ELECTRODE FOR RECHARGEABLE LITHIUM BATTERY, AND RECHARGEABLE LITHIUM BATTERY INCLUDING THE SAME

Description

BACKGROUND OF THE INVENTION

(a) Field of the Invention

[0001] An electrode for a rechargeable lithium battery and a rechargeable lithium battery including the same are disclosed.

(b) Description of the Related Art

[0002] A portable information device such as a cell phone, a laptop, smart phone, and the like or an electric vehicle has used a rechargeable lithium battery having high energy density and easy portability as a driving power source. In addition, research on use of a rechargeable lithium battery as a power source for a hybrid or electric vehicle or a power storage by using high energy density characteristics has recently been actively made.

[0003] One of the main research tasks of such a rechargeable lithium battery is to improve the safety of the rechargeable battery. For example, if the rechargeable lithium battery is exothermic due to internal short circuit, overcharge and overdischarge, and the like, and an electrolyte decomposition reaction and thermal runaway phenomenon occur, an internal pressure inside the battery may rise rapidly to cause battery explosion. Among these, when the internal short circuit of the rechargeable lithium battery occurs, there is a high risk of explosion because the high electrical energy stored in each electrode is conducted in the shorted positive electrode and negative electrode.

[0004] In addition to the damage of the rechargeable lithium battery, the explosion may cause fatal damages to the user. Therefore, it is urgent to develop a technique capable of improving stability of the rechargeable lithium battery. Related examples may be found in CN 106848383 A, EP 1826842 A1 or EP 1079455 A2.

SUMMARY OF THE INVENTION

[0005] An embodiment provides an electrode for a rechargeable lithium battery as defined in claim 1.

[0006] Another embodiment provides a rechargeable lithium battery including the electrode.

[0007] As the reaction rate according to the temperature is improved, an early shutdown function may be realized and stability of the rechargeable lithium battery may be secured.

[0008] Further embodiments could be learned from the depended claims and following description.

BRIEF DESCRIPTION OF THE DRAWINGS

[0009] 

FIG. 1 is a schematic view of a structure of a rechargeable lithium battery according to an embodiment of the present disclosure.

FIG. 2 is a SEM image of spherical-shaped polyethylene particles in water dispersion state.

FIG. 3 is a SEM image of polyethylene particles according to an embodiment.

FIG. 4 is a SEM image of the the active material layer according to an embodiment.

FIG. 5 is a graph showing particle distributions of flake-shaped polyethylene particles included in the electrode according to Examples 1 to 3.

FIG. 6 is a graph showing resistance increase rates of the electrode plates in accordance with a temperature.

FIG. 7 is a graph showing capacity retention for 150 cycles of rechargeable lithium battery cells according to Examples 1 to 3.

FIG. 8 is a schematic view of a coin symmetric cell manufactured to evaluate resistance increase rates of the electrode plates.

DETAILED DESCRIPTION OF THE EMBODIMENTS

[0010] Hereinafter, referring to the drawings, embodiments of the present invention are described in detail. In the following description of the present disclosure, the well-known functions or constructions will not be described in order to clarify the present disclosure.

[0011] In order to clearly illustrate the present disclosure, the description and relationships are omitted, and throughout the disclosure, the same or similar configuration elements are designated by the same reference numerals. Also, since the size and thickness of each configuration shown in the drawing are arbitrarily shown for better understanding and ease of description, the present disclosure is not necessarily limited thereto.

[0012] An electrode for a rechargeable lithium battery according to an embodiment of the present invention includes a current collector and an active material layer disposed on the current collector, wherein

(i) the active material layer includes flake-shaped polyethylene particles and/or

(ii) a coating layer directly disposed on the active material layer comprises flake-shaped polyethylene particles.

[0013] The polyethylene particles according to the present invention may have a flake-shape as shown in FIG. 3, and have a different shape from a spherical-shaped polyethylene particles in a water dispersion state which is typical polyethylene particles as shown in FIG. 2, and an average particle size of the flake-shaped polyethylene particles is defined as D50.

[0014] Particularly, as shown in FIG. 4, the flake-shaped polyethylene particles are disposed in a thin and wide shape on pores in the active material layer according to an example embodiment, so they are melted more rapidly in the thermal runaway due to thermal/physical impacts to suppress ion channels.

[0015] In general, polyethylene may be classified according to density into a high density polyethylene (HDPE) having a density of about 0.94 g/cc to about 0.965 g/cc, a medium density polyethylene (MDPE) having a density of about 0.925 g/cc to about 0.94 g/cc, a low density polyethylene (LDPE) having a density of about 0.91 g/cc to about 0.925 g/cc), and a very low density polyethylene (VLDPE) having a density of about 0.85 g/cc to about 0.91 g/cc.

[0016] The flake-shaped polyethylene particles may include for example polyethylene polymers such as HDPE, MDPE, or LDPE alone or in a mixture of two or more.

[0017] In the case of including the flake-shaped polyethylene particle, a reaction rate according to the temperature is increased under the same reaction condition as compared with the case including the spherical-shaped polyethylene particle, and thus a stability improvement effect of the rechargeable lithium battery may be further improved. In the case of flake-shaped polyethylene particles before melting, an area covering the surfaces of the electrode plate is thinner and wider than spherical-shaped polyethylene particles before melting. If the polyethylene particles are melted at a temperature exceeding a certain temperature and ion channels are closed, an electrode plate area where the flake-shaped polyethylene particles are melted and closed is larger than that where the spherical-shaped polyethylene particles are melted and closed, and may have a fast reaction rate.

[0018] That is, during thermal runaway of a battery, the polyethylene particles are melted and the ion channel is closed, thereby limiting movement of ions and exhibiting a shutdown function, and thus additional electrical chemical reactions may be prevented.

[0019] The flake-shaped polyethylene particles have an average particle size (D50) of 1 µm to 8µm, and specifically 2 µm to 6µm.

[0020] As used herein, average particle size (D50) is measured by automated image analysis (by means of a particle size analyzer), or microscopy ( by means of TEM or SEM photographs). In particular, the particle size analyzer may be a dynamic light-scattering measurement device. From this, the D50 value may be easily obtained through a calculation. Since the polyethylene particles are not of spherical shape, the equivalent spherical diameter (or ESD) of the irregularly shaped object is determined which is the diameter of a sphere of equivalent volume. In other words, the average particle size (D50)

[0021] refers to the ESD of the flake-shaped particles.

[0022] Further, the flake-shaped polyethylene particles has a ratio of the longest Feret diameter to the shortest Feret diameter ranging from 1.1 to 4.5, and specifically from 1.2 to 3.5.

[0023] In addition, the flake-shaped polyethylene particles may have a thickness of 0.2 µm to 4 µm, and specifically, 0.3 µm to 2.5 µm or 0.3 µm to 1.5 µm. A thickness of the flake-shaped polyethylene particles is always less than its average particle size (D50).

[0024] Preferably, the thickness of the flake-shaped polyethylene particles is 0.3 µm to 1.5 µm, the average particle size (D50) is 2 µm to 6 µm and a ratio of the longest Feret diameter to the shortest Feret diameter ranges from 1.2 to 3.5.

[0025] When the flake-shaped polyethylene particles have a size and thickness within the ranges, ion channels may be effectively closed even by using small amounts of the particles.

[0026] The active material layer includes an active material and may further include at least one of a conductive material and a binder.

[0027] The flake-shaped polyethylene particles may be included into the active material layer in an amount of 0.1 wt% to 5 wt%, and specifically 0.2 wt% to 3.0 wt% based on a total weight of the active material layer. If the flake-shaped polyethylene particles are (also) present in the coating layer, the flake-shaped polyethylene particles may be included in an amount of 0.1 wt% to 5 wt%, and specifically 0.2 wt% to 3.0 wt% based on a total weight of the active material layer and the coating layer.

[0028] When the amount of the flake-shaped polyethylene particles is within the ranges, cycle-life characteristics and output characteristics of a battery may be secured.

[0029] When the flake-shaped polyethylene particles are included in the coating layer, the active material layer may be for example a negative active material layer.

[0030] The coating layer may further include inorganic particles and a binder.

[0031] A weight ratio of the sum of the flake-shaped polyethylene particles and the inorganic particles to the binder may be 80:20 to 99:1, and specifically 85:15 to 97:3.

[0032] The flake-shaped polyethylene particles and the inorganic particles may be included in a weight ratio of 95:5 to 10:90, and specifically 30:70 to 70:30.

[0033] The inorganic particles may include, for example, Al₂O₃, SiO₂, TiO₂, SnO₂, CeO₂, MgO, NiO, CaO, GaO, ZnO, ZrO₂, Y₂O₃, SrTiO₃, BaTiO₃, Mg(OH)₂, boehmite, or a combination thereof. Organic particles such as an acrylic compound, an imide compound, an amide compound, or a combination thereof may be further included in addition to inorganic particle.

[0034] The inorganic particles may be spherical, flake-shaped, cubic, or amorphous. The inorganic particles may have an average particle diameter (D50) of 1 nm to 2500 nm, for example 100 nm to 2000 nm, or 200 nm to 1000 nm, or 300 nm to 800 nm. The diameters may be measured similar to the flake-shaped polyethylene particles.

[0035] Meanwhile, the electrode for a rechargeable lithium battery according to the present invention may be a positive electrode including a positive electrode current collector and a positive active material layer or a negative electrode including a negative electrode current collector and a negative active material layer.

[0036] The positive electrode according to an embodiment of the present invention includes a positive electrode current collector and a positive active material layer disposed on the positive electrode current collector.

[0037] The positive electrode current collector may be aluminum or nickel, but is not limited thereto.

[0038] The positive active material may include lithiated intercalation compounds that reversibly intercalate and deintercalate lithium ions.

[0039] Specifically, it may include one or more composite oxides of a metal selected from cobalt, manganese, nickel, and a combination thereof, and lithium.

[0040] Examples of the positive active material may be a compound represented by one of chemical formulae.

[0041] Li_aA_1-bX_bD₂ (0.90 ≤ a ≤ 1.8, 0 ≤ b ≤ 0.5); Li_aA_1-bX_bO_2-cD_c (0.90 ≤ a ≤ 1.8, 0 ≤ b ≤ 0.5, 0 ≤ c ≤ 0.05); Li_aE_1-bX_bO_2-cD_c (0.90 ≤ a ≤ 1.8, 0 ≤ b ≤ 0.5, 0 ≤ c ≤ 0.05); Li_aE_2-bX_bO_4-cD_c (0.90 ≤ a ≤ 1.8, 0 ≤ b ≤ 0.5, 0 ≤ c ≤ 0.05); Li_aNi_1-b-cCo_bX_cD_α (0.90 ≤ a ≤ 1.8, 0 ≤ b ≤ 0.5, 0 ≤ c ≤ 0.5, 0 < α ≤ 2); Li_aNi_1-b-cCo_bX_cO_2-αT_α (0.90 ≤ a ≤ 1.8, 0 ≤ b ≤ 0.5, 0 ≤ c ≤ 0.05, 0 < α < 2); Li_aNi_1-b-cCo_bX_cO_2-αT₂ (0.90 ≤ a ≤ 1.8, 0 ≤ b ≤ 0.5, 0 ≤ c ≤ 0.05, 0 < α < 2); Li_aNi_1-b-cMn_bX_cD_α (0.90 ≤ a ≤ 1.8, 0 ≤ b ≤ 0.5, 0 ≤ c ≤ 0.05, 0 < α ≤ 2); Li_aNi_1-b-cMn_bXO_2-αT_α (0.90 ≤ a ≤ 1.8, 0 ≤ b ≤ 0.5, 0 ≤ c ≤ 0.05, 0 < α < 2); Li_aNi_1-b-cMn_bX_cO_2-α T₂ ( 0.90 ≤ a ≤ 1.8, 0 ≤ b ≤ 0.5, 0 ≤ c ≤ 0.05, 0 < α < 2); Li_aNi_bE_cG_dO₂ (0.90 ≤ a ≤ 1.8, 0 ≤ b ≤ 0.9, 0 ≤ c ≤ 0.5, 0.001 ≤ d ≤ 0.1); Li_aNi_bCo_cMn_dG_eO₂ (0.90 ≤ a ≤ 1.8, 0 ≤ b ≤ 0.9, 0 ≤ c ≤ 0.5, 0 ≤ d ≤ 0.5, 0.001 ≤ e ≤ 0.1); Li_aNiG_bO₂ (0.90 ≤ a ≤ 1.8, 0.001 ≤ b ≤ 0.1); Li_aCoG_bO₂ (0.90 ≤ a ≤ 1.8, 0.001 ≤ b ≤ 0.1); Li_aMn_1-bG_bO₂ (0.90 ≤ a ≤ 1.8, 0.001 ≤ b ≤ 0.1); Li_aMn₂G_bO₄ (0.90 ≤ a ≤ 1.8, 0.001 ≤ b ≤ 0.1); Li_aMn_1-gG_gPO₄ (0.90 ≤ a ≤ 1.8, 0 ≤ g ≤ 0.5); QO₂; QS₂; LiQS₂; V₂O₅; LiV₂O₅; LiZO₂; LiNiVO₄; Li_(3-f)J₂(PO₄)₃ (0 ≤ f ≤ 2); Li_(3-f)Fe₂(PO₄)₃(0 ≤ f ≤ 2); Li_aFePO₄(0.90 ≤ a ≤ 1.8)

[0042] In chemical formulae, A is selected from Ni, Co, Mn, and a combination thereof; X is selected from Al, Ni, Co, Mn, Cr, Fe, Mg, Sr, V, a rare earth element, and a combination thereof; D is selected from O, F, S, P, and a combination thereof; E is selected from Co, Mn, and a combination thereof; T is selected from F, S, P, and a combination thereof; G is selected from Al, Cr, Mn, Fe, Mg, La, Ce, Sr, V, and a combination thereof; Q is selected from Ti, Mo, Mn, and a combination thereof; Z is selected from Cr, V, Fe, Sc, Y, and a combination thereof; and J is selected from V, Cr, Mn, Co, Ni, Cu, and a combination thereof.

[0043] The compounds may have a coating layer on the surface, or may be mixed with another compound having a coating layer. The coating layer may include at least one coating element compound selected from an oxide of a coating element, a hydroxide of a coating element, an oxyhydroxide of a coating element, an oxycarbonate of a coating element, and a hydroxy carbonate of a coating element. The compound for the coating layer may be amorphous or crystalline. The coating element included in the coating layer may include Mg, Al, Co, K, Na, Ca, Si, Ti, V, Sn, Ge, Ga, B, As, Zr, or a mixture thereof. The coating layer may be disposed in a method having no adverse influence on properties of a positive active material by using these elements in the compound. For example, the method may include any coating method (e.g., spray coating, dipping, etc.), but is not illustrated in more detail since it is well-known to those skilled in the related field.

[0044] The positive active material may be included in an amount of about 90 wt% to about 98 wt% based on a total weight of the positive active material layer.

[0045] The positive active material layer may further include optionally a positive electrode conductive material and a positive electrode binder.

[0046] Each amount of the positive electrode conductive material and the positive electrode binder may be about 1 wt% to about 5 wt% based on a total weight of the positive active material layer.

[0047] The positive electrode conductive material is included to provide a positive electrode with conductivity. Any electronically conductive material may be used as a conductive material unless it causes a chemical change in a battery. Examples thereof may be a carbon-based material such as natural graphite, artificial graphite, carbon black, acetylene black, ketjen black, carbon fiber and the like; a metal-based material of a metal powder or a metal fiber including copper, nickel, aluminum silver, and the like; a conductive polymer such as a polyphenylene derivative; or a mixture thereof.

[0048] The positive electrode binder improves binding properties of positive active material particles with one another and with a current collector. Examples thereof may be polyvinyl alcohol, carboxylmethyl cellulose, hydroxypropyl cellulose, diacetyl cellulose, polyvinylchloride, carboxylated polyvinylchloride, polyvinylfluoride, an ethylene oxide-containing polymer, polyvinylpyrrolidone, polyurethane, polytetrafluoroethylene, polyvinylidene fluoride, polyethylene, polypropylene, a styrene-butadiene rubber, an acrylated styrene-butadiene rubber, an epoxy resin, nylon, and the like, but is not limited thereto.

[0049] In addition, the negative electrode according to another embodiment of the present invention may include a negative electrode current collector and a negative active material layer disposed on the negative electrode current collector.

[0050] The negative electrode current collector may include one selected from a copper foil, a nickel foil, a stainless steel foil, a titanium foil, a nickel foam, a copper foam, a polymer substrate coated with a conductive metal, and a combination thereof.

[0051] The negative active material may include a material that reversibly intercalates/deintercalates lithium ions, a lithium metal, a lithium metal alloy, a material capable of doping/dedoping lithium, or transition metal oxide.

[0052] The material that reversibly intercalates/deintercalates lithium ions may include a carbon material that is a generally-used carbon-based negative active material in a rechargeable lithium battery. Examples of the carbon-based negative active material may be crystalline carbon, amorphous carbon, or a mixture thereof. The crystalline carbon may be non-shaped, or sheet, flake, spherical, or fiber shaped natural graphite or artificial graphite. The amorphous carbon may be a soft carbon, a hard carbon, a mesophase pitch carbonization product, fired coke, and the like.

[0053] The lithium metal alloy includes an alloy of lithium and a metal selected from Na, K, Rb, Cs, Fr, Be, Mg, Ca, Sr, Si, Sb, Pb, In, Zn, Ba, Ra, Ge, Al, and Sn.

[0054] The material capable of doping/dedoping lithium may be a silicon-based material, for example, Si, SiO_x (0<x<2), a Si-Q alloy (wherein Q is an element selected from an alkali metal, an alkaline-earth metal, a Group 13 element, a Group 14 element, a Group 15 element, a Group 16 element, a transition metal, a rare earth element, and a combination thereof, and not Si), a Si-carbon composite, Sn, SnO₂, a Sn-R alloy (wherein R is an element selected from an alkali metal, an alkaline-earth metal, a Group 13 element, a Group 14 element, a Group 15 element, a Group 16 element, a transition metal, a rare earth element, and a combination thereof, and not Sn), a Sn-carbon composite, and the like. At least one of these materials may be mixed with SiO₂. The elements Q and R may be selected from Mg, Ca, Sr, Ba, Ra, Sc, Y, Ti, Zr, Hf, Rf, V, Nb, Ta, Db, Cr, Mo, W, Sg, Tc, Re, Bh, Fe, Pb, Ru, Os, Hs, Rh, Ir, Pd, Pt, Cu, Ag, Au, Zn, Cd, B, Al, Ga, Sn, In, Ge, P, As, Sb, Bi, S, Se, Te, Po, and a combination thereof.

[0055] The transition metal oxide includes lithium titanium oxide.

[0056] In the negative active material layer, the negative active material may be included in an amount of about 95 wt% to about 99 wt% based on the total weight of the negative active material layer.

[0057] The negative active material layer may further include optionally a negative electrode conductive material and a negative electrode binder.

[0058] Each amount of the negative electrode conductive material and negative electrode binder may be about 1 wt% to about 5 wt% based on a total weight of the negative active material layer.

[0059] Types of the negative electrode conductive material are the same as the types of the aforementioned positive electrode conductive material.

[0060] The negative electrode binder acts to adhere negative active material particles to each other and to adhere the negative active material to the current collector. The negative electrode binder may be a non-aqueous binder, an aqueous binder, an amphiphilic binder (aqueous/non-aqueous binder), or a combination thereof.

[0061] The non-aqueous binder may be polyvinylchloride, carboxylated polyvinylchloride, polyvinylfluoride, an ethylene oxide-containing polymer, polyvinylpyrrolidone, polyurethane, polytetrafluoroethylene, polyvinylidene fluoride, polyethylene, polypropylene, polyamideimide, polyimide, or a combination thereof.

[0062] The aqueous binder may be a styrene-butadiene rubber, an acrylated styrene-butadiene rubber, polyvinyl alcohol, sodium polyacrylate, a copolymer of propylene and a C2 to C8 olefin, a copolymer of (meth)acrylic acid and (meth)acrylic acid alkyl ester, or a combination thereof.

[0063] The amphiphilic binder may be an acrylated styrene-based rubber, and the like.

[0064] When the negative electrode binder is an aqueous binder, a cellulose-based compound may be further used to provide viscosity as a thickener. The cellulose-based compound includes one or more of carboxylmethyl cellulose, hydroxypropylmethyl cellulose, methyl cellulose, or alkali metal salts thereof. The alkali metals may be Na, K, or Li. The thickener may be included in an amount of about 0.1 to about 3 parts by weight based on 100 parts by weight of the negative active material.

[0065] Hereinafter, a rechargeable lithium battery according to another embodiment of the present disclosure with reference to FIG. 1 is described. FIG. 1 is a schematic view of the structure of a rechargeable lithium battery according to an embodiment.

[0066] Referring to FIG. 1, a rechargeable lithium battery 100 according to an embodiment includes a battery cell including a negative electrode 112, a positive electrode 114 facing the negative electrode 112, a separator 113 interposed between the negative electrode 112 and the positive electrode 114, and an electrolyte (not shown) for a rechargeable lithium battery impregnating the negative electrode 112, the positive electrode 114, and the separator 113, a battery case 120 housing the battery cell, and a sealing member 140 sealing the battery case 120.

[0067] On the other hand, a lithium salt included in the electrolyte is dissolved in a solvent to act as a source of lithium ions in a battery in order to enable the operation of the basic rechargeable lithium battery and to promote transportation of lithium ion between the positive electrode and the negative electrode

[0068] The lithium salt may include LiPF₆, LiSbF₆, LiAsF₆, LiN(SO₂C₂F₅)₂, Li(CF₃SO₂)₂N, LiN(SO₃C₂F₅)₂, LiC₄F₉SO₃, LiClO₄, LiAlO₂, LiAlCl₄, LiN(C_xF_2x+1SO₂)(C_yF_2y+1SO₂) wherein, x and y are natural numbers, for example an integer ranging from 1 to 20), LiCI, Lil, and LiB(C₂O₄)₂ (lithium bis(oxalato) borate, LiBOB), or a combination thereof.

[0069] A concentration of the lithium salt may be about 0.1 M to about 2.0 M. When the lithium salt is included at the above concentration range, an electrolyte may have excellent performance and lithium ion mobility due to optimal electrolyte conductivity and viscosity.

[0070] On the other hand, the electrolyte may further include an organic solvent to dissolve the lithium salt. The organic solvent may be a non-aqueous organic solvent having high ion conductivity, a high dielectric constant, and a low viscosity. The non-aqueous organic solvent serves as a medium for transporting ions taking part in the electrochemical reaction of a battery.

[0071] Such a non-aqueous organic solvent may be, for example, a carbonate-based, ester-based, ether-based, ketone-based, alcohol-based, or aprotic solvent.

[0072] The carbonate-based solvent may include dimethyl carbonate (DMC), diethyl carbonate (DEC), dipropyl carbonate (DPC), methylpropyl carbonate (MPC), ethylpropyl carbonate (EPC), methylethyl carbonate (MEC), ethylene carbonate (EC), propylene carbonate (PC), butylene carbonate (BC), and the like. The ester-based solvent may include methyl acetate, ethyl acetate, n-propyl acetate, dimethylacetate, methyl propionate, ethyl propionate, propyl propionate, γ -butyrolactone, decanolide, valerolactone, mevalonolactone, caprolactone, and the like

[0073] The ether-based solvent may include dibutyl ether, tetraglyme, diglyme, dimethoxyethane, 2-methyltetrahydrofuran, tetrahydrofuran, and the like and the ketone-based solvent may be cyclohexanone, and the like.

[0074] The alcohol based solvent may include ethanol, isopropyl alcohol, and the like, and the aprotic solvent may include nitriles such as T-CN (wherein T is a C2 to C20 linear, branched, or cyclic hydrocarbon group, a double bond, an aromatic ring, or an ether bond), and the like, amides such as dimethyl formamide, and the like, dioxolanes such as 1,3-dioxolane, and the like, sulfolanes, and the like.

[0075] The non-aqueous organic solvent may be used alone or in a mixture. When the organic solvent is used in a mixture, the mixture ratio may be controlled in accordance with a desirable battery performance.

[0076] The carbonate-based solvent is prepared by mixing a cyclic carbonate and a chain-type carbonate. In this case, when the cyclic carbonate and the chain-type carbonate are mixed together in a volume ratio of about 1:1 to about 1:9, performance of an electrolyte may be enhanced.

[0077] The non-aqueous organic solvent may further include an aromatic hydrocarbon-based organic solvent in addition to the carbonate-based solvent. Herein, the carbonate-based solvent and the aromatic hydrocarbon-based organic solvent may be mixed in a volume ratio of about 1:1 to about 30:1.

[0078] The aromatic hydrocarbon-based organic solvent may be an aromatic hydrocarbon-based compound of Chemical Formula 3.

[0079] In Chemical Formula 3, R₃ to R₈ are the same or different and are selected from hydrogen, a halogen, a C1 to C10 alkyl group, a haloalkyl group, and a combination thereof.

[0080] Specific examples of the aromatic hydrocarbon-based organic solvent may be selected from benzene, fluorobenzene, 1,2-difluorobenzene, 1,3-difluorobenzene, 1,4-difluorobenzene, 1,2,3-trifluorobenzene, 1,2,4-trifluorobenzene, chlorobenzene, 1,2-dichlorobenzene, 1,3-dichlorobenzene, 1,4-dichlorobenzene, 1,2,3-trichlorobenzene, 1,2,4-trichlorobenzene, iodobenzene, 1,2-diiodobenzene, 1,3-diiodobenzene, 1,4-diiodobenzene, 1,2,3-triiodobenzene, 1,2,4-triiodobenzene, toluene, fluorotoluene, 2,3-difluorotoluene, 2,4-difluorotoluene, 2,5-difluorotoluene, 2,3,4-trifluorotoluene, 2,3,5-trifluorotoluene, chlorotoluene, 2,3-dichlorotoluene, 2,4-dichlorotoluene, 2,5-dichlorotoluene, 2,3,4-trichlorotoluene, 2,3,5-trichlorotoluene, iodotoluene, 2,3-diiodotoluene, 2,4-diiodotoluene, 2,5-diiodotoluene, 2,3,4-triiodotoluene, 2,3,5-triiodotoluene, xylene, and a combination thereof.

[0081] Meanwhile, as described above, the separator 113 may be disposed between the positive electrode 114 and the negative electrode 112. The separator 113 may include polyethylene, polypropylene, polyvinylidene fluoride, or a multi-layer thereof and may be a mixed multilayer such as a polyethylene/polypropylene double-layered separator, a polyethylene/polypropylene/polyethylene triple-layered separator, a polypropylene/polyethylene/polypropylene triple-layered separator, and the like.

[0082] Hereinafter, the above aspects of the present disclosure are illustrated in more detail with reference to examples. However, these examples are exemplary, and the present disclosure is not limited thereto.

(Manufacture of Rechargeable Lithium Battery Cell)

Example 1: Battery Cell Including Flake-shaped 2µm PE Particles

[0083] 95 wt% of a positive active material in which LiCoO₂/LiFePO₄ (LCO/LFP) were mixed in a weight ratio of 9:1, 3 wt% of a polyvinylidene fluoride binder, and 2 wt% of a ketjen black conductive material were mixed in a N-methyl pyrrolidone solvent to provide a positive active material slurry. The positive active material slurry was coated on both surfaces of an aluminum current collector, dried and compressed to provide a positive electrode formed with a positive active material layer.

[0084] 98 wt% of graphite, 0.8 wt% of carboxylmethyl cellulose, and 1.2 wt% of styrene-butadiene rubber were mixed in pure water to provide a negative active material slurry. The negative active material slurry was coated on both surfaces of a copper current collector, dried, and compressed to provide a negative electrode formed with a negative active material layer.

[0085] 48 wt% of flake-shaped 2µm Polyethylene (PE) particles (average particle diameter D50; longest Feret diameter/ shortest Feret diameter = about 2, thickness= about 0.6µm), 47 wt% of alumina (average particle diameter (D50)=0.7µm), and 5 wt% of an acrylated styrene-based rubber binder were mixed in an alcohol-based solvent to provide a PE/alumina slurry.

[0086] The PE/alumina slurry was coated on both surfaces of the negative electrode, dried, and compressed to provide a negative electrode formed with a coating layer including flake-shaped PE particles.

[0087] The positive electrode, a separator including a PE/PP multi-layer substrate, the negative electrode formed with the coating layer including the flake-shaped PE particles were sequentially stacked to provide an electrode assembly having a structure shown in FIG. 1, and then an electrolyte (1.0 M LiPF₆ in EC/DEC =50:50 v/v) was injected to provide a rechargeable battery cell.

Example 2: Battery Cell Including Flake-shaped 4µm PE Particles

[0088] A rechargeable battery cell was manufactured in accordance with the same procedure as in Example 1, except that the negative electrode was prepared using 4µm flake-shaped PE particles (longest Feret diameter/ shortest Feret diameter = about 2.4, thickness= about 0.6µm).

[0089] Example 3: Battery Cell Including Flake-shaped 6µm PE Particles A rechargeable battery cell was manufactured in accordance with the same procedure as in Example 1, except that the negative electrode was prepared using 6µm flake-shaped PE particles (longest Feret diameter/ shortest Feret diameter = about 2.4, thickness= about 0.6µm).

[0090] The results of particle distributions of flake-shaped polyethylene particles included in the electrode according to Examples 1 to 3 are shown in FIG. 5.

Comparative Example: Battery Cell Including Spherical-shaped PE Particles

[0091] A rechargeable battery cell was manufactured in accordance with the same procedure as in Example 1, except that the negative electrode was prepared using a dispersion in which 4µm spherical-shaped PE particles were dispersed in an alcohol-based solvent instead of the flake-shaped 2µm PE particles.

(Evaluation Examples)

1. Evaluation of Resistance Increase Rate of Electrode Plate

[0092] A negative electrode formed with a coating layer including flake-shaped PE particles according to Example 1, a separator including a PE/PP multi-layer substrate, and a negative electrode formed with a coating layer including flake-shaped PE particles according to Example 1 were sequentially stacked, and an electrolyte including 1M LiBF₄ dissolved in propylene carbonate was injected thereto to provide a coin symmetric cell shown in FIG. 8. Referring to FIG. 8, a coin symmetric cell 200 (which may also be referred to as a symmetrical blocking electrode cell), includes a bottom case 220, a spring 210, a negative electrode 212, a first spacer 216, a separator 218, a second spacer 222, a positive electrode 214, and a top case 224, stacked in the stated order. The spring 210 included 3 springs, the negative electrode 212 had a diameter of 15.5 mm ϕ, the first spacer 216 and the second spacer 222 each had a thickness of 500 µm, and the separator 218 included a polyethylene (PE) separator having a diameter of 19 mm ϕ (612HS). The coin symmetric cell 200 was impregnated with an electrolyte (EL) including 50 µL of 1M LiBF₄ in propylene carbonate (PC).

[0093] FIG. 8 is a schematic view of a coin symmetric cell manufactured to evaluate resistance increase rates of the electrode plates.

[0094] The obtained coin symmetric cell was introduced into a temperature changeable chamber after mounting a temperature sensor and a resistance measurer and evaluated. Changes on a temperature and a resistance of the coin symmetric cell were measured while increasing the temperature at a rate of 10° C/minute, and the results of evaluating the resistance increase rate of an electrode plate according to a temperature are shown in FIG. 6.

[0095] FIG. 6 is a graph showing resistance increase rates of the electrode plates in accordance with a temperature.

[0096] Referring to FIG. 6, it is confirmed that the resistance increase rate of the electrode plate according to Example was significantly higher than Comparative Example at a high temperature of 120° C or higher.

[0097] From this, it may be anticipated that in a case of a battery cell including an electrode according to an embodiment, ion channels are effectively suppressed on a thermal runaway by the thermal/physical impact, so the shut-down function may be expressed in an early stage.

2. Evaluation of Cycle-life Characteristics

[0098] Rechargeable lithium battery cells obtained from Examples 1 to 3 were charged at a rate of 0.5C/0.5C and at 4.4V and then discharged until 3.0V, and the cell capacity decrease rate after 150 cycles was measured, and the results are shown in FIG. 7. At 51 cycles and 101 cycles, they were charged at a rate of 0.2C/0.2C at 4.4V and then discharged at 3.0V to evaluate a recovered capacity.

[0099] FIG. 7 is a graph showing capacity retention for 150 cycles of rechargeable lithium battery cells according to Examples 1 to 3.

[0100] Referring to FIG. 7, excellent capacity retention after 150 cycles are exhibited.

[0101] Resultantly, the rechargeable lithium battery cell according to an embodiment may show effective shut-down functions while maintaining excellent battery characteristics.

<Description of symbols>

[0102] 

100:

rechargeable lithium battery

112:

negative electrode

113:

separator

114:

positive electrode

120:

battery case

140:

sealing member

200:

coin symmetric cell

210:

spring

212:

negative electrode

214:

positive electrode

216:

first spacer

218:

separator

220:

bottom case

222:

second spacer

224:

top case

Claims

1. A electrode for a rechargeable lithium battery (100), comprising a current collector, and

an active material layer disposed on the current collector,

wherein

(i) the active material layer comprises flake-shaped polyethylene particles and/or

(ii) a coating layer directly disposed on the active material layer comprises flake-shaped polyethylene particles,

the flake-shaped polyethylene particles having an average particle size (D50) of 1µm to 8µm and a ratio of the longest Feret diameter to the shortest Feret diameter ranging from 1.1 to 4.5, wherein the average particle size (D50) refers to the equivalent spherical diameter of the flake-shaped particles and is measured by automated image analysis by means of a particle size analyzer or microscopy by means of TEM photographs or SEM photographs.

2. The electrode for a rechargeable lithium battery of claim 1, wherein the flake-shaped polyethylene particles have an average particle size (D50) of 2µm to 6µm.

3. The electrode for a rechargeable lithium battery of any one of the preceding claims, wherein the flake-shaped polyethylene particles have a thickness of 0.2 µm to 4 µm.

4. The electrode for a rechargeable lithium battery of any one of the preceding claims, wherein the active material layer comprises an active material and further comprises at least one of a conductive material and a binder.

5. The electrode for a rechargeable lithium battery of any one of the preceding claims, wherein the flake-shaped polyethylene particles are included in an amount of 0.1 wt% to 5 wt% based on a total weight of the active material layer, respectively based on a total weight of the active material layer and the coating layer.

6. The electrode for a rechargeable lithium battery of claim 1, alternative (ii), wherein the coating layer further comprises inorganic particles and a binder.

7. The electrode for a rechargeable lithium battery of claim 6, wherein a weight ratio of the sum of the flake-shaped polyethylene particles and the inorganic particles to the binder is 80:20 to 99:1.

8. The electrode for a rechargeable lithium battery of claim 6 or 7, wherein the flake-shaped polyethylene particles and the inorganic particles are included in a weight ratio of 95:5 to 10:90.

9. A rechargeable lithium battery comprising the electrode for a rechargeable lithium battery any one of the preceding claims.

Ansprüche

1. Elektrode für eine wiederaufladbare Lithiumbatterie (100), die einen Stromabnehmer umfasst, und

eine aktive Materialschicht, die auf dem Stromabnehmer angeordnet ist,

wobei

(i) die aktive Materialschicht plättchenförmige Polyethylenpartikel umfasst und/oder

(ii) eine direkt auf der aktiven Materialschicht angeordnete Beschichtungsschicht plättchenförmige Polyethylenpartikel umfasst,

wobei die plättchenförmigen Polyethylenpartikel eine durchschnittliche Partikelgröße (D50) von 1 µm bis 8 µm und ein Verhältnis des längsten Feret-Durchmessers zum kürzesten Feret-Durchmesser im Bereich von 1,1 bis 4,5 aufweisen, wobei sich die durchschnittliche Partikelgröße (D50) auf den äquivalenten sphärischen Durchmesser der plättchenförmigen Partikel bezieht und durch automatisierte Bildanalyse mittels eines Partikelgrößenanalysators oder Mikroskopie mittels TEM- oder SEM-Aufnahmen gemessen wird.

2. Elektrode für eine wiederaufladbare Lithiumbatterie nach Anspruch 1, wobei die plättchenförmigen Polyethylenpartikel eine durchschnittliche Partikelgröße (D50) von 2 µm bis 6 µm aufweisen.

3. Elektrode für eine wiederaufladbare Lithiumbatterie nach einem der vorhergehenden Ansprüche, wobei die plättchenförmigen Polyethylenpartikel eine Dicke von 0,2 µm bis 4 µm aufweisen.

4. Elektrode für eine wiederaufladbare Lithiumbatterie nach einem der vorhergehenden Ansprüche, wobei die aktive Materialschicht ein aktives Material und ferner mindestens eines von einem leitfähigen Material und einem Bindemittel umfasst.

5. Elektrode für eine wiederaufladbare Lithiumbatterie nach einem der vorhergehenden Ansprüche, wobei die plättchenförmigen Polyethylenpartikel in einer Menge von 0,1 Gew.-% bis 5 Gew.-%, bezogen auf das Gesamtgewicht der aktiven Materialschicht bzw. bezogen auf das Gesamtgewicht der aktiven Materialschicht und der Beschichtungsschicht, enthalten sind.

6. Elektrode für eine wiederaufladbare Lithiumbatterie nach Anspruch 1, Alternative (ii), wobei die Beschichtungsschicht ferner anorganische Partikel und ein Bindemittel umfasst.

7. Elektrode für eine wiederaufladbare Lithiumbatterie nach Anspruch 6, wobei das Gewichtsverhältnis der Summe der plättchenförmigen Polyethylenpartikel und der anorganischen Partikel zum Bindemittel 80 : 20 bis 99 : 1 beträgt.

8. Elektrode für eine wiederaufladbare Lithiumbatterie nach Anspruch 6 oder 7, wobei die plättchenförmigen Polyethylenpartikel und die anorganischen Partikel in einem Gewichtsverhältnis von 95 : 5 bis 10 : 90 beinhaltet sind.

9. Wiederaufladbare Lithiumbatterie, umfassend die Elektrode für eine wiederaufladbare Lithiumbatterie nach einem der vorhergehenden Ansprüche.

Revendications

1. Electrode pour une batterie rechargeable au lithium (100), comprenant :

un collecteur de courant, et

une couche de matériau actif disposée sur le collecteur de courant,

dans laquelle

(i) la couche de matériau actif comprend des particules de polyéthylène en forme de paillettes et/ou

(ii) une couche de revêtement disposée directement sur la couche de matériau actif comprend des particules de polyéthylène en forme de paillettes,

les particules de polyéthylène en forme de paillettes ayant une granulométrie moyenne (D50) de 1 µm à 8 µm et un rapport du diamètre de Feret le plus long au diamètre de Feret le plus court situé dans la plage allant de 1,1 à 4,5, où la granulométrie moyenne (D50) se réfère au diamètre de sphère équivalente des particules en forme de paillettes et est mesurée par analyse d'image automatisée au moyen d'un analyseur de granulométrie ou par microscopie au moyen de photographies MET ou de photographies MEB.

2. Electrode pour une batterie rechargeable au lithium selon la revendication 1, dans laquelle les particules de polyéthylène en forme de paillettes ont une granulométrie moyenne (D50) de 2 µm à 6 µm.

3. Electrode pour une batterie rechargeable au lithium selon l'une quelconque des revendications précédentes, dans laquelle les particules de polyéthylène en forme de paillettes ont une épaisseur de 0,2 µm à 4 µm.

4. Electrode pour une batterie rechargeable au lithium selon l'une quelconque des revendications précédentes, dans laquelle la couche de matériau actif comprend un matériau actif et comprend en outre au moins l'un parmi un matériau conducteur et un liant.

5. Electrode pour une batterie rechargeable au lithium selon l'une quelconque des revendications précédentes, dans laquelle les particules de polyéthylène en forme de paillettes sont incluses en une quantité de 0,1 % en poids à 5 % en poids par rapport au poids total de la couche de matériau actif, respectivement par rapport au poids total de la couche de matériau actif et de la couche de revêtement.

6. Electrode pour une batterie rechargeable au lithium selon la revendication 1, variante (ii), dans laquelle la couche de revêtement comprend en outre des particules inorganiques et un liant.

7. Electrode pour une batterie rechargeable au lithium selon la revendication 6, dans laquelle un rapport en poids de la somme des particules de polyéthylène en forme de paillettes et des particules inorganiques au liant est de 80:20 à 99:1.

8. Electrode pour une batterie rechargeable au lithium selon la revendication 6 ou 7, dans laquelle les particules de polyéthylène en forme de paillettes et les particules inorganiques sont incluses en un rapport en poids de 95:5 à 10:90.

9. Batterie rechargeable au lithium comprenant l'électrode pour une batterie rechargeable au lithium de l'une quelconque des revendications précédentes.