disclosure, said sand has a maximum diameter less than 12.5 mm, preferably less than 10 mm, still more preferably less than 6 mm, still more preferably less than 4 mm, according to the standard UNI 8520-1 for the compliance and according to the standard UNI 2332 for determining the granulometric distribution. According to the method of preparing the composition according to the present disclosure, said filler, preferably quartz sand or calcareous filler, has a maximum diameter less than 0.25 mm, preferably less than 0.125 mm, still more preferably less than 0.063 mm, according to the standard UNI 8520-1 for the compliance and according to the standard UNI 2332 for determining the granulometric distribution. According to the method of preparing the composition according to the present disclosure, said at least one polymeric fiber is selected among polyolefinic fibers, preferably polypropylene (PP), polyvinyl alcohol (PVA); polyesters; aliphatic polyamides (Nylon); and mixtures thereof. Preferably, said at least one polymeric fiber is a polypropylene (PP) fiber. Preferably, said at least one polymeric fiber, more preferably a polypropylene (PP) fiber, has a diameter or a maximum dimension of the cross-section comprised between 0.12 and 0.8 mm, more preferably comprised between 0.25 and 0.35 mm. Preferably, said at least one polymeric fiber, more preferably polypropylene (PP), has a length less than 60 mm, more preferably comprised between 10 and 57 mm, still more preferably between 40 and 55 mm.

    [0044] According to the method of preparing the composition in agreement with the present disclosure, said at least one superfluidifying agent is selected among polymers optionally modified polycarboxylic polyethers, naphthalene sulfonic polyethers, polyphosphonic polyethers, acrylic polyethers, polypropylene glycols and mixtures thereof. Preferably, said at least one superfluidifying agent is a polymer possibly a modified polycarboxylic polyether. According to the method of preparing the composition in agreement with the present disclosure, the mixing steps from a) to d) are performed at a speed comprised between 20 and 60 rounds per minute, more preferably between 30 and 50 rounds per minute. According to the method of preparing the composition in agreement with the present disclosure, the mixing step a) and c) is extended for a time comprised between 10 seconds and 10 minutes, preferably between 1 minute and 7 minutes, more preferably between 2 minutes and 5 minutes. According to the method of preparing the composition in agreement with the present disclosure, the mixing step b) is extended for a time comprised between 10 seconds and 10 minutes, preferably between 1 minute and 7 minutes, more preferably between 2 minutes and 5 minutes in which all the quantity of water is added; after adding water, the mixing step is extended for a time comprised between 10 seconds and 15 minutes, preferably between 1 minute and 10 minutes, more preferably between 2 minutes and 7 minutes. According to the method of preparing the composition in agreement with the present disclosure, the mixing step d) is extended for a time comprised from 20 seconds to 20 minutes, preferably between 1 minute and 15 minutes, more preferably between 2 minutes and 13 minutes.

    [0045] In a further aspect of the present disclosure, it is provided an use of the cementitious composition according to the invention for 3D printing modules/structures of reinforced cementitious material.

    3.1 EXPERIMENTAL SECTION


    EXAMPLE 1



    [0046] 40 liters of a cementitious composition are prepared. In the step a), about 57.2 kg of sands (maximum diameter: 2 mm) and about 3.98 kg of quartz sand (maximum diameter: 0.125 mm) corresponding respectively to 1,431 kg and 99.5 kg per cubic meter of the final cementitious composition, are introduced into a cylindrical type electric mixer having a maximum capacity of 140 liters, beforehand wetted to saturation. Subsequently, about 19.9 kg of CEM II/A-LL 42.5 R corresponding to 498 kg per cubic meter of the final cementitious composition are added into the mixer, and then the dry powders are mixed for about 3 minutes, at a rotation speed of the mixer of about 40 rounds per minute. In the step b) water is gradually added, for a total of about 7 liters corresponding to 176.5 liters per cubic meter of the final cementitious composition, by mixing for a time corresponding to the addition of all the water quantity, corresponding to about 3 minutes at a rotation speed of the mixer of about 40 rounds per minute; then, the mixing step is extended for about other 5 minutes under the above given same rotation speed conditions of the mixer. In the step 5), polypropylene fibers (MapeFibre CN54, marketed by Mapei) in a quantity of 0.04 kg, corresponding to 1 kg per cubic meter of the final cementitious composition, are added and are mixed for approximately 3 minutes, at a mixer rotation speed of about 40 rounds per minute. In the step d), a quantity of 0.069 kg corresponding to 1.74 kg per cubic meter of the final cementitious composition, of the superfluidifying additive based on a modified polycarboxylic polyether (Melflux® 2651F marketed by BASF) is gradually added (1/3 + 1/3 + 1/3), and is mixed for further 5-10 minutes.

    EXAMPLE 2



    [0047] Determining the consistency class of the cementitious composition prepared as described in the example 1 in a green state, measured according to the standard EN 12350-2:2009. The consistency class was measured by the Abrams cone, consisting of a cone made of galvanized steel or stainless steel having a thickness of about 1.5 mm and having a frustoconical shape with the following internal dimensions:
    • diameter of the lower base: 200 ± 2 mm;
    • diameter of the upper base: 100 ± 2 mm;
    • height: 300 ± 2 mm.


    [0048] The composition described in the example 1 in a green state (before being inserted in the printer) was quickly introduced and completely packed in the frustoconical container by following the suggestions of the cited standard. Immediately after removing the mould, the slump of the cone S was measured by the difference between the nominal height of the mould (hm = 300 mm) and the height of the tallest point of the sample hs, by an approximation to the nearest 10 mm. The slum of the Abrams cone of the cementitious composition of the invention in a green state, was 34 mm, in other words said cementitious composition falls into the consistency class S1.

    EXAMPLE 3



    [0049] Determining the average cubic strength value Rcm and the average cylindrical strength value fcm of the cementitious composition prepared as described in the example 1, hardened after maturing for 28 days, measured according to the standard EN 12390. The average cubic strength Rcm and the average cylindrical strength fcm under an uniaxial compression (by controlling the force) were measured on normalized specimens and therefore respectively on 4 cubic samples having a side of 150 mm and on 4 cylindrical samples having a diameter of 150 mm and a height of 300 mm. The average strength Rcm of the cementitious composition of the invention hardened after curing it for 28 days, is of 53.5 MPa; the average strength fcm of the hardened cementitious composition itself after curing it for 28 days, is of 44.4 MPa. By the data given in the examples 2 and 3, it was found that the cementitious composition in a green state, exhibits an optimal consistency, consequently such cementitious composition exhibits an optimal capacity of being supplied through the supplying head 101 and of remaining separated in layers and supporting the gradually printed layers. Moreover, such hardened cementitious composition has an optimal capacity of opposing to the compression, therefore is capable of compensating possible weaknesses of the connecting points between adjacent layers.

    EXAMPLE 4



    [0050] Determining the average compression strength value fcpm of hollow cylindrical construction elements obtained by 3D-printing the cementitious composition prepared as described in the example 1 and hardened after curing it for 28 days. The cementitious composition was used for preparing three construction elements C1, C2 and C3, by the above described 3D-printing process of the present invention. Such construction elements are hollow cylinders, having a height of 200 mm, and average thickness of the walls of about 50 mm and being formed by 10 layers. The obtained thickness of the walls corresponds to a single layer of the material printed with the above described cementitious composition. The average outer (Dext, ave) and inner diameters (Dint, ave) measured in mm of the three hollow cylinders, and also the average area (Aave) of the cross-section measured in mm2 from these latter, the average area (Aeff) of the effective transversal cross-section measured in mm2 from the effective width of the transversal cross-section (Seff, see Figure 19) obtained by sectioning the specimens after the test, the recorded maximum force (or load) (Fmax) measured in kN, the compression resistance calculated on the average area of the transversal cross-section (fcp), measured in MPa, the average compression strength calculated on the average area of the cross-section (fcpm) measured in MPa of the three construction elements C1, C2, and C3, the compression strength calculated on the average area of the effective cross-section (fcp_eff) measured in MPa, the average compression strength calculated on the average area of the effective cross-section (fcpm_eff) measured in MPA of the three construction elements C1, C2 and C3 are given in table 1.
    Table 1
    SampleDext, ave mmDint, ave mmAave mm2Aeff mm2Fmax kNfcp MPafcpm MPafcp_eff MPafcpm_eff MPa
    C1 218 160 17039 11618 594 34.9   51.1  
    C2 218 165 15763 10464 545 34.6 37.2 52.1 52.9
    C3 218 173 13776 10440 579 42.0 55.4


    [0051] The average compression strength, if calculated on the average surface of the cross-section (fcpm) of the three tested construction elements C1, C2 and C3, is 16% less than the average cylindrical strength fcm of the cementitious composition used for 3D-printing the construction element (37.2 MPa vs 44.4 MPa). The correct calculation performed by considering the effective area of the cross-section, in other words by considering only the net surface in contact with the layers (determined by the segment S_eff shown in the cross-section view of the cylindrical specimen of Figure 19), gives results entirely corresponding to the ones regarding the average cubic strength Rcm of the cementitious composition used for 3D-printing the construction element (52.9 MPa vs. 3.5 MPa). From the data of the example 4, it was found that the material in its printed shape, holds its compression strength capability shown in the "bulk" condition of the cubic specimens.

    EXAMPLE 5



    [0052] Determining the flexural rigidity value of a three-dimensional structure obtained by 3D-printing the cementitious composition prepared as described in the example 1.

    [0053] The cementitious composition was used for preparing, from a determined 2D profile, a three-dimensional structure (INV) long 3.20 m having an overall rectangular cross-section with a width of 0.20 m and a height of 0.40 m, formed by 7 modules, made by the 3D-printing process of the present invention, as shown in Figure 1. The total weight of the three-dimensional structure (INV) was of 2.9 kN, corresponding to q = 0.9 kN/m of the distributed weight. The weight of the three-dimensional structure (INV) corresponds to 45% of the weight of the equivalent solid structure (RIF), the cross-section thereof has the same dimensions, in other words 0.20 m and 0.40 m, and the same longitudinal steel reinforcement, in other words two bars with a diameter of 10 mm and a cover of 40 mm. The flexural rigidity of both structures (INV) and (RIF) was calculated for understanding the possibilities of this technology of designing and printing a beam obtained by modules having a particular shape, as shown in Figure 1. Particularly, the deflection f (or transversal displacement of the axis) of the beam of the structure (INV) was measured at the midline cross-section of the same, under the effect of the own load of the structure abutting on two ends. The measurement was performed by a decimal comparator. The equivalent flexural rigidity (E/eq) of the structure of the invention (INV) was determined by the classic elastic theory of the continuous (solid) beams with rectilinear axis by the following known relationships between the deflection and load applied to the beam (for beams constrained by supports at the ends):

    wherein the value of the (own) load of the beam q and the length thereof I, and the measure deflection f are known; wherein EI is the flexural rigidity, in other words E represents the Young module of the material, and I represents the moment of inertia of the cross-section.

    [0054] Table 2 shows the flexural rigidity values EI of the three-dimensional structure of the invention (INV) and of said equivalent solid structure (RIF) when is uncracked (RIF1, the percentage of cracks is less than 50%) and when is cracked (RIF2, the percentage of cracks is greater than 60%).
    Table 2
    StructureEI N/mm2
    INV 1.20 ∗ 1013
    RIF1 2, 6 ∗ 1013
    RIF2 0.13∗1013


    [0055] The flexural rigidity value of the structure of the invention is intermediate between the one of the solid uncracked structure (RIF1) and of the cracked one (RIF2), this latter was evaluated according to the "Norme Tecniche per le Costruzioni (NTC2008)".

    [0056] From the data shown in the example 5, it was found that, despite the cavities present in the modules printed according to the process of the invention and the smaller quantities of cementitious material present in the structure of the invention could determine a too high deformability of the structure, the present inventors have surprisingly found that the deformability of such structure amounts to acceptable values. This is an interesting result because enables to better exploit the possibilities of the 3D printing for designing shapes which are, at the same time, structurally efficient and characterized by a low use of cementitious material.

    [0057] Finally, the cementitious composition, characterized by the specific quantity of components from (i) to (v), particularly characterized by the ratio between the water quantity and cement quantity, by the quantity of superfluidifying agents and by the granulometry of the inert aggregates, is particularly suitable for making structures of reinforced cementitious material obtained by the 3D printing process of the present invention.


    Claims

    1. Process of making a structure (1) of reinforced cementitious material, said process comprising at least the following steps:

    - making, by a three-dimensional printing process, a plurality of modules of cementitious material, said three-dimensional printing process comprising a step of depositing a plurality of layers (L) of cementitious material one on the other according to a stratification direction (D), said plurality of modules comprising:

    o at least one first module (2) comprising at least one lateral wall (3) delimited by an outer surface (3a) and extending along the stratification direction (D), at least part of said outer lateral surface (3a) of the first module (2) defining a reciprocal coupling surface (3b), said first module (2) further comprising at least one hooking portion (4) defining at least one cavity (4a) extending at least partially along the stratification direction (D),

    o at least one second module (5) comprising at least one lateral wall (6) delimited by an outer surface (6a) and extending along the stratification direction (D), at least part of the outer surface (6a) of the second module (5) defining a reciprocal coupling surface (6b) countershaped to the reciprocal coupling surface (3b) of the outer surface (3a) of the first module (2), said second module (5) further comprising at least one hooking portion (7) defining at least one cavity (7a) extending at least partially along the stratification direction (D),

    - bringing in contact the first and second modules (2, 5) so that the respective coupling reciprocal surfaces (3b, 6b) of said modules abut on each other,

    - following the step of contacting the first and second modules, engaging at least one connecting element (8), on one side, inside the cavity (4a) of the hooking portion (4) of the first module (2) and, on the other side, inside the cavity (7a) of the hooking portion (7) of the second module (5), said connecting element (8) stably constraining the first and second modules (2, 5) and being configured for holding these latter in contact with each other.


     
    2. Process according to the preceding claim, wherein the connecting element (8) comprises at least one reinforcing bar, optionally of metal material, extending along a longitudinal development direction between a first and second end portions (8a, 8b),
    said connecting element (8) comprising - at the first end portion (8a) - a first engagement portion (9) emerging from the reinforcing bar transversally to the longitudinal development direction of the same, said connecting element (8) further comprising - at the second end portion (8b) - a second engagement portion (10) emerging from the reinforcing bar transversally to the longitudinal development direction of the same,
    and wherein the step of engaging the connecting element (8) to the first and second modules (2, 5) comprises at least the following sub-steps:

    - stably engaging the first engagement portion (9) inside the cavity (4a) of the hooking portion (4) of the first module (2),

    - stably engaging the second engagement portion (10) inside the cavity (7a) of the hooking portion (7) of the second module (5).


     
    3. Process according to the preceding claim, wherein the step of engaging the first engagement portion (9) to the first module (2) comprises at least the following sub-steps:

    - inserting the first engagement portion (9) inside the cavity (4a) of the hooking portion (4) of the first module (2),

    - filling at least partially the cavity (4a) of the hooking portion (4) of the first module (2) with a cementitious material at least partially at a liquid state so that this latter can contact at least part of said first engagement portion (9),

    - constraining, by hardening the cementitious material inside the cavity (4a) of the first module (2), said first engagement portion (9),

    and wherein the step of engaging the second engagement portion (10) to the second module (5) comprises at least the following sub-steps:

    - inserting the second engagement portion (10) inside the cavity (7a) of the hooking portion (7) of the second module (5),

    - filling at least partially the cavity (7a) of the hooking portion (7) of the second module (5) with a cementitious material at least partially at a liquid state so that this latter can contact at least part of said second engagement portion (10),

    - constraining, by hardening the cementitious material inside the cavity (7a) of the second module (5), said second engagement portion (10).


     
    4. Process according to claim 2 or 3, wherein the first and second engagement portions of the connecting element (8) are distinct and removably associable to the reinforcing bar,
    the process comprises the step of engaging the first and second engagement portions (9, 10) in the first and second modules respectively and after, a step of constraining the reinforcing bar to said first and second engagement portions (9, 10).
     
    5. Process according to anyone of the preceding claims, wherein the step of depositing, by a three-dimensional printing process, the plurality of layers (L) of cementitious material one on the other according to the stratification direction (D), comprises a superimposing of layers (L) exhibiting substantially the same shape and size,
    each module exhibiting, according to the stratification direction (D), a substantially constant cross-section for essentially defining a profile.
     
    6. Structure (1) of reinforced cementitious material, preferably obtained by the process according to anyone of the preceding claims, said structure comprising:

    - a plurality of modules of cementitious material comprising:

    o at least one first module (2) comprising at least one lateral wall (3) delimited by an outer surface (3a) and extending along a stratification direction (D), at least part of said outer lateral surface (3a) of the first module (2) defining a reciprocal coupling surface (3b), said first module (2) further comprising at least one hooking portion (4) defining at least one cavity (4a) extending at least partially along the stratification direction (D),

    o at least one second module (5) comprising at least one lateral wall (6) delimited by an outer surface (6a) and extending along the stratification direction (D), at least part of the outer surface (6a) of the second module (5) defining a reciprocal coupling surface (6b) countershaped and in contact with the reciprocal coupling surface (3b) of the outer surface (3a) of the first module (2), said second module (5) further comprising at least one hooking portion (7) defining at least one cavity (7a) extending at least partially along the stratification direction (D),

    - at least one connecting element (8) engaged, on one side, inside the cavity (4a) of the hooking portion (4) of the first module (2) and, on the other side, inside the cavity (7a) of the hooking portion (7) of the second module (5), said connecting element (8) being configured for stably constraining the first and second modules (2, 5) and holding these latter in contact with each other.


     
    7. Structure according to the preceding claim, wherein the connecting element (8) comprises at least one reinforcing bar, optionally of metal material, extending along a longitudinal development direction between a first and second end portions (8a, 8b),
    said connecting element (8) comprising - at the first end portion (8a) - a first engagement portion (9) emerging from the reinforcing bar transversally to the longitudinal development direction of the same and engaged inside the cavity (4a) of the hooking portion (4) of the first module (2),
    said connecting element (8) further comprising - at the second end portion (8b) - a second engagement portion (10) emerging from the reinforcing bar transversally to the longitudinal development direction of the same and engaged inside the cavity (7a) of the hooking portion (7) of the second module (2).
     
    8. Structure according to the preceding claim, wherein the first and second engagement portions (9, 10) of the connecting element (8) are distinct and removably associable to the reinforcing bar.
     
    9. Structure according to anyone of the claims from 6 to 8, wherein each module exhibiting, according to the stratification direction (D), a substantially constant cross-section for defining essentially a profile.
     
    10. Structure according to anyone of claims from 6 to 9, wherein the lateral wall (3) of the first module (2) defines a closed outer perimeter, particularly having a polygonal shape,
    wherein the lateral wall (6) of the second module (5) defines an outer closed perimeter, particularly having a polygonal shape,
    wherein the hooking portion (4) of said first module (2) is defined inside said closed outer perimeter, optionally said hooking portion (4) extends for all a development of the first module (2) along the stratification direction (D),
    wherein the hooking portion (7) of said second module (5) is defined inside said outer closed perimeter, optionally said hooking portion (7) extends for all a development of the second module (7) along the stratification direction (D).
     
    11. Structure according to anyone of claims from 6 to 10, wherein the first module (2) is hollow and exhibits an outer closed perimeter, the first module (2) comprising, inside the outer closed perimeter, a reinforcing portion (11) extending inside the outer closed perimeter between two sides substantially opposite to each other,
    wherein the second module (5) is hollow and exhibits an outer closed perimeter, the second module (5) comprising, inside the outer closed perimeter, a reinforcing portion (14) extending inside the outer closed perimeter between two sides substantially opposite to each other.
     


    Ansprüche

    1. Verfahren eines Herstellens einer Struktur (1) von verstärktem Zementmaterial, wobei das Verfahren wenigstens die folgenden Schritte umfasst:

    - Herstellen einer Mehrzahl von Modulen von Zementmaterial durch ein dreidimensionales Druckverfahren, wobei das dreidimensionale Druckverfahren einen Schritt eines Anordnens einer Mehrzahl von Schichten (L) von Zementmaterial eine auf der anderen gemäß einer Schichtungsrichtung (D) umfasst, wobei die Mehrzahl von Modulen umfasst:

    - wenigstens ein erstes Modul (2), welches wenigstens eine laterale Wand (3) umfasst, welche durch eine äußere Fläche (3a) begrenzt ist und sich entlang der Schichtungsrichtung (D) erstreckt, wobei wenigstens ein Teil der äußeren lateralen Fläche (3a) des ersten Moduls (2) eine reziproke Kopplungsfläche (3b) definiert, wobei das erste Modul (2) ferner wenigstens einen Hakenabschnitt (4) umfasst, welcher wenigstens einen Hohlraum (4a) definiert, welcher sich wenigstens teilweise entlang der Schichtungsrichtung (D) erstreckt,

    - wenigstens ein zweites Modul (5), welches wenigstens eine laterale Wand (6) umfasst, welche durch eine äußere Fläche (6a) begrenzt ist und sich entlang der Schichtungsrichtung (D) erstreckt, wobei wenigstens ein Teil der äußeren Fläche (6a) des zweiten Moduls (5) eine reziproke Kopplungsfläche (6b) definiert, welche zu der reziproken Kopplungsfläche (3b) der äußeren Fläche (3a) des ersten Moduls (2) gegenförmig ist, wobei das zweite Modul (5) ferner wenigstens einen Hakenabschnitt (7) umfasst, welcher wenigstens einen Hohlraum (7a) definiert, welcher sich wenigstens teilweise entlang der Schichtungsrichtung (D) erstreckt,

    - In Kontakt bringen der ersten und zweiten Module (2, 5), so dass die entsprechenden reziproken Kopplungsflächen (3b, 6b) der Module gegeneinander anliegen,

    - dem Schritt eines Kontaktierens der ersten und zweiten Module folgend, Eingreifen wenigstens eines Verbindungselements (8) an einer Seite innerhalb des Hohlraums (4a) des Hakenabschnitts (4) des ersten Moduls (2) und an der anderen Seite innerhalb des Hohlraums (7a) des Hakenabschnitts (7) des zweiten Moduls (5), wobei das Verbindungselement (8) die ersten und zweiten Module (2, 5) stabil begrenzt und dazu eingerichtet ist, diese letzteren miteinander in Kontakt zu halten.


     
    2. Verfahren nach dem vorhergehenden Anspruch, wobei das Verbindungselement (8) wenigstens eine Verstärkungsstange, optional aus einem Metall-Material, umfasst, welche sich entlang einer longitudinalen Entwicklungsrichtung zwischen einem ersten und einem zweiten Endabschnitt (8a, 8b) erstreckt,
    wobei das Verbindungselement (8) - an dem ersten Endabschnitt (8a)

    - einen ersten Eingriffsabschnitt (9) umfasst, welcher sich von der Verstärkungsstange transversal zu der longitudinalen Entwicklungsrichtung derselben erhebt, wobei das Verbindungselement (8) ferner - an dem zweiten Endabschnitt (8b) - einen zweiten Eingriffsabschnitt (10) umfasst, welcher sich von der Verstärkungsstange transversal zu der longitudinalen Entwicklungsrichtung derselben erhebt,

    und wobei der Schritt eines Eingreifens des Verbindungselements (8) mit den ersten und zweiten Modulen (2, 5) wenigstens die folgenden Unterschritte umfasst:

    - stabiles Eingreifen des ersten Eingriffsabschnitts (9) innerhalb des Hohlraums (4a) des Hakenabschnitts (4) des ersten Moduls (2),

    - stabiles Eingreifen des zweiten Eingriffsabschnitts (10) innerhalb des Hohlraums (7a) des Hakenabschnitts (7) des zweiten Moduls (5).


     
    3. Verfahren nach dem vorhergehenden Anspruch, wobei der Schritt eines Eingreifens des ersten Eingriffsabschnitts (9) mit dem ersten Modul (2) wenigstens die folgenden Unterschritte umfasst:

    - Einsetzen des ersten Eingriffsabschnitts (9) innerhalb des Hohlraums (4a) des Hakenabschnitts (4) des ersten Moduls (2),

    - Füllen des Hohlraums (4a) des Hakenabschnitts (4) des ersten Moduls (2) wenigstens teilweise mit einem Zementmaterial wenigstens teilweise zu einem Flüssigzustand, so dass dieses letztere wenigstens einen Teil des ersten Eingriffsabschnitts (9) kontaktieren kann,

    - Begrenzen des ersten Eingriffsabschnitts durch Aushärten des Zementmaterials innerhalb des Hohlraums (4a) des ersten Moduls (2), und wobei der Schritt des Eingreifens des zweiten Eingriffsabschnitts (10) mit dem zweiten Modul (5) wenigstens die folgenden Unterschritte umfasst:

    - Einsetzen des zweiten Eingriffsabschnitts (10) innerhalb des Hohlraums (7a) des Hakenabschnitts (7) des zweiten Moduls (5),

    - Füllen des Hohlraums (7a) des Hakenabschnitts (7) des zweiten Moduls (5) wenigstens teilweise mit einem Zementmaterial wenigstens teilweise zu einem Flüssigzustand, so dass dieses letztere wenigstens einen Teil des zweiten Eingriffsabschnitts (10) kontaktieren kann,

    - Begrenzen des zweiten Eingriffsabschnitts (10) durch Aushärten des Zementmaterials innerhalb des Hohlraums (7a) des zweiten Moduls (5).


     
    4. Verfahren nach Anspruch 2 oder 3, wobei die ersten und zweiten Eingriffsabschnitte des Verbindungselements (8) verschieden sind und der Verstärkungsstange lösbar zuordenbar sind,
    wobei das Verfahren den Schritt eines Eingreifens der ersten und zweiten Eingriffsabschnitte (9, 10) in dem ersten bzw. dem zweiten Modul und nach einem Schritt eines Begrenzens der Verstärkungsstange auf die ersten und zweiten Eingriffsabschnitte (9, 10) umfasst.
     
    5. Verfahren nach einem der vorhergehenden Ansprüche, wobei der Schritt des Anordnens der Mehrzahl von Schichten (L) von Zementmaterial eine auf der anderen gemäß der Schichtungsrichtung (D) durch ein dreidimensionales Druckverfahren ein Überlagern von Schichten (L) umfasst, welche im Wesentlichen die gleiche Form und Größe aufweisen,
    wobei jedes Modul gemäß der Schichtungsrichtung (D) einen im Wesentlichen konstanten Querschnitt aufweist, um ein Profil essenziell zu definieren.
     
    6. Struktur (1) eines verstärkten Zementmaterials, welches vorzugsweise durch das Verfahren nach einem der vorhergehenden Ansprüche erhalten wird, wobei die Struktur umfasst:

    - eine Mehrzahl von Modulen von Zementmaterial, umfassend:

    - wenigstens ein erstes Modul (2), welches wenigstens eine laterale Wand (3) umfasst, welche durch eine äußere Fläche (3a) begrenzt ist und sich entlang der Schichtungsrichtung (D) erstreckt, wobei wenigstens ein Teil der äußeren lateralen Fläche (3a) des ersten Moduls (2) eine reziproke Kopplungsfläche (3b) definiert, wobei das erste Modul (2) ferner wenigstens einen Hakenabschnitt (4) umfasst, welcher wenigstens einen Hohlraum (4a) definiert, welcher sich wenigstens teilweise entlang der Schichtungsrichtung (D) erstreckt,

    - wenigstens ein zweites Modul (5), welches wenigstens eine laterale Wand (6) umfasst, welche durch eine äußere Fläche (6a) begrenzt ist und sich entlang der Schichtungsrichtung (D) erstreckt, wobei wenigstens ein Teil der äußeren Fläche (6a) des zweiten Moduls (5) eine reziproke Kopplungsfläche (6b) definiert, welche zu der reziproken Kopplungsfläche (3b) der äußeren Fläche (3a) des ersten Moduls (2) gegenförmig ist, wobei das zweite Modul (5) ferner wenigstens einen Hakenabschnitt (7) umfasst, welcher wenigstens einen Hohlraum (7a) definiert, welcher sich wenigstens teilweise entlang der Schichtungsrichtung (D) erstreckt,

    - wenigstens ein Verbindungselement (8), welches an einer Seite innerhalb des Hohlraums (4a) des Hakenabschnitts (4) des ersten Moduls (2) und an der anderen Seite innerhalb des Hohlraums (7a) des Hakenabschnitts (7) des zweiten Moduls (5) eingegriffen ist, wobei das Verbindungselement (8) dazu eingerichtet ist, die ersten und zweiten Module (2, 5) stabil zu begrenzen und diese letzteren miteinander in Kontakt zu halten.


     
    7. Struktur nach dem vorhergehenden Anspruch, wobei das Verbindungselement (8) wenigstens eine Verstärkungsstange, optional aus einem Metall-Material, umfasst, welche sich entlang einer longitudinalen Entwicklungsrichtung zwischen einem ersten und einem zweiten Endabschnitt (8a, 8b) erstreckt,
    wobei das Verbindungselement (8) - an dem ersten Endabschnitt (8a)

    - einen ersten Eingriffsabschnitt (9) umfasst, welcher sich von der Verstärkungsstange transversal zu der longitudinalen Entwicklungsrichtung derselben erhebt innerhalb des Hohlraums (4a) des Hakenabschnitts (4) des ersten Moduls (2) eingegriffen ist, wobei das Verbindungselement (8) ferner - an dem zweiten Endabschnitt (8b)

    - einen zweiten Eingriffsabschnitt (10) umfasst, welcher sich von der Verstärkungsstange transversal zu der longitudinalen Entwicklungsrichtung derselben erhebt und innerhalb des Hohlraums (7a) des Hakenabschnitts (7) des zweiten Moduls (2) eingegriffen ist.


     
    8. Struktur nach dem vorhergehenden Anspruch, wobei die ersten und zweiten Eingriffsabschnitte (9, 10) des Verbindungselements (8) verschieden sind und der Verstärkungsstange lösbar zuordenbar sind.
     
    9. Struktur nach einem der Ansprüche 6 bis 8, wobei jedes Modul gemäß der Schichtungsrichtung (D) einen im Wesentlichen konstanten Querschnitt aufweist, um ein Profil essenziell zu definieren.
     
    10. Struktur nach einem der Ansprüche 6 bis 9, wobei die laterale Wand (3) des ersten Moduls (2) einen geschlossenen äußeren Umfang definiert, welcher insbesondere eine polygone Form aufweist,
    wobei die laterale Wand (6) des zweiten Moduls (5) einen äußeren geschlossenen Umfang definiert, welcher insbesondere eine polygone Form aufweist,
    wobei der Hakenabschnitt (4) des ersten Moduls (2) innerhalb des geschlossenen äußeren Umfangs definiert ist, wobei sich optional der Hakenabschnitt (4) über eine gesamte Entwicklung des ersten Moduls (2) entlang der Schichtungsrichtung (D) erstreckt,
    wobei der Hakenabschnitt (7) des zweiten Moduls (5) innerhalb des äußeren geschlossenen Umfangs definiert ist, wobei sich optional der Hakenabschnitt (7) über eine gesamte Entwicklung des zweiten Moduls (7) entlang der Schichtungsrichtung (D) erstreckt.
     
    11. Struktur nach einem der Ansprüche 6 bis 10, wobei das erste Modul (2) hohl ist und einen äußeren geschlossenen Umfang aufweist, wobei das erste Modul (2) innerhalb des äußeren geschlossenen Umfangs einen Verstärkungsabschnitt (11) umfasst, welcher sich innerhalb des äußeren geschlossenen Umfangs zwischen zwei Seiten erstreckt, welche einander im Wesentlichen entgegengesetzt sind,
    wobei das zweite Modul (5) hohl ist und einen äußeren geschlossenen Umfang aufweist, wobei das zweite Modul (5) innerhalb des äußeren geschlossenen Umfangs einen Verstärkungsabschnitt (14) umfasst, welcher sich innerhalb des äußeren geschlossenen Umfangs zwischen zwei Seiten erstreckt, welche einander im Wesentlichen entgegengesetzt sind.
     


    Revendications

    1. Procédé de fabrication d'une structure (1) de matériau cimentaire renforcé, ledit procédé comprenant au moins les étapes suivantes :

    - fabrication, par un procédé d'impression tridimensionnelle, d'une pluralité de modules de matériau cimentaire, ledit procédé d'impression tridimensionnelle comprenant une étape de dépôt d'une pluralité de couches (L) de matériau cimentaire l'une sur l'autre selon un sens de stratification (D), ladite pluralité de modules comprenant :

    o au moins un premier module (2) comprenant au moins une paroi latérale (3) délimitée par une surface externe (3a) et s'étendant le long du sens de stratification (D), au moins une partie de ladite surface latérale externe (3a) du premier module (2) définissant une surface d'accouplement réciproque (3b), ledit premier module (2) comprenant en outre au moins une partie en crochet (4) définissant au moins une cavité (4a) s'étendant au moins partiellement le long du sens de stratification (D),

    o au moins un second module (5) comprenant au moins une paroi latérale (6) délimitée par une surface externe (6a) et s'étendant le long du sens de stratification (D), au moins une partie de la surface externe (6a) du second module (5) définissant une surface d'accouplement réciproque (6b) en contre-forme par rapport à la surface d'accouplement réciproque (3b) de la surface externe (3a) du premier module (2), ledit second module (5) comprenant en outre au moins une partie en crochet (7) définissant au moins une cavité (7a) s'étendant au moins partiellement le long du sens de stratification (D),

    - mise en contact du premier et du second module (2, 5) de sorte que les surfaces réciproques respectives d'accouplement (3b, 6b) desdits modules viennent en butée l'une contre l'autre,

    - suivie de l'étape de mise en contact du premier et du second module, engageant au moins un élément de connexion (8), sur un côté, à l'intérieur de la cavité (4a) de la partie en crochet (4) du premier module (2) et, sur l'autre côté, à l'intérieur de la cavité (7a) de la partie en crochet (7) du second module (5), ledit élément de connexion (8) contraignant stablement le premier et le second module (2, 5) et étant configuré pour maintenir ces derniers en contact l'un avec l'autre.


     
    2. Procédé selon la revendication précédente, l'élément de connexion (8) comprenant au moins une barre de renfort, éventuellement de matériau métallique, s'étendant le long d'un sens de développement longitudinal entre une première et une seconde partie d'extrémité (8a, 8b),
    ledit élément de connexion (8) comprenant - à la première partie d'extrémité (8a) - une première partie d'engagement (9) émergeant transversalement de la barre de renfort vers le sens de développement longitudinal de celle-ci, ledit élément de connexion (8) comprenant en outre - à la seconde partie d'extrémité (8b) - une seconde partie d'engagement (10) émergeant transversalement de la barre de renfort vers le sens de développement longitudinal de celle-ci, et l'étape d'engagement de l'élément de connexion (8) vers le premier et le second module (2, 5) comprenant au moins les sous-étapes suivantes :

    - engagement de manière stable de la première partie d'engagement (9) à l'intérieur de la cavité (4a) de la partie en crochet (4) du premier module (2),

    - engagement de manière stable de la seconde partie d'engagement (10) à l'intérieur de la cavité (7a) de la partie en crochet (7) du second module (5).


     
    3. Procédé selon la revendication précédente, l'étape d'engagement de la première partie d'engagement (9) au premier module (2) comprenant au moins les sous-étapes suivantes :

    - insertion de la première partie d'engagement (9) à l'intérieur de la cavité (4a) de la partie en crochet (4) du premier module (2),

    - remplissage au moins partiellement de la cavité (4a) de la partie en crochet (4) du premier module (2) avec un matériau cimentaire au moins partiellement sous un état liquide de sorte que ce dernier puisse contacter au moins une partie de ladite première partie d'engagement (9),

    - contrainte, par durcissement du matériau cimentaire à l'intérieur de la cavité (4a) du premier module (2), de ladite première partie d'engagement (9),

    et l'étape d'engagement de la seconde partie d'engagement (10) au second module (5) comprenant au moins les sous-étapes suivantes :

    - insertion de la seconde partie d'engagement (10) à l'intérieur de la cavité (7a) de la partie en crochet (7) du second module (5),

    - remplissage au moins partiellement de la cavité (7a) de la partie en crochet (7) du second module (5) avec un matériau cimentaire au moins partiellement sous un état liquide de sorte que ce dernier puisse contacter au moins une partie de ladite seconde partie d'engagement (10),

    - contrainte, par durcissement du matériau cimentaire à l'intérieur de la cavité (7a) du second module (5), de ladite seconde partie d'engagement (10).


     
    4. Procédé selon la revendication 2 ou 3, la première et la seconde partie d'engagement de l'élément de connexion (8) étant distinctes et pouvant être associées de manière amovible à la barre de renfort,
    le procédé comprenant l'étape d'engagement de la première et de la seconde partie d'engagement (9, 10) respectivement dans le premier et le second module et après, une étape de contrainte de la barre de renfort auxdites première et seconde partie d'engagement (9, 10).
     
    5. Procédé selon l'une quelconque des revendications précédentes, l'étape de dépôt, par un procédé d'impression tridimensionnelle, de la pluralité des couches (L) du matériau cimentaire l'une sur l'autre selon le sens de stratification (D), comprenant une superposition des couches (L) faisant preuve sensiblement des mêmes forme et taille,
    chaque module faisant preuve, selon le sens de stratification (D), d'une section transversale sensiblement constante pour définir essentiellement un profil.
     
    6. Structure (1) de matériau cimentaire renforcé, obtenue préférablement par le procédé selon l'une quelconque des revendications précédentes, ladite structure comprenant :

    - une pluralité de modules de matériau cimentaire comprenant :

    o au moins un premier module (2) comprenant au moins une paroi latérale (3) délimitée par une surface externe (3a) et s'étendant le long d'un sens de stratification (D), au moins une partie de ladite surface latérale externe (3a) du premier module (2) définissant une surface d'accouplement réciproque (3b), ledit premier module (2) comprenant en outre au moins une partie en crochet (4) définissant au moins une cavité (4a) s'étendant au moins partiellement le long du sens de stratification (D),

    o au moins un second module (5) comprenant au moins une paroi latérale (6) délimitée par une surface externe (6a) et s'étendant le long du sens de stratification (D), au moins une partie de la surface externe (6a) du second module (5) définissant une surface d'accouplement réciproque (6b) en contre-forme et en contact avec la surface d'accouplement réciproque (3b) de la surface externe (3a) du premier module (2), ledit second module (5) comprenant en outre au moins une partie en crochet (7) définissant au moins une cavité (7a) s'étendant au moins partiellement le long du sens de stratification (D),

    - au moins un élément de connexion (8) engagé, sur un côté, à l'intérieur de la cavité (4a) de la partie en crochet (4) du premier module (2) et, sur l'autre côté, à l'intérieur de la cavité (7a) de la partie en crochet (7) du second module (5), ledit élément de connexion (8) étant configuré pour contraindre de manière stable le premier et le second module (2, 5) et pour les maintenir en contact l'un avec l'autre.


     
    7. Structure selon la revendication précédente, l'élément de connexion (8) comprenant au moins une barre de renfort, éventuellement de matériau métallique, s'étendant le long d'un sens de développement longitudinal entre une première et une seconde partie d'extrémité (8a, 8b),
    ledit élément de connexion (8) comprenant - à la première partie d'extrémité (8a) - une première partie d'engagement (9) émergeant transversalement de la barre de renfort vers le sens de développement longitudinal de celle-ci et engagé à l'intérieur de la cavité (4a) de la partie en crochet (4) du premier module (2),
    ledit élément de connexion (8) comprenant en outre - à la seconde partie d'extrémité (8b) - une seconde partie d'engagement (10) émergeant transversalement de la barre de renfort vers le sens de développement longitudinal de celle-ci et engagé à l'intérieur de la cavité (7a) de la partie en crochet (7) du second module (2).
     
    8. Structure selon la revendication précédente, la première et la seconde partie d'engagement (9, 10) de l'élément de connexion (8) étant distinctes et pouvant être associées de manière amovible à la barre de renfort.
     
    9. Structure selon l'une quelconque des revendications de 6 à 8, chaque module faisant preuve, selon le sens de stratification (D), d'une section transversale sensiblement constante pour définir essentiellement un profil.
     
    10. Structure selon l'une quelconque des revendications de 6 à 9, la paroi latérale (3) du premier module (2) définissant un périmètre fermé externe, particulièrement ayant une forme polygonale,
    la paroi latérale (6) du second module (5) définissant un périmètre fermé externe, particulièrement ayant une forme polygonale,
    la partie en crochet (4) dudit premier module (2) étant définie à l'intérieur dudit périmètre fermé externe, éventuellement ladite partie en crochet (4) s'étendant sur l'ensemble d'un développement du premier module (2) le long du sens de stratification (D),
    la partie en crochet (7) dudit second module (5) étant définie à l'intérieur dudit périmètre fermé externe, éventuellement ladite partie en crochet (7) s'étendant sur l'ensemble d'un développement du second module (7) le long du sens de stratification (D).
     
    11. Structure selon l'une quelconque des revendications de 6 à 10, le premier module (2) étant creux et faisant preuve d'un périmètre fermé externe, le premier module (2) comprenant, à l'intérieur du périmètre fermé externe, une partie de renfort (11) s'étendant à l'intérieur du périmètre fermé externe entre deux côtés sensiblement opposés l'un par rapport à l'autre,
    le second module (5) étant creux et faisant preuve d'un périmètre fermé externe, le second module (5) comprenant, à l'intérieur du périmètre fermé externe, une partie de renfort (14) s'étendant à l'intérieur du périmètre fermé externe entre deux côtés sensiblement opposés l'un par rapport à l'autre.
     




    Drawing









































    Cited references

    REFERENCES CITED IN THE DESCRIPTION



    This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

    Patent documents cited in the description