(19)
(11)EP 3 802 704 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
15.06.2022 Bulletin 2022/24

(21)Application number: 20751686.5

(22)Date of filing:  10.06.2020
(51)International Patent Classification (IPC): 
C08L 97/02(2006.01)
C08L 83/04(2006.01)
C08L 23/06(2006.01)
C08G 77/20(2006.01)
(52)Cooperative Patent Classification (CPC):
C08G 77/20; C08L 97/02; C08L 23/06
 
C-Sets:
  1. C08L 97/02, C08L 23/06, C08L 83/04;
  2. C08L 23/06, C08L 97/02, C08L 83/04;

(86)International application number:
PCT/US2020/036890
(87)International publication number:
WO 2021/025775 (11.02.2021 Gazette  2021/06)

(54)

ALKENYL-FUNCTIONAL POLYDIORGANOSILOXANE COMPOSITIONS AND METHODS FOR USE THEREOF IN FORMING WOOD PLASTIC COMPOSITES

ALKENYLFUNKTIONELLE POLYDIORGANOSILOXANZUSAMMENSETZUNGEN UND VERFAHREN ZU DEREN VERWENDUNG ZUR HERSTELLUNG VON HOLZ-KUNSTSTOFF-VERBUNDMATERIALIEN

COMPOSITIONS DE POLYDIORGANOSILOXANE À FONCTION ALCÉNYLE ET LEURS PROCÉDÉS D'UTILISATION DANS LA FORMATION DE COMPOSITES BOIS-PLASTIQUE


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 07.08.2019 US 201962883682 P

(43)Date of publication of application:
14.04.2021 Bulletin 2021/15

(73)Proprietor: Dow Silicones Corporation
Auburn, MI 48686-0994 (US)

(72)Inventors:
  • CHORVATH, Igor
    Michigan 48686-0994 (US)
  • KEENIHAN, James
    Michigan 48686-0994 (US)
  • BRUCE, Keith
    Michigan 48686-0994 (US)
  • GAAL, Sean
    Michigan 48686-0994 (US)

(74)Representative: Murgitroyd & Company 
Murgitroyd House 165-169 Scotland Street
Glasgow G5 8PL
Glasgow G5 8PL (GB)


(56)References cited: : 
CN-A- 104 774 368
CN-A- 106 380 878
CN-A- 106 117 771
US-A1- 2015 093 529
  
      
    Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


    Description

    TECHNICAL FIELD



    [0001] A polydiorganosiloxane is useful in a wood plastic composite (WPC) composition and method for preparing WPC articles. The polydiorganosiloxane may be delivered in liquid or solid form.

    BACKGROUND



    [0002] Conventional processes for producing WPC articles generally require a process aid (which can be internal or external) to facilitate forming and ensure quality (e.g., smoothness of surface and edges) of the WPC articles. Conventional, low cost, organic process aids generally suffer from the drawback of requiring high loading to achieve faster production speeds, thereby impacting cost and/or performance properties. In addition, many conventional process aids may negatively affect physical properties and reduce mechanical properties (such as impact resistance, flexural strength, and flexural modulus) of the WPC articles, especially at elevated use temperatures. Conventional process aids may also migrate from the WPC articles, thus negatively impacting one or more properties of the WPC articles over time, such as physical properties, appearance, feel, ability to overmold, ability to co-extrude, ability to adhere to the surface, ability to print the surface or ability to paint the surface of the WPC articles. In addition, some of the organic process aids volatilize at higher application temperatures, which can lead to formation or bubbles and cracks in the WPC articles, which can compromise long term performance of these articles.

    [0003] Document CN 106 380 878 discloses wood-plastic composite products that comprise a polyethylene and a silicone . Document CN 104 774 368 has a similar disclosure.

    SUMMARY



    [0004] A composition, for preparing a wood plastic article, according to claim 1 is disclosed. Dependent claims relate to embodiments.

    [0005] A method, according to claim 11, for preparing a wood plastic composite article from the composition is also disclosed.

    [0006] A solid carrier component, according to claim 15 or claim 16, is also disclosed. The solid carrier component may be useful for delivering the polydiorganosiloxane to the composition.

    DETAILED DESCRIPTION



    [0007] The composition described above is useful for preparing a wood plastic composite article. The composition may comprise:

    15 weight % to 70 weight % of (a) a lignocellulosic-based filler;

    29.5 weight % to 84.5 weight % of (b) an ethylene-based polymer;

    0.5 weight % to 6 weight % of (c) a polydiorganosiloxane of unit formula:
    (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, where each R is an independently selected monovalent hydrocarbon group of 1 to 18 carbon atoms that is free of aliphatic unsaturation, each R' is an independently selected alkenyl group of 2 to 18 carbon atoms, subscript a is 0 to 2, subscript b is 0 to 2, a quantity (a + b) = 2, subscript c ≥ 0, subscript d ≥ 0, a quantity (a + d) ≥ 1, and a quantity (a + b + c + d) is sufficient to give the polydiorganosiloxane a viscosity of 2,000 mPa·s to 60,000 mPa·s at 25°C measured at 0.1 to 50 RPM on a Brookfield DV-III cone & plate viscometer with #CP-52 spindle; and

    0 to 4 weight % of (d) a maleated ethylene-based polymer;

    each based on combined weights of starting materials (a), (b), (c), and (d) in said composition.


    (a) Lignocellulosic-Based Filler



    [0008] The composition described above comprises starting material (a) a lignocellulosic-based filler. The lignocellulosic-based filler comprises, alternatively consists essentially of, alternatively consists of, a lignocellulosic material. Typically, the lignocellulosic-based filler consists of the lignocellulosic material. The lignocellulosic-based filler, as well as the lignocellulosic material, may comprise any matter derived from any plant source. When the lignocellulosic-based filler consists essentially of or consists of lignocellulosic material, the lignocellulosic material may also include some water or moisture content, although the lignocellulosic material, as well as the lignocellulosic-based filler, is typically dry, i.e., does not contain any free moisture content but for that which may be associated with the relative humidity in an environment in which the lignocellulosic-based filler is prepared, derived, formed, and/or stored. The same is typically true for other species of (a) the lignocellulosic-based filler, but is noted in regards to lignocellulosic-based fillers as lignocellulosic materials generally include some water content as harvested/prepared before any drying or end use.

    [0009] The lignocellulosic-based filler typically comprises carbohydrate polymers (e.g., cellulose and/or hemicellulose), and may further comprise an aromatic polymer (e.g., lignin). The lignocellulosic-based filler is typically a natural lignocellulosic material, i.e., is not synthetically derived. For example, the lignocellulosic-based filler is typically derived from wood (hardwood, softwood, and/or plywood). Alternatively, or in addition, the lignocellulosic-based filler may comprise lignocellulosic material from other non-wood sources, such as lignocellulosic material from plants, or other plant-derived polymers, for example agricultural by-products, chaff, sisal, bagasse, wheat straw, kapok, ramie, henequen, corn fiber or coir, nut shells, flax, jute, hemp, kenaf, rice hulls, abaca, peanut hull, bamboo, straw, lignin, starch, or cellulose and cellulose-containing products, and combinations thereof. The lignocellulosic-based filler may be virgin, recycled, or a combination thereof.

    [0010] Alternatively, the lignocellulosic-based filler may comprise a wood filler. "Wood" is as described in The Chemical Composition of Wood by Pettersen, Roger C., U.S. Department of Agriculture, Forest Service, Forest Products Laboratory, Madison, WI, Chapter 2. Wood may comprise lignin in an amount of 18% to 35% and carbohydrate in an amount of 65% to 75%, and optionally inorganic minerals in an amount up to 10%. The carbohydrate portion of wood comprises cellulose and hemicellulose. Cellulose content may range from 40% to 50% of the dry wood weight and hemicellulose may range from 25% to 35%. Alpha-cellulose content may be 29% to 57%, alternatively 40% to 50%, based on dry weight of the wood filler. The wood filler is derived from wood, e.g., hardwood and/or softwood. Specific examples of suitable hardwoods from which the wood filler may be derived include, but are not limited to, ash, aspen, cottonwood, basswood, birch, beech, chestnut, gum, elm eucalyptus, maple, oak, poplar, sycamore, and combinations thereof. Specific examples of suitable softwoods from which the wood filler may be derived include, but are not limited to, spruce, fir, hemlock, tamarack, larch, pine, cypress, redwood, and combinations thereof. Fillers derived from combinations of different hardwoods, combinations of different softwoods, or combinations of hardwood(s) and softwood(s) may be used together as the wood filler. Alternatively, the lignocellulosic-based filler may consist essentially of a wood filler. Alternatively, the lignocellulosic-based filler may consist of a wood filler.

    [0011] The lignocellulosic-based filler may have any form and size, e.g., from nanometer to millimeter particle size. For example, the lignocellulosic-based filler may comprise a powder, a pulp, a flour, sawdust, a fiber, a flake, a chip, a shaving, a strand, a scrim, a wafer, a wool, a straw, a particle, or any combination thereof. The lignocellulosic-based filler may be formed via a variety of techniques known to one of skill in the art, typically as a function of the form thereof. For example, the lignocellulosic-based filler can be prepared by comminuting logs, branches, industrial wood residue, or rough pulpwood. The lignocellulosic-based filler may be comminuted to a desired particle size. For example, the lignocellulosic-based filler may be comminuted with any convenient equipment, such as a hammer mill, which results in the lignocellulosic-based filler having a particle size suitable for use in mixing processes. The desired particle size is typically selected by one of skill in the art based on the particular mixing process utilized and desired properties of the wood plastic composite article. By particle size, it is meant the dimensions of the lignocellulosic-based filler, regardless of shape, and includes, for example, dimensions associated with the lignocellulosic-based filler when in the form of fibers. As known in the art, lignocellulosic-based fillers may be pelletized, or otherwise in the form of pellets, which may substantially maintain shape and dimension when incorporated into the composition or which may form smaller particles in the composition.

    [0012] The shape and dimensions of the lignocellulosic-based filler is also not specifically restricted. For example, the lignocellulosic-based filler may be spherical, rectangular, ovoid, irregular, and may be in the form of, for example, a powder, a flour, a fiber, a flake, a chip, a shaving, a strand, a scrim, a wafer, a wool, a straw, a particle, and combinations thereof. Dimensions and shape are typically selected based on the type of the lignocellulosic-based filler utilized, the selection of other starting materials included within the WPC composition, and the end use application of the WPC article formed therewith.

    [0013] Starting material (a) may be one lignocellulosic-based filler or may be a combination of two or more lignocellulosic-based polymers that differ from one another by at least one property such as plant source from which the lignocellulosic-based filler was derived, lignin content, alpha-cellulose content, method of preparation, filler shape, filler surface area, average particle size, and/or particle size distribution. Starting material (a) may be present in the composition in an amount of 15% to 70%, alternatively 40% to 70%, and alternatively 45% to 65%, based on combined weights of starting materials (a), (b), (c) and (d).

    (b) Ethylene-Based Polymer



    [0014] The composition described above further comprises starting material (b) an ethylene-based polymer. As used herein, "ethylene-based" polymers are polymers prepared from ethylene monomers as the primary (i.e., greater than 50%) monomer component, though other co-monomers may also be employed. "Polymer" means a macromolecular compound prepared by reacting (i.e., polymerizing) monomers of the same or different type, and includes homopolymers and interpolymers. "Interpolymer" means a polymer prepared by the polymerization of at least two different monomer types. This generic term includes copolymers (usually employed to refer to polymers prepared from two different monomer types), and polymers prepared from more than two different monomer types (e.g., terpolymers (three different monomer types) and tetrapolymers (four different monomer types)).

    [0015] The ethylene-based polymer can be an ethylene homopolymer. As used herein, "homopolymer" denotes a polymer comprising repeating units derived from a single monomer type, but does not exclude residual amounts of other components used in preparing the homopolymer, such as catalysts, initiators, solvents, and chain transfer agents.

    [0016] Alternatively, the ethylene-based polymer can be an ethylene/alpha-olefin ("α-olefin") interpolymer having an α-olefin content of at least 1%, alternatively at least 5%, alternatively at least 10%, alternatively at least 15%, alternatively at least 20%, or alternatively at least 25 wt% based on the entire interpolymer weight. These interpolymers can have an α-olefin content of less than 50%, alternatively less than 45%, alternatively less than 40%, or alternatively less than 35% based on the entire interpolymer weight. When an α-olefin is employed, the α-olefin can have 3 to 20 carbon atoms (C3-C20) and be a linear, branched or cyclic α-olefin. Examples of C3-20 α-olefins include propene, 1-butene, 4-methyl-1-pentene, 1-hexene, 1-octene, 1-decene, 1-dodecene, 1-tetradecene, 1-hexadecene, and 1-octadecene. The α-olefins can also have a cyclic structure such as cyclohexane or cyclopentane, resulting in an α-olefin such as 3-cyclohexyl-1-propene (allyl cyclohexane) and vinyl cyclohexane. Illustrative ethylene/α-olefin interpolymers include ethylene/propylene, ethylene/1-butene, ethylene/1-hexene, ethylene/1-octene, ethylene/propylene/1-octene, ethylene/propylene/1-butene, and ethylene/1-butene/1-octene.

    [0017] Starting material (b) can be one ethylene-based polymer or a combination of two or more ethylene-based polymers (e.g., a blend of two or more ethylene-based polymers that differ from one another by at least one property such as monomer composition, monomer content, catalytic method of preparation, molecular weight, molecular weight distributions, and/or densities). If a blend of ethylene-based polymers is employed, the polymers can be blended by any in-reactor or post-reactor process.

    [0018] The ethylene-based polymer for starting material (b) may be selected from the group consisting of High Density Polyethylene (HDPE), Medium Density Polyethylene (MDPE), Low Density Polyethylene (LDPE), Linear Low Density Polyethylene (LLDPE), Low Density Low Molecular Weight Polyethylene (LDLMWPE), and a combination thereof.

    [0019] Alternatively, starting material (b) can be a LLDPE. LLDPEs are generally ethylene-based polymers having a heterogeneous distribution of comonomer (e.g., α-olefin monomer), and are characterized by short-chain branching. For example, LLDPEs can be copolymers of ethylene and α-olefin monomers, such as those described above. LLDPEs may have densities ranging from 0.91 g/cm3 to 0.94 g/cm3. Densities for the LLDPEs and other ethylene-based polymers described herein are determined by ASTM D792 - 13. LLDPEs suitable for use herein can have a melt index (I2) of 1 g/10 min to 20 g/10 min, alternatively > 2 g/10 min, alternatively 2.3 g/10 min to 20 g/10 min, alternatively 2.3 g/10 min to 12 g/10 min, alternatively 2.3 g/10 min to 6 g/10 min, alternatively 4.4 g/10 min to 20 g/10 min and alternatively 6.8 g/10 min to 20 g/10 min. Values for I2 for LLDPEs and other ethylene-based polymers are determined at 190°C and 2.16 Kg according to ASTM D1238 - 13. The LLDPE can have a melting temperature of at least 124°C, alternatively 124°C to 135°C, and alternatively 124°C to 132°C. Melting temperatures for LLDPEs and other polyethylene-based polymers are determined by DSC according to ASTM D3418 - 15.

    [0020] LLDPE's are known in the art and may be produced by known methods. For example, LLDPE may be made using Ziegler-Natta catalyst systems as well as single-site catalysts such as bis-metallocenes (sometimes referred to as "m-LLDPE"), post-metallocene catalysts, and constrained geometry catalysts. LLDPEs include linear, substantially linear or heterogeneous polyethylene copolymers or homopolymers. LLDPEs may contain less long chain branching than LDPEs, and LLDPEs include: substantially linear ethylene polymers which are further defined in U.S. Patent 5,272,236, U.S. Patent 5,278,272, and U.S. Patent 5,582,923; homogeneously branched linear ethylene polymer compositions such as those in U.S. Patent 3,645,992; and/or heterogeneously branched ethylene polymers such as those prepared according to the process disclosed in U.S. Patent 4,076,698. The LLDPEs can be made via gas-phase, solution-phase or slurry polymerization or any combination thereof, using any type of reactor or reactor configuration known in the art.

    [0021] Alternatively, the ethylene-based polymer can be a MDPE. MDPEs are ethylene-based polymers having densities generally ranging from 0.926 g/cm3 to 0.940 g/cm3. Alternatively, the MDPE can have a density ranging from 0.930 g/cm3 to 0.939 g/cm3. The MDPE can have I2 of 0.1 g/ 10 min to 20 g/10 min, alternatively > 2 g/10 min, alternatively 2.3 g/10 min to 20 g/10 min, alternatively 2.3 g/10 min to 12 g/10 min, alternatively 2.3 g/10 min to 6 g/10 min, alternatively 4.4 g/10 min to 20 g/10 min and alternatively 6.8 g/10 min to 20 g/10 min. The MDPE can have a melting temperature of at least 124°C, alternatively 124°C to 135°C, and alternatively 124°C to 132°C. MDPE may be made using chromium or Ziegler-Natta catalysts or using metallocene, constrained geometry, or single site catalysts, and typically have MWD greater than 2.5.

    [0022] Alternatively, the ethylene-based polymer can be a HDPE. HDPEs are ethylene-based polymers having densities of at least 0.940 g/cm3. Alternatively, the HDPE can have a density of > 0.940 g/cm3 to 0.970 g/cm3, alternatively > 0.940 g/cm3 to 0.965 g/cm3, alternatively > 0.940 to 0.952 g/cm3. The HDPE can have a melting temperature of at least 124°C, alternatively 124°C to 135°C, alternatively 124°C to 132°C, and alternatively 131°C to 132°C. The HDPE can have I2 of 0.1 g/10 min to 66 g/ 10 min, alternatively 0.2 g/10 min to 20 g/10 min, alternatively > 2 g/10 min, alternatively 2.3 g/10 min to 20 g/10 min, alternatively 3 g/10 min to 12 g/10 min, alternatively 4 g/10 min to 7 g/10 min, alternatively 4.4 g/10 min to 20 g/10 min and alternatively 6.8 g/10 min to 20 g/10 min. The HDPE can have a PDI of 1.0 to 30.0, alternatively 2.0 to 15.0, as determined by GPC.

    [0023] The HDPE suitable for use herein can be unimodal. As used herein, "unimodal" denotes an HDPE having a MWD such that its GPC curve exhibits only a single peak with no discernible second peak, or even a shoulder or hump, relative to such single peak. In contrast, "bi-modal" means that the MWD in a GPC curve exhibits the presence of two component polymers, such as by having two peaks or where one component may be indicated by a hump, shoulder, or tail relative to the peak of the other component polymer. The HDPE used herein may be unimodal. Unimodal HDPE is commercially available from The Dow Chemical Company of Midland, MI, USA. HDPEs are known in the art and may be made by known methods. For example, HDPEs may be prepared with Ziegler-Natta catalysts, chrome catalysts or even metallocene catalysts.

    [0024] Alternatively, the ethylene-based polymer for starting material (b) may be selected from the group consisting of HDPE, MDPE, LLDPE, and a combination thereof. Alternatively, the ethylene-based polymer for starting material (b) may be selected from the group consisting of HDPE, LLDPE, and a combination thereof. Alternatively, the ethylene-based polymer for starting material (b) may be selected from the group consisting of HDPE and LLDPE. Preparation methods for ethylene-based polymers are well known in the art. Any methods known or hereafter discovered for preparing an ethylene-based polymer having the desired properties may be employed for making the ethylene-based polymer. Suitable LLDPEs, MDPEs, and HDPEs may be prepared by methods described above or those disclosed in PCT Publication No. WO2018/049555 and U.S. Patent Application Publication No. 2019/0023895, and the references cited therein. Suitable ethylene-based polymers are commercially available from The Dow Chemical Company of Midland, MI, USA, and examples are shown below in Table 1.
    Table 1 - Ethylene-Based Polymers
    TypeDensity (g/cm3)I2 (g/10 min)Melting Temperature (ºC)
    high density polyethylene 0.950 12 132
    narrow molecular weight distribution high density polyethylene homopolymer 0.952 6.8 131
    high density polyethylene 0.952 4.4 131
    high density polyethylene 0.952 10 130
    high density polyethylene 0.954 20 130
    high density polyethylene homopolymer 0.961 0.80 133
    high density polyethylene homopolymer with a narrow molecular weight distribution 0.965 8.3 133
    ethylene/1-octene linear-low-density polyethylene copolymer 0.917 2.3 123
    ethylene/1-octene linear-low-density polyethylene copolymer 0.919 6.0 124
    polyethylene resin, which is a narrow molecular weight distribution copolymer 0.917 25 124


    [0025] The ethylene-based polymer for use in the composition may comprise virgin polymer and/or recycled polymer. Without wishing to be bound by theory, it is thought that the ethylene-based polymer may comprise ≥ 50% recycled polyethylene. The recycled ethylene-based polymer, if utilized, may be sourced from industrial production streams, as well as from post-industrial and/or post-consumer sources. The selection of the specific ethylene-based polymer, as well as any ratio of virgin polymer to recycled polymer, if utilized in concert, is typically a function of cost and desired properties of the WPC article formed therewith.

    [0026] Starting material (b) may be present in the composition in an amount of 29.5% to 84.5%, alternatively 30% to 60%, alternatively 35% to 55%, and alternatively 40% to 50%, based on combined weights of starting materials (a), (b), (c) and (d).

    (c) Polydiorganosiloxane



    [0027] The composition described above further comprises starting material (c) a polydiorganosiloxane having at least one silicon bonded alkenyl group per molecule. The polydiorganosiloxane comprises unit formula: (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, where each R is an independently selected monovalent hydrocarbon group of 1 to 18 carbon atoms that is free of aliphatic unsaturation, each R' is an independently selected alkenyl group of 2 to 18 carbon atoms, subscript a is 0 to 2, subscript b is 0 to 2, a quantity (a + b) = 2, subscript c ≥ 0, subscript d ≥ 0, a quantity (a + d) ≥ 1, and a quantity (a + b + c + d) is sufficient to give the polydiorganosiloxane a viscosity of 2,000 mPa·s to 60,000 mPa·s at 25°C measured at 0.1 to 50 RPM on a Brookfield DV-III cone & plate viscometer with #CP-52 spindle. One skilled in the art would recognize that rotation rate decreases as viscosity increases and would be able to select the appropriate rotation rate when using this test method to measure viscosity. Alternatively, viscosity may be 2,000 mPa·s to 10,000 mPa·s, and alternatively 2,000 mPa·s to 5,000 mPa·s, measured according to the test method described above at 5 RPM. Alternatively, subscript d may be 0 to 4, alternatively 1 to 4, alternatively 1 to 3, and alternatively 2. Alternatively, a quantity (a + d) may be sufficient to provide an amount of alkenyl groups, R', of 0.05% to 7%, alternatively 0.09% to 6.5%, based on weight of the polydiorganosiloxane. Vinyl content may be measured by FTIR.

    [0028] Alternatively, in the unit formula for the polydiorganosiloxane above, each R may be an alkyl group of 1 to 18 carbon atoms, alternatively 1 to 12 carbon atoms, alternatively 1 to 6 carbon atoms, and alternatively 1 to 4 carbon atoms. Suitable alkyl groups include methyl, ethyl, propyl (including n-propyl and iso-propyl), and butyl (including n-butyl, tert-butyl, sec-butyl, and iso-butyl). Alternatively, each R may be methyl.

    [0029] Alternatively, in the unit formula for the polydiorganosiloxane above, each R' may be an alkenyl group of 2 to 12 carbon atoms, alternatively 2 to 6 carbon atoms, and alternatively 2 to 4 carbon atoms. Suitable alkenyl groups include vinyl, allyl, butenyl, and hexenyl. Alternatively, each R' may be vinyl or hexenyl. Alternatively, each R' may be vinyl.

    [0030] The polydiorganosiloxane may have a terminal alkenyl group, a pendant alkenyl group, or both terminal and pendant alkenyl groups. Alternatively, in the unit formula for the polydiorganosiloxane above, subscript a may be 0 and subscript d may be greater than or equal to 1, i.e., the polydiorganosiloxane may have pendant alkenyl groups but not terminal alkenyl groups. Alternatively, subscript a may be 2, subscript b may be 0 and subscript d may be 0, i.e., the polydiorganosiloxane may be a bis-alkenyl-terminated polydiorganosiloxane.

    [0031] The bis-alkenyl-terminated polydiorganosiloxane may comprise formula

    where each R and R' are as described above, and subscript x has a value sufficient to give the polydiorganosiloxane the viscosity of 2,000 mPa·s to 60,000 mPa·s measured as described above. One skilled in the art would recognize that rotation rate decreases as viscosity increases and would be able to select the appropriate rotation rate when using this test method to measure viscosity. Alternatively, viscosity may be 2,000 mPa·s to 10,000 mPa·s, and alternatively 2,000 mPa·s to 5,000 mPa·s, measured according to the test method described above at 5 RPM.

    [0032] Alternatively, each R may be an alkyl group of 1 to 18 carbon atoms, alternatively 1 to 12 carbon atoms, alternatively 1 to 6 carbon atoms, and alternatively 1 to 4 carbon atoms. Suitable alkyl groups include methyl, ethyl, propyl (including n-propyl and iso-propyl), and butyl (including n-butyl, tert-butyl, sec-butyl, and iso-butyl). Alternatively, each R may be methyl.

    [0033] Alternatively, in the formula for the polydiorganosiloxane above, each R' may be an alkenyl group of 2 to 12 carbon atoms, alternatively 2 to 6 carbon atoms, and alternatively 2 to 4 carbon atoms. Suitable alkenyl groups include vinyl, allyl, butenyl, and hexenyl Alternatively, each R' may be vinyl or hexenyl. Alternatively, each R' may be vinyl.

    [0034] Starting material (c) may comprise a polydiorganosiloxane such as
    c-1) α,ω-dimethylvinylsiloxy-terminated polydimethylsiloxane, c-2) α,ω-dimethylvinylsiloxy-terminated poly(dimethylsiloxane/methylphenylsiloxane), c-3) α,ω-dimethylvinylsiloxy-terminated poly(dimethylsiloxane/diphenylsiloxane), c-4) α,ω-phenyl,methyl,vinyl-siloxy-terminated polydimethylsiloxane, c-5) α,ω-dimethylhexenylsiloxy-terminated polydimethylsiloxane, c-6) α,ω-dimethylhexenylsiloxy-terminated poly(dimethylsiloxane/methylphenylsiloxane), c-7) α,ω-dimethylhexenylsiloxy-terminated poly(dimethylsiloxane/diphenylsiloxane), c-8) α,ω-phenyl,methyl,hexenyl-siloxy-terminated polydimethylsiloxane, c-9) α,ω-dimethylvinylsiloxy-terminated poly(dimethylsiloxane/methylvinylsiloxane), c-10) α,ω-dimethylvinylsiloxy-terminated poly(dimethylsiloxane/methylphenylsiloxane/methylvinylsiloxane), c-11) α,ω-dimethylvinylsiloxy-terminated poly(dimethylsiloxane/diphenylsiloxane/methylvinylsiloxane), c-12) α,ω-phenyl,methyl,vinyl-siloxy-terminated poly(dimethylsiloxane/methylvinylsiloxane), c-13) α,ω-dimethylhexenylsiloxy-terminated poly(dimethylsiloxane/methylhexenylsiloxane), c-14) α,ω-dimethylhexenylsiloxy-terminated poly(dimethylsiloxane/methylphenylsiloxane/methylhexenylsiloxane), c-15) α,ω-dimethylhexenylsiloxy-terminated poly(dimethylsiloxane/diphenylsiloxane/methylhexenylsiloxane), c-16) α,ω-phenyl,methyl,hexenyl-siloxy-terminated poly(dimethylsiloxane/methylhexenylsiloxane), c-17) trimethylsiloxy-terminated poly(dimethylsiloxane/methylvinylsiloxane), c-18) trimethylsiloxy-terminated poly(dimethylsiloxane/methylphenylsiloxane/methylvinylsiloxane), c-19) trimethylsiloxy-terminated poly(dimethylsiloxane/diphenylsiloxane/methylvinylsiloxane), c-20) trimethylsiloxy-terminated poly(dimethylsiloxane/methylhexenylsiloxane), c-21) trimethylsiloxy-terminated poly(dimethylsiloxane/methylphenylsiloxane/methylhexenylsiloxane), c-22) trimethylsiloxy-terminated poly(dimethylsiloxane/diphenylsiloxane/methylhexenylsiloxane), c-23) a combination of two or more of c-1) to c-22). Alternatively, the polydiorganosiloxane may be selected form the group consisting of c-1), c-5), c-9), c-13), c-17), c-20), and a combination of two or more thereof. Alternatively, the polydiorganosiloxane may be selected form the group consisting of c-1), c-5), c-9), c-13), and a combination of two or more thereof. Alternatively, the polydiorganosiloxane may be a bis-vinyldimethylsiloxy-terminated polydimethylsiloxane. Polydiorganosiloxanes described above are commercially available. Bis-vinyldimethylsiloxy-terminated polydimethylsiloxanes are commercially available from Dow Silicones Corporation of Midland, Michigan, USA, and examples include bis-vinyldimethylsiloxy-terminated polydimethylsiloxane with a viscosity of 60,000 mPa·s, bis-vinyldimethylsiloxy-terminated polydimethylsiloxane with a viscosity of 10,000 mPa·s, bis-vinyldimethylsiloxy-terminated polydimethylsiloxane with a viscosity of 5,000 mPa·s, and bis-vinyldimethylsiloxy-terminated polydimethylsiloxane with a viscosity of 2,000 mPa·s, where viscosity was measured 25°C at 0.1 to 50 RPM on a Brookfield DV-III cone & plate viscometer with #CP-52 spindle. Suitable polydiorganosiloxanes may be prepared by methods known in the art such as hydrolysis and condensation of appropriate organohalosilane monomers and/or equilibration of linear and cyclic polyorganosiloxanes optionally with endcapping.

    [0035] Starting material (c) may be one polydiorganosiloxane or may be a combination of two or more polydiorganosiloxanes that differ from one another by at least one property such as selection of R groups, selection of R' groups, and viscosity. Starting material (c) may be present in the composition in an amount of 0.5% to 6%, alternatively 1% to 4%, alternatively 0.5% to 3%, alternatively 1% to 2%, and alternatively 1.5% to 2%, based on combined weights of starting materials (a), (b), (c) and (d).

    (d) Maleated Ethylene-Based Polymer



    [0036] The composition described above may further comprise starting material (d) a maleated ethylene-based polymer. As used herein, the term "maleated" indicates a polymer (e.g., an ethylene-based polymer) that has been modified to incorporate a maleic anhydride monomer. Maleic anhydride can be incorporated into the ethylene-based polymer by any methods known or hereafter discovered in the art. For instance, the maleic anhydride can be copolymerized with ethylene and other monomers (if present) to prepare an interpolymer having maleic anhydride residues incorporated into the polymer backbone. Alternatively, the maleic anhydride can be graft-polymerized to the ethylene-based polymer. Techniques for copolymerizing and graft polymerizing are known in the art.

    [0037] The maleated ethylene-based polymer may be an ethylene-based polymer having maleic anhydride grafted thereon. The ethylene-based polymer prior to being maleated can be any of the ethylene-based polymers described above, alternatively, the ethylene-based polymer used for maleating may have a melt index lower than that melt index of the ethylene-based polymer described above. The starting ethylene-based polymer can be selected from a linear-low density polyethylene, a medium-density polyethylene, and a high-density polyethylene. Alternatively, the starting ethylene-based polymer can be a high-density polyethylene.

    [0038] The maleated ethylene-based polymer may have a density of at least 0.923 g/cm3. Alternatively, the maleated ethylene-based polymer can have a density of 0.923 g/cm3 to 0.962 g/cm3, alternatively 0.940 g/cm3 to 0.962 g/cm3, and alternatively 0.923 g/cm3 to 0.940 g/cm3. Density of the maleated ethylene-based polymer may be determined by ASTM D792 - 13. The maleated ethylene-based polymer may have I2 of 0.1 g/10 min to 25 g/10 min, alternatively 0.1 g/10 min to 10 g/10 min, alternatively 1 g/10 min to 2 g/10 min, alternatively 2 g/10 min to 25 g/10 min, alternatively 2 g/10 min to 12 g/10 min, alternatively 3 g/10 min to 25 g/10 min, and alternatively 3 g/10 min to 12 g/10min. Values for I2 for maleated ethylene-based polymers are determined at 190°C and 2.16 Kg according to ASTM D1238 - 13. The maleated ethylene-based polymer can have a maleic anhydride content of at least 0.25%, alternatively an amount of 0.25% to 2.5%, and alternatively 0.5% to 1.5%, each based on the total weight of the maleated ethylene-based polymer. Maleic anhydride concentrations may be determined by a titration method, which takes dried resin and titrates with 0.02N KOH to determine the amount of maleic anhydride. The dried polymers are titrated by dissolving 0.3 to 0.5 grams of maleated ethylene-based polymer in 150 mL of refluxing xylene. Upon complete dissolution, deionized water (four drops) is added to the solution and the solution is refluxed for 1 hour. Next, 1% thymol blue (a few drops) is added to the solution and the solution is over titrated with 0.02N KOH in ethanol as indicated by the formation of a purple color. The solution is then back-titrated to a yellow endpoint with 0.05N HCI in isopropanol.

    [0039] Suitable maleated ethylene-based polymers for starting material (d) may be prepared by known methods, such as those disclosed in PCT Publication No. WO2018/049555 and the references cited therein. Alternatively, maleated ethylene-based polymers may be prepared by a process for grafting maleic anhydride on an ethylene-based polymer, which can be initiated by decomposing initiators to form free radicals, including azo-containing compounds, carboxylic peroxyacids and peroxyesters, alkyl hydroperoxides, and dialkyl and diacyl peroxides, among others. Many of these compounds and their properties have been described (Reference: J. Branderup, E. Immergut, E. Grulke, eds. "Polymer Handbook," 4th ed., Wiley, New York, 1999, Section II, pp. 1-76.). Alternatively, the species that is formed by the decomposition of the initiator may be an oxygen-based free radical. Alternatively, the initiator may be selected from the group consisting of carboxylic peroxyesters, peroxyketals, dialkyl peroxides, and diacyl peroxides. Exemplary initiators, commonly used to modify the structure of polymers, are listed in U.S. Patent No. 7,897,689, in the table spanning col. 48 line 13 - col. 49 line 29. Alternatively, the grafting process for making maleated ethylene-based polymers can be initiated by free radicals generated by thermal oxidative processes. Suitable maleated ethylene-based polymers are commercially available from The Dow Chemical Company, of Midland, MI, USA, such as those described below in Table 2.
    Table 2 - Examples of Maleated Ethylene-Based Polymers
    Typea random ethylene copolymer incorporating a monomer which is classified as being a maleic anhydride equivalenthigh density polyethylene grafted with very high maleic anhydride copolymer graft level
    Density (q/cm3) 0.940 0.962
    I2 (g/10 min) 25 2.0
    Melting Temperature (ºC) 108 130


    [0040] In Table (d), densities were measured by ASTM D792 - 13; I2 values were measured by ASTM D1238 -13 at 190°C and 2.16 Kg; and melting temperatures were measured by DSC according to ASTM D3418 -15.

    [0041] Starting material (d) can be one maleated ethylene-based polymer or a combination of two or more maleated ethylene-based polymers (e.g., a blend of two or more maleated ethylene-based polymers that differ from one another by at least one property such as monomer composition, monomer content, catalytic method of preparation, molecular weight, molecular weight distributions, and/or densities). The maleated ethylene-based polymer may be present in the composition in an amount of 0 to 4%. Alternatively, the maleated ethylene-based polymer may be present in an amount of 0 to 2%, alternatively > 0% to 2%, alternatively 1% to 3%, and alternatively 1% to 2%, based on combined weights of starting materials (a), (b), (c), and (d).

    Additional Starting Materials



    [0042] The composition described above may optionally further comprise one or more additional starting materials. For example, one or more additional starting materials may be selected from the group consisting of (e) an additional filler which is distinct from the lignocellulosic-based filler of starting material (a), (f) a colorant, (g) a blowing agent, (h) a UV stabilizer, (i) an antioxidant, (j) a process aid, (k) a preservative, (I) a biocide, (m) a flame retardant, (n) an impact modifier, and (o) a combination of two or more of starting materials (e) to (n). Each additional starting material, if utilized, may be present in the composition in an amount of greater than 0 to 30% based on combined weights of all starting materials in the composition. The composition may also include other optional additives, as known in the art. Such additives are described, for example, in Walker, Benjamin M., and Charles P. Rader, eds. Handbook of thermoplastic elastomers. New York: Van Nostrand Reinhold, 1979; Murphy, John, ed. Additives for plastics handbook. Elsevier, 2001.

    (e) Additional Filler



    [0043] The composition may optionally further comprise starting material (e) a filler distinct from the lignocellulosic-filler described above as starting material (a). Specific examples of suitable fillers include, but are not limited to, calcium carbonate, silica, quartz, fused quartz, talc, mica, clay, kaolin, wollastonite, feldspar, aluminum hydroxide, carbon black, and graphite. Alternatively, this filler may be a mineral filler. Alternatively, this filler may be selected from the group consisting of calcium carbonate, talc, and combinations thereof. Suitable fillers are known in the art and are commercially available, e.g., ground silica is sold under the name MIN-U-SIL by U.S. Silica of Berkeley Springs, West Virginia, USA. Suitable precipitated calcium carbonates include Winnofil SPM from Solvay and Ultra-pflex and Ultra-pflex 100 from Specialty Minerals, Inc. of Quinnesec, Michigan, USA.

    [0044] The shape and dimensions of the filler is not specifically restricted. For example, the filler may be spherical, rectangular, ovoid, irregular, and may be in the form of, for example, a powder, a flour, a fiber, a flake, a chip, a shaving, a strand, a scrim, a wafer, a wool, a straw, a particle, and combinations thereof. Dimensions and shape are typically selected based on the type of the filler utilized, the selection of other starting materials included within the solid carrier component.

    [0045] Regardless of the selection of the filler, the filler may be untreated, pretreated, or added in conjunction with an optional filler treating agent, described below, which when so added may treat the filler in situ or before incorporation of the filler in the composition described above. Alternatively, the filler may be surface treated to facilitate wetting or dispersion in the composition, which when so added may treat the filler in situ in the composition.

    [0046] The filler treating agent may comprise a silane such as an alkoxysilane, an alkoxy-functional oligosiloxane, a cyclic polyorganosiloxane, a hydroxyl-functional oligosiloxane such as a dimethyl siloxane or methyl phenyl siloxane, an organosilicon compound, a stearate, or a fatty acid. The filler treating agent may comprise a single filler treating agent, or a combination of two or more filler treating agents selected from similar or different types of molecules.

    [0047] The filler treating agent may comprise an alkoxysilane, which may be a mono-alkoxysilane, a dialkoxysilane, a tri-alkoxysilane, or a tetra-alkoxysilane. Alkoxysilane filler treating agents are exemplified by hexyltrimethoxysilane, octyltriethoxysilane, decyltrimethoxysilane, dodecyltrimethoxysilane, tetradecyltrimethoxysilane, phenyltrimethoxysilane, phenylethyltrimethoxysilane, octadecyltrimethoxysilane, octadecyltriethoxysilane, and a combination thereof. In certain aspects the alkoxysilane(s) may be used in combination with silazanes, which catalyze the less reactive alkoxysilane reaction with surface hydroxyls. Such reactions are typically performed above 100°C with high shear with the removal of volatile by-products such as ammonia, methanol and water.

    [0048] Suitable filler treating agents also include alkoxysilyl functional alkylmethyl polysiloxanes, or similar materials where the hydrolyzable group may comprise, for example, silazane, acyloxy or oximo.

    [0049] Alkoxy-functional oligosiloxanes can also be used as filler treating agents. Alkoxy-functional oligosiloxanes and methods for their preparation are generally known in the art. Other filler treating agents include mono-endcapped alkoxy functional polydiorganosiloxanes, i.e., polyorganosiloxanes having alkoxy functionality at one end.

    [0050] Alternatively, the filler treating agent can be any of the organosilicon compounds typically used to treat silica fillers. Examples of organosilicon compounds include organochlorosilanes such as methyltrichlorosilane, dimethyldichlorosilane, and trimethyl monochlorosilane; organosiloxanes such as hydroxy-endblocked dimethylsiloxane oligomer, silicon hydride functional siloxanes, hexamethyldisiloxane, and tetramethyldivinyldisiloxane; organosilazanes such as hexamethyldisilazane and hexamethylcyclotrisilazane; and organoalkoxysilanes such as alkylalkoxysilanes with methyl, propyl, n-butyl, i-butyl, n-hexyl, n-octyl, i-octyl, n-decyl, dodecyl, tetradecyl, hexadecyl, or octadecyl substituents. Organoreactive alkoxysilanes can include amino, methacryloxy, vinyl, glycidoxy, epoxycyclohexyl, isocyanurato, isocyanato, mercapto, sulfido, vinyl-benzyl-amino, benzyl-amino, or phenyl-amino substituents. Alternatively, the filler treating agent may comprise an organopolysiloxane. Alternatively, certain filler treating agents, such as chlorosilanes, may be hydrolyzed at the filler surface. Alternatively, the filler treating agent may take advantage of multiple hydrogen bonds, either clustered or dispersed or both, as the method to bond the organosiloxane to the surface of the filler. The organosiloxane capable of hydrogen bonding has an average, per molecule, of at least one silicon-bonded group capable of hydrogen bonding. The group may be selected from: a monovalent organic group having multiple hydroxyl functionalities or a monovalent organic group having at least one amino functional group. Hydrogen bonding may be a primary mode of bonding of the organosiloxane to the filler. The organosiloxane may be incapable of forming covalent bonds with the filler. The organosiloxane capable of hydrogen bonding may be selected from the group consisting of a saccharide-siloxane polymer, an amino-functional organosiloxane, and a combination thereof. Alternatively, the polyorganosiloxane capable of hydrogen bonding may be a saccharide-siloxane polymer.

    [0051] Alternatively, the filler treating agent may comprise alkylthiols such as octadecyl mercaptan and others, and fatty acids such as oleic acid, stearic acid, titanates, titanate coupling agents, zirconate coupling agents, and a combination thereof. One skilled in the art could optimize a filler treating agent to aid dispersion of the filler without undue experimentation.

    [0052] Starting material (e) may be one additional filler or a combination of two or more additional fillers that differ from one another by at least one property such as type of filler, method of preparation, treatment or surface chemistry, filler composition, filler shape, filler surface area, average particle size, and/or particle size distribution. The additional filler, when present, may be added to the composition in an amount of > 0% to 30%, alternatively 10% to 15%, based on combined weights of all starting materials in the composition.

    [0053] When selecting starting materials to include in the composition, there may be overlap between types of starting materials because certain starting materials described herein may have more than one function. For example, (e) the additional filler may be useful as an additional filler and as a colorant, and even as a flame retardant, e.g., carbon black. When selecting starting materials for the composition, the components selected are distinct from one another.

    Method of Making



    [0054] This invention further relates to a method for preparing a wood plastic composite (WPC) article. The method comprises:
    1. (1) combining starting materials comprising

      15 weight % to 70 weight % of (a) the lignocellulosic-based filler described above;

      29.5 weight % to 84.5 weight % of (b) the ethylene-based polymer described above;

      0.5 weight % to 6 weight % of (c) the polydiorganosiloxane of unit formula (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, where R and R', and subscripts a, b, c, and d are as described above; and

      0 to 4 weight % of (D) a maleated ethylene-based polymer;

      each based on combined weights of starting materials (a), (b), (c), and (d); thereby preparing a composition; and

    2. (2) preparing the WPC article from the composition.


    [0055] In step (1), the composition is formed by combining at least (a) the lignocellulosic-based filler, (b) the ethylene-based polymer, and (c) the polydiorganosiloxane along with any optional starting materials present in the composition. When (c) the polydiorganosiloxane is in the form of a solid carrier component, the method may comprise combining (a) the lignocellulosic-based filler, (b) the ethylene-based polymer, and the solid carrier component comprising (c) the polydiorganosiloxane.

    [0056] The starting materials of the composition may be combined in any order and via any suitable manner. For example, (b) the ethylene-based polymer may be melted before, during, and/or after formation of the composition. For example, (b) the ethylene-based polymer may be heated before and/or during combining the starting materials such that (a) the lignocellulosic-based filler and (c) the polydiorganosiloxane are combined with a melted form of (b) the ethylene-based polymer. Starting materials (a) the lignocellulosic-based filler and (c) the polydiorganosiloxane be combined with the melted form of (b) the ethylene-based polymer in any order, e.g., individually, sequentially, together, or simultaneously. Alternatively, however, (b) the ethylene-based polymer may be combined with (a) the lignocellulosic-based filler and (c) the polydiorganosiloxane before heating or melting starting material (b) the ethylene-based polymer such that (b) the ethylene-base polymer is in solid and unmelted or unsoftened form when preparing the composition. Alternatively, (a) the lignocellulosic-based filler and (c) the polydiorganosiloxane may be combined and heated, then added to (b) the ethylene-based polymer in solid or liquid form when preparing the composition.

    [0057] Starting material (b) the ethylene-based polymer is heated before, during, and/or after formation of the composition to a temperature that is greater than the melting temperature of (b) the ethylene-based polymer, e.g., 10°C to 90°C, alternatively 10°C to 40°C, higher than the melting temperature of (b) the ethylene-based polymer. This ensures melting rather than mere softening of (b) the ethylene-based polymer. Alternatively, lower temperatures may be utilized in combination with shear or mixing to ensure softening and/or melting of (b) the ethylene-based polymer.

    [0058] Starting material (c) the polydiorganosiloxane may be in liquid form or delivered in the form of solid carrier component. The solid carrier component is a solid at room temperature and is a combination comprising (i) the polydiorganosiloxane described above as starting material (c) and (ii) a polymer component selected from the group consisting of an ethylene-based polymer (as described above for starting material (b)), a maleated ethylene-based polymer (as described above for starting material (d)), or a combination of both the ethylene-based polymer and the maleated ethylene-based polymer. The solid carrier component may optionally further comprise a filler, as described below.

    [0059] Alternatively, (a) the lignocellulosic-based filler and (c) the polydiorganosiloxane and at least one other starting material (e.g., one or more of the additional starting materials (e) to (n) described above) may be combined to give a mixture, and the mixture may be combined with (b) the ethylene-based polymer (and any other additional starting materials) to give the composition. Combining (a) the lignocellulosic-based filler and (c) the polydiorganosiloxane may be referred to as surface treating, wetting, or pre-treating (a) the lignocellulosic-based filler, which may be further to or alternatively to surface treating (a) the lignocellulosic-based filler as set forth herein. Alternatively, (a) the lignocellulosic-based filler and (c) the polydiorganosiloxane may be combined by spraying, impregnation, blending or mixing. Combining (a) the lignocellulosic-based filler and (c) the polydiorganosiloxane may further comprise heating, e.g., to combine (c) the polydiorganosiloxane with (a) the lignocellulosic-based filler. Optionally, the resulting combination of (a) the lignocellulosic-based filler and (c) the polydiorganosiloxane may be compacted before being pelletized to form the pellet if a pellet is utilized. Combining (a) the lignocellulosic-based filler and (c) the polydiorganosiloxane may be performed in a separate process or may be integrated into an existing (e.g., extrusion) process for making a WPC article in a pre-mixing step. In the pre-mixing step, the starting materials may be blended together before feeding into an extruder, e.g., all or a portion of (a) the lignocellulosic-based filler, (c) the polydiorganosiloxane and (b) the ethylene-based polymer and one or more optional starting materials, may be mixed in the pre-mixing step and thereafter fed to an extruder.

    [0060] Alternatively, (c) the polydiorganosiloxane may be present in a solid carrier component which comprises, alternatively consists essentially of, alternatively consists of: (a) the lignocellulosic-based filler and (c) the polydiorganosiloxane; and the solid carrier component may be heated. Alternatively, this solid carrier component may be heated in a vacuum. This can be performed for multiple reasons, such as to evaporate the carrier vehicle (if any), to evaporate other components present in the mixture used to form the solid carrier component or to improve the mechanical properties of the solid carrier component before using in the method.

    [0061] The composition may be formed under mixing or shear, e.g., with suitable mixing equipment. For example, the composition may be formed in a vessel equipped with an agitator and/or mixing blades. The vessel may be, for example, an internal mixer, such as a Banbury, Sigma (Z) Blade, or Cavity Transfer style mixer. Alternatively or in addition, the composition may be formed in or processed by an extruder, which may be any extruder, e.g., a single screw extruder with rotational and/or reciprocating (co-kneader) screws, as well as multi-screw devices comprising two or more screws, which may be aligned tangentially or partially/fully intermeshing, revolving in either a co- or counter-rotational direction. Alternatively, a conical extruder may be used for forming the WPC composition described herein.

    [0062] In the method for preparing the WPC article as described above, the method further comprises forming the WPC article from the composition in step 2). The composition may be prepared, e.g., in the vessel, and subsequently removed from the vessel to form the article with separate equipment. Alternatively, the same equipment may be utilized to prepare the composition and subsequently form the WPC article. For example, the composition may be prepared and/or mixed in an extruder, and the extruder may be utilized to form the WPC article with the composition. Alternatively, the WPC article may be formed via molding, e.g., with an injection, compression, or transfer molding process. The composition may be formed independently and disposed in the mold once formed.

    [0063] The method described above comprises forming the WPC article from the composition, which may comprise forming the composition into a desired shape. The desired shape depends on end use applications of the WPC article. One of skill in the art understands how dies for extrusion and molds for molding may be selected and created based on the desired shape of the WPC article.

    [0064] The method may be performed continuously or semi-continuously in an extruder, such as a twin screw extruder (in which the screws are concurrently rotated, partially or fully intermeshing, alternatively counter rotated aligned either tangentially or partially or fully intermeshing). Starting material (c) the polydiorganosiloxane (in liquid state or as part of a solid carrier component) may be disposed in the extruder concurrently with (a) the lignocellulosic-based filler and (b) the ethylene-based polymer. Alternatively, the polydiorganosiloxane may be disposed in the extruder after melting (b) the ethylene-based polymer and before adding (a) the lignocellulosic-based filler. Alternatively, the polydiorganosiloxane may be disposed in the extruder after (a) the lignocellulosic-based filler and (b) the ethylene-based polymer and before the WPC article exits the extruder. Alternatively, (a) the lignocellulosic-based filler may be disposed in the extruder concurrently with the polydiorganosiloxane, where they are heated to effect surface treatment of (a) the lignocellulosic-based filler with (c) the polydiorganosiloxane, then (b) the ethylene-based polymer may be disposed in the extruder to give a mixture and the temperature increased to a temperature suitable for compounding the mixture and forming the WPC article. The extruder may have one or more zones, such as 1 to 3, or 3 to 8, or 1 to 12, zones, where starting materials can be added. The zones may be heated at different temperatures.

    [0065] Alternatively, (b) the ethylene-based polymer may be disposed in a first zone of the extruder, which is heated at +/-30 °C within the melting temperature of (b) the ethylene-based polymer. Starting material (c) the polydiorganosiloxane, which may be delivered in a solid carrier component, may be disposed in a second or later zone of the extruder, which may be heated at 10°C to 90°C above the melting temperature of (b) the ethylene-based polymer. As noted above, the temperature utilized is typically less than a degradation temperature of the starting materials of the composition. Alternatively, the die of the extruder may also be heated, and the temperatures utilized by the extruder, including the temperature of any zone and the die, may be selected such that the temperatures do not exceed a degradation temperature of (a) the lignocellulosic-based filler. The degradation temperature of (a) the lignocellulosic-based filler is contingent on the selection thereof, as understood by one of skill in the art.

    [0066] The method described above may be used to produce various WPC articles, such as building materials. Such WPC building materials include residential and/or commercial building and construction products and applications, e.g., decking, railing, siding, fencing, window framing, trim, skirts, and flooring. When the building material is decking, the method may optionally further comprise step 3), adding a cap stock layer after step 2).

    Solid Carrier Component Composition



    [0067] As described above, (c) the polydiorganosiloxane may be added to the composition for preparing the WPC article in the form of a solid carrier component. The solid carrier component may comprise, alternatively may consist essentially of, alternatively may consist of:

    5% to 20%, alternatively 5% to < 20%, of (i) the polydiorganosiloxane described above as starting material (c);

    > 70% to 95% of (ii) a polymer component selected from the group consisting of:

    an ethylene-based polymer as described above for starting material (b),

    a maleated ethylene-based polymer as described above for starting material (d), and

    a combination of both the ethylene-based polymer and the maleated ethylene-based polymer; and

    0 to 10 % of (iii) a filler.



    [0068] Starting material (i) the polydiorganosiloxane in the solid carrier component is as described above for starting material (c). Starting material (ii) the polymer component may comprise the ethylene-based polymer and may be free of maleated ethylene-based polymer. The ethylene-based polymer in the solid carrier component is as described above for starting material (b). Alternatively, in the solid carrier component the ethylene-based polymer may be selected from the group consisting of LLDPE, HDPE and a combination thereof, alternatively the ethylene-based polymer in the solid carrier component may be HDPE. Alternatively, the ethylene-based polymer in the solid carrier component may be HDPE with a I2 > 2 g/10 min, alternatively 2.3 g/10 min to 20 g/10 min, alternatively 2.3 g/10 min to 12 g/10 min, alternatively 2.3 g/10 min to 6 g/10 min, alternatively 4.4 g/10 min to 20 g/10 min, and alternatively 6.8 g/10 min to 20 g/10 min. Alternatively, (ii) the polymer component may be a maleated ethylene-based polymer, and the solid carrier component may be free of ethylene-based polymer. The maleated ethylene-based polymer for use in the solid carrier component may be as described above for starting material (d). Alternatively, (ii) the polymer component may include both an ethylene-based polymer and a maleated ethylene-based polymer. The filler in the solid carrier component is optional. When present, the filler may comprise a lignocellulosic-based filler as described above for starting material (a), an additional filler, such as a mineral filler, as described above as starting material (e), or a combination of both the lignocellulosic-based filler and the additional filler. Alternatively, the filler in the solid carrier component may be a mineral filler, and alternatively the mineral filler may be selected from the group consisting of talc, calcium carbonate, and a combination thereof. Alternatively, (e) the additional filler may be talc. The solid carrier component may alternatively comprise 5% to < 20% of (i) the polydiorganosiloxane, > 70% to 95% of (ii) the polymer component, and 0 to 10% of (iii) the filler. Alternatively, the solid carrier component may comprise 5% to 18% of (i) the polydiorganosiloxane, alternatively 10% to 18%, and alternatively 10% to 15% of the polydiorganosiloxane. Alternatively, the solid carrier component may contain 0% filler. Alternatively, the solid carrier component may comprise > 75% to 90% of (ii) the polymer component, alternatively 80% to 90% of (ii) the polymer component.

    [0069] The solid carrier component is a solid at ambient temperature and pressure (e.g., 25°C and 1 atmosphere). The solid carrier component may be formed by combining the starting materials in any order. The solid carrier component may be prepared by forming a mixed composition from (ii) the polymer component and (i) the polydiorganosiloxane, and when present (iii), the filler, by dispersing under mixing or shear, e.g., with suitable mixing equipment. For example, the mixed composition may be dispersed in a vessel equipped with an agitator and/or mixing blades. The vessel may be, for example, an internal mixer, such as a Banbury, Sigma (Z) Blade, or Cavity Transfer style mixer. Alternatively or in addition, the mixed composition may be dispersed in or processed by an extruder, which may be any extruder, e.g., a single screw extruder with rotational and/or reciprocating (co-kneader) screws, as well as multi-screw devices comprising two or more screws, which may be aligned tangentially or partially/fully intermeshing, revolving in either a co- or counter-rotational direction. Alternatively, a conical extruder may be used to disperse the mixed composition described herein.

    [0070] The solid carrier components prepared as described above are re-processable and may be prepared for feeding in subsequent processes. The mixed composition prepared as described above may be, for example, substantially continuous ribbons or discontinuous pellets or particles or powders. Substantially continuous ribbons can be formed by pressurizing the mixed composition and passing it through a die to create continuous strands or tapes that are subsequently cooled before being suitably packaged. Alternatively, the strand or tape may be comminuted to form pellets or powders. The mixing device may also produce the pressure and/or heat needed to process the mixed composition through the die when the mixing device is an extruder, which may be any extruder, e.g., BUSS kneader, or a single screw extruder with rotational and/or reciprocating (co-kneader) screws, as well as multi-screw devices comprising two or more screws, which may be aligned tangentially or partially/fully intermeshing, revolving in either a co- or counter-rotational direction. A conical extruder may be used for mixing and pressurizing the mixed composition. Alternately, a gear pump may be used to generate the pressure needed for extrusion after the starting materials have been mixed to form the mixed. Discontinuous forms of the mixed composition may be created by chopping continuous ribbons of mixed composition into shorter lengths. Alternatively, large pieces of mixed composition may be reduced to usable sizes by use of a grinder or shredder.

    [0071] The solid carrier component may be formed by a method performed continuously or semi-continuously in an extruder, such as a twin screw extruder (in which the screws are concurrently rotated, partially or fully intermeshing, alternatively counter rotated aligned either tangentially or partially or fully intermeshing). Alternatively, (i) the polydiorganosiloxane may be disposed in the extruder concurrently with the polymer component and optionally (iii) the filler. Alternatively, (i) the polydiorganosiloxane may be disposed in the extruder after melting (ii) the polymer component (and before adding (iii) the filler, if any will be added to the mixed composition). Alternatively, (i) the polydiorganosiloxane may be disposed in the extruder after (iii) the filler, when present, and before (ii) the polymer component, and before the mixed composition exits the extruder. Alternatively, (iii) the filler may be disposed in the extruder concurrently with (i) the polydiorganosiloxane, then the polymer component may be disposed in the extruder to give a mixture and the temperature increased to a temperature suitable for compounding the mixture. The extruder may have one or more zones, such as 1 to 3, alternatively 1 to 12, alternatively 3 to 12, or alternatively 3 to 10 zones, where starting materials can be added. The zones may be heated at different temperatures and incorporate various functional stages including conveying, melting, mixing, deaeration, vacuum, pressurization, and forming.

    [0072] Alternatively, (ii) the polymer component may be disposed in a first zone of the extruder, which is heated at +/-30 °C within the melting temperature of the polymer component. The (i) polydiorganosiloxane may be disposed in a second zone of the extruder, which is heated at 10°C to 90°C above the melting temperature of (ii) the polymer component. Starting material (iii), the filler, when present, is disposed in one or more of the first, second, or subsequent zones of the extruder. As noted above, the temperature utilized is typically less than a degradation temperature of the starting materials of the solid carrier component. The mixture may be stripped to remove any air, moisture or byproducts prior to pressurization and forming in the die of the extruder. The vacuum, pressurization, and forming zones may also be heated, and the temperatures utilized by the extruder, including the temperature of any zone and the die, does not exceed a degradation temperature of starting materials (i), (ii), and, when present (iii). The degradation temperature of starting materials (i), (ii), and (iii) is contingent on the selection thereof, as understood by one of skill in the art. The resulting extruded strand may be comminuted by any convenient means to form the solid carrier component.

    [0073] The solid carrier component is typically in particulate form, and may be, for example, in the form of particles, pellets, or powders. An average particle size of the solid carrier component is a function of desired properties and end use thereof. The solid carrier component may be a powder. Alternatively, the solid carrier component may be a pellet. Pellets typically have greater average particle sizes than powders.

    EXAMPLES



    [0074] These examples are intended to illustrate the invention to one skilled in the art and are not to be interpreted as limiting the scope of the invention set forth in the claims. The starting materials in Table 3 were used in these examples.
    Table 3 - Starting Materials
    MaterialDescription
    LLDPE 1 ethylene/1 -octene linear-low-density polyethylene copolymer with I2 = 2.3 g/10 min, a density of 0.917 g/cm3, and a melting temperature of 123°C
    LLDPE 2 ethylene/1 -octene linear-low-density polyethylene copolymer with I2 = 25 g/10 min, a density of 0.917 g/cm3, and a melting temperature of 124°C
    HDPE 1 narrow molecular weight distribution high density polyethylene homopolymer with I2 = 6.8 g/10 min, a density of 0.952 g/cm3, and a melting temperature of 131°C
    HDPE 2 high density polyethylene homopolymer with I2 = 0.8 g/10 min, a density of 0.961 g/cm3, and a melting temperature of 133°C
    Si-60,000 bis-vinyl-terminated polydimethylsiloxane with a viscosity of 60,000 mPa·s
    Si-10,000 bis-vinyl-terminated polydimethylsiloxane with a viscosity of 10,000 mPa·s
    Si-5,000 bis-vinyl-terminated polydimethylsiloxane with a viscosity of 5,000 mPa·s
    Si-2,000 bis-vinyl-terminated polydimethylsiloxane with a viscosity of 2,000 mPa·s
    MAPE high density polyethylene grafted with very high maleic anhydride copolymer graft level having density of 0.962 g/cm3 and I2 = 2.0 g/ 10 min
    CaCO3 Calcium Carbonate (untreated with a particle size of 3 µm)
    Filler 40M1 Sixty mesh wood flour purchased from American Wood Fibers and composed of primarily hardwoods such as maple, poplar, ash and beech. The hydroscopic nature of wood results in moisture contents of up to 10% despite being dried at the time of milling. To compensate for these variations, the wood content was adjusted in the final composition for moisture content to result in consistent levels of dried wood for all samples. Moisture was removed from the wood by use of a vacuum vent on the extruder shortly after the introduction of the wood to the polymer component. Using this system the water was removed for uniformly dry pellets at the time of processing. The wood flour had the following particle size distribution:
      >850 µm: 0 - 1%
      425 - 850 µm: 15 - 35%
      250 - 425 µm: 30 - 60%
      180 - 250 µm: 10 - 25%
      150 - 180 µm: 0 - 15%
      Balance Pan, <150 µm 0 - 23%


    [0075] In Table 3, densities of ethylene-based polymers and the maleated ethylene-based polymers were measured according to ASTM D792 - 13, I2 values were measured according to ASTM D1238 - 13 at 190°C and 2.16 Kg, and melting temperatures were measured by DSC according to ASTM D3418 - 15. The ethylene-based polymers and maleated ethylene-based polymers were commercially available from The Dow Chemical Company of Midland, Michigan, USA. Viscosities of bis-vinyl-terminated polydimethylsiloxanes were measured at 25°C at 0.1 to 50 RPM on a Brookfield DV-III cone & plate viscometer with #CP-52 spindle. The bis-vinyl-terminated polydimethylsiloxanes were commercially available from Dow Silicones Corporation of Midland, Michigan, USA.

    Reference Example 1 - Procedure for Preparing WPC Samples



    [0076] For all WPC samples, (a) the lignocellulosic-based filler was added independent of (b) the ethylene-based polymer, and (c) the polydiorganosiloxane through a secondary feed system located at a downstream position on the extruder barrel. By mixing of the solids into the blend of fully melted ethylene-based polymer and polydiorganosiloxane, higher filler content samples could be produced than would have been possible with all materials being fed at the same location.

    [0077] Injection molding was utilized for producing test specimens. Tensile bars were produced and tested in accordance with ASTM D638-14. Each composition was processed with the same conditions for both compounding in the twin screw extruder and injection molding equipment for consistency. For each example, total feed rates, RPM, temperatures, and equipment configurations remained constant for each composition for both the compounding extruders and injection molding equipment.

    [0078] The parameters associated with extrusion, as well as the average break strength of the wood plastic composite article formed by each example, the strand quality, and color of the final injection molded tensile bars is set forth in the tables below.

    [0079] Melt temperature was obtained with a thermocouple hand probe. As this measurement required a level of technique due to the manual method, it was subject to a high level of variation. Experience showed that results could differ by up to 10°C depending on operator and technique. In the case of these tests, care was taken to use the same operator and technique.

    [0080] Extruder torque was noted as a relative percent of the extruder maximum torque.

    [0081] Break strength was measured by producing five samples which were averaged. Testing was performed in accordance with ASTM D638-14.

    [0082] Color (Y) was also measured to quantify the level of thermal decomposition occurring in the wood filler. The Y-value or the luminance was measure as a gauge of the darkening of the wood plastic composite during processing. Higher values of Y correspond to a lighter brown color of the wood. The Y value was measured using an average of 2 measurements on 5 separate injection molded tensile dog bone samples (average of 10 measurements) using a BYK spectro-guide 45/0 gloss meter with D65 illuminant and 10° observer.

    [0083] Comparative Example Compositions are shown in Table 4. Amounts of each starting material are in weight %.
    Table 4.
    Comparative Example(b) Ethylene-Based Polymer(c) Bis-vinyl-terminated Polydimethylsiloxane (PDMS)Amount of Bis-Vi-Terminated PDMS(d) MAPE Amount(a) Lignocellulosic-based Filler Amount
    1 LLDPE 1 None 0 0 55
    2 LLDPE 1 None 0 2 55
    3 LLDPE 1 None 0 0 55
    4 LLDPE 1 None 0 2 55
    5 HDPE 2 Si-2,000 6 4 70


    [0084] Table 5 shows performance of the samples prepared as shown in Table 4.
    Table 5
    Comparative ExampleExtruder Torque (%)Melt Temperature (°C)Avg. Break Strength (MPa)Color (Y)Observation
    1 84 249 7.6 6.9  
    2 84 251 27.1 4.3  
    3 84 245 8.9 6.4  
    4 84 256 27.9 4.9  
    5 45 Could not measure ND ND Had to stop run due to Silicone backup in feed throat
    ND = Not Determined


    [0085] Working Example Compositions are shown in Table 6. Amounts of each starting material are in weight %.
    Table 6
    Working Example(b) Ethylene-Based Polymer(c) Bis-Vi-Terminated PDMS(c) Bis-Vi-Terminated PDMS Amount(d) MAPE Amount(a) Lignocellulosic-based Filler Amount
    1 LLDPE 1 Si-10,000 1 0 55
    2 LLDPE 1 Si-10,000 1.5 0 55
    3 LLDPE 1 Si-10,000 2 0 55
    4 LLDPE 1 Si-10,000 1 2 55
    5 LLDPE 1 Si-10,000 1.5 2 55
    6 LLDPE 1 Si-10,000 2 2 55
    7 LLDPE 1 Si-2,000 1 0 55
    8 LLDPE 1 Si-2,000 1.5 0 55
    9 LLDPE 1 Si-2,000 2 0 55
    10 LLDPE 1 Si-2,000 1 2 55
    11 LLDPE 1 Si-2,000 1.5 2 55
    12 LLDPE 1 Si-2,000 2 2 55
    13 LLDPE 1 Si-60,000 1 0 55
    14 LLDPE 1 Si-60,000 1.5 0 55
    15 LLDPE 1 Si-60,000 2 0 55
    16 LLDPE 1 Si-60,000 1 2 55
    17 LLDPE 1 Si-60,000 1.5 2 55
    18 LLDPE 1 Si-60,000 2 2 55
    19 LLDPE 1 Si-5,000 1 0 55
    20 LLDPE 1 Si-5,000 1.5 0 55
    21 LLDPE 1 Si-5,000 2 0 55
    22 LLDPE 1 Si-5,000 1 2 55
    23 LLDPE 1 Si-5,000 1.5 2 55
    24 LLDPE 1 Si-5,000 2 2 55
    25 HPDE 2 Si-60,000 4 1 55
    26 HDPE 2 Si-2,000 4 1 55
    27 HDPE 1 Si-2,000 0.5 1 40
    28 HDPE 1 Si-2,000 6 4 70
    29 HPDE 2 Si-60,000 4 1 40


    [0086] Starting Material (b) Ethylene-Based Polymer was the balance of each sample shown in Table 6. Table 7 shows performance of the samples prepared as shown in Table 6.
    Table 7
    Working ExampleExtruder Torque (%)Melt Temperature (°C)Avg. Break Strength (MPa)Color (Y)
    1 65 237 6.7 12.6
    2 60 230 6.3 14.2
    3 56 222 6.2 14.9
    4 68 245 25.3 7.9
    5 61 236 23.7 10.5
    6 56 227 22.8 12.7
    7 65 240 7.0 12.1
    8 58 223 6.7 15.6
    9 53 222 6.5 15.8
    10 61 225 25.3 9.5
    11 52 222 24.6 11.8
    12 48 215 24.0 13.1
    13 67 241 6.9 11.7
    14 63 239 7.1 13.0
    15 61 236 6.6 13.5
    16 69 242 25.0 8.3
    17 65 236 24.9 8.2
    18 59 233 24.3 10.6
    19 64 243 7.2 15.1
    20 60 231 6.4 15.5
    21 55 227 6.4 16.3
    22 62 235 25.2 9.6
    23 55 226 23.9 11.1
    24 50 220 23.0 11.8
    25 50 208 26.1 ND
    26 45 206 30.4 ND
    27 73 229 36.2 ND
    28 46 192 24.4 ND
    29 50 216 33.7 ND
    ND=Not Determined


    [0087] In this Reference Example A, solid carrier components in pellet form were produced using a 26 mm twin screw extruder. Starting material (b) the ethylene-based polymer (PE), and optionally starting material (d) the maleated ethylene-based polymer (MAPE), were fed in via the feed throat in the first barrel section. Starting material (c) the polydiorganosiloxane (Vi-terminated PDMS) was injected into the fourth of eleven barrel sections onto a screw section with mixing. The resulting compositions were pelletized using a Gala underwater pelletizer for consistency and collected for testing. The resulting samples, 31 to 40, were cooled to room temperature and aged a minimum of 48 hours before any testing.

    [0088] In this Reference Example B, Solid carrier components in pellet form were produced using a 25 mm twin screw extruder. Starting material (b) the ethylene-based polymer (PE), and optionally starting material (d) the maleated ethylene-based polymer (MAPE), were fed in via the feed throat in the first barrel section. Starting material (c) the polydiorganosiloxane (Vi-terminated PDMS) was injected into the fourth of twelve barrel sections onto a screw section with mixing. When used, (e) the filler CaCO3 (Calcium carbonate which was untreated and had an average particle size of 3 µm) was also fed in via the feed throat in the first barrel section. The resulting composition was cooled via full immersion water bath and pelletized using a strand pelletizer. The resulting samples, 41 to 46, were cooled to room temperature and aged a minimum of 48 hours before any testing.

    [0089] In this Reference Example C, bleed of the polydiorganosiloxane from the pellets prepared according to Reference Example A and Reference Example B was evaluated, as follows. Each sample (4 g) was placed into pre-weighed aluminum pans lined with Whatman # 1 filter paper (5.5 cm diameter) such that the surface of the aluminum pan was covered fully by the filter paper, but the filter paper was not bent. The pellets were evenly spread out across the filter paper in a semi-uniform layer. The samples were left standing at room temperature on the bench or at the said temperature in a convection oven for the specified amount of time. After aging, the pellets were left to stand at room temperature for at least 4 hours, and the pellets were placed in a 20 mL scintillation vial. The filter paper was weighed to determine aged filter paper weight. Bleed was determined according to the formula below:



    [0090] Compositions (Table 8) , aging conditions and polydiorganosiloxane bleed (Table 9) for the pellets are reported below.
    Table 8 - Solid Carrier Components
    (Pellets) Sample(a) PE(a) PE Amt (%)(d) MAPE (%)(c) Vi-terminated PDMSVi-terminated PDMS Amount (%)(e) CaCO3 Amount (%)
    31 HDPE 2 80 0 Si-10,000 20 0
    32 HDPE 1 60 20 Si-10,000 20 0
    33 HDPE 1 65 20 Si-2,000 15 0
    34 HDPE 1 65 20 Si-2,000 15 0
    35 HDPE 1 62 20 Si-2,000 18 0
    36 HDPE 1 62 20 Si-2,000 18 0
    37 HDPE 1 60 20 Si-2,000 20 0
    38 HDPE 1 60 20 Si-2,000 20 0
    39 HDPE 1 58 20 Si-2,000 22 0
    40 HDPE 1 58 20 Si-2,000 22 0
    41 none 0 95 Si-10,000 5 0
    42 LLDPE 2 80 0 Si-2,000 20 0
    43 HDPE 1 85 0 Si-2,000 15 0
    44 LLDPE 1 68 10 Si-10,000 22 0
    45 LLDPE 2 50 30 Si-2,000 20 0
    Comp 46 LLDPE 2 40 30 Si-2,000 20 10
    Table 9 - Solid Carrier Components bleed and pellet properties (Pellets)
    SampleAging T (ºC)Aging time (weeks)Siloxane bleed (%)Could be pelletized?Observations
    31 NA NA NA No  
    32 70 2 21.5 Yes  
    33 70 2 0.8 Yes  
    34 RT 2 0.2 Yes  
    35 70 2 1.2 Yes  
    36 RT 2 0.4 Yes  
    37 70 2 7.3 Yes  
    38 RT 2 3.6 Yes  
    39 70 2 14.5 Yes  
    40 RT 2 0.8 Yes  
    41 70 2 0 Yes good strands, minimal evidence of silicone sheen in pellet water
    42 70 2 0 Yes good strands, no die drool
    43 70 2 0 Yes even flow, potentially inconsistent mixing, moderate to severe die drool
    44 70 2 0 Yes even strands, pellets have long connected tails, moderate die drool
    45 70 2 2.0 Yes lumpy strands, sheen in water (Si), pellets feel slippery, have long tails
    Comp 46 70 2 18.4 No surging at die, large amount of silicone at die, strand looks bad


    [0091] The data in Tables 8 and 9 showed that a solid carrier component could be prepared with the alkenyl-functional polydiorganosiloxane described herein and HDPE 1. However, pelletization with HDPE 2 and no MAPE was not possible under the conditions tested in this example; in that case bleed could not be measured as denoted by NA or "not applicable." Furthermore, solid carrier components with low bleed (i.e., bleed of < 5% of the alkenyl-functional polydiorganosiloxane) could be produced using HDPE and maleated ethylene-based polymer (MAPE), when an alkenyl-functional polydiorganosiloxane in an amount < 20%, alternatively in an amount of 15% to < 20% was used.

    PROBLEM TO BE SOLVED



    [0092] WPC articles are commonly produced by high shear methods such as extrusion or injection molding. Lignocellulosic-based fillers are used to alter mechanical properties, decrease cost (because these are typically less expensive than the ethylene-based polymers), decrease density, and/or meet end use requirements for various applications. Adding fillers can make the starting materials difficult to process because the filler generally increases the viscosity of the melted ethylene-based polymer. When the starting materials are processed with a high shear method, these fillers can require more work to process resulting in higher temperatures and limited extrusion rates. This increase in temperature and stress can result in thermal or mechanical decomposition of the lignocellulosic-based filler. Similarly, some ethylene-based polymers can suffer from decomposition under the mechanical or thermal stress from processing. This decomposition translates in poor mechanical properties, discoloration, poor aesthetics, and/or other undesirable defects in the WPC article produced. Similarly, such processing difficulties translate in the need for a higher energy input for processing, increased torque, and reduced processing speed. Combined these effects can result in lower output for compounders and/or poor product quality.

    INDUSTRIAL APPLICABILITY



    [0093] By adding a polydiorganosiloxane during processing, torque can be substantially reduced. Reducing torque also reduces energy requirements and reduces the melt temperature of the composition. Extrusion of compositions that contained polydiorganosiloxane in working examples 1 through 24 resulted in 48% to 69% torque as compared to comparative examples 1 through 4 that contained no process aid with 84 % torque. Additionally, working examples 1 through 3 and 5 through 24 show reduced melt temperature (< 245 °C) as compared to comparative examples 1 through 4. This temperature reduction can enable higher throughputs, improved material properties, higher filler loadings, improve properties of the WPC article, and/or decrease costs associated with producing the WPC article when the polydiorganosiloxane is used. This reduction in torque, pressure, work, and temperature can also minimize or eliminate process related decomposition of the ethylene-based polymer and/or filler. It has been surprisingly found that this melt temperature reduction (on the order of 5°C to 30°C, alternatively 10°C to 20°C) can be obtained by using a polydiorganosiloxane with alkenyl functional groups (e.g., bis-vinyl-terminated polydimethylsiloxane). Working examples 1 through 3, 5 through 12, 14, 15, 17, 18, and 20 through 24 all showed temperatures ≤ 240°C compared to 245°C to 256°C for comparative examples 1 through 4. The reduction in darkening of the WPC article was a measure of reduced decomposition of the ethylene-based polymer and/or filler. Comparative examples 1 through 4 all had lower values of luminescence (Y = 4.3 to 6.9) compared to values for 7.9 to 16.3 for working examples 1 through 24, demonstrating that the WPC articles prepared in the comparative examples were all darker than the WPC articles prepared by the working examples, and suggesting that that comparative examples showed more signs of degradation than the working examples.

    [0094] It has also been found that polydiorganosiloxanes with viscosity of 2,000 mPa·s to 60,000 mPa·s may provide one or more of the benefits described above to compositions for preparing WPC articles, as compared to a comparative control composition excluding the polydiorganosiloxane. Alternatively, the viscosity of the polydiorganosiloxane may be 2,000 mPa·s to 10,000 mPa·s or 2,000 mPa·s to 5,000 mPa·s.

    DEFINITIONS AND USAGE OF TERMS



    [0095] All amounts, ratios, and percentages herein are by weight, unless otherwise indicated. The terms "comprising" or "comprise" are used herein in their broadest sense to mean and encompass the notions of "including," "include," "consist(ing) essentially of," and "consist(ing) of. The use of "for example," "e.g.," "such as," and "including" to list illustrative examples does not limit to only the listed examples. Thus, "for example" or "such as" means "for example, but not limited to" or "such as, but not limited to" and encompasses other similar or equivalent examples. The abbreviations used herein have the definitions in Table 10.
    Table 10 - Abbreviations
    AbbreviationDefinition
    °C degrees Celsius
    cm centimeters
    DSC differential scanning calorimetrv
    FTIR Fourier Transform Infra Red
    g grams
    GPC gel permeation chromatography
    HDPE high-density polyethylene
    Kg kilograms
    LLDPE linear-low-densitv polyethylene
    MAPE maleated ethylene-based polymer
    MDPE medium-densitv polyethylene
    mg milligrams
    min minutes
    mL milliliters
    mm millimeters
    mPa·s milliPascal·seconds
    MWD molecular weight distribution
    N normal
    PDI polydispersity index
    PE ethylene-based polymer
    PTFE polytetrafluoroethylene
    RPM revolutions per minute
    µL microliters
    µm micrometers
    Vi-terminated PDMS bis-vinyl-terminated polydimethylsiloxane
    WPC wood plastic composite


    [0096] The invention has been described in an illustrative manner, and it is to be understood that the terminology which has been used is intended to be in the nature of words of description rather than of limitation. In addition, with respect to the language which defines or modifies a range, such as "at least," "greater than," "less than," "no more than," and the like, it is to be understood that such language includes subranges and/or an upper or lower limit.


    Claims

    1. A composition for preparing a wood plastic composite article, said composition comprising:

    15 weight % to 70 weight % of (a) a lignocellulosic-based filler;

    29.5 weight % to 84.5 weight % of (b) an ethylene-based polymer;

    0.5 weight % to 6 weight % of (c) a polydiorganosiloxane of unit formula:
    (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, where each R is an independently selected monovalent hydrocarbon group of 1 to 18 carbon atoms that is free of aliphatic unsaturation, each R' is an independently selected alkenyl group of 2 to 18 carbon atoms, subscript a is 0 to 2, subscript b is 0 to 2, a quantity (a + b) = 2, subscript c ≥ 0, subscript d ≥ 0, a quantity (a + d) ≥ 1, and a quantity (a + b + c + d) is sufficient to give the polydiorganosiloxane a viscosity of 2,000 mPa·s to 60,000 mPa·s at 25°C measured at 0.1 to 50 RPM on a Brookfield DV-III cone & plate viscometer with #CP-52 spindle; and

    0 to 4 weight % of (d) a maleated ethylene-based polymer;

    each based on combined weights of starting materials (a), (b), (c), and (d) in said composition.


     
    2. The composition of claim 1, where starting material (a) the lignocellulosic-based filler comprises a lignocellulosic material derived from wood, plants, agricultural by-products, chaff, sisal, bagasse, wheat straw, kapok, ramie, henequen, corn fiber or coir, nut shells, flax, jute, hemp, kenaf, rice hulls, abaca, peanut hull, bamboo, straw, lignin, starch, or cellulose and cellulose-containing products, and combinations thereof, and starting material (a) is present in an amount of 45 weight % to 65 weight %.
     
    3. The composition of claim 1, where starting material (b) the ethylene-based polymer is selected from the group consisting of High Density Polyethylene (HDPE), Medium Density Polyethylene (MDPE), Low Density Polyethylene (LDPE), Linear Low Density Polyethylene (LLDPE), Low Density Low Molecular Weight Polyethylene (LDLMWPE), and a combination thereof, and starting material (b) is present in an amount of 30 weight % to 65 weight %.
     
    4. The composition of claim 3, where the ethylene-based polymer comprises LLDPE.
     
    5. The composition of claim 3 or 4, where the ethylene-based polymer comprises ≥ 50% recycled polyethylene.
     
    6. The composition of claim 1, where the polydiorganosiloxane is a bis-alkenyl-terminated polydiorganosiloxane of formula

    where each R is an independently selected monovalent hydrocarbon group of 1 to 18 carbon atoms that is free of aliphatic unsaturation, each R' is an independently selected alkenyl group of 2 to 18 carbon atoms, and subscript x has a value sufficient to give the polydiorganosiloxane a viscosity of 2,000 mPa·s to 60,000 mPa·s measured at 25°C at 0.1 to 50 RPM on a Brookfield DV-III cone & plate viscometer with #CP-52 spindle
     
    7. The composition of claim 6, where each R is an alkyl group of 1 to 12 carbon atoms, each R' is an alkenyl group of 2 to 12 carbon atoms, and subscript x has a value sufficient to give the polydiorganosiloxane a viscosity of 2,000 mPa·s to 10,000 mPa·s, and the polydiorganosiloxane is present in an amount of 1.5 weight % to 2 weight %.
     
    8. The composition of claim 7, where in each R is a methyl group, each R' is a vinyl group, subscript x has a value sufficient to give the polydiorganosiloxane a viscosity of 2,000 mPa·s to 5,000 mPa·s.
     
    9. The composition of claim 1, where the maleated ethylene-based polymer is present and the maleated ethylene-based polymer has a melt index of 0.1 g/10 min to 25 g/10 min measured according to ASTM D1238 - 13 at 190°C and 2.16 Kg and a maleic anhydride content of 0.25 weight % to 2.5 weight %.
     
    10. The composition of claim 1, further comprising an additional starting material selected from the group consisting of (e) an additional filler which is distinct from the lignocellulosic-based filler of starting material (a), (f) a colorant, (g) a blowing agent, (h) a UV stabilizer, (i) an antioxidant, (j) a process aid, (k) a preservative, (I) a biocide, (m) a flame retardant, (n) an impact modifier, and (o) a combination of two or more thereof.
     
    11. A method for preparing a wood plastic composite article, said method comprising:

    (1) combining starting materials comprising

    15 weight % to 70 weight % of (a) a lignocellulosic-based filler;

    29.5 weight % to 84.5 weight % of (b) an ethylene-based polymer;

    0.5 weight % to 6 weight % of (c) a polydiorganosiloxane comprising unit formula:
    (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, where each R is an independently selected monovalent hydrocarbon group of 1 to 18 carbon atoms that is free of aliphatic unsaturation, each R' is an independently selected alkenyl group of 2 to 18 carbon atoms, subscript a is 0 to 2, subscript b is 0 to 2, a quantity (a + b) = 2, subscript c ≥ 0, subscript d ≥ 0, a quantity (a + d) ≥ 1, and a quantity (a + b + c + d) is sufficient to give the polydiorganosiloxane a viscosity of 2,000 mPa·s to 60,000 mPa·s at 25°C measured at 0.1 to 50 RPM on a Brookfield DV-III cone & plate viscometer with #CP-52 spindle;

    each based on combined weights of starting materials (a), (b), (c), and (d); thereby preparing a composition; and

    (2) preparing the wood plastic composite article from the composition.


     
    12. The method of claim 11, where the method further comprises (i) mixing (a) the lignocellulosic based filler and (b) the polymer before adding (c) the polydiorganosiloxane; (ii) heating (b) the polymer to melt (b) the polymer prior to and/or during forming the composition; (iii) mixing a mixture of (a) the lignocellulosic-based filler and (c) the polydiorganosiloxane before adding (b) the polymer or (iv) any combination of (ii) and (i) or (iii).
     
    13. The method of claim 11, where: (i) (c) the polydiorganosiloxane is a liquid when combining (c) the polydiorganosiloxane with another starting material of the composition; or (ii) (c) the polydiorganosiloxane is present within a solid carrier component, and the method further comprises melting the solid carrier component when combining (c) the polydiorganosiloxane with another starting material of the composition.
     
    14. The method of claim any one of claims 11 to 13, wherein: (i) preparing the wood plastic composite article from the composition further comprises forming the composition into a desired shape; (ii) preparing the wood plastic composite article from the composition comprises extruding the composition; (iii) preparing the wood plastic composite article from the composition comprises molding the composition; or (iv) any combinations of (i) to (iii).
     
    15. A solid carrier component comprising:

    5 weight % to 20 weight % of (i) a polydiorganosiloxane comprising unit formula (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, where each R is an independently selected monovalent hydrocarbon group of 1 to 18 carbon atoms that is free of aliphatic unsaturation, each R' is an independently selected alkenyl group of 2 to 18 carbon atoms, subscript a is 0 to 2, subscript b is 0 to 2, a quantity (a + b) = 2, subscript c ≥ 0, subscript d ≥ 0, a quantity (a + d) ≥ 1, and a quantity (a + b + c + d) is sufficient to give the polydiorganosiloxane a viscosity of 2,000 mPa·s to 60,000 mPa·s at 25°C measured at 0.1 to 50 RPM on a Brookfield DV-III cone & plate viscometer with #CP-52 spindle;

    > 70 weight % to 95 weight % of (ii) a polymer component selected from the group consisting of an ethylene-based polymer, a maleated ethylene-based polymer, and a combination of both the ethylene-based polymer and the maleated ethylene-based polymer; and

    0 to 10 % of a filler.


     
    16. A solid carrier component according to claim 15 comprising:

    5 weight % to < 20 weight % of (i) a polydiorganosiloxane comprising unit formula (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, where each R is an independently selected monovalent hydrocarbon group of 1 to 18 carbon atoms that is free of aliphatic unsaturation, each R' is an independently selected alkenyl group of 2 to 18 carbon atoms, subscript a is 0 to 2, subscript b is 0 to 2, a quantity (a + b) = 2, subscript c ≥ 0, subscript d ≥ 0, a quantity (a + d) ≥ 1, and a quantity (a + b + c + d) is sufficient to give the polydiorganosiloxane a viscosity of 2,000 mPa·s to 60,000 mPa·s at 25°C measured at 0.1 to 50 RPM on a Brookfield DV-III cone & plate viscometer with #CP-52 spindle;

    > 70 weight % to 95 weight % of (ii) a polymer component selected from the group consisting of an ethylene-based polymer, a maleated ethylene-based polymer, and a combination of both the ethylene-based polymer and the maleated ethylene-based polymer; and

    0 to 10 % of a filler.


     


    Ansprüche

    1. Eine Zusammensetzung zum Herstellen eines Holz-Kunststoff-Verbundstoffartikels, wobei die Zusammensetzung Folgendes beinhaltet:

    zu 15 Gew.-% bis 70 Gew.-% (a) einen Füllstoff auf Lignozellulosebasis;

    zu 29,5 Gew.-% bis 84,5 Gew.-% (b) ein Polymer auf Ethylenbasis;

    zu 0,5 Gew.-% bis 6 Gew.-% (c) ein Polydiorganosiloxan der folgenden Einheitsformel:

    (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, wobei jedes R eine unabhängig ausgewählte monovalente Kohlenwasserstoffgruppe mit 1 bis 18 Kohlenstoffatomen ist, die frei von aliphatischer Ungesättigtheit ist, jedes R' eine unabhängig ausgewählte Alkenylgruppe mit 2 bis 18 Kohlenstoffatomen ist, das tiefgestellte a 0 bis 2 ist, das tiefgestellte b 0 bis 2 ist, eine Größe (a + b) = 2, das tiefgestellte c ≥ 0, das tiefgestellte d ≥ 0, eine Größe (a + d) ≥ 1 und eine Größe (a + b + c + d) ausreichend ist, um dem Polydiorganosiloxan eine Viskosität bei 25 °C von 2 000 mPa·s bis 60 000 mPa·s zu verleihen, gemessen bei 0,1 bis 50 U/min auf einem Kegel-Platte-Viskosimeter Brookfield DV-III mit einer #CP-52-Spindel; und

    zu 0 bis 4 Gew.-% (d) ein maleiertes Polymer auf Ethylenbasis;

    jeweils bezogen auf die kombinierten Gewichte der Ausgangsmaterialien (a), (b), (c) und (d) in der Zusammensetzung.


     
    2. Zusammensetzung gemäß Anspruch 1, wobei das Ausgangsmaterial (a), der Füllstoff auf Lignozellulosebasis, ein Lignozellulosematerial beinhaltet, das aus Folgendem abgeleitet ist: Holz, Pflanzen, landwirtschaftlichen Nebenprodukten, Spreu, Sisal, Bagasse, Weizenstroh, Kapok, Ramie, Henequen, Maisfaser oder Kokosfaser, Nussschalen, Flachs, Jute, Hanf, Kenaf, Reisspelzen, Abaca, Erdnusshülsen, Bambus, Stroh, Lignin, Stärke oder Zellulose und zellulosehaltigen Produkten und Kombinationen davon, und wobei das Ausgangsmaterial (a) in einer Menge von 45 Gew.-% bis 65 Gew.-% vorhanden ist.
     
    3. Zusammensetzung gemäß Anspruch 1, wobei das Ausgangsmaterial (b), das Polymer auf Ethylenbasis, aus der Gruppe ausgewählt ist, die aus Folgendem besteht: Polyethylen hoher Dichte (HDPE), Polyethylen mittlerer Dichte (MDPE), Polyethylen niedriger Dichte (LDPE), linearem Polyethylen niedriger Dichte (LLDPE), Polyethylen niedriger Dichte und niedrigen Molekulargewichts (LDLMWPE) und einer Kombination davon, und wobei das Ausgangsmaterial (b) in einer Menge von 30 Gew.-% bis 65 Gew.-% vorhanden ist.
     
    4. Zusammensetzung gemäß Anspruch 3, wobei das Polymer auf Ethylenbasis LLDPE beinhaltet.
     
    5. Zusammensetzung gemäß Anspruch 3 oder 4, wobei das Polymer auf Ethylenbasis zu ≥ 50 % recyceltes Polyethylen beinhaltet.
     
    6. Zusammensetzung gemäß Anspruch 1, wobei das Polydiorganosiloxan ein Bis-alkenylterminiertes Polydiorganosiloxan der Formel

    ist, wobei jedes R eine unabhängig ausgewählte monovalente Kohlenwasserstoffgruppe mit 1 bis 18 Kohlenstoffatomen ist, die frei von aliphatischer Ungesättigtheit ist, jedes R' eine unabhängig ausgewählte Alkenylgruppe mit 2 bis 18 Kohlenstoffatomen ist und das tiefgestellte x einen Wert aufweist, der ausreichend ist, um dem Polydiorganosiloxan eine Viskosität von 2 000 mPa·s bis 60 000 mPa·s zu verleihen, gemessen bei 25 °C bei 0,1 bis 50 U/min auf einem Kegel-Platte-Viskosimeter Brookfield DV-III mit einer #CP-52-Spindel.
     
    7. Zusammensetzung gemäß Anspruch 6, wobei jedes R eine Alkylgruppe mit 1 bis 12 Kohlenstoffatomen ist, jedes R' eine Alkenylgruppe mit 2 bis 12 Kohlenstoffatomen ist und das tiefgestellte x einen Wert aufweist, der ausreichend ist, um dem Polydiorganosiloxan eine Viskosität von 2 000 mPa·s bis 10 000 mPa·s zu verleihen, und wobei das Polydiorganosiloxan in einer Menge von 1,5 Gew.-% bis 2 Gew.-% vorhanden ist.
     
    8. Zusammensetzung gemäß Anspruch 7, wobei jedes R eine Methylgruppe ist, jedes R' eine Vinylgruppe ist, das tiefgestellte x einen Wert aufweist, der ausreichend ist, um dem Polydiorganosiloxan eine Viskosität von 2 000 mPa·s bis 5 000 mPa·s zu verleihen.
     
    9. Zusammensetzung gemäß Anspruch 1, wobei das maleierte Polymer auf Ethylenbasis vorhanden ist und das maleierte Polymer auf Ethylenbasis einen Schmelzindex von 0,1 g/10 min bis 25 g/10 min, gemessen in Übereinstimmung mit ASTM D1238 - 13 bei 190 °C und 2,16 kg, und einen Maleinsäureanhydridgehalt von 0,25 Gew.-% bis 2,5 Gew.-% aufweist.
     
    10. Zusammensetzung gemäß Anspruch 1, ferner beinhaltend ein zusätzliches Ausgangsmaterial, das aus der Gruppe ausgewählt ist, die aus Folgendem besteht: (e) einem zusätzlichen Füllstoff, der sich von dem Füllstoff auf Lignozellulosebasis des Ausgangsmaterials (a) unterscheidet, (f) einem Farbmittel, (g) einem Treibmittel, (h) einem UV-Stabilisator, (i) einem Antioxidationsmittel, (j) einem Verarbeitungshilfsmittel, (k) einem Konservierungsmittel, (I) einem Biozid, (m) einem Flammschutzmittel, (n) einem Schlagzähigkeitsmodifizierer und (o) einer Kombination von zwei oder mehr davon.
     
    11. Ein Verfahren zum Herstellen eines Holz-Kunststoff-Verbundstoffartikels, wobei das Verfahren Folgendes beinhaltet:

    (1) Kombinieren von Ausgangsmaterialien, die Folgendes beinhalten:

    zu 15 Gew.-% bis 70 Gew.-% (a) einen Füllstoff auf Lignozellulosebasis;

    zu 29,5 Gew.-% bis 84,5 Gew.-% (b) ein Polymer auf Ethylenbasis;

    zu 0,5 Gew.-% bis 6 Gew.-% (c) ein Polydiorganosiloxan, das die folgende Einheitsformel beinhaltet: (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, wobei jedes R eine unabhängig ausgewählte monovalente Kohlenwasserstoffgruppe mit 1 bis 18 Kohlenstoffatomen ist, die frei von aliphatischer Ungesättigtheit ist, jedes R' eine unabhängig ausgewählte Alkenylgruppe mit 2 bis 18 Kohlenstoffatomen ist, das tiefgestellte a 0 bis 2 ist, das tiefgestellte b 0 bis 2 ist, eine Größe (a + b) = 2, das tiefgestellte c ≥ 0, das tiefgestellte d ≥ 0, eine Größe (a + d) ≥ 1 und eine Größe (a + b + c + d) ausreichend ist, um dem Polydiorganosiloxan eine Viskosität bei 25 °C von 2 000 mPa·s bis 60 000 mPa·s zu verleihen, gemessen bei 0,1 bis 50 U/min auf einem Kegel-Platte-Viskosimeter Brookfield DV-III mit einer #CP-52-Spindel;

    jeweils bezogen auf die kombinierten Gewichte der Ausgangsmaterialien (a), (b), (c) und (d); wodurch eine Zusammensetzung hergestellt wird; und

    (2) Herstellen des Holz-Kunststoff-Verbundstoffartikels aus der Zusammensetzung.


     
    12. Verfahren gemäß Anspruch 11, wobei das das Verfahren ferner Folgendes beinhaltet:

    (i) Mischen (a) des Füllstoffs auf Lignozellulosebasis und (b) des Polymers vor dem Hinzufügen (c) des Polydiorganosiloxans; (ii) Erwärmen (b) des Polymers zum Schmelzen (b) des Polymers vor und/oder während des Bildens der Zusammensetzung; (iii) Mischen einer Mischung von (a) dem Füllstoff auf Lignozellulosebasis und (c) dem Polydiorganosiloxan vor dem Hinzufügen (b) des Polymers oder (iv) eine beliebige Kombination von (ii) und (i) oder (iii).


     
    13. Verfahren gemäß Anspruch 11, wobei: (i) (c) das Polydiorganosiloxan eine Flüssigkeit ist, wenn (c) das Polydiorganosiloxan mit einem anderen Ausgangsmaterial der Zusammensetzung kombiniert wird; oder (ii) (c) das Polydiorganosiloxan innerhalb einer festen Trägerkomponente vorhanden ist und das Verfahren ferner das Schmelzen der festen Trägerkomponente beinhaltet, wenn (c) das Polydiorganosiloxan mit einem anderen Ausgangsmaterial der Zusammensetzung kombiniert wird.
     
    14. Verfahren gemäß Anspruch einem der Ansprüche 11 bis 13, wobei: (i) das Herstellen des Holz-Kunststoff-Verbundstoffartikels aus der Zusammensetzung ferner das Bilden der Zusammensetzung in einer gewünschten Form beinhaltet; (ii) das Herstellen des Holz-Kunststoff-Verbundstoffartikels aus der Zusammensetzung das Extrudieren der Zusammensetzung beinhaltet; (iii) das Herstellen des Holz-Kunststoff-Verbundstoffartikels aus der Zusammensetzung das Formen der Zusammensetzung beinhaltet; oder (iv) beliebige Kombinationen von (i) bis (iii).
     
    15. Eine feste Trägerkomponente, die Folgendes beinhaltet:

    zu 5 Gew.-% bis 20 Gew.-% (i) ein Polydiorganosiloxan, das die folgende Einheitsformel beinhaltet: (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, wobei jedes R eine unabhängig ausgewählte monovalente Kohlenwasserstoffgruppe mit 1 bis 18 Kohlenstoffatomen ist, die frei von aliphatischer Ungesättigtheit ist, jedes R' eine unabhängig ausgewählte Alkenylgruppe mit 2 bis 18 Kohlenstoffatomen ist, das tiefgestellte a 0 bis 2 ist, das tiefgestellte b 0 bis 2 ist, eine Größe (a + b) = 2, das tiefgestellte c ≥ 0, das tiefgestellte d ≥ 0, eine Größe (a + d) ≥ 1 und eine Größe (a + b + c + d) ausreichend ist, um dem Polydiorganosiloxan eine Viskosität bei 25 °C von 2 000 mPa·s bis 60 000 mPa·s zu verleihen, gemessen bei 0,1 bis 50 U/min auf einem Kegel-Platte-Viskosimeter Brookfield DV-III mit einer #CP-52-Spindel;

    zu > 70 Gew.-% bis 95 Gew.-% (ii) eine Polymerkomponente, die aus der Gruppe ausgewählt ist, die aus Folgendem besteht: einem Polymer auf Ethylenbasis, einem maleierten Polymer auf Ethylenbasis und einer Kombination von sowohl dem Polymer auf Ethylenbasis als auch dem maleierten Polymer auf Ethylenbasis; und

    zu 0 bis 10 % einen Füllstoff.


     
    16. Feste Trägerkomponente gemäß Anspruch 15, die Folgendes beinhaltet:

    zu 5 Gew.-% bis < 20 Gew.-% (i) ein Polydiorganosiloxan, das die folgende Einheitsformel beinhaltet: (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, wobei jedes R eine unabhängig ausgewählte monovalente Kohlenwasserstoffgruppe mit 1 bis 18 Kohlenstoffatomen ist, die frei von aliphatischer Ungesättigtheit ist, jedes R' eine unabhängig ausgewählte Alkenylgruppe mit 2 bis 18 Kohlenstoffatomen ist, das tiefgestellte a 0 bis 2 ist, das tiefgestellte b 0 bis 2 ist, eine Größe (a + b) = 2, das tiefgestellte c ≥ 0, das tiefgestellte d ≥ 0, eine Größe (a + d) ≥ 1 und eine Größe (a + b + c + d) ausreichend ist, um dem Polydiorganosiloxan eine Viskosität bei 25 °C von 2 000 mPa·s bis 60 000 mPa·s zu verleihen, gemessen bei 0,1 bis 50 U/min auf einem Kegel-Platte-Viskosimeter Brookfield DV-III mit einer #CP-52-Spindel;

    zu > 70 Gew.-% bis 95 Gew.-% (ii) eine Polymerkomponente, die aus der Gruppe ausgewählt ist, die aus Folgendem besteht: einem Polymer auf Ethylenbasis, einem maleierten Polymer auf Ethylenbasis und einer Kombination von sowohl dem Polymer auf Ethylenbasis als auch dem maleierten Polymer auf Ethylenbasis; und

    zu 0 bis 10 % einen Füllstoff.


     


    Revendications

    1. Une composition pour préparer un article composite bois-plastique, ladite composition comprenant :

    de 15 % en poids à 70 % en poids (a) d'une charge à base lignocellulosique ;

    de 29,5 % en poids à 84,5 % en poids (b) d'un polymère à base d'éthylène ;

    de 0,5 % en poids à 6 % en poids (c) d'un polydiorganosiloxane de la formule unitaire :

    (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, où chaque R est un groupe hydrocarboné monovalent sélectionné indépendamment de 1 à 18 atomes de carbone qui est exempt d'insaturation aliphatique, chaque R' est un groupe alcényle sélectionné indépendamment de 2 à 18 atomes de carbone, l'indice a va de 0 à 2, l'indice b va de 0 à 2, une quantité (a + b) = 2, l'indice c ≥ 0, l'indice d ≥ 0, une quantité (a + d) ≥ 1, et une quantité (a + b + c + d) est suffisante pour donner au polydiorganosiloxane une viscosité de 2 000 mPa·s à 60 000 mPa·s à 25 °C mesurée à une vitesse de 0,1 à 50 tr/min sur un viscosimètre cône-plan Brookfield DV-III avec une broche #CP-52 ; et de 0 à 4 % en poids (d) d'un polymère à base d'éthylène maléaté ;

    chacun étant rapporté à des poids combinés des matières premières (a), (b), (c), et (d) dans ladite composition.


     
    2. La composition de la revendication 1, où la matière première (a) la charge à base lignocellulosique comprend une matière lignocellulosique dérivée de bois, de plantes, de sous-produits de l'agriculture, de balle, de sisal, de bagasse, de paille de blé, de kapok, de ramie, d'henequen, de fibre de maïs ou de coco, de coques de noix, de lin, de jute, de chanvre, de kenaf, d'écorces de riz, d'abaca, de son d'arachide, de bambou, de paille, de lignine, d'amidon, ou de cellulose et de produits contenant de la cellulose, et de combinaisons de ceux-ci, et la matière première (a) est présente en une quantité de 45 % en poids à 65 % en poids.
     
    3. La composition de la revendication 1, où la matière première (b) le polymère à base d'éthylène est sélectionnée dans le groupe constitué de polyéthylène haute densité (HDPE), de polyéthylène moyenne densité (MDPE), de polyéthylène basse densité (LDPE), de polyéthylène basse densité linéaire (LLDPE), de polyéthylène basse densité de faible masse moléculaire (LDLMWPE), et d'une combinaison de ceux-ci, et la matière première (b) est présente en une quantité de 30 % en poids à 65 % en poids.
     
    4. La composition de la revendication 3, où le polymère à base d'éthylène comprend du LLDPE.
     
    5. La composition de la revendication 3 ou de la revendication 4, où le polymère à base d'éthylène comprend ≥ 50 % de polyéthylène recyclé.
     
    6. La composition de la revendication 1, où le polydiorganosiloxane est un polydiorganosiloxane à terminaison bis-alcényle de la formule

    où chaque R est un groupe hydrocarboné monovalent sélectionné indépendamment de 1 à 18 atomes de carbone qui est exempt d'insaturation aliphatique, chaque R' est un groupe alcényle sélectionné indépendamment de 2 à 18 atomes de carbone, et l'indice x a une valeur suffisante pour donner au polydiorganosiloxane une viscosité de 2 000 mPa·s à 60 000 mPa·s mesurée à 25 °C à une vitesse de 0,1 à 50 tr/min sur un viscosimètre cône-plan Brookfield DV-III avec une broche #CP-52.
     
    7. La composition de la revendication 6, où chaque R est un groupe alkyle de 1 à 12 atomes de carbone, chaque R' est un groupe alcényle de 2 à 12 atomes de carbone, et l'indice x a une valeur suffisante pour donner au polydiorganosiloxane une viscosité de 2 000 mPa·s à 10 000 mPa·s, et le polydiorganosiloxane est présent en une quantité de 1,5 % en poids à 2 % en poids.
     
    8. La composition de la revendication 7, où chaque R est un groupe méthyle, chaque R' est un groupe vinyle, l'indice x a une valeur suffisante pour donner au polydiorganosiloxane une viscosité de 2 000 mPa·s à 5 000 mPa·s.
     
    9. La composition de la revendication 1, où le polymère à base d'éthylène maléaté est présent et le polymère à base d'éthylène maléaté a un indice de fluidité à l'état fondu de 0,1 g/10 min à 25 g/10 min mesuré selon l'ASTM D1238 - 13 à 190 °C et 2,16 kg et une teneur en anhydride maléique de 0,25 % en poids à 2,5 % en poids.
     
    10. La composition de la revendication 1, comprenant en outre une matière première supplémentaire sélectionnée dans le groupe constitué (e) d'une charge supplémentaire, laquelle est distincte de la charge à base lignocellulosique de la matière première (a), (f) d'un colorant, (g) d'un agent gonflant, (h) d'un stabilisant UV, (i) d'un antioxydant, (j) d'un adjuvant de traitement, (k) d'un conservateur, (I) d'un biocide, (m) d'un retardateur de flamme, (n) d'un agent antichoc, et (o) d'une combinaison de deux de ceux-ci ou plus.
     
    11. Un procédé pour préparer un article composite bois-plastique, ledit procédé comprenant :

    (1) la combinaison de matières premières comprenant

    de 15 % en poids à 70 % en poids (a) d'une charge à base lignocellulosique ;

    de 29,5 % en poids à 84,5 % en poids (b) d'un polymère à base d'éthylène ;

    de 0,5 % en poids à 6 % en poids (c) d'un polydiorganosiloxane comprenant la formule unitaire : (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, où chaque R est un groupe hydrocarboné monovalent sélectionné indépendamment de 1 à 18 atomes de carbone qui est exempt d'insaturation aliphatique, chaque R' est un groupe alcényle sélectionné indépendamment de 2 à 18 atomes de carbone, l'indice a va de 0 à 2, l'indice b va de 0 à 2, une quantité (a + b) = 2, l'indice c ≥ 0, l'indice d ≥ 0, une quantité (a + d) ≥ 1, et une quantité (a + b + c + d) est suffisante pour donner au polydiorganosiloxane une viscosité de 2 000 mPa·s à 60 000 mPa·s à 25 °C mesurée à une vitesse de 0,1 à 50 tr/min sur un viscosimètre cône-plan Brookfield DV-III avec une broche #CP-52 ;

    chacun rapporté à des poids combinés des matières premières (a), (b), (c), et (d) ; préparant de ce fait une composition ; et

    (2) la préparation de l'article composite bois-plastique à partir de la composition.


     
    12. Le procédé de la revendication 11, où le procédé comprend en outre (i) le fait de mélanger (a) la charge à base lignocellulosique et (b) le polymère avant l'ajout (c) du polydiorganosiloxane ; (ii) le chauffage (b) du polymère afin de faire fondre (b) le polymère avant et/ou durant le façonnage de la composition ; (iii) le fait de mélanger un mélange (a) de la charge à base lignocellulosique et (c) du polydiorganosiloxane avant l'ajout (b) du polymère ou (iv) toute combinaison de (ii) et de (i) ou (iii).
     
    13. Le procédé de la revendication 11, où : (i) (c) le polydiorganosiloxane est un liquide lors de la combinaison (c) du polydiorganosiloxane avec une autre matière première de la composition ; ou (ii) (c) le polydiorganosiloxane est présent à l'intérieur d'un constituant véhicule solide, et le procédé comprend en outre la fusion du constituant véhicule solide lors de la combinaison (c) du polydiorganosiloxane avec une autre matière première de la composition.
     
    14. Le procédé de la revendication l'une quelconque des revendications 11 à 13, où : (i) la préparation de l'article composite bois-plastique à partir de la composition comprend en outre le façonnage de la composition en une forme souhaitée ; (ii) la préparation de l'article composite bois-plastique à partir de la composition comprend l'extrusion de la composition ; (iii) la préparation de l'article composite bois-plastique à partir de la composition comprend le moulage de la composition ; ou (iv) toutes combinaisons de (i) à (iii).
     
    15. Un constituant véhicule solide comprenant :

    de 5 % en poids à 20 % en poids (i) d'un polydiorganosiloxane comprenant la formule unitaire (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, où chaque R est un groupe hydrocarboné monovalent sélectionné indépendamment de 1 à 18 atomes de carbone qui est exempt d'insaturation aliphatique, chaque R' est un groupe alcényle sélectionné indépendamment de 2 à 18 atomes de carbone, l'indice a va de 0 à 2, l'indice b va de 0 à 2, une quantité (a + b) = 2, l'indice c ≥ 0, l'indice d ≥ 0, une quantité (a + d) ≥ 1, et une quantité (a + b + c + d) est suffisante pour donner au polydiorganosiloxane une viscosité de 2 000 mPa·s à 60 000 mPa·s à 25 °C mesurée à une vitesse de 0,1 à 50 tr/min sur un viscosimètre cône-plan Brookfield DV-III avec une broche #CP-52 ;

    de > 70 % en poids à 95 % en poids (ii) d'un constituant polymère sélectionné dans le groupe constitué d'un polymère à base d'éthylène, d'un polymère à base d'éthylène maléaté, et d'une combinaison à la fois du polymère à base d'éthylène et du polymère à base d'éthylène maléaté ; et

    de 0 à 10 % d'une charge.


     
    16. Un constituant véhicule solide selon la revendication 15 comprenant :

    de 5 % en poids à < 20 % en poids (i) d'un polydiorganosiloxane comprenant la formule unitaire (R2R'SiO1/2)a(R3SiO1/2)b(R2SiO2/2)c(RR'SiO2/2)d, où chaque R est un groupe hydrocarboné monovalent sélectionné indépendamment de 1 à 18 atomes de carbone qui est exempt d'insaturation aliphatique, chaque R' est un groupe alcényle sélectionné indépendamment de 2 à 18 atomes de carbone, l'indice a va de 0 à 2, l'indice b va de 0 à 2, une quantité (a + b) = 2, l'indice c ≥ 0, l'indice d ≥ 0, une quantité (a + d) ≥ 1, et une quantité (a + b + c + d) est suffisante pour donner au polydiorganosiloxane une viscosité de 2 000 mPa·s à 60 000 mPa·s à 25 °C mesurée à une vitesse de 0,1 à 50 tr/min sur un viscosimètre cône-plan Brookfield DV-III avec une broche #CP-52 ;

    de > 70 % en poids à 95 % en poids (ii) d'un constituant polymère sélectionné dans le groupe constitué d'un polymère à base d'éthylène, d'un polymère à base d'éthylène maléaté, et d'une combinaison à la fois du polymère à base d'éthylène et du polymère à base d'éthylène maléaté ; et

    de 0 à 10 % d'une charge.


     






    Cited references

    REFERENCES CITED IN THE DESCRIPTION



    This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

    Patent documents cited in the description




    Non-patent literature cited in the description