(19)
(11)EP 4 053 958 A1

(12)EUROPEAN PATENT APPLICATION
published in accordance with Art. 153(4) EPC

(43)Date of publication:
07.09.2022 Bulletin 2022/36

(21)Application number: 19950266.7

(22)Date of filing:  11.12.2019
(51)International Patent Classification (IPC): 
H01M 10/0562(2010.01)
(52)Cooperative Patent Classification (CPC):
Y02E 60/10; Y02P 70/50
(86)International application number:
PCT/CN2019/124604
(87)International publication number:
WO 2021/082200 (06.05.2021 Gazette  2021/18)
(84)Designated Contracting States:
AL AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HR HU IE IS IT LI LT LU LV MC MK MT NL NO PL PT RO RS SE SI SK SM TR
Designated Extension States:
BA ME
Designated Validation States:
KH MA MD TN

(30)Priority: 01.11.2019 CN 201911061250

(71)Applicant: Ningde Amperex Technology Limited
Ningde, Fujian 352100 (CN)

(72)Inventors:
  • ZHOU, Molin
    Ningde, Fujian 352100 (CN)
  • GU, Feng
    Ningde, Fujian 352100 (CN)
  • JIANG, Xin
    Ningde, Fujian 352100 (CN)
  • XU, Leimin
    Ningde, Fujian 352100 (CN)

(74)Representative: Klunker IP Patentanwälte PartG mbB 
Destouchesstraße 68
80796 München
80796 München (DE)

  


(54)PHOSPHOROUS-FREE SULFIDE SOLID-STATE ELECTROLYTE


(57) The application relates to a solid electrolyte material and an electrochemical device including the same. A general chemical formula of the solid electrolyte material according to the application is Li2+xM2+xM'1-xS6, where M is at least one of Al, Ga or In, M' is at least one of Si or Ge, and 0<x≤0.5. The solid electrolyte material according to the application is simple in composition, contains no phosphorus sensitive to water, and has good Li+ conductivity at the same time. The material is a promising solid electrolyte material.




Description

Field



[0001] The invention relates to a phosphorus-free sulfide solid electrolyte.

Background



[0002] As the electronic technique rapidly develops, electronic equipment such as phones, notebook computers, vidicon and electric tools increases, and people's demand for energy storage power is getting higher. It is urgent to develop secondary batteries with high capacity, long life, and good safety performance. In contrast with lead-acid, nickel-cadmium, nickel-hydrogen batteries, or the like, lithium-ion batteries are characterized in high energy density, high power density, long life, good safety, low self-discharge rate, and wide temperature adaptation range, thereby being most widely used. However, it is required to use a flammable organic solution as an electrolyte for traditional lithium-ion batteries, so a great potential safety hazard exists. Particularly, for lithium-ion batteries with higher energy density, although measures can be taken to improve material, electrode, cell, module, power management, heat management, systematic design, or the like, battery safety still remains prominent and it is hard to completely avoid thermal runaway. In recent years, vicious battery explosion accidents sometimes happen. Therefore, it is especially important to explore lithium-ion secondary batteries with good safety performance.

[0003] In order to solve the above safety problem fundamentally, it is a good scheme to replace an organic electrolyte solution with a solid electrolyte. The solid electrolyte is incombustible, non-volatile, and free from corrosion and liquid leakage, therefore, an all-solid-state battery assembled with the solid electrolyte has extremely high safety. In addition, an all-solid-state battery is characterized in long life and high theoretical energy density. During the use of lithium-ion batteries with the organic electrolyte solution, since an SEI film gets broken and is generated repeatedly during the cyclic process, resulting in accelerating the degradation of battery capacity, and lots of side effects during the cyclic process also have a severe impact on the service life of batteries, the solid electrolyte can solve this problem. In another aspect, most of the solid electrolytes are featured with good mechanical strength and can inhibit lithium dendrites effectively. This can also significantly improve the cycle performance and service life of batteries. In addition, since the solid electrolyte generally has a wide electrochemical window, it can match with more high-voltage positive electrodes; moreover, the all-solid-state battery can greatly simplify the battery thermal management system and can greatly improve the energy density.

[0004] In recent years, researchers have conducted a lot of exploratory work on the solid electrolyte. In summary, there are three types of common solid electrolytes at present: polymer-type, oxide-type and sulfide-type. The concept of polymer solid electrolyte was firstly put forward by Armand in 1978. The polymer solid electrolyte includes a polymer and a lithium salt. Lithium ions and polar groups in a polymer chain are complexing with each other. Under the action of an external electric field, the flexibility of the polymer chain is used for the directional migration of lithium ions. Common polymer solid electrolytes include PEO-based, PPO-based, PAN-based, PMMA-based, and PVDF-based electrolytes, or the like. These kinds of electrolytes have light mass, good viscoelasticity, and good mechanical processability, but very low ionic conductivity has a severe impact on the high-rate charge and discharge capacity of batteries. Chemical copolymerization, grafting, or the like are usually used to reduce the crystallinity of a polymer matrix and improve the ionic conductivity, but improved room temperature ionic conductivity is still very low. Oxide solid electrolytes include Perovskite-type (e.g., Li3xLa2/3-xTiO3), Anti-Perovskite-type (e.g., Li3OCl), NASICON-type (e.g., Li1+xAlxTi2-x(PO4)3), Garnet-type (e.g., Li7La3Zr2O12) electrolytes, or the like. These kinds of electrolytes generally have good chemical stability and can exist in the air stably, but the ionic conductivity is relatively low, the grain boundary resistance is great, and the compatibility with an electrode is poor. Compared with two types of solid electrolytes aforesaid, the sulfide solid electrolyte is characterized in high ionic conductivity, low grain boundary resistance, good electrochemical stability, or the like, receives wide attention from researchers, and is the material that is most promising for scale application. In the sulfide materials, Li2S-SiS2 system is a type of solid electrolyte that is first studied. It is reported that (Hayashi et al., "Characterization of Li2S-SiS2-Li3MO3 M=B, Al, Ga and In) oxysulfide glasses and their application to solid state lithium secondary batteries", 2002, Solid State Ionics, Volume 152-153, Pages 285-290): Li3PO4, LiSiO4, Li3BO3, and Li3AlO3 with glassy-state Li2S-SiS2 can significantly improve the conductivity and inhibit crystallization of materials. In 2001, Tatsumisago, et al. (Tatsumisago et al., "Solid state lithium secondary batteries using an amorphous solid electrolyte in the system (100-x)(0.6Li2S-0.4SiS2)·xLi4SiO4 obtained by mechanochemical synthesis", 2001, Solid State Ionics, Volume 140, Pages 83-87) used mechanical ball milling instead of melt quenching to prepare a glassy-state solid electrolyte (100-x)(0.6Li2S-0.4SiS2)xLi4SiO4, and exhaustively discussed the impact of milling time on the formation of a glassy state and the performance of all-solid-state batteries. Subsequently, Tatsumisago, et al. (Tatsumisago et al., "New, Highly Ion-Conductive Crystals Precipitated from Li2S-P2S5 Glasses", 2005, Advanced Materials, Volume 17, Pages 918-921) reported for the first time in 2005 the preparation of sulfur phosphorus compound material 70Li2S-30P2S5 by energetic ball milling, with the room temperature ionic conductivity up to 3.2×10-3 S/cm, thereby starting a trend of preparing glass-ceramic sulfur phosphorus compound materials by energetic ball milling. In 2011, Tokyo Institute of Technology and Toyota Motor Corporation made a breakthrough (Kamaya et al., "A lithium superionic conductor", 2011, Nature Materials, Volume 10, Pages 682-686). They jointly reported a crystal sulfur phosphide electrolyte with a lithium-ion three-dimensional diffusion channel, Li10GeP2S12 (LGPS), on nature materials, a top international journal of materials science. The room temperature ionic conductivity reaches 1.2×10-2 S/cm, which even can be comparable to the ionic conductivity of common carbonate electrolyte solution, thereby further attracting global attention to sulfur phosphorus compound materials. However, in another aspect, sulfur phosphorus compounds are generally sensitive to water in the air, and can easily generate malodorous H2S gas due to water absorption during the processing in a conventional environment. The gas is harmful to the environment and processing personnel. According to the Hard-Soft Acid-Base theory, P5+ in the sulfur phosphorus compounds is hard acid, and compared with S2-, O2- in water is harder base. Hard acid reacts with hard base firstly, thus sulfides with phosphorus may deteriorate easily when they absorb water. In view of this, exploration of some novel sulfide solid electrolyte materials with good Li+ conductivity and without phosphorus is of great importance.

Summary



[0005] The application provides a novel sulfide solid electrolyte material and an electrochemical device comprising the solid electrolyte material. The solid electrolyte material is simple in composition, contains no phosphorus sensitive to water, and has good Li+ conductivity at the same time. It is a promising solid electrolyte material.

[0006] A first purpose of the application is to disclose a novel sulfide solid electrolyte material.

[0007] A second purpose of the application is to disclose the crystallographic characteristics, structural information, XRD spectrogram, PBE band gap, Li+ migration path, and migration barrier of the solid electrolyte material.

[0008] Specifically, the application discloses a novel sulfide solid electrolyte material, represented by a general chemical formula Li2+xM2+xM'1-xS6, wherein M is at least one of Al, Ga or In, M' is at least one of Si or Ge, and 0<x≤0.5.

[0009] First, the Li2+xM2+xM'1-xS6 material has diamond-like structural characteristics. In the structure, coordination of M3+ (e.g., Al3+) and M'4+ (e.g., Si4+) with S2- forms tetrahedrons. All connected corner-sharing tetrahedrons form a three-dimensional network, and Li+ is filled in the gap between tetrahedrons.

[0010] Next, the application discloses XRD spectrogram characteristics of Li2+xM2+xM'1-xS6. In an XRD spectrogram, strong diffraction peaks may occur at about 14.5°±3°, 15.5°±3°, 17°±3°, 25.5°±3°, 31.5°±3°, 53.0°±3°, or the like.

[0011] Then, by taking Li2+xAl2+xSi1-xS6 as a demonstrative example and using VASP software (Hafner research group of University of Vienna, Vienna Ab-initio Simulation Package) for calculation, a PBE band gap of the Li2+xAl2+xSi1-xS6 material is no less than 2.8eV It is well-known that exchange-correlation functional in the form of PBE may severely underestimate the optical band gap of insulators and semiconductors (refer to the patent document, publication number: CN106684437A), and the intrinsic band gap of the Li2+xAl2+xSi1-xS6 material should be far beyond 2.8eV In 2012, Yin Wenlong, et al. (Yin et al., "Synthesis, Structure, and Properties of Li2In2MQ6 (M = Si, Ge; Q = S, Se): A New Series of IR Nonlinear Optical Materials", 2012, Inorganic Chemistry, Volume 51, Pages 5839-5843) firstly reported the experimental band gap of Li2In2SiS6 is about 3.61eV In the application, Li2In2SiS6 is calculated with the same parameters, and the PBE band gap is 2.08eV It can be seen from this that the intrinsic band gap of Li2+xAl2+xSi1-xS6 should exceed about 4.3eV

[0012] Finally, by taking Li2+xAl2+xSi1-xS6 as an example, the application exhaustively evaluates lithium-ion migration paths and migration barriers of Li2.125Al2.125Si0.875S6, Li2.25Al2.25Si0.75S6, and Li2.5Al2.5Si0.5S6.

[0013] Compared with the prior art, the invention has the following beneficial effects:
The invention provides a novel sulfide solid electrolyte material Li2+xM2+xM'1-xS6, with a diamond-like structure, where coordination of M3+ and M'4+ with four S2- forms [MS4] and [M'S4] tetrahedrons. All corner-sharing tetrahedrons are connected, and Li+ is filled in the gap between tetrahedrons.

[0014] This kind of material has a wide optical band gap. Particularly, for the Li2+xAl2+xSi1-xS6 material, the intrinsic band gap is no less than about 4.3eV, and Li+ migration barrier is no greater than 0.45 eV Overall, this kind of material has a wide band gap and a low Li+ conduction barrier, indicating that it has strong Li+ conducting power and is a novel fast lithium-ion conductor material, with a good application prospect.

[0015] More importantly, compared with sulfur phosphorus family solid electrolytes, according to the Hard-Soft Acid-Base theory, this kind of material does not contain hard acid P5+ and should have good stability. At the same time, it can be seen from the structure that all tetrahedrons are corner-sharing connected, groups are arranged compactly with a little gap, and the structural stability is good.

[0016] In some embodiments, the general chemical formula of the solid electrolyte material is Li2+xM2+xM'1-xS6, wherein M is at least one of Ga or In, M' is at least one of Si or Ge, and 0<x≤0.5.

[0017] In some embodiments, the general chemical formula of the solid electrolyte material is Li2+xAl2+xSi1-xS6, wherein 0<x≤0.5.

[0018] In some embodiments, lattice parameters of the solid electrolyte material are about a=13.0±2.0Å, b=8.0±2.0Å, c=13.0±2.0Å, α=90.0°±5°, β=110.0°±10°, and γ=90.0°±5°.

[0019] In some embodiments, lattice parameters of the solid electrolyte material are about a=12.0±1.0Å, b=7.0±1.0Å, c=12.0±1.0Å, α=90.0°±5°, β=105°±5°, and γ=90.0°±5°.

[0020] In some embodiments, coordination of M3+ (Al3+) and M'4+ (Si4+) in the solid electrolyte material structure with S2- forms [MS4] ([AlS4]) and [M'S4] ([SiS4]). All corner-sharing tetrahedrons are connected, and Li+ is filled in the gap between tetrahedrons.

[0021] In some embodiments, strong diffraction peaks may occur at about 14.5°±3°, 15.5°±3°, 17°±3°, 25.5°±3°, 31.5°±3°, 53.0°±3°, or the like in XRD spectrogram of the solid electrolyte material.

[0022] In some embodiments, Li+ migration barrier of the solid electrolyte material is no greater than about 0.45 eV.

[0023] In some embodiments, the PBE band gap of the solid electrolyte material is no less than about 2.80 eV.

[0024] Unprecedented attention is paid to the safety of batteries. The solid electrolyte material can replace the organic electrolyte solution and is applied to novel lithium-ion batteries. The safety risks arising from thermal runaway are thermal runaways in principle. The invention provides a type of novel sulfide solid electrolyte, with great application potential. The solution is of high innovation and practical value, and can promote the further application of sulfide solid electrolyte.

Brief Description of the Figures



[0025] 

Fig. 1 illustrates a lattice structure and a Li+ migration path of Li2.125Al2.125Si0.875S6.

Fig. 2 illustrates an XRD spectrogram of Li2.125Al2.125Si0.875S6.

Fig. 3 illustrates a state density of Li2.125Al2.125Si0.875S6.

Fig. 4 illustrates a gap Li+ migration barrier of Li2.125Al2.125Si0.875S6.

Fig. 5 illustrates a lattice structure and a Li+ migration path of Li2.25Al2.25Si0.75S6

Fig. 6 illustrates an XRD spectrogram of Li2.25Al2.25Si0.75S6.

Fig. 7 illustrates a state density of Li2.25Al2.25Si0.75S6.

Fig. 8 illustrates a gap Li+ migration barrier of Li2.25Al2.25Si0.75S6.

Fig. 9 illustrates a lattice structure and a Li+ migration path of Li2.5Al2.5Si0.5S6.

Fig. 10 illustrates an XRD spectrogram of Li2.5Al2.5Si0.5S6.

Fig. 11 illustrates a state density of Li2.5Al2.5Si0.5S6.

Fig. 12 illustrates a gap Li+ migration barrier of Li2.5Al2.5Si0.5S6.


Detailed Description of the Embodiments



[0026] Exemplary embodiments of the invention will be described below by reference to the figures. The exemplary embodiments are the interpretation of the invention, instead of limiting the scope of protection of the claims of the invention. The scope of the invention is only defined by the claims attached and equivalents thereof.

I. Solid Electrolyte Material



[0027] In general, inorganic solid electrolyte material usually comprises a stable ion skeleton and a moveable ion (e.g., Li+). Compared with oxide solid electrolytes, the ionic radius of S2- in the sulfide solid electrolytes is much greater than O2-, enabling a much larger movable space for Li+ between skeletons; at the same time, the nucleus of S2- has a lower constraint to the ambient electron cloud, making that the electron cloud is more easily polarized and the charge distribution may cooperate with Li+ more easily during the movement of Li+ to form deformation and reduce the force on lithium-ion, thereby reducing the migration barrier of Li+. On the basis of fully understanding the structural characteristics of sulfide, by replacing with congeners, using part of M3+ instead of M'4+, and introducing the thinking of gap Li+, the inventor finds a novel sulfide solid electrolyte, Li2+xM2+xM'1-xS6. This kind of material does not contain phosphorus, and has a low Li+ migration barrier, with great application potential.

[0028] The embodiments of the application provide a solid electrolyte material. The general chemical formula of the material is Li2+xM2+xM'1-xS6, wherein M is at least one of Al, Ga or In, M' is at least one of Si or Ge, and 0<x≤0.5.

1. Structural characteristics



[0029] The application firstly discloses the structural characteristics of the Li2+xM2+xM'1-xS6 material, which has diamond-like structural characteristics. Lattice parameters are around a=13.0±2.0Å, b=8.0±2.0Å, c=13.0±2.0Å, α=90.0°±5°, β=110.0°±10°, and γ=90.0°±5°. For the Li2+xAl2+xSi1-xS6 in the application, lattice parameters are about a=12.0±1.0Å, b=7.0±1.0Å, c=12.0±1.0Å, α=90.0°±5°, β=105°±5°, and γ=90.0°±5°. Specifically, for a Li2.125Al2.125Si0.875S6 material, lattice parameters are about a=11.7, b=7.2, c=11.6, α=90.3°, β=107.9°, and γ=89.7°; for a Li2.25Al2.25Si0.75S6 material, lattice parameters are about a=11.7, b=7.3, c=11.7, α=89.7°, β=107.5°, and γ=90.1°; for a Li2.5Al2.5Si0.5S6 material, lattice parameters are about a=12.0, b=7.6, c=11.8, α=88.5°, β=102.9°, and γ=90.2°. In the structure, coordination of M3+and M'4+ with four S2-forms tetrahedrons. All connected corner-sharing tetrahedrons form a three-dimensional network, and Li+ is filled in the gap between tetrahedrons. It can be seen from the composition and structural characteristics of elements that Li2+xM2+xM'1-xS6 has good stability.

2. XRD spectrogram



[0030] The application also discloses characteristics of an XRD spectrogram of the Li2+xM2+xM'1-xS6 material. As shown in Figs. 2, 6 and 10, in the XRD spectrogram, strong diffraction peaks may occur at about 14.5°±3°, 15.5°±3°, 17°±3°, 25.5°±3°, 31.5°±3°, 53.0°±3°, or the like. Specifically, for the Li2.125Al2.125Si0.875S6 material, strong diffraction peaks may occur at about 14.6°, 16.0°, 18.0°, 26.0°, 31.3°, and 53.5°; for the Li2.25Al2.25Si0.75S6 material, strong diffraction peaks may occur at about 14.6°, 16.0°, 17.7°, 26.0°, 31.1°, and 53.4°; for the Li2.5Al2.5Si0.5S6 material, strong diffraction peaks may occur at about 14.0°, 15.4°, 16.8°, 25.4°, 30.8°, and 52.1°.

3. Lithium-ion transport characteristics



[0031] Materials that can be used as solid electrolytes must meet the conditions of electronic insulation and ionic conductivity. It is well-known that electronic insulation is greatly related to the optical band gap of materials. Therefore, the invention uses PBE exchange-correlation functional for calculating the total density of states of several Li2+xM2+xM'1-xS6 materials (taking Li2.125Al2.125Si0.875S6, Li2.25Al2.25Si0.75S6, and Li2.5Al2.5Si0.5S6 as demonstrative examples). As shown in Figs. 3, 7, and 11, the PBE band gap of the Li2+xAl2+xSi1-xS6 material is no less than 2.80 eV. It is well-known that exchange-correlation functional in the form of PBE may severely underestimate the optical band gap of insulators and semiconductors (refer to the patent document, publication number: CN106684437A), and the intrinsic band gap of the Li2+xAl2+xSi1-xS6 material should be far beyond 2.8eV. In 2012, Yin Wenlong, et al. (Yin et al., "Synthesis, Structure, and Properties of Li2In2MQ6 (M = Si, Ge; Q = S, Se): A New Series of IR Nonlinear Optical Materials", 2012, Inorganic Chemistry, Volume 51, Pages 5839-5843) firstly reported the experimental band gap of Li2In2SiS6 is about 3.61eV. In the invention, Li2In2SiS6 is calculated with the same parameters, and the PBE band gap is 2.08eV. It can be seen from this that the intrinsic band gap of Li2+xAl2+xSi1-xS6 should exceed about 4.3eV. It is an insulator with a wide energy gap, and is characterized in electrical insulation. Wide energy gap width also indicates the low bonding-state energy, i.e., high oxidation potential, and indicates that the structure has a wide electrochemical window at the same time, conducive to match with high-voltage positive electrode materials.

[0032] Lithium-ion transport characteristics are the most critical characteristics of solid electrolytes. Therefore, the inventor calculates Li+ migration path and migration barrier of the Li2+xM2+xM'1-xS6 material by using First Principle and VASP software (Hafner research group of University of Vienna, Vienna Ab-initio Simulation Package).

[0033] It's understandable that in the Li2+xM2+xM'1-xS6 material, M and M' can be arbitrarily selected from Al, Ga, In and Si, Ge respectively. In order to describe clearly and simply, the invention takes Li2+xAl2+xSi1-xS6 as an example to discuss, and exhaustively calculates Li+ migration path and migration barrier of Li2.125Al2.125Si0.875S6, Li2.25Al2.25Si0.75S6, Li2.5Al2.5Si0.5S6, or the like.

[0034] Figs 1, 5, and 9 illustrate Li+ migration paths of the Li2+xAl2+xSi1-xS6 material, wherein gray Li+ ion is at a transition position artificially inserted between the initial state and the final state, and Li+ transits from the initial state to the final state via the intermediate state. Figs. 4, 8, and 12 illustrate the migration barrier shape of lowest activation energy in these migration channels through the further calculation of transition state. Specifically, the interstitial lithium-ion pushes the lattice lithium-ion to the next gap site and occupies a lattice site, enabling Li+ transport by the means of "interstitialcy". For Li2.125Al2.125Si0.875S6, Li2.25Al2.25Si0.75S6, and Li2.5Al2.5Si0.5S6, the migration barrier is about 0.41, 0.34, and 0.25eV respectively. As a contrast, it is reported in the document (Ceder et al., "First principles study of the Li10GeP2S12 lithium super ionic conductor material", 2012, Chemistry of Materials, Volume 24, Pages 15-17. Mo et al., "Origin of fast ion diffusion in super-ionic conductors", 2017, Nature Communications, Volume 8, Pages 15893.) that Li+ migration barrier of LGPS material (benchmark material in sulfide solid electrolyte) is about 0.2eV It can be seen from this that Li+ in a lattice structure of the Li2.5Al2.5Si0.5S6 material can diffuse easily, and this material is a good potential solid electrolyte material.

[0035] It can be seen from the embodiments above that the Li2+xM2+xM'1-xS6 material disclosed by the invention does not contain phosphorus, and is characterized in improved chemical stability, wide optical band gap (wide electrochemical window), and good Li+ transport capability, thereby having great application potential.

II. Electrochemical Device



[0036] The electrochemical device according to the application includes any device that generates an electrochemical reaction, and specific examples include all kinds of primary batteries, secondary batteries, fuel batteries, solar batteries, or capacitors. Particularly, the electrochemical device is a lithium secondary battery, including a lithium metal secondary battery or a lithium-ion secondary battery. In some embodiments, the electrochemical device according to the application includes a positive electrode, a negative electrode, and the solid electrolyte of the application.

III. Application



[0037] The electrochemical devices manufactured according to the application are applicable to electronic equipment in various fields.

[0038] The electrochemical device according to the application is not particularly limited in the purpose, and can be used for any purpose known in the prior art. In one embodiment, the electrochemical device according to the application can be used for, including but not limited to notebook computers, pen-type computers, mobile computers, e-book players, portable phones, portable fax machines, portable copiers, portable printers, head-mounted stereo headsets, video recorders, liquid crystal TVs, portable cleaners, portable CD players, mini disks, transceivers, electronic notebooks, calculators, memory cards, portable recorders, radios, standby power supplies, motors, automobiles, motorcycles, power-assisted bicycles, bicycles, lighting appliances, toys, game machines, clocks, electric tools, flashlights, cameras, large household batteries, and lithium-ion capacitors.

Embodiments



[0039] The description below is the performance evaluation according to the embodiments of the application.

1. Preparation and performance evaluation of solid electrolyte materials



[0040] The Li2+xM2+xM'1-xS6 material disclosed by the invention can be prepared by many conventional methods. For instance, Li2O, M2O3, and M'O2 can be used as raw materials. They are mixed evenly according to the required molar ratio, ground into the uniform powder by ball milling under the protection of the inert atmosphere, and sintered by the high-temperature solid-state method under the inert atmosphere or vacuum. It can be understood that other preparation means can be selected, e.g., melt quenching. Certainly, appropriate target materials can also be selected, and the solid electrolyte material is prepared by physical or chemical vapor deposition. The expected element molar ratio can be obtained by deposition by adjusting relevant process parameters. Since these preparation processes are familiar to those skilled in the art, they will not be repeated here.

2. Manufacturing of the electrochemical device



[0041] Some embodiments of the invention also provide a secondary battery, which can be a lithium-ion battery or a lithium metal battery. In the secondary battery, the Li2+xM2+xM'1-xS6 material described in the aforesaid embodiments of the invention can be used. Since the structure of the solid secondary battery is familiar to those skilled in the art, it will not be repeated here.

[0042] The embodiments above are demonstrative implementations of the invention. The implementations of the invention are not limited by the embodiments above. The scope of the invention is only defined by the claims attached and equivalents thereof.


Claims

1. A solid electrolyte material, wherein a general chemical formula of the material is Li2+xM2+xM'1-xS6, where M is at least one of Al, Ga or In, M' is at least one of Si or Ge, and 0<x≤0.5.
 
2. The solid electrolyte material according to claim 1, wherein a general chemical formula of the material is Li2+xA2+xSi1-xS6, where 0<x≤0.5.
 
3. The solid electrolyte material according to claim 1, wherein lattice parameters thereof are about a=13.0±2.0Å,b=8.0±2.0Å, c=13.0±2.0Å, α=90.0°±5°, β=110.0°±10°, and γ=90.0°±5°.
 
4. The solid electrolyte material according to claim 2, wherein lattice parameters thereof are about a=12.0±1.0Å, b=7.0±1.0Å, c=12.0±1.0Å, α=90.0°±5°, β=105°±5°, and γ=90.0°±5°.
 
5. The solid electrolyte material according to claim 1 or 2, wherein the material has diamond-like structural characteristics, coordination of M3+and M'4+in a structure with S2- forms tetrahedrons [MS4] and [M'S4], all corner-sharing tetrahedrons are connected, and Li+ is filled in a gap between tetrahedrons.
 
6. The solid electrolyte material according to claim 1, wherein diffraction peaks may occur at about 14.5°±3°, 15.5°±3°, 17°±3°, 25.5°±3°, 31.5°±3°, 53.0°±3°, or the like in an XRD spectrogram.
 
7. The solid electrolyte material according to claim 2, wherein a Li+ migration barrier thereof is no less than about 0.45 eV.
 
8. The solid electrolyte material according to claim 2, wherein a PBE band gap thereof is no less than about 2.80 eV.
 
9. An electrochemical device, comprising a positive electrode, a negative electrode, and the solid electrolyte according to any one of claims 1-8.
 
10. An electronic device, comprising the electrochemical device according to claim 9.
 




Drawing






















Search report













Cited references

REFERENCES CITED IN THE DESCRIPTION



This list of references cited by the applicant is for the reader's convenience only. It does not form part of the European patent document. Even though great care has been taken in compiling the references, errors or omissions cannot be excluded and the EPO disclaims all liability in this regard.

Patent documents cited in the description




Non-patent literature cited in the description