(19)
(11)EP 3 955 041 A1

(12)EUROPEAN PATENT APPLICATION

(43)Date of publication:
16.02.2022 Bulletin 2022/07

(21)Application number: 21185606.7

(22)Date of filing:  14.07.2021
(51)International Patent Classification (IPC): 
G02B 6/44(2006.01)
G02B 6/02(2006.01)
(52)Cooperative Patent Classification (CPC):
G02B 6/4434; G02B 6/4438; G02B 6/443; G02B 6/4494; G02B 6/02395; G02B 6/441
(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR
Designated Extension States:
BA ME
Designated Validation States:
KH MA MD TN

(30)Priority: 13.08.2020 CN 202010810380

(71)Applicant: Yangtze Optical Fibre and Cable Joint Stock Limited Company
East Lake High-tech Development Zone Wuhan Hubei 430073 (CN)

(72)Inventors:
  • HU, Haifeng
    Wuhan, Hubei, 430073 (CN)
  • RUAN, Yunfang
    Wuhan, Hubei, 430073 (CN)
  • YANG, Xiangrong
    Wuhan, Hubei, 430073 (CN)
  • QI, Lin
    Wuhan, Hubei, 430073 (CN)
  • ZHENG, Lei
    Wuhan, Hubei, 430073 (CN)

(74)Representative: Laufhütte, Dieter 
Lorenz Seidler Gossel Rechtsanwälte Patentanwälte Partnerschaft mbB Widenmayerstraße 23
80538 München
80538 München (DE)

  


(54)AIR-BLOWN OPTICAL FIBER CABLE WITH FLEXIBLE TUBES


(57) Disclosed is an air-blown optical fiber cable with flexible tubes. The cable includes a cable core and an outer sheath that covers the cable core. The cable core is a stranded cable core and includes a central strength member and loose tubes that are stranded on the periphery of the central strength member. Optical communication units are sheathed in the loose tubes, characterized in that the loose tubes are made of a flexible coating material, the elasticity modulus of the flexible coating material is 100-700 MPa, and the outermost layer is the outer sheath. The optical fiber cable in the present invention is simple in structure, and has a small diameter, light weight, high optical fiber density and great air-blown installation performance. The loose tubes are made of the flexible coating material, which has great flexibility, is easily bent but not broken, and can realize coiled reservation with a small kink radius in a distribution box, such that optical fibers that are split and reserved in a coiled manner can be better protected and there is no need to break the optical fibers, thereby greatly facilitating the splitting and splicing of the optical fibers and improving the construction efficiency.




Description

TECHNICAL FIELD



[0001] The present invention relates to an air-blown optical fiber cable with flexible tubes, and falls within the technical field of optical-electric transmission.

BACKGROUND ART



[0002] An air-blown micro cable is an optical fiber cable that can be installed by means of air blowing. It has the advantages of high optical fiber density, small diameter, light weight and high air-blown installation efficiency, and is widely applied in a backbone network, a local area network, an access network, etc. The air-blown micro cable having a larger number of optical fibers is generally of a stranded structure. The cable core of the air blown micro cable is formed by means of SZ stranding a center strength member and loose tubes and then binding same by a wrapping yarn, and a sheath is then extrusion molded on the cable core. Loose tubes are made of a secondary coating material, the secondary coating material is PBT, and the elasticity modulus thereof is higher and is about 2200 MPa.

[0003] During the construction of the air-blown micro cable, when optical fibers need coiled reservation after splicing and splitting in a splice box or a distribution box, as for an existing air-blown micro cable, PBT loose tubes cannot be directly reserved in a coiled manner, because the modulus of the material used for the PBT loose tubes is greater whereas the space of the distribution box is smaller, and if the tubes are directly reserved in the coiled manner, the tubes would be bent and optical fibers would be damaged, affecting the transmission performance of the optical fibers. Hence, it is necessary to break the optical fibers, add flexible tube protection and then fuse the optical fibers for coiled reservation. If optical fibers are not broken and no flexible tube protection is added, tube kinking still easily occurs in use, resulting in the optical fibers being broken, thereby affecting the transmission performance of the optical fiber.

[0004] The optical fiber density affects a pipeline occupation fee and a construction efficiency, and therefore, increasing the optical fiber density is an industry development target. Under the condition of an unchanged fiber count, the method for reducing the diameter of an optical fiber cable mainly comprises reducing the diameter of an optical fiber, reducing the diameter of a tube and reducing the wall thickness of a sheath. However, reducing the diameter of the optical fiber and reducing the diameter of the tube would both bring about the problem of the increase of optical fiber attenuation, and the tubes are more easily bent.

SUMMARY OF THE INVENTION



[0005] Aiming at the above-mentioned defects in the prior art, the technical problem to be solved by the present invention is to provide an air-blown optical fiber cable with flexible tubes. The cable has the advantages of high optical fiber density, small diameter, light weight, etc. Furthermore, the split loose tubes are easily bent but not broken, such that coiled reservation with a small radius by means of kinking can be realized, thereby improving the construction efficiency.

[0006] In order to solve the above-mentioned problems, the technical solution used in the present invention is: a cable core and an outer sheath that covers the cable core are included, with the cable core being a stranded cable core. The cable core comprises a central strength member and loose tubes that are stranded on the periphery of the central strength member. Optical communication units are sheathed in the loose tubes, characterized in that the loose tubes are made of a flexible secondary-coating material, the elasticity modulus of the flexible coating material is 100-700 MPa, and the outermost layer is the outer sheath.

[0007] According to the above-mentioned solution, the elasticity modulus of the flexible coating material is 410-590 MPa, which not only ensures the flexibility of the loose tubes, but also has a great comprehensive performance including machining and mechanical performance, thereby reducing the wall thickness of the tubes to the greatest extent, improving the optical fiber density.

[0008] According to the above-mentioned solution, the flexible coating material may be a thermoplastic polyester elastomer (TPEE), a thermoplastic polyurethane elastomer (TPU) or thermoplastic vulcanized rubber (TPV).

[0009] According to the above-mentioned solution, the shrinkage rate of the loose tubes is between 0 and 0.5%, which can reduce the microbend of optical fibers in the loose tubes, so as to ensure the transmission performance of the optical fibers in the loose tubes when temperature changes.

[0010] According to the above-mentioned solution, the one-sided wall thickness of the loose sleeve is 0.1-0.25 mm, the diameter of a 12F/T (12 fibers per tube) loose tube may be reduced to 1.15 mm, the diameter of a 24F/T (24 fibers per tube) loose tube may be reduced to 1.55 mm, the occupying ratio of optical fibers in each loose tube is greater than or equal to 50%, and the optical fiber density in the optical fiber cable is greater than or equal to 3 F/mm2.

[0011] According to the above-mentioned solution, the minimum kink diameter of the loose tube is five times the diameter D of the loose tube, i.e. the minimum kink diameter is 5D.

[0012] According to the above-mentioned solution, the optical communication unit is an optical fiber, an optical fiber strip or an optical fiber bundle.

[0013] According to the above-mentioned solution, the optical fiber is a bending-resistance single-mode optical fiber, and the outer surface of the optical fiber is coated with inner and outer coatings, with the elasticity modulus of the inner coating being less than or equal to 1 MPa, and the elasticity modulus of the outer coating being less than or equal to 1000 MPa (at a test temperature of 25°C).

[0014] According to the above-mentioned solution, the microbend sensitivity of the bending-resistance single-mode optical fiber is less than or equal to 2 dB/km@1550 nm.

[0015] According to the above-mentioned solution, the additional attenuation of the bending-resistance single-mode optical fiber at a temperature of -30°C to +70°C is less than or equal to 0.05 dB/km@1550 nm.

[0016] According to the above-mentioned solution, the outer diameter D of the loose tube is 1.1-2.0 mm, and the inner diameter of the loose tube is 0.8-1.6 mm, and the loose tubes are filled with a water-blocking material.

[0017] According to the above-mentioned solution, the outer sheath is made of HDPE, MDPE, LDPE, PA11 or PA12, and the one-sided wall thickness of the outer sheath is 0.3-0.6 mm.

[0018] The beneficial effects of the present invention lie in: 1. the optical fiber cable is simple in structure, and has a small diameter, light weight, high optical fiber density and great air-blown installation performance; 2. the loose tubes are made of the flexible coating material, which has great flexibility, is easily bent but not broken, almost reaching the minimum kink radius of the optical fiber without being bent, and can realize coiled reservation with a small kink radius in a distribution box, such that the split optical fibers that are reserved in a coiled manner can be better protected and there is no need to break the optical fibers, thereby greatly facilitating the splitting and splicing of the optical fibers, improving the construction efficiency; 3. the elasticity modulus of the flexible coating material is 100-700 MPa, and the tube material is flexible and is easily bent, thus the wall thickness can be smaller without the occurrence of bending, such that the reduction of the tube diameter and the increase of the optical fiber density are achieved, and meanwhile the loose tubes having certain strength can be ensured, thereby protecting the optical fibers in the loose tubes and preventing tube surfaces from having marks caused by the wrapping yarn; 4. the optical fiber is a bending-resistance single-mode optical fiber, which can further improve the bending performance of the present invention. In the present invention, by means of the preferred moduli of inner and outer coatings of the optical fibers and the preferred secondary coating material, the diameter of the optical fibers and the diameter of the tubes are reduced to the greatest extent, and meanwhile the optical fiber cable having excellent transmission performance at a temperature of -30°C to +70°C can also be ensured; 5. the outer sheath has higher strength and rigidity, so as to form an optical fiber cable structure that is hard outside and flexible inside, which can facilitate air-blowing installation and has a great cable protection performance.

BRIEF DESCRIPTION OF THE DRAWINGS



[0019] Figure 1 is a radial cross-sectional view of an embodiment of the present invention.

DETAILED DESCRIPTION OF EMBODIMENTS



[0020] The present invention will be further described below in conjunction with the accompanying drawings and embodiments.

[0021] The embodiment of the present invention is as shown in figure 1. The embodiment comprises an outer sheath 1 and a cable core covered in the outer sheath. The cable core comprises a non-metallic central strength member 5 and loose tubes 2 that are stranded on the periphery of the central strength member. The loose tubes are bound by a wrapping yarn after SZ stranding. Optical communication units 3 are sheathed in the loose tubes, and the loose tubes are also filled with a water-blocking material 4. The water-blocking material is water-blocking powder or water-blocking factice. The loose tubes are formed by means of extrusion molding a material such as TPEE, TPU or TPV at a temperature of 200°C to 240°C, and the elasticity modulus of the tubes is about 450 MPa. The optical communication unit 3 is a bending-resistance single-mode optical fiber, and the outer surface of the optical fiber is coated with inner and outer coatings, with the elasticity modulus of the inner coating being 0.8 MPa, and the elasticity modulus of the outer coating being 900 MPa (at a test temperature of 25°C). There are 12 or 24 optical fibers in each flexible tube. The occupying ratio of the optical fibers in the loose tubes goes beyond 50%. The loose tubes would not be bent when the kink diameter of the tube is 5D. A water-blocking yarn 6 may also be provided in the cable core. The outermost layer of the optical fiber cable is the outer sheath, the outer sheath is made of HDPE, MDPE, LDPE, PA11 or PA12, and the outer sheath has higher strength and rigidity, so as to form an optical fiber cable structure that is hard outside and flexible inside. In order to facilitate opening of a cable, a cable opening string 7 is provided between the cable core and the outer sheath. Table 1 is a parameter list of five embodiments of the present invention, and all the optical fiber densities are more than 3 F/mm2.

[0022] In the present invention, by means of the preferred moduli of inner and outer coatings of the optical fibers and the preferred secondary coating material for the loose tubes, the diameter of the optical fibers and the diameter of the tubes are reduced to the greatest extent, and meanwhile the optical fibers in the optical fiber cable having excellent transmission performance at a temperature of -30°C to +70°C can also be ensured.
Table 1
Structure parameterEmbodiment 1Embodiment 2Embodiment 3Embodiment 4Embodiment 5
Optical fiber count 72 144 144 72 144
Optical fiber diameter (µm) 195 195 195 245 245
Outer diameter D (mm) of loose tube 1.15 1.55 1.65 1.42 1.95
Inner diameter (mm) of loose tube 0.85 1.25 1.25 1.12 1.60
Kink diameter of loose tube is 5D No kink No kink No kink No kink No kink
Loose tube material TPEE TPEE TPU TPEE TPV
elasticity modulus (MPa) of loose tube material 570MPa 430MPa 180MPa 510MPa 290MPa
Diameter (mm) of strength member 1.2 1.6 1.8 1.5 2.0
Optical fiber ratio 63.2% 58.4% 58.4% 57.4% 56.3%
Outer diameter (mm) of optical fiber cable 4.3 5.5 5.9 5.1 6.7
Optical fiber density (F/mm2) 5.0 6.1 5.3 3.5 4.1
Working temperatur e -30 °C to +70°C -30 °C to +70°C -30°C to +70°C -30 °C to +70°C -30 °C to +70°C



Claims

1. An air-blown optical fiber cable with flexible tubes, the cable comprising: a cable core and an outer sheath that covers the cable core, with the cable core being a stranded cable core, the cable core comprising a central strength member and loose tubes that are stranded on the periphery of the central strength member, optical communication units being sheathed in the loose tubes, characterized in that the loose tubes are made of a flexible coating material, an elasticity modulus of the flexible coating material is 100-700 MPa, and the outermost layer is the outer sheath.
 
2. The air-blown optical fiber cable with flexible tubes of claim 1, characterized in that the elasticity modulus of the flexible coating material is 410-590 MPa.
 
3. The air-blown optical fiber cable with flexible tubes of claim 1 or 2, characterized in that the flexible coating material is TPEE, TPU or TPV.
 
4. The air-blown optical fiber cable with flexible tubes of claim 1 or 2, characterized in that the one-sided wall thickness of the loose sleeve is 0.1-0.25 mm, the occupying ratio of optical fibers in the loose tubes is greater than or equal to 50%, an optical fiber density in the optical fiber cable is greater than or equal to 3 F/mm2, and the shrinkage rate of the loose tubes is between 0 and 0.5%.
 
5. The air-blown optical fiber cable with flexible tubes of claim 1 or 2, characterized in that the outer diameter D of the loose tube is 1.1-2.0 mm, and the inner diameter of the loose tube is 0.8-1.6 mm, and the minimum kink diameter of the loose tube is five times the diameter D of the loose tube, i.e. the minimum kink diameter is 5D.
 
6. The air-blown optical fiber cable with flexible tubes of claim 1 or 2, characterized in that the optical communication unit is an optical fiber, an optical fiber strip or an optical fiber bundle.
 
7. The air-blown optical fiber cable with flexible tubes of claim 6, characterized in that the optical fiber is a kinking-resistance single-mode optical fiber, and an outer surface of the optical fiber is coated with inner and outer coatings, with an elasticity modulus of the inner coating being less than or equal to 1 MPa, and an elasticity modulus of the outer coating being less than or equal to 1000 MPa.
 
8. The air-blown optical fiber cable with flexible tubes of claim 7, characterized in that a microbend sensitivity of the bending-resistance single-mode optical fiber is less than or equal to 2 dB/km@1550 nm, and an additional attenuation of the bending-resistance single-mode optical fiber at -30°C to +70°C is less than or equal to 0.05 dB/km@1550 nm.
 
9. The air-blown optical fiber cable with flexible tubes of claim 1 or 2, characterized in that the outer diameter D of the loose tube is 1.0-2.0 mm, and the inner diameter of the loose tube is 0.8-1.6 mm, and the loose tubes are filled with a water-blocking material.
 
10. The air-blown optical fiber cable with flexible tubes of claim 1 or 2, characterized in that the outer sheath is made of HDPE, MDPE, LDPE, PA11 or PA12.
 