(19)
(11)EP 3 601 391 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
06.01.2021 Bulletin 2021/01

(21)Application number: 18712224.7

(22)Date of filing:  23.03.2018
(51)International Patent Classification (IPC): 
C08G 59/02(2006.01)
C08L 63/00(2006.01)
C09D 133/10(2006.01)
C08L 33/08(2006.01)
C08F 283/00(2006.01)
C09D 163/00(2006.01)
C09D 133/08(2006.01)
C08G 59/16(2006.01)
C08G 59/42(2006.01)
(86)International application number:
PCT/EP2018/057473
(87)International publication number:
WO 2018/177939 (04.10.2018 Gazette  2018/40)

(54)

EPOXY ACRYLIC HYBRID RESINS

HYBRIDE EPOXID-ACRYLHARZE

RÉSINES HYBRIDES ÉPOXY-ACRYLIQUES


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 27.03.2017 EP 17163087

(43)Date of publication of application:
05.02.2020 Bulletin 2020/06

(73)Proprietor: Allnex Austria GmbH
8402 Werndorf (AT)

(72)Inventors:
  • STEINER, Andreas J.
    8041 Graz (AT)
  • PAAR, Willibald
    8010 Graz (AT)
  • LUNZER, Florian
    8010 Graz (AT)
  • WANGO, Jörg Christian Karl
    8142 Wundschuh (AT)
  • GRÖLLER, Jacqueline
    8020 Graz (AT)

(74)Representative: Boon, Greet et al
Allnex Belgium, S.A. Patent Department Anderlechtstraat 33
1620 Drogenbos
1620 Drogenbos (BE)


(56)References cited: : 
JP-A- 2008 174 622
US-B2- 6 653 370
JP-A- 2009 041 003
  
      
    Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


    Description


    [0001] The present invention relates to hybrid systems composed of aqueous dispersions of epoxy/amine adduct resins and polymers of one or more ethylenically unsaturated monomers. The aqueous dispersions according to the present invention are particularly suitable for forming coatings or binder agents, especially for decorative and protective coating applications on various substrates.

    [0002] In many architectural applications (e.g.: wood coatings (deck stain, trim), metal coatings, ...) waterborne resins based on ethylenically unsaturated monomers, typically acrylic or styrene-acrylic resins, are used because of their high chemical stability, good weatherability and water resistance, low VOC and easy synthesis via free radical emulsion polymerization.

    [0003] On the other hand, epoxy resins are used in a wide range of coating applications, including metal coatings.

    [0004] In unmodified form, epoxy resins, especially those based on bisphenol A which are customarily used commercially, are very sparingly soluble or insoluble in water. In principle it is possible to obtain water-dilutable, cationically stabilized resins by reacting epoxy resins with amines and then protonating the basic groups. It is also possible, by modifying the epoxy resin with nonionic hydrophilic groups or with anionic groups, to achieve a limited solubility which is sufficient to impart adequate stability to a dispersion of the modified epoxy resin in water. Such dispersions may be diluted with (further) water.

    [0005] The modified epoxy resin can then be processed from the aqueous dispersion; following removal of the water fraction by evaporation or penetration into the substrate, the resin remains on the surface and, given an appropriate composition of the disperse phase, forms a coalesced film which can be chemically crosslinked by adding appropriate curatives. Since, owing to the ring opening of the epoxide groups, the cationic epoxy-amine adducts contain secondary hydroxyl functions, suitable curatives include compounds which enter into addition reactions or condensation reactions with hydroxyl groups, such as melamine resins, phenolic resins and (blocked) polyfunctional isocyanates.

    [0006] US6673877 describes unsaturated fatty acid modified epoxy resins for metal coatings. Applicants have found that some of the resins described in this patent could be used for wood coatings as well, but do not have good durablility and outdoor weathering performances, especially in cold and wet climates.

    [0007] US 6653370 describes certain water-dilutable epoxy resins, obtainable by an advancement reaction from cationic or cationogenic polyfunctional precursors with diepoxides or polyepoxides, suitable for metal and mineral coatings exhibiting good corrosion protection, without necessitating additional curatives. Some of these resins described in US 6653370 are resins of formula ZYWX which have been obtained by first forming an adduct ZYW by reacting an epoxy resin Z with an unsaturated carboxylic acid W to form an hydroxy ester, where the amounts of Z and W were chosen such that a part of the epoxide groups remains unreacted, and then reacting these hydroxy esters ZW under consumption of the remaining epoxide groups with an aliphatic amine Y to yield carboxylic acid-modified epoxy amine adducts ZYW. Another way to form ZYW was to react the unsaturated carboxylic acids W with epoxy amine adducts ZY, in which case the amounts of Z and Y was chosen such that there remain unreacted epoxide groups in the adduct ZY for reaction with the acids W. The compounds ZYW were then at least partly converted into the salt form, transferred to the aqueous phase and then reacted with a further epoxy resin X to form carboxylic acid-modified cationically stabilised water-dilutable epoxy resins ZYWX.

    [0008] Also disclosed in US 6653370 is a hybrid resin resulting from polymerising, in the presence of ZYWX, ethylenically unsaturated monomers V in the presence of radical initiators.

    [0009] It is however noteworthy that the type of hybrid resins disclosed in US 6653370 have intrinsically a very high dynamic viscosity. For this reason, the compositions disclosed in US 6653370 and in particular the examples 4 and 5 therein, comprise more than 3.5% butyl glycol as solvent in order to bring down the viscosity to an acceptable level for handling or formulation. The presence of solvents is however not a desirable feature from an ecological perspective.

    [0010] Furthermore, Applicants have observed that the hybrid resins disclosed in Examples 4 and 5 contain a high amount of unreacted monomers.

    [0011] Furthermore, although US 6653370 states that good adhesion to metals and mineral substrates is achieved by certain water-dilutable epoxy resins disclosed therein, adherence of epoxy resins, and particularly of two components epoxy resins, on some substrates, such as Cathodic ElectroDeposition (CED) pre-coated steel, remains difficult.

    [0012] Applicants have found that the epoxy amine adducts modified with mainly unsaturated fatty acids do not permit to obtain coating resins for wood applications, especially outdour applications with good properties.

    [0013] It is hence an object of the present invention to develop new hybrid systems which overcome one or more of the above drawbacks, especially resins that are particularly performant when used for wood coatings, especially for outdoor applications. In particular it was an objective of the present invention to develop a resin which has excellent tannin-blocking performances, excellent marker-blocking performances, and that showed enhanced external durability, especially in cold and wet climates,

    [0014] Therefore, in a first aspect, the present invention relates to an aqueous dispersion comprising:
    • at least one fatty acid-modified epoxy amine adduct ZYWS containing amino groups which are at least partially protonated wherein the fatty acid WS contains at least 8 carbon atoms and has an iodine number according to DIN 53241-1:1995-05 of lower than 30, and
    • at least one polymer V obtained from the polymerization of one or more ethylenically unsaturated monomers.


    [0015] The aqueous dispersion is preferably obtained by a process comprising the steps of:
    1. a) obtaining a fatty acid-modified epoxy amine adduct ZYWS by a process comprising the steps of reacting:
      • at least one epoxide compound Z containing at least one, preferably at least two, epoxide groups,
      • at least one amine Y containing at least one primary or secondary amino group, and
      • at least one fatty acid WS, wherein the fatty acid contains at least 8 carbon atoms and has an iodine number according to DIN 53241-1:1995-05 lower than 30,
    2. b) adding to the fatty acid-modified epoxy amine adduct ZYWS obtained in step (a) water and at least one acid, in an amount such that the ratio acid value / amine value of the fatty acid-modified epoxy amine adduct ZYWS is at least 0.05 thereby at least partially protonating the amino groups,
    3. c) optionally reacting the adduct ZYWS obtained in step (b) with at least an epoxide compound X having at least one, preferably at least two, epoxy groups per molecule, the amount of said epoxide compound X being such that the equivalent number of amino groups in ZYWS which are reactive in respect of reaction with an epoxide group is at least equal to the equivalent number of the epoxide groups in the epoxide compound X, and which preferably comprises performing the reaction of ZYWS and X until epoxide groups are no longer detectable in the reaction mixture, thereby obtaining a compound ZYWSX, and
    4. d) polymerizing one or more ethylenically unsaturated monomers in presence of the fatty acid-modified epoxide amine adduct ZYWS obtained at step (b) or in presence of the compound ZYWSX obtained at step (c) thereby forming a polymer V.


    [0016] The process for obtaining a fatty acid-modified epoxy amine adduct ZYWS typically leads to the production of various oligomers of complex structures and to a structure distribution.

    [0017] Aqueous solutions obtained after step (b) or (c) present one or more of the following advantages: they may be clear; they may be transparent; they may be stable, even without use of an additional emulsifier or surfactant, for periods longer than 3 months at 40°C ; they may easily enable the polymerization of monomers ; they may enable a rapid emulsion polymerization of monomers ; they may dispense from any pre-emulsion step for introducing monomers therein in view of their emulsion polymerization ; they may permit the formation therein of polymers having multi-domain structures.

    [0018] Aqueous dispersions obtained after step (d) present one or more of the following advantages: they may have a dynamic viscosity excellent for further handling and formulation, even without the addition of solvent; they may have a very low amount of residual unreacted unsaturated monomers ; they may be used to form a binder resin which has excellent tannin-blocking performances; they may be used to form a binder resin which has excellent marker-blocking performances; they may be used to form a binder resin which has cold check performances at least comparable to state of the art binder resins and may show enhanced external durability, especially in cold and wet climates ; they may be added to a resin (for instance a waterborne two component epoxy system) and thereby improve its adhesion on substrates, especially on steel pre-coated with a CED resin.

    [0019] In a second aspect, the present invention relates to the process to prepare the aqueous dispersion according to any embodiment of the first aspect.

    [0020] In a third aspect, the present invention relates to the use of the aqueous dispersions for the preparation of coatings and to a process for the preparation of a coated article comprising the step of coating at least part of said article with at least one layer of the aqueous dispersion according to the invention and a step of drying said coated substrate in order to remove at least part of the water and form a coated substrate.

    [0021] As used herein and unless provided otherwise, the term "aqueous dispersion" relates to particles, and typically oligomer and/or polymer particles, dispersed in a continuous aqueous medium.

    [0022] As used herein and unless provided otherwise, the term "ethylenically unsaturated monomer" relates to a monomer having at least one carbon-carbon double bond which can undergo radical polymerization.

    [0023] As used herein and unless provided otherwise, the prefix "(meth)acryl" when used to name compounds of the present invention encompasses both "acryl" and "methacryl" and refers to compounds comprising at least one CH2=CHCOO- group or CH2=CCH3COO- group, as well as mixtures thereof and mixtures of such compounds.

    [0024] As used herein and unless provided otherwise, the term "water-dilutable" characterizes a dispersion in water that does not undergo spontaneous phase separation and also for which no macroscopic phase separation occurs on storage at room temperature (23°C) for at least 7 days.

    [0025] As used herein and unless provided otherwise, the term "cationogenic" characterizes compounds which on addition of acids are able to form cations in the presence of water.

    [0026] As used herein and unless provided otherwise, the term "surfactant" relates to a compound that reduces interfacial tension between two liquids or a liquid and a solid.

    [0027] As used herein and unless provided otherwise, the term "emulsifier" relates to a surfactant which is suitable for forming an emulsion in the composition where it is used.

    [0028] According to a specific embodiment of the present invention, the fatty acid-modified epoxy amine adduct ZYWS can comprise or can be a chain extended product (ZYWSX) obtained from the reaction of a fatty acid-modified epoxy amine adduct ZYWS with at least one epoxy compound X. Such chain extended product ZYWSX is usually obtained by reacting the protonated amino groups of the fatty acid-modified epoxy amine adduct with an epoxide X containing at least one, preferably at least two, epoxy groups.

    [0029] Step (a) of the processes described here above in relation to the first and second aspects of the present invention relates to obtaining a fatty acid-modified epoxy amine adduct ZYWS by a process comprising the steps of reacting at least one epoxide compound Z, at least one amine Y and at least one fatty acid WS. Typically, this reaction may be carried out at a temperature of at least 70°C, and preferably at least 100°C. Typically, this reaction may be carried out at a temperature of at most 200°C, and preferably at most 180°C. Optionally, Z, Y and WS may be reacted in presence of a solvent which is non-reactive toward any of Z, Y or WS. This is however typically not necessary.

    [0030] The epoxide groups in compound Z typically react faster with primary and/or secondary amino groups present in Y than with carboxylic acid groups present in WS. Also, a primary amino group in Y will react twice with epoxide groups present in Z before to react with carboxylic acid groups in WS. Therefore, if compound Z is reacted with a mixture of Y and WS, the amount of Z and Y are preferably chosen so that after all reactions between Z and Y took place, there remain unreacted epoxide groups for reaction with the fatty acids WS. Fatty acids form hydroxyl esters when reacted with epoxides.

    [0031] Preferably, the quantity of epoxide Z is chosen such that the equivalent number of epoxide groups provided by compound Z used is superior to the equivalent number of hydrogen atoms attached to nitrogen atoms in the amount of compound Y used.

    [0032] In a preferred embodiment, the quantity of epoxide Z is such that the equivalent number of epoxide groups provided by compound Z used is about equal to the sum of the equivalent number of hydrogen atoms attached to nitrogen atoms provided by the compound Y and the equivalent number of carboxylic group provided by the fatty acid WS used.

    [0033] The amounts of Z, Y and WS are preferably chosen such that there remain only a slight number of unreacted epoxide groups and/or unreacted amine and/or unreacted carboxylic acid groups.

    [0034] The fatty acid-modified epoxy amine adduct ZYWS may be obtained by:
    • reacting at least one epoxide compound Z containing at least one epoxide group with one or more fatty acids WS, yielding a hydroxyl ester ZWS that still has unreacted epoxide groups, and then reacting the hydroxyl ester ZWS with at least one amine Y, or by
    • reacting at least one epoxide compound Z containing at least one epoxide group, with at least one amine Y, yielding an epoxy amine adduct ZY which still has unreacted epoxide groups, and then reacting the epoxy amine adduct ZY with one or more fatty acids WS; or by
    • reacting the epoxy compound Z with a mixture of amine Y and fatty acid Ws.


    [0035] The epoxide compound Z used in the present invention may be aromatic or aliphatic. Preferably, the at least one epoxide compound Z has at least two epoxide groups per molecule. Particularly preferred are epoxide compounds comprising two epoxide groups per molecule.

    [0036] More than one epoxide compound Z may be used. For example an epoxide compound comprising one epoxide group and an epoxide compound comprising two or more, preferably two, epoxide groups may be used. Mixtures of epoxide compounds can be used.

    [0037] Glycidyl ethers of monohydric aliphatic or mixed aliphatic-aromatic alcohols, or glycidyl esters of aliphatic or aromatic monocarboxylic acids are preferred as monoepoxides. The alcohols and acids are preferably selected from the group consisting of linear or branched aliphatic alcohols or acids having from 5 to 16 carbon atoms. Epoxide compounds Z having on average two epoxide groups per molecule, and preferably having an epoxide equivalent of from 170 g/mol to 333 g/mol are preferred. Particularly preferred compounds Z are diglycidyl ethers of aromatic or aliphatic diols and diglycidyl esters of aromatic or aliphatic diacids, such as the diglycidyl ethers of bisphenol A and of bisphenol F, the diglycidyl ethers of ethylene glycol, 1,-4-butylene glycol, and of oligomeric or polymeric 1,2-propylene glycols. Especially preferred is the diglycidyl ether of bisphenol A.

    [0038] The amine Y used in the present invention is preferably selected from aliphatic, linear, branched or cyclic, amines each having at least one secondary or at least one primary amino group. Preferred are amines having from two to twenty, more preferably from three to twenty, carbon atoms.

    [0039] Mixtures of amines Y can be used.

    [0040] According to a preferred embodiment of the present invention, the amine Y comprises at least one amine Y1 comprising at least one, preferably one, primary amine group.

    [0041] According to a preferred embodiment, the amine Y comprises at least one amine Y2 comprising at least one, preferably one, secondary amine group.

    [0042] According to a preferred embodiment, at least one amine Y1 and at least one amine Y2 are used.

    [0043] According to a preferred embodiment of the present invention, at least one amine Y1 and/or Y2 is used comprising besides the primary and/or secondary amino group, also at least one tertiary amino group.

    [0044] The amine Y1 and/or Y2 can contain, besides the primary and/or secondary amino group, also one or more further reactive groups such as hydroxyl groups.

    [0045] The amines Y1 are preferably aliphatic amines having one tertiary, and at least one primary amino group, and from four to twenty carbon atoms. Preferred amines are N,N-dimethylaminoethylamine, N,N-diethylaminoethylamine, N,N-dimethylaminopropyl-amine-3, N,N-diethylaminopropylamine-3, N-(2-aminethyl)-piperidine, and N,N'-bis(2-aminoethyl)-piperazine. Mixtures of these can also be used.

    [0046] The amines Y2 are preferably aliphatic amines having one secondary amino group, and from three to twenty carbon atoms, preferably from four to fourteen carbon atoms. Among the preferred amines Y2 are di-n-butylamine, diethanolamine, and bis-2-hydroxypropylamine. Mixtures of these can also be used.

    [0047] By fatty acids Ws, is understood to designate long chain carboxylic acids having one carboxyl group, and at least 8 carbon atoms, preferably from 8 to 30 carbon atoms. For the purpose of the present invention, a fatty acid or a group of more than one fatty acids WS having collectively an iodine number according to DIN 53241-1:1995-05 lower than 30 will be considered "saturated" because such a low iodine number correspond to number of olefinic double bonds which is not very significant. By "collectively having an iodine number lower than 30", it is meant that when the iodine number is measured on the group of one or more fatty acids WS as a whole, the value obtained is below 30.

    [0048] The one or more fatty acids WS used in the present invention are preferably selected from naturally occurring so-called saturated fatty acids. Such fatty acids very often contain traces or small amounts of unsaturated fatty acids but not leading to an iodine number according to DIN 53241-1:1995-05 of 30 or higher.

    [0049] Preferably, the fatty acids or the one or more fatty acids WS preferably have collectively an iodine number according to DIN 53241-1:1995-05 lower than 20.

    [0050] The fatty acids WS used in the present invention may be linear or branched. Typically, they may each individually have from 6 to 36 carbon atoms but the group of one or more carboxylic acid Ws has in average at least 8 carbon atoms per molecule constituting the group, preferably an average of from 8 to 30 carbon atoms. Especially preferred fatty acids WS used in the present invention are Caprylic acid (C8), Decanoic acid (C10), Lauric acid (C12), Myristic acid (C14), Palmic acid (C16), Stearic acid (C18), as well as mixtures thereof. Among the fatty acids derived from natural occurring oils, those containing at least 85 %, preferably at least 90 %, by weight of saturated fatty acids are preferred in the present invention.

    [0051] The fatty acid-modified epoxy amine adduct ZYWS preferably has an amine value according to DIN 53176:2002-11 of at least 50 mg KOH/g. Such high amine values are advantageous as they permit to obtain a clear, transparent aqueous solutions after step (b) or (c). In case the amine value is too low, an opaque solution is obtained instead of a clear and transparent solution, which leads to reduced stability thereof. More preferably, the fatty acid-modified epoxy amine adduct ZYWS has an amine value according to DIN 53176:2002-11 of at least 80 mg KOH/g, and most preferably of at least 120 mg KOH/g. The amine value is usually at most 300 mg KOH/g. Preferably, the nature and the respective amounts of Z, Y and Ws are selected in such a way as to obtain such an amine value.

    [0052] In Step (b) of the process according to the first and second aspect of the present invention, water and at least one acid are added to the fatty acid modified epoxy amine adduct ZYWs obtained after step (a). The quantity of acid added is chosen in order to obtain a ratio acid value / amine value of the fatty acid modified epoxide amine adduct ZYWS of above 0.05.

    [0053] The acid may typically be an organic acid or an inorganic acid. Organic acids are preferred, more specifically volatile acids. Particularly preferred are water-soluble carboxylic acids which have short carbon chains having six carbon atoms or less, preferably 4 carbon atoms or less. Acids are most preferably selected from formic acid, acetic acid and lactic acid.

    [0054] The quantity of water and acid in step (b) is preferably such that a clear and homogeneous aqueous solution of a ZYWS adduct at least partially converted into a salt form (or in other words, at least partially protonated) in an aqueous media. The aqueous media is preferably deionized water.

    [0055] In the conversion step (b) (which may also be called neutralization step b), the amino groups of the fatty acid-modified epoxide amine adduct ZYWS containing tertiary amino groups obtained at step (a) are totally or partially converted with a protonating agent and the adduct is dissolved in an aqueous media (typically water). By totally or partially converted is meant in the present invention that all or at least part of the amine groups present in the adduct are converted in a salt form by an acid.

    [0056] Preferably, at least 5% of the amine groups present in the adduct are converted by an acid.

    [0057] The conversion degree is preferably chosen in such a way that the obtained aqueous dispersion is clear and transparent.

    [0058] The amount of acid used is typically chosen to yield the desired degree of conversion of the tertiary amino groups present in the adduct ZYWS. The degree of conversion is generally defined as the fraction of tertiary amino groups converted into a salt form in the adduct ZYWS.

    [0059] Typically, the at least partially converted adduct ZYWS obtained at step (b) may have a ratio acid value / amine value, corresponding to a conversion degree, of at least 0.1; preferably at least 0.2 ; more preferably at least 0.3 and most preferably at least 0.4.

    [0060] Typically, the at least partially converted adduct ZYWS obtained at step (b) may have a ratio acid value / amine value not larger than 2.0, preferably not larger than 1, more preferably not larger than 0.9 and most preferably not larger than 0.8.

    [0061] For instance, the ratio acid value / amine value may be from 0.2 to 2.0, preferably from 0.2 to 1.0 and more preferably from 0.3 to 0.8.

    [0062] Acid values can be determined according to DIN EN ISO 2114:2002-06.

    [0063] Usually Step (b) is conducted by mixing the adduct ZYWS containing tertiary amino groups obtained at step (a) and a water/acid solution at a temperature of at least 20°C, preferably at least 40°C, more preferably at least 50°C. The temperature generally does not exceed 90°C, preferably 85 °C, more preferably 80°C.

    [0064] The amount of adduct ZYWS and the amount of water/acid (protonating agent) solution are typically chosen to yield a solution of the at least partially converted adduct ZYWS in water of at least 5 weight %, preferably at least 10 weight%, more preferably at least 15 weight % total and most preferably at least 20 weight %. The amount of adduct ZYWS in the solution is determined according to DIN 55671:2002-09. The amount of adduct ZYWs is usually not more than 60, preferably not more than 50 weight %.

    [0065] The mixture of the at least partially converted adduct ZYWS and water/acid mixture is typically stirred until a homogeneous solution is obtained.

    [0066] Typically, the mass fraction of solid in the solution may be from 10 to 60%, preferably from 20 to 50%, as determined according to DIN 55671:2002-09.

    [0067] The aqueous solution obtained at step (b) has typically a pH of at least 4.0, preferably at least 4.5 and more preferably at least 5.0. The pH generally does not exceed 7.0, preferably 6.5 and more preferably 6.0.

    [0068] In a specific embodiment, the process may further comprise a step (c), after step (b), of reacting the at least partially converted adduct ZYWS with at least an epoxide compound X having at least one, preferably at least two, epoxy groups per molecule, the amount of each of said at least an epoxide X being such that the equivalent number of amino groups in ZWSY which are reactive in respect of addition reaction with an epoxide group is at least the same, preferably at least 10% greater and more preferably at least 20% greater, than the equivalent number of the epoxide groups in the at least an epoxide X. This step preferably comprises performing the reaction of ZWSY and X until epoxide groups are no longer detectable in the reaction mixture, thereby obtaining an aqueous solution comprising a compound ZYWSX. In other words, the amount of the epoxy compound X and the epoxy-amine-fatty acid adduct ZYW may be chosen such that the number of reactive (in respect of addition to the epoxide) amino groups in ZYW is at least the same as that of the epoxide groups in X. This aqueous solution is typically clear and transparent.

    [0069] Suitable epoxy compounds X are preferably selected from those described in relation with exoxy compounds Z. The epoxy compound X may be the same of different from epoxy compound Z.

    [0070] The aqueous dispersion obtained at step (c) has typically a pH of at least 4.0, preferably at least 4.5 and more preferably at least 5.0. The pH generally does not exceed 7.0, preferably 6.5 and more preferably 6.0.

    [0071] Performing step (c) typically leads to the reaction of tertiary amino groups present in ZYWs with X to form cationically-charged quaternary amine functionalities. This reaction can be referred to as a quaternization reaction. It typically only occurs after that all the primary and secondary amino groups have reacted. During reaction the progress of quaternization can be monitored via a decrease in acid value according to DIN EN ISO 2114:2002-06.

    [0072] Typically, step (c) may be performed at 40°C or more, preferably 50°C or more and most preferably 60°C or more. Typically, step (c) is performed at 100°C or less, preferably 90°C or less and most preferably 80°C or less. A preferred temperature range is 50 to 90°C and the most preferred temperature range is 60 to 80°C.

    [0073] The reaction is preferably performed until epoxide groups are no longer detectable in the reaction mixture. Typically, this translates into maintaining a temperature as mentioned for step (c) until epoxide groups are no longer detectable.

    [0074] The aqueous solution obtained after step (b) or (c) according to specific embodiment of the present invention is usually further characterized by a solid content of from 15 to 35 wt%, preferably from 20 to 30 wt%, as determined according to DIN 55671:2002-09.

    [0075] The aqueous solutions obtained after step (b) or (c) according to specific embodiment of the present invention may typically have an acid value determined on the solid content of at least 50 mg KOH/g, preferably at least 80 mg KOH/g. The acid value typically does not exceed 150 mg KOH/g, preferably 120 mg KOH/g. It can be measured according to the standard method DIN EN ISO 2114:2002-06.

    [0076] The process according to the invention further comprises a step (d), after step (b), or if a step (c) has been performed, after step (c). In this further step (d), one or more ethylenically unsaturated monomers are polymerized in the aqueous solution obtained at step (b) or (c) thereby forming an aqueous dispersion of a polymer V. These monomers are polymerized by emulsion polymerization, typically in presence of a radical initiator.

    [0077] The obtained reaction products ZYWSV or ZYWSXV are typically simple mixtures of the polymer V, stabilized by the emulsifier polymer ZYWS or ZYWSX. Most typically, the obtained polymer dispersion particles show a core/shell structure with the polymer V forming the "core domain", surrounded by the emulsifier polymer ZYWS or ZYWSX, forming the "shell domain".

    [0078] Emulsion polymerizations of ethylenically unsaturated monomers are known to the skilled person. They are usually distinguished by the fact that radical polymerization of ethylenically unsaturated monomers is carried out in the aqueous phase and in the presence of radical initiators and emulsifiers. In the present case, compound ZYWS or ZYWSX plays the role of the emulsifier.

    [0079] Examples of suitable monomers for the preparation of the copolymer V at step (d) include styrenic derivatives such as styrene, vinyltoluene, alpha-methylstyrene, ethylstyrene, isopropylstyrene, tert-butylstyrene, 2,4-dimethylstyrene, diethylstyrene, o-methyl-isopropylstyrene, chlorostyrene, fluorostyrene, iodostyrene, bromostyrene, 2,4-cyanostyrene, hydroxystyrene, nitrostyrene, phenylstyrene.

    [0080] Further suitable monomers also include esters of (meth)acrylic or crotonic acid with saturated linear or cyclic alcohols containing 1 to 20, more preferably from 1 to 14, carbons on the alkyl or cyclic group. Examples include but are not limited to alkyl(meth)acrylates such as methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, butyl (meth)acrylate, pentyl (meth)acrylate, hexyl (meth)acrylate, heptyl (meth)acrylate, octyl (meth)acrylate, nonyl (meth)acrylate, decyl (meth)acrylate, undecyl (meth)acrylate, dodecyl (meth)acrylate, tridecyl (meth)acrylate, tetradecyl (meth)acrylate and isobornyl (meth)acrylate. Suitable monomers can also be selected from heterocyclic (meth)acrylates like for instance tetrahydrofurfuryl (meth)acrylate, from functionalized (meth)acrylates such as epoxy-functional (meth)acrylates, especially glycidyl (meth)acrylate, and hydroxyl-functionalized (meth)acrylates, such as hydroxyalkyl (meth)acrylates. Some nonlimiting examples are hydroxymethyl (meth)acrylate, hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, hydroxybutyl (meth)acrylate, hydroxypentyl(meth)acrylate, hydroxyhexyl (meth)acrylate hydroxyheptyl (meth)acrylate, hydroxyoctyl (meth)acrylate,hydroxynonyl (meth)acrylate, hydroxydecyl (meth)acrylate, hydroxyundecyl (meth)acrylate, hydroxydodecyl (meth)acrylate, hydroxytridecyl (meth)acrylate, hydroxytetradecyl (meth)acrylate. Amino functionalized monomers can also be used, one nonlimiting example being N,N-dimethylaminoethyl (meth)acrylate.

    [0081] Further usable monomers include (meth)acrylamide, vinyl acetate, (meth)acrylonitrile, N-vinylformamide, N-vinylpyrrolidone, N-butoxymethyl (meth)acrylamide, N-methylol (meth)acrylamide and monomers that contain besides a polymerizable group such as a vinyl or (meth)acryl group also a keto group, such as diacetone (meth)acrylamide, or an aceto acetoxy group such as in acetoaecetoxyethylmethacrylate

    [0082] Mixtures of any of the listed monomers can also be used.

    [0083] Preferably, at least one of said monomers is a (meth)acrylate, a styrenic monomer, an acrylamide monomer or a vinyl carboxylate. More preferably, the one or more monomers are (meth)acrylate monomers, styrenic monomers, acrylamide monomers, vinyl carboxylate monomers or a combination thereof. Preferably at least one of said monomers is a (meth)acrylate, a styrenic monomer, an acrylamide monomer or a vinyl carboxylate.

    [0084] Examples of preferred ethylenically unsaturated monomers used to prepare the polymer V at step (d) are styrenic monomers such as styrene, vinyltoluene, alpha-methylstyrene, ethylstyrene; acrylamides such as, acrylamide, methacrylamide; alkyl(meth)acrylates containing from 1 to 20, preferably from 1 to 14, carbons in the alkyl group such as, methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, butyl (meth)acrylate, pentyl (meth)acrylate, hexyl (meth)acrylate, heptyl (meth)acrylate, octyl (meth)acrylate, nonyl (meth)acrylate, decyl (meth)acrylate, undecyl (meth)acrylate, dodecyl (meth)acrylate, tridecyl (meth)acrylate, tetradecyl (meth)acrylate; heterocyclic (meth)acrylate like for instance tetrahydrofurfuryl (meth)acrylate, isobornyl (meth)acrylate; functionalized (meth)acrylates such as epoxy-functional (meth)acrylates, especially glycidyl (meth)acrylate, and hydroxyl-functionalized (meth)acrylates, such as hydroxyalkyl hydroxyalkyl (meth)acrylates such as hydroxymethyl (meth)acrylate, hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, hydroxybutyl (meth)acrylate, hydroxypentyl(meth)acrylate, hydroxyhexyl (meth)acrylate hydroxyheptyl (meth)acrylate, hydroxyoctyl (meth)acrylate, hydroxynonyl (meth)acrylate, hydroxydecyl (meth)acrylate, hydroxyundecyl (meth)acrylate, hydroxydodecyl (meth)acrylate, hydroxytridecyl (meth)acrylate, hydroxytetradecyl (meth)acrylate and vinyl acetate. Mixtures of any of these monomers can also be used.

    [0085] The most preferred monomers for the preparation of polymer V are styrene, vinyltoluene, alpha-methylstyrene, ethylstyrene, methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, butyl (meth)acrylate, pentyl (meth)acrylate, hexyl (meth)acrylate, heptyl (meth)acrylate, octyl (meth)acrylate, glycidyl (meth)acrylate, hydroxymethyl (meth)acrylate, hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, hydroxybutyl (meth)acrylate, diacetone (meth)acrylamide, acetoacetoxyethyl (meth)acrylate and mixtures thereof.

    [0086] Also poly functional monomers, such as di(meth)acrylates and divinyl monomers can be used as small amounts in the preparation of polymer V, including functionalized di(meth)acrylates such as glycerol di(meth)acrylate. Preferably, at most 3 wt% of the monomers used are monomers having two or more ethylenic unsaturations.

    [0087] The monomers usable for the preparation of copolymer V preferably do not contain large amounts of ethylenically unsaturated monomers bearing an acid group or group capable of forming an acid group when contacted with water. Preferably, at most 5 wt% of the monomers used are monomers having an acid group (e.g. -COOH or -SO3H) or a group capable of forming an acid group when contacted with water.

    [0088] The types and amounts of monomers usable for the preparation of polymer V are preferably chosen so that copolymer V is hydrophobic. Hence, particularly preferred monomers have a low solubility in water, preferably less than 15%, more preferably less than 5%, and most preferably less than 3%. The solubility in water is measured at 25°C, as a percentage of grams of dissolved monomers per 100 grams of water.

    [0089] The monomer mixtures used for the preparation of copolymers V preferably contain at least 15 wt%, more preferably at least 25 wt%, of monomers having a glass transition temperature (Tg) of their homopolymerisate of at least 50°C, based on the total of monomers used in step d. The monomer mixtures preferably do not contain more than 90 wt%, more preferably not more than 80 wt %, of monomers having a glass transition temperature (Tg) of their homopolymerisate of at least 50°C, based on the total of monomers used in step d. Particularly, and especially when used in a formulation without other binder resins, the monomer mixtures most preferably do not contain more than 70 wt% of monomers having a glass transition temperature (Tg) of at least 50 °C, based on the total amount of monomers used in step d. In the present invention, the glass transition temperature (Tg) of polymer is determined according to DIN EN 61006.

    [0090] Preferably the process is performed with the at least partially protonated compound ZYWS or ZYWSX as the sole emulsifier. When the partially or totally protonated adduct ZYWS or ZYWSX of the invention is used in the emulsion polymerization, the good emulsifying power of this adduct advantageously makes the presence of additional emulsifiers unnecessary.

    [0091] If an additional emulsifier is nevertheless used, it may be non-ionic such as alkyl or alkyl phenol ethoxylated derivatives, anionic such as salts of alkyl sulfates, phosphates or sulfonates or cationic such as quaternary ammonium salts of alkyl amines.

    [0092] The amount of ZYWS or ZYWSX in the dispersion preferably is at least 12 wt%, more preferably at least 15 wt% and it does not exceed preferably 37 wt%, more preferably 35 wt% based on the sum of ZYWS or ZYWSX) and V.

    [0093] The aqueous dispersion according to the invention preferably comprises:
    • from 10 wt% to 40 wt% of at least partially protonated adduct ZYWS and/or ZYWSX, and
    • from 60 wt% to 90 wt% of polymer V,
    based on the sum of ZYWS (and/or ZYWSX) and V.

    [0094] Typically, the amount of polymer V represent from 50 wt% to 95 wt%, preferably from 60 wt% to 90 wt%, most preferably from 65 wt% to 80 wt% of the sum of the amount of polymer V and at least partially converted adduct ZYWS or ZYWSX. The components mentioned can be introduced into the emulsion polymerization process in various ways.

    [0095] The amount of polymer V in the dispersion preferably is at least 63 wt%, more preferably at least 65 wt% and it does not exceed preferably 88 wt%, more preferably 85 wt% based on the sum of ZYWS (or ZYWSX) and V.

    [0096] The aqueous dispersion obtained at step (d) has typically a pH of at least 4.0, preferably at least 4.5 and more preferably at least 5.0. The pH generally does not exceed 7.0, preferably 6.5 and more preferably 6.0.

    [0097] Typically, the major portion of the aqueous phase is introduced at the beginning and portions of water can be further added during the reaction in different ways such as in the form of a radical initiator solution or a monomer pre-emulsion.

    [0098] Step (d) can be carried out over a broad temperature range. Typically, the polymerizing step is performed at a temperature of 30°C or more. Also typical is performing the polymerizing step at a temperature of 99°C or less. During the polymerization (step d), the reaction temperature usually ranges from 30 to 99°C. It can be maintained constant or can be varied during step (d).

    [0099] The radical initiator is usually added to the solution in the pure form or in an aqueous solution at once, or continuously or incrementally over the reaction time.

    [0100] Suitable initiators are typically thermal radical-forming compounds like azo compounds such as 2,2'-azobis(isobutylonitrile). Particularly preferred are water soluble azo compounds such as 2,2'-Azobis(2-amidinopropane) dihydrochloride and the like. Other suitable initiators are redox systems. Examples of suitable redox systems are cumene hydroperoxide/sodium metabisulphite, hydrogen peroxide/ascorbic acid and tert-butyl hydroperoxide/ascorbic acid. Other suitable initiators can also be used. "Anionic" initiator systems like ammonium or potassium persulfates are not preferred as anionically charged initiator systems might negatively interfere with the cationic emulsifier polymer ZYWS(X), resulting in reduced monomer conversion. The initiators are generally used in amounts between 0.01 and 5.0 wt% relative to the solution. The amount used is preferably from 0.01 to 2.0 wt%.

    [0101] After addition of at least a portion of the radical initiator, the monomer mixture of step (d) can be introduced in pure form or as a pre-emulsion in water. Alternatively, the radical initiator can be added to the monomer mixture. An advantage of the process according to the present invention is that it enables a very easy and fast emulsion polymerization reaction, without the need of any pre-emulsion step for monomers, as it is the case in most other synthetic routes using additional surfactants. The one or more monomers are preferably introduced in the aqueous solution in a non-pre-emulsified form. More preferably, the monomer mixture of step (d) may be introduced in pure form. The one or more monomers can be introduced in its entirety or continuously or incrementally during the emulsion polymerization. The one or more monomers may for instance be introduced over a period of at least one hour. The one or more monomers may for instance be introduced over a period of at most eight hours. They are preferably introduced over a period of 1 to 8 hours, preferably over a period of 2 to 6 hours.

    [0102] In a particular embodiment of the invention, it is possible to add different monomers or monomer mixtures in sequences. Using this approach, the polymer V (here a copolymer) can be designed to have multi-domain structures, which may show multiple transition temperatures Tg.

    [0103] In a specific variant of this embodiment, at least two different monomers or monomer mixtures are added sequentially to prepare copolymer V and the obtained copolymer V has at least two Tg. For instance a copolymer V may be prepared with a first monomer/monomers mixture having a Tg after copolymerization above 60°C and a second monomer/monomers mixture having a Tg after copolymerization below 15°C. Such dispersions enable to obtain films having high film hardness while excellent film formation is still observed without the need of additional coalescing agents.

    [0104] The polymerization usually proceeds until the residual monomer content is lower than 1 wt%, preferably lower than 0.5 wt%, more preferably lower than 0.1 wt% with respect to the total weight of monomers used. The residual monomer content is determined according to DIN 55682:2000-12.

    [0105] An optional post-initiation can be performed in case the amount of residual monomers is higher than 1 wt% after 8 hours of reaction. It is typically performed by addition of an additional portion of radical initiator or redox-initiator system to ensure a residual monomer content lower than 1 wt%, preferably lower than 0.5 wt%, more preferably lower than 0.1 wt%.

    [0106] The aqueous dispersion obtained after step (d) according to embodiments of the present invention is usually further characterized by a solid content of from 30 to 50 wt%, preferably from 35 to 45 wt%, as determined according to DIN 55671:2002-09.

    [0107] The aqueous dispersions obtained after step (d) according to embodiments of the present invention may typically have an acid value determined on the solid content of at least 15 mg KOH/g, preferably at least 25 mg KOH/g. The acid value typically does not exceed 50 mg KOH/g, preferably 35 mg KOH/g. It can be measured according to the standard method DIN EN ISO 2114:2002-06.

    [0108] The dynamic viscosity of the aqueous dispersions obtained after step (d) according to embodiments of the present invention typically ranges from 50 to 10000, preferably from 50 to 5000, mPa.s at 23°C and a shear rate of 25 s-1, according to DIN EN ISO 3219:1994-10. Particularly preferred are aqueous dispersions having a viscosity in the range of 100 to 2000 mPa.s.

    [0109] In general, it is believed that the particles of the dispersion comprise an inner domain optionally substantially formed by the polymer V and an outer domain optionally substantially formed by the adduct ZYWS or ZYWSX. The outer domain is located at and/or towards the surface of the particles and may form a continuous or one or more discrete domains on the outer surface of the inner domain.

    [0110] It is believed that the emulsifying properties of the partially or totally protonated adduct ZYWS and ZYWS(X) allows the preparation of aqueous dispersions comprising a polymer V that are stable without the need of the addition of an external surfactant. By stable is meant that no noticeable precipitation, sedimentation or coagulation is observed when the aqueous dispersion is stored for at least 3 months at a temperature of 40°C. Hence, the compositions according to the invention are preferably substantially free of additional surfactant. By substantially free is meant that the composition comprises less than 2 wt% on the solid content of external surfactant, preferably less than 1 wt%, more preferably less than 0.5 wt %, most preferably less than 0.1 wt%, or no detectable additional surfactant at all.

    [0111] Various additives and compounds that are known to those skilled in the art may also be added to the aqueous dispersions according to the invention. Those additives and compounds include but are not limited to fungicides, bactericides, pigments and extenders, active and/or inactive fillers, thickeners, substrate wetting agents, driers, organic and/or inorganic solvents, buffers, coalescing agents, defoamers, pigments, leveling additives, oils, waxes and the like.

    [0112] The aqueous dispersions according to the invention are suitable as coating agents or binder agents in general. The aqueous dispersions according to the invention may be used as single binders. They also may be used in blends with at least one other binder. By "other" is meant herein a binder different from the aqueous dispersion according to the invention, including aqueous and non-aqueous binders. Binders that are compatible with the dispersion of the invention are preferred. By "compatible" is meant that no noticeable precipitation, sedimentation or coagulation is observed when the blend is stored for at least 3 months at a temperature of 40°C. Particularly preferred binders are aqueous binders. Examples include but are not limited to blends with alkyd resins, acrylic resins, polyurethane resins, epoxy resins, oils, waxes and the like, other examples include hybrid of the listed resins such as for instance acrylic-alkyd hybrid resins, acrylic-polyurethane hybrid resins, alkyd-polyurethane hybrid resins. Preferred blends are blends with alkyd resins, epoxy resins or polyurethane dispersions.

    [0113] The aqueous dispersions according to the invention may be used on various substrates. Examples of possible substrates include but are not limited to wood, wood fibre, cellulose, polymeric substrates such as polystyrene, polyolefins, polyesters, polyamides, polyurethanes, polycarbonates and the like, inorganic substrates like metal (e.g. steel) and pre-treated metal substrates (e.g. coated metal such as CED pre-coated steel), concrete, glass and silicates in general.

    [0114] The aqueous dispersions according to the invention may be applied to the substrates by various techniques known to those skilled in the art. Those techniques include but are not limited to brushing, spraying, dipping, pouring, draining, electro-deposition, roller coating and the like. The drying of formulations containing the aqueous dispersions according to the invention may either happen at ambient temperature or at forced conditions like elevated temperature and/or reduced pressure for a variable time.

    [0115] The aqueous dispersions according to the invention are particularly suitable for wood stain, wood trim and stain blocking applications. In particular, the dispersions according to the invention are particularly suitable for entering the composition of stain-blocking coatings (e.g. stain-blocking primers) where they provide them with excellent tannin-blocking, marker-blocking, freeze-thaw-resistance, UV-resistance, water-resistance, cold check resistance and external durability. Furthermore, the compositions according to the invention tend to promote the adhesion of primer or coating compositions in which they are incorporated. In particular, when added to a two component epoxy system, the adhesion of the system is markedly improved, in particular on hard to coat substrates such as CED pre-coated steel plates. The enhanced adhesion characteristics may also be advantageous for various other organic and/or inorganic substrates like polymeric, concrete or glass substrates.

    [0116] In a second aspect, the present invention relates to a process for the preparation of an aqueous dispersion. The features of the process are as described above in the first aspect.

    [0117] The present invention further relates to the use of an aqueous dispersion according to any embodiment of the present invention for promoting the substrate adhesion properties of a composition. In an embodiment, the present invention relates to the use of an aqueous dispersion according to any embodiment of the present invention for promoting the adhesion of a composition to a CED coating such as a CED coating on a steel substrate.

    [0118] The present invention further relates to a process for preparing a coated substrate or article, wherein at least part of the surface of the substrate or article is coated with an aqueous dispersion according to any embodiment of the invention. In a further aspect, the invention finally relates to the coated substrates or articles hereby obtained.

    [0119] The examples which follow illustrate embodiments of the invention without limiting it.

    [0120] In these examples, the solid contents of the aqueous dispersions were determined according to DIN 55671:2002-09. The amine values were determined according to DIN 53176:2002-11. The acid values were measured according to the standard method DIN EN ISO 2114:2002-06

    [0121] The types and amounts of reagents used to prepare polymers of examples 1 and 2 and comparative example 3 are summarized in Table 1.

    Preparation of Emulsifier polymers ZYWS (Example 1)



    [0122] In a 4-necked round glass reactor 214,0 g (1,0 mole) of Coconut oil fatty acid (WS), 306,6g (3,0 mole) of dimethylaminopropyl amine (Y1) and 105,1g (1,0 mole) of diethanol amine (Y2) were mixed upon stirring and heated to 60°C. Then 1520g (4,0 mole) of bisphenol-A-diglycidyl ether (BADGE; Z) were continuously added over 60 minutes to the reaction mixture. Due to the exothermic nature of the reaction, the reaction temperature gradually rose to 160°C during the addition of the epoxide. The resulting reaction mixture was stirred for one additional hour at 160°C. Then the viscous reaction product was poured into a pre-mixed solution of 220g aqueous formic acid (85%) in 5000g de-ionized water and further stirred at 70°C until a clear, transparent, brownish aqueous solution of the emulsifier polymer ZYWS was obtained. Finally, the resulting reaction product was adjusted to an overall solids content of 25,1% by the addition of de-ionized water.

    Preparation of Emulsifier polymers ZYWSX (Example 2)



    [0123] Example 1 was repeated except that before adjusting the reaction product to the overall solids content of 25,1%, an additional portion of 107,3g (0,28 mole) bisphenol-A-diglycidyl ether (BADGE; X) was added to this aqueous solution in one shot and stirred for 3 to 5 hours at 70°C until full conversion of the epoxide was observed by titration. A transparent, clear, brownish aqueous solution of emulsifier polymer ZYWSX was obtained as reaction product. Finally, the resulting reaction product was adjusted to an overall solids content of 25,1% by the addition of de-ionized water.

    Preparation of Emulsifier polymers ZYWX (Comparative Example 3)



    [0124] Example 2 was repeated except that 280,0 g (1,00 mole) of tall oil fatty acid was used instead of the 214,0 g (1,00 mole) coconut oil fatty acid.

    [0125] The types and amounts of reagents used to prepare polymers of examples 1 and 2 and comparative example 3 are summarized in Table 1.

    [0126] Characteristics of polymers of examples 1 and 2 and comparative example 3 are summarized in Table 1 and are obtained according to the test methods described in the specification.
    Table 1: Composition (g) of Polymers 1, 2 and Comparative Polymer 3:
    ComponentExample 1Example 2Comp. Example 3
    Coconut oil fatty acid (Ws) 214,0 g (1,0 mole) 214,0 g (1,00 mole) ---
    Tall oil fatty acid (W) --- --- 280,0 g (1,00 mole)
    Dimethylaminopropyl amine (Y1) 306,6 g (3,0 mole) 306,6 g (3,00 mole) 306,6 g (3,00 mole)
    Diethanol amine (Y2) 105,1 g (1,0 mole) 105,1 g (1,00 mole) 105,1 g (1,00 mole)
    BADGE (Z) 1520,0 g (4,00 mole) 1520,0 g (4,00 mole) 1520,0 g (4,00 mole)
    Deionized H2O (in total) 6183 g 6500 g 6700 g
    Aqueous formic acid (85%) 220 g (4,06 mole) 220 g (4,06 mole) 220 g (4,06 mole)
    BADGE (X) --- 107,3 g (0,28 mole) 107,3 g (0,28 mole)
           
    Solids content % 25,1% 25,1% 25,1%
    Amine value (mg KOH/g solids) 183 174 170
    Acid value (mg KOH/g solids) 108 94 93
    pH 5,4 5,4 5,3


    [0127] The types and amounts of reagents used to prepare final dispersions of examples 4 and 5 and comparative example 6 are summarized in Table 2.

    Preparation of final Dispersions ZYWSV (Example 4)



    [0128] 1505g of Emulsifier Polymer solution obtained as reaction product of Example 1 and 660g of de-ionized water were added to a 4-necked round glass reactor and heated to 65°C upon stirring. Then 7,2g of 2,2'-Azobis(2-amidinopropane) dihydrochloride (radical initiator; trade name: WAKO V-50) were added to the solution and dissolved for 10 minutes at 65°C. Then a homogeneous mixture of ethylenically unsaturated monomers consisting of 216g 2-ethylhexyl acrylate, 216g butyl acrylate, 36g styrene and 372g methyl methacrylate was continuously added over a period of 4 hours at 65°C. The reaction mixture was held for one additional hours at 65°C, followed by the addition of 1,2g 2,2'-Azobis(2-amidinopropane) dihydrochloride (radical initiator; trade name: WAKO V-50) and 6g methyl methacrylate for post-initiation. The reaction mixture was held for two additional hours at 70°C before allowed to cool to ambient temperature, which yielded the final product ZYWSV as a yellowish aqueous dispersion. This dispersion proved to be perfectly storage stable for >3 months at 40°C.

    Preparation of final Dispersions ZYWSXV (Example 5)



    [0129] Example 4 was repeated but the reaction product of Example 2 was used instead of the reaction product of Example 1 to yield as a final product, ZYWSXV as a yellowish aqueous dispersion. This dispersion proved to be perfectly storage stable for >3 months at 40°C.

    Preparation of final Dispersions ZYWXV (Comparative Example 6)



    [0130] Example 4 was repeated but the reaction product of Comp. Example 3 was used instead of the reaction product of Example 1 to yield as a final product, ZYWXV as a yellowish aqueous dispersion.

    [0131] Characteristics of final dispersions of examples 4 and 5 and comparative example 6 are summarized in Table 2 and are obtained according to the test methods described in the specification.
    Table 2: Composition (g) of Examples 4, 5 and Comparative Example 6:
    ComponentExample 4Example 5Comp. Example 6
    Emulsifier Polymer Example 1 1505g (377,8g solids)    
    Emulsifier Polymer Example 2   1505g (377,8g solids)  
    Emulsifier Polymer Comp. Example 3     1505g (377,8g solids)
    Deionized water 660 g 660 g 660 g
    WAKO V-50 7,2 g 7,2 g 7,2 g
    2-Ethylhexyl acrylate 216 g 216 g 216 g
    Butyl acrylate 216 g 216 g 216 g
    Styrene 36g 36g 36g
    Methyl methacrylate 372 g 372 g 372 g
    WAKO V-50 1,2 g 1,2 g 1,2 g
    Methyl methacrylate 6,0 g 6,0 g 6,0 g
           
    Solids content % 40,0 % 40,2 % 39,5 %
    Dynamic viscosity (mPas; 23°C; 25 1/s) 159 mPas 246 mPas 10320 mPas
    Amine value (mg KOH/g solids) 55 53 51
    Acid value (mg KOH/g solids) 33 30 30
    Particle size average (nm) 61 nm 61 nm 63 nm
    Overall residual monomer content (%) 0,06% 0,08% 0,65%
    pH 5,4 5,3 5,3


    [0132] From table 2, it can be concluded that at 40% solids content the dispersions 4 and 5 of the present invention show a dynamic viscosity level in the range 100-300 mPas (measured at a shear rate of 25 s-1 @ 23°C), which proves to be excellent for further handling and formulation. Residual monomer levels (combined amount of residual monomers) are found to be below 0,1% for Examples 4 and 5. Those facts represent a clear advantage over Comparative Example 6 which is analog to the prior art published in patent US 6653370 B2. Comparative Example 6 uses unsaturated fatty acids for the reparation of the emulsifier polymer, as it was done in US 6653370 B2. Comparing the residual monomer levels of Example 4 and 5 (<0,1%) to the residual monomer levels of Comparative Example 6 (>0,6%) which contains unsaturated fatty acid moieties shows a strong effect which can be attributed to the presence of unsaturated fatty acids in Example.6.

    [0133] Without being bound by theory, it is hypothesized that the presence of unsaturated fatty acids during radical initiated emulsion polymerization reactions leads to the formation of stabilized fatty acid radicals by radical transfer from growing polymer chains to the unsaturated fatty acid moieties. This radical transfer terminates the growing polymer chains, which leads to incomplete conversion of ethylenically unsaturated monomers, which leads to higher residual monomer levels in the final products (this might cause some VOC and regulatory issues for the final product in certain applications).

    [0134] Furthermore, Comparative Example 6 shows a very high dynamic viscosity of > 10000 mPas (shear rate of 25 s-1 @ 23°C) at an overall solids content of <40%. It has surprisingly been found that replacing the unsaturated tall oil fatty acid (used in Comparative Example 6 and in US 6653370 B2) by a saturated fatty acid (coconut oil fatty acid; Example 5) leads to a huge decrease in dynamic viscosity while long term storage stability (>3 months @ 40°C) is not negatively affected. This finding represents a clear advantage over the prior art as higher solid contents for the dispersions according to the invention are possible while still keeping the dynamic viscosity in a reasonable and workable range for formulation and further processing. Example 5, which uses saturated fatty acids, displays a dynamic viscosity of <300 (shear rate of 25 s-1 @ 23°C) at an overall solids content of >40%.

    [0135] Although Example 4 of prior art US 6653370 B2 only exhibits 120 mPas (shear rate 100 s-1 @ 23°C) at a solid content of 39,7% despite the fact that unsaturated fatty acids (tall oil fatty acids) are used, it was observed that in this case, the low viscosity can only be achieved by addition of >3,5% butyl glycol as solvent. The use of saturated fatty acids as outlined in the present invention eliminates the need of additional organic solvents to bring down the dynamic viscosity. This represents a clear advantage over the prior art with respect to VOC regulations and eco-friendliness.

    Example 7: Preparation and evaluation of the properties of a stain-blocking primer prepared from aqueous dispersion according to the present invention.


    7.1. Formulation of a Primer



    [0136] For evaluating the tannin- and marker blocking performance of the hybrid resins according to the invention the following primer formulations have been prepared as follow:
    1. In a first step a mill base has been prepared according to the following formulation:
    Table 3: Composition of Mill Base 1:
    Amount [g]Substance
    18.93 g De-ionized water
    8.71 g ADDITOL® VXW 6208 (dispersing additive)
    15.44 g ASP 600 (extender)
    40.08 g KRONOS® 2059 (pigment)
    14.20 g Blanc Fixe micro (extender)
    2.64 g ADDITOL® VXW 6386 (defoamer)
    100 g  

    The components of Mill Base 1 were mixed and grinded in a pearl mill containing glass beads of 1.5mm for 30 minutes at approx. 3000 rpm.
    2. In a second step the mill base was blended with the respective binder resins to yield the
    final stain-blocking primers:
    Table 4: Composition of Stain Blocking Primers 1 to 3:
    ComponentStain Blocking Primer 1Stain Blocking Primer 2Stain Blocking Primer 3
    Mill Base 1 50 g 50 g 50 g
    Example 4 --- 43,57 g (17.43 g solids) ---
    Example 5 --- --- 43,36 g (17.43 g solids)
    DUROXYN® EF 2107w/45WA 38.73 g (17.43 g solids) --- ---
    Deionized water Amount adjusted to yield 55% overall solids content


    [0137] The components of Stain Blocking Primers 1 to 3 were blended and mixed upon stirring at ambient temperature to yield the respective stain blocking primers.

    [0138] Stain Blocking Primer 1 is based on the commercial cationic 1K-epoxy stain-blocking resin DUROXYN® EF 2107w/45WA. It serves as a 1K-epoxy based reference primer with known excellent tannin- and stain-blocking ability.

    7.2. Top-Coat Formulation



    [0139] For evaluating the tannin- and marker blocking performance of the hybrid resins according to the invention the following top-coat formulation has been used. This top-coat formulation has been evaluated to show insignificant tannin- and marker-blocking if used without stain-blocking primer (see also evaluations below). Therefore, it is used as reference top-coat with low blocking ability.
    1. In a first step a mill base has been prepared according to the following formulation:
    Table 5: Composition of Mill Base 2:
    Amount [g]Substance
    17.10 g De-ionized water
    3.60 g ADDITOL® VXW 6208 (dispersing additive)
    1.70 g Propylene glycol
    0.80 g ADDITOL® VXW 6214 (slip and underground wetting agent)
    1.90 g ADDITOL® VXW 4973 (defoamer)
    69.30 g Kronos 2310 (pigment)
    5.30 g Acrysol RM 2020 (rheology modifier)
    0.30 g Surfynol DF-66 (defoamer)
    100 g  

    The components of Mill Base 2 were mixed and grinded in a pearl mill containing glass beads of 1.5mm for 30 minutes at approx. 3000 rpm.
    2. In a second step the mill base was blended with other components to yield the final top-coat formulations:
    Table 6: Composition of Top-Coat 1:
    Amount [g]Substance
    57.30 g RESYDROL® VAY 6278w/45WA (binder resin)
    30.00 g Mill Base 2
    5.70 g Ultralube E-359 (wax-emulsion)
    0.40 g ADDITOL® VXL 4930 (slip and leveling agent)
    6.60 g De-ionized water
    100 g  


    [0140] The mill base was carefully mixed into the binder resin. Then the other components were added and mixed upon stirring at ambient temperature to yield the respective Top-Coat 1.

    7.3. Evaluation of Tannin-Blocking Ability



    [0141] For evaluating the tannin-blocking performance of the Stain Blocking Primers 1 to 3 a Merbau-wood board has been divided in 4 equal sections. On sections 1 to 3 the Stain Blocking Primers 1 to 3 have been applied in 100µm wet film thickness using a standardized coating bar. On section 4 (control section) Top-Coat 1 has been applied in 100µm wet film thickness using a standardized coating bar, serving as control area with less tannin blocking ability.

    [0142] After drying of the first coat for 8 hours at ambient temperature, all sections have been top-coated with Top-Coat 1 in 100µm wet film thickness using a standardized coating bar. After drying of the topcoat for 24 hours at ambient temperature the Merbau-wood board has been aged for 7 days at 40°C and 90% relative humidity.

    [0143] Finally, the tannin-blocking efficiency has been rated from 0 - 5 by observation with the human eye. Higher values indicate better tannin-blocking efficiency (0...no tannin-blocking at all - very strong tannin-related discoloration of the top-coat layer; 5...excellent tannin-blocking - no tannin-related discoloration of the top-coat layer).

    [0144] The results of this observation have been summarized in the following table:
    Table 7: Tannin-Blocking Efficiency on Merbau-wood:
     Section 1Section 2Section 3Section 4
    1st coating layer (primer) Stain Blocking Primer 1 Stain Blocking Primer 2 Stain Blocking Primer 3 Top-Coat 1
    2nd coating layer (top-coat) Top-Coat 1 Top-Coat 1 Top-Coat 1 Top-Coat 1
    Tannin-blocking efficiency 5 5 5 1


    [0145] The tannin-blocking performance of the binder resins according to the invention (present in Stain Blocking Primer 2 and 3) was found to be comparable to the tannin blocking performance of the commercial stain-blocking resin DUROXYN® EF 2107w/45WA (present in Stain Blocking Primer 1). In case no stain-blocking primer was used and two layers of Top-Coat 1 were applied instead, no significant tannin-blocking was observed.

    7.4 Evaluation of Marker-Blocking Ability



    [0146] For evaluating the marker-blocking performance of the Stain Blocking Primers 1 to 3 a Leneta card has been coated with a commercial interior wall-paint (Behr Interior Flat - Ultra Pure White® 1050) in 100µm wet film thickness using a standardized coating bar. After drying of the paint for 7 days at ambient temperature, continuous horizontal lines have been drawn on the painted area using different commercial text-markers of various colors:

    ∘ RED Marks-A-lot Permanent

    ∘ BLACK Marks-A-Lot Permanent

    ∘ BLUE Gel pen Pilot G-2

    ∘ BLACK Gel pen Pilot G-2

    ∘ RED Gel pen Pilot G-2

    ∘ GREEN Window Mega Marker

    ∘ BLUE Window Mega Marker

    ∘ PENCIL Bic No. 2



    [0147] After application of the markers, the Laneta card has been stored at ambient temperature for at least 7 days prior to further usage. For testing of the marker-blocking efficiency, the Laneta card has been divided in 4 equal vertical sections, each of them showing the continuous horizontal marker lines. On sections 1 to 3 the Stain Blocking Primers 1 to 3 have been applied in 100µm wet film thickness using a standardized coating bar. On section 4 (control section) Top-Coat 1 has been applied in 100µm wet film thickness using a standardized coating bar, serving as control area with less marker-blocking ability. After drying of the first coat for 8 hours at ambient temperature, all sections have been top-coated with Top-Coat 1 in 100µm wet film thickness using a standardized coating bar. After drying of the topcoat for 24 hours at ambient temperature the marker-blocking efficiency in its overall appearance has been rated from 0 - 5 by observation with the human eye. Higher values indicate better marker-blocking efficiency (0...no marker-blocking at all - very strong marker-related discoloration of the top-coat layer; 5...excellent marker-blocking - no marker-related discoloration of the top-coat layer).

    [0148] The results of this observation have been summarized in the following table:
    Table 8: Marker-Blocking Efficiency on marked Laneta Card:
     Section 1Section 2Section 3Section 4
    1st coating layer (primer) Stain Blocking Primer 1 Stain Blocking Primer 2 Stain Blocking Primer 3 Top-Coat 1
    2nd coating layer (top-coat) Top-Coat 1 Top-Coat 1 Top-Coat 1 Top-Coat 1
    Marker-blocking efficiency (overall appearance rating) 4 4 5 1


    [0149] The marker-blocking performance of the binder resins according to the invention (present in Stain Blocking Primer 2 and 3) was found to be comparable to the marker blocking performance of the commercial stain-blocking resin DUROXYN® EF 2107w/45WA (present in Stain Blocking

    [0150] Primer 1). In case no stain blocking primer was used and two layers of Top-Coat 1 were applied instead, no significant marker blocking was observed.

    7.5 Evaluation of Cold Check Resistance



    [0151] For evaluating the cold check performance of the Stain Blocking Primers 1 to 3 a standard US pine-wood board has been coated on one side with the respective Stain Blocking Primers 1 to 3 using a brush. After 8 hours of drying at ambient temperature half of the coated area has been top-coated with Top-Coat 1.

    [0152] After drying of the pine wood board for 7 days at ambient temperature and humidity, the test specimen has been subjected to the following cyclic test for 10 repeated cycles:

    Cold check testing cycle:



    [0153] 
    1. 1. QUV-A exposure of the coated side of the board for 24 hours according to DIN EN ISO 4892-3 / cycle 1
    2. 2. Water immersion of the coated side of the board for 6 hours at 23°C in tab-water
    3. 3. Immediate freezing of the water soaked board at -18°C for 16 hours
    4. 4. 2 hours of thawing at 23°C and ambient relative humidity
    5. 5. Repeat steps 1 to 4 for 10 times


    [0154] This cyclic test is meant to mimic the freeze-thaw-resistance of a coating in outdoor weathering conditions, including UV exposure and water soaking. The results of this cyclic test are summarized in the following table.
    Table 9: Cold check testing results:
     Pine Board 1Pine Board 2Pine Board 3
    1st coating layer (one side of the board; full board area) Stain Blocking Primer 1 Stain Blocking Primer 2 Stain Blocking Primer 3
    2nd coating layer (on top of 1st coating layer; half board area) Top-Coat 1 Top-Coat 1 Top-Coat 1
    Observations during cyclic cold check testing Severe cracking of primer layer after 3rd cycle; Flaking and peeling of primer layer and cracking of top-coated area after 5th cycle; Testing discontinued after 5th cycle No cracking, blistering, flaking or peeling of the primer layer or the top-coated area observed after completion of 10 cycles No cracking, blistering, flaking or peeling of the primer layer or the top-coated area observed after completion of 10 cycles


    [0155] The cold check testing performance of the binder resins according to the invention (present in Stain Blocking Primer 2 and 3) was found to be superior to the cold check testing performance of the commercial 1K-epoxy stain-blocking resin DUROXYN® EF 2107w/45WA (present in Stain Blocking Primer 1). Those testing results indicate that the binder resins according to the present invention are superior to state-of-the art 1K-epoxy based systems in terms of cold check resistance and may show enhanced external durability, especially in cold and wet climates.

    7.6 Evaluation of Adhesion Promotion



    [0156] Surprisingly, it has been found that the Epoxy/amino/fatty acid/acrylic hybrid resins according to the present invention show a significant adhesion-promotion effect when added to waterborne 2K-epoxy systems. This adhesion promotion effect especially becomes very obvious on hard-to-adhere substrates for 2K-epoxy systems, e.g. CED pre-coated steel plates.

    [0157] Typical levels of addition for the binder resins according to the present invention are found in the range of 1% - 20% of the combined amount of epoxy resin and epoxy hardener, based on the solid content of all components.

    [0158] For evaluating the adhesion promotion performance of the binder resins according to the present invention, the following 2K-epoxy monocoat formulations have been prepared. 2K-Epoxy Formulation 2 contains Example 5 as adhesion promotion additive (8.4% of combined amount of epoxy resin and epoxy hardener based on solid content of all components).
    Table 10: Composition of 2K-Epoxy Formulations 1 and 2:
    PartComponent2K-Epoxy Formulation 12K-Epoxy Formulation 2
    1 De-ionized water 15.81 g 15.81 g
    ADDITIOL® VXW 6208/60 (wetting- and dispersing agent) 3.53 g 3.53 g
    ADDITOL® VXW 6393 (defoamer) 0.30 g 0.30 g
    2 Silitin Z86 (extender) 6.83 g 6.83 g
    Printex U (carbon black pigment) 0.46 g 0.46 g
    Bayferrox 306 (iron oxide black pigment) 23.07 g 23.07 g
    Heucorin FR (flash rust inhibitor) 1.45 g 1.45 g
    EWO 21.34 g 21.34 g
    3 ADDITOL® VXW 6393 (defoamer) 0.20 g 0.20 g
    Texanol (coalescing agent) 0.66 g 0.66 g
    4 ADDITOL® VXW 6388 (thickener) 0.50 g 0.50 g
    ADDITOL® VXW 6503N (substrate wetting agent) 0.33 g 0.33 g
    5 BECKOCURE® EH 2260w/41WA (epoxy hardener) 30.60 g 30.60 g
    Example 5 (adhesion promoter) - 7.17 g
    6 BECKOPOX® EP 2384w/57WA (epoxy resin) 38.28 g 38.28 g
        143.36 g 150.53 g


    [0159] Parts 1 and 2 of the formulation have been pre-mixed on a dissolver, followed by grinding in a pearl mill containing glass beads of 1.5mm for 30 minutes at approximately 3000 rpm. Then, parts 3 and 4 were added to this mixture and mixed-in upon stirring. Finally, the components of part 5 were added in the given order and mixed-in upon stirring at ambient temperature. The epoxy resin (part 6) was added to the formulation at the very end - immediately before application - and blended by stirring at ambient temperature.

    [0160] The 2K-Epoxy Formulations 1 and 2 have been applied on a steel plate (GARDOBOND 265/6800/OC) which has been pre-coated and cured with a standard automotive CED-resin in a dry film thickness of 25 - 30µm. The adhesion properties of the 2K-Epoxy Formulations 1 and 2 to the standard automotive CED-resin have been evaluated after 1 week of drying at 23°C and 50% relative humidity according to DIN EN ISO 2409:2013.

    [0161] Adhesion testing of 2K-Epoxy Formulation 1 according to DIN EN ISO 2409 resulted in a total loss of adhesion (adhesion rating: 5) of the 2K-Epoxy monocoat.

    [0162] Adhesion testing of 2K-Epoxy Formulation 2 (containing Example 5 as adhesion promoter) according to DIN EN ISO 2409 resulted in very good adhesion properties to the pre-coated, cured standard automotive CED-resin (adhesion rating: 1).

    [0163] Surprisingly, it has been found that the Epoxy/amino/fatty acid/acrylic hybrid resins according to the present invention show a significant adhesion-promotion effect when added to waterborne 2K-epoxy systems. Adhesion promoting effects for other resin technologies and substrates are also likely to be observed.


    Claims

    1. An aqueous dispersion comprising:

    - at least one fatty acid-modified epoxy amine adduct ZYWS containing amino groups which are at least partially protonated wherein the fatty acid WS contains at least 8 carbon atoms and has an iodine number according to DIN 53241-1:1995-05 of lower than 30, and

    - at least one polymer V obtained from the polymerization of one or more ethylenically unsaturated monomers.


     
    2. The aqueous dispersion according to claim 1, wherein the fatty acid-modified epoxy amine adduct ZYWS comprises a chain extended product (ZYWSX) obtained from the reaction of a fatty acid-modified epoxy amine adduct ZYWS with at least one epoxy compound X.
     
    3. The aqueous dispersion according to claim 1 or 2 wherein the dispersion is obtained by a process comprising the steps of:

    a) obtaining a fatty acid-modified epoxy amine adduct ZYWS by a process comprising the steps of reacting:

    - at least one epoxide compound Z containing at least one, preferably at least two, epoxide groups,

    - at least one amine Y containing at least one primary or secondary amino group, and

    - at least one fatty acid WS, wherein the fatty acid contains at least 8 carbon atoms and has an iodine number according to DIN 53241-1:1995-05 lower than 30,

    b) adding to the fatty acid-modified epoxy amine adduct ZYWS obtained in step (a) water and at least one acid, in an amount such that the ratio acid value / amine value of the fatty acid-modified epoxy amine adduct ZYWS is at least 0.05 thereby at least partially protonating the amino groups,

    c) optionally reacting the adduct ZYWS obtained in step (b) with at least an epoxide compound X having at least one, preferably at least two, epoxy groups per molecule, the amount of said epoxide compound X being such that the equivalent number of amino groups in ZYWS which are reactive in respect of reaction with an epoxide group is at least equal to the equivalent number of the epoxide groups in the epoxide compound X, and which preferably comprises performing the reaction of ZYWS and X until epoxide groups are no longer detectable in the reaction mixture, thereby obtaining a compound ZYWSX, and

    d) polymerizing one or more ethylenically unsaturated monomers in presence of the fatty acid-modified epoxide amine adduct ZYWS obtained at step (b) or in presence of the compound ZYWSX obtained at step (c) thereby forming a polymer V.


     
    4. The aqueous dispersion according to any of the preceding claims, wherein the epoxide compound Z has at least two epoxide groups per molecule and is selected from diglycidyl ethers of aromatic or aliphatic diols and diglycidyl esters of aromatic or aliphatic diacids.
     
    5. The aqueous dispersion according to any one of the preceding claims, wherein the amine Y is selected from aliphatic, linear, branched or cyclic amines comprising from 2 to 20 carbon atoms and comprises at least an amine Y1 comprising at least one primary amine and preferably at least one tertiary amine group and/or an amine Y2 comprising at least one secondary amine and preferably at least one hydroxyl group.
     
    6. The aqueous dispersion according to any of the preceding claims, wherein the fatty acid WS is selected from caprylic acid, decanoic acid, lauric acid, myristic acid, palmic acid, stearic acid or a mixture thereof.
     
    7. The aqueous dispersion according to any of the preceding claims, wherein the polymer V is obtained from the polymerization of at least one or more (meth)acrylate monomers, styrenic monomers, (meth)acrylamide monomers, vinyl carboxylate monomers or a combination thereof.
     
    8. The aqueous dispersion according to any of the preceding claims, wherein the polymer V is obtained from a monomer mixture containing at least 15 wt % and not more than 90 wt % of monomers having a glass transition temperature Tg of their homopolymerisate of at least 50 °C.
     
    9. The aqueous dispersion according to any of claims 2 to 8 wherein the epoxide compound X has at least two epoxide groups per molecule and is selected from diglycidyl ethers of aromatic or aliphatic diols and diglycidyl esters of aromatic or aliphatic diacids.
     
    10. The aqueous dispersion according to any of the preceding claims wherein the fatty acid-modified epoxy amine adduct ZYWS and/or ZYWSX has an amine value according to DIN 53176:2002-11 of at least 50 mg KOH/g.
     
    11. The aqueous dispersion according to any one of the preceding claims, having a mass fraction of solid of from 10 to 60%, as determined according to DIN 55671:2002-09.
     
    12. The aqueous dispersion according to any of the preceding claims, comprising

    - from 10 to 40 wt % of the fatty acid-modified epoxy amine adduct ZYWS and/or ZYWSX, and

    - from 60 to 90 wt % of polymer V, based on the sum of ZYWS (and/or ZYWSX) and V.


     
    13. Process for the preparation of the aqueous dispersion according to any of the preceding claims comprising the steps of:

    a) obtaining a fatty acid-modified epoxy amine adduct ZYWS by a process comprising the steps of reacting:

    - at least one epoxide compound Z containing at least one, preferably at least two, epoxide groups,

    - at least one amine Y containing at least one primary or secondary amino group, and

    - at least one fatty acid WS, wherein the fatty acid contains at least 8 carbon atoms and has an iodine number according to DIN 53241-1:1995-05 lower than 30,

    b) adding to the fatty acid-modified epoxy amine adduct ZYWS obtained in step (a) water and at least one acid, in an amount such that the ratio acid value / amine value of the fatty acid-modified epoxy amine adduct ZYWS is at least 0.05 thereby at least partially protonating the amino groups,

    c) optionally reacting the adduct ZYWS obtained in step (b) with at least an epoxide compound X having at least one, preferably at least two, epoxy groups per molecule, the amount of said epoxide compound X being such that the equivalent number of amino groups in ZYWS which are reactive in respect of reaction with an epoxide group is at least equal to the equivalent number of the epoxide groups in the epoxide compound X, and which preferably comprises performing the reaction of ZYWS and X until epoxide groups are no longer detectable in the reaction mixture, thereby obtaining a compound ZYWSX, and

    d) polymerizing one or more ethylenically unsaturated monomers in presence of the fatty acid-modified epoxide amine adduct ZYWS obtained at step (b) or in presence of the compound ZYWSX obtained at step (c) thereby forming a polymer V.


     
    14. The process according to claim 13, wherein step c) is executed and wherein the amount of each of said epoxide compound X is such that the equivalent number of amino groups in ZWSY which are reactive in respect of addition reaction with an epoxide group is at least 10% greater than the equivalent number of the epoxide groups in the epoxide compound X.
     
    15. The process according to claim 13 or 14, wherein in step b) the ratio acid value / amine value of the fatty acid-modified epoxy amine adduct ZYWS is from 0.2 to 1.0, preferably from 0.3 to 0.8
     
    16. A process for preparing a coated substrate or article, comprising the step of coating at least part of the surface of the substrate or article with the aqueous dispersion according to any of claims 1 to 12.
     
    17. A substrate or article having at least part of its surface coated with the aqueous dispersion according to any of claims 1 to 12.
     


    Ansprüche

    1. Wässerige Dispersion, umfassend:

    - mindestens ein Fettsäure-modifiziertes Epoxidaminaddukt ZYWs, das Aminogruppen enthält, die zumindest teilweise protoniert sind, wobei die Fettsäure Ws mindestens 8 Kohlenstoffatome enthält und eine lodzahl nach DIN 53241-1:1995-05 kleiner als 30 hat, und

    - mindestens ein Polymer V, das aus der Polymerisation von einem oder mehreren ethylenisch ungesättigten Monomeren erhalten wurde.


     
    2. Wässerige Dispersion nach Anspruch 1, wobei das Fettsäure-modifizierte Epoxidaminaddukt ZYWs ein Kettenverlängerungsprodukt (ZYWsX) umfasst, das aus der Umsetzung eines Fettsäure-modifizierten Epoxidaminadduktes ZYWs mit mindestens einer Epoxidverbindung X erhalten wurde.
     
    3. Wässerige Dispersion nach Anspruch 1 oder 2, wobei die Dispersion durch ein Verfahren erhalten wird, umfassend die folgenden Schritte:

    a) Erhalten eines Fettsäure-modifizierten Epoxidaminadduktes ZYWs durch ein Verfahren, umfassend die Schritte des Umsetzens:

    - mindestens einer Epoxidverbindung Z, die mindestens eine, vorzugsweise mindestens zwei Epoxidgruppen enthält,

    - mindestens eines Amins Y, das mindestens eine primäre oder sekundäre Aminogruppe enthält, und

    - mindestens einer Fettsäure Ws, wobei die Fettsäure mindestens 8 Kohlenstoffatome enthält und eine lodzahl nach DIN 53241-1:1995-05 kleiner als 30 hat,

    b) Zugeben von Wasser zu dem in Schritt (a) erhaltenen Fettsäure-modifizierten Epoxidaminaddukt ZYWs und mindestens einer Säure in einer solchen Menge, dass das Verhältnis Säurezahl/Aminzahl des Fettsäure-modifizierten Epoxidaminadduktes ZYWs mindestens 0,05 beträgt, so dass die Aminogruppen zumindest teilweise protoniert werden,

    c) gegebenenfalls Umsetzen des in Schritt (b) erhaltenen Adduktes ZYWs mit mindestens einer Epoxidverbindung X mit mindestens einer, vorzugsweise mindestens zwei Epoxidgruppen pro Molekül, wobei die Menge der Epoxidverbindung X soviel beträgt, dass die äquivalente Anzahl an Aminogruppen in ZYWs, die bezüglich der Reaktion mit einer Epoxidgruppe reaktiv sind, mindestens gleich der äquivalenten Anzahl der Epoxidgruppen in der Epoxidverbindung X ist, und das vorzugsweise das Durchführen der Umsetzung von ZYWs und X so lange umfasst, bis in dem Reaktionsgemisch keine Epoxidgruppen mehr nachweisbar sind, wodurch eine Verbindung ZYWsX erhalten wird, und

    d) Polymerisieren von einem oder mehreren ethylenisch ungesättigten Monomeren in Gegenwart des in Schritt (b) erhaltenen Fettsäure-modifizierten Epoxidaminadduktes ZYWs oder in Gegenwart der in Schritt (c) erhaltenen Verbindung ZYWsX, wodurch ein Polymer V gebildet wird.


     
    4. Wässerige Dispersion nach einem der vorstehenden Ansprüche, wobei die Epoxidverbindung Z mindestens zwei Epoxidgruppen pro Molekül aufweist und aus Diglycidylethern von aromatischen oder aliphatischen Diolen und Diglycidylestern von aromatischen oder aliphatischen Disäuren ausgewählt ist.
     
    5. Wässerige Dispersion nach einem der vorstehenden Ansprüche, wobei das Amin Y aus aliphatischen, linearen, verzweigten oder cyclischen Aminen, umfassend 2 bis 20 Kohlenstoffatome, ausgewählt ist und mindestens ein Amin Y1, umfassend mindestens eine primäre Amin- und vorzugsweise mindestens eine tertiäre Amingruppe, und/oder ein Amin Y2, umfassend mindestens eine sekundäre Amin- und vorzugsweise mindestens eine Hydroxylgruppe, umfasst.
     
    6. Wässerige Dispersion nach einem der vorstehenden Ansprüche, wobei die Fettsäure Ws aus Octansäure, Decansäure, Laurinsäure, Myristinsäure, Palmitinsäure, Stearinsäure oder einem Gemisch davon ausgewählt ist.
     
    7. Wässerige Dispersion nach einem der vorstehenden Ansprüche, wobei das Polymer V aus der Polymerisation von mindestens einem oder mehreren (Meth)acrylatmonomeren, Styrolmonomeren, (Meth)acrylamidmonomeren, Vinylcarboxylatmonomeren oder einer Kombination davon erhalten wird.
     
    8. Wässerige Dispersion nach einem der vorstehenden Ansprüche, wobei das Polymer V aus einem Monomergemisch erhalten wird, das mindestens 15 Gew.-% und nicht mehr als 90 Gew.-% an Monomeren mit einer Glasübergangstemperatur Tg ihres Homopolymerisates von mindestens 50 °C enthält.
     
    9. Wässerige Dispersion nach einem der Ansprüche 2 bis 8, wobei die Epoxidverbindung X mindestens zwei Epoxidgruppen pro Molekül aufweist und aus Diglycidylethern von aromatischen oder aliphatischen Diolen und Diglycidylestern von aromatischen oder aliphatischen Disäuren ausgewählt ist.
     
    10. Wässerige Dispersion nach einem der vorstehenden Ansprüche, wobei das Fettsäure-modifizierte Epoxidaminaddukt ZYWs und/oder ZYWsX eine Aminzahl nach DIN 53176:2002-11 von mindestens 50 mg KOH/g hat.
     
    11. Wässerige Dispersion nach einem der vorstehenden Ansprüche mit einem Feststoffmassenanteil von 10 bis 60 %, bestimmt nach DIN 55671:2002-09.
     
    12. Wässerige Dispersion nach einem der vorstehenden Ansprüche, umfassend

    - 10 bis 40 Gew.-% des Fettsäure-modifizierten Epoxidaminadduktes ZYWs und/oder ZYWsX und

    - 60 bis 90 Gew.-% des Polymers V, basierend auf der Summe von ZYWs (und/oder ZYWsX) und V.


     
    13. Verfahren zur Herstellung der wässerigen Dispersion nach einem der vorstehenden Ansprüche, umfassend die Schritte:

    a) Erhalten eines Fettsäure-modifizierten Epoxidaminadduktes ZYWs durch ein Verfahren, umfassend die Schritte des Umsetzens:

    - mindestens einer Epoxidverbindung Z, die mindestens eine, vorzugsweise mindestens zwei Epoxidgruppen enthält,

    - mindestens eines Amins Y, das mindestens eine primäre oder sekundäre Aminogruppe enthält, und

    - mindestens einer Fettsäure Ws, wobei die Fettsäure mindestens 8 Kohlenstoffatome enthält und eine lodzahl nach DIN 53241-1:1995-05 kleiner als 30 hat,

    b) Zugeben von Wasser zu dem in Schritt (a) erhaltenen Fettsäure-modifizierten Epoxidaminaddukt ZYWs und mindestens einer Säure in einer solchen Menge, dass das Verhältnis Säurezahl/Aminzahl des Fettsäure-modifizierten Epoxidaminadduktes ZYWs mindestens 0,05 beträgt, so dass die Aminogruppen zumindest teilweise protoniert werden,

    c) gegebenenfalls Umsetzen des in Schritt (b) erhaltenen Adduktes ZYWs mit mindestens einer Epoxidverbindung X mit mindestens einer, vorzugsweise mindestens zwei Epoxidgruppen pro Molekül, wobei die Menge der Epoxidverbindung X soviel beträgt, dass die äquivalente Anzahl an Aminogruppen in ZYWs, die bezüglich der Reaktion mit einer Epoxidgruppe reaktiv sind, mindestens gleich der äquivalenten Anzahl der Epoxidgruppen in der Epoxidverbindung X ist, und das vorzugsweise das Durchführen der Umsetzung von ZYWs und X so lange umfasst, bis in dem Reaktionsgemisch keine Epoxidgruppen mehr nachweisbar sind, wodurch eine Verbindung ZYWsX erhalten wird, und

    d) Polymerisieren von einem oder mehreren ethylenisch ungesättigten Monomeren in Gegenwart des in Schritt (b) erhaltenen Fettsäure-modifizierten Epoxidaminadduktes ZYWs oder in Gegenwart der in Schritt (c) erhaltenen Verbindung ZYWsX, wodurch ein Polymer V gebildet wird.


     
    14. Verfahren nach Anspruch 13, wobei Schritt c) ausgeführt wird und wobei die Menge jeder Epoxidverbindung X soviel beträgt, dass die äquivalente Anzahl an Aminogruppen in ZYWs, die bezüglich einer Additionsreaktion mit einer Epoxidgruppe reaktiv sind, mindestens 10 % mehr beträgt als die äquivalente Anzahl der Epoxidgruppen in der Epoxidverbindung X.
     
    15. Verfahren nach Anspruch 13 oder 14, wobei in Schritt b) das Verhältnis Säurezahl/Aminzahl des Fettsäure-modifizierten Epoxidaminadduktes ZYWs 0,2 bis 1,0, vorzugsweise 0,3 bis 0,8 beträgt.
     
    16. Verfahren zur Herstellung eines beschichteten Substrats oder Gegenstandes, umfassend den Schritt des Beschichtens zumindest eines Teils der Oberfläche des Substrats oder Gegenstandes mit der wässerigen Dispersion nach einem der Ansprüche 1 bis 12.
     
    17. Substrat oder Gegenstand, dessen Oberfläche zumindest teilweise mit der wässerigen Dispersion nach einem der Ansprüche 1 bis 12 beschichtet ist.
     


    Revendications

    1. Dispersion aqueuse comprenant :

    - au moins un adduit époxy-amine modifié par un acide gras ZYWS contenant des groupes amino qui sont au moins en partie protonés, l'acide gras WS contenant au moins 8 atomes de carbone et ayant un indice d'iode selon la norme DIN 53241-1:1995-05 inférieur à 30, et

    - au moins un polymère V obtenu à partir de la polymérisation d'un ou plusieurs monomères à insaturation éthylénique.


     
    2. Dispersion aqueuse selon la revendication 1, dans laquelle l'adduit époxy-amine modifié par un acide gras ZYWS comprend un produit à chaîne allongée (ZYWSX) obtenu à partir de la réaction d'un adduit époxy-amine modifié par un acide gras ZYWS avec au moins un composé époxy X.
     
    3. Dispersion aqueuse selon la revendication 1 ou 2, la dispersion étant obtenue par un procédé comprenant les étapes consistant à :

    a) obtenir un adduit époxy-amine modifié par un acide gras ZYWS par un procédé comprenant les étapes consistant à faire réagir :

    - au moins un composé époxyde Z contenant au moins un, de préférence au moins deux, groupes époxyde,

    - au moins une amine Y contenant au moins un groupe amino primaire ou secondaire et

    - au moins un acide gras WS, l'acide gras contenant au moins 8 atomes de carbone et ayant un indice d'iode selon la norme DIN 53241-1:1995-05 inférieur à 30,

    b) ajouter à l'adduit époxy-amine modifié par un acide gras ZYWS obtenu dans l'étape (a) de l'eau et au moins un acide, en une quantité telle que le rapport indice d'acide/indice d'amine de l'adduit époxy-amine modifié par un acide gras ZYWS est d'au moins 0,05 ce qui permet ainsi de protoner au moins en partie les groupes amino,

    c) éventuellement faire réagir l'adduit ZYWS obtenu dans l'étape (b) avec au moins un composé époxyde X ayant au moins un, de préférence au moins deux, groupes époxy par molécule, la quantité dudit composé époxyde X étant telle que le nombre d'équivalents de groupes amino dans ZYWS qui sont réactifs en ce qui concerne une réaction avec un groupe époxyde est au moins égal au nombre d'équivalents des groupes époxyde dans le composé époxyde X, et ce qui de préférence comprend la mise en œuvre de la réaction de ZYWS et de X jusqu'à ce que des groupes époxyde ne soient plus détectables dans le mélange réactionnel, ce qui permet ainsi d'obtenir un composé ZYWSX, et

    d) polymériser un ou plusieurs monomères à insaturation éthylénique en présence de l'adduit époxyde-amine modifié par un acide gras ZYWS obtenu à l'étape (b) ou en présence du composé ZYWSX obtenu à l'étape (c) ce qui permet ainsi de former un polymère V.


     
    4. Dispersion aqueuse selon l'une quelconque des revendications précédentes, dans laquelle le composé époxyde Z a au moins deux groupes époxyde par molécule et est choisi parmi les éthers diglycidyliques de diols aromatiques ou aliphatiques et les esters diglycidyliques de diacides aromatiques ou aliphatiques.
     
    5. Dispersion aqueuse selon l'une quelconque des revendications précédentes, dans laquelle l'amine Y est choisie parmi les amines aliphatiques linéaires, ramifiées ou cycliques comprenant de 2 à 20 atomes de carbone et comprend au moins une amine Y1 comprenant au moins un groupe amine primaire et de préférence au moins un groupe amine tertiaire et/ou une amine Y2 comprenant au moins un groupe amine secondaire et de préférence au moins un groupe hydroxyle.
     
    6. Dispersion aqueuse selon l'une quelconque des revendications précédentes, dans laquelle l'acide gras WS est choisi parmi l'acide caprylique, l'acide décanoïque, l'acide laurique, l'acide myristique, l'acide palmique, l'acide stéarique ou un mélange de ceux-ci.
     
    7. Dispersion aqueuse selon l'une quelconque des revendications précédentes, dans laquelle le polymère V est obtenu à partir de la polymérisation d'au moins un ou plusieurs monomères (méth)acrylate, monomères styréniques, monomères (méth)acrylamide, monomères carboxylate de vinyle ou d'une association de ceux-ci.
     
    8. Dispersion aqueuse selon l'une quelconque des revendications précédentes, dans laquelle le polymère V est obtenu à partir d'un mélange de monomères contenant au moins 15 % en poids et pas plus de 90 % en poids de monomères ayant une température de transition vitreuse Tg de leur produit d'homopolymérisation d'au moins 50 °C.
     
    9. Dispersion aqueuse selon l'une quelconque des revendications 2 à 8 dans laquelle le composé époxyde X a au moins deux groupes époxyde par molécule et est choisi parmi les éthers diglycidyliques de diols aromatiques ou aliphatiques et les esters diglycidyliques de diacides aromatiques ou aliphatiques.
     
    10. Dispersion aqueuse selon l'une quelconque des revendications précédentes dans laquelle l'adduit époxy-amine modifié par un acide gras ZYWS et/ou ZYWSX a un indice d'amine selon la norme DIN 53176:2002-11 d'au moins 50 mg de KOH/g.
     
    11. Dispersion aqueuse selon l'une quelconque des revendications précédentes, ayant une fraction massique de solide, telle que déterminée selon la norme DIN 55671:2002-09, de 10 à 60 %.
     
    12. Dispersion aqueuse selon l'une quelconque des revendications précédentes, comprenant

    - de 10 à 40 % en poids de l'adduit époxy-amine modifié par un acide gras ZYWS et/ou ZYWSX et

    - de 60 à 90 % en poids de polymère V, par rapport à la somme de ZYWS (et/ou ZYWSX) et de V.


     
    13. Procédé pour la préparation de la dispersion aqueuse selon l'une quelconque des revendications précédentes comprenant les étapes consistant à :

    a) obtenir un adduit époxy-amine modifié par un acide gras ZYWS par un procédé comprenant les étapes consistant à faire réagir :

    - au moins un composé époxyde Z contenant au moins un, de préférence au moins deux, groupes époxyde,

    - au moins une amine Y contenant au moins un groupe amino primaire ou secondaire et

    - au moins un acide gras WS, l'acide gras contenant au moins 8 atomes de carbone et ayant un indice d'iode selon la norme DIN 53241-1:1995-05 inférieur à 30,

    b) ajouter à l'adduit époxy-amine modifié par un acide gras ZYWS obtenu dans l'étape (a) de l'eau et au moins un acide, en une quantité telle que le rapport indice d'acide/indice d'amine de l'adduit époxy-amine modifié par un acide gras ZYWs est d'au moins 0,05 ce qui permet ainsi de protoner au moins en partie les groupes amino,

    c) éventuellement faire réagir l'adduit ZYWS obtenu dans l'étape (b) avec au moins un composé époxyde X ayant au moins un, de préférence au moins deux, groupes époxy par molécule, la quantité dudit composé époxyde X étant telle que le nombre d'équivalents de groupes amino dans ZYWS qui sont réactifs en ce qui concerne une réaction avec un groupe époxyde est au moins égal au nombre d'équivalents des groupes époxyde dans le composé époxyde X, et ce qui de préférence comprend la mise en œuvre de la réaction de ZYWS et de X jusqu'à ce que des groupes époxyde ne soient plus détectables dans le mélange réactionnel, ce qui permet ainsi d'obtenir un composé ZYWSX, et

    d) polymériser un ou plusieurs monomères à insaturation éthylénique en présence de l'adduit époxyde-amine modifié par un acide gras ZYWS obtenu à l'étape (b) ou en présence du composé ZYWSX obtenu à l'étape (c) ce qui permet ainsi de former un polymère V.


     
    14. Procédé selon la revendication 13, dans lequel l'étape c) est exécutée et dans lequel la quantité de chacun dudit composé époxyde X est telle que le nombre d'équivalents de groupes amino dans ZWSY qui sont réactifs en ce qui concerne une réaction d'addition avec un groupe époxyde est au moins 10 % plus grand que le nombre d'équivalents des groupes époxyde dans le composé époxyde X.
     
    15. Procédé selon la revendication 13 ou 14, dans lequel dans l'étape b) le rapport indice d'acide/indice d'amine de l'adduit époxy-amine modifié par un acide gras ZYWS est de 0,2 à 1,0, de préférence de 0,3 à 0,8.
     
    16. Procédé pour la préparation d'un substrat ou article revêtu, comprenant l'étape consistant à revêtir au moins une partie de la surface du substrat ou de l'article avec la dispersion aqueuse selon l'une quelconque des revendications 1 à 12.
     
    17. Substrat ou article dont au moins une partie de la surface est revêtue de la dispersion aqueuse selon l'une quelconque des revendications 1 à 12.
     






    Cited references

    REFERENCES CITED IN THE DESCRIPTION



    This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

    Patent documents cited in the description