(19)
(11)EP 3 838 937 B1

(12)EUROPEAN PATENT SPECIFICATION

(45)Mention of the grant of the patent:
14.09.2022 Bulletin 2022/37

(21)Application number: 20834568.6

(22)Date of filing:  29.06.2020
(51)International Patent Classification (IPC): 
C08F 283/12(2006.01)
C08F 220/18(2006.01)
C08F 2/44(2006.01)
G11B 7/24044(2013.01)
G11B 7/0065(2006.01)
C08F 2/48(2006.01)
C08G 77/442(2006.01)
G07F 7/00(2006.01)
(52)Cooperative Patent Classification (CPC):
C08F 2/44; C08F 283/12; C08G 77/442; G03F 7/001; G03F 7/0757; G03F 7/0046; G03F 7/029; G03F 7/032; G03F 7/033; C08F 283/126; C08F 2/50; C08F 220/1804; G03H 2001/026; G03H 2260/12; G11B 7/245; G11B 7/24044
 
C-Sets:
  1. C08F 283/12, C08F 222/102;
  2. C08F 283/126, C08F 222/102;
  3. C08F 220/1804, C08F 220/14, C08F 220/20;

(86)International application number:
PCT/KR2020/008465
(87)International publication number:
WO 2021/002648 (07.01.2021 Gazette  2021/01)

(54)

PHOTOPOLYMER COMPOSITION

FOTOPOLYMERZUSAMMENSETZUNG

COMPOSITION PHOTOPOLYMÈRE


(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR

(30)Priority: 02.07.2019 KR 20190079367

(43)Date of publication of application:
23.06.2021 Bulletin 2021/25

(73)Proprietor: LG Chem, Ltd.
Seoul 07336, (KR)

(72)Inventors:
  • JANG, Seokhoon
    Daejeon 34122 (KR)
  • KIM, Heon
    Daejeon 34122 (KR)
  • KWON, Se Hyun
    Daejeon 34122 (KR)
  • CHANG, Yeongrae
    Daejeon 34122 (KR)

(74)Representative: Hoffmann Eitle 
Patent- und Rechtsanwälte PartmbB Arabellastraße 30
81925 München
81925 München (DE)


(56)References cited: : 
KR-A- 20050 027 566
KR-A- 20100 055 383
US-A1- 2017 121 469
KR-A- 20090 000 477
KR-A- 20190 069 316
US-B2- 8 722 755
  
  • Swati Sundararajan, Samui Asit B., Kulkarni Prashant S: "Crosslinked polymer networks of poly(ethylene glycol) (PEG) and hydroxyl terminated poly(dimethyl siloxane) (HTPDMS) as polymeric phase change material for thermal energy storage", Solar energy, vol. 181, 15 March 2019 (2019-03-15), pages 187-194, XP055771305, ISSN: 0038-092X, DOI: 10.1016/j.solener.2019.01.091
  
Note: Within nine months from the publication of the mention of the grant of the European patent, any person may give notice to the European Patent Office of opposition to the European patent granted. Notice of opposition shall be filed in a written reasoned statement. It shall not be deemed to have been filed until the opposition fee has been paid. (Art. 99(1) European Patent Convention).


Description

[TECHNICAL FIELD]


CROSS-REFERENCE TO RELATED APPLICATION(S)



[0001] This application claims priority to and the benefits of Korean Patent Application No. 10-2019-0079367 filed on July 2, 2019 with the Korean Intellectual Property Office.

[0002] The present disclosure relates to a photopolymer composition, a hologram recording medium, an optical element and a holographic recording method.

[BACKGROUND ART]



[0003] Hologram recording medium records information by changing a refractive index in the holographic recording layer in the medium through an exposure process, reads the variation of refractive index in the medium thus recorded, and reproduces the information.

[0004] When a photopolymer (photosensitive resin) is used, the light interference pattern can be easily stored as a hologram by photopolymerization of the low molecular weight monomer. Therefore, the photopolymer can be used in various fields such as optical lenses, mirrors, deflecting mirrors, filters, diffusing screens, diffraction elements, light guides, waveguides, holographic optical elements having projection screen and/or mask functions, medium of optical memory system and light diffusion plate, optical wavelength multiplexers, reflection type, transmission type color filters, and the like.

[0005] Typically, a photopolymer composition for hologram production comprises a polymer binder, a monomer, and a photoinitiator, and the photosensitive film produced from such a composition is irradiated with laser interference light to induce photopolymerization of local monomers.

[0006] In a portion where a relatively large number of monomers are present in such photopolymerization process, the refractive index becomes high. And in a portion where a relatively large number of polymer binders are present, the refractive index is relatively lowered and thus the refractive index modulation occurs, and a diffraction grating is generated by such refractive index modulation. The value n of refractive index modulation is influenced by the thickness and the diffraction efficiency (DE) of the photopolymer layer, and the angular selectivity increases as the thickness decreases.

[0007] Recently, development of materials capable of maintaining a stable hologram with a high diffraction efficiency has been demanded, and also various attempts have been made to manufacture a photopolymer layer having a thin thickness and a high refractive index modulation.

[DETAILED DESCRIPTION OF THE INVENTION]


[Technical Problem]



[0008] It is one object of the present disclosure to provide a photopolymer composition that can more efficiently and easily provide a photopolymer layer capable of achieving a higher refractive index modulation value even in a thin thickness range.

[0009] It is another object of the present disclosure to provide a hologram recording medium including a photopolymer layer capable of realizing a higher refractive index modulation value even in a thin thickness range.

[0010] It is still another object of the present disclosure to provide an optical element including the hologram recording medium.

[0011] It is a further object of the present disclosure to provide a holographic recording method including selectively polymerizing photoreactive monomers contained in the hologram recording medium using a coherent laser light.

[Technical Solution]



[0012] Provided herein is a photopolymer composition for forming a hologram recording medium comprising: a polymer matrix or a precursor thereof formed by crosslinking a siloxane-based polymer containing at least one silane functional group (Si-H) and a (meth)acrylic polyol; a photoreactive monomer; and a photoinitiator.

[0013] Also provided herein is a hologram recording medium produced from the photopolymer composition.

[0014] Further provided herein is an optical element including the hologram recording medium.

[0015] Further provided herein is a holographic recording method comprising selectively polymerizing photoreactive monomers contained in the hologram recording medium using a coherent light source.

[0016] Hereinafter, the photopolymer composition, a hologram recording medium, the optical element and the holographic recording method according to a specific embodiment of the present disclosure will be described in more detail.

[0017] As used herein, the term "(meth)acrylate" refers to either methacrylate or acrylate.

[0018] As used herein, the term "(co)polymer" refers to either a homopolymer or a copolymer (including a random copolymer, a block copolymer, and a graft copolymer).

[0019] Further, the term "hologram" as used herein refers to a recording medium in which optical information is recorded in an entire visible range and a near ultraviolet range (300 to 800 nm) through an exposure process, and examples thereof include all of visual holograms such as in-line (Gabor) holograms, off-axis holograms, full-aperture transfer holograms, white light transmission holograms ("rainbow holograms"), Denisyuk holograms, off-axis reflection holograms, edge-lit holograms or holographic stereograms.

[0020] In the present disclosure, the alkyl group may be linear or branched, and the number of carbon atoms thereof is not particularly limited, but is preferably 1 to 40. According to one embodiment, the alkyl group has 1 to 20 carbon atoms. According to another embodiment, the alkyl group has 1 to 10 carbon atoms. According to still another embodiment, the alkyl group has 1 to 6 carbon atoms. Specific examples of the alkyl group include methyl, ethyl, propyl, n-propyl, isopropyl, butyl, n-butyl, isobutyl, tert-butyl, sec-butyl, 1-methyl-butyl, 1-ethyl-butyl, pentyl, n-pentyl, isopentyl, neopentyl, tert-pentyl, hexyl, n-hexyl, 1-methylpentyl, 2-methylpentyl, 4-methyl-2-pentyl, 3,3-dimethylbutyl, 2-ethylbutyl, heptyl, n-heptyl, 1-methylhexyl, cyclopentylmethyl, cyclohexylmethyl, octyl, n-octyl, tert-octyl, 1-methylheptyl, 2-ethylhexyl, 2-propylpentyl, n-nonyl, 2,2-dimethylheptyl, 1-ethyl-propyl, 1,1-dimethylpropyl, isohexyl, 2-methylpentyl, 4-methylhexyl, 5-methylhexyl, and the like, but are not limited thereto.

[0021] In the present disclosure, the alkylene group is a bivalent functional group derived from alkane, and may be, for example, linear, branched or cyclic. Specific examples thereof include a methylene group, an ethylene group, a propylene group, an isobutylene group, a sec-butylene group, a tert-butylene group, a pentylene group, a hexylene group, and the like.

[0022] According to one embodiment of the present disclosure, there is provided a photopolymer composition for forming a hologram recording medium comprising: a polymer matrix or a precursor thereof formed by crosslinking a siloxane-based polymer containing at least one silane functional group (Si-H) and a (meth)acrylic polyol; a photoreactive monomer; and a photoinitiator.

[0023] The present inventors have found through experiments that the hologram produced from the photopolymer composition comprising: a polymer matrix or a precursor thereof formed by crosslinking a siloxane-based polymer containing at least one silane functional group (Si-H) and a (meth)acrylic polyol; a photoreactive monomer; and a photoinitiator can achieve a significantly improved refractive index modulation value and excellent durability against temperature and humidity compared to previously known holograms even in a thinner thickness range, thereby completing the present disclosure.

[0024] At the time of producing a coating film or a hologram from the photopolymer composition, the crosslinking density is optimized, and excellent durability against temperature and humidity compared with existing matrix can be secured. In addition, by optimizing the crosslinking density, mobility between the photoreactive monomer having a high refractive index and other components having a low refractive index can be increased, thereby maximizing the refractive index modulation and improving recording characteristics.

[0025] Further, in the present disclosure, a fluorine-based compound, a phosphate-based compound or the like may be further included as a component of the polymer matrix or the precursor thereof. The fluorine-based compound or the phosphate-based compound has a lower refractive index than the photoreactive monomer, and thus, the refractive index of the polymer matrix can be lowered and the refractive index modulation of the photopolymer composition can be maximized.

[0026] Moreover, the phosphate-based compound severs as a plasticizer to lower the glass transition temperature of the polymer matrix, thereby increasing mobility of the photoreactive monomer and low refractive components, and contributing to improving moldability of the photopolymer composition.

[0027] Meanwhile, the polymer matrix or the precursor thereof formed by crosslinking a siloxane-based polymer containing at least one silane functional group (Si-H) and a (meth)acrylic polyol may serve as a support for the photopolymer composition and a final product produced therefrom.

[0028] Further, the polymer matrix or the precursor thereof can serve to enhance the refractive index modulation of the photopolymer film due to a relatively low refractive index (e.g., n=1.40 to 1.55). Further, the polymer matrix or the precursor thereof can rapidly crosslink the matrix even at room temperature when a Pt-based catalyst is introduced.

[0029] The polymer matrix may include a hydrosilylation reactant between the siloxane-based polymer containing at least one silane functional group (Si-H) and the (meth)acrylic polyol.

[0030] Hydrosilylation between the siloxane-based polymer containing at least one silane functional group (Si-H) and the (meth)acrylic polyol may be performed in the presence of a catalyst such as Karstedt's catalyst.

[0031] The hydrosilylation reactant between the siloxane-based polymer containing at least one silane functional group (Si-H) and the (meth)acrylic polyol have properties that increase the mobility of components due to the flexible main chain of the siloxane-based polymer, and easily ensure reliability after recording through the formation of a siloxane bond having excellent heat resistance and moist heat resistance properties.

[0032] Meanwhile, the siloxane-based polymer containing at least one silane functional groups (Si-H) may include a repeating unit represented by the following Chemical Formula 1 or a repeating unit represented by the following Chemical Formula 2.

in each of the repeating units of Chemical Formula 1, R1 to R2 may be the same as or different from each other, and are hydrogen, halogen, or an alkyl group having 1 to 10 carbon atoms,

n is the number of repetitions of the repeating unit which is 1 to 10,000, and

in at least one of the repeating units, R1 is an alkyl group having 1 to 10 carbon atoms and R2 is hydrogen.

in each of the repeating units of Chemical Formula 2, R11 to R13 may be the same as or different from each other, and are hydrogen, halogen or an alkyl group having 1 to 10 carbon atoms,

n is the number of repetitions of the repeating unit, which is 1 to 10,000, and

in at least one of the repeating units, R11 and R13 are an alkyl group having 1 to 10 carbon atoms, R12 is hydrogen, or R11 and R12 are an alkyl group having 1 to 10 carbon atoms, and R13 is hydrogen.



[0033] The number average molecular weight (measured by GPC) of the siloxane-based polymer containing at least one silane functional group (Si-H) may be 200 to 4,000 or 350 to 2500.

[0034] The number average molecular weight means a number average molecular weight (unit: g/mol) using polystyrene calibration measured by a GPC method. In the process of determining the weight average molecular weight using polystyrene calibration measured by a GPC method, a commonly known analyzing device, a detector such as a refractive index detector, and an analytical column can be used. Commonly applied conditions for temperature, solvent, and flow rate can be used. Specific examples of the measurement conditions can include a temperature of 30°C, tetrahydrofuran solvent and a flow rate of 1 mL/min.

[0035] When the number average molecular weight of the siloxane-based polymer containing at least one silane functional group (Si-H) is too low, it is volatilized in the process of crosslinking with the polyol (40°C), and thus, the degree of crosslinking of the matrix is lowered, which causes deterioration of recording characteristics. Further, when the weight average molecular weight of the siloxane-based polymer containing at least one silane functional group (Si-H) is too high, phase separation of the components occurs due to incompatibility with the photopolymer components, which causes deterioration of recording characteristics.

[0036] The (meth)acrylic polyol can have a structure in which two or more hydroxy groups are bonded to a main chain or side chain of the (meth)acrylate-based polymer. For example, the (meth)acrylic polyol can have a structure in which two or more carboxyl groups of the (meth)acrylate-based polymer are substituted and so the terminal has a hydroxy group.

[0037] More specifically, two or more hydroxy groups bonded to the main chain of the (meth)acrylate-based polymer can be bonded through an aliphatic divalent functional group having 1 to 30 carbon atoms, an aromatic divalent functional group having 6 to 30 carbon atoms, and the like.

[0038] Further, the (meth)acrylic polyol can have a weight average molecular weight of 200,000 to 1,000,000, preferably 400,000 to 700,000. The method of measuring the weight average molecular weight is as described above. When the weight average molecular weight of the (meth)acrylic polyol is too low, the matrix does not server as a support, and thus recording characteristics may be deteriorated with time. Further, when the weight average molecular weight of the (meth)acrylic polyol is too high, the flexibility of the matrix is reduced and the mobility of the components is reduced, which causes deterioration of the recording characteristics.

[0039] Meanwhile, the hydroxy group (-OH) equivalent of the (meth)acrylic polyol can be 500 g/equivalent to 2,500 g/equivalent, or 550 g/equivalent to 2,200 g/equivalent, or 1,000 g/equivalent to 2,000 g/equivalent.

[0040] The hydroxyl group (-OH) equivalent of the (meth)acrylic polyol is the equivalent of one hydroxy functional group (g/equivalent), and is a value obtained by dividing the weight average molecular weight of the (meth)acrylic polyol by the number of hydroxy functional groups per molecule. As the equivalent value is smaller, the density of the functional group is higher, and as the equivalent value is larger, the density of the functional group is lower.

[0041] Consequently, as the (meth)acrylic polyol has the hydroxyl group equivalent, the crosslinking density between the polymer matrix of the photopolymer composition and the (meth)acrylic polyol is optimized, and mobility between the photoreactive monomer having a high refractive index and a component having a low refractive index can be increased, thereby maximizing the refractive index modulation and improving recording properties, and further exhibiting high diffraction efficiency.

[0042] When the hydroxyl group (-OH) equivalent of the (meth)acrylic polyol is too low, the crosslinking density of the matrix is too high, which hinders the mobility of the components, and thus leads to deterioration of recording characteristics. Further, when the hydroxyl group (-OH) equivalent of the (meth)acrylic polyol is too high, the crosslinking density is too low to serve as a support, the interface of the diffraction gratings generated after recording collapses, and the refractive index modulation value may decrease with the passage of time.

[0043] Meanwhile, the photoreactive monomer can include a polyfunctional (meth)acrylate monomer or a monofunctional (meth)acrylate monomer.

[0044] As described above, in a portion where the monomer is polymerized in the process of photopolymerization of the photopolymer composition and the polymer is present in relatively large amounts, the refractive index becomes high. In a portion where the polymer binder is present in relatively large amount, the refractive index becomes relatively low, the refractive index modulation occurs, and a diffraction grating is generated by such refractive index modulation.

[0045] Specifically, an example of the photoreactive monomer can include (meth)acrylate-based α,β-unsaturated carboxylic acid derivatives, for example, (meth)acrylate, (meth)acrylamide, (meth)acrylonitrile, (meth)acrylic acid or the like, or a compound containing a vinyl group or a thiol group.

[0046] An example of the photoreactive monomer can include a polyfunctional (meth)acrylate monomer having a refractive index of 1.5 or more, 1.53 or more, or 1.5 to 1.7. The polyfunctional (meth)acrylate monomer having a refractive index of 1.5 or more, or 1.53 or more, or 1.5 to 1.7 can include a halogen atom (bromine, iodine, etc.), sulfur (S), phosphorus (P), or an aromatic ring.

[0047] More specific examples of the polyfunctional (meth)acrylate monomer having a refractive index of 1.5 or more include bisphenol A modified diacrylate type, fluorene acrylate type (HR6022, etc. manufactured by Miwon Specialty Chemical Co., Ltd.), bisphenol fluorene epoxy acrylate type (HR6100, HR6060, HR6042, etc. manufactured by Miwon Specialty Chemical Co., Ltd.), halogenated epoxy acrylate series (HR1139, HR3362, etc. manufactured by Miwon Specialty Chemical Co., Ltd.).

[0048] Another example of the photoreactive monomer can include a monofunctional (meth)acrylate monomer. The monofunctional (meth)acrylate monomer can contain an ether bond and a fluorene functional group in the molecule. Specific examples of such monofunctional (meth)acrylate monomer include phenoxybenzyl (meth)acrylate, o-phenylphenol ethylene oxide (meth)acrylate, benzyl (meth)acrylate, 2-(phenylthio)ethyl (meth)acrylate, biphenylmethyl (meth)acrylate, or the like.

[0049] Meanwhile, the photoreactive monomer can have a weight average molecular weight of 50 g/mol to 1000 g/mol, or 200 g/mol to 600 g/mol. The weight average molecular weight refers to a weight average molecular weight using polystyrene calibration measured by a GPC method.

[0050] Meanwhile, the photopolymer composition of the embodiment includes a photoinitiator. The photoinitiator is a compound which is activated by light or actinic radiation and initiates polymerization of a compound containing a photoreactive functional group such as the photoreactive monomer.

[0051] As the photoinitiator, commonly known photoinitiators can be used without particular limitation, but specific examples thereof include a photoradical polymerization initiator, a photocationic polymerization initiator, or a photoanionic polymerization initiator.

[0052] Specific examples of the photoradical polymerization initiator include imidazole derivatives, bisimidazole derivatives, N-aryl glycine derivatives, organic azide compounds, titanocene, aluminate complex, organic peroxide, N-alkoxypyridinium salts, thioxanthone derivatives, amine derivatives or the like. More specifically, examples of the photoradical polymerization initiator include 1,3-di(t-butyldioxycarbonyl)benzophenone, 3,3',4,4"-tetrakis(t-butyldioxycarbonyl)benzophenone, 3-phenyl-5-isoxazolone, 2-mercapto benzimidazole, bis(2,4,5-triphenyl)imidazole, 2,2-dimethoxy-1,2-diphenylethane-1-one (product name: Irgacure 651/manufacturer: BASF), 1-hydroxy-cyclohexyl-phenyl-ketone (product name: Irgacure 184/manufacturer: BASF), 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butanone-1 (product name: Irgacure 369/manufacturer: BASF), and bis(η5-2,4-cyclopentadiene-1-yl)-bis(2,6-difluoro-3-(1H-pyrrole-1-yl)-phenyl)titanium (product name: Irgacure 784/manufacturer: BASF), Ebecryl P-1 15(manufacturer: SK entis), and the like.

[0053] The photocationic polymerization initiator may include a diazonium salt, a sulfonium salt, or an iodonium salt, and examples thereof include sulfonic acid esters, imidosulfonates, dialkyl-4-hydroxysulfonium salts, arylsulfonic acid-p-nitrobenzyl esters, silanol-aluminum complexes, (η6-benzene) (η5-cyclopentadienyl)iron (II), or the like. In addition, benzoin tosylate, 2,5-dinitrobenzyltosylate, N-tosylphthalic acid imide, or the like can be mentioned. More specific examples of the photocationic polymerization initiator include commercially available products such as Cyracure UVI-6970, Cyracure UVI-6974 and Cyracure UVI-6990 (manufacturer: Dow Chemical Co. in USA), Irgacure 264 and Irgacure 250 (manufacturer: BASF) or CIT-1682 (manufacturer: Nippon Soda).

[0054] The photoanionic polymerization initiator may be borate salt, for example, butyryl chlorine butyl triphenyl borate, or the like. More specific examples of the photoanionic polymerization initiator include commercially available products such as Borate V (manufacturer: Spectra Group).

[0055] In addition, the photopolymer composition of the embodiment may include monomolecular (type I) initiator or bimolecular (type II) initiator. The (type I) system for free radical photopolymerization may include, for example, an aromatic ketone compounds in combination with a tertiary amine, such as benzophenone, alkylbenzophenone, 4,4'-bis(dimethylamino)benzophenone (Michler's ketone), anthrone and halogenated benzophenone or a mixture of these types. The bimolecular (type II) initiator may include benzoin and derivatives thereof, benzyl ketal, acylphosphine oxide, for example, 2,4,6-trimethylbenzoyldiphenylphosphine oxide, bisacylophosphine oxide, phenylglyoxyl ester, camphorquinone, alpha-aminoalkylphenone, alpha-dialkoxyacetophenone, 1-[4-(phenylthio)phenyl]octane-1,2-dione 2-(O-benzoyloxime), alpha-hydroxyalkylphenone, and the like.

[0056] The photopolymer composition of the embodiment may include 1% to 80wt.% of the polymer matrix or the precursor thereof; 1% to 80wt.% of the photoreactive monomer; and 0.1% to 20wt.% of the photoinitiator. When the photopolymer composition further includes an organic solvent as described hereinafter, the content of the above-mentioned components is based on the total sum of the above-mentioned components (the total sum of the components excluding the organic solvent).

[0057] The photopolymer composition may further include a fluorine-based compound. The fluorine-based compound is stable with little reactivity and has a low refractive index. Therefore, the refractive index of the polymer matrix may be lowered when the fluorine-based compound is added into the photopolymer composition, thereby maximizing the refractive index modulation with the monomer

[0058] The fluorine-based compound may include at least one functional group selected from the group consisting of an ether group, an ester group and an amide group, and at least two difluoromethylene groups. More specifically, the fluorine-based compound may have a structure represented by the following Chemical Formula 4 in which a functional group including an ether group is bonded to both terminal ends of a central functional group including a direct bond between two difluoromethylene groups or an ether bond.



[0059] In Chemical Formula 4, R11 and R12 are each independently a difluoromethylene group, R13 and R16 are each independently a methylene group, R14 and R15 are each independently a difluoromethylene group, and R17 and R18 are each independently a polyalkylene oxide, and m is an integer of 1 or more, 1 to 10, or 1 to 3.

[0060] Preferably in Chemical Formula 4, R11 and R12 are each independently a difluoromethylene group, R13 and R16 are each independently a methylene group, R14 and R15 are each independently a difluoromethylene group, and R17 and R18 are each independently a 2-methoxyethoxymethoxy group, and m is an integer of 2.

[0061] The fluorine-based compound may have a refractive index of less than 1.45, or 1.3 or more and less than 1.45. As described above, since the photoreactive monomer has a refractive index of 1.5 or more and the fluorine-based compound has a lower refractive index than that of the photoreactive monomer, the refractive index of the polymer matrix may be further lowered, thereby maximizing the refractive index modulation with the monomer.

[0062] Specifically, the content of the fluorine-based compound may be 30 to 150 parts by weight, or 50 to 110 parts by weight based on 100 parts by weight of the photoreactive monomer, and the refractive index of the polymer matrix may be 1.46 to 1.53.

[0063] When the content of the fluorine-based compound is excessively decreased based on 100 parts by weight of the photoreactive monomer, the refractive index modulation value after recording may be lowered due to a lack of low refractive components. When the content of the fluorine-based compound is excessively increased, haze may be generated due to poor compatibility with other components or some fluorine-based compounds may be eluted to the surface of the coating layer.

[0064] The fluorine-based compound may have a weight average molecular weight (measured by GPC) of 300 or more, or 300 to 1000. A specific method of measuring the weight average molecular weight is as described above.

[0065] Meanwhile, the photopolymer composition may further include a photosensitizing dye.

[0066] The photosensitizing dye serves as a photosensitizing pigment to sensitize the photoinitiator. More specifically, the photosensitizing dye may be stimulated by the light irradiated on the photopolymer composition and may also serve as an initiator to initiate polymerization of the monomer and the cross-linking monomer. The photopolymer composition may contain 0.01 wt. % to 30 wt. %, or 0.05 wt. % to 20. wt % of the photosensitizing dye.

[0067] Examples of the photosensitizing dye are not particularly limited, and various compounds commonly known in the art can be used. Specific examples of the photosensitizing dye include sulfonium derivative of ceramidonine, new methylene blue, thioerythrosine triethylammonium, 6-acetylamino-2-methylceramidonin, eosin, erythrosine, rose bengal, thionine, basic yellow, Pinacyanol chloride, Rhodamine 6G, Gallocyanine, ethyl violet, Victoria blue R, Celestine blue, QuinaldineRed, Crystal Violet, Brilliant Green, Astrazon orange G, Darrow Red, Pyronin Y, Basic Red 29, pyrylium iodide, Safranin O, Cyanine, Methylene Blue, Azure A, or a combination of two or more thereof.

[0068] The photopolymer composition may further include an organic solvent. Nonlimiting examples of the organic solvent include ketones, alcohols, acetates, ethers, and a mixture of two or more thereof.

[0069] Specific examples of the organic solvent include ketones such as methyl ethyl ketone, methyl isobutyl ketone, acetylacetone or isobutyl ketone; alcohols such as methanol, ethanol, n-propanol, i-propanol, n-butanol, i-butanol or t-butanol; acetates such as ethyl acetate, i-propyl acetate, or polyethylene glycol monomethyl ether acetate; ethers such as tetrahydrofuran or propylene glycol monomethyl ether; or a mixture of two or more thereof.

[0070] The organic solvent may be added at the time of mixing the respective components contained in the photopolymer composition, or may be contained in the photopolymer composition by adding the respective components dispersed or mixed in an organic solvent. When the content of the organic solvent in the photopolymer composition is too low, flowability of the photopolymer composition may be lowered, resulting in the occurrence of defects such as striped patterns on the finally produced film. In addition, when too much organic solvent is added, the solid content is lowered, and coating and film formation are not sufficient, so that physical properties and surface characteristics of the film may be deteriorated and defects may occur during the drying and curing process. Thus, the photopolymer composition may include an organic solvent such that the total solid content concentration of the components contained is 1 wt. % to 70 wt. %, or 2 wt. % to 50 wt. %.

[0071] The photopolymer composition may further include other additives, catalysts, and the like. For example, the photopolymer composition may include a catalyst which is commonly known for promoting polymerization of the polymer matrix or the photoreactive monomer. Examples of the catalyst include platiniumm-based catalysts such as Karstedt's catalyst, rhodium-based catalysts, iridium-based catalysts, rhenium-based catalysts, molybdenum-based catalysts, iron-based catalysts, nickel-based catalysts, alkali metal and alkaline earth metal catalysts. As the non-metal catalyst, a Lewis acids-based catalyst, a carbene-based catalyst, or the like can be used.

[0072] Examples of the other additives include a defoaming agent or a phosphate-based plasticizer, and the defoaming agent may be a silicone-based reactive additive, for example, Tego Rad 2500. Examples of the plasticizer include phosphate compounds such as tributyl phosphate, and the plasticizer may be added in a weight ratio of 1:5 to 5:1 together with the fluorine-based compound. The plasticizer may have a refractive index of less than 1.5 and a molecular weight of 700 or less.

[0073] The photopolymer composition can be used for hologram recording.

[0074] Meanwhile, according to another embodiment of the present disclosure, a hologram recording medium produced from the photopolymer composition can be provided.

[0075] As described above, when the photopolymer composition of one embodiment is used, it is possible to provide holograms capable of achieving a significantly improved refractive index modulation value and a high diffraction efficiency while having a thinner thickness, as compared with holograms previously known in the art.

[0076] The hologram recording medium can realize a refractive index modulation value (n) of 0.020 or more, 0.021 or more, 0.022 or more, 0.023 or more, 0.020 to 0.035, or 0.027 to 0.030 even at a thickness of 5 µm to 30 µm.

[0077] Further, the hologram recording medium may have a diffraction efficiency of 50% or more, 85% or more, or 85 to 99% at a thickness of 5 µm to 30 µm.

[0078] In the photopolymer composition of the one embodiment, the respective components contained therein are homogeneously mixed, dried and cured at a temperature of 20°C or higher, and then predetermined exposure procedures are undertaken, thereby producing a hologram for optical application in the entire visible range and the near ultraviolet region (300 to 800 nm).

[0079] In the photopolymer composition of the one embodiment, the components for forming the polymer matrix or the precursor thereof may be first homogeneously mixed, and then the matrix is crosslinked in a liquid phase at room temperature using a Pt-based catalyst. The monomer and the initiator are added a later time to prepare the final photopolymer coating composition.

[0080] In the photopolymer composition of one embodiment, a mixing device, a stirrer, a mixer, or the like which are commonly used in the art can be used for mixing the respective components contained therein without particular limitation. The temperature in the mixing process may be 0°C to 100°C, preferably 10°C to 80°C, particularly preferably 20°C to 60°C.

[0081] The drying temperature may vary depending on the composition of the photopolymer and the drying is promoted, for example, by heating at a temperature of from 30°C to 180°C.

[0082] At the time of drying, the photopolymer may be in state of being injected into or coated onto a predetermined substrate or mold.

[0083] Meanwhile, as the method of recording a visual hologram on a hologram recording medium produced from the photopolymer composition, generally known methods can be used without particular limitation. The method described in the holographic recording method of the embodiment described hereinafter can be adopted as an example.

[0084] According to another embodiment of the present disclosure, a holographic recording method may be provided, which includes selectively polymerizing photoreactive monomers contained in the photopolymer composition using a coherent laser.

[0085] As described above, through the process of mixing and curing the photopolymer composition, it is possible to produce a medium in which no visual hologram is recorded, and a visual hologram can be recorded on the medium through a predetermined exposure process.

[0086] A visual hologram can be recorded on the media provided through the process of mixing and curing the photopolymer composition, using known devices and methods under commonly known conditions.

[0087] Meanwhile, according to another embodiment of the present disclosure, an optical element including the hologram recording medium can be provided.

[0088] Specific examples of the optical element include optical lenses, mirrors, deflecting mirrors, filters, diffusing screens, diffraction elements, light guides, waveguides, holographic optical elements having projection screen and/or mask functions, medium of optical memory system and light diffusion plate, optical wavelength multiplexers, reflection type, transmission type color filters, and the like.

[0089] An example of the optical element including the hologram recording medium may include a hologram display device.

[0090] The hologram display device includes a light source unit, an input unit, an optical system, and a display unit. The light source unit is a part that irradiates a laser beam used for providing, recording, and reproducing three-dimensional image information of an object in the input unit and the display unit. Further, the input unit is a part that previously inputs three-dimensional image information of an object to be recorded on the display unit, and for example, three-dimensional information of an object such as the intensity and phase of light for each space can be input into an electrically addressed liquid crystal SLM, wherein an input beam may be used. The optical system may include a mirror, a polarizer, a beam splitter, a beam shutter, a lens, and the like. The optical system can be distributed into an input beam for sending a laser beam emitted from the light source unit to the input unit, a recording beam for sending the laser beam to the display unit, a reference beam, an erasing beam, a reading beam, and the like.

[0091] The display unit can receive three-dimensional image information of an object from an input unit, record it on a hologram plate composed of an optically addressed SLM, and reproduce the three-dimensional image of the object. Herein, the three-dimensional image information of the object can be recorded via interference of the input beam and the reference beam. The three-dimensional image information of the object recorded on the hologram plate can be reproduced into a three-dimensional image by the diffraction pattern generated by the reading beam. The erasing beam can be used to quickly remove the formed diffraction pattern. Meanwhile, the hologram plate can be moved between a position at which a three-dimensional image is input and a position at which a three-dimensional image is reproduced.

[ADVANTAGEOUS EFFECTS]



[0092] According to the present disclosure, provided are a photopolymer composition which can more effectively and easily provide a photopolymer layer having a higher refractive index modulation value even in a thin thickness range, a hologram recording medium having a higher refractive index modulation value even in a thin thickness range, an optical element and a holographic recording method.

[DETAILED DESCRIPTION OF THE EMBODIMENTS]



[0093] Hereinafter, the present disclosure will be described in more detail by way of examples. However, these examples are given for illustrative purposes only and are not intended to limit the scope of the present disclosure thereto.

[Preparation Example]


[Preparation Example 1: Preparation of (Meth)acrylic Polyol for Matrix]



[0094] 460 g of butyl acrylate, 276 g of methyl acrylate, and 64 g of hydroxybutyl acrylate were placed in a 2L jacketed reactor and diluted with 1200 g of ethyl acetate. The reaction temperature was set at 60 °C to 70 °C, and stirring was performed for about 30 minutes to 1 hour. 0.28 g of n-dodecyl mercaptan was further added thereto, and stirring was further performed for about 30 minutes. Thereafter, 0.32 g of AIBN as a polymerization initiator was added thereto, and polymerization was performed at the reaction temperature for 4 hours or more, and maintained until the residual acrylate content became less than 1% to obtain a (meth)acrylate-based polyol (co)polymer having a hydroxyl functional group in a branched chain (the weight average molecular weight of about 600,000, the OH equivalent of 1802 g/equivalent).

[Preparation Example 2: Preparation of Non-reactive Low Refractive Material]



[0095] 20.51 g of 2,2'-((oxybis(1,1,2,2-tetrafluoroethane-2,1-diyl))bis(oxy))bis(2,2-difluoroethan-1-ol was placed in a 1000 ml flask, dissolved in 500 g of tetrahydrofuran, and 4.40 g of sodium hydride (60% dispersion in mineral oil) was gently added several times while stirring at 0°C. After stirring at 0°C for 20 minutes, 12.50 ml of 2-methoxyethoxymethyl chloride was slowly dropped. When all of the reactants were confirmed to be consumed by 1H NMR, the reaction solvent was completely removed under reduced pressure. The organic layer was collected by extracting three times with 300 g of dichloromethane, which was then filtered with magnesium sulfate, and all dichloromethane was removed under reduced pressure to obtain 29 g of a liquid product having a purity of 95% or more at a yield of 98%.

[Examples and Comparative Examples: Preparation of Photopolymer Composition]



[0096] As shown in Table 1 or Table 2 below, the (meth)acrylate-based polyol (co)polymer having a hydroxyl functional group in a branched chain of Preparation Example 1, the siloxane-based polymer containing a silane (Si-H) functional group, the non-reactive low-refractive material of Preparation Example 2, Safranin O (dye, manufactured by Sigma-Aldrich), silicone-based reactive additive (Tego Rad 2500) and methyl isobutyl ketone (MIBK) was mixed with light blocked, and stirred with a paste mixer for about 10 minutes. Karstedt's (Pt based) catalyst was added for matrix crosslinking, and liquid crosslinking was performed at room temperature for at least 30 minutes. After liquid crosslinking of the matrix, a photoreactive monomer (high refractive acrylate, refractive index 1.600, HR6022 [Miwon Specialty Chemical Co., Ltd.]) and a Borate V (Spectra Group) initiator were added to the coating solution, and further mixed for 5 minutes or more.

[0097] The coating solution was coated to a thickness of 10 to 15 µm on a TAC substrate having a thickness of 80 µm using a meyer bar, and dried at 60°C within 10 minutes.

Experimental Examples: Holographic Recording



[0098] 
  1. (1) The photopolymer-coated surfaces prepared in each of Examples and Comparative Examples were laminated on a slide glass, and fixed so that a laser first passed through the glass surface at the time of recording.
  2. (2) Measurement of diffraction efficiency (η)


[0099] A holographic recording was done via interference of two interference lights (reference light and object light), and a transmission-type recording was done so that the two beams were incident on the opposite side of the sample. The diffraction efficiencies change with the incident angle of the two beams, and become non-slanted when the incident angles of the two beams are the same. In the non-slanted recording, the diffraction grating is generated parallel to the film because the incident angles of the two beams are equal on the normal basis.

[0100] The recording (reference light = 30° and object light =40°) was done in a transmission-type non-slanted manner using a laser with a wavelength of 532 nm, and the diffraction efficiency (η) was calculated according to the following Equation 1.

in Equation 1, η is a diffraction efficiency, PD is an output amount (mW/cm2) of the diffracted beam of a sample after recording, and PT is an output amount (mW/cm2) of the transmitted beam of the recorded sample.
[Table 1] Measurement results of Experimental Examples of the photopolymer compositions (unit: g) of Examples and the hologram recording medium prepared therefrom
CategoryExampl e 1Exampl e 2Exampl e 3Exampl e 4
(meth)acrylat e-based copolymer Preparation Example 1 32.6 31.3 33.3 29.7
Silane(SiH) group-containing siloxane-based polymer Poly(methylhydrosiloxane), trimethylsilyl terminated (Sigma-Aldrich, Mn=390) 1.9      
Poly(dimethylsiloxane-co-methylhydrosiloxane), trimethylsilyl terminated (Sigma-Aldrich, Mn=950)   3.2    
Poly(methylhydrosiloxane)(Sig ma-Aldrich, Mn=1700∼3200)     1.2  
Poly(dimethylsiloxane), hydride terminated(Sigma-Aldrich, Mn=580)       4.8
Photoreactive monomer HR6022 34.5 34.5 34.5 34.5
Dye safranin O 0.2 0.2 0.2 0.2
Borate salt Borate V 0.3 0.3 0.3 0.3
Non-reactive low refractive material (P3) Preparation Example 2 30 30 30 30
Catalyst Karstedt(Sigma-Aldrich) 0.003 0.003 0.003 0.003
Additive Tego Rad 2500 0.3 0.3 0.3 0.3
Solvent MIBK 234 234 234 234
Coating thickness (unit: µm) 15 15 15 15
Diffraction efficiency (%) 95 80 70 90
[Table 2] Measurement results of Experimental Examples of the photopolymer compositions of Comparative Examples and the hologram recording medium prepared therefrom
CategoryComparative Example 1Comparative Example 2Comparative Example 3
Polymer matrix Polyvinyl acetate (Sigma-Aldrich/ Mw=50,000) 27.6    
Cellulose acetate Butyrate(Sigma-Aldrich/ Mw=70,000)   27.6  
Cellulose acetate propionate (Sigma-Aldrich/ Mw=75000)     27.6
Photoreactive monomer HR6022 41.4 41.4 41.4
Dye safranin O 0.2 0.2 0.2
Borate salt Borate V 0.3 0.3 0.3
Non-reactive low refractive material (P3) Preparation Example 2 30 30 30
Additive Tego Rad 2500 0.5 0.5 0.5
Solvent MIBK 200 200 200
Coating thickness (unit: µm) 15 15 15
Diffraction efficiency (%) 40 10 0


[0101] As seen from Table 1 and Table 2 above, the photopolymer composition to which the crosslinked matrix of the (meth)acrylate-based polyol (co)polymer having a hydroxyl functional group in a branched chain of Preparation Example 1 and a polymer containing a silane (S-H) group was applied showed a diffraction efficiency of 70% or more at a coating thickness of 15 µm.

[0102] On the contrary, the photopolymer compositions to which non-crosslinked commercial polymer products was applied as a matrix showed relatively low diffraction efficiency of 40% or less.


Claims

1. A photopolymer composition for forming a hologram recording medium comprising:

a polymer matrix or a precursor thereof formed by crosslinking a siloxane-based polymer containing at least one silane functional group (Si-H) and a (meth)acrylic polyol;

a photoreactive monomer; and

a photoinitiator.


 
2. The photopolymer composition according to claim 1, wherein the siloxane-based polymer containing at least one silane functional groups (Si-H) includes a repeating unit represented by Chemical Formula 1 or a repeating unit represented by Chemical Formula 2:

wherein, in each of the repeating units of Chemical Formula 1, R1 and R2 are the same as or different from each other, and are hydrogen, halogen, or an alkyl group having 1 to 10 carbon atoms,

n is the number of repetitions of the repeating unit which is 1 to 10,000, and

in at least one of the repeating units, R1 is an alkyl group having 1 to 10 carbon atoms and R2 is hydrogen.



wherein, in each of the repeating units of Chemical Formula 2, R11 to R13 are the same as or different from each other, and are hydrogen, halogen or an alkyl group having 1 to 10 carbon atoms,

n is the number of repetitions of the repeating unit, which is 1 to 10,000, and

in at least one of the repeating units, R11 and R13 are an alkyl group having 1 to 10 carbon atoms, R12 is hydrogen, or R11 and R12 are an alkyl group having 1 to 10 carbon atoms, and R13 is hydrogen.


 
3. The photopolymer composition according to claim 1, wherein the siloxane-based polymer containing at least one silane functional groups (Si-H) has number average molecular weight of 200 to 4,000.
 
4. The photopolymer composition according to claim 1, wherein the (meth)acrylic polyol has a structure in which two or more hydroxy groups are bonded to a main chain or side chain of an (meth)acrylate-based polymer, and
wherein the (meth)acrylic polyol has a weight average molecular weight of 200,000 to 1,000,000.
 
5. The photopolymer composition according to claim 1, wherein the (meth)acrylic polyol has a hydroxy group equivalent of 500 g/equivalent to 2,500 g/equivalent.
 
6. The photopolymer composition according to claim 1, wherein the polymer matrix includes a hydrosilylation reactant between the siloxane-based polymer containing at least one silane functional group (Si-H) and the (meth)acrylic polyol.
 
7. The photopolymer composition according to claim 1, wherein the photoreactive monomer includes a polyfunctional (meth)acrylate monomer or a monofunctional (meth)acrylate monomer.
 
8. The photopolymer composition according to claim 1, wherein the photoreactive monomer has a refractive index of 1.5 or more.
 
9. The photopolymer composition according to claim 1, wherein the photopolymer composition further comprises a fluorine-based compound.
 
10. The photopolymer composition according to claim 9, wherein the fluorine-based compound comprises at least one functional group selected from the group consisting of an ether group, an ester group and an amide group, and at least two difluoromethylene groups.
 
11. The photopolymer composition according to claim 9, wherein the fluorine-based compound has a refractive index of less than 1.45.
 
12. The photopolymer composition according to claim 1, wherein the polymer matrix has a refractive index of 1.46 to 1.53.
 
13. A hologram recording medium comprising the photopolymer composition of claim 1.
 
14. An optical element comprising the hologram recording medium of claim 13.
 
15. A holographic recording method comprising:
selectively polymerizing photoreactive monomers contained in the photopolymer composition of claim 1 using a coherent light source.
 


Ansprüche

1. Photopolymerkomposition zur Herstellung eines Hologramm-Aufzeichnungsmediums, umfassend:

eine Polymermatrix oder ein Präkursor davon, gebildet durch Vernetzung eines siloxanbasierten Polymers, enthaltend mindestens eine funktionelle Silangruppe (Si-H), und ein (Meth)acrylpolyol;

ein photoreaktives Monomer; und

einen Photoinitiator.


 
2. Photopolymerkomposition gemäß Anspruch 1, wobei das siloxanbasierte Polymer, enthaltend mindestens eine funktionelle Silangruppe (Si-H), eine sich wiederholende Einheit, dargestellt durch Chemische Formel 1, oder eine sich wiederholende Einheit, dargestellt durch Chemische Formel 2, enthält:

wobei in jeder der sich wiederholenden Einheiten der Chemischen Formel 1, R1 und R2 gleich oder verschieden voneinander sind und Wasserstoff, Halogen oder eine Alkylgruppe mit 1 bis 10 Kohlenstoffatomen sind,

n ist die Anzahl der Wiederholungen der Wiederholungseinheit, welche 1 bis 10.000 beträgt, und

in mindestens einer der sich wiederholenden Einheiten ist R1 eine Alkylgruppe mit 1 bis 10 Kohlenstoffatomen und R2 ist Wasserstoff;

wobei in jeder der sich wiederholenden Einheiten der Chemischen Formel 2, R11 bis R13 gleich oder verschieden voneinander sind und Wasserstoff, Halogen oder eine Alkylgruppe mit 1 bis 10 Kohlenstoffatomen bedeuten,

n ist die Anzahl der Wiederholungen der Wiederholungseinheit, welche 1 bis 10.000 beträgt, und

in mindestens einer der sich wiederholenden Einheiten sind R11 und R13 eine Alkylgruppe mit 1 bis 10 Kohlenstoffatomen, R12 ist Wasserstoff, oder R11 und R12 sind eine Alkylgruppe mit 1 bis 10 Kohlenstoffatomen, und R13 ist Wasserstoff.


 
3. Photopolymerkomposition gemäß Anspruch 1, wobei das siloxanbasierte Polymer, enthaltend mindestens eine funktionelle Silangruppe (Si-H), ein zahlenmittleres Molekulargewicht von 200 bis 4.000 aufweist.
 
4. Photopolymerkomposition gemäß Anspruch 1, wobei das (Meth)acrylpolyol eine Struktur aufweist, in welcher zwei oder mehr Hydroxygruppen an eine Hauptkette oder Seitenkette eines (meth)acrylatbasierten Polymers gebunden sind, und
wobei das (Meth)acrylpolyol ein gewichtsmittleres Molekulargewicht von 200.000 bis 1.000.000 aufweist.
 
5. Photopolymerkomposition gemäß Anspruch 1, wobei das (Meth)acrylpolyol ein Hydroxygruppenäquivalent von 500 g/Äquivalent bis 2.500 g/Äquivalent aufweist.
 
6. Photopolymerkomposition gemäß Anspruch 1, wobei die Polymermatrix einen Hydrosilylierungsreaktanten zwischen dem siloxanbasierten Polymer, enthaltend mindestens eine funktionelle Silangruppe (Si-H), und dem (Meth)acrylpolyol enthält.
 
7. Photopolymerkomposition gemäß Anspruch 1, wobei das photoreaktive Monomer ein polyfunktionelles (Meth)acrylatmonomer oder ein monofunktionelles (Meth)acrylatmonomer enthält.
 
8. Photopolymerkomposition gemäß Anspruch 1, wobei das photoreaktive Monomer einen Brechungsindex von 1,5 oder mehr aufweist.
 
9. Photopolymerkomposition gemäß Anspruch 1, wobei die Photopolymerkomposition ferner eine fluorbasierte Verbindung umfasst.
 
10. Photopolymerkomposition gemäß Anspruch 9, wobei die fluorbasierte Verbindung mindestens eine funktionelle Gruppe umfasst, ausgewählt aus der Gruppe bestehend aus einer Ethergruppe, einer Estergruppe und einer Amidgruppe, und mindestens zwei Difluormethylengruppen.
 
11. Photopolymerkomposition gemäß Anspruch 9, wobei die fluorbasierte Verbindung einen Brechungsindex von weniger als 1,45 aufweist.
 
12. Photopolymerkomposition gemäß Anspruch 1, wobei die Polymermatrix einen Brechungsindex von 1,46 bis 1,53 aufweist.
 
13. Hologramm-Aufzeichnungsmedium, umfassend die Photopolymerkomposition gemäß Anspruch 1.
 
14. Optisches Element, umfassend das Hologramm-Aufzeichnungsmedium gemäß Anspruch 13.
 
15. Holographisches Aufzeichnungsverfahren, umfassend:
Selektives Polymerisieren photoreaktiver Monomere, enthalten in der Photopolymerkomposition gemäß Anspruch 1, unter Verwendung einer kohärenten Lichtquelle.
 


Revendications

1. Composition de photopolymère pour former un support d'enregistrement d'hologramme comprenant :

une matrice polymère ou un précurseur de celle-ci formé par la réticulation d'un polymère à base de siloxane contenant au moins un groupe fonctionnel silane (Si-H) et un polyol (méth)acrylique ;

un monomère photoréactif ; et

un photoinitiateur.


 
2. Composition de photopolymère selon la revendication 1, dans laquelle le polymère à base de siloxane contenant au moins un groupe fonctionnel silane (Si-H) inclut un motif répétitif représenté par la formule chimique 1 ou un motif répétitif représenté par la formule chimique 2 :

dans laquelle, dans chacun des motifs répétitifs de formule chimique 1, R1 et R2 sont identiques l'un à l'autre ou différents l'un de l'autre, et sont un hydrogène, un halogène, ou un groupe alkyle présentant de 1 à 10 atomes de carbone,

n est le nombre de répétitions du motif répétitif qui est de 1 à 10 000, et

dans au moins un des motifs répétitifs, R1 est un groupe alkyle présentant 1 à 10 atomes de carbone et R2 est un hydrogène.

dans laquelle, dans chacun des motifs répétitifs de formule chimique 2, R11 à R13 sont identiques les uns aux autres ou différents les uns des autres, et sont un hydrogène, un halogène ou un groupe alkyle présentant de 1 à 10 atomes de carbone,

n est le nombre de répétitions du motif répétitif, qui est de 1 à 10 000, et

dans au moins un des motifs répétitifs, R11 et R13 sont un groupe alkyle présentant 1 à 10 atomes de carbone, R12 est un hydrogène, ou R11 et R12 sont un groupe alkyle présentant 1 à 10 atomes de carbone, et R13 est un hydrogène.


 
3. Composition de photopolymère selon la revendication 1, dans laquelle le polymère à base de siloxane contenant au moins un groupe fonctionnel silane (Si-H) présente un poids moléculaire moyen en nombre de 200 à 4 000.
 
4. Composition de photopolymère selon la revendication 1, dans laquelle le polyol (méth)acrylique présente une structure dans laquelle deux groupes hydroxy ou plus sont liés à une chaîne principale ou à une chaîne latérale du polymère à base de (méth)acrylate, et
dans laquelle le polyol (méth)acrylique présente un poids moléculaire moyen en poids de 200 000 à 1 000 000.
 
5. Composition de photopolymère selon la revendication 1, dans laquelle le polyol (méth)acrylique présente un équivalent en groupe hydroxy de 500 g/équivalent à 2 500 g/équivalent.
 
6. Composition de photopolymère selon la revendication 1, dans laquelle la matrice polymère inclut un réactif d'hydrosilylation entre le polymère à base de siloxane contenant au moins un groupe fonctionnel silane (Si-H) et le polyol (méth)acrylique.
 
7. Composition de photopolymère selon la revendication 1, dans laquelle le monomère photoréactif inclut un monomère de (méth)acrylate polyfonctionnel ou un monomère de (méth)acrylate monofonctionnel.
 
8. Composition de photopolymère selon la revendication 1, dans laquelle le monomère photoréactif présente un indice de réfraction de 1,5 ou plus.
 
9. Composition de photopolymère selon la revendication 1, dans laquelle la composition de photopolymère comprend en outre un composé à base de fluor.
 
10. Composition de photopolymère selon la revendication 9, dans laquelle le composé à base de fluor comprend au moins un groupe fonctionnel sélectionné dans le groupe consistant en un groupe éther, un groupe ester et un groupe amide, et au moins deux groupes difluorométhylène.
 
11. Composition de photopolymère selon la revendication 9, dans laquelle le composé à base de fluor présente un indice de réfraction inférieur à 1,45.
 
12. Composition de photopolymère selon la revendication 1, dans laquelle la matrice polymère présente un indice de réfraction de 1,46 à 1,53.
 
13. Support d'enregistrement d'hologramme comprenant la composition de photopolymère selon la revendication 1.
 
14. Élément optique comprenant le support d'enregistrement d'hologramme selon la revendication 13.
 
15. Procédé d'enregistrement holographique comprenant :
la polymérisation sélective de monomères photoréactifs contenus dans la composition de photopolymère selon la revendication 1 en utilisant une source de lumière cohérente.
 






Cited references

REFERENCES CITED IN THE DESCRIPTION



This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

Patent documents cited in the description